Dr. Mumtaz Hasan Malik
7/30/2019 class lecture of Post spinning
2/44
Objectives
To assemble long length of yarn into suitable package
form for use in subsequent processes e.g. warping,
weaving, knitting;
To remove sizeable yarn faults by cutting and then by
joining the cut ends; and
To apply lubricant on yarn surface, if required.
7/30/2019 class lecture of Post spinning
3/44
Important Aspects of Package Winding
Package formation
Thread-line dynamics and tensioning
Yarn clearing
Piecing
Waxing
7/30/2019 class lecture of Post spinning
4/44
1. Winding units
2. Ring and rewound yarn packages
3. Basic winding actions
Bobbin rotation
Yarn traverse
7/30/2019 class lecture of Post spinning
5/44
7/30/2019 class lecture of Post spinning
6/44
7/30/2019 class lecture of Post spinning
7/44
7/30/2019 class lecture of Post spinning
8/44
Wind Angle: The angle between the yarn lay on the
package and a plane perpendicular to the bobbin axis is
called the wind angle. It is calculated as under:
tan = Vts /2rNb ---------------------(1)
where:
= wind angle
Vts = traverse speed (m/min)
r = radius (m) of yarn layer being wound
Nb = bobbin rotation speed (rpm)
7/30/2019 class lecture of Post spinning
9/44
Greater the wind angle more stable the package.
Maximum limit of wind angle is achieved when slipping
of yarn during traverse reversal does not take place.
Coil Angle: The angle between the yarn lay on the
package and the direction of the traverse length is called
coil angle.
7/30/2019 class lecture of Post spinning
10/44
------------(2)
Where
Vwy
= yarn winding speed (m/min)
Vbs = bobbin surface speed (m/min)
Vts = traverse speed (m/min)
Vbs = 2rNb ---------------(3)
Vts = 2LNt ---------------(4)
Where
L = traverse lengthNt = traverse frequency
---------------(5)
7/30/2019 class lecture of Post spinning
11/44
1. Drum Winders for making random wound packages
of staple-spun yarns.
2. Precision Winders for making precision wound
packages of filament yarns.
7/30/2019 class lecture of Post spinning
12/44
Drum Winders:
Forming package rotates through surface contact of a
rotating cylinder.
Yarn traversing takes place either by grooves of the drum
which rotates the package or by an independent wing cam
(Fig 7.5)
7/30/2019 class lecture of Post spinning
13/44
7/30/2019 class lecture of Post spinning
14/44
Grooved Drum:
Surface speed of the drum and traverse speed are constant.
Interconnected clockwise and counterclockwise helical
grooves are made on the drum.
Continuous groove guides the yarn along the traverse length
during yarn winding.
Continuous helix has points of crossover of clockwise and
counterclockwise helices.
Retention of yarn in correct groove is ensured by making one
groove deeper and shallower groove is slightly angled.
7/30/2019 class lecture of Post spinning
15/44
The drum constant kis given as:
---------------------------- (6)
Where Nd = Drum rotational speed
Nt = Traverse frequency
For every turn of drum one double traverse takes place.
With grooved drum the constant k is always a whole
number which is twice the number of crossings of grooves
e.g. a crossing of 3 kbecomes 6
7/30/2019 class lecture of Post spinning
16/44
crossing drum with k= 1 is called a split drum
From equation 4 and 6
---------------------------- (7)
The traverse ratio TR is
---------------------------- (8)
Where Dd = Diameter of drum
Db = Diameter of cylindrical bobbin
7/30/2019 class lecture of Post spinning
17/44
For conical package:
TR= k Dd/d
m
Where dm = Mean diameter of conical package.
As package diameter increases its rotational speed
decrease resulting in reduction of wind and traverse ratios,
but angle of wind or coil angel remain constant.
Stable packages are made when ranges from 9o to 22o or
ranges from 81o to 68o.
Decrease in traverse ratio with increasing package
diameter poses a problem in winding process.
7/30/2019 class lecture of Post spinning
18/44
Wing Cam:
Following figure shows an independent yarn traverse
system
7/30/2019 class lecture of Post spinning
19/44
End A of yarn guide bar moves yarn whereas end B of
yarn guide bar moves around periphery of cam, traveling
one cycle of periphery per rotation of camshaft.
As B makes one cycle of cam, A reciprocates, moving the
yarn through a return traverse along length of bobbin .
Due to inertia on reversal yarn guide limits winding
speed.
7/30/2019 class lecture of Post spinning
20/44
Reciprocating guides are replaced by a spirally traverse
roller, which enables winding speed of more than 1500
m/min.
Grooved traverse roller does not need threading up
mechanism.
7/30/2019 class lecture of Post spinning
21/44
Patterning / Ribboning:
As the diameter of package increases the traverse ratiodecreases because .
During winding, traverse ratio passes through a series of
integer values
Rate of change of package diameter determines how long
the traverse ratio remains at any particular integer value
At smaller diameter the rate of change of package
diameter is high therefore patterning does not occurs
7/30/2019 class lecture of Post spinning
22/44
At larger diameter, the rate of change of package diameter
is low, yarn coils of successive traverse follow exactly the
same path of wind and ribbonning on package takes place
Patterning can also occur when traverse ratio TR = integer
+ 1/2 or 1/3, 2/3, 1/4, 3/4, 1/5, 2/5, 3/5, 4/5 etc.
A ribboned package may give uneven dyeing of yarn
7/30/2019 class lecture of Post spinning
23/44
Sloughing-off:
During unwinding, two or more overlaid coils can be
undesirably pulled off together from the bobbin.
Such unintentional removed leads to entanglement of coils.
This fault is known as sloughing-off.
Sloughed-off material has to be cut away, thus the loss of
material and lower productivity in subsequent processes.
Sloughing-off may cause needle breakage in weft knitting.
Yarn coils in patterning zone can also cause high tension
variations during unwinding
7/30/2019 class lecture of Post spinning
24/44
Anti-patterning Devices:
1. Variation of Traverse Frequency
For cam-operated traverse machine, a small sinusoidal change
to the normal running speed of cam shaft changes the traverse
speed, thus the start of each double traverse changes position
from the pervious one.
Therefore patterning is avoided.
7/30/2019 class lecture of Post spinning
25/44
2. Variation of Drum Speed:
For rotary drum machine, small reduction and increase in
drum speed (20-30 times per minute) control patterning.
Slippage of package from the drum during low and then higher
drum speed changes the coil lays and therefore traverse ratio
which ultimately avoids ribboning.
7/30/2019 class lecture of Post spinning
26/44
3. Lifting of Bobbin:
About 1 mm lift of bobbin, 20-30 time per minute, from the
drum surface can also introduce slippage of package thus
change in coils lay, resulting in anti-patterning.
4. Rock-and-Roll of Bobbin:
This method is used during cone winding.
The lower diameter part of the package (nose) rises about
1mm several times per minute, which introduces slippage of
the package, thus change in coils lay.
7/30/2019 class lecture of Post spinning
27/44
Filament yarns are particularly wound on precision winding
machines.
On precision winding machines, package is mounted onto a
spindle and a traversing guide, driven by cam coupled to the
spindle moves the yarn along the traverse length.
Traverse guide limits the winding speed because of inertia on
reversals.
The term precision refers to the controlled positioning of yarn
coils during winding on bobbin, a precise ratio of spindle to
traverse speed .
7/30/2019 class lecture of Post spinning
28/44
With the increase in package diameter, the wind and TR
remain constant.
Therefore, for precision winders
------------------------- (9)
and
------------ (10)
Therefore, as Db increases increases and decreases.
As filament yarns are prone to slip at reversals, is kept in the
range of 70o-80o.
7/30/2019 class lecture of Post spinning
29/44
If machine is set such that TR is not an integer or a multiple of
0.5 no patterning occurs and no anti-patterning system
requires.
If Nb is kept constant, surface speed and yarn tension will
increase as the package diameter increases, resulting in uneven
package density and higher yarn breakage rate.
Precision winders may have:
Constant or variable spindle speed
Constant or variable surface speed
A combination system
7/30/2019 class lecture of Post spinning
30/44
Constant spindle speed requires minimum tension fluctuations.
Variable spindle speed provides a constant mean winding
tension.
Constant surface speed requires spindle speed reduction as
package diameter increases.
For combination approach, spindle speed first increases to give
the required production rate, after which surface speed is kept
constant.
Advantage of combination approach can be shown with the
following example.
7/30/2019 class lecture of Post spinning
31/44
For constant spindle speed:
Vlimit = 600m/minVw = Db(max)Nb/100
Nt = 264.5 cycles/min.
With 264.5 cycles/min Vw =
7/30/2019 class lecture of Post spinning
32/44
For combination system, the winding speed at the early stage
of package build up can be at the fastest, matching the yarn
limiting speed.
Reduction in winding speed occurs when diameter of package
reaches the value of
If Nt = 350 cycle/min, Db = 10.91cm will be the diameter and
76.9o
7/30/2019 class lecture of Post spinning
33/44
In the second stage of winding, package builds up at 600m/min
until diameter reaches 14.44 cm and = 80o.
Following figure shows a comparison of two winding systems.
7/30/2019 class lecture of Post spinning
34/44
7/30/2019 class lecture of Post spinning
35/44
7/30/2019 class lecture of Post spinning
36/44
7/30/2019 class lecture of Post spinning
37/44
a. Package Surface Speed:
Different surface speeds along the traverse length.
One point of drive of the cone by the drum.
Slippage at all surface contact points expect the point of drive.
Drive length y is the distance along the traverse from the
cone base to the point of drive, which remains constant during
winding except negligible variation in y when cone is small.
Production speed of winding is the mean surface speed and not
the speed at the point of drive.
7/30/2019 class lecture of Post spinning
38/44
7/30/2019 class lecture of Post spinning
39/44
7/30/2019 class lecture of Post spinning
40/44
Mean surface speed of cone Vm can be calculated :
Nd.D
d= N
b.d
d
Where Nd = Rotational drum speed
Dd = Drum diameter
Nb = Rotational cone speed
dd = Diameter of drive point
If the cone angle and d cone base diameter then
7/30/2019 class lecture of Post spinning
41/44
If = the cone angle and db = cone base diameter, then,
dd = db2ysin
b Abrasion at Cone Nose:
7/30/2019 class lecture of Post spinning
42/44
b. Abrasion at Cone Nose:
Slippage at nose cause abrasion resulting localized fusion of
polyester.
Cam-operated traverse system (split drum), one part is solid
and the shorter part (loose shell) is free to rotate and support
the rotating cone nose
In drum traverse systems, cylindrical drum is replaced by
slights tapered drum.
7/30/2019 class lecture of Post spinning
43/44
7/30/2019 class lecture of Post spinning
44/44
c. Traverse Motion:
With cone package, surface area is greater at base of the cone.
To achieve uniform density, yarn length wound per unit area
should be a constant value.
Accelerated traverse motion, yarn guide moves rapidly across
the traverse at nose.
More coils at the base.
Accelerated traverse is achieved by a cam at nose and for drum
grooves are widely spaced.