DATA SHEET
KAST-O-LITE 30 LI G
DESCRIPTION: Kast-O-Lite 30 LI G is a high alumina, lightweight insulating gun mix. It has a hydraulic set and is
suitable for use up to 1650C. It can be used as both a hot face and back-up lining. APPLICATIONS: Typical applications for Kast-O-Lite 30 LI G are aluminum furnace stacks, aluminum holding
furnace doors, reheat furnace discharge doors, carbon black furnace back-up linings, petrochem heaters, sulphur recovery unit back-up linings and air heaters.
CHEMICAL ANALYSIS - Calcined Basis
Silica SiO2 .................................................................................................. 35.5% Alumina Al2O3 .................................................................................................. 57.5% Iron Oxide Fe2O3 .................................................................................................. 0.7% Titania TiO2 .................................................................................................. 1.5% Lime - CaO .................................................................................................. 4.0% Magnesia - MgO .................................................................................................. 0.2% Alkalies Na2O + K2O .................................................................................................. 1.0%
NOTE The test data shown are based on average results of control tests and are subject to normal variation on
individual tests. These results cannot be taken as maximum or minimum requirements for specification purposes.
Ref: 166/4/9/08
KAST-O-LITE 30 LI G
PHYSICAL PROPERTIES
Gunned Data
MAXIMUM RECOMMENDED TEMPERATURE 1650C QUANTITY REQUIRED Net 1570 Kgs/m3 BULK DENSITY Kgs/m3 Cured and Then Dried at 105C 1550 - 1730 Heated at 820C 1490 - 1670 MAXIMUM TIME FROM ADDING WATER TO PLACING MATERIAL
10 Minutes
PERMANENT LINEAR CHANGE ASTM C113 AND C865 Expansion or Shrinkage Cured and Then Dried at 105C Heated at 820C and Then Cooled Heated at 1100C and Then Cooled Heated at 1370C and Then Cooled Heated at 1600C and Then Cooled