Contents · SaranTM Resin Selection Guide Increasing Permeability High barrier Slower crystalization Coextrusion Medium barrier Gassy Cheese ... Blow Molding 2500 0.963 0.28 290 -

Contents

Construction

Automotive

Consumer

Energy

Packaging

Applications

Applications

Primacor™(EAA)

Primacor™ IO(Ionomer)

Saran™(PVDC)

Nexlene™(Metallocene Technology)

Smart™(mLLDPE/mMDPE)

Supreme™(POP)

Solumer™(POE)

Yuclair™/Yuzex™ (PE)

Yuplene™(PP)

Xplene™(HCPP)

Suprene®(EPDM)

Solutack™(HMA)

Global Network

3

4

5

6

7

8

9

10

12

14

15

16

18

20

2 3

1. Measured at 190℃, 2.16kg2. Dispersible

Primacor™ ApplicationsLaminated Tube Aseptic Packaging Condiment Packaging Powder Coating

Easy Peel Carpet Backing Wire & Cable Steel Coating

- Excellent taste and odor performance- Excellent hot tack and heat seal- Puncture & Tear resistance- Environmental stress crack resistance (ESCR) - Moisture insensitivity- Excellent seal through contamination

- Superior seal through contamination- Excellent hot tack strength over a broad temperature range - Low seal initiation temperature- Excellent oil and grease resistance- Superior clarity- Excellent puncture resistance

Superior Adhesion to Foil or Metalized Substrates Superior Chemical Resistance and Seal Through Contamination

Primacor™(EAA) Primacor™ IO (Ionomer)

Primacor™ Technical Information

DivisionProperties Acrylic Acid Content MI1) Density Melting Point Vicat Softening Point

Unit wt% g/10min g/cm3 ℃ ℃ASTM D4094 D1238 D792 SK Method D1525

Film

1321 6.5 2.5 0.932 103 89

1410 9.7 1.0 0.938 98 81

1430 9.7 5.0 0.938 96 76

ExtrusionCoating

3150 3.0 11 0.924 104 89

3330 6.5 5.5 0.932 100 85

3003 6.5 7.5 0.935 100 90

4608 6.5 7.7 0.932 99 86

3340 6.5 9.0 0.932 101 84

3002 8.0 9.5 0.936 100 82

3540 8.5 7.0 0.936 98 85

3004 9.7 8.5 0.938 98 81

3440 9.7 10 0.938 98 81

3460 9.7 20 0.938 95 72

High Acid

5980I2) 20.5 300 0.958 77 42

5986 20.5 300 0.958 77 42

5990I2) 20 1300 0.955 75 40

1. Measured at 190℃, 2.16kg

Primacor™ IO Technical Information

ProcessProperties Ion Type MI1) Density Melting Point Vicat Softening Point

Unit - g/10min g/cm3 ℃ ℃ASTM - D1238 D792 SK Method D1525

Extrusion Coating

3701 Zn 5.2 0.94 100 79

3702 Zn 14 0.95 95 65

Blown Film 3801 Na 1.3 0.94 98 74

Primacor™ IO ApplicationsVacuum Skin Packaging Fresh and Processed Meat Packaging

Oil/Sauce Packaging Fatty Food Packaging Shock Tube

4 5

MetalloceneCatalyst Tech.

Bimodal Solution Process Tech.

ProductTailoring Tech.

Performance Processibility Hygiene· Saran™ is polyvinylidene chloride having excellent barrier properties against oxygen and water. MA(methyl acrylate) is copolymerized with ~10% by weight. Comonomer modifies melting point and crystallinity.

Saran™ for Barrier FilmPremium polyethylene based on technology of the integration of single-site catalysts, solution process, and unimodal/bimodal product design

Nexlene™ Technology

Well balanced characteristics between physical properties, hygienic properties and processibilityTotal solution provider of premium polyethylene fromPOE to mMDPE

Nexlene™ Products

1) Measured at 190℃, 2.16kg2) Partitioning agents dusted grade available for improved handling.3) Additves added grade for improved slipping properties.

Product Type Grade Density (g/cm3) MI1) (g/10min) Applications

Solumer™(POE)

8512) 0.857 1.0 Compound-Ultra high impact strength86052) 0.863 0.5 Compound8612) 0.863 1.0 Compound8652) 0.863 5.0 Compound

86132) 0.863 13 Compound – High flowability8705 0.868 0.5 Compound, Footwear, Wire & Cable8712) 0.868 1.0 Compound, Footwear, Wire & Cable8752) 0.868 5.0 Compound, Footwear, Wire & Cable

87302) 0.868 30 Compound - Ultra high flowability883 0.880 3.0 Compound, Footwear, Wire & Cable891 0.885 1.0 Compound, Footwear, Wire & Cable

Supreme™(POP)

871 0.868 1.0 Packaging Film875 0.868 5.0 Stretch Film883 0.880 3.0 Stretch Film891 0.885 1.0 Packaging Film

001(S)3) 0.900/0.903(S) 1.0 Sealant layer004 0.900 3.5 Stretch Film

006S 3) 0.900 6.0 Sealant layer, Stretch film021(S)3) 0.902/0.905(S) 1.0 Packaging film

024 0.902 3.5 Packaging film028 0.902 7.5 Packaging film, Extrusion coating051 0.905 0.8 Packaging film, Stretch film

081(S)3) 0.908/0.909(S) 1.0/0.8(S) Packaging film1015 0.910 15 Extrusion coating

Smart™mLLDPE/mMDPE

121(S)3) 0.912/0.913(S) 1.0 Packaging film124 0.912 3.5 Stretch film, Silage film

151(S)3) 0.915/0.916(S) 1.0 Packaging film153 0.915 3.0 Stretch film, Silage film154 0.915 3.5 Stretch Film, Silage Film

181(S)3) 0.918/0.919(S) 1.0 Industrial film183 0.918 3.0 Stretch film, Breathable film184 0.918 3.5 Stretch film, Breathable film401 0.941 0.5 PE-RT

Nexlene™ Products Grades

· Saran™ offers superior moisture barrier regard-less the humidity. So dry products stay dry in the most humid conditions and moist products stay moist in arid conditions.

Saran™ Barrier Property

BETTER PROTECTION

BETT

ER P

ROTE

CTIO

N

Water Vapor Transmission g•㎛/㎡•day@38 ℃,90%RH

Oxy

gen

Tran

smis

sion

㏄

•㎛

/㎡•

day•

atm

SaranEVOH

PA6

PET

HDPE,PP

1 100,00010,0001,00010010

100,

000

10,0

001,

000

100

10

Saran™ Applications

Meat Packaging Sausage Casing Cheese Packaging

SaranTM Resin Selection Guide

Increasing Permeability

High barrierSlower crystalization

Coextrusion

Medium barrierGassy Cheese

High barrierCoextrusion

Medium barrierGassy Cheese

Ultra-high barrierCoextrusion

Good barrierMonolayer film

FiberFaster crystallization C

ryst

allin

e M

eltin

g Po

int

%Plasticizer

%MA

Increasing % Crystallinity

Saran™(PVDC) Nexlene™ (Metallocene Technology)

6 7

Smart™ film Z/N LLDPE film



Impa

ct st

reng

thTr

ansp

aren

cyHy

gien

e

Global Top Properties of SmartTM Film

Smart™ Characteristics

Smart™ Applications

Toughness

Transparency Sealability

Reference1

Reference2

Smart™

ProcessibilityHygiene

Z/N LLDPE

Sealing Layer of Multilayer Films

Container Liner Bag Cling Layer of Stretch Films Stretch Hood

Supreme™ Characteristics

Supreme™ Applications

Performance Processibility Hygiene

· Enhanced toughness· Excellent impact strength· Superior transparency

· Increment of output· Decrement of load and pressure· Better thickness uniformity

· Low migration· Improved organoleptic property· Low odor during processing

Performance Processibility Hygiene· Ultimate toughness· Excellent low seal initiation temperature· Wide range of hot-tack temperature window· Superior transparency· Great abuse resistance

· Easy processing· Better thickness uniformity

· Low migration· Improved organoleptic property· Low odor during processing

Smart™(mLLDPE/mMDPE) Supreme™(POP)

2.75

3.00

0.00

0.25

0.50

0.75

1.00

1.25

1.50

1.75

2.00

2.25

2.50

Hot

tack

str

engt

h (N

/25m

m)

Film : 40umx25mmSeal pressure : 0.3 N/mm2Seal time : 1.0 sDelay time : 0.2 s

Supreme001m-LLDZ-N LLD

Hot Tack Performance

Temperature (℃)

65 70 75 80 85 90 95 100 105 110 115 120 125

Blown Films Cast Films PE-RT Pipes

0

200

400

600

800

1000

1200

1400

1600

1800

Heat Seal Performance

Hea

t-sea

l Str

engt

h (g

)

Temperature (℃)

Seal Pressure: 0.2 MPaSeal Time: 1.0 s

Supreme001m-LLDZ-N LLD

65 70 75 80 85 90 95 100 105 110 115 120 125

8 9

Soft, Light, and Easy to foamReplacing EVA for lighter weight, better physical propertyApplied to sole (midsole, etc.)

Footwear Foam

No lamination defects, Moisture resistance, Weather resistanceReplacing EVA for enhanced durability, better physi-cal property and better electrical performance.

Photovoltaic Encapsulant

Excellent compatibility, Superior adhesive propertyProviding excellent impact properties in Nylon compounds Applied to automotive parts as impact modifier and adhesive layers on steel pipes

Maleic anhydride (MAH) grafted POE

Home appliance Injection Hot Melt Adhesive

Others

Easy processing, High electric resistivity and Heat resistance (with crosslinked)Replacing EVA for better physical propertyReplacing PE for higher filler loading and flexibilityApplied to power cable, instrumentation & commu-nication cable

Wire & Cable

Solumer™(POE)

Solumer™ CharacteristicsPerformance Processibility Hygiene

· Excellent impact strength· Excellent light transmittance· Low shrinkage· High filler loading

· Excellent processibility· Compatible with most olefins· Recyclable for environment· Pellet form for easy processing

· Low VOCs· Low odor during processing

Superior Impact strength, Low temperature ductility Better physical properties than C4 POEApplied bumper, side sill panel, instrument panel and door trim, etc.

•TPO Compound (Impact Modifier)

High filler loading, Light weight and ProcessibilityReplacing EVA for lighter weight, better physical property and lower VOCs.

•NVH (Noise, Vibration, Harshness)

Solumer™ Applications

Side Sill Panel NVH

Door TrimBumper Instrument Panel

Automotive

10 11

DivisionProperties Density Melt Index

Tensile strength at yield

Tensile strength at break

Elongationat Break

FlexualModulus

Izod ImpactStrength

ApplicationsUnit g/cm3 g/10min kg/cm2 kg/cm2 % kg/cm2 kg·cm/cm

ASTM D1505 D1238 D638 D638 D638 D790 D256

BlowMolding

2500 0.963 0.28 290 - >500 12,000 NB Container

2520 0.958 0.35 280 - - 11,000 12 Container

2600S 0.961 0.18 290 - - 12,000 NB Container

2600D 0.96 0.18 280 - - 11,000 NB Container

2600Y 0.959 0.14 290 - - 10,500 NB Container

Yarn3301 0.955 0.8 250 - <220 9,000 - Yarn

MD700 0.954 1.1 220 - - 8,000 - Yarn

Film

8700 0.954 0.075 220 290 >500 9,000 NB High speed processability

8700K 0.956 0.065 230 300 > 500 10,000 NB High speed & thin film

8800 0.956 0.048 230 300 >500 10,000 NB Industrial, Shopping bags, Trash bags

8800S 0.956 0.048 230 300 > 500 10,000 NB Industrial, Shopping bags, Trash bags

8800U 0.956 0.040 230 300 > 500 10,000 NB Mulching film

8810 0.957 0.037 230 300 >500 10,000 NB Large blown film, Industrial, Trash bags




Elongationat Break

ApplicationsUnit g/cm3 g/10min kg/cm2 kg/cm2 %

ASTM D1505 D1238 D882 D882 D882

PipeDX800 0.9335 0.64 - 390 800

Heating pipe, Pipe for hot &Cold water, Type I

6100 0.953 0.052 240 420 - Pressure Pipe (Gas, Water Pipe)




Elongationat Break

FlexualModulus

Izod ImpactStrength


ASTM D1505 D1238 D638 D638 D638 D790 D256

Pipe Coating

MB509U 0.939 0.35 - 280 900 - NB Pipe coating

Irrigation Pipe PI500 0.941 0.33 - 280 900 6,900 NB Pipe coating

RotoMolding

RG300U 0.93 5.00 145 250 900 5,800 NB Container, Powder coating

RG500U 0.938 5.00 180 250 700 6,500 NB Container, Large container


Izod ImpactStrength

SofteningPoint


Elongationat Break

FlexualModulus

ApplicationsUnit g/cm3 g/10min kg·cm/cm ℃ kg/cm2 % kg/cm2

ASTM D1505 D1238 D256 D1525 D638 D638 D790

Cap

7300 0.965 1.0 8 128 300 > 500 12,500 Bottle cap, Aseptic Cap

7302 0.957 1.0 11 123 230 > 500 8,500 CSD Bottle Cap

7303 0.956 2.0 16 122 220 > 500 8,000 CSD Bottle Cap

7303S 0.956 2.0 16 122 220 > 500 8,000 CSD Bottle Cap

7304 0.959 2.8 8 123 230 > 500 8,000 Hot Fill, 38mm CAP

DivisionCo-

mono-mer

Properties Density Melt IndexTensile strength

at yieldTensile strength

at breakElongation at

break Anti-blocking agent

Processing aid

Slip agent ApplicationsUnit g/cm3 g/10min kg/cm2 kg/cm2 %

ASTM D1505 D1238 D882 D882 D882

Film

C8

FT810 0.918 2.0 100/100 470/430 700/750 - - - Diaper, Stretch wrap

FT810P 0.918 2.4 100/100 450/410 720/780 - - - Diaper, Stretch wrap

FN810 0.919 0.9 120/110 550/500 700/800 - - - Industrial film

FN812 0.919 0.9 120/110 550/500 700/800 O - - Industrial film

FN840 0.919 0.9 120/110 550/500 700/800 O O O Industrial film

FT850 0.919 3.0 110/110 460/430 800/830 - - - Diaper, Electrical, Food wrap


FN800M 0.935 1.0 150/150 550/500 600/650 - O - Industrial film

C4

FG450 0.917 1.0 115/105 420/350 750/850 O O O General purpose

FU149S 0.919 1.0 120/110 430/360 750/850 O O O General purpose

FU149M 0.919 1.2 120/110 430/360 750/850 O O O General purpose

FN435 0.919 1.2 125/115 340/320 680/820 O O O Dry-lamination, Protective film

FV149M 0.919 1.8 120/110 380/350 790/870 O O O General purpose

FN410 0.919 1.8 120/110 430/360 750/850 O O - Industrial film, Agricultural film

FN430 0.919 1.8 120/110 340/320 680/820 O O O Industrial film, Agricultural film





Elongation at break

ApplicationsUnit g/cm3 g/10min kg/cm2 kg/cm2 %

ASTM D1505 D1238 D882 D882 D882

Extrusion Coating

CA100 0.919 7.0 101 150 600 Coating

CA110 0.921 16 110 150 500 Coating

CA119 0.921 12 110 130 550 Coating

Injection Molding

JL210 0.924 20 150 120 600 Lid, Containers

Wire & Cable

WE100 0.919 2.8 101 212 790 Wire & Cable

LLDPE




Elongationat Break

FlexualModulus

Izod ImpactStrength


ASTM D1505 D1238 D638 D638 D638 D790 D256

Injection

7200 0.968 5.0 320 170 > 500 13,000 5 Container

7210 0.960 5.5 270 100 > 500 9,200 9 Bottle cap, Pail bottle

JG910 0.963 5.0 260 130 > 500 10,000 10 Injection

JH910 0.962 8.5 260 100 >500 12,000 8 Crate, Paint bottle, Spray bottle

JK910 0.961 20 260 50 220 9,200 4 Home appliances, Large product

Fiber

MK710 0.956 20 255 - - 9,000 6 Bicomponent fiber, Staple fiber

MK910 0.956 20 255 - - 9,000 6 Bicomponent fiber, Staple fiber

MM810 0.954 30 250 - - 9,000 6 Spun bond

HDPE/MDPE

Yuclair™/Yuzex™ (PE)

12 13

Yuplene™ (PP) Xplene™ (HCPP)

DivisionProperties Melt Index

Izod ImpactStrength

(Notched, 23℃)

SofteningPoint

Tensile trengthat Yield

Elongationat Yield

FlexualModulus Applications Characteristics

Grade g/10min kg·cm/cm ℃ kg/cm2 % kg/cm2

ASTM D1238 D256 D1525 D638 D638 D790

Injection H360F 12 4.0 154 380 >500 16,000 Commodity, Home Appliances High Stiffness

Coating H680S 25 4.0 150 300 > 500 13,000 Coating Coating processability, Heat resistance

Yarn H730F 3.5 5.0 152 370 > 500 15,000 Rope, Sheet, Tapes, Tents, Woven bags Processability, Tenacity

Homo PP


Izod ImpactStrength

(Notched, 23℃)

SofteningPoint


Elongationat Yield



ASTM D1238 D256 D1525 D638 D638 D790

Injection

BK3505 10 12 155 301 <300 17,000

Automobile applications, Home appliances, Indus-trial parts for electronic

Stiffness, Hear resistance, Impacr strength, High flow

BK3801 30 7 155 350 <200 21,000

BK3805 30 9 155 301 <200 19,000

BK3901 61 6.5 155 350 <100 21,000

BK3905 61 8 155 301 <100 19,000

Advanced Impact HCPP


Izod ImpactStrength

(Notched, 23℃)

SofteningPoint


Elongationat Yield



ASTM D1238 D256 D1525 D638 D638 D790

Injection

R370Y 18 6.0 135 300 > 500 12000

Food container, Home appliances,Transparent container

High Transparency, High GlossRX3600 18 13.0 125 250 > 500 11000 High Transparency & impact strength, High GlossR362Y 14 6.5 135 310 > 500 13000 High Transparency, High GlossR365Y 14 6.5 135 300 > 500 12000 High Transparency, High GlossR366Y 14 5.5 143 330 > 500 14000 High Transparency, High GlossR380Y 29 4.0 135 300 > 500 12000 High Transparency, High GlossR380K 29 4.0 135 300 > 500 12000 High Transparency, High GlossR390Y 45 6.0 130 300 > 500 12000 High Transparency, High Gloss, High FlowR392Y 75 5.0 155 270 > 250 12000 High Transparency, High Gloss, High Flow

SheetR930Y 4.5 8.0 140 320 > 500 14000 High transparent

sheetHigh Transparency, High Gloss, Impact strength

R931Y 3.5 10.0 135 310 > 500 13000 High transparent sheet

High Transparency, High Gloss, Impact strength

EPP R940U 5.8 8.0 131 260 >500 10000 Expandable PP UV StabilityR940F 5.8 8.0 131 260 >500 10000 Expandable PP High transparency, Impact strength

Coating R680S 28 14.0 125 250 >500 10000 Coating(food packaging), Lamination(BOPP)

Coating processability, Adhesive, Heat resistance

BlowMolding

R520F 1.8 10.0 135 290 > 500 11000 Intravenous bottle, Transparent container USP Certification

R520Y 1.8 9.5 140 320 > 500 14000 Transparent container(High transparent sheet) High Transparency, High Gloss

Film(CPP)

R140M 6 8.0 132 260 > 500 10000 CPP co-extrusion, Retort pouch

High Transparency,High Gloss,Low heat sealing temperature

R140H 6 8.0 132 260 > 500 10000 CPP co-extrusion, Retort pouch

R151A 7 8.0 131 260 > 500 10000 Film/CPP co-extru-sion, Retort pouch

RANDOM PP


Izod ImpactStrength

(Notched, 23℃)

SofteningPoint


Elongationat Yield



ASTM D1238 D256 D1525 D638 D638 D790

InjectionBH3500 10 >50 (NB) 150 230 <500 13,000 Automobile

applications, Home appli-ances, Industrial parts for electronic

Very high Impact Impact Strength

BH3820 28 >50 (NB) 150 210 <300 11,000BH3910 60 >50 (NB) 150 180 <200 8,000

HSPP


Izod ImpactStrength

(Notched, 23℃)

SofteningPoint


Elongationat Yield



ASTM D1238 D256 D1525 D638 D638 D790

Injection

HX3300H 5 4 158 390 < 300 22,000

Automobile applications, Home appliances,Industrial parts for electronic

Heat Resistance (RTI), High Stiffness

HX3700 20 3 156 400 < 300 21,000

High StiffnessHX3800 45 2.5 156 410 < 300 21,000

HX3900 65 2 156 410 < 300 21,000

Homo HCPP


Izod ImpactStrength

(Notched, 23℃)

SofteningPoint


Elongationat Yield



ASTM D1238 D256 D1525 D638 D638 D790

Injection

B310F 1.5 25.0 150 270 > 500 12,000

Automobile applications, Battery case, Home appliances,Industrial parts for electronic

High Impact Strength

B330F 3.5 16.0 150 270 > 500 12,000B340F 7 15.0 150 270 > 500 12,000B350F 9 12.0 150 270 > 500 12,000B351F 9 12.0 150 270 > 500 12,000B360F 16 9.0 150 270 > 500 12,000B370F 20 9.0 150 260 > 500 12,000B380G 28 9.0 150 260 < 300 12,000

Automobile applications, Industrial parts for electronic, Large container

High Stiffness, Impact Strength,High flow

B391G 40 7.5 150 260 > 500 13,000B391M 40 7.5 150 260 > 500 13,000B393G 60 7.0 150 270 > 500 15,000

Impact PP


Izod ImpactStrength

(Notched, 23℃)

SofteningPoint


Elongationat Yield



ASTM D1238 D256 D1525 D638 D638 D790

Injection

BX3500 10 10 155 320 <300 17,000

Automobile applications, Home appliances, Industrial parts for electronic

Stiffness, Heat resistance, 1Impact strength, High flow, low VOCs

BX3500H 10 10 155 320 <300 17,000 Heat Resistance (RTI), High Stiffness

BX3800 30 7 155 330 <200 19,000Stiffness, Heat resistance, Impact strength, High flow, low VOCs

BX3900 61 6.5 155 330 <100 19,000

BX3920 110 6 155 330 <100 19,000 Stiffness, Heat resistance, Impact strength, High flow, low VOCs

BX3950 160 6 155 330 <100 19,000 Excellent flow

BT3500 8 10 155 300 <200 15,000 Battery case Stiffness, Heat resistance, Impact strength, High flow, low VOCsBY3500 9 10 155 300 <300 15,000 Bottle cap

Impact HCPP

14 15

SK Global Chemical supplies a high value-added synthetic rubber that performed well in all weather and heating conditions and is also ozone resistant. The rubber is primarily used in the manufacturing of auto-mobiles and industrial rubber components. SK Global Chemical supplies top-quality products to meet the expectations of our valuable customers. Global demand for EPDM is expected to increase by more than 4 percent per year. Especially the demand in China is expected to grow by around 8 percent, due to growing demand from automobile and various other industries.

Phys

ical

Pro

pert

ies

Processability

Grade

Mooney Viscosity(ML 1+4)

Ethylenecontents

Dienecontents Oil

Applications Characteristics

100 ℃ 125℃ 150℃ wt% wt% phr

S501A 46 (30) 53 4.1Molding Products, Complicated Products, Gasket, Electric parts.

Low Mooney and ENB type, Excellent millprocessability and good flow properties, Suitable for molding complicated shape and extrusion.

S505A 45 (29) 55 9.4Automotive tire, Sponge Prod-ucts, Rubber coated fabrics, Automotive parts.

Low Mooney and high ENB type.Good mill processability. Blend with diene type rubber.Having a superb mold flow and fast cure rate

S537-3 35 57 2.3 Tire inner tube,Mechanical goods.

Low Mooney and low ENB type.Excellent heat resistance, weathering and impact resis-tance at low temperature. Usually blended with IIR

S512F 63 69 4.5 Hose, window gasket,Various extrusion Products.

High ethylene and high green strength as raw polymer. Outstanding physical properties and processability. As a friable bale, short mixing time make good energy saving.

S552 84 58 4.1 Hose, General industrial goods, Gaskets, Weather strip solid.

Excellent extrusion processability and physical proper-ties, Better flexibility at low temperature.

S552-1 84 58 5.7 Hose, General industrial goods, Gaskets, Weather strip solid.

Excellent extrusion processability and physical prop-erties, Excellenet elastic property and fast cure rate. Better flexibility at low temperature.

S5890F (87) 64 68 5.5Weather strip solid,Radiator hose,Mold, Auto parts

Friable bale, Excellent high loading and well balanced physical properties and processability.

S553 (98) 72 62 4.5Window seals,Automotive exterior parts,Roofing sheet.

Non-oil extended grade with very high Mooney viscosity. Excellent extrusion processability and physical properties with high loading of filler. Good flexibility at low temperature.

S5206F (84) 61 60 8.5

Automotive sponge,Heat insulation sponge,Weather seal sponge, Bicycle tire.

Non-oil extended grade with very high Mooney viscosity.Excellent extrusion processability and physical prop-erties with high loading of filler. Good flexibility at low temperature.

S5527F (109) 81 60 8.5

Automotive sponge,Heat insulation sponge,Weather seal sponge, Bicycle tire.

High molecular weight and high ENB content grade.Good shape retention and low compression set.

S7486F (94) 67 60 9Automotive sponge,Heat insulation sponge,Weather seal sponge.

Friable bale, high molecular weight and high ENB content grade. It shows low compression set and fast cure rate.

S6090WF 53 70 5.7 50Mold, Gasket, Automobile and Industrial goods, Electric appliances.

High ethylene and High molecular weight.Control low hardness blend with other grades.Good processability and physical properties.

S6075WF 50 60 4.7 75Mold, Gasket, Automobile and Industrial goods, Electric appliances.

It has good properties at low temperature. Friable bale, high molecular weight and well balanced physical properties and processability.

S675WF 62 70 4.7 75Mold, Gasket, Automobile and industrial goods, Electric appliances, TPV.

Oil extended Friable bale. With High ethylene and High molecular weight, it shows excellent physical proper-ties. Good for high loading applications.

S600WF 61 (41) 72 4 100Bicycle tire, Automobile and industrial goods, Electric appliances, TPV.

Oil extended Friable bale. It can be formulated to make products of low hardness. It is possible to load high concentration of filler.

S6800WF 47 72 8.5 100Mold, Gasket, Automotive and industrial goods, Electric appliances, TPV.

Oil extended Friable bale with very High molecular weight, High Ethylene content and High ENB content, shows excellent phys-ical properties, even in highly loaded formulations. Especially good for lower hardness profiles and colored rubber parts.

HeatResistance↑

CuringProperties↑

Processability↑

Physical Properties↑Processability↑

Physical Properties↑High Loading

S5527F

S553

S552-1

S5890F

S600WF

S6800WF

S675WF

good low temperatureproperties↑

S6075WF

S501A

S537-3 S505A

S6090WF

S512F

S552

S5206F

S7486F

C-Set↑

PhysicalProperties↑


high cure rate↑C-set↑


Low TempProperties↑

Curing Properties↑

Physical Properties↑Control Hardness↑

Physical Properties↑ High Loading

The Innovative Chemical Company, Creating Values with Technology & Solutions

Suprene® Grade Selection Guide

Suprene® (EPDM)

Suprene® Technical Information

16 17

SOLUTACK™6805

SOLUTACK™6810

SOLUTACK™7405

SOLUTACK™7410 Unit Test

Method

PhysicalProperties

Density 0.868 0.868 0.874 0.874 g/cm3 ASTM D792

Melt index (2.16kg @190℃)

500 1000 500 1000 g/10minSK

Method1)

MechanicalProperties


1.5 1.4 2.0 1.85 MPa ASTM D638

Elongation at break 220 100 110 120 % ASTM D638

ThermalProperties

Meltingtemperature

36,70 32,70 53, 80 53, 78 ℃SK

Method

Glass transition temperature

-63 -65 -57 -58 ℃SK

MethodShear AdhesionFailure Temperature(SAFT, base resin only)

74 72 80 79 ℃SK

Method

ViscosityBrookfield Viscosity (177℃)

17 8.2 17 8.2 Pa·sSK

Method

1) Estimated value: Calculated via Advanced Expansion System (ARES)

NotesThese are typical values and not be construed as specifications. Customers should confirm performance by their own tests.

Solutack™ Hotmelt Adhesive· Solutack™ Technology makes it possible to precisely control the various elements of low molecular weight polymer architecture including crystallinity, molecular weight, molecular weight distribution, density distribution, etc.

· SK launched highly valued Solutack™ that deliver market differentiation, superior resin performance, productivity, and cost efficiency with broad product portfolio. Furthermore, tailored product with controlled melt viscosity, service temperature range, temperature dependency of melt viscosity can be supplied for customers.

HMA Formulated with Solutack™ HMA Formulated with General EVA

Service Temperature(˚C)-50 -35 -20 -5 10 25 40 55 70 85 100

Thermal Stability (190℃)

Solutack™ 6810

Reference(MI 1000)

~3hr ~24hr ~48hr ~72hr ~96hr ~120hr· Since Solutack™ do not have any oxygen moieties in the backbone, they show superior thermal stability during HMA process

· Because of optimized polymer archi-tecture & specific additive, Solutack™ shows superior thermal stability than other HMA resins.

· High adhesion strength · Wide service temperature range.

Solutack™ (HMA)

Solutack™ Characteristics

Solutack™ Applications

Solutack™ Technical Information

Solutack™ Handling Guide

Material Characteristic Thermal Properties Adhesion Properties

·Low density·Less odor·Ultra high flowability

· Low glass transition & melting temperature(Tg,Tm)

·Low temperature flexibility·Thermal stability & resistance· Wide service temperature range

·High bonding strength· Less angel- hair & Spider webs·Less plugging·Shorter set time·Versatility

Frozen Food Packaging Carton Box Personal Hygiene

· Low temperature flexibility· Wide service temperature range

· Ultra high flowability· Down gauging· Versatility

· Low odor· Short set time· Wide service temperature range

Thermal Stability and Service Temperature Range

· Resins have very broad range of melting and running temperatures for processing (Recommended range : Melting 120 ~ 230 ℃, Running 90 ~ 190℃). ·Do not double-stack resin bags.·Store the resins under mild conditions

18 19

CREATING VALUES WITH TECHNOLOGY & SOLUTIONS

Since its foundation in 1972, SK Global Chemical has been shaping and leading the petrochemical industry of Korea over the last four decades. Having been newly organized, in 2011 as SK Innovation, the company continues to consolidate the bases for its growth into the leader of the international pet-rochemical industry with its independent and accountable management system.

The company is now ushering in a new and better future for the chemical industry by pursuing self-innovation, performing advanced research and development, and investing greatly in the projects growth.

SK Global Chemical has enhanced its productivity and the quality of its products based on its optimized production and operation systems. It is also upgrading its business portfolio with increasing focus on high value added prod-ucts. The company’s potential is growing immeasurably as it has succeeded in commercializing a number of high-tech, next-generation material. The company’s clientele is rapidly expanding worldwide, to the emerging and growing markets in China, Southeast Asia, the Middle East, and Latin America.

SK Global Chemical will continue this direction of growth and innovation fuelled by the unity and drive of all employees and Board members.SK Global Chemical is ready to spearhead the efforts to create a happier and more prosperous future for all stakeholders.

We ask you to continue to support our journey to a brighter future with your attention and encouragement.

THE INNOVATIVE CHEMICAL COMPANY

Global NetworkFrankfurt

Dubai

Beijing

WuhanHangzhou

Guangzhou

Singapore

Seoul

TokyoRudongShanghaiNingbo

Midland

Houston

Freeport

Tarragona

Seoul Shanghai TS&D Center

26 Jong-ro, Jongno-gu, Seoul, Korea No.1438, Hongqiao Road Shanghai, China 200336

No. 338 Jialilue Road, Zhangjiang Hi-Tech Park, Pudong New

Area, Shanghai, China

·Packaging Sales UnitTel l 82-2-2121-6747Fax l 82-2-2121-3765 Tel l 86-21-6197-0100

Fax l 86-21-6197-0352Tel l 86-21-6105-2138Fax l 86-21-6197-0100·Automotive Sales Unit

Tel l 82-2-2121-6837Fax l 82-2-2121-3765

Location Tel. Address

Chemicals R&D Center 82-42-609-8626 325 Expo-ro, Yuseong-gu, Daejeon, Korea

Tokyo 81-3-3591-0343 NBF Hibiya Bldg, 8F 1-1-7, Uchisaiwai-cho, Chiyoda-ku, Tokyo 100-0011, Japan SKGC

Singapore 65-6671-1566 23 Church street, #10-05/06 Capital Square, Singapore 049481

Houston 1-713-395-1778 1300 Post Oak BD., Ste #425, Houston, Texas, USA 77056

Dubai 971-4-252-5277 #1003, AI Nouf Tower, P.O.Box 126494, Dubai,UAE

Frankfurt 49-6967738103 Lyonerstrasse 36, 60528 Frankfurt am Main, Germany

Guangzhou 86-13826103319 Unit2001,20th floor ,TaiKoo Hui Tower 1, No.385 Tianhe Road, Guangzhou

Wuhan 86-13982017272 Room 709-712, NO.198 Yuncai Road ,Office Building, Oceanwide City Square, JiangHan District, Wuhan, China

Beijing 86-10-5920-5660 35th Floor, SK Tower, No.6 Jia Jian Guomenwai Avenue, Chao Yang District, Beijing, China 100022

Dalian86-411-8369-330 (ext.109)

14F, Senmao building, No.147, Zhongshan Road, Xigang District,Dalian, China 116001

Qingdao 86-532-8387-4333 Room 1902 Huayin BLDG,#5 Donghai West Road, Qingdao, China 266071

Chengdu 86-13982017272 Room 1706, South Tower of Poly Center, No.7 Lingshiguan Road, Chengdu, China

Xiamen 86-592-516-0453 Room 538, Caizhi Square, #628 Xiahe Road, Siming District, Xiamen, China 361004

DaejeonUlsan

DalianQingdao

Xiamen

Chengdu

20 21

Documents

Contents · SaranTM Resin Selection Guide Increasing Permeability High barrier Slower crystalization Coextrusion Medium barrier Gassy Cheese ... Blow Molding 2500 0.963 0.28 290 -