Index
History and organization Production and innovation Quality Environment Products and applications Aerospace Automotive Power/Transport Fluid/Oil and Gas Marine Metallurgy/Moulds Alloys Instructions for using the tables Tables Compliance with main standards
4 6 8 10 14 16 18 20 22 24 26 28 29 30 44
5
7
9
11
13
15
17
19
21
23
25
27
29
Nominal composition %
Alloy
Standards Nearest international standards Electrical conductivity %IACS 83 98 100 100 75
Cu NFA 51050 EN 12420 CuDHP CW024A 99,90 UNS 12200 DIN 1708 SF-Cu 2.0090
Bi
O
Cr
Zr
Co
Be
Ni
Fe
Mn
Al
Si
Zn
Sn
Pb
P
Other
Cu b1
0,013 to 0,050
8,9
Cu HCP
EN 12420 CW021A UNS C10800 Cu OFLP DIN 1708 SE-Cu ISO 1337
99,95 0,0005
0,005
0,002 to 0,007
0,03
8,9
Cu OF
NFA 51050 Cu c1 EN 12420 CuDHP CW008A 99,95 0,0005 0,0010 ASTM B152 10200 DIN 1708 OF-Cu 2.0040
0,005
0,03
8,9
Cu ETP
NFA 51050, Cu a1 EN 12420 CW004A ASTM B152 UNS 11000 99,90 0,0005 0,040 DIN 1708 E1 Cu58 2.0061
0,005
0,03
8,9
CRM16CuCr1Zr
ASTM: C18100-C18150 MIL 19311 RWMA class 2 SAE CA 184 BS 2874 CC 102 EN 12163, EN 12165, EN 12420, EN 12167 CW106C, CW105C DIN 17666 WN 2.1293 DIN 17672 DIN 44759 NFA 82100 ISO 5182 A2/3 ISO 1336
remainder
0,4 to 1
0,03 to 0,15
0,08
0,2
8,9
Density
Forms/process
Mechanical properties
Available forms
Yield strength 0,2% offset or 0,5% E.U.L. (1)
Elongation 5,65 S
Physical properties Tensile strength
Impact strength KCU (1) or IZOD (2)
Forgings or stamped parts
Semi-finished products
Hardness
Tubes
Remarks Electrical resistivity at 20c cm Coefficient of expension 20 to 200 c x 10 - 6 K-1
Relative magnetic permeability
Thermal conductivity 20 to 200c W/mk
Young s modulus kN/mm2
Mpa ; * = Mpa
Extruded or forged
ksi ; * = Mpa
Forged blanks
Hexagones
2,1
320
18
1,01
110
1000 mm , dimension above on demand
205
30
60
9
35
45
1,75
320
18
1,01
110
1000 mm , dimension above on demand
205
30
40
6
35
45
1,724
320
18
1,01
110
1000 mm , dimension above on demand
205
30
40
6
35
45
1,724
320
18
1,01
110
1000 mm , dimension above on demand
205
30
40
6
35
45
cold formed electrodes 13 20 mm - 0,5 in. 0,8 in. machined electrodes 10 40 mm - 0,40 in. 1,57 in. round rod 10 25,4 mm 0,40 in. 1 in. square, flat, hexagone, thickness 10 25,4 mm 0,40 in. 1 in. TER condition
160
150
480
70
420
61
18
150
2,3
320
17,5 1,01
120
round rod 26 45 mm - 1. in. < 1,80 in. square, flat, hexagone, thickness 26 to 60 mm - 1,02 in.to 2,4 in. TER condition
480
70
420
61
18
140
round rod 45 < 80 mm 1,80 in. < 3,15 in. temper TER
440
64
360
52
18
140
round rod 20 350 mm 0,80 in. 13,8 in. square, flat of equivalent section TR condition
350
51
240
35
20
120
plate 16 thickness 250 mm - 0,60 thickness 10 in. TR condition
380
55
280
41
20
120
plate 4 thickness 10 mm 0,16 thickness 0,40 TER condition
400
58
350
51
10
125
Machined
Extruded
Stamped
Squares
Section
Rounds
Drawn
Drawn
Plates
Mpa
Tubes
Rings
Discs
Flats
ksi
HRB
HV5
%
HB
Parts
Rods
31
Nominal composition %
Alloy
Standards Nearest international standards Electrical conductivity %IACS 75 85 85 43 28
Cu
Bi
O
Cr
Zr
Co
Be
Ni
Fe
Mn
Al
Si
Zn
Sn
Pb
P
Other
CRM16ECuCr1Zr
ASTM: C18100-C18150 MIL 19311 RWMA class 2 SAE CA 184 BS 2874 CC 102 EN 12163, EN 12165, EN 12420, EN 12167 CW106C,CW105C DIN 17666 WN 2.1293 DIN 17672 DIN 44759 NFA 82100 ISO 5182 A2/3 ISO 1336
remainder
0,4 to 1
0,03 to 0,25
0,08
0,2
8,9
ZR16XCuZr
ASTM: C15000 RWMA class 1 DIN 17666 wn 2.1580 DIN 17672 ISO 5182 A2/4 EN 12163, EN 12167, EN 12420 CW120C
remainder
0,15
8,9
BICOPCuAl2O3
C 15735
remainder
0,6
8,8
CuCO2Be
CB4
BS 2874 CC 112 DIN 17666 wn 2.1285 DIN 17672- DIN 44759 ISO 1187- NFA 82100 ASTM B441- B534- B 870: C 17500 MIL 46087- RWMA class 3 SAE CA 184
remainder
2,2
0,5
8,9
CBE2CuBe2
ASTM B196: C 17200 AMS 4533 : C17200 AMS 4535 : C17200 RWMA class 4 QQC 530 DIN 17666, DIN 17672 wn 2.1247 NFL 14709 EN 12163 CW 101C
remainder
>0,2
1,8 to 2
8,3
Density
Forms/process
Mechanical properties
Available forms
Yield strength 0,2% offset or 0,5% E.U.L. (1)
Elongation 5,65 S
Physical properties Tensile strength
Impact strength KCU (1) or IZOD (2)
Forgings or stamped parts
Semi-finished products
Hardness
Tubes
Remarks Electrical resistivity at 20c cm Coefficient of expension 20 to 200 c x 10 - 6 K-1
Relative magnetic permeability
Thermal conductivity 20 to 200c W/mk
Young s modulus kN/mm2
Mpa ; * = Mpa
Extruded or forged
ksi ; * = Mpa
Forged blanks
Hexagones
2,3
320
17
1,01
120
discs and rings TR condition
380
55
280
41
15
130
2,05
320
17
1,01
110
TER condition
320
46
280
41
18
120
2,05
340
17
1,01
120
sizes and dimensions on demand
430
62
410
50
12
150
section< 1000 mm2 - < 1,550 in.2 TR or TER condition 4 200 17,5 1,01 130
700
101
650
94
10
240
section 1000 mm2 - 1,550 in.2 TR condition discs 200 400 mm 7,9 in. 15,7 in. plates 25 thickness 250 1 in. thickness 10 in. rods 19,05 < 50,8 mm 0,75 in. < 2 in. TER condition rods 50,8 76,2 mm 2 in. 3 in. TER condition rods 19,05 150 mm 0,75 in. 5,9 in. TR condition
700
101
550
80
10
220
1050
152
850
123
2
320
1140
165
965
140
2
340
1240
180
1061
154
3
360
6
110
17
1,01
130
1210
175
1040
151
4
360
1150
167
965
140
4
340
rods 19,05 150 mm 0,75 in. 5,9 in. T condition
570
83
35
150
80
rings TR condition
1050
152
850
123
2
320
Machined
Extruded
Stamped
Squares
Section
Rounds
Drawn
Drawn
Plates
Mpa
Tubes
Rings
Discs
Flats
ksi
HRB
HV5
%
HB
Parts
Rods
33
Nominal composition %
Alloy
Standards Nearest international standards Electrical conductivity %IACS 38 45
Cu
Bi
O
Cr
Zr
Co
Be
Ni
Fe
Mn
Al
Si
Zn
Sn
Pb
P
Other
CuNi2Si
NS5
DIN 17666 wn 2.0855 DIN 17672 w 2.0855 DIN 44759 cl A3.2 NFL 14-701 ISO 1187 EN 12163, EN 12167, EN 12420, EN 12165 CW111C DTD 498- RWMA class 3
remainder
2,3
0,6
8,8
CuNi2Si
NS6
RWMA class 3: C18000
remainder
0,6
2,3
0,6
8,8
Density
Forms/process
Mechanical properties
Available forms
Yield strength 0,2% offset or 0,5% E.U.L. (1)
Elongation 5,65 S
Physical properties Tensile strength
Impact strength KCU (1) or IZOD (2)
Forgings or stamped parts
Semi-finished products
Hardness
Tubes
Remarks Electrical resistivity at 20c cm Coefficient of expension 20 to 200 c x 10 - 6 K-1
Relative magnetic permeability
Thermal conductivity 20 to 200c W/mk
Young s modulus kN/mm2
Mpa ; * = Mpa
Extruded or forged
ksi ; * = Mpa
Forged blanks
Hexagones
section 1000 mm2 - 1,55 in. TER temper
650
94
590
86
10
195
4,5
180
16
1,01
130
1000 1 in. forged plate 19 thickness 25 mm - 0,75 in. thickness 1 in. forged plate 25 thickness 51 mm - 1 in. thickness 2 in. forged plate thickness> 51 mm - thickness > 2 in.
650
94
500
72
10
195
590
86
440
64
8
190
490
71
340
49
8
160
655 650 610
95 94 88
590 500 500
86 72 72
9 9 9
195 195 195
90 90 90
610
88
345
50
9
195
90
655
95
590
86
9
195
90
3,83
180
16
1,01
130
610
88
345
50
9
195
90
650
94
345
50
9
195
90
620
90
345
50
9
195
90
610
88
345
50
9
195
90
Machined
Extruded
Stamped
Squares
Section
Rounds
Drawn
Drawn
Plates
Mpa
Tubes
Rings
Discs
Flats
ksi
HRB
HV5
%
HB
Parts
Rods
35
Nominal composition %
Alloy
Standards Nearest international standards Electrical conductivity %IACS 9 5
Cu
Bi
O
Cr
Zr
Co
Be
Ni
Fe
Mn
Al
Si
Zn
Sn
Pb
P
Other
NAVINIC 10CuNi10Fe1Mn
ASTM B151-B171B466-B467: C70600, C70620 MIL T 16420 K, MIL C 15726, MIL C 24679 SAE J 463 CA 706 BS 2871 CN 102, BS 2874 CN 102 NES 779 JISH 3300 DIN 17664 wn 2.0872, DIN 17671-DIN 17672 DIN 86019 2.1972, CuNi10Fe1,6Mn, DIN 86028, DIN 86036, DIN 86037, DIN 86086, DIN 86087, DIN 86088, DIN 86089, DIN 86090, DIN 1755 VG 85 004 EEMUA 144, 145, 146 GAM MM11 - GAM MM13 INDRET IT 108 NFA 51-102 ISO 429 SIS 1456.67 EN 12163, EN 12449, EN 12165 CW352H
remainder
10
1,6
0,7
8,9
NAVINIC 30CuNi30Mn1Fe
ASTM B151-B171B466-B467: C71500, C71520 MIL T 16420 K, MIL C 15726, MIL C 24679 SAE J 463 CA 71500 BS 2871, BS 2874 CN 107 DGS 320, NES 780 DIN 17664 wn 2.0882 DIN 17671, DIN 17672 NFA 51-102, GAM MM11 INDRET IT-108 ISO 429 SIS 1456-82 JISH 3300 C7150 NES 780 70/30 EN 12163, EN 12420, EN 12165 EN 12449 CW354H
remainder
30
0,5
1
8,9
Density
Physical properties
34 Electrical resistivity at 20c cm Thermal conductivity 20 to 200c W/mk Coefficient of expension 20 to 200 c x 10 - 6 K-1 1,1 Relative magnetic permeability Young s modulus kN/mm2 50 17 1,1 130
19
30
16
130
annealed condition annealed condition Remarks
cold worked condition cold worked condition .22 annealed condition Extruded or forged Drawn Extruded Drawn Rods Tubes Forgings or stamped parts 310 320 310 350 Mpa ; * = Mpa ksi ; * = Mpa Mpa ksi % 70 HB HRB 70 70 HV5 Impact strength KCU (1) or IZOD (2) Rounds Squares Flats Hexagones Section Tubes Plates Discs Rings Forged blanks Stamped Machined Parts Hardness Tensile strength 44 46 51 44 110 110 160 250 16 23 36 16 35 25 15 35 70 100 11000 mm - section > 17 in as manufactured temper M
780
113
590
86
10
215
19
30
17
1,01 145
740
107
540
78
7
205
720
104
500
72
7
200
690
100
320
46
13
180
rods 12,7 25,4 mm - 0,5 in. 1 in. HR50 temper
760
110
469(1)
68(1)
10
201 to 248 201 to 248
rods 25,4 < 50,8 mm - 1 in.< 2 in. HR50 temper 22 40 16 1,5 125
760
110
413(1)
60(1)
10
rods 50,8 < 76,2 mm - 2 in. < 3 in. HR50 temper
723
105
379(1)
55(1)
10
187 to 241
rods 76,2 < 254 mm - 3 in.< 10 in. HR50, TQ50 temper tubes 50 mm - 2 in., thickness 10 mm - 0,4 in. HR50,TQ50 temper 15 25mm - 0,60 in. 1 in. , equivalent diameter 22 40 16 1,5 125 25 < 100 mm - 1in.< 4 in., equivalent diameter > 100 mm - > 4 in. , equivalent diameter rods 16 18 mm rods 18 < 80 mm rods > 80 mm 22 40 16 1,5 125 tubes 50 80, thickness 10 mm tubes, rings, discs > 80 mm, thickness 10 mm section 500 mm - section 0,8 in. 500< section 2000 mm - 0,8 in.< section 3,1 in. 20 45 16 1,1 120 2000 < section 5000 mm 3,1 in.< section 7,8 in.
689
100
345(1)
50(1)
10
187 to 241
689
95
345(1)
50(1)
10
190 165 24(2), 25(1) 27(2), 25(1) 23(2), 25(1)
680
99
325
47
17
640
93
295
43
17
160
620 700 700 650 700
90 102 94 94 94
250 400 370 320 370
36 58 54 46 54
18 15 12 15 12
150 190 190 190 190
650
94
320
46
12
190
640 640
93 93
280 270
41 39
15 16
165 160
25(1)
25(1) 25(1) 25(1) 25(1)
620 500
90 72 72
250 180 180
36 26 26
16 25 30
155 115 115
anneal temper
500
Machined
Extruded
Stamped
Squares
Section
Rounds
Drawn
Drawn
Plates
Mpa
Tubes
Rings
Discs
Flats
ksi
HRB
HV5
%
HB
Parts
Rods
39
Nominal composition %
Alloy
Standards Nearest international standards Electrical conductivity %IACS 8 8 12 12 8 9 6
Cu
Bi
O
Cr
Zr
Co
Be
Ni
Fe
Mn
Al
Si
Zn
Sn
Pb
P
Other
CuAl11Ni5Fe5
NCS
NFA 51-116 NFL 14-706 DIN 17665 WN 20978 DIN 17672 WN 20978 EN 12167, EN 12163, EN 12420 CW308G
remainder
5
5
11
7,5
AMS4590
AMS 4590 ASTM B150 : C63020
remainder
5
5
11
7,5
CuAl10Mn7Fe2
VNC
remainder
2,5
7
9
7,5
CuAl7Fe
VF7
ASTM B150 C61300 SAE J 463 C 641 DIN 17665 , DIN 17672 wn 2.0932
remainder
2,5
7
0,3
7,9
CuAl3Si
A3S
C 63600
remainder
3,5
1
8,3
CuSi3Fe2Zn3
SI45Z
AMS4616
remainder
1,5
3
3
8,6
CuZn23Al4MnFeNi
ZA4
NFL14708 ASTMB 138 C67000 alloy ASTMB171 C86200 alloy SAE J 461 CA 862 DIN 1709
remainder
1
2
2,5
5
23
7,8
CuZn19Al6MnFe
ZA9
NFL 14707 DIN 1709
remainder
3,5
5,5
7
18
7,6
Density
Forms/process
Mechanical properties
Available forms
Yield strength 0,2% offset or 0,5% E.U.L. (1)
Elongation 5,65 S
Physical properties Tensile strength
Impact strength KCU (1) or IZOD (2)
Forgings or stamped parts
Semi-finished products
Hardness
Tubes
Remarks Electrical resistivity at 20c cm Coefficient of expension 20 to 200 c x 10 - 6 K-1
Relative magnetic permeability
Thermal conductivity 20 to 200c W/mk
Young s modulus kN/mm2
Mpa ; * = Mpa
Extruded or forged
ksi ; * = Mpa
Forged blanks
Hexagones
740 22 40 16 1,5 125 .97 condition 740
107
390
57
8
185
107
440
64
5
185
19 25,4 - 0,75 in. 1 in. 22 40 16 125 25,4 < 50,8 - 1 in. < 2 in. 50,8 < 101,6 - 2 in. < 4 in.
931
135
689
100
6
255
896 896
130 130
655 621
95 90
6 6
255 255
16
120
690
320
13
170
25,4 < 50,8 mm - 1 in.< 2 in. HR50 temper 14 56 16 1,2 115 50,8 < 76,2 mm - 2 in.< 3 in. HR50 temper
495
72
275(1)
40(1)
30
485
70
240
(1)
35
(1)
30
14
57
17
110
stamped
316
46
80
12
30
30
21,5
30
17,5
110
cold worked temper H
540
78
340
49
12
150
as manufactured temper M
390
57
140
20
30
90
18
40
17
1,2
105
590
86
270
39
15
170
section 2000 mm - section 3,1in.2 28 35 17 1,2 110 section > 2000 mm - section > 3,1 in.2
830 780 780
120 113 113
590 540 540
86 78 78
10 7 7
225 225 225
Machined
Extruded
Stamped
Squares
Section
Rounds
Drawn
Drawn
Plates
Mpa
Tubes
Rings
Discs
Flats
ksi
HRB
HV5
%
HB
Parts
Rods
41
Nominal composition %
Alloy
Standards Nearest international standards Electrical conductivity %IACS 11 24 11
Cu
Bi
O
Cr
Zr
Co
Be
Ni
Fe
Mn
Al
Si
Zn
Sn
Pb
P
Other
CuZn39Pb2
LBU
NFL14710 NFA 51-105 EN 12164 CW612N ISO 426 DIN 17660 WN 20402 ASTMB124 C37700 ASTMB121 C35300 ASTMB283 C37700 SAE J 463 CA 377 BS 250 (CZ122)
remainder
39
0,5
2
8,4
CuZn36Ni2Mn
LB5
NFA 51-106 ISO 1338-426 DIN 17660 WN 20540
remainder
2
0,5
2
0,5
36
8,3
CuSn8,5P
BE10
DIN17662 WN 21030 EN 12163 CW453K NFL14703 ISO427 DTD 265 A QQB 750 D BS 2874 PB 104 SAE J 461 CA 521
remainder
8
0,15
8,8
TER = Quenched, cold worked and aged TR = Quenched and aged T= Quenched
Density
Physical properties
15 15 7 Electrical resistivity at 20c cm Thermal conductivity 20 to 200c W/mk 17 17,5 Coefficient of expension 20 to 200 c x 10 - 6 K-1 Relative magnetic permeability 100 105 115 Young s modulus kN/mm2 67 18
hard temper 1/2 hard temper section 2000 mm - section 3,1 in.2 1/2 hard temper section > 2000 mm - section> 3,1 in.2 1/2 hard temper section 25000 mm - section 38,75 in.2 1/2 hard temper Remarks Extruded or forged Drawn Extruded Drawn Rods Tubes Forgings or stamped parts 490 440 400 380 380 470 540 71 64 320 250 170 240 200 46 10 15 22 15 80 110 115 135 105 150 30 60 20 115 32 25 220 175 120 20 90 58 400 Mpa ; * = Mpa ksi ; * = Mpa Mpa ksi % HB HRB HV5 Impact strength KCU (1) or IZOD (2) Rounds Squares Flats Hexagones Section Tubes Plates Discs Rings Forged blanks Stamped Machined Parts Hardness Tensile strength
Forms/process
Yield strength 0,2% offset or 0,5% E.U.L. (1)
Mechanical properties
Elongation 5,65 S
Available forms
Semi-finished products
43
45
NOTES
Factory Z.I voie de Chlons - RD 977 51600 Suippes - France Tel. : +33 (0) 3 26 69 28 28 Fax : +33 (0) 3 26 70 16 82
Sales and Marketing 2 boulevard de Strasbourg 94130 Nogent-sur-Marne - France Tel. : +33 (0) 3 26 69 28 28 Fax : +33 (0) 1 43 94 61 32
Bronze Inox 10 avenue des Chtaigners 95153 Taverny cedex - France Tel. : +33 (0) 1 34 18 26 26 Fax : +33 (0) 1 39 60 04 292011 - Conception - ralisation : Bol dAir / www.bol-d-air.net - Crdit photos : Jean-Marie Proneau - Axing
Le Bronze Industriel Deutschland GmbH Auf dem Wrtenberg 2A D-35075 Gladenbach Tel. : +49 (0) 6462 / 916 95 - 0 Fax : +49 (0) 6462 / 916 95 - 20
Le Bronze Industriel North America (LBINA) C/O F.A.C.C The Merchandise Mart Suite 940 Chicago, II 60654 U.S.A
le Bronze Industriel Sige social/ Head office 3, avenue du Gnral Leclerc 51600 Suippes - France