Vol.:(0123456789)1 3

Topics in Catalysis https://doi.org/10.1007/s11244-018-1024-0

ORIGINAL PAPER

Investigating the Influence of Fe Speciation on  N2O Decomposition Over Fe–ZSM-5 Catalysts

Nia Richards1 · Ewa Nowicka1 · James H. Carter1 · David J. Morgan1 · Nicholas F. Dummer1 · Stanislaw Golunski1 · Graham J. Hutchings1

© The Author(s) 2018

AbstractThe influence of Fe speciation on the decomposition rates of N2O over Fe–ZSM-5 catalysts prepared by Chemical Vapour Impregnation were investigated. Various weight loadings of Fe–ZSM-5 catalysts were prepared from the parent zeolite H-ZSM-5 with a Si:Al ratio of 23 or 30. The effect of Si:Al ratio and Fe weight loading was initially investigated before focussing on a single weight loading and the effects of acid washing on catalyst activity and iron speciation. UV/Vis spec-troscopy, surface area analysis, XPS and ICP-OES of the acid washed catalysts indicated a reduction of ca. 60% of Fe loading when compared to the parent catalyst with a 0.4 wt% Fe loading. The TOF of N2O decomposition at 600 °C improved to 3.99 × 103 s−1 over the acid washed catalyst which had a weight loading of 0.16%, in contrast, the parent catalyst had a TOF of 1.60 × 103 s−1. Propane was added to the gas stream to act as a reductant and remove any inhibiting oxygen species that remain on the surface of the catalyst. Comparison of catalysts with relatively high and low Fe loadings achieved comparable levels of N2O decomposition when propane is present. When only N2O is present, low metal loading Fe–ZSM-5 catalysts are not capable of achieving high conversions due to the low proximity of active framework Fe3+ ions and extra-framework ɑ-Fe species, which limits oxygen desorption. Acid washing extracts Fe from these active sites and deposits it on the surface of the catalyst as FexOy, leading to a drop in activity. The Fe species present in the catalyst were identified using UV/Vis spectroscopy and speculate on the active species. We consider high loadings of Fe do not lead to an active catalyst when propane is present due to the formation of FexOy nanoparticles and clusters during catalyst preparation. These are inactive species which lead to a decrease in overall efficiency of the Fe ions and consequentially a lower TOF.

Keywords Nitrous oxide · Iron zeolites · Fe–ZSM-5 · N2O decomposition · Acid washing · Iron species · Chemical vapour impregnation · UV/Vis · XPS

1 Introduction

Nitrous oxide (N2O) is a highly potent greenhouse gas, hav-ing a global warming potential of roughly 300, therefore the effect on the atmosphere is far more devastating than carbon dioxide [1–3]. N2O is produced by both natural and anthro-pogenic sources [4–6]. There are many sources of anthro-pogenic N2O such as sewage treatment, fuel and biomass combustion, industrial chemical processes, and contributions from the agriculture sector [4]. Agricultural processes lead to around 60% of the global emissions. The main industrial

processes that lead to the formation of N2O such as adipic and nitric acid production [1], with adipic acid production leading to around 80% of the global industrial emission of N2O (~ 10% total) [6, 7]. There are also small industrial uses such as hospital and dental surgeries [8]. Therefore it is extremely important to decompose N2O before it is released into the atmosphere. Decomposition of N2O takes place through dissociation into O2 and N2 (Eq. 1, [9, 10]).

There are many types of catalysts that can be used for N2O decomposition including perovskites [11–15], ceria-based catalysts [16–18], spinels [19–21] and iron contain-ing zeolites [22]. In the latter case, H-ZSM-5 has been fre-quently used as a support [23–25]. Xie et al. reported 100% conversion at 450 °C using 7.46 wt % Fe [26] while Wood

(1)2N2O → N

2+ O

2(Δ

rH◦(298) = −163 kJ mol

−1)

* Nia Richards RichardsN8@cardiff.ac.uk

1 Cardiff Catalysis Institute, School of Chemistry, Cardiff University, Cardiff CF10 3AT, UK

Topics in Catalysis

1 3

and co-workers [27] reported 84% conversion at 500 °C using an Fe/ZSM-5 catalyst with a loading of 0.57 wt%. Sobalik et al. showed that when using Ferrierite (FER) a Si:Al ratio of 8.5 outperformed Si:Al 10.5 when the same Fe loading is prepared for N2O decomposition [28]. Rauscher et al. reported that low Si:Al ratios are more effective for N2O decomposition catalysts [23]. Fe–ZSM-5 (Si:Al = 11.4) exhibited 95% conversion of N2O at 500 °C in contrast to Fe-BEA (93) achieving just 20% conversion of N2O at 575 °C [29]. The work of both these groups show that Si/Al ratio is an important factor for activity of an N2O decomposition catalyst.

Furthermore, it was shown that zeolites with different framework structures can be used for the decomposition of N2O with MFI (ZSM-5), beta (BEA) and ferrierite (FER) zeolites acting as supports for Fe [29–31]. Jisa et al. reported that low loaded Fe-FER was the most active, achieving 85% conversion at 450 °C [32]. FER had the lowest Si/Al ratio (8.6) out of all the zeolites tested compared to 15.5 for BEA and 13.4 for MFI. Supporting the earlier findings that a low Si:Al ratio is necessary for high N2O conversion. As the active Fe site is considered to form on the Al moiety in the zeolite framework, low Si:Al ratio zeolites can facilitate a higher concentration of active species [26].

The rate-limiting step in the decomposition of N2O is typ-ically the recombination of oxygen to form O2. Specifically, the dissociation of N2O on the active Fe species is facile and leaves an oxidised Fe active site. The surface oxygen must then recombine with another oxygen atom to form O2. It has been demonstrated that the addition of a reductant can facili-tate the abstraction of oxygen from the oxidised active site, significantly increasing the observed rate of N2O decomposi-tion at lower temperatures [27, 33–38]. Propane [26, 39–42] has been used as a reductant, in addition to ethane, methane and CO [26, 43–47].

Fe–ZSM-5 can be prepared by various ion-exchange methods, including via wet [48–51] or solid state [23, 50, 52], or sublimation [28, 32, 53–56] methodologies. Wet ion exchange includes the use of solvents, while solid state includes solventless mechanical mixing. Sublimation makes use of low evaporation temperature salts, usually FeCl3, as precursors. One challenge with this preparation method is that Cl− ions tend to remain after sublimation and a post-preparation washing step may be required. To combat this we have used a variation of this preparation method: chemi-cal vapour impregnation (CVI). In this method, Fe(acac)3 is used instead of FeCl3, as acetylacetonate precursors are easily removed under vacuum [57–59].

During the deposition of Fe on zeolites it is possible to form various types of Fe species such as framework Fe3+ (formed during isomorphous substitution), isolated Fe3+ or Fe2+ anchored to the zeolite framework by either Si–O–Fe or Al–O–Fe bridges, di-nuclear Fe–O–Fe species either in

the framework or in the channels, oligomeric Fe oxo-spe-cies, and both small nanoparticles and bulk FeOx particles [26, 59–61]. Determination of the active Fe species for N2O decomposition remains a challenge; thus far nano-particulate iron [26, 62] and extra-framework Fe have been suggested to catalyse the decomposition of N2O. However, most sug-gest that extra framework Fe is the active species due to enabling the formation of α-oxygen, [38, 63–68] which is formed by decomposing N2O over reversible redox α-Fe sites that switch between Fe2+ and Fe3+ [69, 70].

Treatment of catalysts with acids was reported to increase both their activity and stability, due to the removal of specta-tor Fe species (FexOy nano-particulates and clusters), with extended periods of time for acid washing not required to remove Fe species, with Fe being removed almost immedi-ately [59]. Due to the stability of the zeolites, acid washing does not greatly affect the pore channels and new mesopores were not created. During mild acid washing only a small quantity of surface Al is removed [71]. This stability implies that only the Fe species present will be affected by the acid washing and the zeolite will remain unchanged [72]. Alter-natively literature shows that steaming pre-treatments can be used to extract iron from the pores and into the extra-framework sites [53, 73–76], however we will not consider this technique in this work.

In this work we have investigated the importance of dif-ferent Fe species in Fe–ZSM-5 for the decomposition of N2O in the presence and absence of a reductant, propane. In addition to comparing different Fe loadings, we have evalu-ated the efficacy of acid washing to increase the efficiency of the Fe in the active catalyst and we have used UV/Vis spectroscopy to identify the different Fe species.

2 Experimental

2.1 Catalyst Preparation

A series of Fe–ZSM-5 catalysts (0.4, 1.25, 2.5 wt%) were prepared by CVI following the procedure described by Forde et al. [58]. Prior to catalyst preparation, ZSM-5 (23) and (30) (Zeolyst, 2 g) were dried under vacuum, and then placed into a Schlenk flask and evacuated at room temperature using a vacuum line, followed by heating at 150 °C for 1 h under continuous vacuum to remove any surface water species. ZSM-5 (23 or 30) (Zeolyst, 0.975–0.996 g) and iron acety-lacetonate Fe(acac)3 (Sigma Aldrich, 0.0253–0.1582 g) were placed into a glass vial and mixed by manual shaking. The obtained mixture was then transferred to a 50 mL Schlenk flask fitted with a magnetic stirrer bar and sealed. The flask was then evacuated at room temperature using a vacuum line followed by heating at 150 °C for 2 h under continuous vacuum conditions with stirring to induce sublimation and

Topics in Catalysis

1 3

deposition of the organometallic precursor onto the support. The flask was then brought up to atmospheric pressure with air and the sample removed and calcined at 550 °C in static air for 3 h.

Acid washing was performed by heating 10 v/v% HNO3(aq) (50 mL) to 50 °C, adding the catalyst (0.25 g) and stirring for 10 min. The solution was filtered and washed with deionised water (1 L g−1) followed by drying in an oven at 110 °C for 16 h. The samples obtained using this method were denoted as Acid Washed (AW).

2.2 Catalyst Testing

All reactions were performed at atmospheric pressure in a continuous-flow fixed-bed reactor. A 35 cm length of 1/4 in outer diameter stainless steel tubing was packed with 0.0625 g of catalyst that was sandwiched between two lay-ers of quartz wool. The reaction temperature was tested in the range 200–600 °C. The total flow for all reactions was 100 mL min−1 (GHSV of 45,000 h−1) and the gas feed was 5 v/v% N2O in He or 5 v/v% N2O, 5 v/v% C3H8 in He. All out-going gaseous products were analysed online using an Agi-lent 7890B Gas Chromatograph (GC) [columns: Hayesep Q (80–100 mesh, 1.8 m) MolSieve 5A (80–100 mesh, 2 m)] fitted with a thermal conductivity detector.

Here we define Turnover Frequency (TOF) based on the total moles of Fe present by ICP (Eq. 2) as it is a challenge to determine the concentration of surface active sites.

2.3 Catalyst Characterisation

Diffuse reflectance UV/Vis spectra was collected using an Agilent Cary 4000 UV/Vis spectrophotometer. Samples were scanned between 200 and 800 nm (150 nm min−1).

X-ray photoelectron spectroscopy (XPS) was performed on a Thermo Fisher Scientific K-alpha+ spectrometer. Sam-ples were analysed using a micro-focused monochromatic Al X-ray source (72 W) over an area of approximately 400 microns. Data were recorded at pass energies of 150 eV for

(2)

Turnover frequency(TOF) =mol of N

2O converted per second

total mol of Fe

survey scans and 40 eV for high resolution scan with 1 eV and 0.1 eV step sizes respectively. Charge neutralisation of the sample was achieved using a combination of both low energy electrons and argon ions. Data analysis was per-formed in CasaXPS using a Shirley type background and Scofield cross sections, with an energy dependence of -0.6.

Nitrogen adsorption isotherms were collected on a Micro-metrics 3Flex. Samples (0.050 g) were degassed (250 °C, 9 h) prior to analysis. Analyses was carried out at − 196 °C with P0 measured continuously. Free space was measured post analysis with He. Pore size analysis was carried out using DFT (N2-Cylindrical Pores-Oxide surface) via the Micrometrics 3Flex software.

Inductively Coupled Plasma – Optical Emission Spec-troscopy (ICP-OES) was performed by Exeter Analytical Services using HF digestion to get an accurate Fe loading. The sample was digested by Anton Paar Multiwave 3000 microwave with nitric and HF acids—then the HF was neu-tralised with the addition of boric acid. A reagent blank was carried out. An internal standard was added to the result-ing solutions, and the blank and sample were run against Fe standards by ICP-OES using Thermo Fisher iCAP Duo 7400.

3 Results and Discussion

Although iron-containing zeolites catalyse N2O decompo-sition, [24–27, 48–50, 72, 78] high reaction temperatures (> 450 °C) are typically required. The effect of varying the Si:Al ratio has been investigated previously [23, 29], the Fe:Al ratio is also an important parameter, as the maximum population of ɑ-Fe sites is directly proportional to the Al content of the zeolite [27, 50, 79]. Additionally, the presence of spectator or extraneous Fe species remains a challenge with respect to calculating real TOF values.

Fe–ZSM-5 Catalysts were prepared with Fe loadings of 0.4 and 1.25 wt% with two different Si:Al ratios. It is clear that the lower Si:Al ratio exhibits higher relative activity (Table 1).The addition of propane enhances the decomposi-tion of N2O by reducing the oxidised α-Fe sites that remain on the surface of the catalysts, preventing turnover of N2O

Table 1 Influence of Fe:Al ratio on 0.4 wt% Fe and 1.25 wt% Fe–ZSM-5 for N2O Decomposition both with and without propane present

Reaction Conditions: Total flow rate 100 mL min−1, 0.06 g catalyst, temperature range 400–600 °C, GHSV 45,000 h−1, either 5 v/v% N2O in He or 5 v/v% N2O, 5 v/v% C3H8 in He

Catalyst Fe:Al ratio N2O conversion at 550 °C without propane (%)

N2O conversion at 550 °C with propane (%)

0.4 wt% Fe–ZSM-5 (23) 0.072 20 900.4 wt% Fe–ZSM-5 (30) 0.092 12 811.25 wt% Fe–ZSM-5 (23) 0.224 35 811.25 wt% Fe–ZSM-5 (30) 0.288 29 68

Topics in Catalysis

1 3

[27, 33–38]. Due to the higher activity of the Fe–ZSM-5 (23) parent zeolite catalyst, further investigation was carried out on this Si:Al ratio zeolite [26].

In order to understand the effect of Si:Al ratio, UV/Vis spectroscopy of the various catalysts was performed (Fig. 1). When Fe is added to ZSM-5, four UV-active species can be differentiated. These absorb at: 200–250 nm (isolated Fe3+ in framework sites), 250–350 nm (isolated or oligomeric extra framework Fe species in zeolite channels), 350–450 nm (iron oxide clusters) and > 450 nm (large surface oxide species) [61, 80]. UV/Vis shows how higher Al content leads to high absorbance in the region 250–350 nm due to the presence of more extra-framework ɑ-Fe.

An additional Fe–ZSM-5 (23) catalyst was prepared with an Fe weight loading of 2.5% and contrasted to the 0.4 and 1.25 wt% catalysts. Figure 2 (closed symbols) illustrates the conversion of N2O over the four Fe–ZSM-5 (23) catalysts across the temperature range of 400–600 °C. The increas-ing weight loading of Fe in ZSM-5 increased the conver-sion of N2O, up to ca. 70% conversion over the 1.25 wt% catalyst, compared to 40% conversion over the 0.4 wt% Fe–ZSM-5 catalyst. Increasing the Fe loading to 2.5 wt% did not increase the N2O conversion further (Fig. 2). The 0.4% Fe catalyst exhibited limited activity despite the pres-ence of active extra-framework ɑ-Fe species. Therefore, when N2O decomposition takes place at these sites oxygen recombination is limited due to the oxygen species proximity

to combine to form molecular oxygen and, therefore, effec-tively blocking active sites.

High loadings of Fe lead to a high proportion of active framework and extra-framework species and due to the increased density of these species, the rate of oxygen recombination is higher, leading to a higher conversion. UV/Vis spectroscopy (Fig. 3) shows that there are a number of distinct Fe species present in the high loaded catalysts, with both FexOy nanoparticle and cluster species present, indicating that not all the Fe is efficiently utilised. There-fore, while a significant proportion of Fe is not necessarily active, there is a high concentration of extra-framework ɑ-Fe sites that can facilitate oxygen recombination and high N2O conversion.

When propane is added to the reaction feed-stream, the onset of activity shifts from 400 to 450 °C to a much lower temperature (Fig. 2 open symbols). In this context, propane acts as a reductant [26, 39, 40, 42, 81] and limits the forma-tion of site blocking oxygen species on the surface of the catalyst. The rate-limiting step without propane is oxygen recombination. Propane can activate the oxidised α-Fe site forming CO and CO2, which regenerates the active site and allows the reaction to proceed [27, 33–36]. At lower tem-peratures (< 500 °C) minor quantities of propene, ethene and ethane are produced, however, at higher temperatures the selectivity shifts to exclusively CO and CO2.

Comparing the reaction data (Fig. 2) to the UV/Vis spectroscopy (Fig. 3), it is possible to observe that the more active catalysts have a higher proportion of frame-work and extra framework ɑ-Fe species. This is the case in

Fig. 1 UV/Vis spectra of a series of Fe–ZSM-5 (23 or 30) catalysts and H-ZSM-5 support. Filled triangle framework Fe3+, filled dia-mond extra framework species, filled circle FexOy clusters, filled square large FexOy species. a H-ZSM-5 (23), b H-ZSM-5 (30), c 0.4 wt% Fe–ZSM-5 (23), d 0.4 wt% Fe–ZSM-5 (30), e 1.25 wt% Fe–ZSM-5 (23), f 1.25 wt% Fe–ZSM-5 (30)

Fig. 2 The influence of Fe weight loading on N2O conversion over Fe–ZSM-5 catalysts. Closed symbols: N2O present 5  v/v% N2O in He, open symbols: N2O + Propane present: 5  v/v% N2O, 5  v/v% C3H8 in He, circle 0.4  wt% Fe–ZSM-5 (23), square 1.25  wt% Fe–ZSM-5 (23), triangle 2.5 wt% Fe–ZSM-5 (23). Conditions; total flow rate 100 mL min−1, 0.06 g catalyst, temperature range 200–600  °C, GHSV 45,000 h−1

Topics in Catalysis

1 3

the 0.4 wt% Fe–ZSM-5 catalyst, where UV/Vis spectros-copy (Fig. 3) shows that framework and extra-framework species are present, with only a small absorbance due to FexOy nano-particles and clusters. By contrast, the poor activity of 1.25 wt% Fe–ZSM-5 correlates with the high proportion of nanoparticles and clusters of FexOy present,

which limit the number of Fe ions available to form the active species.

Peneau et al. demonstrated that using dilute HNO3, it is possible to remove excess iron and spectator species from the catalyst, which was investigated for the selective oxi-dation of ethane by H2O2 [59]. Here, 0.4 wt% Fe–ZSM-5 (23) was identified as a suitable catalyst formulation for acid washing, due to the presence of extra-framework ɑ-Fe spe-cies and minor levels of spectator FexOy nano-particulates and clusters. Previous work within the group has shown that it is difficult to distinguish between the Fe species present at higher weight loadings, therefore lower weight loadings were selected for acid washing to enable changes to be noted [82, 83]. After acid washing the calcined catalyst, ICP-OES analysis of the digested samples revealed that the weight loading had reduced to 0.16%. Figure 4a illustrates the activity of the as-prepared parent catalyst, the acid washed 0.4 wt% Fe–ZSM-5 catalyst, a 0.16 wt% Fe–ZSM-5 (pre-pared by CVI for comparison to the AW catalyst) as well as the analogous H-ZSM-5 catalysts, which were tested to con-firm that the support alone was not active for the reaction. The 0.4 wt% Fe–ZSM-5 (23) sample has an N2O conversion of 40% at 600 °C, however, over the acid washed catalyst the conversion was lower at 600 °C at 25%.

UV/Vis Spectroscopy (Fig. 3) supports the hypothesis that the decrease in activity observed after acid washing was due to the removal of framework Fe3+ ions which are extracted and deposited onto the surface of the catalyst as nanoparticles of FexOy (270 nm). UV/Vis Spectroscopy of 0.16 wt% Fe–ZSM-5 suggests that the Fe is present as framework Fe3+ and extra-framework ɑ-Fe species only

Fig. 3 UV/Vis spectra of a series of Fe–ZSM-5 (23) catalysts and H-ZSM-5 support. Filled circle framework Fe3+, filled diamond extra framework species, filled circle FexOy clusters, filled square Large FexOy species. a H-ZSM-5 (23), b H-ZSM-5 (23) AW, c 0.16  wt% Fe–ZSM-5 (23), d 0.4  wt% Fe–ZSM-5 (23), e 0.4  wt% Fe–ZSM-5 (23) AW, f 1.25 wt% Fe–ZSM-5 (23), g 2.5 wt% Fe–ZSM-5 (23)

Fig. 4 a Influence of Fe loading and acid washing over Fe–ZSM-5 catalysts for N2O conversion (closed symbols); Left pointed trian-gle 0.16 wt% Fe–ZSM-5 (23), circle 0.4 wt% Fe–ZSM-5 (23), right pointed triangle 0.4  wt% Fe–ZSM-5 (23) acid washed, diamond H-ZSM-5 (23), inverted triangle H-ZSM-5 (23) acid washed. Con-

ditions: 5  v/v% N2O in He, total flow rate 100  mL  min−1, 0.06  g catalyst, temperature range 400–600  °C, GHSV 45,000  h−1. b N2O conversion with propane present; open symbols. Conditions: 5 v/v% N2O, 5 v/v% C3H8 in He total flow rate 100 mL min−1, 0.06 g cata-lyst, temperature range 400–600 °C, GHSV 45,000 h−1

Topics in Catalysis

1 3

(Fig. 3). The lower activity of this catalyst further suggests that the proximity of the Fe sites to each other is crucial to achieve high activity in N2O decomposition. When propane is present (Fig. 4b) however, the relative proximity of active sites does not affect activity as propane can abstract oxygen from a single oxidised Fe site.

UV/Vis Spectroscopy was further used to understand the contrasting influence of the Fe loading concentration on N2O decomposition with and without propane. The spectrum of H-ZSM-5 (23) shows that framework Fe3+ species are pre-sent in the parent zeolite due to the absorbance at 220 nm (Fig. 3) and are likely to be impurities introduced during manufacture [84]. However, acid washing the H-ZSM-5 has the effect of re-dispersing the Fe species and forming Fe with extra-framework character. The 0.16 wt% Fe–ZSM-5 catalyst appears to possess both framework (< 250 nm) and extra-framework Fe (280 nm) only. Both the 1.25 wt% Fe–ZSM-5 and 2.5 wt% Fe–ZSM-5 catalysts contains all species present, with framework (< 250 nm), extra-frame-work Fe (280 nm), iron oxide nanoparticles (400 nm) and large clusters of iron oxide (> 450 nm). The spectrum of 0.4 wt% Fe–ZSM-5 (23) shows that there are three species of Fe present, framework Fe3+, extra-framework ɑ-Fe and large FexOy clusters. In contrast, the spectrum of 0.4 wt% Fe–ZSM-5 (23) acid washed sample shows that there are all four species of Fe present. Most notably, a reduced absorb-ance due to extra- framework ɑ-Fe being extracted and an increased absorbance from deposited FexOy nanoparticles and clusters.

Further characterisation was performed on the 0.4 wt% Fe–ZSM-5 and acid washed samples with XPS (Table 2). XPS measurements revealed a significant loss of Fe from the surface of the catalyst following acid washing, as the atomic % of Fe dropped from 2.02 to 0.28%, in addition to a decrease in the intensity of the Fe peak (Fig. 5). Considera-tion of the surface and bulk Fe content, as determined using XPS and ICP-OES showed a drop in the surface:bulk Fe ratio after acid washing (5.05 and 1.75 for the as-prepared and acid washed 0.4 wt% Fe–ZSM-5 catalysts, respectively). This confirmed that Fe was preferentially removed from the

surface of the catalyst rather than within the micro-porous channels. Furthermore, XPS showed that the binding energy of Fe is 711 eV in the calcined and acid washed catalysts, this alongside the satellite at 719 eV indicates that there is Fe3+ species present [85, 86]. After the addition of iron to the ZSM-5 the binding energy of both the Al and Si shift to slightly higher binding energies. Shifts in the Al spectrum from 102.9 eV in ZSM-5 to 103.4 eV in the calcined and acid washed catalyst, with Si shifting from 74.1 to 74.9 eV were observed in both catalysts. This shift to a higher bind-ing energy indicates that Fe has substituted into the lattice, [87–89] and corresponds with the UV/Vis spectroscopy as there is a larger absorption in the framework Fe3+ region indicating that Fe has substituted into the framework.

Surface area measurements for all catalysts remained constant at around 430 m2 g−1. This is consistent with the parent zeolite, which has a surface area of 423 m2 g−1. The micropore volume of H-ZSM-5 (23) is 0.167 cm3 g−1, this varies by ± 0.003 cm3 g−1 when iron is added and calcined

Table 2 Surface composition, Fe binding energies, surface area and micropore volume of a series of 0.4  wt% Fe–ZSM-5 (23) catalysts and H-ZSM-5 (23) support as reported by XPS analysis. Degas conditions—9 h at 250 °C prior to analysis

Catalyst Al 2p (at.%) Na 1s (at.%) O 1s (at.%) Si 2p (at.%) Fe 3p (at.%) Fe binding energy (eV)

Fe satellite binding energy (eV)

Surface area (m2 g−1)

Micropore volume (cm3 g−1)

H-ZSM-5 (23) 3.17 0.41 62.52 33.90 – – – 423 0.1670.4 wt% Fe–

ZSM-5 (23)3.77 0.12 49.35 44.74 2.02 711.2 719 437 0.169

0.4 wt% Fe–ZSM-5 (23) AW

3.22 0.28 49.87 46.63 0.28 711.0 719 428 0.164

Fig. 5 XPS data of the Fe region of 0.4 wt% Fe–ZSM-5 (23) calcined and acid washed

Topics in Catalysis

1 3

and then acid washed, (Table 2). The consistency of surface area and micropore volume during the catalyst preparation, calcination, and acid washing indicates that H-ZSM-5 (23) is stable under the pre-treatment conditions.

Due to the complexity in resolving the active Fe species, the TOF over the catalysts samples was calculated for N2O decomposition (Fig. 6a) using the total moles of Fe pre-sent in the sample. The low loaded Fe–ZSM-5 sample with 0.16 wt% Fe achieved a TOF of ca. 3.99 × 103 s−1 at 600 °C. The TOF of the acid washed H-ZSM-5 catalyst at 600 °C is an order of magnitude greater than the Fe based catalyst, when propane is present at 600 °C (Fig. 6b). This is due to the zeolite achieving 52% conversion (Fig. 6b) and only having trace amounts of iron present (245 ppm) typically in framework positions. This results in an extremely high TOF based on the ppm of iron present, however in reality a very low yield of nitrogen was observed. The activity of the H-ZSM-5 after acid washing is due to the formation of active extra-framework ɑ-Fe from Fe that has been removed from the framework [63, 64, 90]. The TOF of the acid washed catalyst was calculated to be 0.94 × 103 s−1, which compares to 0.69 × 103 s−1 achieved over the parent catalyst at 600 °C (Fig. 6a). When comparing the activity of the parent and acid washed catalyst in the presence of propane, the difference in activity is less significant and at higher temperatures (> 550 °C) the activity is comparable: both catalysts achieved 95% N2O conversion at 600 °C (Fig. 4b). In terms of TOF, the activity of the acid washed Fe–ZSM-5 catalyst was two and a half times that of the calcined equiva-lent catalyst (Fig. 6b). However, the TOF over the 0.16 wt% Fe–ZSM-5 catalyst is ca. 8.5 × 103 s−1 at > 550 °C, with

propane present. Park et al. reported a TOF of 1.8 × 103 s−1 for N2O decomposition at 550 °C using 1.96 wt% Fe–ZSM-5 (27) [50] compared to 2.59 × 103 s−1 achieved by 0.16% Fe–ZSM-5 (23) at 550 °C under similar conditions, demon-strating the superior activity of the catalyst prepared herein.

4 Conclusions

At low Fe loadings, Fe–ZSM-5 (23) catalysts prepared by CVI have two species of Fe present, Framework Fe3+ and isolated extra-framework FexOy in the pores, as shown by UV/Vis spectroscopy. However, when high-loading Fe–ZSM-5 is prepared by this method there are two addi-tional species of Fe present: FexOy nanoparticles and large clusters. The species of iron present in low loaded catalysts, framework and extra-framework Fe, are the active species for N2O decomposition, which lead to high conversion when propane is present, however without propane the activity of these catalysts is limited by slow oxygen desorption, due to the low proximity of active Fe sites. Therefore, the oxy-gen desorption step becomes rate limiting. At higher weight loadings with only N2O present the activity of the catalyst is increased as the density of the active sites increase, there-fore, increasing the rate of oxygen desorption. When acid washing is performed it is not possible to selectively remove the FexOy nanoparticles and clusters, but instead extra-framework Fe is extracted from the pores and deposited on the surface, leading to a decrease in conversion, but increase in TOF.

Fig. 6 a TOF of N2O decomposition over a series of Fe–ZSM-5 cat-alysts that have been calcined or acid washed, closed symbols. Left pointed triangle 0.16 wt% Fe–ZSM-5 (23), circle 0.4 wt% Fe–ZSM-5 (23), square 1.25 wt% Fe–ZSM-5 (23), triangle 2.5 wt% Fe–ZSM-5 (23) right pointed triangle 0.4  wt% Fe–ZSM-5 (23) AW. Condi-

tions: 5 v/v% N2O in He, total flow rate 100 mL min−1, 0.06 g cat-alyst, temperature range 400–600  °C, GHSV 45,000  h−1. b TOF of N2O decomposition with propane present, open symbols; Conditions: 5 v/v% N2O, 5 v/v% C3H8 in He, total flow rate 100 mL min−1, 0.06 g catalyst, temperature range 400–600 °C, GHSV 45,000 h−1

Topics in Catalysis

1 3

Acknowledgements ERC Funding ‘After the GoldRush’ code, ERC-AtG-291319. Cardiff Catalysis Institute would like to thank Exeter Analytical for the ICP-OES data. The authors would like to thank Dr. Robert Armstrong for fruitful discussion.

Open Access This article is distributed under the terms of the Crea-tive Commons Attribution 4.0 International License (http://creat iveco mmons .org/licen ses/by/4.0/), which permits unrestricted use, distribu-tion, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

References

1. Pérez-Ramírez J, Kapteijn F, Schöffel K, Moulijn JA (2003) For-mation and control of N2O in nitric acid production: where do we stand today? Appl Catal B 44:117–151. https ://doi.org/10.1016/S0926 -3373(03)00026 -2

2. Weimann J (2003) Toxicity of nitrous oxide. Best Pract Res Clin Anaesthesiol 17:47–61

3. Grace P, Barton L (2014) http://theco nvers ation .com/meet-n2o-the-green house -gas-300-times -worse -than-co2-35204 . In: http://theco nvers ation .com/meet-n2o-the-green house -gas-300-times -worse -than-co2-35204 . Accessed 12 June 2017

4. IPCC (2007) Climate change 2007: synthesis report. In: The Core Writing Team, Pachauri RK, Reisinger A (eds), Contribution of working groups I, II and III to the fourth assessment report of the intergovernmental panel on climate change. IPCC, Geneva, p 104

5. Li L, Xu J, Hu J, Han J (2014) Reducing nitrous oxide emissions to mitigate climate change and protect the ozone layer. Environ Sci Technol 48:5290–5297. https ://doi.org/10.1021/es404 728s

6. IPCC (2013) Climate Change 2013: The physical science basis. Contribution of working group I to the Fifth Assessment Report of the Intergovernmental Panel on Climate Change

7. UNEP (2013) Drawing down nitrous oxide to protect climate and the ozone layer. United Nations Environment Programme, Nairobi

8. Maroufi SS, Gharavi MJ, Behnam M, Samadikuchaksaraei A (2011) Nitrous oxide levels in operating and recovery rooms of Iranian hospitals. Iran J Public Health 40:75–79

9. Space Propulsion Group (2012) http://www.spg-corp.com/nitro us-oxide -safet y.html. In: http://www.spg-corp.com/nitro us-oxide -safet y.html

10. Kapteijn F, Rodriguez-Mirasol J, Moulijn JA (1996) Heteroge-neous catalytic decomposition of nitrous oxide. Appl Catal B 9:25–64. https ://doi.org/10.1016/0926-3373(96)90072 -7

11. Kumar S, Teraoka Y, Joshi AG et  al (2011) Ag promoted La0.8Ba0.2MnO3 type perovskite catalyst for N2O decomposition in the presence of O2, NO and H2O. J Mol Catal A 348:42–54. https ://doi.org/10.1016/j.molca ta.2011.07.017

12. Kumar S, Vinu A, Subrt J et al (2012) Catalytic N2O decom-position on Pr0.8Ba0.2MnO3 type perovskite catalyst for indus-trial emission control. Catal Today 198:125–132. https ://doi.org/10.1016/j.catto d.2012.06.015

13. Dacquin JP, Lancelot C, Dujardin C et al (2009) Influence of preparation methods of LaCoO3 on the catalytic performances in the decomposition of N2O. Appl Catal B 91:596–604. https ://doi.org/10.1016/j.apcat b.2009.06.032

14. Kartha KK, Pai MR, Banerjee AM et al (2011) Modified sur-face and bulk properties of Fe-substituted lanthanum titanates enhances catalytic activity for CO + N2O reaction. J Mol Catal A 335:158–168. https ://doi.org/10.1016/j.molca ta.2010.11.028

15. Russo N, Mescia D, Fino D et al (2007) N2O decomposition over perovskite catalysts. Ind Eng Chem Res 46:4226–4231. https ://doi.org/10.1021/ie061 2008

16. Zabilskiy M, Erjavec B, Djinović P, Pintar A (2014) Ordered mesoporous CuO-CeO2 mixed oxides as an effective catalyst for N2O decomposition. Chem Eng J 254:153–162. https ://doi.org/10.1016/j.cej.2014.05.127

17. Zhou H, Hu P, Huang Z et al (2013) Preparation of NiCe mixed oxides for catalytic decomposition of N2O. Ind Eng Chem Res 52:4504–4509. https ://doi.org/10.1021/ie400 242p

18. Zhou H, Huang Z, Sun C et al (2012) Catalytic decomposition of N2O over CuxCe1-xOy mixed oxides. Appl Catal B Environ 125:492–498. https ://doi.org/10.1016/j.apcat b.2012.06.021

19. Abu-Zied BM, Soliman SA, Abdellah SE (2015) Enhanced direct N2O decomposition over CuxCo1-xCo2O4(0.0 ≤ x ≤ 1.0) spinel-oxide catalysts. J Ind Eng Chem 21:814–821. https ://doi.org/10.1016/j.jiec.2014.04.017

20. Stelmachowski P, Maniak G, Kaczmarczyk J et al (2014) Mg and Al substituted cobalt spinels as catalysts for low temperature deN2O-evidence for octahedral cobalt active sites. Appl Catal B 146:105–111. https ://doi.org/10.1016/j.apcat b.2013.05.027

21. Amrousse R, Tsutsumi A, Bachar A, Lahcene D (2013) N2O catalytic decomposition over nano-sized particles of Co-substi-tuted Fe3O4 substrates. Appl Catal A 450:253–260. https ://doi.org/10.1016/j.apcat a.2012.10.036

22. Konsolakis MI (2015) Recent advances on nitrous oxide (N2O) decomposition over non–noble metal oxide catalysts: catalytic performance, mechanistic considerations and surface chemistry aspects. ACS Catal. https ://doi.org/10.1021/acsca tal.5b016 05

23. Rauscher M, Kesore K, Mönnig R et al (1999) Preparation of a highly active Fe-ZSM-5 catalyst through solid-state ion exchange for the catalytic decomposition of N2O. Appl Catal A 184:249–256. https ://doi.org/10.1016/S0926 -860X(99)00088 -5

24. Abu-Zied BM, Schwieger W, Unger A (2008) Nitrous oxide decomposition over transition metal exchanged ZSM-5 zeolites prepared by the solid-state ion-exchange method. Appl Catal B 84:277–288. https ://doi.org/10.1016/j.apcat b.2008.04.004

25. Sklenak S, Andrikopoulos PC, Boekfa B et al (2010) N2O decom-position over Fe-zeolites: structure of the active sites and the ori-gin of the distinct reactivity of Fe-ferrierite, Fe-ZSM-5, and Fe-beta. A combined periodic DFT and multispectral study. J Catal 272:262–274. https ://doi.org/10.1016/j.jcat.2010.04.008

26. Abdulhamid H, Fridell E, Skoglundh M (2004) Influence of the type of reducing agent (H2, CO, C3H6 and C3H8) on the reduc-tion of stored NOX in a Pt/BaO/Al2O3 model catalyst. Top Catal 30/31:161–168. https ://doi.org/10.1023/B:TOCA.00000 29745 .87107 .b8

27. Reimer RWoodB, Bell J AT (2002) Studies of N2O adsorption and decomposition on Fe–ZSM-5. J Catal 209:151–158. https ://doi.org/10.1006/jcat.2002.3610

28. Sobalik Z, Novakova J, Dedecek J et al (2011) Tailoring of Fe-ferrierite for N2O decomposition: on the decisive role of frame-work Al distribution for catalytic activity of Fe species in Fe-ferrierite. Microporous Mesoporous Mater 146:172–183. https ://doi.org/10.1016/j.micro meso.2011.05.004

29. Melián-Cabrera I, van Eck ERH, Espinosa S et al (2017) Tail gas catalyzed N2O decomposition over Fe-beta zeolite. On the promoting role of framework connected AlO6 sites in the vicinity of Fe by controlled dealumination during exchange. Appl Catal B 203:218–226. https ://doi.org/10.1016/j.apcat b.2016.10.019

30. Mauvezin M, Delahay G, Coq B et al (2001) Identification of iron species in Fe-BEA: influence of the exchange level. J Phys Chem B 105:928–935. https ://doi.org/10.1021/jp002 1906

31. Øygarden AH, Pérez-Ramírez J (2006) Activity of commercial zeolites with iron impurities in direct N2O decomposition. Appl Catal B 65:163–167. https ://doi.org/10.1016/j.apcat b.2006.03.002

Topics in Catalysis

1 3

32. Jíša K, Nováková J, Schwarze M et al (2009) Role of the Fe-zeolite structure and iron state in the N2O decomposition: comparison of Fe-FER, Fe-BEA, and Fe-MFI catalysts. J Catal 262:27–34. https ://doi.org/10.1016/j.jcat.2008.11.025

33. Guesmi H, Berthomieu D, Kiwi-Minsker L (2008) Nitrous oxide decomposition on the binuclear [Fe II (µ-O)(µ-OH)Fe II] center in Fe-ZSM-5 zeolite. J Phys Chem C 112:20319–20328. https ://doi.org/10.1021/jp808 044r

34. Sang C, Kim BH, Lund CRF (2005) Effect of NO upon N2O decomposition over Fe/ZSM-5 with low iron loading. J Phys Chem B 109:2295–2301. https ://doi.org/10.1021/jp048 884m

35. Hansen N, Heyden A, Bell AT, Keil FJ (2007) A reaction mecha-nism for the nitrous oxide decomposition on binuclear oxygen bridged iron sites in {Fe-ZSM-5}. J Phys Chem C 111:2092–2101. https ://doi.org/10.1021/jp065 574q

36. Bulushev DA, Kiwi-minsker L, Renken A (2004) Dynamics of N2O decomposition over Fe/ZSM-5 catalysts: effects of. 211:2004

37. Sun K, Xia H, Hensen E et al (2006) Chemistry of N2O decom-position on active sites with different nature: effect of high tem-perature treatment of Fe/ZSM-5. J Catal 238:186–195. https ://doi.org/10.1016/j.jcat.2005.12.013

38. Pirngruber GD (2003) The surface chemistry of N2O decomposi-tion on iron containing zeolites (I). J Catal 219:456–463. https ://doi.org/10.1016/S0021 -9517(03)00220 -3

39. Ohtsuka H, Tabata T, Okada O et al (1997) A study on selective reduction of NOx by propane on Co-Beta. Catal Lett 44:265–270

40. Ohtsuka H, Tabata T, Okada O et al (1998) A study on the roles of cobalt species in NOx reduction by propane on Co-Beta. Catal Today 42:45–50. https ://doi.org/10.1016/S0920 -5861(98)00075 -3

41. Van Den Brink RW, Booneveld S, Verhaak MJFM, De Bruijn FA (2002) Selective catalytic reduction of N2O and NOx in a single reactor in the nitric acid industry. Catal Today 75:227–232. https ://doi.org/10.1016/S0920 -5861(02)00073 -1

42. Centi G, Vazzana F (1999) Selective catalytic reduction of N2O in industrial emissions containing O2, H2O and SO2: behavior of Fe/ZSM-5 Catalysts. Catal Today 53:683–693. https ://doi.org/10.1016/S0920 -5861(99)00155 -8

43. Djéga-Mariadassou G, Fajardie F, Tempère JF et al (2000) A gen-eral model for both three-way and deNO(x) catalysis: dissociative or associative nitric oxide adsorption, and its assisted decomposi-tion in the presence of a reductant. Part I. Nitric oxide decomposi-tion assisted by CO over reduced or oxidized rhodiu. J Mol Catal A 161:179–189. https ://doi.org/10.1016/S1381 -1169(00)00334 -4

44. He L, Wang LC, Sun H et al (2009) Efficient and selective room-temperature gold-catalyzed reduction of nitro compounds with CO and H2O as the hydrogen source. Angew Chem Int Ed 48:9538–9541. https ://doi.org/10.1002/anie.20090 4647

45. Teramura K, Tanaka T, Ishikawa H et  al (2004) Photocata-lytic reduction of CO2 to CO in the presence of H2 or CH4 as a reductant over MgO. J Phys Chem B 108:346–354. https ://doi.org/10.1021/jp036 2943

46. Yogo K, Ihara M, Terasaki I, Kikuchi E (1993) Selective reduc-tion of nitrogen monoxide with methane or ethane on gallium ion-exchanged ZSM-5 in oxygen-rich atmosphere. Chem Lett 22:229–232. https ://doi.org/10.1246/cl.1993.229

47. Burch R, Loader PK (1994) Investigation of Pt/Al2O3, and Pd/Al2O3 & catalysts for the combustion of methane at low concen-trations. Appl Catal B 5:149–164

48. Pieterse JAZ, Booneveld S, Van Den Brink RW (2004) Evalu-ation of Fe-zeolite catalysts prepared by different methods for the decomposition of N2O. Appl Catal B 51:215–228. https ://doi.org/10.1016/j.apcat b.2004.02.013

49. Li L, Shen Q, Li J et al (2008) Iron-exchanged FAU zeolites: prep-aration, characterization and catalytic properties for N2O decom-position. Appl Catal A 344:131–141. https ://doi.org/10.1016/j.apcat a.2008.04.011

50. Park JH, Choung JH, Nam IS, Ham SW (2008) N2O decompo-sition over wet- and solid-exchanged Fe-ZSM-5 catalysts. Appl Catal B 78:342–354. https ://doi.org/10.1016/j.apcat b.2007.09.020

51. Chen B, Liu N, Liu X et al (2011) Study on the direct decomposi-tion of nitrous oxide over Fe-beta zeolites: from experiment to theory. Catal Today 175:245–255. https ://doi.org/10.1016/j.catto d.2011.04.010

52. Christoforou SC, Efthimiadis EA, Vasalos IA (2002) Catalytic conversion of N2O to N2 over metal-based catalysts in the pres-ence of hydrocarbons and oxygen. Catal Lett 79:137–147

53. Zhu Q, Hensen EJ, Mojet BL et al (2002) N2O decomposition over Fe/ZSM-5: reversible generation of highly active cationic Fe species. Chem Commun. https ://doi.org/10.1039/B2028 43C

54. Kucherov a V, Montreuil CN, Kucherova TN, Shelef M (1998) In situ high-temperature ESR characterization of FeZSM-5 and FeSAPO-34 catalysts in flowing mixtures of NO, C3H6, and O-2. Catal Lett 56:173–181

55. Lee H-T, Rhee H-K (1999) Stability of Fe/ZSM-5 De-NOx cata-lyst: effects of iron loading and remaining Brønsted acid sites. Catal Lett 61:71–76. https ://doi.org/10.1023/A:10190 44032 219

56. Lobree LJ, Hwang I, Reimer J, Bell AT (1999) An in situ infra-red study of NO reduction by C3H8 over Fe-ZSM-5. Catal Lett 63:233–240

57. Forde MM, Armstrong RD, Hammond C et al (2013) Partial oxi-dation of ethane to oxygenates using Fe- and Cu-containing ZSM-5. J Am Chem Soc 135:11087–11099. https ://doi.org/10.1021/ja403 060n

58. Forde MM, Armstrong RD, McVicker R et al (2014) Light alkane oxidation using catalysts prepared by chemical vapour impreg-nation: tuning alcohol selectivity through catalyst pre-treatment. Chem Sci. https ://doi.org/10.1039/c4sc0 0545g

59. Peneau V, Armstrong RD, Shaw G et al (2017) The low-tempera-ture oxidation of propane by using H2O2 and Fe/ZSM-5 catalysts: insights into the active site and enhancement of catalytic turnover frequencies. ChemCatChem 9:642–650. https ://doi.org/10.1002/cctc.20160 1241

60. Ates A, Hardacre C, Goguet A (2012) Oxidative dehydrogenation of propane with N2O over Fe-ZSM-5 and Fe–SiO2: influence of the iron species and acid sites. Appl Catal A 441–442:30–41. https ://doi.org/10.1016/j.apcat a.2012.06.038

61. Pérez-Ramírez J, Groen JC, Brückner A et al (2005) Evolution of isomorphously substituted iron zeolites during activation: com-parison of Fe-beta and Fe-ZSM-5. J Catal 232:318–334. https ://doi.org/10.1016/j.jcat.2005.03.018

62. Kapteijn F, Mul G, Moulijn J, Pérez-Ramírez J (2002) Highly active SO2-resistant ex -framework FeMFI catalysts for direct N2O decomposition. Appl Catal B 35:227–234

63. Sun K, Zhang H, Xia H et al (2004) Enhancement of α-oxygen formation and N2O decomposition on Fe/ZSM-5 catalysts by extraframework Al. Chem Commun. https ://doi.org/10.1039/B4088 54A

64. Hensen EJM, Zhu Q, Hendrix MMRM et al (2004) Effect of high-temperature treatment on Fe/ZSM-5 prepared by chemical vapor deposition of FeCl3: I. Physicochemical characterization. J Catal 221:569–583. https ://doi.org/10.1016/j.jcat.2003.09.024

65. Pérez-Ramírez J (2003) Active site structure sensitivity in N2O conversion over FeMFI zeolites. J Catal 218:234–238. https ://doi.org/10.1016/S0021 -9517(03)00087 -3

66. Sobolev V (1993) Catalytic properties of ZSM-5 zeolites in N2O decomposition: the role of iron. J Catal 139:435–443

67. Panov GI, Kharitonov AS, Sobolev VI (1993) Oxidative hydroxy-lation using dinitrogen monoxide: a possible route for organic synthesis over zeolites. Appl Catal A 98:1–20. https ://doi.org/10.1016/0926-860X(93)85021 -G

68. Panov GI, Sobolev VI, Kharitonov AS (1990) The role of iron in N2O decomposition on ZSM-5 zeolite and reactivity of the

Topics in Catalysis

1 3

surface oxygen formed. J Mol Catal 61:85–97. https ://doi.org/10.1016/0304-5102(90)85197 -P

69. Panov GI, Starokon EV, Pirutko LV et al (2008) New reaction of anion radicals O-with water on the surface of FeZSM-5. J Catal 254:110–120. https ://doi.org/10.1016/j.jcat.2007.12.001

70. Parfenov MV, Starokon EV, Pirutko LV, Panov GI (2014) Qua-sicatalytic and catalytic oxidation of methane to methanol by nitrous oxide over FeZSM-5 zeolite. J Catal 318:14–21. https ://doi.org/10.1016/j.jcat.2014.07.009

71. Fernandez C, Stan I, Gilson JP et al (2010) Hierarchical ZSM-5 zeolites in shape-selective xylene isomerization: role of mesopo-rosity and acid site speciation. Chemistry 16:6224–6233. https ://doi.org/10.1002/chem.20090 3426

72. Wu M, Wang H, Zhong L et al (2016) Effects of acid pretreatment on Fe-ZSM-5 and Fe-beta catalysts for N2O decomposition. Cui-hua Xuebao/Chinese J Catal 37:898–907. https ://doi.org/10.1016/S1872 -2067(15)61052 -X

73. Sun K, Zhang H, Xia H et al (2004) Enhancement of α-oxygen formation and N2O decomposition on Fe/ZSM-5 catalysts by extraframework Al. Chem Commun 216:2480–2481. https ://doi.org/10.1039/B4088 54A

74. Dubkov KA, Ovanesyan NS, Shteinman AA et al (2002) Evolu-tion of iron states and formation of α-sites upon activation of FeZSM-5 zeolites. J Catal 207:341–352. https ://doi.org/10.1006/jcat.2002.3552

75. Ribera A, Arends IWCE, De Vries S et al (2000) Preparation, characterization, and performance of FeZSM-5 for the selective oxidation of benzene to phenol with N2O. J Catal 195:287–297. https ://doi.org/10.1006/jcat.2000.2994

76. Panov GI, Uriarte AK, Rodkin MA, Sobolev VI (1998) Generation of active oxygen species on solid surfaces. Opportunity for novel oxidation technologies over zeolites. Catal Today 41:365–385. https ://doi.org/10.1016/S0920 -5861(98)00026 -1

77. Forde MM, Kesavan L, Bin Saiman MI et al (2014) High activity redox catalysts synthesized by chemical vapor impregnation. ACS Nano 8:957–969. https ://doi.org/10.1021/nn405 757q

78. Li G, Pidko EA, Filot IAW et al (2013) Catalytic properties of extraframework iron-containing species in ZSM-5 for N2O decomposition. J Catal 308:386–397. https ://doi.org/10.1016/j.jcat.2013.08.010

79. Wood BR, Reimer JA, Bell AT et al (2004) Nitrous oxide decom-position and surface oxygen formation on Fe-ZSM-5. J Catal 224:148–155. https ://doi.org/10.1016/j.jcat.2004.02.025

80. Kumar MS, Perez-Ramirez J, Debbagh MN et al (2006) Evidence of the vital role of the pore network on various catalytic conver-sions of N2O over Fe-silicalite and Fe-SBA-15 with the same iron constitution. Appl Catal B 62:244–254. https ://doi.org/10.1016/j.apcat b.2005.07.012

81. Van Den Brink RW, Booneveld S, Verhaak MJFM, De Bruijn FA (2002) Selective catalytic reduction of N2O and NOx in a single reactor in the nitric acid industry. Catal Today. 75(1–4):227–232

82. Chow YK, Dummer NF, Carter JH et al (2018) A kinetic study of methane partial oxidation over Fe-ZSM-5 using N2O as an oxidant. ChemPhysChem 19:402–411. https ://doi.org/10.1002/cphc.20170 1202

83. Xu J, Armstrong RD, Shaw G et al (2016) Continuous selec-tive oxidation of methane to methanol over Cu- and Fe-modified ZSM-5 catalysts in a flow reactor. Catal Today 270:93–100. https ://doi.org/10.1016/j.catto d.2015.09.011

84. Hammond C, Forde MM, Ab Rahim MH et al (2012) Direct cata-lytic conversion of methane to methanol in an aqueous medium by using copper-promoted Fe-ZSM-5. Angew Chem Int Ed 51:5129–5133. https ://doi.org/10.1002/anie.20110 8706

85. Biesinger MC, Payne BP, Grosvenor AP et al (2011) Resolving surface chemical states in XPS analysis of first row transition met-als, oxides and hydroxides: Cr, Mn, Fe, Co and Ni. Appl Surf Sci 257:2717–2730. https ://doi.org/10.1016/j.apsus c.2010.10.051

86. Graat PCJ, Somers MAJ (1996) Simultaneous determination of composition and thickness of thin iron-oxide films from XPS Fe 2p spectra. Appl Surf Sci 100–101:36–40. https ://doi.org/10.1016/0169-4332(96)00252 -8

87. Södergren S, Siegbahn H, Rensmo H et al (1997) Lithium interca-lation in nanoporous anatase TiO2 studied with XPS. J Phys Chem B 101:3087–3090. https ://doi.org/10.1021/jp963 9399

88. Chen W, Xu Q, Hu YS et al (2002) Effect of modification by poly(ethylene oxide) on the reversibility of insertion/extraction of Li+ ion in V2O5 xerogel films. J Mater Chem 12:1926–1929. https ://doi.org/10.1039/b2030 56j

89. Stakheev AY, Shpiro ES, Apijok J (1993) XPS and XAES study of titania-silica mixed oxide system. J Phys Chem 97:5668–5672. https ://doi.org/10.1021/j1001 23a03 4

90. Pérez-Ramírez J, Kapteijn F, Brückner A (2003) Active site struc-ture sensitivity in N2O conversion over FeMFI zeolites. J Catal 218:234–238. https ://doi.org/10.1016/S0021 -9517(03)00087 -3