INFINO® Polycarbonate (PC) is named for polycarbonate, a non-toxic transparent engineering plastic resin that comes with the high level of impact strength compared with commodity plastics by Samsung Cheil Industries Chemical division. INFINO® PC is equipped with good mechanical strength, cold and heat resistance, stable optical characteristic and balanced electrical property.
INFINO® PC Alloy named for the product line of amorphous, thermoplastic polymer compounding based on polycarbonate (PC) and acrylonitrile butadiene styrene copolymer (ABS), PC and Polyethyleneterephthalate (PET) or PC and polybutyleneterephthalate (PBT) by Samsung Cheil Industries Chemical division. INFINO® PC alloy provides valuable benefits with combination of mechanical, thermal and physical Properties. PC alloy are widely used in a broad range of industries, including automotive, electric and electronics, display, mobile devices, lighting, building & construction, optical lenses and other appliances.
03INFINO® PC & PC Alloy
eco-friendly ® pC
® pC non-pHosGene proDUCtion teCHnoloGY
INFINO® PC is produced with the environmentally friendly and clean technology that made it possible to get neither phosgene nor chlorine involved in any part of its production process.
® pCM baseD pC & pC alloY
INFINO® PCM-based PC and PC Alloy are based on Samsung Cheil Industries’ unique compounding technology that uses recycled PC without compromising the standard PC’s balanced set of properties including excellent mechanical strength, heat resistance and dimensional stability. These material lineups are designed to better help comply with the environment regulations such as EPEAT in the United States helping reduce the emissions of CO2.
non-paintinG solUtion lUMinoUs
Luminous is a premium-class eco-friendly painting alternative material that enables manufacturing of plastic parts without painting.
Key Advantages of Luminous:
• Flow mark and weld line improvement
• Eco-friendly process with efficiency
• Superior appearance: bright, high gloss, metal like resin
lUMinoUspaintinG proCess
Injection
Non-Painting Resin
Primer CoatingInjection
Spray gun
Base Coating Clear Coating
04 Samsung Cheil Industries
product portfolio
General
Optical
Sheet
General
High Impact
Eco-Friendly
High Impact
FR
High Impact
High Modulus
Anti-Scratch
General
High Heat Resistant
Low Gloss
General
High Flow
High Heat Resistance
General
High Heat Resistant
High Weld Strength
High Flow
Chemical Resistant
General
Transparent
Non-Halogen
High Heat Resistant
General
Adhesion
High Impact
Super FR
High Heat Resistant
General
Chemical Resistant
General
High Flow
Polymerization General PC/ABS/GF
PC/PET
PC/PMMA
PC/ASA
Transparent High Performance/ Heat Resistant
Low Gloss
Eco-Friendly
Anti-Static
General
General FR
Metal Plating
Advanced Physical Property
High Impact
Luminous
Lubricant
Eco-Friendly
High Flow
High Heat Resistant
Eco-Friendly
Extrusion
Blow Molding
Super FR
Insulation Film
Light Diffusion
High Reflectivity
High Impact/Flow
High Gloss/High Flow
High Modulus
Scratch Resistance
Metal Plating
Eco-Friendly
Luminous
Extrusion
pC (General)
pC (fr)
pC/abs (General)
pC/abs (fr) pC/Gf pC alloy
pC & pC alloy
05INFINO® PC & PC Alloy
INFINO® Transparent PC resin features its outstanding optical clarity. Thanks to its superior flowability and thermal stability, INFINO® PC resin stays completely transparent without discoloration at elevated temperatures. Samsung Cheil Industries’ unique manufacturing technology to remove the low molecular weight oligomers made it possible to minimize the mold deposits during injection process. This advantage makes INFINO® Transparent PC most suitable for a wide variety of applications from small to large sized goods with complex design.
KeY featUres • Excellent optical characteristic: High transmittance,
UV resistant
• High impact strength
• Lightweight solution
• Good processability: Low molding temperature and short cycle time
appliCations
• Lighting: Automotive headlamp, Lighting lens • Light guide plate: Mobile display• Building & Construction: Roofing, Wall sheet extrusion • Data storage: CDs, DVDs • Optical lenses, Eyewear• Furniture
proDUCt line-Up
sHeet
PC00-SC-1060U00
PC00-SC-1080F00
General
PC00-SC-1100R00
PC00-SC-1100UR0
PC00-SC-1220R00
PC00-SC-1220UR0
PC00-SC-1280UR0 (Lighting)
optiCal
PC00-FX-8500L (LGP)
transparent pC®
06 Samsung Cheil Industries
proDUCt
INFINO® Light Diffusion PC is a noble blend of Samsung Cheil Industries’ high quality PC and light diffuser. A wide range of light diffusion PC lineups are available for both injection molding and extrusion. A variety of colors based on the diffusion and transparency levels are also available.
KeY featUres• Superior optical properties: High transparency
and high degree of diffusion
• Eco-friendly non-halogen flame retardant systme
• High productivity
• Excellent injection molding process: Minimize gate marks
• Outstanding durability
appliCations• LED/Conventional lighting lens cover
proDUCt line-Up
extrUsion
FD-1010 (3.0T V0)
FD-1112 (0.8T V2)
FD-1510D (1.2T V0)
bloW MolDinG/inJeCtion
FD-1122 (0.8T V2)
Diffusion pC®
07INFINO® PC & PC Alloy
proDUCt
High impact pC & pC alloyINFINO® High Impact PC and PC Alloy, which come with not only good mechanical strength but also excellent chemical resistance, are widely used in small electrical and electronic devices such as digital cameras and mobile handsets.
KeY featUres• Good processability
• Impact strength
• Heat resistant
• Good appearance
appliCations• Mobile devices
• Digital camera
proDUCt line-Up
®
proDUCt
reinforCeD
CF-3104HF (GF 10%)
CF-3200HF (GF 20%)
CF-3300HF (GF 30%)
CF-3300LW (GF 30%, Low Warpage)
sCratCH resistant
IV-1071 (F, High Gloss)
PF-1035 (HB, High Impact)
HiGH iMpaCt
General
QF-1035
Chemical resistant
CF-1050
transparent
CF-1011T
CF-1051T
eCo-frienDlY
GW-1030S (PCM 70%)
GW-1043 (PCM 80%)
08 Samsung Cheil Industries
reinforCeD
General GF 10%
HN-3102G (1.5T V0)
GF 20%
NH-3204G (2.0T V0, High flow)
NH-3208GL (0.75T V0)
HF-3201GL (1.5T V0)
GF 40%
NH-3402F (2.0T V1)
High Heat resistant GF 10%
HN-3104 (1.5T V0/3.0mm 5VB, F1)
flame retardant pC & pC alloyINFINO® Flame Retardant PC and PC Alloy have been developed so that they can provide the most suitable solutions to the safety and the environment regulations at the same time. High Impact Flame Retardant PC & PC/ABS are applicable to laptop computers and smart meters thanks to its well-balanced mechanical properties and processability.
KeY featUres• High flowability, High gloss, High modulus
• High impact
• Non-halogen flame retardant
• Good colorability
• Excellent appearance
appliCations• TV
• Battery
• Charger
• Note PC
• OA machine
• Smart meter
Transparent
High Flow
TN-1045M/S (2.0T V2)
TN-1100 (2.5T V0)
TN-1200 (2.0T V0)
High Heat Resistant
TH-1100 (VST 144°C, 2.0T V0)
High Heat Resistant
HN-1064IA (1.5T V0, RTI 130°C)
High Flow
UF-1017S (0.8T V0)
Back Light Unit
LB-1010W (0.75T V2, WH)
LH-1070W (1.5T V0, WH)
LB-1090HK (1.5T V0, BK)
Gf LS-1150G
(0.8T V2)
LS-1159 (High flow)
talc Talc 8%
NH-1101 (1.2T V0)
Talc 15%
NH-1150HH (1.2T V0)
fr pC proDUCt line-Up fr pC/abs proDUCt line-Up
®
proDUCt
non-reinforCeD HiGH MoDUlUsnon-HaloGen
General NH-1017 (2.0T V0/5VB)
High impact NH-1015 (1.5T V0) superior flame retardant NH-1027HF (1.2T V0/1.5T 5VB)
NE-1029 (1.2T V0/1.5T 5VB, Thin wall)
High Gloss/High flow
NE-1010 (1.5T V0)
NE-1030 (1.5T V0, High flow)
eco-friendly GC-1015 (1.5T V0, PCM 30%)
GC-1150 (1.5T V0, Talc 15%, PCM 30%)
luminous
LX-1031 (1.5T V0, High impact, Sparkle)
LX-1080 (1.2T V1, Metallic-look)
09INFINO® PC & PC Alloy
High Flow PC Alloy, generally used for automotive interior parts, has excellent processability together with other well-balanced properties such as good paintability and high impact strength.
INFINO® Metal Plating PC Alloy features its outstanding adhesion strength and superior appearance thanks to the cutting-edge technology from Samsung Cheil Industries. It is widely used for the automotive exterior parts by global automotive OEMs.
KeY featUres• High flow
• Good paintability
• Chemical resistance
• Impact strength
• Low TVOC
appliCations• Automotive cockpit module
KeY featUres • Excellent surface
• High adhesion strength
• Quality consistency
appliCations• Automotive door handle
• Radiator grille
• Rear garnish
High flow pC alloy
Metal plating pC alloy
® ®
pC/abs proDUCt line-Up for aUtoMotiVe
General
HP-1000X (High impact)
HP-1000XA (High flow)
High Heat resistant
LI-1000 (VST 140°C)
High Weld strength
HP-1011
HiGH perforManCe/HiGH Heat resistant
WP-1069 (VST 120°C)
WP-1089 (VST 130°C)
HiGH floW Metal platinG CHeMiCal resistant loW Gloss
WP-1041 (Good adhesion)
WP-1041G (Eching efficiency)
WP-1059 WP-1098 (UV resistant)
• Outside mirror
• Emblem
proDUCt
10 Samsung Cheil Industries
Sheet General
Properties Test Method Condition Unit PC00-SC-1060U00 PC00-SC-1080F00 PC00-SC-1100R00 PC00-SC-1100UR0
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm3 1.19 1.19 1.19 1.19
Water absorption ASTM D570 23°C % 0.2 0.2 0.2 0.2
Melt Flow Index
ASTM D1238300°C, 1.2kg g/10min 6 8 11.5 11.5
250°C, 1.2kg g/10min
ISO 1133300°C, 1.2kg g/10min 6 8 11.5 11.5
250°C, 1.2kg g/10min
Mold Shrinkage ASTM D955 % 0.5-0.7 0.5-0.7 0.5-0.7 0.5-0.7
MeChAniCAl ProPerties
Tensile Strength at YieldASTM D638 50mm/min kgf/cm2 660 640 640 640
ISO 527-1A 50mm/min Mpa 62 65 65 65
Tensile Strain at BreakASTM D638 50mm/min % 110 110 110 110
ISO 527-1A 50mm/min % 5.5 6 6 6
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 920 920 920 920
ISO 178 2mm/min Mpa 91 91 91 91
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 23,000 23,000 23,000 23,000
ISO 178 2mm/min Mpa 2,300 2,300 2,300 2,300
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 16 15 15 15
(notched) 1/8 kgf·cm/cm 90 88 87 87
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 80 80
Izod Impact Strength ISO 180 1A (notched) KJ/m2 90
Rockwell HardnessASTM D785 R-Scale 120 120 120 120
ISO 2039-2 R-Scale 120 120 120 120
therMAl ProPerties
Heat Deflection Temperature
ASTM D648 18.6kgf/cm2 °C 137 136 135 135
ISO 75-21.8MPa °C 127 127 125 125
0.45MPa °C 137 137 135 135
VICAT Softening Temperature ISO R306 B/50 °C 147 146 145 145
FlAMe ChArACteristiCs
Flammability UL94
HB mm
V-2 mm 0.8-2.5 0.8-2.5 0.8-2.5 0.8-2.5
V-1 mm
V-0 mm
5VA mm
5VB mm
transparent pC®
11INFINO® PC & PC Alloy
proDUCt seleCtion GUiDe
transparent pCGeneral Optical
Properties Test Method Condition Unit PC00-SC-1220R00 PC00-SC-1220UR0 PC00-SC-1280UR0 PC00-SC-1620P00
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.19 1.19 1.19 1.19
Water absorption ASTM D570 23°C % 0.2 0.2 0.2 0.2
Melt Flow Index
ASTM D1238300°C, 1.2kg g/10min 21.8 22.2 28
250°C, 1.2kg g/10min 10.5
ISO 1133300°C, 1.2kg g/10min 22 22 28
250°C, 1.2kg g/10min 10.5
Mold Shrinkage ASTM D955 % 0.5-0.7 0.5-0.7 0.5-0.7 0.5-0.7
MeChAniCAl ProPerties
Tensile Strength at YieldASTM D638 50mm/min kgf/cm2 640 640 640 640
ISO 527-1A 50mm/min Mpa 66 66 66 65
Tensile Strain at BreakASTM D638 50mm/min % 90 90 90 50
ISO 527-1A 50mm/min % 6.5 6.5 6.5 6
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 920 920 920 920
ISO 178 2mm/min Mpa 91 91 91 91
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 23,000 23,000 23,000 23,000
ISO 178 2mm/min Mpa 2,300 2,300 2,300 2,300
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 15 15 15
(notched) 1/8 kgf·cm/cm 75 75 50
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 15 15
Izod Impact Strength ISO 180 1A (notched) KJ/m2
Rockwell HardnessASTM D785 R-Scale 120 120 120 120
ISO 2039-2 R-Scale 121 124 120 119
therMAl ProPerties
Heat Deflection Temperature
ASTM D648 18.6kgf/cm2 °C 134 134 134 130
ISO 75-21.8MPa °C 123 123 123 120
0.45MPa °C 133 133 133 132
VICAT Softening Temperature ISO R306 B/50 °C 144 144 144 142
FlAMe ChArACteristiCs
Flammability UL94
HB mm
V-2 mm 0.8-3.2 0.8-3.2 0.8-3.2 0.8-3.2
V-1 mm
V-0 mm
5VA mm
5VB mm
12 Samsung Cheil Industries
proDUCt seleCtion GUiDe
®
Extrusion Blow Molding/ Injection
Properties Test Method Condition Unit FD-1010 FD-1112 FD-1122 FD-1510D
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm3 1.2 1.19 1.18 1.2
Melt Flow IndexASTM D1238 250°C, 10kg g/10min 16 14.6 35 12
250°C, 10kg g/10min 16 14.6 35 12
MeChAniCAl ProPerties
Tensile Strength at YieldASTM D638 50mm/min kgf/cm2 760 630 650 660
ISO 527-1A 50mm/min Mpa 62 68 61 61
Tensile Strain at BreakASTM D638 50mm/min % 130 100 106
ISO 527-1A 50mm/min % 100 113 112
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 840 930 950 960
ISO 178 2mm/min Mpa 87 90 91 88
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 21,000 21,000 23,000 22,000
ISO 178 2mm/min Mpa 2,100 2,100 2,200 2,100
Izod Impact Strength ASTM D256 (notched) 1/4 kgf·cm/cm 10 10 10
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 20 15 10 7
Izod Impact Strength ISO 180 1A (notched) KJ/m2 14 12 10
Rockwell HardnessASTM D785 R-Scale 120
ISO 2039-2 R-Scale 120 122 122
therMAl ProPerties
Heat Deflection Temperature
ASTM D648 18.56kgf/cm2 °C 133 130 122
ISO 75-2 1.8Mpa °C 125 125 122
ISO 75-2 0.45MPa °C 123
VICAT Softening Temperature ISO R306 B/50 °C 145 145 143
FlAMe ChArACteristiCs
Flammability UL94
HB mm
V-2 mm 1.5~2.0 0.8-3.0 0.8-3.0
V-1 mm
V-0 mm 3 1.2
5VA mm
5VB mm
Diffusion pC®
13INFINO® PC & PC Alloy
proDUCt seleCtion GUiDe
High Impact Eco-Friendly Reinforced Scratch Resistance
Properties Test Method Condition Unit QF-1035 CF-1050 CF-1011T CF-1051T GW-1030S GW-1043 CF-3104HF CF-3200HF CF-3300HF CF-3300LW IV-1071 PF-1035
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.17 1.18 1.18 1.18 1.18 1.18 1.25 1.33 1.4 1.4 1.18 1.16
Water absorption ASTM D570 % <0.1 0.3 0.3
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 19 22
300°C,1.2kg g/10min 23
250°C, 10kg g/10min 20 22 18 19 23 23 22 23 30 17
ISO 1133
220°C, 10kg g/10min 19
300°C, 1.2kg g/10min 23
250°C, 10kg g/10min 20 22 19 23 23 23 30 17
Mold Shrinkage ASTM D955 % 0.5-0.7 0.3~0.6 0.5-0.7 0.3-0.5 0.3-0.5
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 600 600 650 650 600 580 740 620
5mm/min kgf/cm2 600 1,000 1,180 1,300
ISO 527-1A50mm/min Mpa 58 57 59 65 57 118 57 63
5mm/min Mpa 60 100
Tensile Strain at BreakASTM D638 50mm/min % 100 112
ISO 527-1A 50mm/min % 93 114 98 59
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 880 900 850 900 850 780 950 1,400 1,570 1,700 1,050 820
ISO 178 2mm/min Mpa 84 84 98 92 82 95 170 167 100 88
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 22,000 20,000 22,000 22,000 20,500 20,000 30,000 56,000 63,940 75,000 23,500 21,500
ISO 178 2mm/min Mpa 2,100 2,100 2,490 2,110 2,000 3,000 6,000 7,500 2,500 2,200
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 50 61 6 43
(notched) 1/8 kgf·cm/cm 70 75 58 76 80 77 28 19 19 19 6 63
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 67 61 51 70 27 25 19 7 47
Izod Impact Strength ISO 180 1A (notched) KJ/m2 58 59 50 61 27 19 18 5 43
Rockwell HardnessASTM D785 R-Scale 117 120 120 120 118 118 116 116 123 118
ISO 2039-2 R-Scale 119 119 120 120 118 116 116 123 120
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 128 123 124 127 141 141 135 138 110
ISO 75-2 1.8MPa °C 122 121 119 108
VICAT Softening Temperature ISO R306 B/50 °C 144 143 136 137 140 140 137 137 130
FlAMe ChArACteristiCs
Flammability UL94
HB mm 0.8, 3.0 0.8, 1.5, 3.0
V-2 mm 0.8, 2.5, 3.0 0.8 0.8 0.8
V-1 mm 3.2 3.2 3.2
V-0 mm
5VA mm
5VB mm
High impact pC & pC alloy®
14 Samsung Cheil Industries
proDUCt seleCtion GUiDe
High Impact Eco-Friendly Reinforced Scratch Resistance
Properties Test Method Condition Unit QF-1035 CF-1050 CF-1011T CF-1051T GW-1030S GW-1043 CF-3104HF CF-3200HF CF-3300HF CF-3300LW IV-1071 PF-1035
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.17 1.18 1.18 1.18 1.18 1.18 1.25 1.33 1.4 1.4 1.18 1.16
Water absorption ASTM D570 % <0.1 0.3 0.3
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 19 22
300°C,1.2kg g/10min 23
250°C, 10kg g/10min 20 22 18 19 23 23 22 23 30 17
ISO 1133
220°C, 10kg g/10min 19
300°C, 1.2kg g/10min 23
250°C, 10kg g/10min 20 22 19 23 23 23 30 17
Mold Shrinkage ASTM D955 % 0.5-0.7 0.3~0.6 0.5-0.7 0.3-0.5 0.3-0.5
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 600 600 650 650 600 580 740 620
5mm/min kgf/cm2 600 1,000 1,180 1,300
ISO 527-1A50mm/min Mpa 58 57 59 65 57 118 57 63
5mm/min Mpa 60 100
Tensile Strain at BreakASTM D638 50mm/min % 100 112
ISO 527-1A 50mm/min % 93 114 98 59
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 880 900 850 900 850 780 950 1,400 1,570 1,700 1,050 820
ISO 178 2mm/min Mpa 84 84 98 92 82 95 170 167 100 88
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 22,000 20,000 22,000 22,000 20,500 20,000 30,000 56,000 63,940 75,000 23,500 21,500
ISO 178 2mm/min Mpa 2,100 2,100 2,490 2,110 2,000 3,000 6,000 7,500 2,500 2,200
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 50 61 6 43
(notched) 1/8 kgf·cm/cm 70 75 58 76 80 77 28 19 19 19 6 63
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 67 61 51 70 27 25 19 7 47
Izod Impact Strength ISO 180 1A (notched) KJ/m2 58 59 50 61 27 19 18 5 43
Rockwell HardnessASTM D785 R-Scale 117 120 120 120 118 118 116 116 123 118
ISO 2039-2 R-Scale 119 119 120 120 118 116 116 123 120
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 128 123 124 127 141 141 135 138 110
ISO 75-2 1.8MPa °C 122 121 119 108
VICAT Softening Temperature ISO R306 B/50 °C 144 143 136 137 140 140 137 137 130
FlAMe ChArACteristiCs
Flammability UL94
HB mm 0.8, 3.0 0.8, 1.5, 3.0
V-2 mm 0.8, 2.5, 3.0 0.8 0.8 0.8
V-1 mm 3.2 3.2 3.2
V-0 mm
5VA mm
5VB mm
High impact pC & pC alloy
15INFINO® PC & PC Alloy
proDUCt seleCtion GUiDe
Non-Reinforced Non-Reinforced Reinforced
Properties Test Method Condition Unit TN-1045M TN-1045S TN-1100 TN-1200 TH-1100 HN-1064IA UF-1017S LB-1010W LH-1070W HN-3102G NH-3204G NH-3208GL
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.21 1.21 1.23 1.22 1.2 1.18 1.2 1.26 1.42 1.27 1.32 1.34
Water Absorption ASTM D570 %
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 19 24
300°C, 1.2kg g/10min 41 34
250°C, 10kg g/10min 92 72 75 60 17 17 50 65 33 36
ISO 1133
220°C, 10kg g/10min 19 24
300°C, 1.2kg g/10min 41 34
250°C, 10kg g/10min 92 72 17 50 36
Mold Shrinkage ASTM D955 % 0.3-0.4 0.2-0.4
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 750 730 740 700 650 580 620 530 580
5mm/min kgf/cm2 860 900 1,070
ISO 527-1A50mm/min Mpa 73 72 55 61 55 109 120
5mm/min kgf/cm2
Tensile Strain at BreakASTM D638 50mm/min %
ISO 527-1A 50mm/min % 95 95 93 87 3
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,100 1,100 1,100 1,100 960 790 910 780 850 1,500 1,100 1,400
ISO 178 2mm/min Mpa 111 112 80 90 82 146 159
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 27,000 26,500 27,000 26,500 22,000 17,000 23,500 21,000 23,000 41,000 45,000 59,300
ISO 178 2mm/min Mpa 2,900 3,000 1,700 2,350 2,200 6,000 6,400
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 65
(notched) 1/8 kgf·cm/cm 2.5 3 4 4.5 >5 75 65 50 15 7 7.5 9
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 3.6 4 65 67 47 8 10
Izod Impact Strength ISO 180 1A (notched) KJ/m2 4.5 4.4 65 64 43 7 9
Rockwell HardnessASTM D785 R-Scale 124 123 123 122 119 117 119 120 90 91
ISO 2039-2 R-Scale 122 123 117 119 116 120
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 97 100 95 95 130 129 122 137 115 93
ISO 75-2 1.8MPa °C 89 92 93 117 93
VICAT Softening Temperature ISO R306 B/50 °C 105 110 106 108 144 143 109 139 136 100
FlAMe ChArACteristiCs
Flammability UL94
HB mm
V-2 mm 2.0, 3.0 2.0, 3.0 0.75 0.4 0.75
V-1 mm 2
V-0 mm 2.5 2 2 1.5, 3.0 0.7 1.5 1.5-1.6 2.5 0.75
5VA mm
5VB mm
flame retardant pC & pC alloy®
16 Samsung Cheil Industries
proDUCt seleCtion GUiDe
Non-Reinforced Non-Reinforced Reinforced
Properties Test Method Condition Unit TN-1045M TN-1045S TN-1100 TN-1200 TH-1100 HN-1064IA UF-1017S LB-1010W LH-1070W HN-3102G NH-3204G NH-3208GL
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.21 1.21 1.23 1.22 1.2 1.18 1.2 1.26 1.42 1.27 1.32 1.34
Water Absorption ASTM D570 %
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 19 24
300°C, 1.2kg g/10min 41 34
250°C, 10kg g/10min 92 72 75 60 17 17 50 65 33 36
ISO 1133
220°C, 10kg g/10min 19 24
300°C, 1.2kg g/10min 41 34
250°C, 10kg g/10min 92 72 17 50 36
Mold Shrinkage ASTM D955 % 0.3-0.4 0.2-0.4
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 750 730 740 700 650 580 620 530 580
5mm/min kgf/cm2 860 900 1,070
ISO 527-1A50mm/min Mpa 73 72 55 61 55 109 120
5mm/min kgf/cm2
Tensile Strain at BreakASTM D638 50mm/min %
ISO 527-1A 50mm/min % 95 95 93 87 3
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,100 1,100 1,100 1,100 960 790 910 780 850 1,500 1,100 1,400
ISO 178 2mm/min Mpa 111 112 80 90 82 146 159
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 27,000 26,500 27,000 26,500 22,000 17,000 23,500 21,000 23,000 41,000 45,000 59,300
ISO 178 2mm/min Mpa 2,900 3,000 1,700 2,350 2,200 6,000 6,400
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 65
(notched) 1/8 kgf·cm/cm 2.5 3 4 4.5 >5 75 65 50 15 7 7.5 9
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 3.6 4 65 67 47 8 10
Izod Impact Strength ISO 180 1A (notched) KJ/m2 4.5 4.4 65 64 43 7 9
Rockwell HardnessASTM D785 R-Scale 124 123 123 122 119 117 119 120 90 91
ISO 2039-2 R-Scale 122 123 117 119 116 120
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 97 100 95 95 130 129 122 137 115 93
ISO 75-2 1.8MPa °C 89 92 93 117 93
VICAT Softening Temperature ISO R306 B/50 °C 105 110 106 108 144 143 109 139 136 100
FlAMe ChArACteristiCs
Flammability UL94
HB mm
V-2 mm 2.0, 3.0 2.0, 3.0 0.75 0.4 0.75
V-1 mm 2
V-0 mm 2.5 2 2 1.5, 3.0 0.7 1.5 1.5-1.6 2.5 0.75
5VA mm
5VB mm
flame retardant pC & pC alloy
17INFINO® PC & PC Alloy
proDUCt seleCtion GUiDe
Reinforced Non-Halogen
Properties Test Method Condition Unit HF-3201GL NH-3402F HN-3104 NH-1017 NH-1015 NH-1027HF NE-1029 NE-1010 NE-1030 GC-1015 GC-1150 LX-1031 LX-1080
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.32 1.51 1.27 1.17 1.18 1.19 1.17 1.18 1.18 1.2 1.29 1.2 1.19
Water Absorption ASTM D570 % 0.15 0.15 0.2
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 55 24 55 35 48 53 25 31 30 48
300°C, 1.2kg g/10min
250°C, 10kg g/10min 11 33 10.8
ISO 1133
220°C, 10kg g/10min 55 24 55 35 48 53 25 31 48
300°C, 1.2kg g/10min
250°C, 10kg g/10min 11 10.8
Mold Shrinkage ASTM D955 % 0.1-0.3 0.1-0.3 0.5-0.7
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 580 630 610 630 650 640 620 650 630
5mm/min kgf/cm2 1,000 1,430 500 600
ISO 527-1A50mm/min Mpa 114 60 57 60 61 56 64 60 58 64 59
5mm/min kgf/cm2
Tensile Strain at BreakASTM D638 50mm/min % 8.8 102 25
ISO 527-1A 50mm/min % 4 8 10 51 39 55 4.3 35 96 14
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,700 1,800 850 830 880 900 850 960 890 900 950 830 870
ISO 178 2mm/min Mpa 168 98 85 88 92 90 92 90 90 93 88
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 56,000 110,000 36,000 24,000 24,500 24,000 24,000 28,000 25,000 25,000 41,000 25,000 24,000
ISO 178 2mm/min Mpa 5,800 3,300 2,500 2,500 2,600 1,500 2,600 2,500 2,500 3,922 2,400
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 19 17 16 36 11
(notched) 1/8 kgf·cm/cm 16 11 10 58 60 55 40 50 71 7 46 12
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 15 12 14 44 17 12 11 17 55 7 10
Izod Impact Strength ISO 180 1A (notched) KJ/m2 13 10 13 40 17 11 10.6 16 52 6 10
Rockwell HardnessASTM D785 R-Scale 91 122 116 118 115 116 116 118
ISO 2039-2 R-Scale 120 118 116 118 121 115 120 118 117 118
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 141 110 139 80 80 86 73 85
ISO 75-2 1.8MPa °C 142 137 75 81 82 78 80 77 81 81
VICAT Softening Temperature ISO R306 B/50 °C 151 148 91 98 98 91 96 93 98 96 91 98
FlAMe ChArACteristiCs
Flammability UL94
HB mm 1
V-2 mm 1.5 1.2,1.5, 3.0
V-1 mm 1.5 2 1 1 1.2
V-0 mm 1.5, 3.0, 6.0 2.5, 3.0 1.5 2.0, 3.0 1.5 1.2,1.5, 3.0 1.2-3.0 1.5 1.5, 3.0 1.5 1.2, 3.0 1.5-3.0
5VA mm 3 3 3
5VB mm 2.0, 30 2 1.5, 3.0 1.5 2
flame retardant pC & pC alloy®
18 Samsung Cheil Industries
proDUCt seleCtion GUiDe
Reinforced Non-Halogen
Properties Test Method Condition Unit HF-3201GL NH-3402F HN-3104 NH-1017 NH-1015 NH-1027HF NE-1029 NE-1010 NE-1030 GC-1015 GC-1150 LX-1031 LX-1080
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.32 1.51 1.27 1.17 1.18 1.19 1.17 1.18 1.18 1.2 1.29 1.2 1.19
Water Absorption ASTM D570 % 0.15 0.15 0.2
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 55 24 55 35 48 53 25 31 30 48
300°C, 1.2kg g/10min
250°C, 10kg g/10min 11 33 10.8
ISO 1133
220°C, 10kg g/10min 55 24 55 35 48 53 25 31 48
300°C, 1.2kg g/10min
250°C, 10kg g/10min 11 10.8
Mold Shrinkage ASTM D955 % 0.1-0.3 0.1-0.3 0.5-0.7
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 580 630 610 630 650 640 620 650 630
5mm/min kgf/cm2 1,000 1,430 500 600
ISO 527-1A50mm/min Mpa 114 60 57 60 61 56 64 60 58 64 59
5mm/min kgf/cm2
Tensile Strain at BreakASTM D638 50mm/min % 8.8 102 25
ISO 527-1A 50mm/min % 4 8 10 51 39 55 4.3 35 96 14
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,700 1,800 850 830 880 900 850 960 890 900 950 830 870
ISO 178 2mm/min Mpa 168 98 85 88 92 90 92 90 90 93 88
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 56,000 110,000 36,000 24,000 24,500 24,000 24,000 28,000 25,000 25,000 41,000 25,000 24,000
ISO 178 2mm/min Mpa 5,800 3,300 2,500 2,500 2,600 1,500 2,600 2,500 2,500 3,922 2,400
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 19 17 16 36 11
(notched) 1/8 kgf·cm/cm 16 11 10 58 60 55 40 50 71 7 46 12
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 15 12 14 44 17 12 11 17 55 7 10
Izod Impact Strength ISO 180 1A (notched) KJ/m2 13 10 13 40 17 11 10.6 16 52 6 10
Rockwell HardnessASTM D785 R-Scale 91 122 116 118 115 116 116 118
ISO 2039-2 R-Scale 120 118 116 118 121 115 120 118 117 118
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 141 110 139 80 80 86 73 85
ISO 75-2 1.8MPa °C 142 137 75 81 82 78 80 77 81 81
VICAT Softening Temperature ISO R306 B/50 °C 151 148 91 98 98 91 96 93 98 96 91 98
FlAMe ChArACteristiCs
Flammability UL94
HB mm 1
V-2 mm 1.5 1.2,1.5, 3.0
V-1 mm 1.5 2 1 1 1.2
V-0 mm 1.5, 3.0, 6.0 2.5, 3.0 1.5 2.0, 3.0 1.5 1.2,1.5, 3.0 1.2-3.0 1.5 1.5, 3.0 1.5 1.2, 3.0 1.5-3.0
5VA mm 3 3 3
5VB mm 2.0, 30 2 1.5, 3.0 1.5 2
flame retardant pC & pC alloy
19INFINO® PC & PC Alloy
proDUCt seleCtion GUiDe
High Modulus
Properties Test Method Condition Unit LS-1150G LS-1159 NH-1101 NH-1150HH
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm3 1.28 1.28 1.23 1.29
Water Absorption ASTM D570 %
Melt Flow Index
ASTM D1238
220°C, 10kg g/10min 27 30
300°C, 1.2kg g/10min
250°C, 10kg g/10min 24
ISO 1133
220°C, 10kg g/10min 27 30
300°C, 1.2kg g/10min
250°C, 10kg g/10min 24
Mold Shrinkage ASTM D955 % 0.12
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D63850mm/min kgf/cm2 630 600
5mm/min kgf/cm2 900 800
ISO 527-1A50mm/min Mpa 86 61 60
5mm/min kgf/cm2 80
Tensile Strain at BreakASTM D638 50mm/min % 7
ISO 527-1A 50mm/min % 3.6 29 7
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,400 1,200 950 900
ISO 178 2mm/min Mpa 135 110 93 90
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 46,000 48,000 34,000 38,000
ISO 178 2mm/min Mpa 4,400 5,000 3,400 3,400
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 8
(notched) 1/8 kgf·cm/cm 9 6 8 8
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 8 6 13 8
Izod Impact Strength ISO 180 1A (notched) KJ/m2 8 6 13 8
Rockwell HardnessASTM D785 R-Scale 114 110
ISO 2039-2 R-Scale 121 115
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 127 91 81 81
ISO 75-2 1.8MPa °C 120 81
VICAT Softening Temperature ISO R306 B/50 °C 128 95 94
FlAMe ChArACteristiCs
Flammability UL94
HB mm
V-2 mm 0.8-3.0
V-1 mm 1.5
V-0 mm 2.5 1.2 1.2
5VA mm
5VB mm
flame retardant pC & pC alloy®
20 Samsung Cheil Industries
proDUCt seleCtion GUiDe
High Heat Resistance High Flow
Properties Test Method Condition Unit HP-1000X HP-1000XA LI-1000 HP-1011 WP-1069 WP-1089
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.15 1.12 1.2 1.12 1.13 1.13
Melt Flow Index
ASTM D1238
250°C, 10kg g/10min 43 28 28 35 47 47
250°C, 2.16kg g/10min 6
260°C, 5kg g/10min 27
ISO 1133
250°C, 10kg g/10min 43 28 35 47
250°C, 2.16kg g/10min 6
260°C, 5kg g/10min 27
Mold Shrinkage ASTM D955 % 0.4~0.6 0.4-0.6 0.3~0.7 0.5~0.6
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D638 50mm/min kgf/cm2 570 550 600 530 580 540
ISO 527-1A50mm/min Mpa 54 50 50 53 52
5mm/min kgf/cm2
Tensile Strain at BreakASTM D638 50mm/min % 110 100 80 80
ISO 527-1A 50mm/min % 108 100 92 50 60
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 810 750 800 750 800 770
ISO 178 2mm/min Mpa 77 80 74 78 80
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 22,000 20,500 2,000 20,000 22,500 21,500
ISO 178 2mm/min Mpa 2,000 2,100 2,000 2,120 2,200
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 58 45 45 43
(notched) 1/8 kgf·cm/cm 80 60 66 58 60
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 60 45 49 45 51
Izod Impact Strength ISO 180 1A (notched) KJ/m2 50 45 46 41 46
Rockwell HardnessASTM D785 R-Scale 115 113 110 108
ISO 2039-2 R-Scale 116 112 110 113 110
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 109 110 111 110
ISO 75-2 1.8MPa °C 107 102 99 101 104
VICAT Softening Temperature ISO R306 B/50 °C 129 123 144 121 122 120
pC/abs for automotive®flame retardant pC & pC alloy
21INFINO® PC & PC Alloy
proDUCt seleCtion GUiDe
Metal Plating Chemical Resistant Low Gloss
Properties Test Method Condition Unit WP-1041 WP-1041G WP-1059 WP-1098
PhysiCAl ProPerties
Specific Gravity ASTM D792 g/cm2 1.09 1.05 1.12 1.13
Melt Flow Index
ASTM D1238
250°C, 10kg g/10min 35 31 45 32
250°C, 2.16kg g/10min 4 3
260°C, 5kg g/10min
ISO 1133
250°C, 10kg g/10min 35 31 45 32
250°C, 2.16kg g/10min 4 3
260°C, 5kg g/10min
Mold Shrinkage ASTM D955 % 0.5~0.6 0.5~0.6
MeChAniCAl ProPerties
Tensile Strength at Yield
ASTM D638 50mm/min kgf/cm2 490 500 540 520
ISO 527-1A50mm/min Mpa 47 47 52
5mm/min kgf/cm2 54
Tensile Strain at BreakASTM D638 50mm/min % 25 100
ISO 527-1A 50mm/min % 22 73 62
Flexural StrengthASTM D790 2.8mm/min kgf/cm2 670 670 750 700
ISO 178 2mm/min Mpa 73 70 75 76
Flexural ModulusASTM D790 2.8mm/min kgf/cm2 19,000 19,500 21,000 20,000
ISO 178 2mm/min Mpa 2,000 2,000 2,250 2,200
Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 40 42
(notched) 1/8 kgf·cm/cm 55 55 48 62
Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 47 47 45 49
Izod Impact Strength ISO 180 1A (notched) KJ/m2 44 45 45 48
Rockwell HardnessASTM D785 R-Scale 103 105 112 114
ISO 2039-2 R-Scale 103 107 112 114
therMAl ProPerties
Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 99 100 105 105
ISO 75-2 1.8MPa °C 93 93 100
VICAT Softening Temperature ISO R306 B/50 °C 110 111 124
pC/abs for automotive®
22 Samsung Cheil Industries
proDUCt seleCtion GUiDe
appliCations
tV/Monitor
1. front Cover
MABS BF-0950
ABS HG-0760TV, SD-0150
FR PC/ABS NH-1017D, NE-1030, NH-1017SG
TR ABS TX-0510T
Double injection
FR PC TN-1045
FR PC/ABS NE-1010
MABS TF-0930, SF-0505HW, BF-0950
2. back light frame
PC/ABS/GF LS-1150G
FR PC LH-1070W
3. Middle Cover
PC/ABS/GF 15% LS-1159
4. rear Cover
mPPE NH-1904
FR PS VE-1801, VE-1805
5. Guide stand neck
PC/GF 20% HF-3200 H
FR PC/GF 20% HF-3202H
6. stand base
MABS BF-0950
ABS HG-0760TV, SD-0150
FR PC/ABS NH-1017D, NH-1017SG
Metal plating ABS MP-0670
Metal plating PC/ABS QP-1010
➊
➎
➏
➋
➌
23INFINO® PC & PC Alloy
note pC
appliCations
1. front bezel
FR PC/PMMA NF-3017 (Scratch resistant)
FR PC/ABS NH-1021 (High gloss)
2. rear Cover base
FR PC/ABS NH-1015, GC-1015
FR PC/ABS Talc 10% NH-1101
FR PC/ABS Talc 15% NH-1150HH
FR PC/GF NH-3280GL
FR PPA/GF MX-4500G
3. antenna Cover palm rest
FR PC/ABS NH-1015, GC-1015
FR PC/ABS Talc 10% NH-1101
FR PC/ABS Talc 15% NH-1150HH
FR PC/GF NH-3280GL
FR PPA/GF MX-4500G
4. battery pack
FR PC UF-1017S
5. Keyboard frame
FR PC/ABS NH-1021
ABS HG-0760TV
➊
➎
➋
➋
➌
24 Samsung Cheil Industries
Mobile phone
appliCations
1. Keypad
PC/PMMA IV-1071
ABS SF-0941
2. front Cover
PC CF-1050
PC CF-1070
PC CF-1030
3. battery
FR PC UF-1017S
4. rear Cover
PC CF-1050
PC/GF CF-3104HF
PC/GF CF-3200HF
PC/GF CF-3300HF
PC/GF CF-3300LW
PPA/GF CF-4150
PA/GF MKD-1016
5. battery Cover
PC CF-1050
PC CF-1070
PC CF-1051T
PC CF-1011T
PC/GF CF-3104HF
PC/ABS ST-1009
PC/ABS HI-1001BN
PC/ABS HP-1011
➊
➎
➋
➌
25INFINO® PC & PC Alloy
smart Meter
appliCations
1. Meter Cover
PC (V2) SC-1220UR
2. terminal block
FR PC/GF 10% HN-3104
3. Cover Meter
FR PC/GF 10% HN-3104
4. base Meter/base frame
FR PC/GF 10% HN-3104
5. Meter Cover
PC (V2) SC-1220UR
6. Meter body
PC(V2) SA-1100
PC(V2) SA-1220
7. terminal block
FR PC/GF 10% HN-3104
(IEC) Smart Meter
(ANSI) Smart Meter
(ieC) smart Meter
(ansi) smart Meter
➎
➏
➐
➊
➋
➌
26 Samsung Cheil Industries
automotive
appliCations
1. interior
Power Window Switch Cover: Heat Resistance ABS
Air Vent: PC/PBT, PC/ABS
Center Fascia: PC, PC/ABS
Overhead Console: PC/ASA
Console: Heat Resistance ABS
2. UtH
Junction Box: mPPE
HEV Battery Housing: PA/GF
Eco Wire : PPE/Elastomer
3. lighting
Head Lamp Bezel: PBT/PET
Rear Lamp Housing: PC/ABS
4. exterior
Tailgate Garnish: PC/ABS, MP ABS
Rear Spoiler: Blow Molding ABS
Wheel Cover: MP PC/ABS, PC/ABS
Outside Door Handle: MP PC/ABS
Side Mirror: ASA, PBT/PET/GF
Radiator Grill: MP ABS, ASA
5. structure
Panorama Sunroof Frame: PBT/ASA/GF
Fuel Filler Door: PA/PPE/CNT
Fender: PA/PPE/CNT
➊
➊ ➎
➎
➋
➌
➌
27INFINO® PC & PC Alloy
Development support
• Color development
• CAE analysis support
Quality support
• Field evaluation
• Technical solution
total solution platform
inteGrateD soltions
total solUtion proViDer
inteGrateDsolUtions
Material Solution
Global Supply Chain
Solution
Design Solution
Technical Solution
Broad product line-up
Speedy development
Cost reduction
Global production & supply system
Exclusive color development
Advanced technology
CAE support
Global tech support
Enhancing productivity
Global quality control
Development support
• CTQ analysis
• Material selection with optimal properties
Product support
• Mold design technical support
Consulting mass production schedule
• Productivity improvement
Market Research
Product Planning
DesignReliability
Test
Concept Establishment
Mold Manufacturing Pilot Injection
Mass Production
Sales
28 Samsung Cheil Industries
Global network
HeaDQUarters
Global sUbsiDiarY
Samsung Cheil Industries Inc.332-2 Gocheon-dong Uiwang-si Gyeonggi-do, 437-711, Korea Tel: +82-31-596-3408 Fax: +82-31-596-3490 E-mail: [email protected]
Los Angeles, USA Samsung Chemical Inc.
Tel: +1-562-229-1307 E-mail: [email protected]
Frankfurt, Germany Samsung Chemical Europe GmbH
Tel: +49-6196-66-7490
E-mail: [email protected]
Shanghai, China Samsung Chemical Material Trading (Shanghai) Co., Ltd.
Tel: +86-21-6270-3000(325)
E-mail: [email protected]
Bangkok, Thailand Samsung Chemical Thailand
Tel: +66-2-624-6715
E-mail: [email protected]
Tokyo, Japan Samsung Chemical Inc.
Tel: +81-3-6234-2197
E-mail: [email protected]
sales / serViCe offiCe
plant
asiaShenzhen, ChinaTel: +86-755-8203-2323 E-mail: [email protected]
Tianjin, ChinaTel: +86-22-2836-4261 E-mail: [email protected]
Nagoya, JapanTel: +81-52-569-1807 E-mail: [email protected]
Osaka, JapanTel: +81-6-6949-3162 E-mail: [email protected]
Kuala Lumpur, MalaysiaTel: +60-3-2174-4534, 4570 E-mail: [email protected]
Chennai, IndiaTel: +91-98401-04251 E-mail: [email protected]
Delhi, IndiaTel: +91-81302-19193 E-mail: [email protected]
Dubai, U.A.ETel: +971-4-447-3411 E-mail: [email protected]
europeBratislava, SlovakiaTel: +421-90-170-2001 E-mail: [email protected]
Istanbul, TurkeyTel: +90-541-231-0314 E-mail: [email protected]
Milano, ItalyTel: +39-2-83111840 E-mail: [email protected]
americaChicago, U.S.A.Tel: +1-847-407-2845 E-mail: [email protected]
San Diego, U.S.A.Tel: +1-619-278-0961 E-mail: [email protected]
Detroit, U.S.A.Tel: +1-248-276-8484 E-mail: [email protected]
Yeosu, Republic of KoreaTel: +82-61-689-1221 E-mail: [email protected]
Tianjin, ChinaTel: +86-22-5868-0291 E-mai: [email protected]
Kornye, HungaryTel: +36-34-814-120 E-mail: [email protected]
Tijuana, MexicoTel: +52-664-627-4947 E-mail: [email protected]
HeaDQUarters
Global sUbsiDiarY
sales offiCe
plant
MexicoTijuana
USALos AngelesChicagoSan DiegoDetroit
GermanyFrankfurt
TurkeyIstanbul
SOUTH KOREAUiwangYeosuGumiBusanGwangju
SlovakiaBratislava
HungaryKornye
IndiaChennaiDelhi
EgyptCairo
ItalyMilano
ThailandBangkok
U.A.EDubai
JapanTokyoNagoyaOsaka
MalaysiaKuala Lumpur
ChinaSanghaiTianjinShenzhen
29INFINO® PC & PC Alloy
samsung Cheil industries - Chemical
30 Samsung Cheil Industries
note The information contained herein is provided by Samsung Cheil Industries, Inc. and its subsidiaries and affiliates (collectively referred to as “SAMSUNG”) for information purposes only and should be used by individuals with technical experience and knowledge in the area. Samsung Cheil Industries does not make any representation or warranties of the usefulness or expected result of the information, and does not assume any responsibility whatsoever related to the use of the information. SCI-M-042013
We provide value to turn your imagination into reality with our innovative materials and optimal solutions.
Value+ your imagination
www.samsungchemical.com