PC & PC Alloy

Contents

INFINO® PC & PC Alloy Overview 03

Eco-Friendly INFINO® PC 04

Product Portfolio 05

Product 06

Product Selection Guide 11

Applications 23

Total Solution Platform 28

Global Network 29

INFINO® Polycarbonate (PC) is named for polycarbonate, a non-toxic transparent engineering plastic resin that comes with the high level of impact strength compared with commodity plastics by Samsung Cheil Industries Chemical division. INFINO® PC is equipped with good mechanical strength, cold and heat resistance, stable optical characteristic and balanced electrical property.

INFINO® PC Alloy named for the product line of amorphous, thermoplastic polymer compounding based on polycarbonate (PC) and acrylonitrile butadiene styrene copolymer (ABS), PC and Polyethyleneterephthalate (PET) or PC and polybutyleneterephthalate (PBT) by Samsung Cheil Industries Chemical division. INFINO® PC alloy provides valuable benefits with combination of mechanical, thermal and physical Properties. PC alloy are widely used in a broad range of industries, including automotive, electric and electronics, display, mobile devices, lighting, building & construction, optical lenses and other appliances.

03INFINO® PC & PC Alloy

eco-friendly ® pC

® pC non-pHosGene proDUCtion teCHnoloGY

INFINO® PC is produced with the environmentally friendly and clean technology that made it possible to get neither phosgene nor chlorine involved in any part of its production process.

® pCM baseD pC & pC alloY

INFINO® PCM-based PC and PC Alloy are based on Samsung Cheil Industries’ unique compounding technology that uses recycled PC without compromising the standard PC’s balanced set of properties including excellent mechanical strength, heat resistance and dimensional stability. These material lineups are designed to better help comply with the environment regulations such as EPEAT in the United States helping reduce the emissions of CO2.

non-paintinG solUtion lUMinoUs

Luminous is a premium-class eco-friendly painting alternative material that enables manufacturing of plastic parts without painting.

Key Advantages of Luminous:

• Flow mark and weld line improvement

• Eco-friendly process with efficiency

• Superior appearance: bright, high gloss, metal like resin

lUMinoUspaintinG proCess

Injection

Non-Painting Resin

Primer CoatingInjection

Spray gun

Base Coating Clear Coating

04 Samsung Cheil Industries

product portfolio

General

Optical

Sheet

General

High Impact

Eco-Friendly

High Impact

FR

High Impact

High Modulus

Anti-Scratch

General

High Heat Resistant

Low Gloss

General

High Flow

High Heat Resistance

General

High Heat Resistant

High Weld Strength

High Flow

Chemical Resistant

General

Transparent

Non-Halogen

High Heat Resistant

General

Adhesion

High Impact

Super FR

High Heat Resistant

General

Chemical Resistant

General

High Flow

Polymerization General PC/ABS/GF

PC/PET

PC/PMMA

PC/ASA

Transparent High Performance/ Heat Resistant

Low Gloss

Eco-Friendly

Anti-Static

General

General FR

Metal Plating

Advanced Physical Property

High Impact

Luminous

Lubricant

Eco-Friendly

High Flow

High Heat Resistant

Eco-Friendly

Extrusion

Blow Molding

Super FR

Insulation Film

Light Diffusion

High Reflectivity

High Impact/Flow

High Gloss/High Flow

High Modulus

Scratch Resistance

Metal Plating

Eco-Friendly

Luminous

Extrusion

pC (General)

pC (fr)

pC/abs (General)

pC/abs (fr) pC/Gf pC alloy

pC & pC alloy


INFINO® Transparent PC resin features its outstanding optical clarity. Thanks to its superior flowability and thermal stability, INFINO® PC resin stays completely transparent without discoloration at elevated temperatures. Samsung Cheil Industries’ unique manufacturing technology to remove the low molecular weight oligomers made it possible to minimize the mold deposits during injection process. This advantage makes INFINO® Transparent PC most suitable for a wide variety of applications from small to large sized goods with complex design.

KeY featUres • Excellent optical characteristic: High transmittance,

UV resistant

• High impact strength

• Lightweight solution

• Good processability: Low molding temperature and short cycle time

appliCations

• Lighting: Automotive headlamp, Lighting lens • Light guide plate: Mobile display• Building & Construction: Roofing, Wall sheet extrusion • Data storage: CDs, DVDs • Optical lenses, Eyewear• Furniture

proDUCt line-Up

sHeet

PC00-SC-1060U00

PC00-SC-1080F00

General

PC00-SC-1100R00

PC00-SC-1100UR0

PC00-SC-1220R00

PC00-SC-1220UR0

PC00-SC-1280UR0 (Lighting)

optiCal

PC00-FX-8500L (LGP)

transparent pC®


proDUCt

INFINO® Light Diffusion PC is a noble blend of Samsung Cheil Industries’ high quality PC and light diffuser. A wide range of light diffusion PC lineups are available for both injection molding and extrusion. A variety of colors based on the diffusion and transparency levels are also available.

KeY featUres• Superior optical properties: High transparency

and high degree of diffusion

• Eco-friendly non-halogen flame retardant systme

• High productivity

• Excellent injection molding process: Minimize gate marks

• Outstanding durability

appliCations• LED/Conventional lighting lens cover

proDUCt line-Up

extrUsion

FD-1010 (3.0T V0)

FD-1112 (0.8T V2)

FD-1510D (1.2T V0)

bloW MolDinG/inJeCtion

FD-1122 (0.8T V2)

Diffusion pC®


proDUCt

High impact pC & pC alloyINFINO® High Impact PC and PC Alloy, which come with not only good mechanical strength but also excellent chemical resistance, are widely used in small electrical and electronic devices such as digital cameras and mobile handsets.

KeY featUres• Good processability

• Impact strength

• Heat resistant

• Good appearance

appliCations• Mobile devices

• Digital camera

proDUCt line-Up

®

proDUCt

reinforCeD

CF-3104HF (GF 10%)

CF-3200HF (GF 20%)

CF-3300HF (GF 30%)

CF-3300LW (GF 30%, Low Warpage)

sCratCH resistant

IV-1071 (F, High Gloss)

PF-1035 (HB, High Impact)

HiGH iMpaCt

General

QF-1035

Chemical resistant

CF-1050

transparent

CF-1011T

CF-1051T

eCo-frienDlY

GW-1030S (PCM 70%)

GW-1043 (PCM 80%)


reinforCeD

General GF 10%

HN-3102G (1.5T V0)

GF 20%

NH-3204G (2.0T V0, High flow)

NH-3208GL (0.75T V0)

HF-3201GL (1.5T V0)

GF 40%

NH-3402F (2.0T V1)

High Heat resistant GF 10%

HN-3104 (1.5T V0/3.0mm 5VB, F1)

flame retardant pC & pC alloyINFINO® Flame Retardant PC and PC Alloy have been developed so that they can provide the most suitable solutions to the safety and the environment regulations at the same time. High Impact Flame Retardant PC & PC/ABS are applicable to laptop computers and smart meters thanks to its well-balanced mechanical properties and processability.

KeY featUres• High flowability, High gloss, High modulus

• High impact

• Non-halogen flame retardant

• Good colorability

• Excellent appearance

appliCations• TV

• Battery

• Charger

• Note PC

• OA machine

• Smart meter

Transparent

High Flow

TN-1045M/S (2.0T V2)

TN-1100 (2.5T V0)

TN-1200 (2.0T V0)

High Heat Resistant

TH-1100 (VST 144°C, 2.0T V0)

High Heat Resistant

HN-1064IA (1.5T V0, RTI 130°C)

High Flow

UF-1017S (0.8T V0)

Back Light Unit

LB-1010W (0.75T V2, WH)

LH-1070W (1.5T V0, WH)

LB-1090HK (1.5T V0, BK)

Gf LS-1150G

(0.8T V2)

LS-1159 (High flow)

talc Talc 8%

NH-1101 (1.2T V0)

Talc 15%

NH-1150HH (1.2T V0)

fr pC proDUCt line-Up fr pC/abs proDUCt line-Up

®

proDUCt

non-reinforCeD HiGH MoDUlUsnon-HaloGen

General NH-1017 (2.0T V0/5VB)

High impact NH-1015 (1.5T V0) superior flame retardant NH-1027HF (1.2T V0/1.5T 5VB)

NE-1029 (1.2T V0/1.5T 5VB, Thin wall)

High Gloss/High flow

NE-1010 (1.5T V0)

NE-1030 (1.5T V0, High flow)

eco-friendly GC-1015 (1.5T V0, PCM 30%)

GC-1150 (1.5T V0, Talc 15%, PCM 30%)

luminous

LX-1031 (1.5T V0, High impact, Sparkle)

LX-1080 (1.2T V1, Metallic-look)


High Flow PC Alloy, generally used for automotive interior parts, has excellent processability together with other well-balanced properties such as good paintability and high impact strength.

INFINO® Metal Plating PC Alloy features its outstanding adhesion strength and superior appearance thanks to the cutting-edge technology from Samsung Cheil Industries. It is widely used for the automotive exterior parts by global automotive OEMs.

KeY featUres• High flow

• Good paintability

• Chemical resistance

• Impact strength

• Low TVOC

appliCations• Automotive cockpit module

KeY featUres • Excellent surface

• High adhesion strength

• Quality consistency

appliCations• Automotive door handle

• Radiator grille

• Rear garnish

High flow pC alloy

Metal plating pC alloy

® ®

pC/abs proDUCt line-Up for aUtoMotiVe

General

HP-1000X (High impact)

HP-1000XA (High flow)

High Heat resistant

LI-1000 (VST 140°C)

High Weld strength

HP-1011

HiGH perforManCe/HiGH Heat resistant

WP-1069 (VST 120°C)

WP-1089 (VST 130°C)

HiGH floW Metal platinG CHeMiCal resistant loW Gloss

WP-1041 (Good adhesion)

WP-1041G (Eching efficiency)

WP-1059 WP-1098 (UV resistant)

• Outside mirror

• Emblem

proDUCt


Sheet General

Properties Test Method Condition Unit PC00-SC-1060U00 PC00-SC-1080F00 PC00-SC-1100R00 PC00-SC-1100UR0

PhysiCAl ProPerties

Specific Gravity ASTM D792 g/cm3 1.19 1.19 1.19 1.19

Water absorption ASTM D570 23°C % 0.2 0.2 0.2 0.2

Melt Flow Index

ASTM D1238300°C, 1.2kg g/10min 6 8 11.5 11.5

250°C, 1.2kg g/10min

ISO 1133300°C, 1.2kg g/10min 6 8 11.5 11.5

250°C, 1.2kg g/10min

Mold Shrinkage ASTM D955 % 0.5-0.7 0.5-0.7 0.5-0.7 0.5-0.7

MeChAniCAl ProPerties

Tensile Strength at YieldASTM D638 50mm/min kgf/cm2 660 640 640 640

ISO 527-1A 50mm/min Mpa 62 65 65 65

Tensile Strain at BreakASTM D638 50mm/min % 110 110 110 110

ISO 527-1A 50mm/min % 5.5 6 6 6

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 920 920 920 920

ISO 178 2mm/min Mpa 91 91 91 91

Flexural ModulusASTM D790 2.8mm/min kgf/cm2 23,000 23,000 23,000 23,000

ISO 178 2mm/min Mpa 2,300 2,300 2,300 2,300

Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 16 15 15 15

(notched) 1/8 kgf·cm/cm 90 88 87 87

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 80 80

Izod Impact Strength ISO 180 1A (notched) KJ/m2 90

Rockwell HardnessASTM D785 R-Scale 120 120 120 120

ISO 2039-2 R-Scale 120 120 120 120

therMAl ProPerties

Heat Deflection Temperature

ASTM D648 18.6kgf/cm2 °C 137 136 135 135

ISO 75-21.8MPa °C 127 127 125 125

0.45MPa °C 137 137 135 135

VICAT Softening Temperature ISO R306 B/50 °C 147 146 145 145

FlAMe ChArACteristiCs

Flammability UL94

HB mm

V-2 mm 0.8-2.5 0.8-2.5 0.8-2.5 0.8-2.5

V-1 mm

V-0 mm

5VA mm

5VB mm

transparent pC®


proDUCt seleCtion GUiDe

transparent pCGeneral Optical

Properties Test Method Condition Unit PC00-SC-1220R00 PC00-SC-1220UR0 PC00-SC-1280UR0 PC00-SC-1620P00

PhysiCAl ProPerties


Water absorption ASTM D570 23°C % 0.2 0.2 0.2 0.2

Melt Flow Index

ASTM D1238300°C, 1.2kg g/10min 21.8 22.2 28

250°C, 1.2kg g/10min 10.5

ISO 1133300°C, 1.2kg g/10min 22 22 28

250°C, 1.2kg g/10min 10.5

Mold Shrinkage ASTM D955 % 0.5-0.7 0.5-0.7 0.5-0.7 0.5-0.7



ISO 527-1A 50mm/min Mpa 66 66 66 65


ISO 527-1A 50mm/min % 6.5 6.5 6.5 6


ISO 178 2mm/min Mpa 91 91 91 91


ISO 178 2mm/min Mpa 2,300 2,300 2,300 2,300

Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 15 15 15

(notched) 1/8 kgf·cm/cm 75 75 50

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 15 15

Izod Impact Strength ISO 180 1A (notched) KJ/m2


ISO 2039-2 R-Scale 121 124 120 119

therMAl ProPerties


ASTM D648 18.6kgf/cm2 °C 134 134 134 130

ISO 75-21.8MPa °C 123 123 123 120

0.45MPa °C 133 133 133 132

VICAT Softening Temperature ISO R306 B/50 °C 144 144 144 142


Flammability UL94

HB mm

V-2 mm 0.8-3.2 0.8-3.2 0.8-3.2 0.8-3.2

V-1 mm

V-0 mm

5VA mm

5VB mm



®

Extrusion Blow Molding/ Injection

Properties Test Method Condition Unit FD-1010 FD-1112 FD-1122 FD-1510D

PhysiCAl ProPerties


Melt Flow IndexASTM D1238 250°C, 10kg g/10min 16 14.6 35 12

250°C, 10kg g/10min 16 14.6 35 12



ISO 527-1A 50mm/min Mpa 62 68 61 61

Tensile Strain at BreakASTM D638 50mm/min % 130 100 106

ISO 527-1A 50mm/min % 100 113 112


ISO 178 2mm/min Mpa 87 90 91 88


ISO 178 2mm/min Mpa 2,100 2,100 2,200 2,100

Izod Impact Strength ASTM D256 (notched) 1/4 kgf·cm/cm 10 10 10

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 20 15 10 7

Izod Impact Strength ISO 180 1A (notched) KJ/m2 14 12 10

Rockwell HardnessASTM D785 R-Scale 120

ISO 2039-2 R-Scale 120 122 122

therMAl ProPerties


ASTM D648 18.56kgf/cm2 °C 133 130 122

ISO 75-2 1.8Mpa °C 125 125 122

ISO 75-2 0.45MPa °C 123

VICAT Softening Temperature ISO R306 B/50 °C 145 145 143


Flammability UL94

HB mm

V-2 mm 1.5~2.0 0.8-3.0 0.8-3.0

V-1 mm

V-0 mm 3 1.2

5VA mm

5VB mm

Diffusion pC®



High Impact Eco-Friendly Reinforced Scratch Resistance

Properties Test Method Condition Unit QF-1035 CF-1050 CF-1011T CF-1051T GW-1030S GW-1043 CF-3104HF CF-3200HF CF-3300HF CF-3300LW IV-1071 PF-1035

PhysiCAl ProPerties

Specific Gravity ASTM D792 g/cm2 1.17 1.18 1.18 1.18 1.18 1.18 1.25 1.33 1.4 1.4 1.18 1.16

Water absorption ASTM D570 % <0.1 0.3 0.3

Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 19 22

300°C,1.2kg g/10min 23

250°C, 10kg g/10min 20 22 18 19 23 23 22 23 30 17

ISO 1133

220°C, 10kg g/10min 19

300°C, 1.2kg g/10min 23

250°C, 10kg g/10min 20 22 19 23 23 23 30 17

Mold Shrinkage ASTM D955 % 0.5-0.7 0.3~0.6 0.5-0.7 0.3-0.5 0.3-0.5


Tensile Strength at Yield

ASTM D63850mm/min kgf/cm2 600 600 650 650 600 580 740 620

5mm/min kgf/cm2 600 1,000 1,180 1,300

ISO 527-1A50mm/min Mpa 58 57 59 65 57 118 57 63

5mm/min Mpa 60 100

Tensile Strain at BreakASTM D638 50mm/min % 100 112

ISO 527-1A 50mm/min % 93 114 98 59

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 880 900 850 900 850 780 950 1,400 1,570 1,700 1,050 820

ISO 178 2mm/min Mpa 84 84 98 92 82 95 170 167 100 88

Flexural ModulusASTM D790 2.8mm/min kgf/cm2 22,000 20,000 22,000 22,000 20,500 20,000 30,000 56,000 63,940 75,000 23,500 21,500

ISO 178 2mm/min Mpa 2,100 2,100 2,490 2,110 2,000 3,000 6,000 7,500 2,500 2,200


(notched) 1/8 kgf·cm/cm 70 75 58 76 80 77 28 19 19 19 6 63

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 67 61 51 70 27 25 19 7 47

Izod Impact Strength ISO 180 1A (notched) KJ/m2 58 59 50 61 27 19 18 5 43

Rockwell HardnessASTM D785 R-Scale 117 120 120 120 118 118 116 116 123 118

ISO 2039-2 R-Scale 119 119 120 120 118 116 116 123 120

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 128 123 124 127 141 141 135 138 110

ISO 75-2 1.8MPa °C 122 121 119 108

VICAT Softening Temperature ISO R306 B/50 °C 144 143 136 137 140 140 137 137 130


Flammability UL94

HB mm 0.8, 3.0 0.8, 1.5, 3.0

V-2 mm 0.8, 2.5, 3.0 0.8 0.8 0.8

V-1 mm 3.2 3.2 3.2

V-0 mm

5VA mm

5VB mm

High impact pC & pC alloy®



High Impact Eco-Friendly Reinforced Scratch Resistance

Properties Test Method Condition Unit QF-1035 CF-1050 CF-1011T CF-1051T GW-1030S GW-1043 CF-3104HF CF-3200HF CF-3300HF CF-3300LW IV-1071 PF-1035

PhysiCAl ProPerties


Water absorption ASTM D570 % <0.1 0.3 0.3

Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 19 22

300°C,1.2kg g/10min 23

250°C, 10kg g/10min 20 22 18 19 23 23 22 23 30 17

ISO 1133

220°C, 10kg g/10min 19

300°C, 1.2kg g/10min 23

250°C, 10kg g/10min 20 22 19 23 23 23 30 17

Mold Shrinkage ASTM D955 % 0.5-0.7 0.3~0.6 0.5-0.7 0.3-0.5 0.3-0.5



ASTM D63850mm/min kgf/cm2 600 600 650 650 600 580 740 620

5mm/min kgf/cm2 600 1,000 1,180 1,300

ISO 527-1A50mm/min Mpa 58 57 59 65 57 118 57 63

5mm/min Mpa 60 100


ISO 527-1A 50mm/min % 93 114 98 59

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 880 900 850 900 850 780 950 1,400 1,570 1,700 1,050 820

ISO 178 2mm/min Mpa 84 84 98 92 82 95 170 167 100 88


ISO 178 2mm/min Mpa 2,100 2,100 2,490 2,110 2,000 3,000 6,000 7,500 2,500 2,200


(notched) 1/8 kgf·cm/cm 70 75 58 76 80 77 28 19 19 19 6 63

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 67 61 51 70 27 25 19 7 47

Izod Impact Strength ISO 180 1A (notched) KJ/m2 58 59 50 61 27 19 18 5 43


ISO 2039-2 R-Scale 119 119 120 120 118 116 116 123 120

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 128 123 124 127 141 141 135 138 110

ISO 75-2 1.8MPa °C 122 121 119 108

VICAT Softening Temperature ISO R306 B/50 °C 144 143 136 137 140 140 137 137 130


Flammability UL94

HB mm 0.8, 3.0 0.8, 1.5, 3.0

V-2 mm 0.8, 2.5, 3.0 0.8 0.8 0.8

V-1 mm 3.2 3.2 3.2

V-0 mm

5VA mm

5VB mm

High impact pC & pC alloy



Non-Reinforced Non-Reinforced Reinforced

Properties Test Method Condition Unit TN-1045M TN-1045S TN-1100 TN-1200 TH-1100 HN-1064IA UF-1017S LB-1010W LH-1070W HN-3102G NH-3204G NH-3208GL

PhysiCAl ProPerties


Water Absorption ASTM D570 %

Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 19 24

300°C, 1.2kg g/10min 41 34

250°C, 10kg g/10min 92 72 75 60 17 17 50 65 33 36

ISO 1133

220°C, 10kg g/10min 19 24

300°C, 1.2kg g/10min 41 34

250°C, 10kg g/10min 92 72 17 50 36

Mold Shrinkage ASTM D955 % 0.3-0.4 0.2-0.4



ASTM D63850mm/min kgf/cm2 750 730 740 700 650 580 620 530 580

5mm/min kgf/cm2 860 900 1,070

ISO 527-1A50mm/min Mpa 73 72 55 61 55 109 120

5mm/min kgf/cm2

Tensile Strain at BreakASTM D638 50mm/min %

ISO 527-1A 50mm/min % 95 95 93 87 3

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,100 1,100 1,100 1,100 960 790 910 780 850 1,500 1,100 1,400

ISO 178 2mm/min Mpa 111 112 80 90 82 146 159


ISO 178 2mm/min Mpa 2,900 3,000 1,700 2,350 2,200 6,000 6,400

Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 65

(notched) 1/8 kgf·cm/cm 2.5 3 4 4.5 >5 75 65 50 15 7 7.5 9

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 3.6 4 65 67 47 8 10

Izod Impact Strength ISO 180 1A (notched) KJ/m2 4.5 4.4 65 64 43 7 9


ISO 2039-2 R-Scale 122 123 117 119 116 120

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 97 100 95 95 130 129 122 137 115 93

ISO 75-2 1.8MPa °C 89 92 93 117 93

VICAT Softening Temperature ISO R306 B/50 °C 105 110 106 108 144 143 109 139 136 100


Flammability UL94

HB mm

V-2 mm 2.0, 3.0 2.0, 3.0 0.75 0.4 0.75

V-1 mm 2

V-0 mm 2.5 2 2 1.5, 3.0 0.7 1.5 1.5-1.6 2.5 0.75

5VA mm

5VB mm

flame retardant pC & pC alloy®



Non-Reinforced Non-Reinforced Reinforced

Properties Test Method Condition Unit TN-1045M TN-1045S TN-1100 TN-1200 TH-1100 HN-1064IA UF-1017S LB-1010W LH-1070W HN-3102G NH-3204G NH-3208GL

PhysiCAl ProPerties



Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 19 24

300°C, 1.2kg g/10min 41 34

250°C, 10kg g/10min 92 72 75 60 17 17 50 65 33 36

ISO 1133

220°C, 10kg g/10min 19 24

300°C, 1.2kg g/10min 41 34

250°C, 10kg g/10min 92 72 17 50 36

Mold Shrinkage ASTM D955 % 0.3-0.4 0.2-0.4




5mm/min kgf/cm2 860 900 1,070

ISO 527-1A50mm/min Mpa 73 72 55 61 55 109 120

5mm/min kgf/cm2

Tensile Strain at BreakASTM D638 50mm/min %

ISO 527-1A 50mm/min % 95 95 93 87 3

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,100 1,100 1,100 1,100 960 790 910 780 850 1,500 1,100 1,400

ISO 178 2mm/min Mpa 111 112 80 90 82 146 159


ISO 178 2mm/min Mpa 2,900 3,000 1,700 2,350 2,200 6,000 6,400


(notched) 1/8 kgf·cm/cm 2.5 3 4 4.5 >5 75 65 50 15 7 7.5 9

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 3.6 4 65 67 47 8 10

Izod Impact Strength ISO 180 1A (notched) KJ/m2 4.5 4.4 65 64 43 7 9


ISO 2039-2 R-Scale 122 123 117 119 116 120

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 97 100 95 95 130 129 122 137 115 93

ISO 75-2 1.8MPa °C 89 92 93 117 93

VICAT Softening Temperature ISO R306 B/50 °C 105 110 106 108 144 143 109 139 136 100


Flammability UL94

HB mm

V-2 mm 2.0, 3.0 2.0, 3.0 0.75 0.4 0.75

V-1 mm 2

V-0 mm 2.5 2 2 1.5, 3.0 0.7 1.5 1.5-1.6 2.5 0.75

5VA mm

5VB mm

flame retardant pC & pC alloy



Reinforced Non-Halogen

Properties Test Method Condition Unit HF-3201GL NH-3402F HN-3104 NH-1017 NH-1015 NH-1027HF NE-1029 NE-1010 NE-1030 GC-1015 GC-1150 LX-1031 LX-1080

PhysiCAl ProPerties

Specific Gravity ASTM D792 g/cm2 1.32 1.51 1.27 1.17 1.18 1.19 1.17 1.18 1.18 1.2 1.29 1.2 1.19

Water Absorption ASTM D570 % 0.15 0.15 0.2

Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 55 24 55 35 48 53 25 31 30 48

300°C, 1.2kg g/10min

250°C, 10kg g/10min 11 33 10.8

ISO 1133

220°C, 10kg g/10min 55 24 55 35 48 53 25 31 48

300°C, 1.2kg g/10min

250°C, 10kg g/10min 11 10.8

Mold Shrinkage ASTM D955 % 0.1-0.3 0.1-0.3 0.5-0.7




5mm/min kgf/cm2 1,000 1,430 500 600

ISO 527-1A50mm/min Mpa 114 60 57 60 61 56 64 60 58 64 59

5mm/min kgf/cm2

Tensile Strain at BreakASTM D638 50mm/min % 8.8 102 25

ISO 527-1A 50mm/min % 4 8 10 51 39 55 4.3 35 96 14

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,700 1,800 850 830 880 900 850 960 890 900 950 830 870

ISO 178 2mm/min Mpa 168 98 85 88 92 90 92 90 90 93 88

Flexural ModulusASTM D790 2.8mm/min kgf/cm2 56,000 110,000 36,000 24,000 24,500 24,000 24,000 28,000 25,000 25,000 41,000 25,000 24,000

ISO 178 2mm/min Mpa 5,800 3,300 2,500 2,500 2,600 1,500 2,600 2,500 2,500 3,922 2,400

Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 19 17 16 36 11

(notched) 1/8 kgf·cm/cm 16 11 10 58 60 55 40 50 71 7 46 12

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 15 12 14 44 17 12 11 17 55 7 10

Izod Impact Strength ISO 180 1A (notched) KJ/m2 13 10 13 40 17 11 10.6 16 52 6 10

Rockwell HardnessASTM D785 R-Scale 91 122 116 118 115 116 116 118

ISO 2039-2 R-Scale 120 118 116 118 121 115 120 118 117 118

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 141 110 139 80 80 86 73 85

ISO 75-2 1.8MPa °C 142 137 75 81 82 78 80 77 81 81

VICAT Softening Temperature ISO R306 B/50 °C 151 148 91 98 98 91 96 93 98 96 91 98


Flammability UL94

HB mm 1

V-2 mm 1.5 1.2,1.5, 3.0

V-1 mm 1.5 2 1 1 1.2

V-0 mm 1.5, 3.0, 6.0 2.5, 3.0 1.5 2.0, 3.0 1.5 1.2,1.5, 3.0 1.2-3.0 1.5 1.5, 3.0 1.5 1.2, 3.0 1.5-3.0

5VA mm 3 3 3

5VB mm 2.0, 30 2 1.5, 3.0 1.5 2




Reinforced Non-Halogen

Properties Test Method Condition Unit HF-3201GL NH-3402F HN-3104 NH-1017 NH-1015 NH-1027HF NE-1029 NE-1010 NE-1030 GC-1015 GC-1150 LX-1031 LX-1080

PhysiCAl ProPerties

Specific Gravity ASTM D792 g/cm2 1.32 1.51 1.27 1.17 1.18 1.19 1.17 1.18 1.18 1.2 1.29 1.2 1.19

Water Absorption ASTM D570 % 0.15 0.15 0.2

Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 55 24 55 35 48 53 25 31 30 48

300°C, 1.2kg g/10min

250°C, 10kg g/10min 11 33 10.8

ISO 1133

220°C, 10kg g/10min 55 24 55 35 48 53 25 31 48

300°C, 1.2kg g/10min

250°C, 10kg g/10min 11 10.8

Mold Shrinkage ASTM D955 % 0.1-0.3 0.1-0.3 0.5-0.7




5mm/min kgf/cm2 1,000 1,430 500 600

ISO 527-1A50mm/min Mpa 114 60 57 60 61 56 64 60 58 64 59

5mm/min kgf/cm2

Tensile Strain at BreakASTM D638 50mm/min % 8.8 102 25

ISO 527-1A 50mm/min % 4 8 10 51 39 55 4.3 35 96 14

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,700 1,800 850 830 880 900 850 960 890 900 950 830 870

ISO 178 2mm/min Mpa 168 98 85 88 92 90 92 90 90 93 88

Flexural ModulusASTM D790 2.8mm/min kgf/cm2 56,000 110,000 36,000 24,000 24,500 24,000 24,000 28,000 25,000 25,000 41,000 25,000 24,000

ISO 178 2mm/min Mpa 5,800 3,300 2,500 2,500 2,600 1,500 2,600 2,500 2,500 3,922 2,400

Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 19 17 16 36 11

(notched) 1/8 kgf·cm/cm 16 11 10 58 60 55 40 50 71 7 46 12

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 15 12 14 44 17 12 11 17 55 7 10

Izod Impact Strength ISO 180 1A (notched) KJ/m2 13 10 13 40 17 11 10.6 16 52 6 10

Rockwell HardnessASTM D785 R-Scale 91 122 116 118 115 116 116 118

ISO 2039-2 R-Scale 120 118 116 118 121 115 120 118 117 118

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 141 110 139 80 80 86 73 85

ISO 75-2 1.8MPa °C 142 137 75 81 82 78 80 77 81 81

VICAT Softening Temperature ISO R306 B/50 °C 151 148 91 98 98 91 96 93 98 96 91 98


Flammability UL94

HB mm 1

V-2 mm 1.5 1.2,1.5, 3.0

V-1 mm 1.5 2 1 1 1.2

V-0 mm 1.5, 3.0, 6.0 2.5, 3.0 1.5 2.0, 3.0 1.5 1.2,1.5, 3.0 1.2-3.0 1.5 1.5, 3.0 1.5 1.2, 3.0 1.5-3.0

5VA mm 3 3 3

5VB mm 2.0, 30 2 1.5, 3.0 1.5 2

flame retardant pC & pC alloy



High Modulus

Properties Test Method Condition Unit LS-1150G LS-1159 NH-1101 NH-1150HH

PhysiCAl ProPerties



Melt Flow Index

ASTM D1238

220°C, 10kg g/10min 27 30

300°C, 1.2kg g/10min

250°C, 10kg g/10min 24

ISO 1133

220°C, 10kg g/10min 27 30

300°C, 1.2kg g/10min

250°C, 10kg g/10min 24

Mold Shrinkage ASTM D955 % 0.12



ASTM D63850mm/min kgf/cm2 630 600

5mm/min kgf/cm2 900 800

ISO 527-1A50mm/min Mpa 86 61 60

5mm/min kgf/cm2 80

Tensile Strain at BreakASTM D638 50mm/min % 7

ISO 527-1A 50mm/min % 3.6 29 7

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 1,400 1,200 950 900

ISO 178 2mm/min Mpa 135 110 93 90


ISO 178 2mm/min Mpa 4,400 5,000 3,400 3,400




Izod Impact Strength ISO 180 1A (notched) KJ/m2 8 6 13 8

Rockwell HardnessASTM D785 R-Scale 114 110

ISO 2039-2 R-Scale 121 115

therMAl ProPerties

Heat Deflection TemperatureASTM D648 18.56kgf/cm2 °C 127 91 81 81

ISO 75-2 1.8MPa °C 120 81



Flammability UL94

HB mm

V-2 mm 0.8-3.0

V-1 mm 1.5

V-0 mm 2.5 1.2 1.2

5VA mm

5VB mm




High Heat Resistance High Flow

Properties Test Method Condition Unit HP-1000X HP-1000XA LI-1000 HP-1011 WP-1069 WP-1089

PhysiCAl ProPerties

Specific Gravity ASTM D792 g/cm2 1.15 1.12 1.2 1.12 1.13 1.13

Melt Flow Index

ASTM D1238

250°C, 10kg g/10min 43 28 28 35 47 47

250°C, 2.16kg g/10min 6

260°C, 5kg g/10min 27

ISO 1133

250°C, 10kg g/10min 43 28 35 47

250°C, 2.16kg g/10min 6

260°C, 5kg g/10min 27

Mold Shrinkage ASTM D955 % 0.4~0.6 0.4-0.6 0.3~0.7 0.5~0.6



ASTM D638 50mm/min kgf/cm2 570 550 600 530 580 540

ISO 527-1A50mm/min Mpa 54 50 50 53 52

5mm/min kgf/cm2


ISO 527-1A 50mm/min % 108 100 92 50 60

Flexural StrengthASTM D790 2.8mm/min kgf/cm2 810 750 800 750 800 770

ISO 178 2mm/min Mpa 77 80 74 78 80

Flexural ModulusASTM D790 2.8mm/min kgf/cm2 22,000 20,500 2,000 20,000 22,500 21,500

ISO 178 2mm/min Mpa 2,000 2,100 2,000 2,120 2,200


(notched) 1/8 kgf·cm/cm 80 60 66 58 60

Charpy Impact Strength ISO 179 1eA (notched) KJ/m2 60 45 49 45 51

Izod Impact Strength ISO 180 1A (notched) KJ/m2 50 45 46 41 46


ISO 2039-2 R-Scale 116 112 110 113 110

therMAl ProPerties


ISO 75-2 1.8MPa °C 107 102 99 101 104

VICAT Softening Temperature ISO R306 B/50 °C 129 123 144 121 122 120

pC/abs for automotive®flame retardant pC & pC alloy



Metal Plating Chemical Resistant Low Gloss

Properties Test Method Condition Unit WP-1041 WP-1041G WP-1059 WP-1098

PhysiCAl ProPerties


Melt Flow Index

ASTM D1238

250°C, 10kg g/10min 35 31 45 32

250°C, 2.16kg g/10min 4 3

260°C, 5kg g/10min

ISO 1133

250°C, 10kg g/10min 35 31 45 32

250°C, 2.16kg g/10min 4 3

260°C, 5kg g/10min

Mold Shrinkage ASTM D955 % 0.5~0.6 0.5~0.6



ASTM D638 50mm/min kgf/cm2 490 500 540 520

ISO 527-1A50mm/min Mpa 47 47 52

5mm/min kgf/cm2 54


ISO 527-1A 50mm/min % 22 73 62


ISO 178 2mm/min Mpa 73 70 75 76


ISO 178 2mm/min Mpa 2,000 2,000 2,250 2,200

Izod Impact Strength ASTM D256(notched) 1/4 kgf·cm/cm 40 42



Izod Impact Strength ISO 180 1A (notched) KJ/m2 44 45 45 48


ISO 2039-2 R-Scale 103 107 112 114

therMAl ProPerties


ISO 75-2 1.8MPa °C 93 93 100


pC/abs for automotive®



appliCations

tV/Monitor

1. front Cover

MABS BF-0950

ABS HG-0760TV, SD-0150

FR PC/ABS NH-1017D, NE-1030, NH-1017SG

TR ABS TX-0510T

Double injection

FR PC TN-1045

FR PC/ABS NE-1010

MABS TF-0930, SF-0505HW, BF-0950

2. back light frame

PC/ABS/GF LS-1150G

FR PC LH-1070W

3. Middle Cover

PC/ABS/GF 15% LS-1159

4. rear Cover

mPPE NH-1904

FR PS VE-1801, VE-1805

5. Guide stand neck

PC/GF 20% HF-3200 H

FR PC/GF 20% HF-3202H

6. stand base

MABS BF-0950

ABS HG-0760TV, SD-0150

FR PC/ABS NH-1017D, NH-1017SG

Metal plating ABS MP-0670

Metal plating PC/ABS QP-1010

➊

➎

➏

➋

➌


note pC

appliCations

1. front bezel

FR PC/PMMA NF-3017 (Scratch resistant)

FR PC/ABS NH-1021 (High gloss)

2. rear Cover base

FR PC/ABS NH-1015, GC-1015

FR PC/ABS Talc 10% NH-1101

FR PC/ABS Talc 15% NH-1150HH

FR PC/GF NH-3280GL

FR PPA/GF MX-4500G

3. antenna Cover palm rest

FR PC/ABS NH-1015, GC-1015

FR PC/ABS Talc 10% NH-1101

FR PC/ABS Talc 15% NH-1150HH

FR PC/GF NH-3280GL

FR PPA/GF MX-4500G

4. battery pack

FR PC UF-1017S

5. Keyboard frame

FR PC/ABS NH-1021

ABS HG-0760TV

➊

➎

➋

➋

➌


Mobile phone

appliCations

1. Keypad

PC/PMMA IV-1071

ABS SF-0941

2. front Cover

PC CF-1050

PC CF-1070

PC CF-1030

3. battery

FR PC UF-1017S

4. rear Cover

PC CF-1050

PC/GF CF-3104HF

PC/GF CF-3200HF

PC/GF CF-3300HF

PC/GF CF-3300LW

PPA/GF CF-4150

PA/GF MKD-1016

5. battery Cover

PC CF-1050

PC CF-1070

PC CF-1051T

PC CF-1011T

PC/GF CF-3104HF

PC/ABS ST-1009

PC/ABS HI-1001BN

PC/ABS HP-1011

➊

➎

➋

➌


smart Meter

appliCations

1. Meter Cover

PC (V2) SC-1220UR

2. terminal block

FR PC/GF 10% HN-3104

3. Cover Meter


4. base Meter/base frame


5. Meter Cover

PC (V2) SC-1220UR

6. Meter body

PC(V2) SA-1100

PC(V2) SA-1220

7. terminal block


(IEC) Smart Meter

(ANSI) Smart Meter

(ieC) smart Meter

(ansi) smart Meter

➎

➏

➐

➊

➋

➌


automotive

appliCations

1. interior

Power Window Switch Cover: Heat Resistance ABS

Air Vent: PC/PBT, PC/ABS

Center Fascia: PC, PC/ABS

Overhead Console: PC/ASA

Console: Heat Resistance ABS

2. UtH

Junction Box: mPPE

HEV Battery Housing: PA/GF

Eco Wire : PPE/Elastomer

3. lighting

Head Lamp Bezel: PBT/PET

Rear Lamp Housing: PC/ABS

4. exterior

Tailgate Garnish: PC/ABS, MP ABS

Rear Spoiler: Blow Molding ABS

Wheel Cover: MP PC/ABS, PC/ABS

Outside Door Handle: MP PC/ABS

Side Mirror: ASA, PBT/PET/GF

Radiator Grill: MP ABS, ASA

5. structure

Panorama Sunroof Frame: PBT/ASA/GF

Fuel Filler Door: PA/PPE/CNT

Fender: PA/PPE/CNT

➊

➊ ➎

➎

➋

➌

➌


Development support

• Color development

• CAE analysis support

Quality support

• Field evaluation

• Technical solution

total solution platform

inteGrateD soltions

total solUtion proViDer

inteGrateDsolUtions

Material Solution

Global Supply Chain

Solution

Design Solution

Technical Solution

Broad product line-up

Speedy development

Cost reduction

Global production & supply system

Exclusive color development

Advanced technology

CAE support

Global tech support

Enhancing productivity

Global quality control

Development support

• CTQ analysis

• Material selection with optimal properties

Product support

• Mold design technical support

Consulting mass production schedule

• Productivity improvement

Market Research

Product Planning

DesignReliability

Test

Concept Establishment

Mold Manufacturing Pilot Injection

Mass Production

Sales


Global network

HeaDQUarters

Global sUbsiDiarY

Samsung Cheil Industries Inc.332-2 Gocheon-dong Uiwang-si Gyeonggi-do, 437-711, Korea Tel: +82-31-596-3408 Fax: +82-31-596-3490 E-mail: [email protected]

Los Angeles, USA Samsung Chemical Inc.

Tel: +1-562-229-1307 E-mail: [email protected]

Frankfurt, Germany Samsung Chemical Europe GmbH

Tel: +49-6196-66-7490

E-mail: [email protected]

Shanghai, China Samsung Chemical Material Trading (Shanghai) Co., Ltd.

Tel: +86-21-6270-3000(325)


Bangkok, Thailand Samsung Chemical Thailand

Tel: +66-2-624-6715


Tokyo, Japan Samsung Chemical Inc.

Tel: +81-3-6234-2197


sales / serViCe offiCe

plant

asiaShenzhen, ChinaTel: +86-755-8203-2323 E-mail: [email protected]

Tianjin, ChinaTel: +86-22-2836-4261 E-mail: [email protected]

Nagoya, JapanTel: +81-52-569-1807 E-mail: [email protected]

Osaka, JapanTel: +81-6-6949-3162 E-mail: [email protected]

Kuala Lumpur, MalaysiaTel: +60-3-2174-4534, 4570 E-mail: [email protected]

Chennai, IndiaTel: +91-98401-04251 E-mail: [email protected]

Delhi, IndiaTel: +91-81302-19193 E-mail: [email protected]

Dubai, U.A.ETel: +971-4-447-3411 E-mail: [email protected]

europeBratislava, SlovakiaTel: +421-90-170-2001 E-mail: [email protected]

Istanbul, TurkeyTel: +90-541-231-0314 E-mail: [email protected]

Milano, ItalyTel: +39-2-83111840 E-mail: [email protected]

americaChicago, U.S.A.Tel: +1-847-407-2845 E-mail: [email protected]

San Diego, U.S.A.Tel: +1-619-278-0961 E-mail: [email protected]

Detroit, U.S.A.Tel: +1-248-276-8484 E-mail: [email protected]

Yeosu, Republic of KoreaTel: +82-61-689-1221 E-mail: [email protected]

Tianjin, ChinaTel: +86-22-5868-0291 E-mai: [email protected]

Kornye, HungaryTel: +36-34-814-120 E-mail: [email protected]

Tijuana, MexicoTel: +52-664-627-4947 E-mail: [email protected]

HeaDQUarters

Global sUbsiDiarY

sales offiCe

plant

MexicoTijuana

USALos AngelesChicagoSan DiegoDetroit

GermanyFrankfurt

TurkeyIstanbul

SOUTH KOREAUiwangYeosuGumiBusanGwangju

SlovakiaBratislava

HungaryKornye

IndiaChennaiDelhi

EgyptCairo

ItalyMilano

ThailandBangkok

U.A.EDubai

JapanTokyoNagoyaOsaka

MalaysiaKuala Lumpur

ChinaSanghaiTianjinShenzhen


samsung Cheil industries - Chemical


note The information contained herein is provided by Samsung Cheil Industries, Inc. and its subsidiaries and affiliates (collectively referred to as “SAMSUNG”) for information purposes only and should be used by individuals with technical experience and knowledge in the area. Samsung Cheil Industries does not make any representation or warranties of the usefulness or expected result of the information, and does not assume any responsibility whatsoever related to the use of the information. SCI-M-042013

We provide value to turn your imagination into reality with our innovative materials and optimal solutions.

Value+ your imagination

www.samsungchemical.com