Analytical detection of paraoxon using acetylcholinesterase as an enzyme on polyaniline/ferric chloride composite film by potentiostatic method
Vikas.B. Deshmukha, Kiran.S. Paithankara,Urrmila.N. Shelkea, Vikas.K. Gadeb*
aDepartment of Physics Hutatma Rajguru Mahavidyalaya,Rajgurunagar, (M.S.) IndiaaDepartment of Physics Research Center,Ahmednagar College Ahmednagar (M.S.) India
bDepartment of Physics, Shri Anand College, Pathardi (M.S.) India
[email protected] [email protected]:
In this paper, a novel responsive electrochemically synthesized composite film was used for
development of biosensor to determination of paraoxon. The sensor was fabricated by coating a
polyanilne (PANI) and ferric chloride (FeCl3) on indium tin oxide (ITO) by electrochemical
deposition process. The PANI/FeCl3 composite film plays the important roles to immobilized
acetylcholinestrase (AChE) to improve the electrochemical response. Under optimized condition,
the detection of paraoxon in a linear range from 0.1µM to 0.9µM was obtained and the detection
limits was 0.1µM. The resulting sensor was sensitive and highly stable for paraoxon. It shows
very good storage stability and recovery rate was 50% of its primary activity within 36 days
while keep at 6 0C.
Keywords: Polyaniline, Electrochemical, Sensor, Acetylcholinesterase, Paraoxon.
1. Introduction
Paraoxon, synthetic phosphorus plays an considerable task in new agricultural production for the
reason that it can protect from insects and agricultural pests or unwanted plants and to improve
plant quality [1-2] However paraoxon residue in fruits, food and environment has harmful to
human health due to its high toxicity, so novel responsive electrochemically synthesized sensor
was developed for the determination of paraoxon. Now a day, many methods have been used for
detection of pesticide such as ‘gas chromatography’ [3] ‘liquid chromatography’ [4] and ‘thin
layer chromatography’ [5] these methods are responsive and reliable but they usually suffer from
costly instrumentation and time consuming [6] compared with biosensor made by
electrochemical synthesis, it is sensitive, quick response and has low-cost, This sensor has wide
application in biological, agricultural and environmental analysis. However there are some
reports on the electrochemical detection of paraoxon such as Fabiana Arduini et.al [7] prepared
1
‘an bounded screen-printed electrode customized with butyrylcholinesterase and Prussian blue
nanoparticles for detection of paraoxon whose linear range was 7×10−9M-4×10−8 M and detection
limit was 4× 10−9 M.’ Yan Ping et al employed ‘new AChE biosensor for detection of paraoxon
based on porous graphene oxide modified glass carbon electrode, the linear range was 10-45
ng/ml and detection limit was 1.58 ng/ml’ [8]. The electro-analytical method is sensitive but
shows poor selectivity therefore to develop electrochemical biosensor with high selectivity for
detection of paraoxon. Conducting polymer composite film means biosensor is a good choice for
detection of pesticides, it is independent device that integrates immobilized biological element
like enzyme [9-13].The enzyme based sensor is a good choice because of their simple synthesis
and measurement process, high responsive, short response time, sensitive, and reproducible. The
inhibition activity of enzyme is controlled by oxidation current by applied certain potential. To
study of the structural, electrical and optical properties of polymer films for immobilization point
of views AChE enzyme is easy immobilization on thin film for determination of pesticides [14].
AChE enzyme is excellent inhibitor for polymer film to produce sensor which is sensitive
microenvironment for bio-molecules and good bonding to the anlyte [15-16]. In present work
the electrochemical polymerization takes place due to redox reaction with suitable concentration
of aniline, H2SO4 and FeCl3 and Indium tin oxide (ITO), platinum foil and silver/silver chloride
(Ag/AgCl) electrodes are used in cell. PANI/FeCl3 composite film is synthesized for
development of pesticide sensor by immobilization of AChE enzyme for clean with phosphate
buffer solution [17-18].
2. Experimental methods
2.1 Reagents
Aniline (98%), Paraoxon (99%), and Acetylcholinesterase was purchased from Sigma Aldrich,
Required chemicals and ITO Sheet purchased from Lobachemie Pvt. Ltd. Mumbai, India.
2.2. Apparatus
UV-visible spectroscopy-Analytic Jena specord 210 plus Wavelength (200 nm-800 nm), Fourier
transformation infrared radioscopy FTIR-6100 type, Scanning electron microscopy-FEI (Nova
NanoSEM 450) with Energy Dispersive Spectrometer (EDS), Single Crystal- X-Ray
Diffractometer (SC-XRD) was taken by Savitribai Phule Pune University, CIF (Central
Instrumentation Facility) Pune, India.
2
2.3. Electrochemical Synthesis of PANI/FeCl3
Electrolytic solution was made by 0.5M H2SO4, 0.5M FeCl3 and 0.1N an aqueous solution of
aniline (98%) monomer in double distilled water in electrochemical cell [19-20]. The pH of
aqueous medium was maintained by using phosphate buffer solution. The electrochemical
polymerization of aniline monomer and FeCl3 was synthesized by galvanostatic method [21-24].
PANI film is composed with FeCl3 on ITO substrate.
2.4. Synthesis of enzyme based biosensor AChE/PANI/FeCl3/ITO
Pure 8.0 µL enzyme (AChE) was dropped on the surface of the PANI/FeCl3/ITO thin film (PBS)
and incubates it at 200C for 24 h. then rinse with distilled water, dried out and keep at 60C prior
to use. Then this electrode was prepared for electrochemical measurement, it constitute an actual
role from the composite surface for the effectiveness of the biosensor without the cross-linking
agents to build bonding to the active site of enzymes [25-26].
2.5. Electrochemical Measurement
The current response of the sensor for detection of pesticide was measured with a two-step
process. The AChE/PANI/FeCl3/ITO sensor was immersed in a cell contain 10 ml buffer
solution (pH 7.0) and observed current response was I0 then the sensor was incubated for 20 min.
in 0.5M of standard solution of paraoxon. After the incubation the sensor was washed with
buffer solution, then immersed to the cell containing buffer solution pH 7.0 and measured current
response which was I1. The inhibition rate of the pesticides was calculated by following formula.
∆I (%) = (I0-I1)/I0 X100
Where, ∆I= inhabited rate, I0= initial current response of sensor without paraoxon and I1 = current
response in standard solution of paraoxon [27].
2.6. Acetylcholinestrase reactivation
For the purpose of second time use and economy, PANI/FeCl3/ITO electrode was recovered by
pyridine 2-aldoxime methochloride (2-PAM), the sensor was free to pesticides, it was wash with
PBS (pH-7) and distilled water and reactivated with 4.0 mM 2-PAM for 10 minutes, then
transferred to the electrochemical cell of 10 ml PBS (pH-7) under slow magnetic stirring.
Paraoxon was added and the peak current was recorded as I2. The reactivation efficiency (R %) is
calculated as the following equation [28].
R % = (I2/I0) ×100%
Where, I2= the current response after AChE reactivation.
3
3. Result and Discussion
3.1. Ultraviolet–Visible spectroscopy
The absorption spectrum of PANI/FeCl3/ITO film was recorded at room temperature by
Analytic Jena specord210 plus spectrophotometer with wavelength range 200 -800 nm as shown
in fig.1 the spectra shows three peaks at around 264nm, 331nm and 491nm. The peak at around
264 nm shows π→ π* transitions which is available in compounds with unsaturated centers and
aromatics compounds. Second peak 331nm absorption is responsible for bi-polaron state and
peak 491 nm shows charge transfer bands indicates conductivity of thin film having band gap
energy is 2.56 eV. The peak 491 nm indicates aniline is more doped has resulted in stronger
absorption. The absorption spectrum observed for synthesized composite film has good
agreement with the earlier reported work [29]. This shows excellent semblance with the
polymerization potential.
3.2. Fourier Transformation Infrared Radiation (FTIR) analysis
The FTIR spectrum of PANI/FeCl3/ITO composite film with immobilization of AChE enzyme is
shown in fig. 2 the spectra show various peaks, the peak at 3325.33 cm -1 tends to N-H stretching.
The peaks at 1230.38 and 1338.19 cm-1 which is assigned to evidence of the presence of anion in
the polymer film i.e. S=O stretching in sulfonate. The peak having wave number 1709.33 cm-1
shows vibration bands (C=O) these peaks indicate to the characteristic for aniline it shows really
nice agreement with previous reported work [30]. Thus the FTIR spectral results confirm the
existence of polyaniline.
3.3. X-ray diffraction
X-ray spectroscopy of PANI/FeCl3/ITO film is shown in fig.3 the intensity of observed peaks is
indicates that the composites film is developed using di and tri basic acid solutions compare with
the monobasic acid. The report of the characteristic peak of PANI/FeCl3/ITO at 2Ɵ =25.110 the
obtained pattern shows a mostly amorphous material with few crystalline phases.
3.4. Scanning Electron Microscopy and Energy dispersive X-ray spectroscopy
The SEM images of PANI/FeCl3/ITO of synthesized thin films with and without immobilization
of enzyme are shown in fig.4 (a, b, c and d) having magnifications 30KX and 50KX. Image a, b
shows porous morphology of composite film. Such nature is easily supportive for immobilization
of enzymes for the biosensor application. Image c and d show morphology changed with enzyme
immobilized onto the modified electrode further, uniform and granular coating of the enzyme
4
proved that the sensor electrode before immobilization serves as a very good host-guest platform
for bimolecular immobilization. Fig. 4.e and f shows E-DAX spectrum and graphical
representation of electrode. It indicates composition of various chemical compounds used for
synthesized film. E-DAX image also finds parentages of chemical elements present in a sample.
4. Optimization parameters of experimental
4.1. Effect of potential
The potential of the PBS solution was measured by AChE/PANI/FeCl3/ITO electrode with
current. Fig.5 shows the current increases rapidly with increase in potential which indicates that
the response of the AChE electrode was controlled by the electrochemical method. The rate of
redox reaction is related to the concentration of electro active group, the pH value of solution and
applied potential [31]. The response of the electrode at higher potential is decreased but at 0.9V,
the current was nearly steady at which the rate of limiting process of enzyme, diffusion-control
of H2O2 and substrate [32]. So we had set the potential at 0.9V for the further studies of sensor
electrode.
4.2. Effect of pH
The pH of the electrolytic solution was adjusted by using HCl and NaOH. The pH reading of
solution is measured by taking the range from 1 to 9. It prevents loss of the enzyme activity
under polymerization conditions [33].Therefore pH is important for enzymatic sensor response
of the sampling solution. The effect of pH on the performance of the AChE electrode was
studied with 0.1 M PBS with 0.5 µM paraoxon. The current is measured at 0.9V by various pH
values as is shown in fig.6. In electrochemical polymerization the doping response for
electrolytic substance and dopants was quite better at pH range from 2 to 5 and the peak current
occur at pH 7 [34].
4.3. Current response
The current response of AChE/PANI/FeCl3/ITO sensor was measured for various paraoxon
concentrations with time set at 0.9V constant potential. The current is measured in the linear
range 0.1 µM to 0.9 µM of paraoxon concentration. It was found that, the current increases with
increasing paraoxon concentration as shown in fig.7 In the present case, the enzyme is uniformly
immobilized on the composite film so the reaction takes place mainly on the surface of the film
5
in the lower concentration and the dispersion taking place at the same time at higher
concentrations delays the response time.
4.4. Michaelis–Menten constant (Km)
Michaelis–Menten constant shows the concentration of the substrate when reaction velocity is
equal to one half of the maximum velocity. The relationship between current-1 against paraoxon-1
concentration in 0.1 M PBS is shown in Fig.8 at the maximum current (Imax) was 29 μA. The
value of Km is 0.9 it depends on immobilization of enzyme, low value of Km shows reaction
approaches more rapidly and faster response of the sensor.
4.5. Effect of incubation time
The enzyme activity of pesticides sensor was tested for incubation times (0–20 min) in a 0.5µM
pesticide solution. It was observed that enzyme inhibition increased with incubation period until
getting a stable level as shown in fig.9 however the decrease in activity was less prominent after
10 minutes for pesticide so incubation time was 10 min. which is better than earlier works [35].
4.6. Reactivation of the AChE electrode with 2-pyridine aldoximemethiodide (2-PAM)
The sensor was reactivated by cleaned with PBS and immersed in a 4.0 mML -1solution of 2-
PAM, 90% activity of AChE was restored of its original value by 2-PAM treatment for 15 min.
i.e. irreversible inhibition of AChE pesticides electrode was reactivated by this process.
Table1. Comparison of performance of various sensor electrodes for pesticide detection
Sensor electrode Pesticide (Analyte)
Linear range Detection limit
Inhibition time (min)
References
Au/PANI modified CPE Atrazine 1-18µMol/L 0.3µMol/L
- 24
AChE/Fe3O4/Gr/ SPE Chlorpyrifos 0.05-100 μg/L 0.02 μg/L 15 26
AuNps/MPS/Au/AChE Carbamate 0.003-3.0µM 1.0nM 10 32
AChE/SnO2cMWCNTs/Cu MethylParathion
1-160 𝜇M 0.1𝜇M - 31
PANI/AuNPs/Pt/AChE Paraoxon 3.6 × 10−7-3.6 × 10−4 𝜇M
0.026 × 10−5 𝜇M20 34
BChE immobilized on PBNPs/SPE
Paraoxon 7 × 10−9M-4 × 10−8 M
4 × 10−9 M 10 7
6
AChE/HGO/GCE Paraoxon 10-45 ng/ml 1.58 ng/ml 10 8
AChE/PANI/FeCl3/ITO Paraoxon 0.1µM- 0.9µM 0.1µM 10 This work
5. Storage stability
The sensor shows long term stability for the suitable use of its application. The storage stability
of the sensor was tested for 6 weeks of storage in 0.1 M PBS (pH 7.0) at 25°C as shown in
fig.10. There was decrease in sensitivity of the sensor of about 10% from the primary value for
every week, It is observed that a very good conservation of the bioactivity than other work.
6. Conclusion
The stability of electrode was enhanced by using ferric chloride as to immobilize the AChE. The
AChE/PANI/FeCl3/ITO electrode shows excellent conductivity, simple and uniform deposition
on surface area of film and good stability as well as sensor is highly responsive, wide detection
range and response time is short. This is inexpensive and simple fabrication method of
AChE/PANI/FeCl3/ITO sensor. The method is used to immobilize enzymes to build a range of
sensors as well as to develop other biological molecules, such as DNA and antibody of sensor.
Acknowledgements
Central Instrumentation Facilities (CIF) Savitribai Phule Pune University (SPPU), Department of
Chemistry and Physics SPPU, Pune, (India) was provided characterization facility. Physics
research centre, Ahmednagar College, Ahmednagar (M.S.) India was provided laboratory
facility.
References
1. Carvalho Fernando P. Food and Energy Security 2017 6(2) 48–60
2. Dr. Pandya Ishan Y. Asian Journal of Applied Science and Technology 2017 2(2) 894-
900
3. Nshimiyimana François Xavier , Abidi Abdellah El , Fekhaoui Mohamed , Benbakhta
Bouchaib , Barakate Nezha , Hami Hind and Soulaymani Abdelmajid Journal of Life
Sciences 2014 8(6) 489-495
4. Baig Sajjad Ahmad, Akhtera Niaz Ahmad, Muhammad Ashfaq and Muhammad Rafique
Asi, American-Eurasian J. Agric. & Environ. Sci. 2009 6 (5) 513-519
7
5. Khan M. H. Azad A.K. Chowdhury A.Z. Rahman M.S. Malek M.A. Journal of Applied
Science and Technology 2010 7 91-94
6. Chauhan Nidhi, Narang Jagriti, Pundir C.S. International journal of Biological
macromolecules 2011 49 (5) 923-929
7. Arduini Fabiana, Neagu Daniela, Scognamiglio Viviana, Patarino Sabrina, Moscone
Danila and Palleschi Giuseppe Chemo sensors 2015 3 129-145
8. Ping Yan, Li R Li, Zhao Rui Xia, Han Gao Yi, and Xiao Yao Ming, Electro analysis
2018 30 2258- 2264
9. Stoytcheva M. Zlatev R. InTech Croatia 2011 143–164
10. Sassolas Andrey, Beatriz Peieto-Siman, Matry Taen-Lows American Journal of
Analytical Chemistry 2012 3 210-252
11. Stoytcheva M. Gochev V. Velkova Z. Curr. Anal. Chem. 2016 12 37-42
12. Zhao Guo, Yemin Guo, Xia Sun, Xiangyou Wang, Int. J. Electrochem.Sci. 2015 10 3387
- 3399
13. Mohamed E. I. Badawy and Ahmed F. El-Aswad International Journal of Analytical
Chemistry 2014 1155 8-10
14. Dhull Vikas, Gahlaut Anjum, Dilbaghi Neeraj, and Hooda Vikas, Biochemistry research
international 2013 18
15. Abdulla Hasoon Salah and Abbo Abdullah Ibrahim Int. J. Electrochem. Sci. 2012 7
10666-10678
16. Monika, Kumar Rajesh, Chauhan R.P. Kumar R. Chakarvarti S.K. Indian Journal of
Pure & Applied Physics 2010 48 524-526
17. Ates Murat Materials Science and Engineering C 2013 1853-1859
18. Chauhan Nidhi, Pundir Chandra Shekhar Electrochimica Acta 2012 67 79-86
19. Patel Heta A. Sawant Aishwarya M. Rao Vandana J. Patel Arun L. Catal Lett 2017 147
2306-2312
20. Yazid Mohammed Izzuddeen Mohd, Ghani Supri Abdul, Siti Azlin Fazlina Osmanand
Hajar Mohd Din Journal of Physical Science 2018 29 (1) 49-63
21. Zeng Fanxin, Qi Zongyi, Liang Banglei, Tao Li, NaLiu, Meifang Zhu, Materials
International 2015 25 512-519
8
22. Shukla S.K. Bharadvaj Anand, Tiwari Ashutosh, Parashar G.K. Dubey G.C. Adv. Mat.
Letts. 2010 1(2) 129-134
23. Chougule Manik A. Pawar Shailesh G. Godse Prasad R. Mulik Ramesh N. Sen
Shashwati, Patil Vikas B. Soft Nanoscience Letters 2011 1 6-10
24. Soreta Tesfaye Rafera, Gojeh Mary, Moses Yilleng, Yakubu Yahaya and Bahago
Nathaniel Journal of Applied Chemistry 2015 8(10) 2278-5736
25. Montes R. Céspedes F. Gabriel D. and Baeza M. Hindawi Journal of Nanomaterials
2018 13
26. Wang Hui, Zhao Guo, Chen Dongfei, Wang Zhiqiang, Liu Gang Int. J. Electrochem. Sci.
2016 11 10906-10918
27. Chauhana N. Narang J. and Jain U. Journal of Experimental Nanoscience 2016 11(2)
111-122
28. Sarmah Smritimala and Kumar A Bull. Mater. Sci. 2013 36(1) 31-36
29. Singh Susheel Kumar, Verma Arvind Kumar, and Shukla R. K. Int. J. Curr. Microbiol.
App. Sci 2014 3(7) 512-517
30. Butoi Bogdan, Groza Andreea, Dinca Paul, Balan Adriana and Barna Valentin Polymers
2017 9 732
31. Dhull Vikas, Hindawi International Journal of Analytical Chemistry2018 10 1155
32. Jingyi Yonghai Song, Chen Min Sun, Coucong Gong, Yonggui Yuan Shen, Wang Song
Li Journal of Hazardous Materials 2015 10 1016
33. Marinov I. Ivanov Y. Gabrovska K. and Godjevargova T. Journal of Molecular Catalysis
B: Enzymatic 2010 62(1) 66-74
34. Upadhyay S. Rao G. R. Sharma M. K. Bhattacharya B. K. Rao V. K. Vijayaragha-van R.
Bioelectron. 2009 25 832
35. Rajangam Bhuvanagayathri, Daniel David K. Krastanov Albert Ivanov Eng. Life Sci.
2018 18 4-19
Figures title
Fig .1 UV–Vis studies of PANI/FeCl3/ITO Electrode
Fig. 2 FTIR studies PANI/FeCl3/ITO based Electrode.
Fig. 3 XRD of PANI/FeCl3/ITO
9
Fig. 4.a SEM of PANI/FeCl3/ITO film without enzyme (Mag. 30 KX)
Fig. 4.b SEM of PANI/FeCl3/ITO film without enzyme (Mag. 50 KX)
Fig.4.c SEM of PANI/FeCl3/ITO film with enzyme (Mag. 30 KX)
Fig.4.d SEM of PANI/FeCl3/ITO film with enzyme (Mag. 50 KX)
Fig.4.e E-DAX of PANI/FeCl3/ITO film
Fig. 5 Current verses potential curves for the AChE/PANI/FeCl3/ITO sensor in 0.1M PBS
Fig. 6 Effect of pH on the AChE/PANI/FeCl3/ITO sensor response of paraoxon
Fig. 7 Current response curve of AChE/PANI/FeCl3/ITO sensor
Fig.8 Michaelis–Menten constant (Km) for the AChE/PANI/FeCl3/ITO sensor in 0.1M PBS
Fig.9 Effect of inhibition time on paraoxon (in 0.5 µML−1) at 0.9 V vs. Reference electrode
Fig.10 Storage stability of the AChE/PANI/FeCl3/ITO sensor in 0.1M PBS
Fig .1 UV–Vis studies of PANI/FeCl3/ITO Electrode
Fig. 2 FTIR studies PANI/FeCl3/ITO based Electrode
10
Fig. 3 XRD of PANI/FeCl3/ITO (Intensity-1237 and 2θ-25.61)
Fig.4 (a) SEM of PANI/FeCl3/ITO film without enzyme (Mag. 30 KX), (b) SEM of
PANI/FeCl3/ITO film without enzyme (Mag. 50 KX)
Fig.4 (c) SEM of PANI/FeCl3/ITO film with enzyme (Mag. 30 KX), (d) SEM of
PANI/FeCl3/ITO film with enzyme (Mag. 50 KX)
11
Fig.4 (e) E-DAX of PANI/FeCl3/ITO film
Fig.4 (f) E-DAX shows composition of PANI/FeCl3/ITO film
Fig. 5 Current verses potential curves for the AChE/PANI/FeCl3/ITO sensor in 0.1M PBS
12
Fig. 6 Effect of pH on the AChE/PANI/FeCl3/ITO electrode response of paraoxon
Fig. 7 Current response curve of (AChE/PANI/FeCl3/ITO) electrode
Fig.8 Michaelis–Menten constant (Km) for the AChE/PANI/FeCl3/ITO sensor in 0.1M PBS
13
Fig.9 Effect of inhibition time on paraoxon (in 0.5 µML−1) at 0.9 V vs. Reference electrode
Fig.10 Storage stability of the AChE/PANI/FeCl3/ITO sensor in 0.1M PBS
14