Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
1.0330 St12 A366
F C45U
L K X210Cr12 D3 T 30403 SKD1 CH12 K100X42Cr13 420
K 62SiMnCr4 K24521MnCr5
115CrV3 L2 T61202
40CrMnNiMo8-6-4 P20 40 CMD 8
1.2312 40CrMnMoS 8-6 P20
1.2316 X36CrMo17 420F
A W X38CrMoV5-1 H11 T 20811 Z38CDV5 BH11 X37CrMoV5 X37CrMoV5-1 KU SKD6 4Ch5MFs W300A W X40CrMoV5-1 H13 T 20813 2242 Z40CDV5 BH13 X40CrMoV5 X40CrMoV5-1 KU SKD61 4Ch5MF1S W302A K X50CrMoV5-1 K306
K X100CrMoV-5-1 A2 T 30102 2260 Z100CDV5 BA2 X100CrMoV5 X100CrMoV5 1KU SKD12 9Ch5VF K305A W 32CrMoV12-28 H10 T 20810 32DCV28 BH10 30CrMoV12 30CrMoV12-27 KU SKD7 3Ch3M3F W320A W X38CrMoV5-3 Z38CDV5-3 W303
W350
W360W600
L K D2 T 30402 SKD11 Ch12F1 K110K X220CrVMo13-4 D7 K190
L X210CrW12 D6 2312 X210CrW12 X215CrW12 1KU K107K 100MnCrW4 O1 T 31501 2140 90MWCV5 BO1 95MnCrW5 95MnWCr5 KU SKS3 9ChVG K460K 60WCrV7 S1 T 41901 55WC20 60WCrSi8 58WCr9 KU 6ChhV2S K455
1.2581 W X30WCrV9-3 H21 T 20821 Z30WCV9 BH21 X30WCrV9 X30WCrV9-3 KU SKD5 3Ch2V8F W100
L K X165CrMoV12 D2 T 30402 BD2 X165CrMoW12 KU Ch12M K105M X3NiCoMoTi18-9-5 W722VMR
W 54NiCrMoV6 L6 T 61206 55NCDV7 BS224 55NiCrMoV7 56NiCrMoV7 KU SKT4 W500
W 56NiCrMoV7 L6 T 61206 55NCDV7 5 F5307 56NiCrMoV7 KU SKT4 W500
50NiCr13 2550 K6051.2746 45NiCrMoV16-6
UNS
/ASTM
1.17301.20801.20831.21011.21621.22101.2311
1.23431.23441.23451.23631.23651.2367W350W360W6001.2379 X155CrVMo12-1
1.23801.24361.25101.2550
1.26011.27091.27111.27141.2721
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
K X45NiCrMo4 Y35NCD16 42NiCrMo15 7 K600W X6NiCrTi26-15 660 S 66286 Z6NCT25-15 W750VMRK 90MnCrV8 O2 T 31502 K720
1.2885 W X32CrMoCoV3-3-3 30DCKV28 BH10A 30CrMoCoV12-30-12 KU W321K K329K K340K K353
K K360K K390K K490K K890
A X45MoCrV5-3-1
S BT42 F5553 HS10-4-3-10 SKH57 S700
S HS6-5-5-5 M41 T11341 2723 BM35 F5613 HS6-5-2-5 SKH55 S705S HS6-5-3-8 S590 Microclean
1.3247 S HS2-9-1-8 M42 T11342 2716 BM42 F5617 HS2-9-1-8 SKH59 S500
S M52 T11352 S404
S HS6-5-2C M2 BM2 SKH9/SKH51 R6M5 S600S S630S HS6-5-3-8 M3 Cl. 2 T11323 Z120WDCV F5605 HS6-5-3 SKH53 S607
S M3 Class 2 T11323 S790
S HS2-91 M1 T11301 BM1 HS1-8-1 S401
1.3348 S HS2-9-2 M7 T11307 F5607 HS2-9-2 SKH58 S400
S HS6-5-4 M4 T11304 BM4 SKH54 S690S HS18-0-1 T1 T12001 Z80WCV18-04-01 BT1 F5520 HS18-0-1 SKH2 R18 S200
1.3554 S M2 reg. C T11302 2722 Z80WDCV6 BM2 F5603 HS6-5-2 SKH51 R6M5 S600
S S290 MicrocleanS S390 Microclean
1.27671.27791.2842
K329K340K353K360K390K490K890
1.2999
1.3207Z130WKCDV10-10-
04-04-03
1.3243Z90WDKCV06-05-
05-04-02
1.3244Z110DKCWV09-08-
04-02-01
1.3326
1.3343Z85WDCV06-05-04-02
1.33441.3345
1.3346Z85DCWV08-04-02-
01Z100DCWV09-04-
02-02
1.33511.3355
S290S390
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
1.3813 X40MnCrN19
1.3815 A1.3910 Magnifer 36
A Ni36 K 93601 Pernifer® 361.3917 Ni42 SEW 385
Magnifer 50 nMg1.3926 Ni48
A X2CrNiMoN18-14-3 AMANOX 3952A X2CrNiMnMoNNb21-16-5-3 SEW 390
1.3974 X2CrNiMnMoNNb23-17-6-3
A X3NiCo29-18 Pernifer® 2918
F/M X6Cr13 403 S 40300 2301 Z6C13 403 S17 SUS 403 08 Ch 13
F/M X7Cr14 429 S 42900 SUS 429
F/M X6CrAl13 405 S 40500 Z8CA12 405 S17 SUS 405
F X2CrNi12
F/M X12CrS13 416 S 41600 2380 Z11CF13 416 S21 SUS 416
F/M X12Cr13 410 S 41000 2302 Z10C13 410 S21 SUS 410 12 Ch 13
M X35Cr14 420 S 42000
1.4008 F/M GX8CrNi13 GX7CrNiMo12-1 GX7CrNiMo12-1
1.4009 A X8Cr14
1.4015 A X8Cr18
F/M X6Cr17 430 S 43000 2320 Z8C13 430 S15 SUS 430 12 Ch 17
F X6CrNi17-1
F/M X20Cr13 420 S 42000 2303 Z20C13 420 S37 SUS 420 J1 20 Ch 13
F/M X15Cr13 2302 Z12C13 403 S17 SUS 403
1.4027 F/M GX20Cr14 Z20C13M
F/M X30Cr13 420 S 42000 2304 420 S45 SUS 420 J2
M X39Cr13 SUS 420 J2 40 Ch 13
M X46Cr13 2304 Z40C14 420 S45 SUS 420 J2 40 Ch 13
M X65Cr13
M X22CrNi17 431 S 43100 2321 Z15CN17.03 431 S29
1.3912
1.3922
1.39521.3964
1.39811.40001.40011.40021.40031.40051.40061.4007
1.40161.40171.40211.4024
1.40281.40311.40341.40371.4044
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
M X20CrNi17 2 431 S 43100 2321 Z15CN16.02 431 S29 SUS 431
1.4059 F/M GX22CrNi17 Z20CN17.2M
1.4085 F/M GX70Cr29
1.4086 F/M GX120Cr29
F/M X12CrMoS17 430F S 43020 2383 Z13CF17 441 S29 SUS 430 F
F/M X4CrMoS17 430F Z8CF17
1.4106 F/M X10CrMo13
1.4107 F/M GX8CrNi12
M X30CrMoN15-1
1.4109 M X65CrMo14
M X55CrMo14 Z50CD15CI
1.4111 M X110CrMoV15
1.4112 M X90CrMoV18 440 B S 44003 SUS 440B
F/M X6CrMo17-1 434 S 43400 Z8CD17.01 434 S17 SUS 434
1.4115 M X20CrMo17-1
M X50CrMoV15 308 S92
1.4117 M X38CrMoV15 425 C11
1.4119 F/M X15CrMo13
F/M X20CrMo13 Z20CD14
M X35CrMo17
M X40CrMoVN16-2 420 mod. S 42025 X40CrMoVN16.02
M X105CrM017 440 C S 44004 Z100CD17 X102CrMo17 KU 108CR17 SUS 440 C 95 Ch 18
1.4136 M GX70CrMo29-2 Z60CD29.2M
1.4138 M GX120CrMo29-2
D X2CrMnNiN22-5-2 2101 S 32101
A 304 S 30400 2332 Z6CN18.09 304 S15 SUS 304 08 Ch 18 N 10
1.4302 F/M X5CrNi199 308 S96
A X4CrNi1812 305 S 30500 2332 Z6CN18-09 304 S16 SUS 305 06 Ch 18 N 11
A X8CrNiS18-9 303 S 30300 2346 Z8CNF18.09 303 S31 SUS 303
A X2CrNi19-11 304L S 30403 2352 Z3CN18.10 304 S11 SUS 304 L 03 Ch 18 N 11
A X2CrNi18-9 304L S 30403 2353 Z3CN18.10 304 S11 SUS 304 L 04 Ch 18 N 10
1.4057
1.41041.4105
1.4108
1.4110
1.4113
1.4116
1.41201.41221.41231.4125
1.41621.4301 X5CrNi1810
1.43031.43051.43061.4307
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
A X10CrNi18-8 301 S 30100 2331 Z12CN18.09 301 S22 SUS 301 07 Ch 16 N 6
A X2CrNiN18-10 304LN S 30453 2371 Z3CN18.10Az 304 S61 SUS 304 LN
1.4312 A GX10CrNi18-8 Z10CN18.9M 302 C25
F/M X3CrNiMo13-4 CA6-NM 2384 Z4ND13.04M 425 C11 SCS5
A X5CrNiN19-9 304N Z6CN19-09AZ
1.4316 X1CrNi19-9 Z1CN20-10
A X2CrNiN18-7 301LN Z3ZN18-07AZ
A X5CrNi17-7 302 S 30200 2331 Z10CN18-09 302 S25 SUS 302
1.4320 M X2CrNiMo13-4
1.4321 F/M X2NiCr18-16
1.4332 F/M X3CrNi24-12 Z2CN24.13 309 S92
A X1CrNi25-21
1.4337 F/M X10CrNi309 Z10CN30-09 312 S94
1.4340 F/M GX40CrNi27-4
1.4347 F/M GX6CrNiN26-7
1.4350 A X5CrNi189 304 2332 Z6CN18.09 304 S31 SUS 304
1.4351 F/M X3CrNi13-4
A X2CrNiSi18-15
D X2CrNiN23-4 S 32304 2327 Z3CN23.04 Az
A X11CrNiMnN19-8-6
1.4370 A X15CrNiMn18-8 202 Z8CnM19-09-07 307 S98
A X2CrMnNiN17-7-5 SUS 202
A X12CrMnNiN17-7-5 201 S 20100
A X12CrMnNiN18-9-5 284 S16
1.4375 X6CrNiMoTi 17-12-2 S 21904
A X8CrMnNi19-6-3 H400A X5CrNiMo17-12-2 316 S 31600 2347 Z6CND17.11 316 S31 SUS 316 08 Ch 16 N 11 M 3
A X2CrNiMo17-12-2 316L S 31603 2348 Z3CND18.12.02 316 S11 SUS 316 L
A1.4405 F/M GX5CrNiMo165
A X2CrNiMoN17-11-2 316LN S 31653 2370 Z3CND17.11.02 316 S61 SUS 316 LN
1.43101.4311
1.43131.4315
1.43181.4319
1.4335
1.43611.43621.4369
1.43711.43721.4373
1.43761.44011.4404
316plus
1.4406
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
1.4408 A GX6CrNiMo1810
D X2CrNiMoN25-7-4 S 32750 2328
1.4417 D X2CrNiMoSi19 5 S 31500 2376
M X4CrNiMo16-5-1 2387 Z6CND16.05.01
M X38CrMo14
A X2CrNiMoN20-8-1
M X1CrNiMoCu12-5-2
M X1CrNiMoCu12-7-3
M X2CrNiMoSi18-5-3
A X4CrNiMoS18-11 316F
A X2CrNiMoN17-13-3 316LN S 31653 2375 Z3CND17-12-Az 316 S63 SUS 316 LN
1.4430 F/M X2CrNiMo1912 Z2CND19.12 316 S93
A X2CrNiMo17-12-3 316L 2353 Z3CND17.12.03 316 S13 03 Ch 17 N 14 M 2
A X2CrNiMo18-14-3 316L S 31603 2353 Z3CND18.14.03 316 S11 SUS 316 L 03 Ch 17 N 14 M 2
A X3CrNiMo17-13-3 316 S 31600 2343 Z7CND18.12.3 316 S31 SUS 316
1.4437 F/M GX6CrNiMo18-12 317 C12
A X2CrNiMo18-15-4 317L S 31703 2367 Z3CND19.15.4 317 S12 SUS 317L
A X2CrNiMo17-13-5 317LMN S 31726 Z3CND18.14.05.Az
1.4440 F/M X2CrNiMo18-16-5
1.4441 A X2CrNiMo18-15-3
1.4446 F/M GX2CrNiMoN17-13-2
1.4448 F/M GX6CrNiMo17-13 317 C16
14449 F/M X5CrNiMo17-13 317 S 31700 317 S16
1.4452 A1.4455 F/M X2CrNiMoN20-16
1.4456 AD X4CrNiMoN27-5-2 329 S 32900 2324 Z5CND17.05.AZ SUS 329 J1
D S 31803 2377 Z3CND22.05Az 318 S13 SUS 329 J3L
1.4463 F/M GX6CrMoCuNb2018
A X1CrNiMoN25-25-2 S 31726 Z2CND25.22 Az
A X1CrNiMoN25-22-2 S 310050
1.4410
1.44181.44191.44201.44221.44231.44241.44271.4429
1.44321.44351.4436
1.44381.4439
1.44601.4462 X2CrNiMoN22-5-3
1.44651.4466
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
D X2CrNiMoN29-7-2
D S 32760
1.4502 F/M X8CrTi18
A X3NiCrCuMoTi27-23 Z3CND25-06Az
A X5NiCrMoCuNb20-18
1.4506 A X5NiCrMoCuTi20-18
D X2CrNiMoCuN25-6-3
F X2CrTiNb18 441 S 43940
F X3CrTi17 430Ti/439 S 43035 SUS 430 LX 08 Ch 17 T
F X3CrNb17 430Nb Z4CNb17 SUS 430 LX
F 409 S 40900 Z6CT12 SUH 409
F X2CrMoTi17-1
F X2CrNiTi12
F X2CrTi17 Cronifer 2328F 444 S 44400 SUS 444
F X2CrMoTiS18-2
F 436 S 43600
1.4528 F/M X105CrCoMo18-2
A X1NiCrMoCuN25-20-7 N 08926
1.4531 F/M GX2NiCrMoCuN20-18
M X3CrNiMoAl13-8-2 S 13800
1.4535 F/M X90CrCoMoV17
1.4536 F/M GX2NiCrMoCuN25-20
A X1CrNiMoCuN25-25-5
A X1NiCrMoCuN25-20-5 904L N 08904 2562 Z2NCDU25.20 904 S13
A X6CrNiTi18-10 321 S 32100 2337 Z6CNT18.10 321 S31 SUS 321 08 Ch 18 N 10 T
M X5CrNiCuNb16-4 630 S 17400 Z7CNU15.05 SUS 630
1.4543 F/M X5CrNiNb18-9
1.4544 A X7CrNiTi18-9
1.4545 X5CrNiCuNb15-5-4
1.4546 X5CrNiNb18-10 348 S 34800
1.44771.4501 X2CrNiMoCuWN25-7-4
1.45031.4505
1.45071.45091.45101.45111.4512 X2CrTi12
1.45131.45161.45201.4521 X2CrMoTi18-2
1.45231.4526 X6CrMoNb17-1
1.4529
1.4534
1.45371.45391.45411.4542
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
A X1CrNiMoCuN20-18-6 S 31254 2378
1.4548 X5CrNiCuNb17-4-4
A X6CrNiNb18-10 347 S 34700 2338 Z6CNNb18.10 347 S31 SUS 347 08 Ch 18 N 12 B
1.4551 F/M X5CrNiNb19-9
1.4552 A GX5CrNiNb18-9
A X2NiCrAlTi32-20
A X1CrNiMoTi18-13-2 316L
A Alloy 31 N 08031 3127 hMoA X1NiCrMoCu31-27-4 N 08028 2584 Z2NCDU31.27 3127 LCA X2CrNiMnMoNbN25-18-5-4 S 34565
1.4566 X3CrNiMnMoCuNbN23-17-5-3
A X3CrNiCu18-9-4 304Cu S 30430 SUS XM 7
D X7CrNiAl17-7 631 2388 Z8CNA17.07 361 S17 09 Ch 17 N 7 Ju
A X6CrNiMoTi17-12-2 316Ti S 31635 2350 Z6CNDT17.12 320 S31 SUS 316 Ti 10 Ch 17 N 13 M 2 T
1.4573 A X10CrNiMoTi18-12 316L 320 S33
1.4575 D X1CrNiMoNb28-4-2
1.4576 F/M X5CrNiMoNb19-12
A X5CrNiMoTi25-25
A X3CrNiCuMo17-11-3-2
A X6CrNiMoNb17-12-2 316L Z6CNDNb17-12
1.4581 A GX5CrNiMoNb18-10
1.4582 D X4CrNiMoNb25-7
1.4583 A X10CrNiMoNb18-12 318 Z6CNDNb17 13B
1.4585 A GX7CrNiMoCuNb18-18
1.4586 A GX7CrNiMoCuNb22-18
F/M X5CrNiMoTi15-2 S 42035
F X2CrNbZr17
A X1CrNiMoCuN33-32-1 Nicrofer 3033
F X2CrMoTi29-4
F X1CrNi15
A X8CrMnCuNB17-8-3
1.4547
1.4550
1.45581.45611.45621.4563
1.4565 S
1.45671.45681.4571
1.45771.45781.4580
1.45891.45901.45911.45921.45951.4597
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
F X2 CrNbTi 20
1.4610FFA 201
F X2CrNbCu21 S 44500
F X2CrTiNbVCu22
A X5CrNiCu19-6-2
A X1CrNiMoCuN24-22-8 S 32654
D X2CrNiCuN23-4
A X1CrNiMoCuNW24-22-6
1.4660 347 S 34700
F X10CrAl7 Z8CA7
1.4718 X45CrSi9-3 HNV3 S 65007 SUH 1
F X10CrAl13 405 (Z10C13) 403 S17 SUS 405
1.4729 M GX40CrSi13
F X6 Cr'Al 18-4
1.4740 M GX40CrSi17
F X10CrAl18 430 Z10CAS18 430 S15 SUS 430
1.4745 M GX40CrSi23
1.4747 M X80CrNiSi20 HNV6 Z80_CSN20.02 443 S65 SUH4
F X18CrN28 446-1 S 44600 2322 Z10C24 SUH 446
F X1CrWNbTiLa22-2
F X1CrTiLa22 S 44535 Crofer 22 APUF X10CrAlSi24 o. 446 S 44900 2322 Z10CAS24 SUH 446
F CrAl20-5
1.4776 M GX40CrSi29
1.4791 X10CrSi29
A X6CrNiSiNCe19-10
1.4820 X12CrNiSi26-5
1.4821 A X15CrNiSi25-4 327 Z20CNS25.04
1.4607
1.46111.46131.4618 X9CrMnNiCu17-8-5-2
1.46211.46221.46401.46521.46551.4659
1.4713
1.4724
1.4737
1.4742
1.47491.47551.47601.47621.4767
1.4818
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
1.4823 A GX40CrNiSi27-4
1.4825 A GX25CrNiSi18-9
1.4826 A GX40CrNiSi22-9
A 309 S 30900 Z15CNS20.12 309 S24 SUH 309
A X12CrNi23-13 309S Z15CN23.13 309 S16
A X9CrNiSiNCe21-11-2 S 30815 2368 MA 253A X15CrNiSi25-20 314 S 31400 Z15CNS25.20 314 S25 SUH 310
1.4842 X12CrNi25-21 310S S 31008 2361 Z12CN25-20 SUH 310 S
A X8CrNi25-21 310S S 31008 2361 Z12CN25.20 310 S24 SUH 310 S
1.4848 A GX40CrNiSi25-20
A X6NiCrSiNCe35-25 S 35315 MA 353A X12NiCrSi35-16 330 N 08303 Z12CNS35.16 3076 NA17
1.4869 NiCr80-20
1.4871 F/M X53CrMnNiN21 9 EV8 Z52CMN21.09 349S54 SUH35, -36
DA X10NiCrAlTi32-21 B163 Z8NC32.21 3076 NA15H NCF2B
1.4877 A X6NiCrNbCe32-27 S 33228
A X8CrNiTi18-10 321 S 32100 2337 Z6CNT18.12 321 S51 SUS 321
1.4882 F/M X50CrMnNiNbN21-9
A X10NiCrSiLa 38-22 Cronifer 40B1.4891 A X2CrMoTiS18-2 S 30415 2372 MA 153
M X10CrMoVNb9-1
A X3CrNiMoN17-13-3
M X19CrMoNbVN11-1
M X20CrMoV11-1 2317
M X22 CrMoV 12-1
1.4931 M GX22CrMoV12-1
F X12CrNoMoV12-3 904L Z12CNDV12-02
1.4941 A X8CrNiTi18-10
A X6NiCrTi26-15 660 S 66286 Z6NCTDV25 15B HR51 SUH 660
A X6CrNi18-10 304H 2333 Z6CN18.09 304 S51
1.4828 X15CrNiSi20-12
1.48331.48351.4841
1.4845
1.48541.4864
1.4872 X22CrMnNi 25-9-5
1.4876
1.4878
1.4888
1.49031.49101.49131.49221.4923
1.4939
1.49441.4948
Deutschland USA USA Schweden Frankreich England Spanien Italien China Japan GUS Markenname
W.-Nr. DIN/DIN EN AISI SS / SIS AFNOR BS UNE UNI GB JIS GOST Böhler, …
DINAustenit AMartensit MFerrit FDuplex DLedeburitisch L
UNS
/ASTM
1.4949 A X3CrNi18-11
1.4952 NiCr20TiAl
1.4957 GX15CrNiCo21-20-20
A X2CrNiN23-4 N 08811
1.4961 A X8CrNiNb16-13
1.4970 X10CrNiMoTiB15-15
A X6NiCrTiMoVB25-15-2 A286 S 66286 Thermon 4980
1.4981 A X8CrNiMoNb16-16
1.4986 X8CrNiMnCrCNb12-5/Ni
1.5415 15Mo3
1.63541.63551.6587 18CrNiMo7-6
M Ultrafort1.6981 21CrMoNiV4-7
1.7219 26CrMo4
42CrMo4 4137 A331 14 2244 42CD4 708M40 F1252 SCM4
1.7258 24CrMo5
1.7335 13CrMo4-4
1.7337 16CrMo4-4 A182 SFVA F 12
1.7383 10CrMo9-10
N 34CrAlMo5 K 23510 34CrAlMo7
1.8550 N 34CrAlNi7-10
1.4959
1.4980
1.6908
1.7225
1.8507
Brennstoffzelle
Legierungsbestandteile Edelstahl Seite14
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
L 2.00 11.50 0.35 0.25
0.40 13.50 0.30 0.40 0.030 0.30
0.63 0.60 1.10 1.10
0.18 1.00 1.10 0.15 0.000 0.0000.24 1.30 1.40 0.35 0.030 0.030
1.10 0.50 0.20 0.15 0.000 0.07 01.25 0.80 0.40 0.30 0.030 0.12 0,03
0.35 1.80 0.15 1.30 0.200.45 2.10 0.25 1.60 0.40 0.035 0,035
A 0.39 5.01 0.21 1.14 0.43 0.97 0.006 0.35 0,015
A 0.39 5.20 1.40 0.40 1.10 0.95
A 0.51 5.00 1.40 0.30 0.95 1.40
1.00 5.20 1.10 0.55 0.30 0.25
0.31 2.90 2.80 0.35 0.30 0.50
0.38 5.00 2.80 0.40 0.40 0.55
L 1.55 11.30 0.75 0.30 0.30 0.75
2.30 12.50 1.10 0.30 0.60 4.00
0.95 0.55 1.10 0.25 0.10
2.10 11.50 0.40 0.25
0.63 1.10 0.30 0.60 0.18
0.29 2.70 0.30 0.25 0.35
A 1.60 11.50 0.60 0.30 0.35 0.30
18.00 4.85 1.000.005
0.55 1.10 1.70 0.50 0.75 0.25 0.10
0.55 1.00 3.00 0.25 0.40 0.30
0.48 1.30 4.00 0.25 0.40 0.23
1.40 6.40 1.50 3.70
1.2080
1.2083
1.2101
1.2162
1.2210
1.2311
1.2343
1.2344
1.2345
1.2363
1.2365
1.2367
1.2379
1.2380
1.2510
1.2436
1.2550
1.2581
1.2601
1.2709
1.2711
1.2721
1.2767
K490
Legierungsbestandteile Edelstahl Seite15
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
0.38 5.00 1.75 0.55 0.20 0.55
0.50 4.50 3.00 0.25 0.20 0.55
0.32 1.90 3.30 0.20 0.150.10
0.02 15.00 25.00 1.25 2.50 1.40 0.25 0.300.20
0.90 0.35 2.00 0.25 0.10
0.39 2.90 2.80 0.35 0.30 0.65
1.26 4.00 3.60 0.30 0.25 3.20
0.92 4.10 5.00 0.30 0.40 1.90
1.29 4.20 5.00 0.30 0.60 3.00
1.10 3.90 9.20 0.20 0.50 1.00
0.89 4.10 4.50 0.30 0.30 1.90
0.89 4.10 5.00 1.80
1.21 4.10 5.00 0.30 0.25 2.90
1.29 4.20 5.00 0.30 0.60 3.00
0.84 3.80 8.60 0.30 0.40 1.20
1.02 3.80 8.60 0.30 0.40 1.90
1.35 4.10 5.00 0.30 0.60 4.10
0.75 4.10 0.30 0.25 1.10
0.90 4.10 5.00 1.80
2.00 3.80 2.50 0.30 0.50 5.10
1.64 4.80 2.00 0.30 0.60 4.80
A min. - 35.00max. 0.15 0.25 37.00 0.60 0.40 0.0 0,025
A min. - 16.50 13.00 2.50 0.15max. 0.03 18.50 15.00 3.00 0.22
A min. - 20.00 15.00 3.00 4.00max. 0.03 21.50 17.00 3.50 6.00
W350
W360
W600
1.2779
1.2842
1.2885
1.3207
1.3243
1.3244
1.3247
1.3326
1.3343
1.3344
1.3345
1.3346
1.3348
1.3351
1.3355
1.3554
S290
S390
1.3912
1.3952
1.3964
Legierungsbestandteile Edelstahl Seite16
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
F min. - 12.00 -max. 0.08 14.00 1.00
1.4001 min.max. 0.06 13.50
F min. - 12.00 - 0.10max. 0.08 14.00 1.00 0.30
F min. - 10.50 0.30 - -max. 0.03 12.50 1.00 0.03 1.50
M min. 0.08 12.00 - 0.15max. 0.15 14.00 0.60 0.35
M min. 0.08 11.50 - -max. 0.15 13.50 0.75 1.50
F min. - 16.00 -max. 0.08 18.00 1.00
F min. - 16.00 1.20 -max. 0.08 18.00 1.60 1.00 1.00 0.015
M min. 0.16 12.00 -max. 0.25 14.00 1.50
M min. 0.26 12.00 -max. 0.35 14.00 1.50
M min. 0.36 12.50 -max. 0.42 14.50 1.00
M min. 0.43 12.50max. 0.50 14.50 1.00
M min. 0.58 12.50 -max. 0.70 14.50 0.015
M min. 0.12 15.00 1.50max. 0.22 17.00 2.50
M min. 0.10 15.50 0.20 0.15max. 0.17 17.50 0.60 0.35
F min. - 16.00 0.20 0.15max. 0.08 18.00 0.60 0.35
M min. 0.25 14.00 0.85 0.30max. 0.35 16.00 0.50 1.10 0.50 1.00 1.00
M min. 0.85 17.00 0.90 0.07max. 0.95 19.00 1.30 1.00 1.00 0.015 0.12 0.04
F min. - 16.00 0.90 -max. 0.08 18.00 1.40 1.00
M min. 0.45 14.00 0.50 0.10max. 0.55 15.00 0.80 0.20
FU min. 0.17 12.50 - 0.90 -max. 0.22 14.00 1.00 1.30 1.00
M min. 0.33 15.50 - 0.80max. 0.45 17.50 1.00 1.30
M min. 0.37 15.00 - 1.50 0.15 0.20max. 0.45 16.00 0.50 1.90 0.25 0.60 0.60 0.005 0.40
M min. 0.95 16.00 0.40max. 1.20 18.00 0.80 1.00 1.00 0.015 ,04
1.4000
1.4002
1.4003
1.4005
1.4006
1.4016
1.4017
1.4021
1.4028
1.4031
1.4034
1.4037
1.4057
1.4104
1.4105
1.4108
1.4112
1.4113
1.4116
1.4120
1.4122
1.4123
1.4125
Legierungsbestandteile Edelstahl Seite17
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
D min. 21.00 1.35 0.10 0.20 4.00max. 0.04 22.00 1.70 0.80 0.25 6.00
A min. - 17.00 8.00 -max. 0.07 19.50 10.50 2.00
A min. - 17.00 11.00 -max. 0.06 19.00 13.00 2.00
A min. - 17.00 8.00 0.15max. 0.10 19.00 10.00 0.35
A min. - 18.00 10.00 -max. 0.03 20.00 12.00 2.00
A min. - 17.50 8.00 -max. 0.03 19.50 10.00 2.00
AF min. 0.05 16.00 6.00 - - -max. 0.15 19.00 9.50 0.80 0.11 2.00
A min. - 17.00 8.50 0.12max. 0.03 19.50 11.50 0.22
M min. - 12.00 3.50 0.30 0.02max. 0.05 14.00 4.50 0.70
A min. - 18.00 8.00 0.12max. 0.06 20.00 11.00 0.22
A min. - 16.50 6.00 0.1 -max. 0.03 18.50 8.00 0.2 2.00
1.4319 min.max.
A min. - 24.00 20.00 - - - - -max. 0.02 26.00 22.00 0.1? 2.00 0.15 0.005 0.025
A min. - 17.00 14.00 - - - -max. 0.02 18.50 15.50 0.20 2.00 0.010 0.025
D min. 22.00 3.50 0.10 0.05 0.1max. 0.03 24.00 5.50 0.60 0.20 0.6
1.4372 A min.max.
A min. - 17.00 - - 6.00 - - -max. 0.10 19.50 3.50 0.3 9.00 1.00 0.015 0.045
A min. - 16.50 10.00 2.00 -max. 0.07 18.50 13.00 2.50 2.00
A min. - 16.50 10.00 2.00 - - -max. 0.03 18.50 13.00 2.50 0.11 2.00 1.00
A min. 19.50 8.00 0.50 0.14max. 0.03 21.50 9.50 1.50 0.25 2.00
1.4406 A min.max.
1.4410 D min. 24.00 6.00 3.00 0.24max. 0.03 26.00 8.00 4.50 0.35
M min. - 15.00 4.00 0.80 0.02max. 0.06 17.00 6.00 1.50
1.4419 M typ. 0.38 14.00 0.80 0.35 0.30
1.4162
1.4301
1.4303
1.4305
1.4306
1.4307
1.4310
1.4311
1.4313
1.4315
1.4318
1.4335
1.4361
1.4362
1.4376
1.4401
1.4404
316plus
1.4418
Legierungsbestandteile Edelstahl Seite18
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
AF min. - 16.50 11.00 2.50 0.15max. 0.05 18.50 14.00 3.00 0.22
A min. - 16.50 11.00 2.50 0.12max. 0.03 18.50 14.00 3.00 0.22
A min. - 16.50 10.50 2.50 -max. 0.03 18.50 13.00 3.00 2.00
A min. - 17.00 12.50 2.50 -max. 0.03 19.00 15.00 3.00 2.00
A min. - 16.50 10.50 2.50max. 0.05 18.50 13.00 3.00
A min. - 17.50 13.00 3.00max. 0.03 19.50 16.00 4.00
A min. - 16.50 12.50 4.00 0.12 -max. 0.03 18.50 14.50 5.00 0.22 2.00
1.4449 A min.max.
1.4460 D min.max.
D min. - 21.00 4.50 2.50 0.10 -max. 0.03 23.00 6.50 3.50 0.22 2.00
A min. - 24.00 22.00 2.00 0.08 - -max. 0.02 26.00 25.00 2.50 0.16 2.00 0.70
A min. - 24.50 21.50 2.00 0.10 1.50 -max. 0.02 25.50 22.50 2.30 0.14 2.00 0.40 0.015 0.02
D min. 0.00 24.00 6.00 3.00 0.20 0.5max. 0.03 26.00 8.00 4.00 0.30 1.0
1.4503 min.max.
A min. - 16.50 19.00 2.00 - 1.8max. 0.05 18.50 21.00 2.50 1.00 2.2
F min. - 17.50 0.10 -max. 0.03 18.50 0.60 1.00
F min. - 16.00 4x(C+N)+0.15 -max. 0.05 18.00 0.80 1.00
F min. - 16.00max. 0.03 18.00
F min. - 10.50 6x(C+N) - -max. 0.03 12.50 0.65 1.00 1.00
F min. - 16.00 - 0.30 -max. 0.03 18.00 0.015 0.60 0.50
F min. - 17.00 1.80 - 4x(C+N)+0.15 -max. 0.03 20.00 2.50 0.03 0.80 1.00
F min. - 18.00 2.30 0.60 0.50 0.3(C+N) max. 0.03 18.00 2.30 0.60 0.50 0.50 0.3
F mit. 0.04 17.50 1.25 0.50 0.40
A min. - 19.00 24.00 6.00 0.15 0.5max. 0.02 21.00 26.00 7.00 0.25 1.5
1.4427
1.4429
1.4432
1.4435
1.4436
1.4438
1.4439
1.4462
1.4465
1.4466
1.4501
1.4505
1.4509
1.4510
1.4511
1.4512
1.4520
1.4521
1.4523
1.4526
1.4529
Legierungsbestandteile Edelstahl Seite19
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
M min. 12.25 7.50 2.00 0.90max. 0.05 13.25 8.50 2.50 0.01 0.10 0.20 0.10 1.35 0.008 0,01
A min. - 19.00 24.00 4.00 - - 1.2max. 0.02 21.00 26.00 5.00 0.15 2.00 2.0
A min. - 17.00 9.00 5xC -max. 0.08 19.00 12.00 0.70 2.00
M min. - 15.00 3.00 5xC 3.0max. 0.07 17.00 5.00 0.45 5.0
1.4546 min.max.
1.4547 A min.max.
A min. - 17.00 9.00 10xC -max. 0.08 19.00 12.00 1.0 2.00
A min. - 20.00 32.00 8x(C+N) - 0.15max. 0.03 23.00 35.00 0.60 1.00 0.45
A min. - 17.00 11.50 2.00 0.40 -max. 0.02 18.50 13.50 2.50 0.60 2.00
1.4562 min.max.
A min. - 26.00 30.00 3.00 0.04 - - 0.8max. 0.02 28.00 32.00 4.00 0.15 2.00 0.70 1.5
A min. - 23.00 16.00 3.50 0.4 3.50 -max. 0.03 25.00 18.00 5.00 0.6 6.50 1.00
A min. - 17.00 8.50 3.0max. 0.04 19.00 10.50 4.0
D min. - 16.00 6.50 - 0.70max. 0.09 18.00 7.80 1.00 1.50
A min. - 16.50 10.50 2.00 5xC -max. 0.08 18.50 13.50 2.50 0.70 2.00
A min. - 24.00 24.00 2.00 10x%C - -max. 0.04 26.00 26.00 2.50 0.60 2.00 0.50
A min. - 16.50 10.00 2.00 3.0max. 0.04 17.50 11.00 2.50 3.5
A min. - 16.50 10.50 2.00 - -max. 0.08 18.50 13.50 2.50 2.00 1.00
1.4582 D min.max.
FM min. - 13.50 1.00 0.20 0.30 -max. 0.08 15.50 2.50 1.20 0.50 1.00
A min. - 31.00 30.00 0.50 0.35 - - 0.3max. 0.02 35.00 33.00 2.00 0.60 2.00 0.50 1.2
1.4652 min.max.
F typ. 19.10 0.15
A min. 16.50 4.50 5.50 1.0max. 0.10 18.50 5.50 0.15 9.50 1.00 2.5 0.010 0,07
1.4534
1.4539
1.4541
1.4542
1.4550
1.4558
1.4561
1.4563
1.4565 S
1.4567
1.4568
1.4571
1.4577
1.4578
1.4580
1.4589
1.4591
1.4607
1.4618
Legierungsbestandteile Edelstahl Seite20
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
A min. 0.03 18.00 5.50 0.03 1.50 1.3max. 0.08 19.00 6.90 0.11 4.00 2.0
1.4660 min.max.
F min. - 6.00 0.50max. 0.12 8.00 1.00
1.4718 min.max.
F min. - 12.00 - 0.70 0.70max. 0.12 14.00 1.00 1.40 1.20
F min. 17.00 3.50max. 0.08 19.00 0.50 0.50 0.60 5.00 0.5 0.030 0,04
F min. - 17.00 - 0.70 0.70max. 0.12 19.00 1.00 1.40 1.20
1.4749 min.max.
F min. - 23.00 - 0.70 1.20max. 0.12 26.00 1.00 1.40 1.70
F min. - 19.00 - - - - 5.50max. 0.05 21.00 0.30 0.01 0.50 0.50 6.00
1.4821 min.max.
A min. - 19.00 11.00 1.50max. 0.20 21.00 13.00 2.50
1.4833 A min. - 22.00 12.00 - -max. 0.15 24.00 14.00 2.00 1.00
A min. - 24.00 19.00 - - 1.50max. 0.20 26.00 22.00 0.11 2.50 2.50
1.4842 min.max.
A min. - 24.00 19.00 - -max. 0.15 26.00 22.00 2.00 0.75
1.4854 typ. 0.05 27.50 35.00 0.15 1.60 0.85
1.4864 min.max.
D min. 0.20 23.00 4.00 8.00 -max. 0.30 26.00 7.00 10.00 1.00
A min. 0.06 19.00 30.00 0.20 0.50 0.20 0.20 -max. 0.08 21.00 32.00 0.50 1.00 0.60 0.40 0.5
A min. - 17.00 9.00 4x%C - -max. 0.10 19.00 12.00 0.80 2.00 1.00
1.4891 A 1.4818 mit. 18.50 9.50 0.15 1.30max. 0.05
A 1.4835 min. 0.05 20.00 10.00 0.12 1.40max. 0.12 22.00 12.00 0.20 2.50
M min. 0.08 8.00 0.85 0.03 0.18max. 0.12 9.50 1.05 0.07 0.25
1.4640
1.4713
1.4724
1.4737
1.4742
1.4762
1.4767
1.4828
1.4841
1.4845
1.4872
1.4876
1.4878
1.4893
1.4903
Legierungsbestandteile Edelstahl Seite21
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
A min. - 16.00 12.00 2.00 0.10max. 0.04 18.00 14.00 3.00 0.18
M min. 0.17 10.00 0.20 0.50 0.05 0.25 0.10max. 0.23 11.50 0.60 0.80 0.10 0.55 0.30
M min. 0.17 10.00 0.30 0.80 0.20max. 0.23 12.50 0.80 1.20 0.35
min. 0.18 11.00 0.30 0.80 0.25max. 0.24 12.50 0.80 1.20 0.35
F min. 0.08 11.00 2.00 1.50 0.02 0.50 0.25max. 0.13 12.50 3.00 2.00 0.04 0.90 0.40
1.4948 min.max.
A min. 0.06 19.00 30.00 0.30 0.50 0.20 0.30 -max. 0.10 22.00 32.00 0.60 1.00 0.60 0.60 0.5
A min. 0.03 13.50 24.00 1.00 1.90 0.10max. 0.08 16.00 27.00 1.50 2.30 0.50
min. 0.15 1.50 1.40 0.25 0.50max. 0.21 1.80 1.70 0.35 0.90 0.40
M min. - 8.50 8.50 4.50 0.50 - -max. 0.03 10.50 11.00 5.50 1.00 0.30 0.30
1.4910
1.4913
1.4922
1.4923
1.4939
1.4959
1.4980
1.6587
1.6908
Legierungsbestandteile Edelstahl Seite22
W Nb Andere
0.55
0.70
2.00
8.50
0.50
Co 9,25
3.50
Legierungsbestandteile Edelstahl Seite23
W Nb Andere
1.80
B 0,005
Co 2,9
9.30 Co 10
6.20 Co 4,8
6.30 Co 8,4
1.40 Co 7,8
1.20
6.20
6.20
6.30
1.80
1.80
5.90
18.00
6.20
14.30 Co 11
10.40 Co 8
Co 0,5
-0.25
Legierungsbestandteile Edelstahl Seite24
W Nb Andere
Legierungsbestandteile Edelstahl Seite25
W Nb Andere
Legierungsbestandteile Edelstahl Seite26
W Nb Andere
0.501.00
3xC+ 0,3
1.0
12xC0.40
0.6
≥ 8x % C
Legierungsbestandteile Edelstahl Seite27
W Nb Andere
-0.1
10x%C1.0
Legierungsbestandteile Edelstahl Seite28
W Nb Andere
Y, Zr, Hf
Zr, YHf
Ce
Ce 0.030.08
0.060.10
Legierungsbestandteile Edelstahl Seite29
W Nb Andere
B 0.00150.0050
B 0.0030.01
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 30 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1200°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A FerritMartensit M Duplex
F 340 700-850 210 14 7.85 12.5 13 13.6 14.1 0 1.13 44.9 41,6/350 460L 850 210 7.7 10.5 11 11 11.5 12 12 11.50 20 460
1600 2050 200 7.8 10.5 11 11.6 11.9 13.50 16 460210 7.7 12.4 12.1 12.6 12.8 13 0.60 30 460
720 210 7.85 12.2 12.9 13.5 13.9 14.2 14.5 14.8 1 1.3 41.5 460750 210 7.8 10 12.7 13.7 14.2 14.9 15.8 16.8 0.5 0.8 34.2 460
1100 210 7.83 11.1 12.9 13.4 13.8 14.2 14.6 14.9 34A 1400 1380 1300 1180 1020 780 510 200 1500 215 10 7.8 11.5 12 12.2 12.5 12.9 13 13.2 9.29 26 29.5 460A 215 7.8 11.5 12 12.2 12.5 12.9 13 13.2 9.82 24.3 27.7 460A 215 7.8 11.5 12 12.2 12.5 12.9 9.62 25 460
190 7.7 12 12.1 11.9 11.6 11.7 8.83 26 460A 215 7.85 12 12.5 12.7 13 13.2 13.4 13.7 12.14 30 30.1 460A 1420 1370 1310 1230 1080 850 510 215 7.85 11.5 12 12.2 12.5 12.9 13 13.2 14.24 30.8 30.4 460L 423 860 210 7.7 11 11.4 11.9 12.2 12.7 12.8 12.1 13.78 16.7 20,5/350 460
7.6 12.2 12.5 13 13.2 13.7 14 13.7 16.13 21.5210 7.85 11.5 12 12.2 12.5 12.8 0.55 30 460210 8 11 12.5 13 13.5 14 1.10 25 460215 8.4 11.5 12 12.2 12.5 12.9 13 13.2 2.70 30 460
M 1100 200 8.1 10.3 10.7 11 11.3 11.6 16.00 21 420215 7.8 12.5 13.1 13.4 13.9 14 14.3 14.5 2.75 36 36.8 460210 7.85 11 12.5 13 13.5 14 1.82 28 460210 7.85 11 12.5 13 13.5 14 2.12 28 460
1.2779 800 800 760 670 340 1050 208 15 7.95 16.5 16.8 17.1 17.3 17.5 17.7 18 19.12 13 26/700 420210 7.85 11.5 12 12.2 12.5 12.8 0.35 30 460215 7.9 11.5 12 12.2 12.5 12.9 13 13.2 9.24 30 33.6 460
A 980 215 11.3 11.9 12.2 12.6 13 13.3 13.5 19.50 31.4 35,2/350 460223 7.79 10.6 11.1 11.6 11.9 12.3 12.6 12.8 11.35 19.6 450
A 7.6 11.1 11.5 11.9 12.3 12.8 13.2 13.6 14.40 31.5 31.9217 8.3 9.6 10 10.1 10.3 10.5 10.7 10.7 15.88 19 460224 7.9 11.5 11.7 12.2 12.4 12.7 13 12.9 20.60 21 420240 8.05 10 10.5 10.8 11.2 11.3 11.4 11.6 20.70 22 420
1.3247 220 8.1 11 11.5 11.9 12.3 12.4 12.5 12.5 34.26 20 429217 7.9 11.5 11.7 12.2 12.4 12.7 13 12.9 18.95 19 460217 8.2 11.5 11.7 12.2 12.4 12.7 13 12.9 20.60 32.8217 8.1 11.5 11.7 12.2 12.4 12.7 13 12.9 20.60 19 460230 8 11.5 11.7 12.2 12.4 12.7 13 12.9 20.70 24 420217 8 11 11.5 11.9 12.3 12.4 12.5 12.5 32.18 19 460
1.3348 217 8.3 11 11.5 11.9 12.3 12.4 12.5 12.5 32.18 19 4601.3351 226 7.9 11.5 11.7 12.2 12.4 12.7 13 12.9 20.60 20 4401.3355 217 8.7 10 10.5 10.8 11.2 11.3 11.4 11.6 4.10 19 4601.3554 219 8.1 11.5 11.7 12.2 12.4 12.7 13 12.9 20.60 22 433
242 8.3 9.6 10 10.3 10.6 10.9 11.2 11.6 12.05 19 410231 8.1 10 10.5 10.8 11.2 11.3 11.4 11.6 11.40 17 420
A typ. 270 180 115 95 90 90 75 490 143 40 8.1 0,6-1,4 1,6-2,5 4,4-5,5 7,4-8,4 8,9-9,7 10-10,7 0 0.25 12.8 18.1 515A mind. 295 590-785 200 40 7.8 16.5 17.5 18 18.5 26.67 31.92 15 460A 365 890 108 35 7.9 15.7 17 17.5 17.8 33.1 38.6 14 460F 250 220 210 200 190 400-600 220 19 7.7 10.5 11 11.5 12 12 12 14 30 460F 245 220 210 200 190 216 20 7.65 10.5 11 11.5 12 12 13.5 13.5 30 460F 250 220 210 200 190 400-600 220 17 7.7 10.5 11 11.5 12 12 12 14 30 460F 320 240 230 215 450-650 220 20 7.7 10.4 10.8 11.2 11.6 11.9 10.5 12.98 25 430M 450 <730 215 12 7.7 10.5 11 11.5 12 12 12 15.98 30 460M 450 420 400 365 305 <600 215 20 7.7 10.5 11 11.5 12 12 14 30 460F 240 220 210 200 190 450-600 220 20 7.7 10 10 10.5 10.5 11 16 18 25 460F 350 500-750 220 12 7.7 10.2 10.8 16 18 30 460M QT700 500 420 400 365 305 700-850 215 13 7.7 10.5 11 11.5 12 12 12 14 30 460
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
1.17301.20801.20831.21011.21621.22101.23111.23431.23441.23451.23631.23651.23671.23791.23801.25101.25501.25811.27091.27111.27211.2767
1.28421.28851.2999K490W3601.32071.32431.3244
1.33261.33431.33441.33451.3346
S290S390
1.39121.39521.39641.40001.40011.40021.40031.40051.40061.40161.40171.4021
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 31 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1200°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A FerritMartensit M Duplex
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
M QT550 400 550-750 216 15 7.7 11 12 12 14 30 460M 650 <740 215 15 7.7 10.5 11 11.5 12 12 12 14 30 460M QT800 650 <800 215 12 7.7 10.5 11 11.5 12 12 12.5 14.5 30 460M QT800 650 <780 215 12 7.7 10.5 11 11.5 12 12.5 14.5 30 460M <850 220 7.7 10.5 11 11.5 12 12.5 14.5 30 460M 600 540 505 470 375 800-950 216 14 7.7 10 10.5 11 11 11 12.5 25 460M QT800 >600 515 475 435 355 <950 215 14 7.7 10 10.5 10.5 10.5 17.5 21.26 25 460D 450 380 330 300 650 200 30 7.8 9.5 11.5 12 25.2 26.68 15 480F >550 <730 220 15 7.7 10 10.5 10.5 10.5 11 16.16 19.48 25 460F >250 230 215 205 195 430-630 220 20 7.7 10 10.5 10.5 10.5 11 16 18 25 460M 1850 2105 223 3 7.72 10.4 10.8 11.2 11.6 11.9 21.61 27.63 14 430M 850 215 12 7.7 11 12 14.65 17.64 30 460M WG 427 738 215 18 7.7 10.4 10.8 11.2 11.6 11.9 19.97 23.29 15 430F 280 250 230 210 200 450-630 220 18 7.7 10 10.5 10.5 10.5 11 16.97 22.62 25 460M <850 215 12 7.7 10.5 11 11 11.5 15.65 17.64 30 460F 550 520 500 480 410 <770 220 14 7.7 10.4 10.8 11.2 11.6 11.9 14.97 18.29 25 430M 550 540 530 510 470 750-950 220 12 7.7 10.4 10.8 11.2 11.6 18.47 20.46 29 430M 195 7.7 10.4 10.5 10.8 22.35 26.27 30 460M 448 758 215 14 7.7 10.4 10.8 11.2 11.6 12 17.32 20.64 15 430D >450 380 330 300 650 200 30 7.7 13.5 14 14.5 26.01 15 500A 230 157 127 110 98 92 540-750 200 45 7.9 16 16.5 17 17.5 18 17 19.5 15 500A 220 155 127 110 98 92 500-650 200 46 7.9 16 16.5 17 17.5 18 17 19 15 500A 190 500-700 200 35 7.9 16 16.5 17 17.5 18 17 20.76 15 500A 220 147 118 100 89 81 520-670 200 45 7.9 16 16.5 17 17.5 18 18 20.76 15 500A 220 147 118 100 89 81 520-700 200 45 7.9 16 16.5 17 17.5 18 16.5 20.26 15 500
1.4308 A 175 440-640 200 30 7.9 17 18 20 17 460A 250 210 190 180 600-900 200 40 7.9 16 17 17 18 18 16 23.4 15 500A 270 205 157 136 125 119 550-750 200 40 7.9 16 17 17 18 18 18.92 23.02 15 500M Verg I 520 500 480 460 650-830 200 15 7.7 10.5 10.9 11.3 11.6 13.31 16.63 25 430A 290 210 170 140 590-785 200 40 7.9 17 17.5 18 19.92 23.52 15 440A 350 265 185 170 650-850 200 35 7.9 16 16.5 17 17.5 18 18.1 21.7 15 450A 230 550-750 200 45 7.9 16.5 17.5 16 18 15 500
1.4332 SZS 400 600 30A 180 165 130 115 105 470-670 197 35 8 15.8 16.1 16.5 16.9 17.3 24.3 26.3 12 450A 220 196 177 152 130 540-740 190 35 7.8 16.5 17 17.5 18 17.66 19.16 16.5 500D 400 330 280 600-830 200 30 7.8 13 13.5 14 23.13 29.13 15 500A 300 650-850 200 45 7.8 17 17.5 18.5 19.18 15 500A 350 295 230 205 750-950 200 45 7.8 15.7 17.5 16.8 22 15 500A 340 680-880 200 45 7.8 17.5 18.4 17.8 23 15 503A 400 350 290 260 230 200 160 120 60 600-900 200 41 7.9 16 16.5 17 17.5 18 17 24.3 15 500A 240 177 147 127 115 110 530-680 200 40 8 16 16.5 17 18.5 18 23.1 28.5 15 500A 240 166 137 118 108 100 530-680 200 40 8 16 16.5 17 18.5 18 23.1 28.5 15 500A 310 635 200 45 7.9 16 23.39 30.45 15 500A 300 211 167 145 135 128 580-780 200 40 8 16.5 17.5 25.02 30.27 15 500D 550 750-1000 200 15 7.8 12.5 13.5 37.74 46.45 15 500M QT760 550 520 500 480 760-960 200 16 7.7 10.8 10.8 11.2 11.6 17.95 22.27 15 430M 360 760 215 15 7.7 11 12 14.98 17.8 30 460A 390 710 200 43 7.9 16 25.81 15
1.40241.40281.40311.40341.40371.40441.40571.40621.41041.41051.41081.41101.41121.41131.41161.41201.41221.41231.41251.41621.43011.43031.43051.43061.4307
Guss1.43101.43111.43131.43151.43181.4319
1.43351.43611.43621.43711.43721.43731.43761.44011.4404
316plus1.44061.44101.44181.44191.4420
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 32 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1200°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A FerritMartensit M Duplex
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
AF 210 170 140 120 110 500-700 200 15 7.95 16.5 17.5 17.5 18.5 18.5 24.75 28.4 15 500A 295 225 178 155 145 138 580-800 200 40 8 16.5 17.5 17.5 18.5 18.5 26.67 31.92 15 500A 240 166 137 118 108 100 550-700 200 40 8 16 16.5 17 17.5 18 24.75 28.4 15 500A 290 225 185 165 150 135 590 200 40 8 16 16.5 17 17.5 18 31 14 500A 240 165 137 119 108 100 550-700 200 40 8 16 16.5 17 17.5 18 25.25 30.66 15 500A 200 175 127 118 110 100 500-700 200 40 7.98 16 16.5 17 17.5 18 24.75 30.16 15 500A 220 172 147 127 115 110 520-720 200 40 8 16.5 17.5 18 18.5 19 27.4 32.7 14 500A 290 225 185 165 150 580-780 200 35 8 16 16.5 17 17.5 18 31.62 38.52 14 500D 450 360 310 295 620-880 200 20 7.8 13 13.5 14 30.09 37.8 15 500D 500 360 315 300 700-950 200 20 7.8 13 13.5 14 30.85 38.07 15 500A 260 195 155 135 125 115 540-740 198 40/35 8 15.8 16.5 16.9 17.3 31.88 36.81 12 450A 255 230 210 185 160 540-740 195 30 7.9 15.8 16.4 16.7 17.1 17.4 32.7 35.33 13 450D 650 800-1050 200 20 7.7 12 14 37.75 44.98 13 470D 530 450 400 730-930 200 25 7.8 13 13.5 14 37.1 44 15 500A 210 180 150 135 125 500 196 35 8 16.7 17.2 17.7 18.1 18.4 18.8 30.25 33.9 11.9 472A 225 185 165 145 135 130 490-740 200 35 8 16.3 16.9 17.3 17.8 18.2 23.1 26.75 14 450D 550 750-1000 200 17 7.8 12.5 13.5 37.1 44 15 500F 250 230 210 200 430-630 220 18 7.7 10 10 10.5 10.5 17.5 18.5 25 460F 240 195 185 165 420-600 220 23 7.7 10 10 10.5 10.5 11 16 18 25 460F 240 218 210 200 190 400-630 220 7.7 7.7 10 10 10.5 10.5 11 16 18 25 460F 210 200 190 180 380-560 220 25 7.7 10.5 11 11.5 12 12 16 18 25 460F 220 400-550 220 23 7.7 10.5 10.5 18.64 22.94 25 460F 320 450-650 220 23 7.7 10.5 11.5 10.5 12.5 30 460F 200 195 170 155 380-530 200 24 7.7 10.4 10.8 11.2 11.6 11.9 16 18.24 20 430F 320 250 230 210 200 420-640 220 20 7.7 10.4 10.8 11.2 11.6 11.9 22.94 28.73 23 430F 370 335 300 280 520 225 30 7.7 10 11 11.5 25.59 22 460F 370 520 220 27 7.7 11.7 12.1 12.7 14.2 21.63 30 440A 300 230 190 170 160 120 650-850 193 40 8.1 15 15.7 16.1 16.4 16.7 42.2 48.1 12 415M 1440 1360 1260 1160 1050 720 1520 202 9 7.74 10.5 10.7 11.2 11.3 11.6 19.96 13 21 500A 290 600-800 195 40 8.1 42.23 48.81 14 500A 240 205 175 145 125 110 530-730 195 35 8 15.8 16.1 16.5 16.9 17.3 37.2 44.9 12 450A 220 176 157 136 125 119 520-720 200 40 7.9 16 16.5 17 17.5 18 17 19 15 500M P800 520 500 480 460 800-950 200 16 7.8 10.9 11.1 15 18.98 16 500A 320 20 190 170 160 148 650-850 195 35 8 17 18 42.18 47.6 14 500A 220 177 157 136 125 119 520-720 200 40 7.9 16 16.5 17 17.5 18 17 19 15 500A 180 155 140 130 120 450-700 197 35 8 15.8 16.1 16.5 16.9 17.3 20 23 12 450A 190 166 137 118 108 100 490-690 200 40 7.9 17 17.58 18 23.6 26.75 15 440A 276 210 180 165 150 135 650 198 40 8.1 14.3 14.7 15.1 15.5 15.7 15.9 48.2 55.1 11.7 452A 215 190 160 150 135 120 500-700 197 35 8 15.8 16.1 16.5 16.9 17.3 36.54 43.6 12 450A 420 350 270 240 210 210 800-950 190 35 8 14.5 15.5 16.3 16.8 17.2 40.95 51.1 12 450A 175 450-650 200 45 7.9 16.7 17.2 17.7 18.1 18.4 17 20.76 15 500D 330 <1030 200 19 7.8 13 13.5 14 16 18 16 500A 240 185 167 145 135 129 540-690 200 40 8 16.5 17.5 18 18.5 19 23.1 26.75 15 500F 500 600-750 215 20 7.7 32.48 38.25 14.5 400A 205 175 145 130 120 490-740 197 40 8 15.8 16.1 16.5 16.9 17.3 30.6 34.25 12 450A 175 450-650 45 7.98 16.7 23.1 27.51 15 500A 215 186 167 145 135 129 510-740 200 35 7.98 16.5 17.5 18 18.5 19 23.1 26.75 15 500
FM 420 550-750 220 16 7.7 10.5 11 11.5 12 12 14.16 19.46 25 460
1.44271.44291.44321.44341.44351.44361.44381.44391.44601.44621.44651.44661.44771.45011.45031.45051.45071.45091.45101.45111.45121.45131.45161.45201.45211.45231.45261.45291.45341.45371.45391.45411.45421.45471.45501.45581.45611.45621.4563
1.4565 S1.45671.45681.45711.45751.45771.45781.45801.4589
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 33 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1200°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A FerritMartensit M Duplex
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
F 250 400-550 220 23 7.7 16 17.5 26 460A 380 320 270 240 220 210 720 195 40 7.9 14.5 15.3 15.3 15.7 16.1 38.25 51.2 13.4 500F 450 550-700 220 20 7.7 37.55 45.57 17 440F 220 380-560 220 25 7.7 10.8 11.6 14 19.2 30 460A 300 580-780 200 40 7.8 16.5 17 18.4 28.5 15 500F 330 430-580 220 30 7.7 10.3 19.1 18 390F 310 540-750 205 31 7.7 10 10.1 10.6 21 22.3 26 460F 330 490 205 30 7.7 10 10.1 10.6 23.8 25.3 26 460A 330 650 200 50 7.7 17.4 18.5 18.08 15 500F 360 320 295 270 260 225 150 90 510 210 29 7.7 11.5 12 12.6 13.5 20.2 21.3 450F 360 470 220 30 7.7 10 21 25A 230 175 135 112 98 92 540-750 200 43 7.9 16 17 17 18 18 18.48 20.76 15 500A 430 350 315 300 295 280 750-1000 190 40 8 15 15.4 16.2 53.3 60.2 9 500D 420 600-850 200 20 7.8 13.5 23.13 29.18 15 500
420 350 300 280 800-1000 190 40 8.2 15.5 16.3 46.75 54.45 12 450F 220 420-620 215 20 7.7 11.5 12 12.5 13 6 8 23 500F 250 450-650 200 15 7.7 10.5 11.5 12 12.5 12 14 21 23 500F 420 550 7.3 10.9 11.3 11.6 12 12.4 12.7 13.2 13.8 14.3 14.8 17 19 14.8 19.6 500F 270 500-700 200 13 7.7 10.5 11.5 12 12.5 13.5 17 19 19 25 500F 280 500-700 200 13 7.7 10 11 28.4 33 17 500F 320 450 208 18 7.8 9.8 10.1 10.5 10.8 11 11.2 11.4 11.8 12.3 12.8 20 24.64 20 469F 250 350 220 20 7.7 10.3 10.8 11.2 11.4 11.6 11.9 12.3 12.7 20 24 26 470F 280 520-720 220 10 7.7 10.5 11.5 12 12 13.5 23 26 17 23 500F 510 650 15 7.16 12.2 12.4 12.6 12.9 13.3 13.6 13.8 14.3 14.8 19 22.16 9.8 16.9 490A 290 200 165 150 140 130 120 110 600-800 200 30 7.8 16.5 18 19.92 23.2 15 500
1.4823 D 490-780 200 7.7 14.5 15.5 16.5 25 29.65 25 460A 230 165 107 58 450 8 7.8 17.2 18.3 18.8 21 24.65 14 504A 230 140 116 100 91 85 82 550-750 196 30 7.77 16.5 17.5 18 18.5 19.5 19 21 15 500A 310 140 116 100 91 85 82 500-700 196 45 7.77 16 17.5 18 18.5 19.5 22 25.76 15 19 500A 310 230 185 170 160 150 140 130 650-850 200 40 7.8 17 18 18.5 19 19.5 21.9 25.2 15 500A 220 163 78 47 450 12 7.8 17.5 18.4 19.3 24 28.65 14 500A 230 550-750 196 30 7.76 15.5 17 17.5 18 19 19.5 24 29.3 15 19 500A 210 140 116 100 91 85 82 500-750 196 35 7.76 17 18.8 19.4 20 24 26 14 19 500A 220 170 69 450 186 8 7.8 17 18 19 24 28.65 14.6 500A 300 650-850 190 40 7.9 15.5 16.5 25.92 29.2 11 450A 285 265 240 220 210 200 195 175 135 85 48 650 194 30 8 15.1 15.7 16.2 16.6 17 17.4 17.7 18 18.3 18.6 15 17 11.4 19.5 472A 285 265 240 220 210 200 195 175 135 85 48 650 194 30 8 15.1 15.7 16.2 16.6 17 17.4 17.7 18 18.3 18.6 15 17 11.4 19.5 472D 500 390 380 370 360 325 245 190 150 125 850-1050 25 7.8 16.5 18 18.5 19 19.5 23 36 14.5 500A 170 140 115 95 85 80 75 450 194 30 8 15.1 15.7 16.2 16.6 17 17.4 17.7 18 18.3 18.6 19 21 11.5 19.6 472A 185 160 140 120 105 95 90 80 500-750 191 30 8 15.1 15.5 15.9 16.2 16.5 16.9 17.3 17.7 18.1 18.4 26 28 12 20 445A 190 162 142 132 123 113 103 500-720 196 45 7.92 18 19 19.4 17 19 13.9 472A 330 272 228 203 192 170 132 74 34 600 28 7.95 16.4 16.7 17 17.3 17.8 20 23 12 490M 450 410 380 360 340 300 215 630-730 218 17 7.7 11.3 12 12.7 10.81 12.97 29.2 460A 260 205 170 150 135 125 121 550-750 200 35 8 16.3 16.9 17.3 17.6 18.2 18.5 18.7 24.2 30.76 16 450M 750 701 651 627 577 495 305 900-1050 216 12 7.7 10.5 12.5 12.45 15.74 29.2 460M 500 460 430 390 360 290 700-850 210 14 7.7 10.5 12.5 12.64 16.46 29.2 460M QT1 600 570 530 480 420 345 210 800-950 200 14 7.7 10.5 11 11.5 12 12.3 12.5 16 18 24 29/650 460F 700 800 760 705 585 350 900-1100 210 12 7.75 10.8 12.1 16.27 19.74 22 460
1.45901.45911.45921.45951.45971.46071.46111.46131.46181.46211.46221.46401.46521.46551.4659 A1.47131.47241.47371.47421.47491.47551.47601.47621.47671.4818
Guss1.4826 Guss1.48281.48331.48351.4837 Guss1.48411.48451.4848 Guss1.48541.48621.48641.48721.48761.48771.48781.48881.49031.49101.49131.49221.49231.4939
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 34 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1200°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A FerritMartensit M Duplex
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
A 600 590 570 555 535 510 465 315 80 900-1200 201 14 7,95 16,5 16,8 17,1 17,3 17,5 17.7 18 18.5 19.29 13 26/700 460A 210 157 127 108 98 88 78 510-710 196 45 7.93 18.8 19.4 20 18.1 14.3 472A 170 140 115 95 85 80 75 450 194 30 8 15.1 15.7 16.2 16.6 17 17.4 17.7 18 18.3 18.6 19 22 11.5 19.6 472A 600 580 560 540 520 490 430 900-1150 211 15 8 17 18.7 18.5 16.8 20.95A 490 430 390 355 315 255 640-840 200 17 7,9 15,7 16,7 17.1 17.4 17.6 17.8 18 18.7 22.44 15 460
1.6587 685 840-1270 210 7 7,77 11,5 12,5 13.3 13.9 2.32 2.95 49 431M 970 203 8 8.1 9.9 10.7 11.1 11.2 23.35 28.65 440
500 750-900 210 14 7.72 11.1 12.1 12.9 13.5 0.9 2.19 42.6 4701.8507 600 800-1000 14 11.1 12.1 12.9 13.5 13.9
600 800-1000 210 10 7.6 11.1 12.1 12.9 13.5 2 2.62 42.6 470
1.49441.49481.49591.49801.4986
1.69081.7225
1.8550
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 35 von 78
EW
bei 20°C
0.120.65
0.350.160.33
0.520.520.520.520.370.50.650.590.350.30.330.420.30.30.30.910.350.5
0.550.590.80.490.610.520.5
0.540.540.60.650.530.50.470.560.610.760.750.70.60.60.60.60.60.60.60.70.6
(Ω mm²/m)
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 36 von 78
EW
bei 20°C(Ω mm²/m)
0.60.550.550.650.550.70.70.70.70.70.80.620.80.70.650.60.650.80.80.750.730.730.730.730.730.550.730.730.60.70.80.73
10.750.80.70.70.70.730.750.750.750.750.80.70.62
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 37 von 78
EW
bei 20°C(Ω mm²/m)
0.750.750.750.80.750.750.850.850.80.81
0.90.80.80.960.880.80.60.60.60.60.70.60.70.8
0.70.960.610.85
10.730.710.850.73
10.71.03
10.920.730.80.750.81
0.750.750.6
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 38 von 78
EW
bei 20°C(Ω mm²/m)
0.61.040.670.60.730.650.60.60.770.7
0.730.780.81
0.690.751.220.930.70.560.551.11.40.850.55
0.850.780.84
0.90.9
11.041.040.751.010.960.741.06
0.77
0.6
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 39 von 78
EW
bei 20°C(Ω mm²/m)
0.910.711.01
0.860.120.470.19
0.19
Deutschland USA USA Schweden Frankreich UK Japan
W.-Nr. DIN/DIN EN JIS
Austenit
Ni 99.2 N 02200 NA 11/NA 12LCNi99 B160 N 02201NiCu30Fe B164 N 04400 Nu 30 3076 Na13NiCu30Al N 05500 3076 Na18NiFe15Mo A 753
2.4600 NiMo29Cr N 10675N 06022
2.4605 NiCr23Mo16Al N 060592.4610 NiMo16Cr16Ti N 06455 3076 Na452.4617 N 10665
NiCr25FeAlY N 060252.4642 N 066902.4647
NiCo20Cr20MoTi N 07263 NCK 20 DN 08020
NiCr23Co12Mo N 06617NiCr22Fe18Mo N 06002 NC 22 FeDNiCr19Fe19Nb5Mo3 N 07718 NC 19 FeNb NA 51NiCr15Fe7TiAl AMS 559 8A N 07750 NC 15 FNbA HR 505NiCr22Co12Mo9 N 06617NiCr23Mo16Cu N 06200
2.46772.4733 NiCr22W14Mo N 062302.4816 NiCr15Fe B166 N06600 3076 Na14
N 10276NiCr23Fe N 06601 NC 23 FeA
2.4852 N 09925NiCr22Mo9Nb N 06625 NC 22 DNb NA 21NiCr22Mo9Nb N 06626 NA 21NiCr21Mo N 08825 NC 21 FeDU NA 16
2.4867 N 060042.4951 N 06075
N 070802.4969 NiCr20Co18Ti AMS 5829 N 07090 NC 20 KTA 2HR2
AISI1 )UNS 2)
/ASTM SS 3) AFNOR 4) BS 5)
2.40662.40682.43602.43752.4545
2.4602
2.4633
2.46502.46602.46632.46652.46682.46692.46732.4675
2.48192.4851
2.48562.48562.4558
2.4952
Markenname
201400K5004B3C22Alloy 59Hastelloy C4B2602 CA690603 GT
20CB3617Hastelloy X718X-750617 BC20002100 GT
600
601925625625LCF825
7580A90
W.-Nr. Werkstoff Alloy-Bez. Ni Cr Si C Al Ti Fe Sonstige
1.4847 Nicrofer 2020 840 20 20 – 0.06 0.3 0.4 58 –1.4876 Nicrofer 3220 800 31 20 – 0.06 0.25 0.4 47 –1.4862 Nicrofer 3718 DS*) 36 18 2.2 0.08 0.15 0.15 42 –
2.4066 Nickel 99.2 99,2 0,1 0,1
2.4068 LC-Nickel 99.2 99,2 0,1 0,022.4633 NiCr25FeAlY 62 25 0,2 2,1 0,15 9,5 Y 0,08, Zr 0,05,2.4642 Nicrofer 6030 690 61 29 – < 0,02 – – 9 –2.4851 Nicrofer 6023 601 60 23 – 0.06 1.4 0.4 14 –2.4816 Nicrofer 7216 600 74 16 – 0.07 0.2 0.2 9 –2.4951 Nicrofer 7520 75 75 20 – 0.1 0.2 0.4 3 –2.4889 Nicrofer 45 TM TM 47 27 2.7 0.08 – – 23 0,1 SE
Nicrofer 6009 Al 10 10 Al 57 8 – – 10 – 26 0,1 HF2.4658 Cronix 70 NiCr 70/30 68 30 1.3 0.05 – – – 0,03 SE2.4869 Cronix 80 NiCr 80/20 78 20 1.3 0.06 – – – 0,03 SE
W.-Nr. Werkstoff Alloy-Bez. Ni Cr Mo C Al Ti Fe Sonstige
1.4958 Nicrofer 3220 H 800 H 31 21 – 0.07 0.25 0.35 47 –1.4959 Nicrofer 3220 HAT 800 HP 30 21 – 0.09 0.5 0.5 47 –1.4877 Nicrofer 3228 NbCe AC 66 32 28 – 0.05 – – 39 0,8 NB, 0,07 Ce2.4851 Nicrofer 6023 H 601 H 60 23 – 0.06 1.4 0.5 14 –2.4816 Nicrofer 7216 H 600 H 74 16 – 0.07 0.2 0.2 9 –2.4608 Nicrofer 4626 MoW 333 46 25 3 0.05 0.1 – 17 3 W, 3 Co, 1 Si2.4665 Nicrofer 4722 Co X 48 22 9 0.07 – – 18 1 Co2.4650 Nicrofer 5120 CoTi C-263 51 20 6 0.06 0.5 2.1 0.5 20 Co2.4668 Nicrofer 5219 Nb 718 53 19 3 0.05 0.6 0.9 18 5,2 Nb2.4663 Nicrofer 5520 Co 617 54 22 9 0.06 1 0.5 1 12 Co2.4856 625 61 21 9 0.10 0.4 0.4 2.5 1 Co, 3.6 Nb2.4633 Nicrofer 6025 HT 602 CA 62 25 – 0.18 2.3 0.2 9.5 0,1 Y, 0,01 Zr2.4647 Nicrofer 6125 GT 603 GT 62 25 – 0.22 2.8 0.2 9 0,1 Y, 0,01 Zr2.4669 Nicrofer 7016 TiNb X-750 72 16 – 0.05 0.6 2.7 7 1 Nb2.4673 Nicrofer 5520 Co ´B 617 B 22 9 0,06 1 0,4 0,7 0,6 Nb, 0,3 V 2.4952 Nicrofer 7520 Ti 80 A 75 20 – 0.06 1.4 2.3 – –2.4677 Nicrotan 6325 hAiC 2100 GT 63 25 – 0.3 3 – 1 8 Ta, 0,1 Y
– Cronix 70 NS 70 NS 67 30 – 0.08 0.15 – – 2,3 Si, 0,4 N, 0,2 Y
0,4 Fe, 0,3 Mn, 0,25 Cu, 0,05 Mg, 0,005 S
0,4 Fe, 0,3 Mn, 0,25 Cu, 0,05 Mg, 0,01-0,1
TI, 0,005 S
Tabelle 3 - Chemische Zusammensetzung hitzebeständiger Nickellegierungen und Sonderedelstählen in Masse %
Tabelle 4 - Chemische Zusammensetzung hochwarmfester Nickellegierungen und Sonderedelstählen in Masse %
OutokumpuOutokumpuOutokumpu
VDM
VDMVDMVDMVDMVDMVDMVDMVDMVDMVDM
OutokumpuOutokumpuOutokumpu
Outokumpu / SMOutokumpu / SM
VDMVDMVDMVDM
Outokumpu / SMSpecial Metals
VDMVDMVDMVDMVDMVDMVDM
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 46 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1100°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A
A 100 380 205 40 8.9 13.3 13.9 14.3 14.8 15.2 15.6 15.8 16.2 16.5 16.7 70.5 57.5 456A 80 70 65 60 55 50 40 340 205 8.9 13.3 13.9 14.3 14.8 15.2 15.6 15.8 16.2 16.5 16.7 79 58.5 456A wg 180 150 135 130 130 450 182 35 8.8 13.9 15.5 15.8 16 16.3 16.6 17 17.4 17.7 26 44 430A 690 670 640 620 600 570 490 1100 179 8.5 13.7 14.6 14.9 15.2 15.5 16 16.6 17 17.5 17.4 30.5 420A 170 450 30 16.2A 340 315 285 270 255 700 - 1000 217 40 9.22 90,1 108,6 11.2 373A 310 270 225 195 175 690 206 45 8.7 12.4 12.4 12.5 13.1 13.7 14.3 14.9 15.5 15.8 16.2 61.25 70.35 9.4 19.5 406A 340 290 250 220 190 690 210 30 8.6 11.9 12.2 12.5 12.7 12.9 13.1 71.5 78.45 10.4 18.6 414A 305 285 255 245 225 700 211 40 8.6 10.9 11.9 12.5 12.9 13.2 13.6 14 14.5 15.1 15.9 60.7 73.6 10.1 18.4 408A 340 315 285 270 255 755 217 40 9.2 10.3 10.8 11.1 11.4 11.6 11.8 86.2 100 11.4 17.3 377A 270 240 220 200 190 180 175 170 675 215 30 7.9 11.9 13.5 14 14.5 14.7 14.9 15.7 16.6 17.1 17.5 17.6 24 26 11.3 19.2 450A 240 586 215 30 8.2 27 31 12 450
2.4647 AA 400 540 222 15 8.4 10.7 12 12.5 13 13.5 14.1 14.9 15.9 17.2 18.2 11.7 19.7 426A 240 210 180 160 550 202 30 8.1 15 15.6 16 16.4 16.7 17.1 17.4 25.6 30.9 11.5 19.8 456A 300 270 230 220 210 200 190 185 700 212 35 8.4 11.6 12.6 13.1 13.6 13.9 14 14.8 15.4 15.8 16.3 46.4 56 13.4 20.9 420A 310 725 205 30 8.3 13.6 13.9 14.3 14.6 14.9 15.2 15.6 15.9 16.3 16.7 43.3 53 11.3 19.5 435A 550 965 205 30 8.2 12.6 13.4 13.8 14.1 14.4 14.8 15.4 16.1 16.8 26.24 31.89 11.1 18.9 432A 630 980 214 8 8.2 12.9 14 14.5 14.8 15.4 16.3 17.1 17.8 14 17 12 18.5 430A 300 270 230 220 210 200 190 185 700 212 30 8.7 12.6 13.1 13.4 13.7 14.1 14.6 15.3 16 16.6 17.1 17.6 47.4 56 11.7 20.7 450A 330 295 255 225 195 185 710 - 1000 218 45 8.5 12.4 71.5 80.1 9.1 428
2.4677 AA
2.4816 AAA 300 650 207 30 8.1 13.8 14.4 14.6 14.8 15.1 15.7 16.3 16.7 17.2 17.7 18.3 25 25 11.3 19.2 450
2.4852 AAA 415 350 320 300 280 830 209 30 8.4 12.8 13.1 13.4 13.7 14.1 14.6 15.2 15.8 16.4 17 47.4 56 9.8 17.3 415A 240 205 180 170 160 585 195 30 8.1 14.1 14.9 15.2 15.6 15.8 16 16.7 17.2 17.6 17.9 27.75 35.05 10.8 18.3 440
2.4867 A2.4951 A
A2.4969 A
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
2.40662.40682.43602.43752.45452.46002.46022.46052.46102.46172.46332.4642
2.46502.46602.46632.46652.46682.46692.46732.4675
2.4733
2.48192.4851
2.48562.48562.4558
2.4952
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 47 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1100°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 48 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1100°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 49 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C E-Modul Dichte PRE WLF sp. W
W.-Nr. [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C 800°C 900°C 1000°C 1100°C UG OG W/(mxK) W/(mxK) J/(kgxK)DIN EN bei 20°C bei 20°C bei 500°C bei 20°C
Austenit A
RP 0.2 RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°C
kg/dm3
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 50 von 78
EW
bei 20°C
0.90.9
0.5130.61
1.371.141.261.241.371.181.15
1.151.071.221.151.231.211.221.28
1.19
1.281.12
(Ω mm²/m)
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 51 von 78
EW
bei 20°C(Ω mm²/m)
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 52 von 78
EW
bei 20°C(Ω mm²/m)
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 53 von 78
EW
bei 20°C(Ω mm²/m)
Fontargenloteinterne Bezeichnung DIN EN 1044DIN 8513 EN ISO 3677 AWS AMS
NickelbasislotNI 102 L-Ni2 B-Ni82CrSiBFE-970/1000 B Ni-2 4777 FNI 102 L-Ni2 B-Ni82CrSiBFE-970/1000 B Ni-2 4777 F
Ni 103 L-Ni3 B-Ni92SiB-980/1040 B Ni-3 4778 D
HTL 6 / HTL 6 AP Ni 106 L-Ni6 B-Ni89P-875 B Ni-6Ni 106 L-Ni6 B-Ni89P-875 B Ni-6
HTL 7 / HTL 7 AP Ni 107 L-Ni7 B-Ni76CrP-980 B Ni-7Ni 107 L-Ni7 B-Ni76CrP-980 B Ni-7Ni 107 L-Ni7 B-Ni76CrP-980 B Ni-7
Kupferbasislot4764 E
HTL 2 AP BHTL 2 AP (L)HTL 270 / HTL 270 APHTL 3 / HTL 3 APHTL 5 M / HTL 5 M AP
HTL 6 AP B
HTL 7 AP (L)HTL 7 AP Nr.4
HTL 9 / HTL 9 AP
Rolls Royce
9500/979500/97
FontargenloteZusammensetzung Cr Cu Si B Fe C P Ni Mn
Nickelbasislot7,0 4.5 3.1 3,0 <0,06 <0,02 Rest7,0 4.5 3.1 3,0 <0,06 <0,02 Rest11,8 10,0 8,0 Rest
4,5 3,1 <0,5 <0,06 <0,02 Rest18,0 8,0 2,0 Rest
<0,06 11,0 Rest<0,06 11,0 Rest
14,0 <0,10 <0,01 <0,20 <0,06 10,1 Rest14,0 <0,10 <0,01 <0,20 <0,06 10,1 Rest14,0 <0,10 <0,01 <0,20 <0,06 10,1 Rest
Kupferbasislot52,5 9,5 Rest
HTL 2 AP BHTL 2 AP (L)HTL 270 / HTL 270 APHTL 3 / HTL 3 APHTL 5 M / HTL 5 M APHTL 6 / HTL 6 APHTL 6 AP BHTL 7 / HTL 7 APHTL 7 AP (L)HTL 7 AP Nr.4
HTL 9 / HTL 9 AP
Fontargenlote
Zusammensetzung Viskositäts-bereichEinheit [°C] [°C] [°C] [mm] [mPas] [%]
Nickelbasislot1010 - 1177 1040 970 - 1000 0,02 - 0,20 90.000 - 115.000 901010 - 1170 1080 970 - 1000 0,02 - 0,15 100.000 - 115.000 90980 - 1050 870 - 890 bis 0,2 90.000 - 110.000 81
1010 - 1177 1040 980 - 1040 0,01 - 0,20 95.000 - 110.000 901050 - 1070 1060 971 - 1051 0,02 - 0,10 55.000 - 65.000 89927 - 1093 875 bis 0,05 60.000 - 80.000 90927 - 1093 875 bis 0,05 90.000 - 115.000 90927 - 1093 980 890 bis 0,05 60.000 - 80.000 90927 - 1093 980 890 bis 0,05 60.000 - 80.000 90927 - 1093 980 890 bis 0,05 90.000 - 110.000 89
Kupferbasislot1010 - 1093 1065 827 - 927 0,02 - 0,08
Arbeits-temperatur
empf. Löt-temperatur
Schmelz-bereich
Lötspalt-breite
Metall-anteil
HTL 2 AP BHTL 2 AP (L)HTL 270 / HTL 270 APHTL 3 / HTL 3 APHTL 5 M / HTL 5 M APHTL 6 / HTL 6 APHTL 6 AP BHTL 7 / HTL 7 APHTL 7 AP (L)HTL 7 AP Nr.4
HTL 9 / HTL 9 AP
[°C] [N/mm²] [N/mm²]
982 383 255982 383 255
982 393 234
760760855855855
538
Oxidations-beständigkeit
Scher-festigkeit
Scherfestig-keit bei RT
Deutschland USA USA Schweden Frankreich UK Japan GUS
W.-Nr. DIN/DIN EN JIS GOST
DINAustenit AMartensit MFerrit FDuplex D
M 48CrMoV6-7 45CDV6 SKT5 4ChMFS
A X38CrMoV5-1 H11 T 20811 Z38CDV5 BH11 SKD6 4Ch5MFs
A X40CrMoV5-1 H13 T 20813 Z40CDV5 BH13 SKD61
A X50CrMoV5-1
A 32CrMoV12-28 H10 T 20810 32DCV28 BH10 SKD7 3Ch3M3F
A X38CrMoV5-3 Z38CDV5-3
M X3NiCoTi18-9-5
A 54NiCrMoV6
A X45MoCrV5-3-1
AA
W620 AA
AISI1 )UNS 2)
/ASTM SS 3) AFNOR 4) BS 5)
1.23231.23431.23441.23451.23651.23671.27091.27111.2999W360W600
HTCS-130
Deutschland USA USA Schweden Frankreich UK Japan GUS
W.-Nr. DIN/DIN EN JIS GOST
DINAustenit AMartensit MFerrit FDuplex D
AISI1 )UNS 2)
/ASTM SS 3) AFNOR 4) BS 5)
Deutschland USA USA Schweden Frankreich UK Japan GUS
W.-Nr. DIN/DIN EN JIS GOST
DINAustenit AMartensit MFerrit FDuplex D
AISI1 )UNS 2)
/ASTM SS 3) AFNOR 4) BS 5)
Markenname Hersteller
PHM, W326 Märker, Böhler
W300 BöhlerW302 Böhler
W320 BöhlerW403VMR, W303 BöhlerWM722VM Böhler
W360 Böhler
Rovalma
Markenname Hersteller
Markenname Hersteller
Legierungsbestandteile Edelstahl Seite65
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
M 0.45 1.45 0.75 0.75 0.25 0.30
A min. 0.39 5.01 0.21 1.14 0.43 0.97 0.006 0.35 0,015max.
A 0.39 5.20 1.40 0.40 1.10 0.90
A 0.5 5.00 1.40 1.00 1.00
A 0.32 2.95 2.80 0.30 0.25 0.55
A 0.38 5.00 3.00 0.45 0.40 0.55
M min.max. 0.005 4.85 18.00 1.00
A 0.45 3.00 5.00 0.30 0.30 1.00
A 0.5 4.50 3.00 0.25 0.20 0.55
A 0.32 <0,1 2.00 3.30 0.25 0.10
W620 A 0.32 3.30 0.25 0.12
A 0.31 0.08 0.08 3.10 0.16 0.17 0.1
1.2323
1.2343
1.2344
1.2345
1.2365
1.2367
1.2709
1.2999
W360
W600
HTCS-130
Legierungsbestandteile Edelstahl Seite66
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
Legierungsbestandteile Edelstahl Seite67
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
Legierungsbestandteile Edelstahl Seite68
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
Legierungsbestandteile Edelstahl Seite69
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
Legierungsbestandteile Edelstahl Seite70
C Cr Ni Mo N Ti Nb Mn Si Al Cu S V PW.-Nr.
DIN EN
Legierungsbestandteile Edelstahl Seite71
W Nb Andere
Co: 9,25
1.8
1.8
1.85
Legierungsbestandteile Edelstahl Seite72
W Nb Andere
Legierungsbestandteile Edelstahl Seite73
W Nb Andere
Legierungsbestandteile Edelstahl Seite74
W Nb Andere
Legierungsbestandteile Edelstahl Seite75
W Nb Andere
Legierungsbestandteile Edelstahl Seite76
W Nb Andere
05/10/2023 mechanische, physikalische und chemische Kennwerte von Edelstählen Michael Ernst Müller
Seite 77 von 78
100°C 200°C 300°C 400°C 500°C 600°C 700°C KSZ E-Modul Dichte PRE WLF sp. W EW
W.-Nr.[N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] [N/mm2] Joule [N/mm2] [kN/mm2] % 100°C 200°C 300°C 400°C 500°C 600°C 700°C UG OG W/(mxK) W/(mxK) J/(kgxK) %
DIN EN bei 20°C bei 20°C bei 500°C bei 20°C bei 20°CAustenit A FerritMartensit M Duplex
M vergütet 1400 1200 1100 900 600 400 1600 200 7.85 11.5 12 12.2 12.5 12.9 13 13.2 3.93 36 33 460 0.3A 1400 1380 1300 1180 1020 780 510 200 400 1500 215 10 7.8 11.5 12 12.2 12.5 12.9 13 13.2 25.3 29.5 460 0.52A 1520 1250 1150 1030 850 530 480 1820 215 7.8 11.5 12 12.2 12.5 12.9 13 13.2 9.92 25.6 28,4/350 460 0.52
1.2345 A 11.7 12.7 13.4 13.8 9.62 19.5 24,8/350A 1420 1370 1290 1230 1040 840 520 430 1570 215 7.85 12 12.7 12.9 13.2 13.5 13.8 14.1 12.19 32.1 30.1 460 0.36A 1420 1370 1310 1230 1080 850 510 430 1570 215 7.85 11.5 12 12.2 12.5 12.9 13 13.2 14.24 30.8 30.4 460 0.5
1.2709ESU M Gehärtet 1800 1830 1720 1620 1490 1130 25 1900-2100 200 9 8.1 10.3 10.7 11 11.3 11.6 16 18.4 24 420 0.42 -0.08AA vergütet 11.3 11.9 12.2 12.6 13 13.3 13.5 19.50 31.4 35,2/350A 2120 212 7.6 11.1 11.5 11.9 12.3 12.8 13.2 13.6 14.40 31.9 0.59A 1500 1550 212 7.97 11.4 12.1 12.6 13.1 13.4 13.6 10.89 10.99 45.1 36.7 460
W620 A 50.8 37.3A 192 8 11.7 12.4 13 13.5 13.9 14.2 14.4 11.59 57.2 39.5 460
RP 0.2
1% ZDG (1000h) bei
500°C RM A80 Wärmeausdehnung in 10-6 x K-1 zw 20°CMaßänderung
beim Ausharten
kg/dm3 (Ω mm²/m)
1.23231.23431.2344
1.23651.2367
1.27111.2999W360W600
HTCS-130
Werkstoff Werkstoff ISONummer Kurzzeichen Reg. Nr.
3.0255 Al99,5 F83.0615 AlMgSiPb F283.1325 AlCuMg1 F393.1645 AlCuMgPb F373.1655 AlCuBiPb F373.2315 AlMgSi1 F303.3206 AlMgSi0,2 F223.3210 AlMgSi0,73.3315 AlMg13.3535 AlMg3 W193.3547 AlMg4,5Mn W283.4335 AlZn4,5Mg13.4345 AlZnMgCu0,53.4365 AlZnMgCu1,5 F53-48 T 7075 angefragt