Electronic Supplementary information (ESI)
For
Oxidation-driven self-assembly gives access to high -nuclearity molecular
copper vanadium oxide clusters
Johannes Forster, Benedikt Rösner, Rainer H. Fink, Leanne C. Nye, Ivana
Ivanovic-Burmazovic, Katharina Kastner, Johannes Tucher and Carsten Streb*
Department Chemistry and Pharmacy, Friedrich-Alexander-University Erlangen-
Nuremberg, Egerlandstr. 1, 91058 Erlangen, Germany.
*Email: [email protected]
1. Instrumentation
X-ray diffraction: Single-crystal X-ray diffraction studies were performed on a Nonius
Kappa CCD Single-crystal X-ray diffractometer equipped with a graphite monochromator
using MoKα radiation (wavelength λ(Mo-kα) = 0.71073Å).
UV-Vis spectroscopy: UV-Vis spectroscopy was performed on a Shimadzu UV-
2401PC spectrophotometer, Varian Cary 50 spectrophotometer or Varian Cary 5G
spectrophotometer equipped with a Peltier thermostat. All systems were used with
standard cuvettes (d = 10.0 mm).
Thermogravimetry analysis (TGA): TGA was performed on a Setaram Setsys CS Evo,
30-1000°C @ 10K/min, 200 mL/min He, Graphite crucib le 0.5 mL.
Atomic absorption spectroscopy: Atomic absorption spectroscopy analysis was
performed on a Perkin Elmer 5100 PC spectrometer.
FT-IR spectroscopy: FT-IR spectroscopy was performed on a Shimadzu FT-IR-8400S
spectrometer. Samples were prepared as KBr pellets. Signals are given as
wavenumbers in cm-1 using the following abbreviations: vs = very strong, s = strong, m =
medium, w = weak and b = broad.
Elemental analysis: Elemental analysis was performed on a Euro Vector Euro EA 3000
Elemental Analyzer.
Mass spectrometry (MS) : MS measurements were performed on a UHR-TOF Bruker
Daltonik (Bremen, Germany) maXis, an ESI-ToF MS capable of resolution of at least
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
40,000 FWHM. Detection was in negative-ion mode, the source voltage was 4 kV, first
skimmer potential: -33 V. The flow rates were 500 µL/hour. The drying gas (N2) was held
at 180 °C. The machine was calibrated prior to every experiment via direct infusion of
the Agilent ESI-TOF low concentration tuning mixture, which provided an m/z range of
singly charged peaks up to 2700 Da.
Cyclic Voltammetry (CV): CV was performed using an Ivium CompactStat
potentiometer. Working electrode: carbon disc electrode, reference electrode, counter
electrode: Pt wire. Dry solvents were used with nBu4NPF6 as the electrolyte. Scan rates
were between 20 - 100 mV/s
General remarks: All chemicals were purchased from Sigma Aldrich or ACROS and
were of reagent grade. The chemicals were used without further purification unless
stated otherwise. (nBu4N)6[H6V18O42] was prepared according to reference S1,
(nBu4N)4[V4O12] was prepared according to reference S2.
2. Synthetic section:
2.1. Synthesis of {Cu6V30}: (nBu4N)4[Cu6V30O82(NO3)2(CH3CN)6] x solvent:
(nBu4N)6[H6V18O42] (200 mg, 66.4 µmol) and Cu(NO3)2·3H2O (101 mg, 418 µmol) were
dissolved in 15 ml acetonitrile. The resulting solution was vigorously stirred for one hour
at ambient temperature. Diffusion of diethyl ether into the reaction mixture over a period
of ca. 1 week gave brown needle crystals, which were suitable for X-ray diffraction.
Yield: 117 mg (25.7 µmol, 36.8 % based on Cu).
Elemental analysis for the dried compound (all acetonitrile molecules removed)
C64Cu6H144N6O88V30 in wt.-% (calcd.): C 18.17 (17.81), H 3.93 (3.36), N 1.53 (1.95), Cu
8.97 (8.83), V 35.63 (35.40).
Characteristic UV-Vis signals (in acetonitrile): λmax1 = 769 nm (shoulder), ε = 3.22 x 102
M-1 cm-1. λmax2 = 224 nm, ε = 1.35 x 106 M-1 cm-1
2.2. Reaction under inert atmosphere: The reaction under N2 atomsphere was
conducted as described above (2.1.), but de-aereated acetonitrile was used
under nitrogen to exclude oxygen / air from the reaction.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
2.3. High quality single crystal synthesis of {Cu 6V30}:
(nBu4N)4[V4O12] (99 mg, 72.5 µmol), (nBu4N)6[H6V18O42] (225 mg, 73.8 µmol) and
Cu(NO3)2·3H2O (235 mg, 972.6 µmol) were dissolved in 13 ml acetonitrile. The resulting
solution was vigorously stirred for one hour at ambient temperature. Diffusion of diethyl
ether into the clear reaction mixture gave brown needle crystals, which were suitable for
X-ray diffraction. Yield: 121 mg (26.5 µmol, 16.4 % based on Cu).
2.4. Synthesis of [VO(dmso)5](NO3)2: (nBu4N)6[H6V18O42] (298 mg, 97.7 µmol) was dissolved in a dimethyl sulfoxide/water
mixture (3 ml, 9:1, v:v). To this concentrated nitric acid (65 wt. %, 460 µl, 6.74 mmol)
were slowly added. The emerald green solution was stirred at room temperature over
night. Diffusion crystallizations were set up using ethyl acetate as diffusion solvent and
light blue single crystals were obtained as the only solid product. The crystals were
washed with ethyl acetate and dried under vacuum. Yield: 450 mg (775 µmol, 44.2 %
based on V).
Elemental analysis for C10H30N2S5VO11 (Mw: 581.62 g/mol) in wt.-% (calcd.): C 20.75
(20.65), H 5.11 (5.19), N 4.79 (4.82), S 27.96 (27.57).
2.5. Oxidative fragmentation of [H6V18O42]6- and formation of [VIV
2VV
8O26]4-
(nBu4N)6[H6V18O42] (250 mg, 81.7 µmol) was dissolved in a N,N’dimethyl formamide (5
ml). The solution was exposed to air and over a period several days, the solution colour
changed from deep green to deep purple. Crystallization of the solution gave deep
purple rod crystals. Single-crystal XRD analysis, elemental analysis and FT-IR showed
that the material obtained corresponds to [nBu4N]4[VIV
2VV
8O26].
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
2.6. IR-spectroscopy of {Cu6V30}
Figure S 1: FT-IR spectrum of {Cu 6V30} showing the characteristic V-O vibrational modes in the fingerprint region < 1000 cm-1 and the characteristic nitrate-based N-O stretching vibration at 1383 cm-1.S3
2.5. UV-Vis spectroscopy
Figure S 2 : UV-Vis spectra of the mixed-valent (nBu4N)4[V10O26] cluster (= {VIV2V
V8},
red), the fully VIV-based (nBu4N)6[H6V18O42] (= {VIV18}, green) and {Cu 6V30} (black).
3. Crystallographic information
Single-Crystal Structure Determination: Suitable single crystals of the respective
compound were grown and mounted onto the end of a thin glass fibre using Fomblin oil.
X-ray diffraction intensity data were measured at 150 K on a Nonius Kappa CCD
diffractometer [λ(Mo-Kα) = 0.71073 Å] equipped with a graphite monochromator.
Structure solution and refinement was carried out using the SHELX-97 packageS4 via
WinGX.S5 Corrections for incident and diffracted beam absorption effects were applied
using empiricalS6 methods. Structures were solved by a combination of direct methods
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
and difference Fourier syntheses and refined against F2 by the full-matrix least-squares
technique. Crystal data, data collection parameters and refinement statistics are listed in
Table S1. These data can be obtained free of charge via
www.ccdc.cam.ac.uk/conts/retrieving.html or from the Cambridge Crystallographic Data
Center, 12, Union Road, Cambridge CB2 1EZ; fax:(+44) 1223-336-033; or
[email protected]. CCDC reference numbers 890307 (1) and 890308 (2)
Table S1: Summary of the crystallographic information
Compound 1 Compound 2
Formula C76H162Cu6N12O88.67V30 C10H30N2O12S5V1
Mr g mol –1 4561.64 581.60
crystal system Trigonal Triclinic
space group P3121 P-1
a [Å] 20.411(3) 9.4145(19)
b [Å] 20.411(3) 11.119(2)
c [Å] 40.340(5) 13.183(2)
α [º] 90 67.27(3)
β [º] 90 77.71(2)
γ [º] 120 89.25(3)
V [Å 3] 14554 (3) 1240.0(4)
ρcald [g cm -3] 1.511 1.558
Z 3 2
µ(MoKα) mm -1 2.084 0.875
T [K] 150(2) 150(2)
no. rflns (measd) 167266 13758
no. rflns (unique) 19763 4904
no. params 839 299
R1 (I>2σ(I) 0.0479 0.0276
wR2 (all data) 0.1222 0.0721
GooF 1.039 1.144
Max/min resd e 0.706/-0.453 0.474/-0.280
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
Figure S 3: ORTEP-plot of compound 1, (nBu4N)4[Cu6V30O82(NO3)2(CH3CN)6],
probability ellipsoids given at 50 %. The carbon atoms of the (nBu4N)+ tetra-n-
butylammonium cation based around N6 were refined isotropically due to strong
structural disorder. One ligand acetonitrile molecule was heavily disordered and was
refined isotropically. The metal oxide cluster atoms were refined fully anisotropically.
This allowed refinement of the structure to satisfactory R values.
Figure S 4: ORTEP-plot of compound 2, [VO(dmso)5](NO3)2, probability ellipsoids given
at 50 %. All non-hydrogen atoms were refined anisotropically.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
4. Mass spectrometry
Figure S 5: Negative mode high resolution ESI mass spectrum of {Cu 6V30} ([{Cu 6V30}] ca. 9 x 10-5 M in acetonitrile). Assigned peaks are marked with an asterisk (*)
Table S2: Peak assignments for the ESI mass spectrum of {Cu 6V30}
recorded m/z calculated m/z peak assignment
280.79[a] 280.79S8 [V6O16]2-
371.72[a] 371.72S8 [V8O21]2-
462.65[a] 462.65S8 [V5O13]-
644.52[a] 644.52S8 [V7O18]-
836.34[b] 836.36 [Cu6V30O82(NO3)2]4-
941.77 941.77 (nBu4N)2[Cu5V30O82(NO3)2]4-
1016.24[c] 1016.23 (nBu4N)2[CuV15O40(NO3)(H2O)]2-
1195.88[b] 1195.91 (nBu4N)1[Cu6V30O82(NO3)2]3-
1336.46[b] 1336.46 (nBu4N)3[Cu5V30O82(NO3)2]3-
1476.31[b] 1476.34 (nBu4N)5[Cu4V30O82(NO3)2]3-
[a] Fragmentation product; [b] full {Cu6V30} cluster anion; [c] {CuV15} sub-shell
*
*
*
*
* *
* * *
*
* *
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
Figure S 6: Experimental and simulated ESI mass spectrum of the full cluster anion (nBu4N)1[Cu6V30O82(NO3)2]
3- at m/z = 1195.88.
Figure S 7: Experimental and simulated ESI mass spectrum of the full cluster anion [Cu6V30O82(NO3)2]
4- observed at m/z = 836.34.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
Figure S 8: Experimental and simulated ESI mass spectrum of a {CuV15} sub-shell
(nBu4N)2[CuV15O40(NO3)(H2O)]2- observed at m/z = 1016.24 m/z.
Figure S 9: Experimental an simulated ESI mass spectrum showing the loss of one CuII
centre from the cluster shell: (nBu4N)1[Cu5V30O82(NO3)2]4- observed at m/z = 941.77.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
5. Thermogravimetric analysis
Figure S 10: Thermogravimetric analysis of {Cu 6V30} (performed under air, heating rate:
10 ˚ C /min) showing the loss of adsorbed solvent and water up to T= 200 ˚ C (weight
loss: 8.9 wt.-%) and decomposition of the organic nBu4N+ cations T= 200 - 350 ˚ C
(weight loss: 22.8 wt.-%, calculated: xy 21.2 wt.-%). At temperatures above 350 ˚ C,
further decomposition of compound 1 is observed.
6. Cyclic Voltammetry
Figure S 11: Cyclovoltammogram of {Cu 6V30} ([{Cu 6V30} ca. 10 mM) in DMF containing
0.1 M (nBu4N)PF6. Scan rate: 50 mV/s, rest potential: -0.4 V.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
7. Redox titration
Figure S 12: Redox-titration of {Cu 6V30} in DMF ([{Cu 6V30}] = 0.1 M) using cerium
ammonium nitrate (CAN, 0.05 M) as the oxidant.
8. NEXAFS spectroscopy
Samples for NEXAFS spectroscopy were prepared by suspending the material under
investigation in a small amount of ethanol and depositing the suspension on the support.
Samples were dried under vacuum to remove excess solvent.
NEXAFS spectroscopy on {Cu6V30}, {V10} and {V18} clusters was performed as described
in the experimental section of the paper. The spectra were normalized to define the pre-
edge region as 0 and the edge jump as 1. It has to be noted that this normalization
contains the vanadium L3-edge, the vanadium L2-edge as well as the oxygen K-edge.
The spectra were fitted to a sigmoidal function for the edge jump and Gaussian functions
for the near-edge resonances to chi-square values of 0.06, 0.04 and 0.023 (due to a
higher noise level). The energy position of the first fitted Gaussian was taken as a direct
measure for the oxidation state of the vanadium contained in the cluster as known from
the literature.S9 It has been found that the {Cu6V30} cluster shows the first resonance at
518.6 eV, which is typical of vanadium (V). The reference spectra (Fig. S 14 and S 15)
confirm this finding since the first resonance peak in the {V18} cluster is at a much lower
energy at 517.3 eV.
A NEXAFS spectrum of the copper L3-edge was recorded in the same way in order to
confirm the oxidation state +II. The main resonance peak is again in agreement with
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
copper (II). A copper (I) reference (Cu-TCNQ) and at the literature confirm these
findings.S10
Figure S 13: NEXAFS spectrum of {Cu 6V30}.
Figure S 14: NEXAFS spectrum of {Cu 6V30} and CuI reference spectrum using
CuITCNQ as reference compound.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012
9. Literature references cited in ESI
S1 A. Müller, R. Sessoli, E. Krickemeyer, H. Bögge, J. Meyer, D. Gatteschi, L. Pardi, J.
Westphal, K. Hovemeier, R. Rohlfing, J. Döring, F. Hellweg, C. Beugholt, M.
Schmidtmann, Inorg. Chem. 1997, 36, 5239-5250.
S2 J. Forster, B. Rösner, M. M. Khusniyarov, C. Streb, Chem. Commun. 2011, 47, 3114-
3116.
S3 Hesse, M., Meier, H., Zeeh B. Spektroskopische Methoden in der organischen Chemie,
2005, Vol. 7, 57.
S4 G. M. Sheldrick, Acta Crystallogr. 2008, A64, 112.
S5 L. J. Farrugia, J. Appl. Crystallogr. 1999, 32, 837.
S6 R. H. Blessing, Acta Crystallogr. 1995, A51, 33.
S7 P. Coppens, L. Leiserowitz, D. Rabinovich, Acta Crystallogr. 1965, 18, 1035.
S8 T. McGlone, J. Thiel, C. Streb, D. L. Long, L. Cronin, Chem. Commun. 2012, 48, 359-
361.
S9 J. G. Chen, C. M. Kim, B. Frühberger, B. D. Devries and M. S. Touvelle, Surf. Sci. 1994,
321, 145-155.
S10 A. B. Gurevich, B. E. Bent, A. V. Teplyakov, J. G. Chen, Surf. Sci. 1999, 442, L971-L976.
Electronic Supplementary Material (ESI) for Chemical ScienceThis journal is © The Royal Society of Chemistry 2012