PAINT FAULTS, BITTINESSPAINT FAULTS, BITTINESS
INCLUSIONS, INCLUSIONS, EITHER AIRBORN EITHER AIRBORN OR FROM THE OR FROM THE PAINT ITSELF. PAINT ITSELF. COULD BE COULD BE PARTIALLY CURED PARTIALLY CURED PAINT, OUT OF PAINT, OUT OF SHELF LIFE.SHELF LIFE.
COATING FAULTS BLEEDINGCOATING FAULTS BLEEDING
THE SOLVENT THE SOLVENT FROM THE TOP FROM THE TOP COAT SOFTENS COAT SOFTENS THE UNDER LYING THE UNDER LYING MATERIAL AND MATERIAL AND ALLOWS IT TO ALLOWS IT TO PASS INTO AND PASS INTO AND THROUGH THE THROUGH THE LAYER, CAUSING LAYER, CAUSING DISCOLOURATION. DISCOLOURATION. BROWN FOR BROWN FOR BITUMEN, YELLOW BITUMEN, YELLOW FOR COAL TARS.FOR COAL TARS.
COATING FAULTS BLISTERINGCOATING FAULTS BLISTERING
BLISTERS CAN BE FILLED WITH GAS, BLISTERS CAN BE FILLED WITH GAS, LIQUID OR CRYSTALSLIQUID OR CRYSTALS
COATING FAULTS CHALKINGCOATING FAULTS CHALKING
DEGRADATION OF A DEGRADATION OF A BINDER DUE TO BINDER DUE TO DISRUPTIVE DISRUPTIVE FACTORS IN THE FACTORS IN THE ENVIRONMENTENVIRONMENT
COATING FAULTS CISSINGCOATING FAULTS CISSING
CAUSED BY CAUSED BY INADEQUATE INADEQUATE SURFACE SURFACE PREPARATION.PREPARATION.
A DIFFERENCE IN A DIFFERENCE IN SURFACE ENERGY SURFACE ENERGY CAUSES LOCAL LACK CAUSES LOCAL LACK OF ADHESION.OF ADHESION.
COATING FAULTS CRACKINGCOATING FAULTS CRACKING
COATING AGE AND COATING AGE AND DIFFERENTIAL DIFFERENTIAL EXPANSIONEXPANSION
COATING FAULTS CRATERINGCOATING FAULTS CRATERING
BOWL SHAPED BOWL SHAPED DEPRESSIONS. DEPRESSIONS. CAUSED BY ESCAPING CAUSED BY ESCAPING SOLVENT OR GASES. SOLVENT OR GASES. PAINT IS OF TOO LOW PAINT IS OF TOO LOW A VISCOSITY TO FLOW A VISCOSITY TO FLOW AND FILL THE AND FILL THE DEPRESSIONSDEPRESSIONS
COATING FAULTS CURTAINS, SAGS, RUNS AND COATING FAULTS CURTAINS, SAGS, RUNS AND TEARSTEARS
CAUSED BY OVER CAUSED BY OVER APPLICATION. REMOVE APPLICATION. REMOVE OFFENDING EXCESS OFFENDING EXCESS MATERIAL, LIGHTLY MATERIAL, LIGHTLY ABRADE, RECOAT.ABRADE, RECOAT.
COATING FAULTS FLAKINGCOATING FAULTS FLAKING
MATERIAL MATERIAL PROGRESSIVELY PROGRESSIVELY GETS BRITTLE GETS BRITTLE WITH AGE, WITH AGE, CRACKS AND CRACKS AND BEGINS TO BEGINS TO DETACHDETACH
COATING FAULTS HOLIDAYSCOATING FAULTS HOLIDAYS
DEFINED AS DEFINED AS BEING :- A VOID, A BEING :- A VOID, A MISS, OR AN MISS, OR AN UNCOATED AREAUNCOATED AREA
COATING FAULTS LIFTINGCOATING FAULTS LIFTING
CAUSED BY SOLVENT STRENGTH AND ALSO CAUSED BY SOLVENT STRENGTH AND ALSO LACK OF OBSERVANCE OF STATED LACK OF OBSERVANCE OF STATED
OVERCOATING TIMEOVERCOATING TIME
ORANGE PEELORANGE PEEL
SIMILAR SIMILAR APPEARANCE TO A APPEARANCE TO A
CITRUS FRUIT SKINCITRUS FRUIT SKIN
CAUSED BY PAINT CAUSED BY PAINT VISCOSITY VISCOSITY
PROBLEMS OR BY PROBLEMS OR BY APPLICATOR APPLICATOR TECHNIQUETECHNIQUE
COATING FAULTS ROPINESSCOATING FAULTS ROPINESS
BRUSHMARKSBRUSHMARKS
ALGAE AND MOULD GROWTHALGAE AND MOULD GROWTH
COATING FAULTS WRINKLING AND COATING FAULTS WRINKLING AND RIVELLINGRIVELLING
QUANTITITIVE TESTS FOR HYGROSCOPIC SALTS
MERKOQUANT TEST
BRESLE SAMPLE PATCH
SALTS DETECTION, BRESLE SAMPLE PATCH KITSALTS DETECTION, BRESLE SAMPLE PATCH KIT
COLOUR MUNSELL AND BS COLOUR MUNSELL AND BS 48004800L= LUMINANCE, CHROMAL= LUMINANCE, CHROMA
a= FROM GREEN TO REDa= FROM GREEN TO RED
b= FROM BLUE TO YELLOWb= FROM BLUE TO YELLOW
YELLOW THROUGH GREEN ,BLUEYELLOW THROUGH GREEN ,BLUE
PURPLE, RED AND BACK TO PURPLE, RED AND BACK TO YELLOWYELLOW
HEALTH AND SAFETY DRAGER TUBE AND HEALTH AND SAFETY DRAGER TUBE AND BELLOWSBELLOWS
RUST GRADES
RUST GRADES
BLASTING GRADES A Sa 2.5 and Sa 3
BLASTING GRADES B Sa 1 and Sa 2
BLASTING GRADES B Sa 2.5 and Sa 3
BLASTING GRADES, COMPARISONS
BLASTING GRADES C Sa 1 and Sa 2
BLASTING GRADES C Sa 2.5 and Sa 3
BLASTING GRADES D Sa 1 and Sa 2
BLASTING GRADES D Sa 2.5 and Sa 3
SURFACE PROFILE ASSESSMENT
SURFACE COMPARATOR TO BS 7079 Pt C, ISO 8503
SHOT BLAST COMPARATOR. NOT TO BE USED FOR SURFACE CLEANLINESS. ONLY FOR ASSESSMENT OF SHOT BLASTED SUBSTRATES. GRIT BLAST COMPARATOR CAN ALSO BE USED ON SUBSTRATES BLASTED WITH GRIT/SHOT MIX
DRY ABRASIVE BLASTING
MEASURING PRESSURE AT THE NOZZLEHYPODERMIC NEEDLE
GAUGE
INSERT THE NEEDLE THROUGH THE HOSE WITH THE NEEDLE TOWARDS THE NOZZLE, AT AN ANGLE OF APP.
45 DEGREES
SURFACE PREPARATION
HAND AND POWER TOOL CLEANING B St 2 and St 3
SURFACE PREPARATION
HAND AND POWER TOOL CLEANING C St 2 and St 3
SURFACE PREPARATION
HAND AND POWER TOOL CLEANING D St 2 and St 3
SURFACE PREPARATION FLAME CLEANING
COPPER SLAG. COPPER SLAG.
CONTAMINATED CONTAMINATED COPPER SLAG. COPPER SLAG.
GARNET.GARNET.
METALLIC GRITMETALLIC GRIT
METALLIC SHOTMETALLIC SHOT
METALLIC GRIT AND METALLIC GRIT AND SHOT MIX. SHOT MIX.
WHIRLING HYGROMETERWHIRLING HYGROMETER
DENSITYDENSITY THE DENSITY ( SG ) CUPTHE DENSITY ( SG ) CUP
HEGMAN GRIND GAUGEHEGMAN GRIND GAUGE
FOR FINENESS OF GRIND, DEGREE OF FOR FINENESS OF GRIND, DEGREE OF DISPERSIONDISPERSION
REPLICA TAPE AND DIAL MICROMETERREPLICA TAPE AND DIAL MICROMETER
ROTATIONAL ROTATIONAL VISCOMETERVISCOMETER
KREBS STORMER VISCOMETERKREBS STORMER VISCOMETER
MECHANICAL THUMB TEST, THROUGH DRYINGMECHANICAL THUMB TEST, THROUGH DRYING
FLOW VISCOSITYFLOW VISCOSITY
A FORD FLOW CUPA FORD FLOW CUP
FORD FLOW CUP IN FORD FLOW CUP IN ITS RETORT AND ITS RETORT AND SHOWING THE 4mm SHOWING THE 4mm DIA HOLEDIA HOLE
VISCOSITY. FORD FLOW CUPVISCOSITY. FORD FLOW CUP
WET FILM MEASUREMENTWET FILM MEASUREMENT
ECCENTRIC WHEELECCENTRIC WHEEL
WET FILM THICKNESS MEASUREMENTWET FILM THICKNESS MEASUREMENT
COMB GAUGESCOMB GAUGES
ADHESION TESTS CROSS CUT ( CROSS HATCH ) ADHESION TESTS CROSS CUT ( CROSS HATCH ) TEST SPECIAL CUTTER TOOLTEST SPECIAL CUTTER TOOL
DESTRUCTIVE TEST GAUGES. THE SABERG TEST DESTRUCTIVE TEST GAUGES. THE SABERG TEST DRILLDRILL
DFT MEASUREMENTS ELECTRONIC GAUGESDFT MEASUREMENTS ELECTRONIC GAUGES
ELECTROPHYSIELECTROPHYSICC
MINI TESTMINI TESTTHE EXACTOTHE EXACTO
ELCOMETERELCOMETER
456456
DRY FILM THICKNESS MEASUREMENT, DRY FILM THICKNESS MEASUREMENT, MAGNETIC.MAGNETIC.
THE TINSLEY PENCILTHE TINSLEY PENCIL
DRY FILM THICKNESS MEASUREMENT, MAGNETIC,DRY FILM THICKNESS MEASUREMENT, MAGNETIC,
HORSESHOE GAUGEHORSESHOE GAUGE
DRY FILM THICKNESS MEASUREMENTS, DRY FILM THICKNESS MEASUREMENTS, MAGNETICMAGNETIC
THE BANANA GAUGE MODEL 211THE BANANA GAUGE MODEL 211SCALE SCALE MOVES TO MOVES TO THE CURSERTHE CURSER
DRY FILM THICKNESS MEASUREMENTDRY FILM THICKNESS MEASUREMENT
COLOUR CODED CALIBRATION SHIMSCOLOUR CODED CALIBRATION SHIMS
PURPLE PURPLE 25um25um
BLUE BLUE 50um50um
BROWN BROWN 125um125um
WHITE WHITE 250um250um
YELLOW YELLOW 500um500um
nominal valuesnominal values
ADHESION TESTS THE HYDRAULIC ADHESION ADHESION TESTS THE HYDRAULIC ADHESION TESTERTESTER
ADHESION TESTS THE DOLLY TESTADHESION TESTS THE DOLLY TEST
DESTRUCTIVE TEST GAUGES THE P.I.G.DESTRUCTIVE TEST GAUGES THE P.I.G.
OPACITY, THE PFUND CRYPTOMETEROPACITY, THE PFUND CRYPTOMETER
HIDING POWER CHARTS AND ADJUSTABLE HIDING POWER CHARTS AND ADJUSTABLE APPLICATORAPPLICATOR
FLEXIBILITY TEST CONICAL MANDRELFLEXIBILITY TEST CONICAL MANDREL
WOLFF- WILBORN PENCIL SCRATCH TESTWOLFF- WILBORN PENCIL SCRATCH TEST
USES THE PENCIL USES THE PENCIL HARDNESS HARDNESS RATING.RATING.