CRA and Wear Claddings or the Oil and Gas Industry
CermaClad is a patented process that uses high energy density IR usion tometallurgically bond a layer o API compliant metal alloy such as 625, 316L, and
nickel tungsten carbide or similar to a steel substrate. Due to input controllability
and a scalable rate o application, a ull range o long term unctional alloys or
chemical, temperature, and abrasion resistance can be applied. The result is an
unparalleled level o perormance.
CermaClad, a true advancement in metal usion technology.
CermaClad has an application rate 10 to 100 times aster than advanced thermal/plasma or weld/laser cladding with much greater uniormity and reliability.
Application Width: 12 to 30 cm Application Width: 0.7 cm
CermaClad TraditionalLaser Cladding
24112 Rockwell Drive Euclid, Ohio 4411
www.mesocoat.com
Phone: 425-823-5568
Mesocoat is a global leader in metal alloy coatingand cladding technology. Its breakthrough PComP
nanocomposite cermet hard chrome alternatives and
CERMACLAD CRA and wear claddings lead the industrFinish surface using CermaClad process.
The Meso and Nano scale engineered
structure o the CermaClad consumable
controls the wetting and viscosity o the
cladding, to enable a pinhole-ree, smooth,
uniorm cladding/coating to be applied.
http://www.mesocoat.com/http://www.mesocoat.com/8/2/2019 CermaClad Brochure
2/2
he CermaClad usion process creates a complete metallurgical bond with very low dilution and thermal impact.
Cross cut sample etched in 50% HCL @ 200X Cross cut sample etched in 50% HCL @ 800X 3 mm Inconel 625 applied on API X65 Bas
For more inormation contact:
John Neukirchen: 425-823-5568, Mario Medanic: 818-519-6675 www.mesocoat.c
Metallurgical bond
Unprecedented durability and resiliencyh
0 to 100 times aster than current cladding technologies
Cost Competitiveh
erormance and Reliability
Refned grain size and controlled uniorm usion processh
Little to no substrate back mixingh
Low thermal impact, does not degrade high strength pipeh
Large scale application processPipe plant or mill production cladding capabilityh
Low environmental risk and compliance
Wide range o material compositionsHigh corrosion, wear, and temperature resistanceh
Application thickness rom 0.1mm mils to 3mm per passh
Application o multi layer compositions and thicknessesh
Uniorm, smooth fnish - does not require post processing
Application to Pipe Interior Suraces
Unparalleled Benefts
Step 1 Step 2 Step 3
EM Fusion Lamps
Fused
Metal OverlayHigh Energy Density IR FusionLamp produce a metallurgicalbond to the surace at a high
rate o application.
Metal Alloy
ApplicationAPI compliant metalalloy is applied at a
designed thickness o10 to 160 mils per pass.
White Metal Blast
Surace Preparation