Multilayer on Polymer Waveguide
for Advanced Integrated Photonics
Ezekiel Obadia Kuhoga
MSc Thesis
June 2018
Department of Physics and Mathematics
University of Eastern Finland
Ezekiel Obadia Kuhoga Master student, 39 pages
University of Eastern Finland
Master’s Degree Programme in Photonics
Supervisor Prof. Matthieu Roussey
Abstract
Recently Bloch surface waves (BSWs) based devices have been attracting a lot of
interests, and especially for sensing application. BSW devices are purely dielectric-
based platforms exhibiting lower losses and therefore longer propagation length com-
pared to their equivalent using metallic film for sustaining surface plasmon polari-
tons (SPP). In this work we demonstrate the possibility to excite, confine and guide
BSWs in a slot waveguide combined with the two photonic crystals (PhCs). This
configuration will make a great deal contribution to the on-chip integrated sen-
sors development. Its applications extend in many aspects such chemical sensing,
biosensing, enhanced raman scattering, and enhanced fluorescence detection.
Keywords: Bloch surface waves; Photonic crystals; Polymer waveguides; Guided
waves; Integrated optic devices; Sensors; Optical waveguides; Refractive index; Ef-
fective index; Photonic band gap.
Preface
For long time I have had a desire to work with optical waveguides following their
daily life applications. To be in the institute of photonics at the university of Eastern
Finland is a great opportunity happened to me. I am grateful as well for being a
part of the for part of the integrated optics group where where I have been able to
learn about presentation, and other necessary skills.
Well, first of all I thank God the Almighty for it is by His grace and mercy that I
have managed to be where I am now. With all the people I have met, all the places
I have been, have made me who I am now, and I do know it is by His doing, and so
glory to Him.
Moreover, there are people who have been so helpful to me, and i would love
to acknowledge their presence in my life. I extend my heart of appreciation to the
supervisor of my thesis work, Prof. Matthieu Roussey for his guidance, supervision
and patience towards me, his trust and mostly his selfless spirit. All of this make my
learning process possible, easy and enjoyable. I also thank Prof Seppo Honkanen for
his consultation and words of encouragement which push me forward. I acknowlegde
the support from Dr. Martti Makinen in this work for he had given his own time
to help me understand the matlab codes which also played a very important role in
this work. I would also love to thank M.S. Lewis Asilevi and M.S. Segolene Peliset
for their support in perfoming the simulation works.
My heartfelt appreciation also goes to my mother Enid Kuhoga. She has trusted
me and she has been willing and supported me always even when it seemed least
convenient. In addition to that, I also would love to acknowledge my other family
members i.e. my father Obadia Kuhoga, and a brother Ibrahim Kuhoga for being
ready to support me in the time of my need. Surely, without the support from my
family, I wouldnt have been here. On top of that, I would love to appreciate my
girlfriend, Linda Yuda for her support from the beginning up to the moment.
My regards to M.S. Boniphace Kanyathare for his support during his presence at
the university. In addition to that I appreciate M.S. Leonard Shayo and Ms. Elemina
John for they were the bridge that connected me to the university of Eastern Finland.
Nevertheless, I deeply would love to thank the whole UEF staff panel in the
photonics department; I believe the learning especially related to physics/photonics
is not always easy, but the bridge developed between the staff and the students
iii
makes the learning process very accomodative.
Lastly, I would love to acknowledge all of my fellow students in the photonics
class 2016-2018 for the friendship, togetherness and support that we all had for each
other. I would also love to appreciate all those who contributed to this work on one
way or the other but I have forgotten to show my acknowledgement to you, just
know that your contribution to my work is highly appreciated.
Joensuu, the 5th of May 2018 Ezekiel Obadia Kuhoga
iv
Contents
1 Introduction 1
2 Theory on optical waveguides 4
2.1 Dielectric slab waveguides . . . . . . . . . . . . . . . . . . . . . . . . 4
2.2 Maxwell’s equations . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6
2.3 Boundary conditions . . . . . . . . . . . . . . . . . . . . . . . . . . . 6
2.4 Wave propagation in slab waveguides . . . . . . . . . . . . . . . . . . 7
2.5 Slot waveguide . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9
3 Theory on Bloch surface waves 14
3.1 Bloch surface waves . . . . . . . . . . . . . . . . . . . . . . . . . . . . 14
3.2 BSWs propagation in 1-DPhCs . . . . . . . . . . . . . . . . . . . . . 16
3.3 Photonic band-gap . . . . . . . . . . . . . . . . . . . . . . . . . . . . 20
3.4 BSWs characterization and application . . . . . . . . . . . . . . . . . 20
4 Simulations on BSWs 23
4.1 Proposed design . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23
4.2 Simulations based on TMM . . . . . . . . . . . . . . . . . . . . . . . 24
4.3 FDTD simulations . . . . . . . . . . . . . . . . . . . . . . . . . . . . 26
4.3.1 Influence of the slot width . . . . . . . . . . . . . . . . . . . . 27
4.3.2 Influence of the angle of incidence . . . . . . . . . . . . . . . . 29
4.4 Discussion and Analysis . . . . . . . . . . . . . . . . . . . . . . . . . 30
4.4.1 Dielectric material selection . . . . . . . . . . . . . . . . . . . 30
v
4.4.2 PBG and BSWs . . . . . . . . . . . . . . . . . . . . . . . . . . 30
4.4.3 Sensitivity . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 31
5 Conclusions and future outlook 32
References 34
vi
Chapter I
Introduction
For many years there has been a strong interest on photonic sensors in both research
and industrial applications, such as biomedics, security, environment exploration,
and many other fields. This follows their advantages compared to conventional sen-
sors such as high selectivity and sensitivity, no electrical and electromagnetic inter-
ferences, temperature stability, compactness, more affordability, and flexibility [1].
However, with respect to the advancement of photonic integrated circuits (PICs),
there has been a rise in interests to have more sensitive and compact optical sen-
sors [2]. Passaro et al. in [3] have mentioned some of recently advanced integrated
photonic sensors for instance, waveguide based devices such as ring resonators, sur-
face plasmon resonance sensors, Sagnac effect based sensors, Fano resonance based
sensors, Mach-Zehnder interferometers sensors, and sensors based on photonic crys-
tals (PhCs).
PhCs are photonic composite materials with a periodically varying dielectric con-
stants in one, two or three dimensions [4]. However in this work we focus mainly on
1-DPhC. 1D-PhCs are stacks made of two alternating layers of dielectric materials
with different refractive indices [5]. A PhC can exhibit a photonic band gap (PBG)
in its spectrum, for which wavelengths no light is allowed to propagate through the
structure [6–9]. PhCs, in this work, are transparent to light in the visible range
for angles less than critical angles. For angles larger than the critical angle the
total internal reflection (TIR) is experienced. TIR is a condition where almost all
of the incident light from the high index medium towards low index medium is re-
flected at the interface back to high index medium. However, electric field can still
penetrate the interface carrying the energy in form of an evanescent wave for nano
1
scale distance before bringing them back to the incident medium [10]. This can be
demonstrated by adding a third high index medium next to low index medium in
nanometer scale distance from the first medium. This offers the frustrating effects
referred to as the frustrated TIR where the energy is trapped and prevented from
going back into the medium one [10–12]. During TIR the Bloch wave vector K
becomes complex within the PBG, and the imaginary part gives rise to evanescent
waves which are now referred to as Bloch surface waves (BSWs) [6]. BSWs can be
excited at the surface of a PhC using different angles of the incident light through
Kretschmann’s configuration [13]. Kretschmann’s configuration uses a prism to cou-
ple light and thus excite the surface waves on the surface of a truncated PhC [13,14].
BSWs propagates at the interface between PhC and low index medium [15,16]. One
way of which BSWs can be analyzed is by observing angular dependence of the
reflected light. BSWs are characterized by a resonance dip at a particular angle of
incidence and wavelength within the PBG of the structure. BSWs have found their
application in many fields such as in biosensing [15, 17–20], enhanced fluorescence
detection [21–23], gas sensing, and enhanced Raman scattering [17].
BSWs are compared to surface plasmon polaritons SPP in many ways including
their excitation, operations, sensitivity, and application [23–26]. The advantages of
BSWs compared to SPPs is their lower propagation losses [27]. This is mainly due
to dielectrics having less absorption compared to metals in SPP thus having sharper
resonance dips and stronger local fields with longer propagation length [21, 22, 28].
Another advantage with BSWs is that it is possible to excite a BSW at a specific
wavelength by adjusting multilayer parameters, i.e., layers’ thicknesses, number of
periods, and the angle of incidence of the illumination [29]. On top of that, TM and
TE polarized BSWs can be excited at the same time, while SPPs are only compatible
with TM polarization [30]. Moreover, BSW-based sensors have a potentially higher
sensitivity [31,32]. Currently most of BSWs based sensors are based on the angular
and spectral intensity reflection measurement [29].
A slot waveguide is a recently developed waveguide composed of two high refrac-
tive index rails separated by a thin low index gap, typically less than 100 nm [33–35].
From the boundary conditions as discussed by Yariv, A and Yeh, P in [6], we can
see that, the tangential component of electric field is continuous at the boundary
surface. In addition to that, the normal component of electric field is discontinuous
across the interface [6]. Slot waveguide configuration uses electric field discontinuity
2
at the interfaces to confine and enhance the optical field intensity within the low
index slot [33–36]. Confinement factor within the slot makes this configuration very
useful for optical sensing.
In this work we demonstrate how to excite BSWs at a wavelength of 488nm
and confine the surface waves within a slot-waveguide. This involves designing and
combining together two identical PhCs in close proximity to each other such that
they form a slot in between. The size of the slot is 50 nm which is smaller than the
decay length of the BSWs and it leads to the enhancement of the confined waves.
The illumination beams are guided through a polymer waveguide towards the PhCs’
surfaces and are made incident on both sets of PhCs with an angle of incidence of
around 55◦ for BSWs excitations. The excited BSWs from both PhCs are therefore
being superimposed and confined within the formed slot. The designed PhCs are
composed of a high refractive index layer Titanium oxide TiO2 and a low refractive
index layer Al2O3 with thicknesses 62 nm and 94 nm respectively, and TiO2 as a top
additional layer of 30 nm thickness. The BSWs excitation and confinement within
the slot is demonstrated using transfer matrix method (TMM) and finite difference
time domain (FDTD) method using matlab and optiwave softwares respectively.
TiO2 and Al2O3 are transparent in the visible range, chemically, thermally, and
physically stable [37–39]. Using polymer, allows a relaxed and cost-efficient fabrica-
tion [36,40].
In this work on chapter two we explain briefly the basic theory related to optical
waveguides. Chapter three gives a brief theory related to photonic band gap and
BSWs. In chapter four we demonstrate simulations done using both TMM and
FDTD methods, discussed, analyzed, and justified the results obtained. Lastly,
chapter five provides the conclusion and the future outlook of this work.
3
Chapter II
Theory on optical waveguides
In this chapter, the basic theory on optical waveguides in given in brief. This is
expected to provide a basic understanding on how optical waveguides operate.
2.1 Dielectric slab waveguides
Optical waveguides are structures used in guiding light waves as the light propagates
from one point to another. Dielectric slab waveguides are the simplest optical waveg-
uides in structure and geometry [41]. The structure of slab waveguide includes a
core which is a high refractive index region, a substrate, and a surrounding medium
having lower refractive index compared with the core [42]. Figure (2.1) shows a sim-
ple structure of a slab waveguide. The principle of operation of the slab waveguide
is based on a total internal reflection (TIR) phenomenon whereby the propagating
waves are being confined and propagate within the core [42]. In slab waveguides,
TIR is experienced when the light from the core hits the core-cover or core-substrate
interface at an angle of incidence larger than the critical angle. This Phenomenon
causes the light to be reflected back to the core. Equation showing how to achieve
the condition for total internal reflection in slab waveguide is expressed as [42],
ncore sin(π/2− φ) ≥ nclad, (2.1)
where ncore is the refractive index of the core, nclad is the refractive index of the
cladding and φ is the refracted angle at the air-core interface. The expressed phe-
nomena leads to the definition of the acceptance angle of incident light at the air-core
4
Figure 2.1: Schematic diagram showing the geometry of a symmetric slab
waveguide. The guiding layer is a slab with a refractive index n2, surrounded
by low index media of refractive index n1 [6].
interface so known as the numerical aperture (NA) of an interface. NA is the max-
imum acceptable angle of an incident light at the air-core interface for getting the
total internal reflection. NA is defined on the equation below [42]
NA = θmax = ncore
√2∆, (2.2)
where ∆ is the refractive index contrast of a waveguide presented as [42],
∆ =ncore − nclad
ncore
(2.3)
However, due to phase shifting of reflected light rays at the core-cladding interface
within the waveguide, not all light rays incident within the acceptable angle are able
to propagate in the waveguide. For light rays to propagate successfully they need to
satisfy the phase-matching condition for optical paths. Phase-matching condition is
expressed as [42],
tan(kncorea sinφ− mπ
2
)=
√2∆
sin2 φ− 1 (2.4)
5
where φ is the angle between the ray and the z-axis, a is the core radius, and
m = 0,+1,+2, .... The field allowed to propagate at m = 0 is referred to as the
fundamental mode, while other modes propagating at m ≥ 1 are being referred to
as higher-order modes [42]. The propagation constants along z and x axes are given
as [42],
β = kncore cosφ, (2.5)
κ = kncore sinφ. (2.6)
2.2 Maxwell’s equations
Propagation of electromagnetic waves in a medium obeys Maxwell’s equations which
are [6],
∇×E = −∂B
∂t, (2.7)
∇×H =∂D
∂t+ J , (2.8)
∇ ·D = ρ, (2.9)
∇ ·B = 0, (2.10)
where E and H are electric and magnetic fields, D and B are electric displace-
ment and magnetic field vectors and J and ρ represent electric current and charge
density respectively. Moreover, Maxwell’s equations are being constituted by the
constitutive equations for electric displacement and magnetic induction vector [6]
D = εE, (2.11)
B = µH , (2.12)
where ε is makes the relative permittivity of the medium and µ makes relative
permiability of the particular medium.
2.3 Boundary conditions
When a light is propagating across one or more interfaces between dielectric media
the physical properties associated with permittivity ε and permiability µ change
6
abruptly [6]. However, despite the change in the physical properties there ex-
ists a continuity relationship at the interfaces for some of the components of the
fields. These continuity relations are derived from Maxwell’s equations and ex-
pressed through equations known as boundary conditions [6]. Equations 2.13 to
2.16 express the boundary conditions for both electric and magnetic fields. From
these conditions we can see that the tangential component of the electric field is
always continuous across the interface while the normal component of electric field
is discontinuous across the interface [6]. As we are dealing the dielectric material,
therefore the charge and current densities becomes zero for this case. The following
equations represents boundary conditions [6],
B2n = B1n, (2.13)
D2n = D1n, (2.14)
E2t = E1t, (2.15)
H2t = H1t, (2.16)
The normal component of B and the tangential component of E are continuous
across the interface. The normal component of D and the tangential component
of H are not. If there are no charges at the interface then the normal component
of D is continuous, if there are no current, then the tangential component of H is
continuous.
2.4 Wave propagation in slab waveguides
Consider a monochromatic wave propagating along z-direction in a symmetric slab
waveguide as shown in figure 2.1. Its propagation can be analyzed using Maxwell’s
equations [6],
∇×H = iωε0n2E, (2.17)
∇×E = −iωµH , (2.18)
where n represents the refractive index profile of the structure, ω is the angular fre-
quency of fields. ε0 and µ represent vacuum permittivity and absolute permeability
7
of the particular medium. Solutions to wave equations (2.17) and (2.18) represents
the wave equations for electric and magnetic fields respectively [6],
E(x, t) = Em(x) exp[i(ωt− βz)], (2.19)
H(x, t) = Hm(x) exp[i(ωt− βz)], (2.20)
where β is the propagation constant, E(x) and H(x) are the wavefunctions of the
modes guided in a waveguide and m representing the mode number. From equations
(2.17) and (2.18), TE-mode electric field is expressed as [6],
(∂2
∂x2+
∂2
∂y2
)E(x, y) + [k2
0n2(r)− β2]E(x, y) = 0, (2.21)
where k0 represents the wavenumber in vacuum, β is the propagation constant. The
condition for β of a guided mode in a waveguide is such that,
β >n1ω
c, (2.22)
β <n2ω
c, (2.23)
where n1 and n2 are the refractive indices for surrounding media and the core re-
spectively as defined by the refractive index profile in equation 2.24 [6]. All the
modes confined in the core satisfy the propagation condition as given in the above
equations [6],
n(x) =
{n2, if |x| < d/2,
n1, if otherwise.(2.24)
Propagating modes in the slab waveguide can be categorized generally into two
modes which are transverse-electric (TE) modes and transverse magnetic (TM)
modes. TE-modes have electric field amplitude oscillating perpendicular to the
plane of propagation, and TM-modes have electric field propagating tangential to
the plane of incidence [6]. TE-mode field amplitude is expressed as [6],
Ey(x, y, z) = Em(x) exp[i(ωt− βz)], (2.25)
8
where Em(x) represents the wavefunction of a mode as a function of distance from
the centre of the waveguide [6],
Em(x) =
⎧⎪⎨⎪⎩A sinhx+B coshx, if |x| < 1
2d
C exp(−qx), if x > 12d
D exp(qx), if x < −12d.
(2.26)
A, B, C and D are constants and h and q parameters represents propagation constant
relation where [6];
h =
[(n2ω
c
)2
− β2
] 12
, (2.27)
q =
[β2 −
(n2ω
c
)2] 1
2
. (2.28)
2.5 Slot waveguide
Slot waveguide is formed when the low index slot is situated between high index
dielectric slabs [35](see figure 2.2). As a result of TIR within high index slab(s),
electromagnetic waves penetrate the high-low index interface into the slot in form
of evanescent waves [43]. The propagating fields in the slot can be categorized into
transverse electric (TE) and transverse magnetic (TM) fields where in TE field the
component of electric field oscillates perpendicular to the plane of propagation and in
TM field the the component of magnetic field oscillates perpendicular to the plane of
propagation. The continuity behaviour of the fields due to the boundary conditions
results into high confinement of optical intensity for TE fields [33,35,36,44,45].
The size of the slot is always made smaller than the decay length of an evanescent
tail. This always helps to enhance the field intensity in the slot [35]. Figure 2.3 shows
a field intensity profile of a slot waveguide. We can see that due to factors such as
discontinuity of the TE-mode electric field, and nanometer scale slot, the intensity in
the slot region is highly enhanced. Equation 2.29 shows the analytical solution of the
transverse electric field profile of the fundamental TM eigenmode of the slab-based
slot waveguide [43],
9
Ex(x) = A
⎧⎪⎪⎪⎪⎨⎪⎪⎪⎪⎩1n2Scosh(γSx), |x| < a
1n2Hcosh(γSa) cos[κH(|x| − a)] + γS
n2SκH
sinh[κ(|x| − a)], a < |x| < b
1n2C
{cosh(γSa) cos[κH(b− a)] +
n2HγS
n2SκH
sinh(γSa)
× sin[κH(b− a)]}exp[−γC(|x| − b)], |x| > b
(2.29)
where κH is the transverse wavenumber in the high index medium, γC is the field
decay coefficient in the cladding, γS is the field decay coefficient in the slot, a and
b are the distances of low-to-high and high-to-low interfaces respectively from the
centre of the slot as shown in figure 2.2b), and constant A is given by the following
equation [43].
A = A0
√k0n2
H − κ2H
k0, (2.30)
Where A0 is a constant and k0 = 2π/λ0.
(a) (b)
Substrate
High refractive index rails
slot
Figure 2.2: Diagram showing (a) the basic structure and (b) the geometry
of an optical slot-based waveguide [43].
With slot-waveguides, the sensing application is always done by placing the an-
alyte as a cover or as medium within the slot. The presence of the analyte would
result in the change of effective index of the whole structure or the slot depending
where it is placed. Change in effective index would in turn affect the position of
characteristic resonance and the magnitude of the confined optical intensity. Solving
10
x-axis(wafer width)
slot region
high index regions
Norm
alized inte
nsity
Figure 2.3: Intensity distribution on the cross-section of a slot waveguide(x-axis).
equation 2.29, leads to a relationship between amplitude on the interface in the low
index side and amplitude in the high index region. The relationship is such that
the amplitude at the interface in the low index side, is n2H/n
2S times as much as the
amplitude in the high index medium [43]. High confinement and enhancement of
the optical intensity within the slot, thus leads to strong light analyte interaction.
This effect paves a way to high sensitivity sensors and biosensors.
The magnitude of field confinement in the slot is dependent on the refractive
index contrast between high and low index media across an interface. From the
boundary conditions we have seen that we have seen that that at the interface
rail/slot, the field amplitude in the slot is n2H/n
2S times as much as the field amplitude
in the high index region. High confinement and enhancement of the optical fields
in the slot results into a very strong light-analyte interaction hence enhancing the
sensitivity of sensor [43, 45]. Figure 2.4 shows the relationship between the power
confinement factor and the refractive index in the slot region while keeping the index
of the slabs constants.
Homogeneous sensing is defined as changing of the effective index of the guid-
ing medium with respect to the change in the refractive index of the cover [46,
47]. Through this optical sensitivity of the waveguide it becomes possible to mea-
sure/sense the concentration of fluid/liquid/gaseous solution material placed as cover
11
Figure 2.4: Dependence of power confinement factor in the slot region pro-
vided the refractive index of the rails is constant [33].
to the slot waveguide. Homogenous sensitivity is mentioned in [46] to be propor-
tional to the optical field confinement factor in the cover. Homogeneous sensitivity
is generally expressed in equation 2.31 [46].
Sh =dneff
dnc
(2.31)
where neff is the effective index of the propagating mode.
Confinement factors in the slot and the cover are given as [46],
ΓS =
∫∫S|E(x, y)|2dxdy∫∫
∞ |E(x, y)|2dxdy,(2.32)
ΓC =
∫∫C|E(x, y)|2dxdy∫∫
∞ |E(x, y)|2dxdy, (2.33)
whereE(x, y), S and C indicates the electric field, slot and cover regions respectively.
Effective index of the slot can be calculated from the decay rate of the field at
the cladding from the center of the slot waveguide taking the assumption that the
field is exponentially decaying with respect to the radial distance towards the centre
of the waveguide [35].
neff ≈ (n2C +
γ2
k20
)12 , (2.34)
12
where neff is the effective index, nC is the cladding index, k0 is the wavenumber in
the vacuum and γ is the decay rate of the field.
Slot waveguide can also do surface sensing where the particles or molecules of a
particular medium to be measured are passed through the slot or cover medium
of the waveguide. In this case the effective index of the mode will be affected by
the change in thickness of the added layer.Hence the waveguide sensitivity can be
generally expressed as [46];
Ss =dneff
dρ, (2.35)
where ρ is represents the molecular layer thickness.
13
Chapter III
Theory on Bloch surface waves
This chapter explains the basic theory on Bloch surface waves (BSWs), photonic
bandgaps (PBGs) and their associated features and behaviours. By the end of
this chapter the reader should be able understand what are BSWs and how they
are excited, the conditions for excitation and propagation, their characteristics and
their possible application.
3.1 Bloch surface waves
Boch surface waves (BSWs) are electromagnetic waves generated at the interface
between a truncated PhC, i.e., a non-infinite multilayer and a low index medium
as a result of frustrated TIR. Dielectric multilayer structures, also referred to as
photonic crystals (PhCs), are formed by periodically alternating two dielectric media
of different refractive indices. PhCs can be arranged periodically in either 1-D, 2-
D or 3-D as shown in figure 3.1. A PhC possesses a region within a wavelength
range known as a photonic band gap (PBG) [48]. A PBG is a region where no light
waves are allowed to propagate through the structure. This causes almost all the
light which is incident on the surface of the multilayer to reflect back, see figure
3.5(b). However because of TIR, small part of light passing through a multilayer
is reflected back but cannot enter back because of the PBG. This squeezed wave
between the two media is the BSW. BSWs are excited within the PBG of a multilayer
structure [49, 50]. Width and location of a PBG can be controlled by parameters
such as layers’ thicknesses, number of periods, and refractive indices. On top of
the multilayer structure often lays a top layer which can also be used to control the
location, wavelength, and profile of the BSW mode [50].
14
Figure 3.1: Diagram showing 1-D, 2-D and 3-D PhCs [5].
BSWs are excited in Kretschmann’s configuration where a prism is used to couple
light to the multilayer structure as shown in figure 3.2. If light is incident on a
interface as it propagates from high index medium to low index at an angle of
incidence larger than the critical angle, total internal reflection will occur. However,
not all the light is reflected back as some of the energies always penetrate an interface
as evanescent waves. For the case of multilayer structures, these leaky waves are
trapped on the surface of the multilayer therefore leading to what is known as Bloch
surface waves (BSWs). Hence BSWs are waves sustained on a surface of a multilayer
structure and they are decaying exponentially in the direction perpendicular to the
surface. This is shown and explained later in Figure 3.6(b), for instance.
Incident light
Reflected light
Multilayer structureTop layer
Prism
BSWs
Figure 3.2: Diagram showing BSWs excitation using Kretschmann’s config-
uration. Λ represents one period of the PhC.
15
3.2 BSWs propagation in 1-DPhCs
Figure 3.3: Periodic layered structure with refractive indices n1 and n2 and
thicknesses a and b respectively [6].
Propagation of waves in a dielectric multilayer structure is demonstrated using
a simple diagram as shown in Figure 3.3. The structure is composed of alternating
layers of refractive indices n1 and n2 with thicknesses a and b respectively. The
medium is assumed to be homogeneous along the y-axis and the optic waves gener-
ated in the structure are assumed to propagate along the z-axis [6]. In these periodic
structures, material properties like dielectric and permeability constants are periodic
functions of position, and are shown as [6]
ε(z) = ε(z + Λ), (3.1)
µ(z) = µ(z + Λ), (3.2)
where Λ = a + b represents one period of the multilayer with a and b being thick-
nesses for high and low index layers respectively. Propagation of light waves in the
homogeneous dielectric media can also be explained by Maxwell’s equations given
J = 0 and σ = 0 [51]. For instance incase of dielectric multilayers, equations 2.17
and 2.18 give rise to what is known as Bloch theorem. In this theory, the trans-
lational symmetry of the periodic medium is used to define the normal modes of
propagation expressed as [6],
E = EK(z) exp−iK.z , (3.3)
H = HK(z) exp−iK.z , (3.4)
16
where by the amplitudes EK(z) and HK(z) are periodic functions with respect to
period Λ and K represents the Bloch wavevector [6]
EK(z) = EK(z + Λ), (3.5)
HK(z) = HK(z + Λ). (3.6)
The solution for the wave equation in the medium shown in figure 3.3, can be
given as [6],
E(x,y, z) = E(z) exp i(ωt− kyy), (3.7)
where
E(z) =
⎧⎪⎪⎪⎨⎪⎪⎪⎩an exp−ik1z(z − nΛ)
+bn exp+ik1z(z − nΛ, nΛ− a < z < nΛ
cn exp−ik2z(z − nΛ + a)
+dn exp+ik1z(z − nΛ + a), (n− 1)Λ < z < nΛ− a,
(3.8)
where an, bn, cn and dn are constants, n represents nth layer, and
k1z =
√(n1ω
c
)− k2
y, (3.9)
k2z =
√(n2ω
c
)− k2
y, (3.10)
Taking into consideration the continuity conditions on the electric and magnetic
fields inside the multilayer structure, and with the help of equation 3.8, the fields
relationship between one layer and the other layer of the same refractive index can
be expressed by the use of translation matrix given as [6],[an−1
bn−1
]=
[A B
C D
][an
bn
], (3.11)
17
where the elements of matrix for TE modes are
A = exp i(k1za)
[cos(k2zb) +
i
2
(k2z
k1z
+k1z
k2z
)sin(k2zb)
], (3.12)
B = exp−i(k1za)
[i
2
(k2z
k1z
− k1z
k2z
)sin(k2zb)
], (3.13)
C = exp i(k1za)
[− i
2
(k2z
k1z
− k1z
k2z
)sin(k2zb)
], (3.14)
D = exp−i(k1za)
[cos(k2zb)−
i
2
(k2z
k1z
− k1z
k2z
)sin(k2zb)
], (3.15)
and the elements for TM modes are,
A = exp i(k1za)
[cos(k2zb) +
i
2
(n22k1z
n21k2z
+n21k2z
n22k1z
)sin(k2zb)
], (3.16)
B = exp−i(k1za)
[i
2
(n22k1z
n21k2z
− n21k2z
n22k1z
)sin(k2zb)
], (3.17)
C = exp i(k1za)
[− i
2
(n22k1z
n21k2z
− n21k2z
n22k1z
)sin(k2zb)
], (3.18)
D = exp−i(k1za)
[cos(k2zb)−
i
2
(n22k1z
n21k2z
− n21k2z
n22k1z
)sin(k2zb)
]. (3.19)
Taking into account equation (3.3), and equation 3.5, propagating wave can be
expressed in terms of the column vectors as shown in equation3.20. The field is now
assumed to propagate normal to the interfaces along the z-axis within a multilayer
structure with a period Λ.[an
bn
]= exp−i(KΛ)
[an−1
bn−1
]. (3.20)
Now, taking into account the translation matrix as expressed in equation 3.11, the
periodic condition can be re-expressed as in equation 3.21 making the phase factor
exp i(KΛ) the eigenvalue of the translation matrix [6],[A B
C D
][an
bn
]= exp i(KΛ)
[an
bn
]. (3.21)
The phase factor, exp i(KΛ) can be expressed as cos(KΛ) = 12(A +D) and is used
to provide the dispersion relation existing between the frequency ω, propagation
18
wavenumber along the y-axis, ky and the Bloch wavenumber K as shown in equation
[6],
K(ω,ky) =1
Λcos−1[
1
2(A+D)]. (3.22)
From the expression given in equation 3.22 it is clear that the real values of K(ω,ky)
will be obtained for values of 12(A + D) ranging between −1 and 1. This region
corresponds to the allowable region for the Bloch waves to propagate. However,
outside of that range, the values forK(ω,ky) will be complex with an imaginary part
representing the Bloch wave as an evanescent wave. The regions where the values
of K are complex are referred to as photonic bandgap of the multilayer structure
as shown in figure 3.4. The Bloch wave vector at the edges of the bandgap is
determined by the values where |12(A+D)| = 1 [6,7]. The dark zones in the diagram
represents the regions where the value of Bloch wavenumber K is real, hence the
Bloch waves can propagate in the medium, and the lighter regions before the dashed
line represents the photonics bandgaps. The dashed line is ky = (ω/c) sin θB and it
marks the area where the bandgaps vanish at the brewster angle as the incident and
the reflected waves are uncoupled. When a light wave is incident on a multilayer
(a) (b)
Figure 3.4: Photonic band structure for (a)TE and (b)TM waves. The dark
regions corresponds to areas where values of K are real, hence allowable pho-
tonic bands. The black dashed line in (b) marks the region where the bandgaps
for TM modes vanishes at the brewster angle and is represented by the prop-
agation wavevector ky = (ω/c)n2 sin θB [6].
structure, a normal wave will propagate for the regions where the Bloch wavenumber
19
is real, meaning there are allowed bands. For the case where the light frequency
corresponds to the photonic bandgap, an evanescent wave is generated which decays
exponentially as it propagates in the structure and is referred to as a Block surface
wave. In this region of photonic bandgap, the multilayer structure acts as a good
reflector of an incident wave corresponding to that particular frequency range. Yariv
and Yeh in [6], has related this phenomenon to the diffraction of X-rays by the crystal
lattice planes and hence is referred to as a Bragg reflector.
3.3 Photonic band-gap
Taking into account the dispersion relation ω = ω(K) existing in multilayers, for
the case where angle of incidence is less than the critical angle, Bloch wavevector
K becomes a real vector. The situation leads to a normal propagation of waves
as in homogeneous medium where the amplitudes will still be periodic functions of
position and there would be no losses. When the angle of incidence is larger than
the critical angle, K becomes a complex vector. In this case the waves do not
propagate in the infinite periodic structure. The spectral regions where we have a
complex Bloch wavevector are referred to as photonic bandgaps (PBG). However, as
explained above the BSWs are excited within the PBG of a mutlilayer structure [6].
The propagating BSWs modes in the multilayer structure are highly confined near
the edges following the fact that modes in the centre of the band gap experience
strong attenuation comparing to those near the edges [50]
Propagation constant β of the BSW in the bandgap increases with respect to
the increase in thickness of the top most layer as shown in figure 3.5(a). The green
continuous line in figure 3.5(b) shows the angular reflectance of a reflected light.
Propagation constant of the BSW in the bandgap is expressed as [6],
β =
(2π
λ
)n sin θ, (3.23)
where λ, n and θ are the wavelength of the incident light, the refractive index of the
prism and the incident angle respectively.
3.4 BSWs characterization and application
Usually BSWs are characterized by a resonance dip in the angular reflectance as
shown in figure 3.6(a). In comparison with SPPs, BSWs are created from and
20
Figure 3.5: Diagram showing (a) the relation between dispersion line in the
band gap and the thickness of the top layer vs additional layer (b) plot of
absorption and reflection spectrum of the structure with the additional layer
of 60 nm with respect to effective index [50].
propagates on pure dielectric material. Therefore they possess lower absorption
losses and this results into a narrower resonance dip and longer propagation length.
This property offers more sensitivity to the device. Moreover, the presence of a PBG
offers high wavelength selectivity to the BSWs based optical device by filtering out
all of unwanted wavelengths.
Despite BSWs being excited and propagating on dielectric lossless material, yet
they experience some losses. One main factor for the losses is the field leakage into
the prism. On top of that, there is also a leakage of the field into the multilayer.
However the decay coefficient for leakage into the multilayer can be minimized ex-
ponentially with respect to increased number in multilayers [50].
Following their method of excitation, and their characterization, BSWs based
devices are potential for use as sensors and biosensors.
21
Figure 3.6: Diagram showing (a) the characteristic dip in the angular-
reflectance spectrum, and (b)a field distribution as the light is coupled to
the PhC and hence leading to excitement of the surface wave [13].
22
Chapter IV
Simulations on BSWs
This chapter presents the configuration for BSWs excitation and confinement. In
addition, it demonstrates the simulations perfomed using transfer matrix method
(TMM) and finite difference time domain (FDTD) through Matlab and Optiwave
softwares respectively.
4.1 Proposed design
The proposed structure includes two similar 1DPhCs, which are placed close to each
other to make a slot in between, and polymer layers which guide the incident light
beams towards the multilayer surfaces and the reflected beam away from the surface.
This structure is to be fabricated on top of a silicon dioxide (SiO2) substrate. The
excitation of the two BSWs is done by illuminating a beam of light on the surface
of a multilayer with an angle of incidence larger than the critical angle at polymer-
multilayer interface. The wavelength of interest in this work is 488 nm. Therefore
parameters of the whole structure will be adjusted to excite and enhance BSWs at
this wavelength.
The multilayer structure is composed of titanium dioxide (TiO2) and aluminium
oxide (Al2O3) layers with refractive indices 2.4823 and 1.6071 respectively at λ =
488 nm. The multilayer is a stack of five periods of alternating layers TiO2 and Al2O3
with thicknesses 62 nm and 94 nm respectively, and TiO2 as a top terminating layer
with a thickness of 30 nm. In a first approximation the input waveguides are replaced
by side slab layers, intended to be fabricated in polymer, of refractive index n = 1.57.
The slot embedded between multilayer stacks is filled with air medium and has a
size of 50 nm.
23
(a) (b)
Incident light beam
Reflected light waves
Substrate
Polymer waveguide
Multilayer structures
slot
BSWs
sideslab
Λ
Incident light Reflected light
50 nm
Confined BSWs
slot
Multilayer
Structure
Polymer waveguide
9.18 μm
toplayers
slot
sideslab
Figure 4.1: Proposed structure showing (a) BSWs-based photonic integrated
structure and (b) the top view of the structure. Λ = a + b is one period of
the multilayer, where a = 62 nm and b = 94 nm are thicknesses of the TiO2
and Al2O3 layers respectively. The structure has five periods and a top layer
of TiO2 with the thickness of 30 nm.
4.2 Simulations based on TMM
Simulations were performed using TMM and FDTD methods. In TMM we were
able to demonstrate the presence of PBG, as well as, the presence and the location
of the excited BSWs.
The calculations are performed in simulations using the effective indices of the
materials. For this, we take into account the SiO2 wafer, and the cover which is air
with refractive index 1,the calculated effective indices for TM0-modes are as follows:
Polymer waveguide has effective index of 1.453, TiO2 layer has effective index of
2.225 and Al3O3 has an effective index of 1.465. We consider for all materials an
imaginary part of the refractive index of 0.001.
Figure 4.2 shows the spectral-angular reflectance in the wavelength range 300 nm
- 800 nm and incident angles 0◦ - 90◦. Using effective indices in the calculation, the
polymer-multilayer interface exhibits a critical angle of 43.6 degrees. Figure 4.2(a)
indicates the presence and location of a PBG of the multilayer structure. The PBG
spans between λ = 470 nm and 650 nm. Figure 4.2(b) is the reflectance after the
critical angle only, showing with a better contrast the BSW inside the PBG.
The BSWs are indicated by the the characteristic dips as shown on figure 4.3
both on the spectral and angular reflectances. For the case of spectral reflectance,
24
(a) (b)
Figure 4.2: Angular and spectral dependence of the reflection through the
structure: a) over a broad range and b) in the interesting zone.
the angle of incidence used for calculation is 54.5◦ and the wavelength range of
interest is from 300 nm to 450 nm. BSWs is located at wavelength 488 nm. For the
case of angular reflectance the range of angles used in the calculation are from 40◦
to 80◦. BSWs is seen to be excited at an angle 54.5◦.
It is to be noted that the geometrical parameters, i.e., the period, the thicknesses
of the layers, and the terminating layer, have been optimized thoroughly in order to
obtain a BSW at the desired wavelength.
(a) (b)
Figure 4.3: Diagrams showing (a) the spectral reflectance at an angle 54.5◦
with the characteristic dip located at 488 nm and (b) the angular reflectance
at the wavelength of 488 nm with the dip located at 54.5◦.
25
4.3 FDTD simulations
Finite difference time domain is a computational electromagnetic simulation tool
which solves time dependent Maxwell’s equations using explicit leapfrom time-
stepping scheme [52, 53]. The parameters defined above, i.e., thicknesses, effective
indices for TiO2, Al2O3, and polymer layers, number of periods for the multilayer
stack and, the size of the air slot embedded between multilayer stacks were used in
FDTD simulation.
Figure 4.4(a) shows the excited BSWs from the multilayer structure after the
illuminating beam is incident on a multilayer surface at an angle of incidence 55
degrees. Figure 4.4(b) shows the normalized intensity distribution on along the
x-axis at the position along z highlighted by a white dashed line.
(a) (b)
air
polymer
multilayerstack
BSWs
reflected lightincident light
BSWs
air polymer
multilayer stack
Figure 4.4: Single multilayer: (a) Amplitude distribution of Ex-field in the
plane of the structure. (b) Field intensity profile along x-axis at the position
along z-axis indicated by a dashed line.
Figure 4.5 shows the field amplitude in (a) and intensity distribution in (b) when
the two multilayer structures are put close to each other to form the slot in between.
The BSWs are confined and enhanced in the slot. One can remark that for the single
BSW, the maximum is 1, while for the double stack, the maximum is close to 3.
This proves the effect of the slot waveguide, without which the maximum intensity
would have been only twice the intensity of a single BSW structure.
The simulations was also performed on a slightly different design where 500 nm
wide polymer strips acted as input to guide the incoming light to the multilayers.
26
(a) (b)
BSWs
Multilayerstacks
(slot region)
polymer
polymer
BSWs
polymer
multilayer stacks
polymer
Figure 4.5: two multilayer stacks forming a 50 nm slot in between: (a)
Amplitude distribution of Ex-field in the plane of the structure. (b) Field
intensity profile along x-axis at the position along z-axis indicated by a dashed
line.
For instance figure 4.6 shows the field amplitude and intensity distribution when the
angle of incidence was 75◦.
(a) (b)
polymer layers
BSWs
Multilayer stacks
BSWsmultilayer stacks
polymer polymer
Figure 4.6: two multilayer stacks with a 500 nm wide polymer layer acting
as the input waveguide: (a) Amplitude distribution of Ex-field in the plane of
the structure. (b) Field intensity profile along x-axis at the position on the
z-axis indicated by a dashed line.
4.3.1 Influence of the slot width
The slot width ws represents the spacing between the two faces of the multilayers
bounding the slot. For this study we consider an infinite polymer layer with a slit
in the middle and the multilayer inside the slit. Two Gaussian waves illuminate the
27
multilayers from the positive and negative regions at angles θ and −θ corresponding
to BSWs excitation angle. In this case the slot width is adjusted from 0 nm to
200 nm. For BSWs study, the transverse electric field is more interesting. Figure
4.7 shows the results of the calculations performed by 2D-FDTD with a spatial
mesh size of 10 nm. Note that for the polymer layer we consider the effective index
approximation (light is guided in this layer), while for the materials constituting the
multilayer, i.e., TiO2 and Al2O3, the refractive index is taken into account as well
as an absorption of 10−4.
0
0.5
-0.5
1
-1
1.5
-1.5
2
-2
2.5
-2.5
x[µ
m]
0 20 40 60 80 100 120 140 160 180 200
ws [nm]
0
0.4
0.8
1.2
1.6
2
Inte
nsi
ty[a
.u.]
|E|
x
2
0 20 40 60 80 100 120 140 160 180 2000
0.2
0.4
0.6
0.8
1
1.2
1.4
1.6
1.8
2
Am
pli
tude
in t
he
slot
[a.u
.]
ws [nm]
Max
imum
enhan
cem
ent
a) b)
Multilayer
} Polymer
Increasingslot width
Figure 4.7: Influence of the slot width. (a) Field intensity as a function of
the slot width for 0 nm<ws<200 nm. (b) Maxima in the centre of the slot.
Figure 4.7(a) represents the electric field intensity as a function of the slot width
and the direction x (perpendicular to the slot). In this study θ = 64◦. One can first
remark fringes on both polymer sides corresponding to the interference between the
incident light and the reflection on the multilayer. The periodicity of these fringes
does not vary with ws because the multilayer, and therefore its reflection coefficient,
and the incident angle θ do not vary.
An obvious increase of the field intensity inside the slot is clearly visible when
ws increases. This enhancement can be quantified on figure 4.7 where the maxima
in the center of the slot as a function of ws are plotted. The maximum is obtained
when ws = 90 nm.
Three regions can be clearly identified: 1) ws = 0 nm corresponds to a thick
multilayer for which the reflection is relatively high, i.e., higher than a multilayer
with fewer amount of layers. No BSW are visible because the system is symmetric
and no total internal reflection can occur. 2) 0 nm < ws < 90 nm, is the region
28
where the BSW overlap is predominant and one can see that the intensity in the
slot increases, and the contrast of the fringes reduces. 3) For ws > 90 nm, one can
see a slow decrease of the field inside the slot corresponding to two separate BSWs.
One can also note, for region 2, that the intensity inside the multilayer increases,
which is a signature of the transmission of the amplitude through the different layers,
and thus of the frustrated TIR leading to the BSW. This region can therefore be
attributed to the BSW excitation region with slot enhancement.
4.3.2 Influence of the angle of incidence
For a slot width ws = 50 nm, we have performed FDTD calculations for incident
angle 60◦ < θ < 80◦. Results are presented in Fig. 4.8. In this representation of
the results, the fields have been normalized so they can be compared. The total
input field intensity remains the same in all the calculation. A part is reflected by
the multilayer and a part is partially transmitted through the multilayer to benefit
(or not, depending on θ) to the BSW. All fields are normalized by the amount
of intensity inside the polymer layer. From Fig. 4.8b), in particular, one can see
a maximum around θ = 78◦. This represent a significant variation compared to
the results obtained with the TMM. This can be explained by the more realistic
structure simulated here, but also by the relatively large spatial mesh, which does
not allow a good enough definition of the multilayer. And as we have seen earlier,
the BSW resonance depends drastically on all the geometrical parameters.
0
0.5
-0.5
1
-1
1.5
-1.5
2
-2
2.5
-2.5
x[µ
m]
60 62 64 66 68 70 72 74 76 78 80
q [nm]
0
0.2
0.4
0.6
0.8
1
Norm
aliz
ed i
nte
nsi
ty [
a.u.]
Am
pli
tude
in t
he
slot
[a.u
.]
a) b)
Multilayer
} Polymer
60 62 64 66 68 70 72 74 76 78 800
0.1
0.2
0.3
0.4
0.5
0.6
0.7
0.8
0.9
1
Max
imum
enhan
cem
ent
q [nm]
Figure 4.8: Influence of the angle of incidence. (a) Field intensity as a
function of the angle of incidence for 60◦ < θ < 80◦. (b) Maxima in the centre
of the slot.
29
4.4 Discussion and Analysis
In this section we present the discussion in general about the proposed design. More-
over it discusses on the results obtained from the simulations in chapter two.
4.4.1 Dielectric material selection
The objective for this proposed design is to be able to excite BSWs at wavelength
488nm which corresponds to the excitation wavelength for dyes. We have chosen
layers of TiO2 and Al2O3 for making a PhC because they are transparent in the
visible range. On top of that these materials are chemically, physically and thermally
stable. Moreover, polymer waveguide is also transparent in the visible spectrum.
Also, it allows the fast and inexpensive inexpensive fabrication.
4.4.2 PBG and BSWs
At normal incidence of the illumination beam towards the surface of a multilayer
structure in the given spectrum, PBG is seen to extend the wavelengths 470 nm-650
nm. This means that all the light waves with wavelengths belonging to the PBG,
will be reflected back and all light outside of that range will be fully transmitted.
PBG seems to be shifting to lower wavelengths with respect to increase in the angles
of incidence from normal as shown in figure 4.2(a). BSWs seem to be excited from
an angle of incidence 43◦ to around 75◦; see figure 4.2(b). However, BSW excited
for each different angle correspond to a different wavelength. This gives the ability
to select any wavelength of interest just by adjusting the angle of incidence of the
illumination beam. The parameters of the proposed design i.e. number of periods,
thicknesses of dielectric layers and indices have a direct effect on the location and
width of the PBG in the angular-spectral reflectance [51]. Not only that, the pa-
rameters also have effect on the magnitude and location of BSWs excited within the
PBG.
In this case, the wavelength of interest was 488nm, and so the proposed param-
eters make the PBG to be situated in wavelength range 470nm-650nm. BSWs at
wavelength 488nm are generated when the incident light beam needs hits the surface
of a multilayer at an incident angle of around 54.5 degrees. In figure 4.3a) BSWs are
indicated by a characteristic dip at at 488nm. In figure 4.3b) BSWs are indicated
by a characteristic dip on angle 54.5◦.
30
In FDTD simulations, this angle is slightly different because of reasons inherent
to the calculation method itself. Mainly, the mesh used in the code does not allow
all the layer thicknesses and the refractive indices are slightly different. Moreover, it
is to be noted that TMM is a very simplified method, showing as a result the ideal
case.
4.4.3 Sensitivity
Overall effective index and thickness of the PhC is 1.782 and 0.81 µm respectively.
Now, analytically from equation 2.29 we know that the field amplitude at the inter-
face in the slot region should be as n2H/n
2S times higher than that in the high index
medium. Therefore we get to see that the ratio of the optical intensity in the slot
with respect to intensity in the high index medium (total effective index), is 10.11:1
as the slot is filled with air medium with index 1. Hence the enhancement is 10.11
times as much as in the high index dielectric walls of the multilayer.
Angular reflectance of the structure by TMM as shown in figure 4.3 gives us the
normalized intensity transmittance of about 0.35/µm2 at an angle of incidence 54.5
degrees. From figure 4.5 we can see that the amplitude goes as high as 1.69/µm
which give rise to around 2.86/µm2 intensity.
From the FDTD simulation, sum of the field intensity along x-axis is around
103.5123/µm2 , and sum of intensity within the slot at the same point is 13.9948/µm2.
With respect to equation 2.32 we get the slot confinement factor of about 0.1352.
This value marks the maximum value for this configuration since the cover is as-
sumed to be air with a refractive index of 1. Once a cover medium is introduced
the confinement factor will decrease thus creating a sensing effect. Hence confine-
ment factor establishes a direct relationship to sensitivity of the optical slot-based
waveguide sensor.
31
Chapter V
Conclusions and future outlook
In this work simulations on photonic band gap (PBG) and Block surface waves
(BSWs) has been demonstrated. The proposed design configuration involves polmwer
waveguides which guides the light waves of the illuminating beam towards and away
from the multilayer surface. It also have a two sets of dielectric multilayer structures,
which all together make a nanometer size slot between them. This configuration is
designed to operate in the visible light wavelength range 300nm-800nm.
This thesis work focuses on combining two main ideas which are excitation of
BSWs at wavelength 488nm; and confinement and enhancement of the excited BSWs
in the slot. This will thus results into a BSWs-based polymer slot-waveguide pho-
tonic structure. Advantages experienced from the multilayer includes high wave-
length selectivity. This is contributed first by the presence of PBG where all wave-
lengths within the gap are rejected. Second, BSWs of a particular wavelength can
be excited with a different angle of incidence of the illumination beam. Hence it is
possible and easy to select the wavelength of an excited BSWs by simply adjusting
the angle of incidence of illuminating beam. In this work the PBG is available in the
wavelength range 470nm-650nm through the window 300nm-800nm for the case of
normal incidences. However as you increase the angle of incidence, the PBG shifts
to lower wavelengths. BSWs are excited within PBG for angles of incidence larger
than the critical angle which is around 43.5 degrees.
For the case of slot waveguide, the proposed configuration uses the discontinuity
conditions to confine and enhance the optical intensity in the embedded slot. High
confinement and enhancement of the optical intensity in the slot improves the sen-
sitivity of the device. Enhancement in the slot is also affected by the relationship
32
between the index in the high index medium to low index medium. The relationship
is such that field amplitude at the interface in the slot region is n2H/n
2S times as much
as the field amplitude in the high index medium. The BSWs on the surface have an
evanescent tail which decays exponentially as they propagate away from the surface.
Having a slot size which is much less than the decay length of the evanescent tail,
will results in the enhancement of the optical intensity of the fields. The size of the
slot used in the proposed design is 50nm and is filled with air which has an index
of 1. Taking into account both cases, the optical intensity in the slot has reached a
level of 2.86µm2.
On top of that, in comparison to SPPs, this proposed design will advantages
such as possessing both TE and TM-modes BSWs, lower absorption losses which
results to longer propagation lengths and sharper resonance dips. All this together
improves the sensitivity of the device.
At the moment fabrication was not possible as the electron beam which is to be
used for fabrication, was faulty. However in the near future we wish and are looking
forward to fabrication of the proposed device. Moreover, we recommend more study
of the spectral properties of the BSWs. Success in this would assist a big deal to
miniaturization of the proposed device.
Last but not least, fabrication and success of a proposed design will play a great
role to on-chip fabrication of photonic devices. Photonic device with this feature
could be applicable to sensing and biosensing.
33
References
[1] D. Ahuja and D. Parande, “Optical sensors and their applications,” Journal of
Scientific Research and Reviews 1, 060–068 (2012).
[2] R. Wang, A. Vasiliev, M. Muneeb, A. Malik, S. Sprengel, G. Boehm, M.-C.
Amann, I. Simonyte, A. Vizbaras, K. Vizbaras, et al., “III–V-on-Silicon Pho-
tonic Integrated Circuits for Spectroscopic Sensing in the 2–4 µm Wavelength
Range,” Sensors 17, 1788 (2017).
[3] V. Passaro, C. d. Tullio, B. Troia, M. L. Notte, G. Giannoccaro, and F. D.
Leonardis, “Recent advances in integrated photonic sensors,” Sensors 12,
15558–15598 (2012).
[4] A. Modinos and N. Stefanou, “Photonic crystals: a novel class of functional
materials.,”Materials Science (0137-1339) 23 (2005).
[5] J. D. Joannopoulos, S. G. Johnson, J. N. Winn, and R. D. Meade, Photonic
crystals: molding the flow of light (Princeton university press, 2011).
[6] A. Yariv and P. Yeh, Photonics: optical electronics in modern communications,
Vol. 6, (Oxford University Press New York, 2007).
[7] R. Rizzo, One dimensional photonic crystal for label-free and fluorescence sens-
ing application, PhD thesis (Politecnico di Torino, 2017).
[8] F. Seydou and T. Seppanen, “Photonic Crystals: from Theory to Practice,”
(2006).
34
[9] B. Wang, W. Dai, A. Fang, L. Zhang, G. Tuttle, T. Koschny, and C. M. Souk-
oulis, “Surface waves in photonic crystal slabs,” Physical Review B 74, 195104
(2006).
[10] T. Young and B. Rothrock, “Theory of frustrated total reflection involving
metallic surfaces,” J. Res. Natl. Bur. Stand. A 67, 115–125 (1963).
[11] Z. Voros and R. Johnsen, “A simple demonstration of frustrated total internal
reflection,”American journal of physics 76, 746–749 (2008).
[12] M. Qu and Z.-X. Huang, “Frustrated total internal reflection: resonant and
negative Goos–Hanchen shifts in microwave regime,” Optics Communications
284, 2604–2607 (2011).
[13] M. U. Khan and B. Corbett, “Bloch surface wave structures for high sensitiv-
ity detection and compact waveguiding,” Science and technology of advanced
materials 17, 398–409 (2016).
[14] E. Kretschmann and H. Raether, “Radiative decay of non radiative surface
plasmons excited by light,” Zeitschrift fur Naturforschung A 23, 2135–2136
(1968).
[15] R. Wang, Y. Wang, D. Zhang, G. Si, L. Zhu, L. Du, S. Kou, R. Badugu,
M. Rosenfeld, J. Lin, et al., “Diffraction-free Bloch surface waves,” ACS nano
11, 5383–5390 (2017).
[16] S. G. Johnson and J. D. Joannopoulos, Photonic crystals: the road from theory
to practice (Springer Science & Business Media, 2001).
[17] A. Delfan, Planar resonant structures for biosensing applications, PhD thesis
(University of Toronto (Canada), 2014).
[18] F. Frascella, S. Ricciardi, P. Rivolo, V. Moi, F. Giorgis, E. Descrovi, F. Miche-
lotti, P. Munzert, N. Danz, L. Napione, et al., “A fluorescent one-dimensional
photonic crystal for label-free biosensing based on Bloch surface waves,”Sensors
13, 2011–2022 (2013).
35
[19] R. Rizzo, M. Alvaro, N. Danz, L. Napione, E. Descrovi, S. Schmieder,
A. Sinibaldi, S. Rana, R. Chandrawati, P. Munzert, T. Schubert, E. Maillart,
A. Anopchenko, P. Rivolo, A. Mascioletti, E. Forster, F. Sonntag, M. Stevens M,
F. Bussolino, and F. Michelotti, “Bloch surface wave enhanced biosensor for the
direct detection of Angiopoietin-2 tumor biomarker in human plasma,”Biomed-
ical Optics Express 9, 529–542 (2018).
[20] A. Sinibaldi, C. Sampaoli, N. Danz, P. Munzert, F. Sonntag, F. Centola, A. Oc-
chicone, E. Tremante, P. Giacomini, and F. Michelotti, “Bloch Surface Waves
Biosensors for High Sensitivity Detection of Soluble ERBB2 in a Complex Bi-
ological Environment,”Biosensors 7, 33 (2017).
[21] M. Ballarini, F. Frascella, F. Michelotti, G. Digregorio, P. Rivolo, V. Paeder,
V. Musi, F. Giorgis, and E. Descrovi, “Bloch surface waves-controlled emission
of organic dyes grafted on a one-dimensional photonic crystal,”Applied Physics
Letters 99, 144 (2011).
[22] R. Badugu, K. Nowaczyk, E. Descrovi, and J. R. Lakowicz, “Radiative decay
engineering 6: Fluorescence on one-dimensional photonic crystals,” Analytical
biochemistry 442, 83–96 (2013).
[23] A. Angelini, E. Enrico, N. De Leo, P. Munzert, L. Boarino, F. Michelotti,
F. Giorgis, and E. Descrovi, “Fluorescence diffraction assisted by Bloch sur-
face waves on a one-dimensional photonic crystal,”New Journal of Physics 15,
073002 (2013).
[24] A. Sinibaldi, N. Danz, E. Descrovi, P. Munzert, U. Schulz, F. Sonntag, L. Do-
minici, and F. Michelotti, “Direct comparison of the performance of Bloch
surface wave and surface plasmon polariton sensors,” Sensors and Actuators B:
Chemical 174, 292–298 (2012).
[25] A. Sinibaldi, R. Rizzo, G. Figliozzi, E. Descrovi, N. Danz, P. Munzert,
A. Anopchenko, and F. Michelotti, “A full ellipsometric approach to opti-
cal sensing with Bloch surface waves on photonic crystals,”Optics express 21,
23331–23344 (2013).
36
[26] K.-E. Peiponen, R. Myllyla, and A. V. Priezzhev, Optical measurement tech-
niques: innovations for industry and the life sciences, Vol. 136, (Springer, 2009).
[27] J. B. Khurgin, “How to deal with the loss in plasmonics and metamaterials,”
Nature nanotechnology 10, 2 (2015).
[28] W. Kong, Y. Wan, W. Zhao, S. Li, and Z. Zheng, “Bloch-Surface-Polariton-
Based Hybrid Nanowire Structure for Subwavelength, Low-Loss Waveguiding,”
Applied Sciences 8, 358 (2018).
[29] Y. Li, T. Yang, Z. Pang, G. Du, S. Song, and S. Han, “Phase-sensitive Bloch
surface wave sensor based on variable angle spectroscopic ellipsometry,”Optics
Express 22, 21403–21410 (2014).
[30] R. Dubey, “Near-field characterization of Bloch surface waves based 2D optical
components,” PhD thesis, Ecole Polytechnique Federale de Lausanne (2017).
[31] E. Kadomina, E. Bezus, and L. Doskolovich, “Diffraction-grating-based Bloch
surface wave refractive index sensors,” in CEUR Workshop Proceedings, Vol.
1638 (2016), pp. 49–54.
[32] K. V. Sreekanth, S. Zeng, K.-T. Yong, and T. Yu, “Sensitivity enhanced biosen-
sor using graphene-based one-dimensional photonic crystal,” Sensors and Ac-
tuators B: Chemical 182, 424–428 (2013).
[33] M. Iqbal, Z. Zheng, and J. Liu, “Slot optical waveguides simulations and mod-
eling,” in Passive Microwave Components and Antennas (InTech, 2010).
[34] R. Sun, P. Dong, N.-n. Feng, C.-y. Hong, J. Michel, M. Lipson, and L. Kimer-
ling, “Horizontal single and multiple slot waveguides: optical transmission at
λ= 1550 nm,”Optics express 15, 17967–17972 (2007).
[35] Q. Xu, V. R. Almeida, R. R. Panepucci, and M. Lipson, “Experimental demon-
stration of guiding and confining light in nanometer-size low-refractive-index
material,”Optics letters 29, 1626–1628 (2004).
[36] P. Bettotti, A. Pitanti, E. Rigo, F. De Leonardis, V. Passaro, and L. Pavesi,
“Modeling of slot waveguide sensors based on polymeric materials,”Sensors 11,
7327–7340 (2011).
37
[37] R. Hussin, K. L. Choy, and X. H. Hou, “Growth of TiO2 Thin Films by Atomic
Layer Deposition (ALD),”Advanced Materials Research 1133, 352 (2016).
[38] K.-H. Choi, K. Ali, C. Y. Kim, and N. M. Muhammad, “Characterization of
Al2O3 Thin Films Fabricated at Low Temperature via Atomic Layer Deposition
on PEN Substrates,”Chemical Vapor Deposition 20, 118–124 (2014).
[39] V. Pore, A. Rahtu, M. Leskela, M. Ritala, T. Sajavaara, and J. Keinonen,
“Atomic layer deposition of photocatalytic TiO2 thin films from titanium
tetramethoxide and water,”Chemical Vapor Deposition 10, 143–148 (2004).
[40] M. Hiltunen, J. Hiltunen, P. Stenberg, S. Aikio, L. Kurki, P. Vahimaa, and
P. Karioja, “Polymeric slot waveguide interferometer for sensor applications,”
Optics Express 22, 7229–7237 (2014).
[41] P. Liao, Theory of Dielectric Optical Waveguides 2e (Academic press, 2012).
[42] K. Okamoto, Fundamentals of optical waveguides (Academic press, 2010).
[43] V. R. Almeida, Q. Xu, C. A. Barrios, and M. Lipson, “Guiding and confining
light in void nanostructure,”Optics letters 29, 1209–1211 (2004).
[44] N.-N. Feng, J. Michel, and L. C. Kimerling, “Optical field concentration in low-
index waveguides,” IEEE journal of Quantum Electronics 42, 885–890 (2006).
[45] C. A. Barrios, “Optical slot-waveguide based biochemical sensors,” Sensors 9,
4751–4765 (2009).
[46] F. Dell Olio and V. M. Passaro, “Optical sensing by optimized silicon slot
waveguides,”Optics Express 15, 4977–4993 (2007).
[47] G. Veldhuis, O. Parriaux, H. Hoekstra, and P. Lambeck, “Sensitivity enhance-
ment in evanescent optical waveguide sensors,” Journal of lightwave technology
18, 677 (2000).
[48] S. G. Johnson and J. D. Joannopoulos, “Introduction to photonic crystals:
Blochs theorem, band diagrams, and gaps (but no defects),” Photonic Crystal
Tutorial 1–16 (2003).
38
[49] S.-Y. Su and T. Yoshie, “Optical surface edge Bloch modes: low-loss
subwavelength-scale two-dimensional light localization,” Optics letters 37,
4398–4400 (2012).
[50] R. Dubey, E. Barakat, M. Hayrinen, M. Roussey, S. K. Honkanen, M. Kuittinen,
and H. P. Herzig, “Experimental investigation of the propagation properties of
bloch surface waves on dielectric multilayer platform,” Journal of the European
Optical Society-Rapid Publications 13, 5 (2017).
[51] J. Jagerska, “Dispersion properties of photonic crystals and silicon nanostruc-
tures investigated by Fourier-space imaging,” (2011).
[52] D. M. Sullivan, Electromagnetic simulation using the FDTD method (John
Wiley & Sons, 2013).
[53] V. P. Nobes, C. V. Ross, V. T. Namiki, and K. V. Takefumi, “Advanced methods
for electromagnetic simulation,” Fujitsu Sci. Tech. J 43, 524–531 (2007).
39