Available online at www.worldscientificnews.com
WSN 80 (2017) 29-42 EISSN 2392-2192
Development and SEM/EDS characterisation of
porous coatings enriched in magnesium and copper obtained on titanium by PEO with ramp voltage
Krzysztof Rokosza, *Tadeusz Hryniewiczb, Kornel Pietrzakc, Łukasz Dudekd
Division of Bioengineering and Surface Electrochemistry, Department of Engineering and Informatics Systems, Faculty of Mechanical Engineering, Koszalin University of Technology,
Racławicka 15-17, PL 75-620 Koszalin, Poland
E-mail address: [email protected], [email protected],
[email protected], [email protected],
*Corresoponding author: [email protected]
ABSTRACT
In the present paper, the SEM and EDS results of porous and enriched in calcium and/or zinc
coatings, which were obtained during 3-minute treatments by Plasma Electrolytic Oxidation/ Micro
Arc Oxidation processes on CP Titanium Grade 2 at ramp potentials (liner polarization) from 0 up to
650 VDC in electrolytes containing 500 g Mg(NO3)2∙6H2O and/or 500 g Cu(NO3)2∙3H2O in 1 L H3PO4,
are reported. It was found that the obtained coatings, dependent on the PEO process conditions, have
pores with different shapes and diameters. The Mg/P and Cu/P ratios by atomic concentration are the
same and equal to 0.09±0.01 (by wt %) | 0.11±0.01 (by at%) and/or 0.40±0.08 (by wt %) | 0.19±0.04
(by at%), respectively. That may testify the hydroxyapatite-like structures of Mg-Ti-PO43–
and/or Cu-
Ti-PO43–
have been identified to occur.
Keywords: Plasma Electrolytic Oxidation (PEO), Micro Arc Oxidation (MAO), CP Titanium Grade 2,
calcium nitrate Mg(NO3)2∙6H2O, zinc nitrate Ca(NO3)2∙3H2O, ramp voltage, linear polarization
World Scientific News 80 (2017) 29-42
-30-
1. INTRODUCTION
Titanium and its alloys are key biomaterials used for medical devices like orthopaedic
and dental implants. This is because titanium holds a unique combination of surface and bulk
properties, which includes high surface TiO2 stability, Young’s modulus closer to that of
human bone and high specific strength [1-3]. The surface topography and composition of
surface layer play important roles on guiding the bone integration between the implant surface
and cells. The manufacturing process can improve the corrosion resistance, wear behavior and
affect various other functional properties. The surface modification of titanium and its alloys
has increased the number of potential applications of these materials in different fields and
industries, such as aerospace, marine, chemical industry, automotive and biomaterials [3-5].
Metals have poor biocompatibility because metals or alloys tend to release metal ions
that cause pathological changes in cells, alter genes, and form cancer cells. An appropriate
surface treatment is critically required for the biomedical implants such as dental implants,
artificial hips and knee components to modify and improve their bioactivity and mechanical
properties. To improve the chemical features and biocompatible abilities, numerous surface
modification techniques have been progressively developed and applied to different metals,
alloys or ceramics for biomedical purposes. Moreover, enhancing the corrosion resistance of
titanium and its alloys are crucial to increasing the biocompatibility. The life quality of
patients could be improved by using biomaterials that may interact with biological systems
having minimal flaws and long service. Therefore, thanks to improved properties, they may be
used for manufacturing human body implants [3-6].
This paper is a continuation of the works on fabrication and surface characterization of
porous coatings which were obtained on Titanium by Plasma Electrolytic Oxidation process
in electrolytes containing selected nitrates, what was first related partly in reference [7]. It has
to be pointed out that with use of electrochemical methods it may be possible to obtain both
nano-layers as well as micro-layers (micro-coatings).
Therefore a standard electropolishing (EP) [8-11], magnetoelectropolishing (MEP) [12-
21] or high-current density electropolishing (HDEP) [22-24] may be used to form nano-layers
on metals and alloys, whereas the micro coatings may be obtained by the Plasma Electrolytic
Oxidation (PEO) also known as Micro Arc Oxidation (MAO) [25-44]. Among the different
surface modification techniques (CVD, PVD, ion implantation, electroplating, plasma
nitriding, thermal oxidation), anodic oxidation, especially the plasma electrolytic oxidation
(PEO) process has become increasingly important since it has advantages over other methods
of surface modification [1-6, 25-44]. The PEO process creates porous coatings on titanium [2,
7, 25-33] and its alloys [2-6, 34-39], which may be enriched in bactericidal copper [45-55] as
well as in magnesium, which may accelerate the healing of wounds [56-57].
The aim of this paper is the development and SEM/EDS characterisation of PEO porous
coatings, enriched in magnesium and copper, obtained on titanium. The three primary factors
of biocompatibility on the cellular level are genotoxicity, carcinogenicity, and cytotoxicity.
The pore size and surface roughness formed by PEO play an important role in the adsorption
of proteins, adhesion of cells, and the rate of osseointegration.
World Scientific News 80 (2017) 29-42
-31-
2. METHOD
The samples of CP Titanium Grade 2 with dimensions 10 10 2 mm were treated by
Plasma Electrolytic Oxidation (Micro Arc Oxidation) for the surface studies. The plasma
electrolytic oxidation (PEO) was performed at the ramp voltages from 0 up to 650 VDC. For
the studies, the electrolyte based on orthophosphoric acid H3PO4 with 500 g/L of calcium
nitrate Mg(NO3)2∙6H2O or copper nitrate Cu(NO3)2∙3H2O was used. For each run, the
electrolytic cell made of glass was used, containing up to 500 ml of the electrolyte.
Scanning Electron Microscope (SEM) FEI Quanta 650 FEG equipped with Energy-
Dispersive X-ray Spectroscopy (EDS) for surface analysis was used. The microscope
operated under the following conditions: voltage 15 kV, current 8-10 nA, beam diameter
6 μm, decreased vacuum in the chamber with the pressure of 50 Pa. The identification of
spectral lines was performed by means of a spectral decomposition using the holographic
peak deconvolution function.
3. RESULTS AND DISCUSSION
In Figures 1-3, the SEM pictures of coating formed on Titanium after PEO treatment at
ramp voltages from 0 till 650 VDC (linear polarization) in electrolyte containing of 500 g
Mg(NO3)2∙6H2O in 1 L H3PO4, are presented. The EDS spectrum of obtained coating is
shown in Figure 4. These EDS peaks of phosphorus, titanium and magnesium show that
formed PEO coating is built mainly of phosphorus-titanium-magnesium compounds, what
may suggest the existence of hydroxyapatite-like structure enriched in magnesium, which
replaced the calcium in that structure.
In the PEO coating, apart from the titanium (40.3±1.1 wt% | 29.9±0.8 at%), which is a
substrate, and which signal may partly come from matrix, phosphorus (54.9±0.7 wt% |
63.1±0.6 at%) and magnesium (4.8±0.4 wt% | 7.0±0.5 at%) were also recorded, what is
presented in Figure 5. In addition, the median and range of results were found out. Thus the
medians of magnesium, phosphorus and titanium were equal to 4.8 wt% (6.7 at%), 55 wt%
(63.1 at%) and 40.1 wt% (29.7 at%), respectively. The highest range of obtained results were
observed for titanium (2.9 wt%|2.2 at%), while the smallest one for magnesium (0.9 wt%|1.3
at %). In Figures 6-8, the SEM pictures of coating formed on Titanium after PEO treatment at
ramp voltages from 0 till 650 VDC (linear polarization) in electrolyte containing of 500 g
Cu(NO3)2∙3H2O in 1 L H3PO4, are presented. The EDS spectrum of obtained coating is shown
in Figure 9. These EDS peaks of phosphorus, titanium and magnesium show that formed PEO
coating is built mainly of phosphorus-titanium-copper compounds, what may suggest the
existence of hydroxyapatite-like structure enriched in copper, which replaced the calcium in
that structure.
In the PEO coating behind the titanium (52.3±4.9 wt% | 45.4±4.9 at%), which is a
substrate, and which signal may partly come from matrix, phosphorus (34.2±4.0 wt% |
45.7±4.5 at%) and copper (13.5±2.2 wt% | 8.8±1.4 at%) were also recorded, what is presented
in Figure 10. Thus the medians of copper, phosphorus and titanium were equal to 13.8 wt%
(8.9 at%), 33.4 wt% (44.7 at%) and 53.3 wt% (46.7 at%), respectively. The highest range of
obtained results were observed for titanium (11.6 wt%|11.1 at%), while the lowest one for
copper (4.7 wt%|3.3 at%).
World Scientific News 80 (2017) 29-42
-32-
Fig. 1. SEM picture of coating formed on Titanium after PEO treatment at ramp voltages
from 0 till 650 VDC in electrolyte containing of 500 g Mg(NO3)2∙6H2O in 1 L H3PO4.
Magnification 2 500 times
Fig. 2. SEM picture of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Mg(NO3)2∙6H2O in 1 L H3PO4.
Magnification 5 000 times
World Scientific News 80 (2017) 29-42
-33-
Fig. 3. SEM picture of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Mg (NO3)2∙6H2O in 1 L H3PO4.
Magnification 10 000 times
Fig. 4. SEM picture of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Mg(NO3)2∙6H2O in 1 L H3PO4
World Scientific News 80 (2017) 29-42
-34-
Fig. 5. Comparison of mean values of EDS results of coating formed on Titanium after PEO
treatment at voltages from 0 till 650 VDC in electrolyte containing
of 500 g Mg(NO3)2∙6H2O in 1 L H3PO4
Fig. 6. SEM picture of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Cu(NO3)2∙3H2O in 1 L H3PO4.
Magnification 2 500 times
World Scientific News 80 (2017) 29-42
-35-
Fig. 7. SEM picture of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Cu(NO3)2∙3H2O in 1 L H3PO4.
Magnification 5 000 times
Fig. 8. SEM picture of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Cu(NO3)2∙3H2O in 1 L H3PO4.
Magnification 10 000 times
World Scientific News 80 (2017) 29-42
-36-
Fig. 9. EDS result of coating formed on Titanium after PEO treatment at voltages from 0 till
650 VDC in electrolyte containing of 500 g Cu(NO3)2∙3H2O in 1 L H3PO4
Fig. 10. Comparison of mean values of EDS results of coating formed on Titanium after PEO
treatment at voltages from 0 till 650 VDC in electrolyte containing of 500 g Cu(NO3)2∙3H2O
in 1 L H3PO4
World Scientific News 80 (2017) 29-42
-37-
To characterize the metal surface after PEO treatment, the two ratios (Figure 11), i.e.
Mg/P and Cu/P, which were equal to 0.09±0.01 (by wt%) | 0.11±0.01 (by at%) and 0.40±0.08
(by wt%) | 0.19±0.04 (by at%), were calculated. Based on the experimental results it may be
concluded that in hydroxyapatite-like structures obtained, there is about two times more atoms
of copper than those ones of magnesium forming a similar structure.
Fig. 11. Mg/P and Cu/P ratios of EDS results of coating formed on Titanium after PEO
treatment at voltages from 0 till 650 VDC in electrolyte containing of 500 g MgNO3)2∙6H2O or
CuNO3)2∙3H2O in 1 L H3PO4
4. CONCLUSIONS
At this stage of the PEO studies, the following conclusions may be drawn:
during the PEO process with use of a liner polarization (ramp voltage) from 0 till 650
VDC, it is possible to obtain the porous surface enriched in calcium and phosphorus in
electrolyte containing 500 g Mg(NO3)2∙6H2O and/or 500 g Cu(NO3)2∙3H2O in 1 L
H3PO4
the Mg/P and Cu/P ratios by atomic concentration are the same and equal to 0.09±0.01
(by wt %) | 0.11±0.01 (by at %) and 0.40±0.08 (by wt %) | 0.19±0.04 (by at %),
respectively; such a composition of porous coating suggests the hydroxyapatite-like
structure consisting with Mg-Ti-PO43–
and/or Cu-Ti-PO43–
.
World Scientific News 80 (2017) 29-42
-38-
This way it is proved the PEO has been becoming a promising technique for surface
modifications.
Acknowledgements
This work was supported by subsidizing by Grant OPUS 11 of National Science Centre, Poland, with
registration number 2016/21/B/ST8/01952, titled "Development of models of new porous coatings obtained on
titanium by Plasma Electrolytic Oxidation in electrolytes containing phosphoric acid with addition of calcium,
magnesium, copper and zinc nitrates".
Assoc. Prof. Jan Valíček and Dr Dalibor Matýsek from Vysoká škola báňská - Technická univerzita Ostrava -
VŠB-TUO, Czech Republic, are given thanks for providing access to the SEM/EDS apparatus allowing to
perform the studies.
References
[1] Isabella da Silva Vieira Marques,Nilson Cristino da Cruz, Richard Landers, Judy Chia-
Chun Yuan, Marcelo Ferraz Mesquita, Cortino Sukotjo, Mathew T. Mathew, and
Valentin Ricardo Barao, Incorporation of Ca, P, and Si on bioactive coatings produced
by plasma electrolytic oxidation: The role of electrolyte concentration and treatment
duration, Biointerphases, 11 (2016) 031008; http://doi.org/10.1116/1.4960654
[2] Yavari S.A., Necula B.S., Fratila-Apachitei L.E., Duszczyk J., Apatichei I.,
Biofunctional surfaces by plasma electrolytic oxidation on titanium biomedical alloys,
Surface Engineering, 32(6) (2016) 411-417; DOI: 10.1179/1743294415Y.0000000101
[3] Quintero D., Galvis O., Calderón J.A., Gómez M.A., Castaño J.G., Echeverría F.,
Habazaki H., Control of the physical properties of anodic coatings obtained by plasma
electrolytic oxidation on Ti6Al4V alloy, Surface and Coatings Technology, 283 (2015)
210-222
[4] Davis J.R., ‘Handbook of materials for medical devices’, Chapter 3, ‘Metallic
materials’, 21–50; 2003, Materials Park, OH, ASM International.
[5] Ming-Tzu Tsai, Yin-Yu Chang, Henh-Li Huang, Yu-Hsuan Wu, Tzong-Ming Shieh,
Micro-arc oxidation treatment enhanced the biological performance of human
osteosarcoma cell line and human skin fibroblasts cultured on titanium–zirconium films,
Surface and Coatings Technology, 303A (2016) 268-276
[6] Mónica Echeverry-Rendón, Oscar Galvis, David Quintero Giraldo, Juan Pavón, Jose
Luis López-Lacomba, Emilio Jimenez-Pique, Marc Anglada, Sara M. Robledo, Juan G.
Castaño, Felix Echeverrıa, Osseointegration improvement by plasma electrolytic
oxidation of modified titanium alloys surfaces, Journal of Materials Science: Materials
in Medicine, 72 (2015) 26 (18 pages); DOI 10.1007/s10856-015-5408-4
[7] Rokosz K., Hryniewicz T., Pietrzak K., SEM and EDS studies of porous coatings
enriched in calcium and zinc obtained by PEO with ramp voltage, World Scientific
News, 77(2) (2017) 242-255
[8] Hryniewicz T., Physico-chemical and technological fundamentals of electropolishing
steels (Fizykochemiczne i technologiczne podstawy procesu elektropolerowania stali),
World Scientific News 80 (2017) 29-42
-39-
Monograph No. 26 (1989) Koszalin University of Technology Publishing House, ISSN
0239-7129 (in Polish).
[9] Hryniewicz T., On the surface treatment of metallic biomaterials (Wstęp do obróbki
powierzchniowej biomateriałów metalowych), Koszalin University of Technology
Publishing House (2007) ISSN 0239-7129 (in Polish).
[10] Hryniewicz T., Rokosz K., Zschommler Sandim H.R., SEM/EDX and XPS studies of
niobium after electropolishing, Applied Surface Science, 263 (2012) 357-361.
[11] Rokosz K., Electrochemical Polishing in magnetic field (Polerowanie elektrochemiczne
w polu magnetycznym), Koszalin University of Technology Publishing House (2012)
ISSN 0239-7129 (in Polish).
[12] Hryniewicz T., Rokicki R., Rokosz K., Co-Cr alloy corrosion behaviour after
electropolishing and "magnetoelectropolishing" treatments, Surface and Coatings
Technology, 62(17-18) (2008) 3073-3076
[13] Hryniewicz T., Rokosz K., Analysis of XPS results of AISI 316L SS electropolished
and magnetoelectropolished at varying conditions, Surface and Coatings Technology,
204(16-17) (2010) 2583-2592
[14] Hryniewicz T., Rokicki R., Rokosz K., Magnetoelectropolishing for metal surface
modification, Transactions of The Institute of Metal Finishing, 85(6) (2007) 325-332
[15] Hryniewicz T., Rokicki R., Rokosz K., Corrosion and surface characterization of
titanium biomaterial after magnetoelectropolishing, Surface and Coatings Technology,
203(9) (2008) 1508-1515
[16] Hryniewicz T., Rokosz K., Polarization characteristics of magnetoelectropolishing
stainless steels, Materials Chemistry and Physics, 122(1) (2010) 169-174
[17] Rokosz K., Hryniewicz T., Raaen S., Characterization of passive film formed on AISI
316L stainless steel after magnetoelectropolishing in a broad range of polarization
parameters, Journal of Iron and Steel Research, 83(9) (2012) 910-918
[18] Hryniewicz T., Rokosz K., Investigation of selected surface properties of AISI 316L SS
after magnetoelectropolishing, Materials Chemistry and Physics, 123(1) (2010) 47–55.
[19] Hryniewicz T., Rokosz K., Corrosion resistance of magnetoelectropolished AISI 316L
SS biomaterial, Anti-Corrosion Methods and Materials, 61(2) (2014) 57-64
[20] Hryniewicz T., Rokosz K., Valiček J., Rokicki R., Effect of magnetoelectropolishing on
nanohardness and Young’s modulus of titanium biomaterial, Materials Letters, 83
(2012) 69-72
[21] Hryniewicz T., Rokosz K., Rokicki R., Prima F., Nanoindentation and XPS Studies of
Titanium TNZ Alloy after Electrochemical Polishing in a Magnetic Field, Materials, 8
(2015) 205-215
[22] Rokosz K., Hryniewicz T., Simon F., Rzadkiewicz S., Comparative XPS analysis of
passive layers composition formed on AISI 304 L SS after standard and high-current
density electropolishing, Surface and Interface Analysis, 47(1) (2015) 87-92
World Scientific News 80 (2017) 29-42
-40-
[23] Rokosz K., Lahtinen J., Hryniewicz T., Rzadkiewicz S., XPS depth profiling analysis of
passive surface layers formed on austenitic AISI 304L and AISI 316L SS after high-
current-density electropolishing, Surface and Coatings Technology, 276 (2015) 516-520
[24] Rokosz K., Hryniewicz T., Simon F., Rzadkiewicz S., Comparative XPS analyses of
passive layers composition formed on duplex 2205 SS after standard and high-current-
density electropolishing, Tehnicki vjesnik - Technical Gazette, 23(3) (2016) 731-735
[25] Rokosz K., Hryniewicz T., Chapon P., Raaen S., Zschommler Sandim H.R., XPS and
GDOES characterisation of porous coating enriched with copper and calcium obtained
on Tantalum via Plasma Electrolytic Oxidation, Journal of Spectroscopy, Article ID
7093071 (2016) 7 pages, http://dx.doi.org/10.1155/2016/7093071.
[26] Han Y., Hong S.H., Xu K.W., Structure and in vitro bioactivity of titania-based films by
micro-arc oxidation, Surface and Coatings Technology, 168 (2003) 249-258
[27] Simka W., Sadowski A., Warczak M., Iwaniak A., Dercz G., Michalska J., Maciej A.,
Modification of titanium oxide layer by calcium and phosphorus, Electrochimica Acta,
56(24) (2009) 8962-8968
[28] Rokosz K, Hryniewicz T., Raaen S., Chapon P., Dudek Ł., GDOES, XPS and SEM
with EDS analysis of porous coatings obtained on Titanium after Plasma Electrolytic
Oxidation, Surface and Interface Analysis, 49(4) (2016) 303-315; DOI:
10.1002/sia.6136
[29] Han Y., Hong S.H., Xu K.W., Synthesis of nanocrystalline titania films by micro-arc
oxidation, Materials Letters, 56 (2002) 744-747
[30] Fei C., Hai Z., Chen C., Yangjian X., Study on the tribological performance of ceramic
coatings on titanium alloy surfaces obtained through microarc oxidation, Progress in
Organic Coatings, 64 (2009) 264-267
[31] Aliasghari S. Plasma Electrolytic Oxidation of Titanium. PhD thesis of Faculty of
Engineering and Physical Sciences, The University of Manchester, School of Materials
(2014) 223 pages
[32] Teh T.H., Berkani A., Mato S., Skeldon P., Thompson G.E., Habazaki H., Shimizu K.
Initial stages of plasma electrolytic oxidation of titanium, Corrosion Science, 45(2003)
2757-2768
[33] Wang Y., Jiang B., Lei T., Guo L., Dependence of growth features of microarc
oxidation coatings of titanium alloy on control modes of alternate pulse, Materials
Letters, 58(12) (2004) 1907-1911
[34] Simka W., Nawrat G., Chlode J., Maciej A., Winiarski A., Szade J., Radwanski K.,
Gazdowicz J., Electropolishing and anodic passivation of Ti6Al7Nb alloy, Przemysł
Chemiczny, 90(1) (2011) 84-90
[35] Krząkala A., Mlynski J., Dercz G., Michalska J., Maciej A., Nieuzyla L., Simka W.,
Modification of Ti-6Al-4V alloy surface by EPD-PEO process in ZrSiO4 suspension,
Archives of Metallurgy and Materials, 59(1) (2014) 199-204
[36] Rokosz K., Hryniewicz T., Raaen S., Development of Plasma Electrolytic Oxidation
for improved Ti6Al4V biomaterial surface properties, International Journal of
World Scientific News 80 (2017) 29-42
-41-
Advanced Manufacturing Technology, 85 (2016) 2425-2437; DOI: 10.1007/s00170-
015-8086-y
[37] Rokosz K., Hryniewicz T., Raaen S., Chapon P., Investigation of porous coatings
obtained on Ti-Nb-Zr-Sn alloy biomaterial by Plasma Electrolytic Oxidation:
Characterisation and Modelling, International Journal of Advanced Manufacturing
Technology, 87 (2016) 3497-3512, DOI 10.1007/s00170-016-8692-3
[38] Rokosz K., Hryniewicz T., Raaen S., Chapon P., Development of copper-enriched
porous coatings on ternary Ti-Nb-Zr alloy by Plasma Electrolytic Oxidation,
International Journal of Advanced Manufacturing Technology, 89 (9-12) (2017) 2953-
2965; DOI 10.1007/s00170-016-9206-z
[39] Rokosz K., Hryniewicz T., Raaen S., SEM, EDS and XPS analysis of nanostructured
coating obtained on NiTi biomaterial alloy by Plasma Electrolytic Oxidation (PEO),
Tehnički vjesnik-Technical Gazette, 24(1) (2017) 193-198
[40] Elliott J.C., Structure and Chemistry of Apatites and Other Calcium Orthophosphates.
Elsevier, Amsterdam, The Netherlands, 1st edition, (1994) 404 pages, eBook ISBN:
9781483290317, Hardcover ISBN: 9780444815828
[41] Elliott J.C., Wilson R.M., Dowker S.E.P., Apatite Structures, Advances in X-ray
Analysis, 45 (2002) 172-181
[42] Dorozhkin S.V., Calcium orthophosphates in nature, biology and medicine, Materials,
2(2) (2009) 399-498
[43] LeGeros R.Z., Calcium phosphate-based osteoinductive materials, Chemical Reviews,
108(11) (2008) 4742-4753
[44] Zakharov N.A., Polunina I.A., Polunin K.E., Rakitina N.M., Kochetkova E.I., Sokolova
N.P., Kalinnikov V.T., Calcium hydroxyapatite for medical applications, Inorganic
Materials, 40(6) (2004) 641-648
[45] Kolmas J., Groszyk E., Kwiatkowska-Róhycka D., Substituted Hydroxyapatites with
Antibacterial Properties, BioMed Research International Article ID 178123, 15 pages
(2014) 1-15; DOI: dx.doi.org/10.1155/2014/178123
[46] Gallo J., Holinka M., Moucha C.S., Antibacterial Surface Treatment for Orthopaedic
Implants, International Journal of Molecular Sciences, 15 (2014) 13849-13880, DOI:
10.3390/ijms150813849
[47] Xiangyu Zhang, Xiaobo Huang, Yong Ma, Naiming Lin, Ailan Fan, Bin Tang
Bactericidal behavior of Cu-containing stainless steel surfaces, Applied Surface Science,
258 (2012) 10058-10063
[48] Hempel F., Finke B., Zietz C., Bader R., Weltmann K.-D., Polak M., Antimicrobial
surface modification of titanium substrates by means of plasma immersion ion
implantation and deposition of copper, Surface and Coatings Technology, 256 (2014)
52-58
[49] Xiaohong Yao, Xiangyu Zhang, Haibo Wu, Linhai Tian, Yong Ma, Bin Tang,
Microstructure and antibacterial properties of Cu-doped TiO2 coating on titanium by
micro-arc oxidation, Applied Surface Science, 292 (2014) 944-947
World Scientific News 80 (2017) 29-42
-42-
[50] Rokosz K., Hryniewicz T., Dudek Ł., Matysek D., Valiček J., Harničarova M., SEM
and EDS Analysis of Surface Layer Formed on Titanium After Plasma Electrolytic
Oxidation in H3PO4 with the Addition of Cu(NO3)2, Journal of Nanoscience and
Nanotechnology, 16 (2016) 7814-7817
[51] Rokosz K., Hryniewicz T., Dalibor M., Raaen S., Valiček J., Dudek Ł., Harničarova M.,
SEM, EDS AND XPS Analysis of the Coatings Obtained on Titanium after Plasma
Electrolytic Oxidation in Electrolytes Containing Copper Nitrate, Materials, 9(318)
(2016) 1-12; DOI: 10.3390/ma9050318
[52] Rokosz K., Hryniewicz T., Raaen S., Chapon P., Dudek Ł., GDOES, XPS and SEM
with EDS analysis of porous coatings obtained on Titanium after Plasma Electrolytic
Oxidation, Surface and Interface Analysis, 49(4) (2016) 303-315; DOI:
10.1002/sia.6136
[53] Rokosz K., Hryniewicz T., Malorny W., Characterisation of porous coatings obtained
on materials by Plasma Electrolytic Oxidation, Materials Science Forum, 862 (2016)
86-95
[54] Rokosz K., Hryniewicz T., Raaen S., Chapon P., Dudek Ł., GDOES, XPS and SEM
with EDS analysis of porous coatings obtained on Titanium after Plasma Electrolytic
Oxidation, Surface and Interface Analysis, 49(4) (2016) 303-315, DOI:
10.1002/sia.6136
[55] Rokosz K., Hryniewicz T., Raaen S., Malorny W., Fabrication and characterisation of
porous coatings obtained by plasma electrolytic oxidation, Journal of Mechanical and
Energy Engineering, 1(1|41) (2017) 23-30
[56] Aina V., Lusvardi G., Annaz B., Gibson I.R., Imrie F.E., Malavasi G., Menabue L.,
Cerrato G., Martra G., Magnesium- and strontium-co-substituted hydroxyapatite: the
effect of doped ions on the structure and chemico-physical properties, Journal of
Materials Science: Materials in Medicine, 23(12) (2012) 2867-2879
[57] Webster T.J., Ergun C., Doremus R.H., Bizios R., Hydroxylapatite with substituted
magnesium, zinc, cadmium, and yttrium. II. Mechanisms of osteoblast adhesion,
Journal of Biomedical Materials Research, 59(2) (2002) 312-317
( Received 10 June 2017; accepted 02 July 2017 )