Using the model and algorithm shown to the right, we obtain the theoretical images above. These images, with A=4.2*107 cm3/s (defect pixel) and A=8.2*104 cm3/s (non-defect pixels), produced the lowest error.
Photoluminescence images are obtained from an undoped GaAs/GaInP heterosturcture. The excitation intensity-dependent images shown above center on a native defect in the thin, passivated GaAs layer.
Imaging and modeling diffusion to defects in GaAsMac Read and Tim Gfroerer, Davidson College, Davidson, NCMark Wanlass, National Renewable Energy Lab, Golden, CO
AbstractDefect-related electron-hole recombination impairs the performance of many semiconductor devices. At high excitation, the density of electrons and holes is higher, so they encounter each other more frequently. Early encounters reduce the average lifetime and diffusion distance so the carriers are less likely to reach defects. We observe native defects in a GaAs epilayer where the area of the defect-dominated region depends strongly on excitation intensity. We model the behavior with a simulation that allows for lifetime-limited diffusion of carriers, and we report good qualitative agreement between the experimental and simulated images.
Motivation
Conduction Band
Valence Band
ENER
GY Defect Level
HEATHEAT
+
-
Conduction Band
Valence Band
LIGHT
+
Electrons can recombine with holes in semiconductors by hopping through localized defect states and releasing heat. This defect-related trapping and recombination process is a loss mechanism that reduces the efficiency of many semiconductor devices.
-
Defect-related Recombination Radiative Recombination
D
-
x
y D-
- +
d
+
-
--+
D
d
The carrier lifetime is determined by how long it takes an electron to find a suitable hole for recombination. At low excitation density, electrons are more likely to encounter a defect before a hole, allowing for defect-related trapping and recombination. At high excitation, the electrons and holes don’t live as long, reducing the diffusion length d and the probability of reaching a defect before radiative recombination occurs.
Low-excitation
Defect Electron Hole
DiffusionHigh-excitation
+
++
y
x
Experimental Setup
Low density
High density
A=4.2*107 cm3/s
A=8.2*104 cm3/s
Carrier density is reducedby diffusion to the defect
We model the defect as an isolated pixel with an augmented defect (A) coefficient. Diffusion to this pixel reduces the carrier density n near the defect, and since the brightness is proportional to the radiative rate Bn2, the adjacent region appears darker.
Diffusion to Defect Model
-
-
-
The defect-related recombination rate scales linearly with the carrier density n, while the radiative rate is proportional to n2. A and B are coefficients that set the magnitude of the defect and radiative rates, respectively.
2
2
__
_
BnAn
Bn
rateionrecombinattotal
rateradiativeefficiency
The radiative efficiency is the ratio of the radiative and total recombination rates:
The algorithm to find steady state carrier densities (n) follows a simple rate equation including generation, recombination, and Laplacian diffusion:
)()(
)()(2
22 t
dx
ndDAnBn
dE
Itn n
ex
ex
The Algorithm
Where Eex is the photon energy, d is the layer thickness, and Dn is the diffusion coefficient for electrons in GaAs.• The different A coefficients produce different recombination rates in the
defect and non-defect pixels, which yield different carrier densities.• We use Laplacian diffusion to determine the flux between adjacent pixels
during each time step and then calculate new carrier densities.• We allow the diffusion process to continue until the average lifetime of
the generated carriers is reached.• Then we adjust the defect and non-defect A coefficients to minimize the
error between model and experiment.
Conclusions• Even for high-quality semiconductor materials with few defects, diffusion can lead to significant
defect recombination at low excitation intensity.• At low density, carriers diffuse more readily to defective regions rather than recombining
radiatively, producing larger effective “dead” areas.• If the defect constant A is non-uniform throughout the sample, diffusion will contribute to a
reduction in net efficiency. • The behavior can be modeled by assigning a larger A coefficient to the defect and allowing
diffusion to control the density of carriers.• Although not shown here, our model also appears to be qualitatively consistent with preliminary
temperature-dependent measurements.
We thank Jeff Carapella for growing the test structures and the Donors of the American Chemical Society – Petroleum Research Fund for supporting this work.
Acknowledgment
Experimental Images
Modeling Results