Thermal resistance up to 1500°C

Thin coatings (0.3 to 0.7 mm)

High corrosion resistance with or without erosion

Substrate not thermally affected. No deformation. No regulatory restrictions

Large, complex surface areas possible to coat

Easy to apply either on site or in workshop

Industrial solutions for surface protection against wear and corrosion

BTC

SO

LUTI

ON

SEnduring Performance...

Stronger, with Castolin Eutectic

NEW BTC DENSIFIED THERMAL SPRAY COATING RANGE

When corrosion is severe or in combination with abrasion or erosion

Stronger with Castolin Eutectic

www.castolin.com www.eutectic.com

Your resources for protection, repair and joining solutions

For additional informationFrance : Mr. Didier Mattiuzzi +33 60 887 6921Worldwide : Mr. Alain Tremblay +41 79 686 6107

www.castolin.com www.eutectic.com

Arc Spray process

● Substrate not thermally affected

● Excellent mechanical bonding

● High efficiency process

● Extremely competitive coating costs

● Large, complex surface areas

Densification

● Chemical reaction with the alloy that creates an exceptional barrier against corrosion

● Densifier range withstanding temperatures up to 1500°C

● Important improvement of the metallic coating performances

Material selection

● The BTC solution is chosen to resist against the specific conditions of the corrosive and/or erosive environment

● Wide range of alloys:

• Nickel based alloys such as Inconel 625 and 686,

Hastelloy, Incoloy, etc.

• Cobalt based alloys

• Special iron based alloys

Implementation

● Our specialists will analyse your wear/corrosion problems and propose a tailored solution

● BTC coating technology is only available through our CastoLab Services© workshops

Wire

Wire

Current

Arc

Spray stream

Coating

Air

Current

Our new BTC densified thermal spray coatings include a range of solutions based on the arc

wire spray and densification technologies developed in house. Castolin Eutectic, as the pro-

ducer of coating equipments, cored wires and densifiers, has fully optimised the process pa-

rameters.