Properties of Some Metals and Alloys
COPPER AND COPPER ALLOYS • WHITE METALS AND ALLOYS • A L U M I N U M A N D A L L O Y S • MAGNESIUM ALLOYS • TITANIUM ALLOYS • RESISTANCE HEATING ALLOYS • MAGNETIC ALLOYS • CON-TROLLED EXPANSION AND CON-STANT — MODULUS ALLOYS • NICKEL AND ALLOYS • MONEL* NICKEL-COPPER ALLOYS • INCOLOY* NICKEL-IRON-CHROMIUM ALLOYS • INCONEL* NICKEL-CHROMIUM-IRON ALLOYS • N I M O N I C * N I C K E L - C H R O M I U M ALLOYS • HASTELLOY* ALLOYS • CHLORIMET* ALLOYS • ILL IUM* ALLOYS • HIGH TEMPERATURE-HIGH STRENGTH ALLOYS • IRON AND STEEL ALLOYS • CAST IRON ALLOYS • WROUGHT STAINLESS STEEL • CAST CORROSION AND HEAT RESISTANT ALLOYS* REFRACTORY METALS AND A L L O Y S • P R E C I O U S M E T A L S
Copyright 1982, The International Nickel Company, Inc.
INTRODUCTION
The information assembled in this publication has been obtained from various sources. The chemical compositions and the mechanical and physical proper-ties are typical for the metals and alloys listed. The sources that have been most helpful are the metal and alloy producers, ALLOY DIGEST, WOLDMAN’S ENGI-NEERING ALLOYS, International Nickel’s publications and UNIFIED NUMBERING SYSTEM for METALS and ALLOYS.
These data are presented to facilitate general compari-son and are not intended for specification or design purposes. Variations from these typical values can be expected and will be dependent upon mill practice and material form and size. Strength is generally higher, and ductility correspondingly lower, in the smaller sizes of rods and bars and in cold-drawn wire; the converse is true for the larger sizes. In the case of carbon, alloy and hardenable stainless steels, mechanical proper-ties and hardnesses vary widely with the particular heat treatment used.
REFERENCES
Many of the alloys listed in this publication are marketed under well-known trademarks of their pro-ducers, and an effort has been made to associate such trademarks with the applicable materials listed herein. Such trademarks, together with their proprietors, are listed on page 84.
Specifications, mainly those published by the Amer-ican Society for Testing and Materials, are shown for many of the materials. Other specifications may also be available. Where specifications appear, their latest date of issue should apply. Sources of additional information on properties and specifications are shown on page 85.
This listing and the data were compiled from sources believed reliable; however, possible errors and/or omissions may exist. We would welcome corrections or suggestions for use in periodically revising the publica-tion. Thus your interest and help will contribute in making it as accurate as possible with up-to-date information.
Properties of Some Metals and Alloys
*See page 84 for list of trademarks.
Page Bronze, Wrought
Aluminum (C61400) .............................................................. 4 High Silicon (C65500) ........................................................... 6 Nickel-Aluminum (C63200) .................................................. 6 Phosphor(C51000) ................................................................ 4 Phosphor (C52400)................................................................ 4
Carbon Steel ...............................................................................46 CARPENTER* No.10 .................................................................60 CARPENTER 20Cb-3* ...............................................................60 Cast Iron Alloys (see Iron, Cast) CHLORIMET* 2 ...........................................................................38 CHLORIMET* 3 ...........................................................................38 Coinage Alloy ................................................................................ 6 Columbium ...................................................................................78 Columbium-Tantalum-Tungsten Alloy .......................................78 Columbium-Vanadium Alloy .......................................................78 Columbium-Zirconium Alloy .......................................................78 Constantan .................................................................................... 6 Controlled Expansion Alloys ......................................................24 Copper Alloys, Cast
C83600 (Leaded Red Brass) ............................................... 8 C90300 (M Bronze) ............................................................... 8 C90500 (G Bronze) ............................................................... 8 C93200 (Leaded Tin Bronze) ............................................... 8 C94700 (Nickel-Tin Bronze, Type A) ................................... 8 C94800 (Nickel-Tin Bronze, Type B) ................................... 8 C95800 (Nickel-Alumimum Bronze) .................................... 8 C96200(Copper-Nickel) ....................................................... 8 C96400(Copper-Nickel) ......................................................10 C97300 (Nickel Silver) ........................................................10 C97600 (Nickel Silver) ........................................................10 C97800 (Nickel Silver) ........................................................10
Copper Alloys, Wrought C11000(Copper) .................................................................... 4 C17000 (Copper Beryllium) .................................................. 4 C17200 (Copper Beryllium) .................................................. 4 C17500 (Copper Beryllium) .................................................. 4 C17600 (Copper Beryllium 50) ............................................ 4 C23000 (Red Brass) ............................................................. 4 C26000 (Cartridge Brass) ..................................................... 4 C27000 (Yellow Brass) ......................................................... 4 C28000 (Muntz Metal) .......................................................... 4 C44300 (Admiralty Brass) .................................................... 4 C44400 (Admiralty Brass) .................................................... 4 C44500 (Admiralty Brass) .................................................... 4 C46400 (Naval Brass) ........................................................... 4 C51000 (Phosphor Bronze) ................................................. 4 C52400 (Phosphor Bronze) ................................................. 4 C61400 (Aluminum Bronze) ................................................. 4 C63200 (Nickel-Aluminum Bronze) ..................................... 6 C65500 (High Silicon Bronze) .............................................. 6 C70600 (Copper Nickel, 90-10 + Fe) .................................. 6 C71000 (Copper Nickel, 79-21) ........................................... 6 C71300 (Copper Nickel) ....................................................... 6 C71500 (Copper Nickel, 70-30 + Fe) .................................. 6 C71640 (Copper Nickel) ....................................................... 6 C72200 (Copper Nickel) ....................................................... 6 C72500 (Copper-Nickel-Tin) ................................................ 6 C72600 (Copper-Nickel-Tin) ................................................ 6 C72700 (Copper-Nickel-Tin) ................................................ 6 C72800 (Copper-Nickel-Tin) ................................................ 6 C72900 (Copper-Nickel-Tin) ................................................ 6 C73500 (Nickel Silver) .......................................................... 8 C75200 (Nickel Silver) .......................................................... 8 C76600 (Nickel Silver) .......................................................... 8 C77000 (Nickel Silver) .......................................................... 8
Copper Beryllium Alloys C17000,C17200,C17500 & C17600 ................................... 4 Copper-Nickel Alloys C70600, C71000, C71300, C71500, C71640 & C72200.................................................................................... 6 (55-45) .................................................................................... 6 Castings .............................................................................8,10 Copper-Nickel-Tin Alloys C72500, C72600, C72700, C72800 & C72900 .................. 6 Cunico ...........................................................................................22 Cunife ............................................................................................22 CUSTOM 455* Stainless Steel ..................................................64
Page D-979 Alloy ............................................................................46 DISCALOY* ...........................................................................46 DURANICKEL* Alloy 301......................................................26 Ductile Irons...........................................................................52 DURIRON* ............................................................................54 DURICHLOR*........................................................................54 DURIMET* 20 Stainless Steel, Cast.....................................74 E-BRITE* ...............................................................................68 ELINVAR*..............................................................................24 EVANOHM* ...........................................................................20 FERRALIUM* Alloy 255 ........................................................60 GMR 235D Alloy....................................................................38 Gold
Pure ................................................................................80 18K White .......................................................................80 WE. No. 1 .......................................................................80
Greek Ascoloy Stainless Steel..............................................66 HASTELLOY* alloys
B-2, C-276 & C-4............................................................34 G, G-3, N, S & W............................................................36 X .....................................................................................38 M-532 .............................................................................60
HAYNES* alloy 25 & 188 .........................................................................42 556..................................................................................40
Heat Resistant Alloys, Cast HA, HC & HD..................................................................74 HE, HF, HH, HI, HK, HL, HN, HP HP50-WZ, HT & HU............................................................................76 HW & HX ........................................................................78 IN-657.............................................................................76 IN-519.............................................................................78
High-Temperature High-Strength Alloys GMR 2350 ......................................................................38 713C, 713LC, 901, HAYNES* 556, A-286, IN-100 &IN-102....................................................................40 IN-738, IN-792, IN-939, L-605, HAYNES* 188 & MAR-M* 246 ............................................................42 M-252, RENE 41*, RA 333*, S-816, TO Nickel, UDIMET* 500, UDIMET* 700 & WI-52 ...................44 Waspaloy, B-1900, D-979, X-40, N-155 & DISCALOY* ............................................................ 46
High-Yield-Strength Alloy Steels...........................................50 ILLIUM* alloys
B, G & 98 ........................................................................38 P .....................................................................................74
IN-100 Alloy ...........................................................................40 IN-102 Alloy .......................................................................... 4C IN-519 Alloy ...........................................................................78 IN-657 Alloy ...........................................................................76 IN-738 Alloy ...........................................................................42 IN-787 Alloy Steel..................................................................50 IN-792 Alloy ...........................................................................42 IN-849 Stainless Steel...........................................................74 IN-862 Stainless Steel...........................................................74 IN-939 Alloy ...........................................................................42 INCOLOY* alloys
800,801,802 & 825.........................................................30 903..................................................................................24
INCONEL* alloys 600, 601, 611 & 617.......................................................30 625, 690, 718, X-750 & 751...........................................32
Ingot Iron................................................................................ 46 INVAR* ..................................................................................24 Iridium ....................................................................................80 Iron, Cast
Gray ................................................................................52 Ductile.............................................................................52 Malleable ........................................................................52 Ni-Hard, Types 1, 2 & 4 .................................................54 Ni-Resist, Types 1, 2, 5 & D2 ........................................52 Types D5 & D-5S ...........................................................54 Iron-Silicon Alloy (DURIRON*) ......................................54 Iron-Silicon-Molybdenum Alloy (DURICHLOR*) ...........54
Page 2½% Nickel Steel, Cast ..............................................................50 3½% Nickel Steel ........................................................................48 3½% Nickel Steel, Cast ..............................................................50 9% Nickel Steel ............................................................................50 15-5 PH* Stainless Steel ............................................................64 17-4 PH* Stainless Steel ............................................................64 17-7 PH* Stainless Steel ............................................................64 17-14 Cu Mo Stainless Steel ......................................................66 18-9 LW* Stainless Steel ............................................................62 18K White Gold ...........................................................................80 19-9 DL Alloy ................................................................................66 29-4 Stainless Steel ....................................................................68 29-4-2 Stainless Steel .................................................................68 35-20 Ni Cr bal Fe Alloy...............................................................20 38-7 Ni Cr + Fe Alloy ...................................................................24 42% Ni Fe Alloy............................................................................24 49% Ni Fe Controlled Expansion Alloy .....................................24 49% Ni Fe Magnetic Alloy ...........................................................22 60-15 Ni Cr bal Fe Alloy ..............................................................20 79-4 Ni Mo bal Fe Alloy ..............................................................22 80-20 Ni Cr Alloy ..........................................................................20 200 ALLOY*..................................................................................20 300M Alloy Steel .........................................................................48 611 Alloy, Cast .............................................................................30 625 Alloy, Cast ............................................................................32 713C Alloy.....................................................................................40 713LC Alloy ..................................................................................40 901 Alloy .......................................................................................40 904 L Stainless Steel ..................................................................60 9310 Alloy Steel............................................................................48 A-286 Alloy....................................................................................40 AISI 4340 Alloy Steel ..................................................................48 AISI 4620 Alloy Steel ..................................................................48 AISI 4820 Alloy Steel ..................................................................48 AISI 8620 Alloy Steel ..................................................................48 AL6X* Stainless Steel .................................................................60 ALCHROME*................................................................................20 ALOYCO* 20 Stainless Steel, Cast ...........................................74 Alnico Alloys (Permanent Magnet Alloys) II ............................................................................................ 20 III, IV, V, VI, VII & VIII ...........................................................22 Aluminum Alloys, Cast
413.0 ......................................................................................12 B443.0, A380.0, 295.0, 514.0, 520.0, 336.0 & 242.0 .........14
Aluminum Alloys, Wrought 1100, 2017, Alclad 2024, 3003, 5052, 6061 & 7075.........12 AM 350* Stainless Steel ..............................................................64 AM 355* Stainless Steel ..............................................................64 Antimony .......................................................................................10 B-1900 Alloy ................................................................................46 Bismuth-Lead Alloy .....................................................................10 Bi-Pb-Sn-Cd Alloy .......................................................................10 Bi-Pb-In-Cd-Sn Alloy ...................................................................10 Bismuth-Tin Alloy ........................................................................10 Brass, Cast Leaded Red Brass (C83600) ...............................................8 Brass, Wrought
Admiralty (C44300, C44400 & C44500) ...............................4 Cartridge (C26000) ..................................................................4 Naval (C46400) ........................................................................4 Red(C23000)............................................................................4
Yellow (C27000).......................................................................4 Bronze, Cast G(C90500) ............................................................................. 8 M(C90300) ............................................................................. 8
Leaded Tin (C93200) ............................................................8 Nickel-Aluminum (C95800) ..................................................8 Nickel-Tin, Type A (C94700) .................................................8 Nickel-Tin, Type B (C94800) .................................................8
INDEX
Page Iron, Wrought .........................................................................46 Iron-Chromium-Aluminum Alloy ............................................20 Iron-Nickel Temperature Compensating Alloys ....................24 ISO-ELASTIC* .......................................................................24 JESSOP JS700*....................................................................60 JESSOP JS777*....................................................................60 JESSOP* Type 317L Plus.....................................................58 KANTHAL*.............................................................................20 KARMA*.................................................................................20 KOVAR*.................................................................................24 L-605 Alloy.............................................................................42 Lead
Pure ................................................................................10 Antimonial .......................................................................10 Tellurium.........................................................................10
Lead-Tin Solders 50-50 & 40-60.................................................................10 M-252 Alloy............................................................................44 Magnesium Alloys
AZ 318, AZ 80A, AZ 918, AZ 91C & AZ 92A.................14 EZ 33A & HK 31A...........................................................14 HZ 32A & ZK 60A...........................................................16
Magnetic Alloys ................................................................20,22 Malleable Iron ........................................................................52 Manganese Alloy 772............................................................12 Maraging Steels 18-200,18-250,18-300....................................................50 MAR-M* 246 Alloy .................................................................42 Moly Permalloy 4/79..............................................................22 Molybdenum ..........................................................................78 Molybdenum—0.5% Titanium Alloy ......................................78 MONEL* Alloys
400, 401, 404, R-405 & K-500 .......................................28 410 (Cast), 411 (Cast) & 505 (Cast) ..............................28
Mu Metal ................................................................................20 Muntz Metal (C28000) .............................................................4 N-155 Alloy ............................................................................46 Nickel Alloys, Cast
Nickel 210.......................................................................26 Nickel Beryllium M2206..................................................26 Nickel Beryllium CR-1 ....................................................26
Nickel Alloys, Wrought 200, 201, 205, 211 & 270...............................................26 Nickel Beryllium 440.......................................................26 DURANICKEL* Alloy 301...............................................26 PERMANICKEL* Alloy 300 ............................................26 TD Nickel ........................................................................44
Nickel-Chromium Alloys 80-20...............................................................................20 60-15 + Fe ......................................................................20 35-20 + Fe ......................................................................20
Nickel-Chromium-Aluminum Alloy ........................................20 Nickel-Chromium-Iron Alloys (see INCONEL*) Nickel-Copper Alloys (see MONEL*) Nickel-Iron Alloys
Controlled expansion alloy .............................................24 Magnetic alloy.................................................................22
Nickel-Iron-Chromium Alloys (see INCOLOY*) Nickel-Iron-Cobalt Alloy.........................................................24 Nickel-Molybdenum Alloy (80-4) ...........................................22 Nickel Silver Alloys, Cast C97300, C97600 & C97800...........................................10 Nickel Silver Alloys, Wrought C73500, C75200, C76600 & C77000..............................8 Nickel-Titanium Alloy (Nitinol) ...............................................28 Ni-Hard Cast Irons Types 1, 2 & 4 ................................................................54 NIKROTHAL*.........................................................................20 NIMONIC* Alloys 75, 80A, 90 & 115...........................................................34 Ni-Resist Cast Irons
Types 1, 2, 5 & D-2 ........................................................52 Types D5 & D-5S ...........................................................54
NI-SPAN C* ...........................................................................24 Nitinol Memory Alloy..............................................................28
*See page 84 for list of trademarks.
Page NITRALLOY* N Alloy Steel ...................................................48 NITRONIC* Stainless Steels 20, 32, 33, 40, 50 & 60...................................................62 Non-Galling Alloys
WAUKESHA METAL* No. 23.........................................26 WAUKESHA METAL* No.88..........................................28
Palladium ...............................................................................80 Palladium Alloy No. 934 ........................................................82 Palladium-Ruthenium Alloy ...................................................82 Palladium-Silver Alloy............................................................82 Permalloy 49..........................................................................22 PERMANICKEL* Alloy 300 ...................................................26 PH 13-8 Mo* Stainless Steel .................................................64 PH 14-8 Mo* Stainless Steel .................................................64 PH 15-7 Mo* Stainless Steel .................................................64 Platinum .................................................................................80 Platinum-Iridium Alloy............................................................80 Platinum-Rhodium Alloy ........................................................82 Platinum-Ruthenium Alloy .....................................................82 Precious Metals & Alloys.................................................80, 82
RA 333* Alloy.........................................................................44 Refractory Metals & Alloys ..............................................78, 80 RENÉ 41* Alloy......................................................................44 Resistance Heating Alloys.....................................................20 Rhodium.................................................................................80 RODAR*.................................................................................24 Ruthenium..............................................................................82
S-816 Alloy ............................................................................44 SAE 1020 Steel .....................................................................46 SANDUSKY* Alloy 75............................................................74 SEA-CURE* Stainless Steel..................................................68 Silver
Coin.................................................................................80 Fine .................................................................................80 Sterling............................................................................80
Silver Brazing Alloys EASY-FLOW* .................................................................80 R-T Alloy .........................................................................80
Solders 50-50(Sn-Pb) ..................................................................10 60-40(Sn-Pb) ..................................................................10
Stainless Steels, Cast CA-15, CA-40, CA-6NM & CB-7 Cu-1 ...........................68 CB-7 Cu-2, CB-30, CC-50 & CE-30...............................68 CF-3, CF-8, CF-3M & CF-8M.........................................68 CF-8C, CF-16F & CF-20 ................................................68 CG-8M, CH-20, CK-20, & CN-7M ..................................72 CD-4MCu, CW-12M-1 & CW-12M-2..............................72 N-12M-1 & N-12M-2 .......................................................72 ALOYCO* 20 ..................................................................74 DURIMET* 20.................................................................74 ILLIUM* P .......................................................................74 IN-849 .............................................................................74 IN-862 .............................................................................74 SANDUSKY* Alloy 75 ....................................................74
Stainless Steels, Wrought .....................................................54 Types 201, 202 & 301 ....................................................56 Types 302, 303, 303 Se & 304 ......................................56 Types 304L, 304 +,Boron & 305 ....................................56 Types 309, 310 &, 314 ...................................................56 Types 316, 316L, 317 & 317LM* ...................................56 Types 321, 329, 330 & 347 ............................................58 Types 405, 409, 410 & 414 ............................................66 Types 402, 430 & 431 ....................................................66 Types 440C & 446..........................................................68 15-5PH*,17-4PH* & 17-7PH*.........................................64 17-14 Cu Mc ...................................................................66 18-9LW*..........................................................................62 19-9 DL ...........................................................................66 29-4.................................................................................68 29-4-2..............................................................................68 904L ................................................................................60 AL-6X* ............................................................................60 AM 350* & AM 355* .......................................................64 CARPENTER* No. 10 ....................................................60 CARPENTER 20Cb-3* ...................................................60 CUSTOM 455*................................................................64 E-BRITE* 26-1................................................................68
Page FERRALIUM* 255 ..........................................................60 Greek Ascoloy ................................................................66 HASTELLOY* M-352 .....................................................60 JESSOP* JS700 & JS777..............................................60 NITRONIC* 20, 32, 33, 40, 50 & 60 ..............................62 PH 13-8 Mo*, PH 14-8 Mo* & PH 15-7 Mo* ..................64 SEA-CURE* ...................................................................68 STAINLESS “W”* ...........................................................64
Steel, Alloy 3½% Nickel ....................................................................48 9% Nickel........................................................................50 300M...............................................................................48 9310................................................................................48 AISI 4340, 4620, 4820 & 8620.......................................48 High-Yield-Strength........................................................50 IN-787.............................................................................50 Maraging 18-200,18-250 & 18-300................................50 NITRALLOY* N ..............................................................48
Steel, Carbon.........................................................................46 Steel, Cast
2½% Nickel ....................................................................50 3½% Nickel ....................................................................50
Super-Invar ............................................................................ 24 Tantalum................................................................................ 78 TD Nickel ...............................................................................44 THERLO*...............................................................................24 Tin ..........................................................................................10 TINEL* Alloy A.......................................................................28 Titanium Alloys
Ti-35A, Ti-50A & Ti-75A.................................................16 Ti-0.2 Pd .........................................................................16 Ti-5 AI-2.5 Sn .................................................................16 Ti-8 AI-1 Mo-1 V .............................................................16 Ti-6 AI-2 Sn-4 Zr-2 Mo ...................................................18 Ti-6 AI-6 V-2 Sn..............................................................18 Ti-6 AI-4 V ......................................................................18 Ti-6 AI-2 Sn-4 Zr-6 Mo ...................................................18 Ti-13 V-11 Cr-3 AI ..........................................................18 Ti-10 V-2 Fe-3 Al ............................................................20 Ti Code 12......................................................................18 TINEL* Alloy A................................................................28
Tungsten................................................................................ 78 Tungsten Alloys
Tungsten - 2.5 (Ni + Cu) ................................................78 Tungsten - 7.5 Ni-2.5 Cu................................................78 Tungsten - Rhenium.......................................................78
UDIMET* Alloy 500 ...............................................................44 UDIMET* Alloy 700 ...............................................................44 Uranium .................................................................................80 Waspaloy ............................................................................... 46 WAUKESHA METAL*
No. 23 .............................................................................26 No. 88 .............................................................................28
White Gold, 18K ....................................................................80 WI-52 Alloy ............................................................................44 Wrought Iron..........................................................................46 X-40 Alloy ..............................................................................46 YORCORON* ..........................................................................6 ZILLOY* 15............................................................................12 Zinc ........................................................................................12 Zinc Alloys
Zinc - 4 AI .......................................................................12 Zinc - 4 Al-1 Cu ..............................................................12
Zirconium............................................................................... 80 Zirconium-Hafnium Alloy .......................................................80
INDEX
4
PROPERTIES OF SOME METALS AND ALLOYS
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C O P P E R A N D C O P P E R A L L O Y S
Copper C11000 Sheet—ASTM B 152 Rod—ASTM B 124, B 133 Wire—ASTM B 1, B 2, B 3
Cu —99.90 min
Strip Annealed
Spring Temper
10a
50a
32
55
45
4
RF40
RB60
Copper Beryllium C17000 Plate, Sheet & Strip—ASTM B 194 Rod—ASTM B 124
Cu —bal Be —1.7 Co —0.25
Strip Annealed plus age
Hard plus age
145
170
165
190
7
3
RC35
RC40
Copper Beryllium C17200 Sheet & Strip—ASTM B 194 Wire—ASTM B 197 Rod—ASTM B 196
Cu —bal Be —1.9 Co —0.25
Strip Annealed plus age
Hard plus age
150
180
175
200
6
2
RC38
RC42
Copper Beryllium C17500 Plate, Sheet & Strip—ASTM B 534 Rod—ASTM B 441
Cu —bal Be —0.6 Co —2.5
Annealed plus age
Hard plus age
90
110
110
120
11
8
RB96
RB99
Copper Beryllium 50 C17600
Cu —bal Be —0.38 Co —1.55 Ag —1
Bar Annealed plus age
½ Hard plus age
90
110
110
120
17
14
RB96
RB99
Red Brass C23000 Strip, Sheet, Plate & Bar—ASTM B 36 Wire—ASTM B 134 Tube—ASTM B 135
Cu —85 Zn —15
Strip Annealed
Hard Temper
15a
60a
40
75
50
7
50
135
Cartridge Brass C26000 Sheet—ASTM B 19 Plate—ASTM B 36 Wire—ASTM B 134 Tube—ASTM B 135
Cu —70 Zn —30
Strip Annealed
Spring Temper
11a
65a
44
94
66
3
RF54
RB91
Yellow Brass C27000 Strip, Sheet, Plate & Bar—ASTM B 36 Tube—ASTM B 135 & B 587 Wire—ASTM B 134
Cu —65 Zn —bal
Strip Annealed
Spring Temper
14a
62a
46
91
65
30
RF58
RB90
Muntz Metal C28000 Tube—ASTM B 135 Tube—ASTM B 111
Cu —61 Zn —bal
Annealed
½ Hard
21a
50a
54
70
45
10
RF80
RB75
Admiralty Brass C44300, C44400, C44500 Plate—ASTM B 171 Tube—ASTM B 111 & B 543
Cu —71 Zn —bal Sn —1 As, Sb or P—0.06
Annealed
22a
53
65
RF75
Naval Brass C46400 Rods, Bars & Shapes—ASTM B 21 Plate—ASTM B 171
Cu —60.5 Zn —bal Sn —0.75
Annealed
¼ Hard
25a
58a
58
70
49
17
RB56
RB75
Phosphor Bronze C51000 Sheet—ASTM B 103 Rod—ASTM B 139 Wire—ASTM B 159
Cu —bal Sn —5 P —0.2
Annealed
Spring Temper
19a
80a
47
100
64
4
RF73
RB95
Prosphor Bronze C52400 Sheet—ASTM B 103 Rod—ASTM B 139 Wire—ASTM B 159
Cu —bal Sn —10 P —0.2
Annealed
Spring Temper
28a
—
66
122
68
4
RB55
RB101
Aluminum Bronze C61400 Sheet—ASTM 8 169 Rod—ASTM B 124, B 150 Pipe—ASTM B 315 & B 608
Cu —bal AI —7 Fe —2.5
Soft
Hard
45a
60a
82
89
40
32
RB84
RB87
a = 0.5% extension under load
5
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C O P P E R A N D C O P P E R A L L O Y S
0.322
—
8.91
—
1980
—
0.092
—
9.41
9.82
2512
3
—
10.3
—
17
—
6.4
—
Copper C11000
0.298
—
8.26
—
1600 to 1800
—
—
—
9.3
—
7503 to 900
—
39
—
—
—
—
—
Copper Beryllium C17000
0.298
—
8.26
—
1600 to 1800
—
0.10
—
9.3
—
7503 to 900
—
39
—
19
17
7.3
6.5
Copper Beryllium C17200
0.316
—
8.75
—
1885 to 1955
—
—
—
9.84
—
14503 to 1800
—
20
—
—
—
—
—
Copper Beryllium C17500
0.316
—
8.75
—
1850 to 1900
—
—
—
9.82
—
15003 to 1700
—
19
—
—
—
—
—
Copper Beryllium 50 C17600
0.316
—
8.75
—
1880
—
0.09
—
10.42
—
11043
—
28
—
17
—
6.4
—
Red Brass C23000
0.308
—
8.53
—
1750
—
0.09
—
11.12
—
8403
—
37
—
16
—
6.0
—
Cartridge Brass C26000
0.306
8.47
1710
0.09
11.32
8043
38.4
15
5.6
Yellow Brass C27000
0.303 8.39 1660 0.09 11.62 8523 37 15 5.6 Muntz Metal
C28000
0.308
8.53
1720
0.09
11.22
7683
41.5
16
6.0
Admiralty Brass C44300 C44400 C44500
0.304 8.41 1650 0.09 11.82 804 39.9 15 5.6 Naval Brass
C46400
0.320
—
8.86
—
1920
—
0.09
—
9.92
—
4803
—
69.1
—
16
—
6
—
Phosphor Bronze C51000
0.317
—
8.78
—
1830
—
0.09
—
10.22
—
3483
—
94.3
—
16
—
6
—
Phosphor Bronze C52400
0.285
—
7.89
—
1915
—
0.09
—
9.022
—
4683
—
74.1
—
17
—
6.4
—
Aluminum Bronze C61400
1 = 68 to 212°F 2 = 68 to 572°F 3 = at 68°F 4 = 68 to 392°F
6
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C O P P E R A N D C O P P E R A L L O Y S ( C o n t i n u e d )
Nickel-Aluminum Bronze C63200 Rod, Bar & Shapes—ASTM B 150
Cu —82 AI —9 Ni —5 Fe —4
Rod Annealed 52a 103 24 RB94
High Silicon Bronze C65500 Sheet—ASTM B 96 & B 97 Rod—ASTM B 98 & B 124 Wire—ASTM B 99
Cu —bal Si — 3.3
Annealed Spring Temper
21a 62a
56 110
63 4
RB76 RB97
Copper-Nickel C70600 Tube—ASTM B 111 & B 552 Plate—ASTM B 171 & B 402 Rod—ASTM B 151
Cu —bal Ni —10 Fe — 1.25 Mn — 0.3
Tube Annealed Light Drawn
16a 57a
44 60
42 10
RB65 RB72
Copper-Nickel C71000 Sheet, Strip, Plate & Bar—ASTM B 122 Pipe & Tube—ASTM B 466 Wire—ASTM B 206
Cu —79 Ni —21
Strip Annealed Spring Temper
14 79
52 82
35 3
RB27 RB84
Copper-Nickel C71300 (Coinage Alloy)
Cu —bal Ni —25 Zn — 1 max Mn — 1 max
Annealed Spring Temper
18 82
52 86
42 6
RF79 RB89
Copper-Nickel C71500 Sheet—ASTM B 122 Plate—ASTM B 171 Tube—ASTM B 111
Cu —bal Ni —30 Fe — 0.55 Mn — 0.5
Tube Annealed 25a 60 45 RB45
Copper-Nickel C71640 (YORCORON*)
Cu —bal Ni —30 Fe —2 Mn — 2
Plate Annealed Plate Hard
29 98
67 104
45 6
107 194
Copper-Nickel C72200 Plate, Sheet, Strip & Bar—ASTM B 122 & B 402 Tube—ASTM B 111
Cu —bal Ni —16 Fe —0.8 Cr —0.5 Mn —0.5
Annealed 18 46 46 RB30
Copper-Nickel 55-45 (Constantan, etc.)
Cu —55 Ni —45
Annealed
Cold Worked
21a
—
60
135
32
2
80
250
Copper-Nickel-Tin C72500 Plate, Sheet, Strip & Bar—ASTM B 122
Cu —bal Ni —9.5 Sn —2.3
Soft
Hard
22
81
55
83
35
3
RB42
RB85
Cu-Ni-Sn Spinodal Alloy C72600
Cu —92 Ni —4 Sn —4
Strip 53% Cold worked, aged
95 101 649 —
Cu-Ni-Sn Spinodal Alloy C72700
Cu —85 Ni — 9 Sn —6
Strip 50% Cold worked, aged
143
50 163 4 —
Cu-Ni-Sn Spinodal Alloy C72800
Cu —81.8 Ni —9 Sn —8 Cb —0.2
Strip 1/4 hard, Aged
155
170
7
RC36
Cu-Ni-Sn Spinodal Alloy C72900
Cu —77 Ni —15 Sn —8
Strip 78% Cold worked, aged
162
50 178 2 —
*See page 84 for list of trademarks a = 0.5% extension under load 49 = in 1 in. 50 = 0.05 % offset
PROPERTIES OF SOME METALS AND ALLOYS
7
2 = 68 to 572°F 3 = at 68°F 5 = at 77°F
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C O P P E R A N D C O P P E R A L L O Y S ( c o n t i n u e d )
0.276
7.64
1905-1940
0.1053
9.02
240
3
148
17
6.4
Nickel-AluminumBronze C63200
0.308
—
8.53
—
1880
—
0.09
—
10.02
—
252
3
—
148
—
15
—
5.6
—
High Silicon Bronze C65500
0.323
—
8.94
—
2100
—
0.09
—
9.52
—
312
3
—
115
—
18
—
6.8
—
Copper-Nickel C70600
0.323
—
8.94
—
2100-2190
—
0.09
—
9.12
—
252
3
—
160
—
20
—
7.5
—
Copper-Nickel C71000
0.323
—
8.94
—
2225
—
—
—
—
—
—
—
193
—
—
—
—
—
Copper-Nickel C71300 (Coinage Alloy)
0.323
8.94
2260
0.09
9.02
204
3
225
22
8.3
Copper-Nickel C71500
0.323
—
8.86
—
—
—
—
—
8.33
—
173
3
—
301
—
22
—
—
—
Copper-Nickel C71640 (YORCORON*)
0.323
8.94
2052-2148
0.0943
8.82
139
3
159
5
20
8.2
Copper-Nickel C72200
0.321
—
8.89
—
2355
—
—
—
8.28
—
155
—
300
—
24
—
—
—
Copper-Nickel 55-45 (Constantan, etc.)
0.321
—
8.89
—
2065
—
—
—
9.22
—
372
3
—
94.3
—
20
—
7.5
—
Copper-Nickel-TinC72500
0.321 8.89 1950 — — — 69 16 — Cu-Ni-Sn
Spinodal AlloyC72600
0.321 8.89 2012 — — — 94 17 — Cu-Ni-Sn
Spinodal AlloyC72700
0.321
8.89
2012
—
—
—
104
17
—
Cu-Ni-Sn Spinodal AlloyC72800
0.321 8.89 2039 — — — 147 18 — Cu-Ni-Sn
Spinodal AlloyC72900
8
Typical Mechanical Properties
Material
Nominal Composition%
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C O P P E R A N D C O P P E R A L L O Y S ( c o n t i n u e d )
Nickel Silver C73500 Sheet, Strip, Plate & Bar—ASTM B 122
Cu —72 Zn —bal Ni —18
Soft
Hard
22a
65a
55
78
40
5
RB35
RB85
Nickel Silver C75200 Sheet, Strip, Plate & Bar—ASTM B 122 Wire-ASTM B 206
Cu —65 Zn —bal Ni —18
Annealed
Hard
25a
74a
58
85
40
3
RB40
RB87
Nickel Silver C76600
Cu —56.5 Zn —bal Ni —12
Soft
Hard
24a
65a
60
97
40
5
RB45
RB88
Nickel Silver C77000 Sheet, Strip, Plate & Bar—ASTM B 122 Rod & Bar—ASTM B 151 Wire—ASTM B 206
Cu —55 Zn —bal Ni —18
Annealed
Hard
27a
85a
60
100
40
3
RB55
RH91
Leaded Red Brass C83600 (85-5-5-5) Castings—ASTM B 62, B 271, B 505 & B 584
Cu —85 Zn — 5 Pb — 5 Sn — 5
As Cast
17a
35
25
60
6 Bronze C90500 (88-10-0-2) Castings—ASTM B 22, B 271, B 505 & B 584
Cu —bal Sn —10 Zn — 2
As Cast 21a 45 31 80
M Bronze C90300 (88-8-0-4) Casting—ASTM B 271, B 505 & B 584
Cu —bal Sn — 8.5 Zn — 4
As Cast 22a 52 48 70
Leaded Tin Bronze C93200 (83-7-7-3) Casting—ASTM B 271, B 505 & B 584
Cu —83 Sn — 7 Pb — 7 Zn — 3
As Cast
19a
34
18
60
Nickel-Tin Bronze Type A C94700 Castings—ASTM B 505 & B 584
Cu —bal Ni — 5 Sn — 5 Zn — 2
As Cast
Heat Treated 1400°F MO.) and 600°F
23a
60a
50
85
35
10
85
180
Nickel-Tin Bronze Type B C94800 Casting—ASTM B 505 & B 584
Cu —bal Ni — 5 Sn — 5 Pb — 1 Zn — 2
As Cast
Aged (575°F)
23a
30a
50
60
35
8
80
120
Nickel-Aluminum Bronze C95800 Castings—ASTM B 148, B 271 & B 505; & MIL-B-21230
Cu —81 AI — 9 Ni — 5 Fe —4 Mn — I
As Cast
38a
95
25
159
Copper-Nickel C96200 Castings—ASTM B 369
Cu —bal Ni —10 Mn — 0.9 Fe — 1.4 Si — 0.2 Cb — 0.5
As Cast
25
45
30
90
a = 0.5% extension under load
PROPERTIES OF SOME METALS AND ALLOYS
9
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C O P P E R A N D C O P P E R A L L O Y S ( c o n t i n u e d )
0.319
—
8.82 —
2100
—
—
—
—
—
—
—
—
—
—
—
—
—
Nickel Silver C73500
0.316
—
8.73 —
2030
—
0.09 —
9.02
—
228
3
—
173
—
18
—
6.8
—
Nickel Silver C75200
0.310
—
8.58 —
1832
—
—
—
—
—
264
3
—
189
—
—
—
—
—
Nickel Silver C76600
0.314
—
8.70
—
1930
—
0.09
—
9.32
—
204
3
—
189
—
18
—
6.8
—
Nickel Silver C77000
0.317
8.75
1840
—
10.2
500
63
13
—
Leaded Red BrassC83600 (85-5-5-5)
0.315 8.72 1800 — — — — 15 — G Bronze
C90500 (88-10-0-1)0
0.318 8.80 1832 — 102 — — 14 — M Bronze
C90300 (88-8-0-4)
0.322
8.93
1800
—
10
—
—
14.5
—
Leaded Tin BronzeC93200 (83-7-7-3)
0.320
—
8.86 —
1880
—
0.093
—
114
—
374
3
—
—
—
15
—
—
—
Nickel-Tin BronzeType A C94700
0.320
—
8.86 —
1880
—
0.093
—
112
—
268
3
—
—
—
15
14
—
—
Nickel-Tin BronzeType B C94800
0.276
7.64
1910—1940
0.1053
9.02
250
3
—
16
—
Nickel-Aluminum Bronze C95800
0.323
8.94
2100
—
9.52
—
—
17
—
Copper Nickel C96200
2 = 68 to 572°F 3 = at 68°F 4 = 68 to 392°F
10
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C O P P E R A N D C O P P E R A L L O Y S ( c o n t i n u e d )
Copper-Nickel C96400 Castings—ASTM B 369 & B 505
Cu — bal Ni — 30 Mn — 0.8 Fe — 0.8 Si — 0.4 Cb — 0.7
As Cast
40b
75b
25b
120b
Nickel Silver C97300 Castings—ASTM B 271, B 505 & B 584
Cu — bal Zn — 20 Ni — 12 Pb — 9 Sn — 2
As Cast 18 35 15 55
Nickel Silver C97600 Castings—ASTM B 271, B 505 & B 584
Cu — bal Zn — 8 Ni — 20 Pb — 4 Sn — 4
As Cast 26 47 22 85
Nickel Silver C97800 Castings—ASTM B 271, B 505 & B 584
Cu — bal Zn — 2 Ni — 25 Pb — 2 Sn — 5
As Cast 25a 50 18 58
W H I T E M E T A L S A N D A L L O Y S
Antimony (UNS M00998) Ingots—ASTM B 237 Grade A
Sb — 99.8 min.
Cast (Ingot)
—
1.56
—
42
Bismuth-lead Alloy
Bi — 55.5 Pb — 44.5
Cast
—
6.4
65
10
Bismuth-Tin Alloy
Bi — 58 Sn — 42
Cast
—
8.0
200
22
Bismuth-Lead-Tin-Cadmium Alloy
Bi — 50 Pb — 26.7 Sn — 13.3 Cd — 10
Cast
—
5.99
200
9
Bismuth-Lead-Indium-Cadmium-Tin Alloy
Bi — 44.7 Pb — 22.6 In — 19.1 Cd — 5.3 Sn — 8.3
Cast — 5.4 1.5 12
Lead Pig Form—ASTM B 29
Pb — 99.9 min
Rolled
1.9
2.5
50
5
Antimonial Lead (UNS L05090) Die Castings—ASTM B 102 Grade Y10A
Pb — 90 Sb — 10
Cast
Rolled
—
—
6.8
4.1
24
47
13
9
Tellurium Lead
Pb — 99.85 Te — 0.04 Cu — 0.06
Rolled 2.2 3 45 6
50-50 Tin-Lead Solder (UNS L05500) ASTM B 32 Grade 50A
Sn — 50 Pb — 50
Cast
—
6.8
50
14
60-40 Tin-Lead Solder (UNS L13600) ASTM B 32 Grade 60A
Sn — 60 Pb — 40
Cast
—
7.1
45
15
Tin (UNS L13008) ASTM B 339 Grade A Sn — 99.8 min Chill Cast — 2.1 70 3.9
a = 0.5% extension under load b = Depends on cooling rate
PROPERTIES OF SOME METALS AND ALLOYS
11
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C O P P E R A N D C O P P E R A L L O Y S ( c o n t i n u e d )
0.323
8.94
2260
—
9.42
—
—
18
—
Copper-Nickel C96400
0.320 8.86 1830 0.12 10.0 120 204 19 —
Nickel Silver C97300
0.321 8.89 2090 — — 150 — 19 —
Nickel Silver C97600
0.320 8.86 1910 — — — — 19 — Nickel Silver C97800
W H I T E M E T A L S A N D A L L O Y S
0.249
6.62
1166
0.092
5.5
131
234
11.3
2.8
Antimony
0.380
10.5
255
0.03C
11.6
—
—
—
—
Bismuth-Lead
Alloy
0.315
8.72
281
0.045C
8.3C
—
—
—
—
Bismuth-Tin
Alloy
0.339
9.38
158
0.040C
12.2C
—
—
—
—
Bismuth-Lead- Tin-Cadmium Alloy
0.320 8.85 117 0.035C 13.8C — — — —
Bismuth-Lead- Indium- Cadmium- Tin Alloy
0.410
11.35
621
0.030
16.4
240
124
2
—
Lead
0.393
—
10.88
—
545
—
0.032
—
15.1
—
200
—
152
—
3
—
—
—
Antimonial Lead
0.410 11.35 621 0.030 16.4 240 124 2 — Tellurium Lead
0.321
8.89
421
0.051
13.1
310
93
—
—
50-50 Tin-Lead Solder
0.306
8.50
374
0.055
12.2
330
90
—
—
60-40 Tin-Lead Solder
0.263
7.29
449
0.053
12.8
428
66
6
2.4
Tin
2 = 68 to 572°F c = Estimated
12
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W H I T E M E T A L S A N D A L L O Y S ( c o n t i n u e d )
Zinc (UNS 221310) Rolled—ASTM B 69
Zn —bal Pb —0.08
Hot Rolled (Longitudinal)
Cold Rolled
—
—
19.5
21
65
50
38
—
ZILLOY* 15 (UNS 245330) Rolled—ASTM B 69
Zn —bal Mg —0.01 Cu —1
Hot Rolled (Longitudinal)
Cold Rolled
—
—
35
42
25
20
130
150
Zinc-Aluminum Alloy (UNS 233520) Die Castings—ASTM B 86
Zn —bal AI —4 Mg —0.04
Die Cast — 41 10 82
Zinc-Aluminum-Copper Alloy (UNS 235530) ASTM B 86
Zn —bal AI —3.9 Mg —0.05 Cu —1
Die Cast — 47.6 7 91
C.D.C. Manganese Alloy 772 (UNS M27200) ASTM B 388
Mn —72 Cu —18 Ni —10
Rolled 95 115 6.5 220
A L U M I N U M A N D A L L O Y S
Aluminum Alloy 1100 (UNS A91100) Sheet & Plate—ASTM B 209 Bar, Rod & Wire—ASTM B 211 Tube—ASTM B 243
AI —99.0 min
Sheet Annealed
Cold Rolled
5
22
13
24
35
5
23
44
Aluminum Alloy 1017 (UNS A92017) Bar, Rod & Wire—ASTM B211
AI —bal Cu —4 Mn —0.5 Mg —0.5
Bar Annealed
Heat Treated
10
40
26
62
22
22
45
105
Aluminum Alloy Alclad 2024 (UNS A92024) Sheet & Plate—ASTM B 209 Bar, Rod & Wire—ASTM B 211 Pipe & Tube—ASTM B 241
Core: 2024 AI —bal Cu — 4.5 Mn — 0.6 Mg — 1.5 Cladding: AI —99.3 min
Sheet Annealed
Heat Treated
11
42
26
64
20
19
—
—
Aluminum Alloy 3003 (UNS A93003) Sheet & Plate—ASTM B 209 Bar, Rod & Wire—ASTM B 211 Pipe & Tube—ASTM B 241 & B 483
AI —bal Mn —1.2
Sheet Annealed
Cold Rolled
6
27
16
29
30
4
28
55
Aluminum Alloy 5052 (UNS A95052) Sheet & Plate—ASTM B 209 Bar, Rod & Wire—ASTM B 211 Pipe & Tube—ASTM B 241 & B 483
AI —bal Mg —2.5 Cr —0.25
Sheet Annealed
Cold Rolled
13
37
28
42
25
7
47
77
Aluminum Alloy 6061 (UNS A96061) Sheet & Plate —ASTM B 209 Bar, Rod & Wire—ASTM B 211 Pipe & Tube—ASTM B 241 & B 483
AI —bal Si —0.6 Cu —0.25 Mg —1 Cr —0.25
Sheet Annealed
Heat Treated
8
40
18
45
25
12
30
95
Aluminum Alloy 7075 (UNS A97075) Bar, Rod, Wire & Shapes—ASTM B 221 Sheet & Plate—ASTM B 209 Forgings—ASTM B 247
AI —bal Zn —5.6 Cu —1.6 Mg —2.5 Cr —0.25
Bar Annealed
Heat Treated
15
73
33
83
16
11
60
150
Cast Aluminum Alloy 413.0 (UNS A04130) Castings—ASTM B 85 Grade S12B
AI —bal Si —12
Die Casting
As Cast 21 43 2.5 —
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
13
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W H I T E M E T A L S A N D A L L O Y S ( c o n t i n u e d )
0.258
—
7.14
—
786
—
0.094
—
18
—
746
—
35.5
—
—
—
—
—
Zinc
0.259
—
7.18
—
792
—
0.096
—
19.3
—
726
—
38
—
11
—
—
—
ZILLOY* 15
0.24 6.6 728 0.10 15.2 784 38.2 — — Zinc-Aluminum
Alloy
0.240
6.70
727
0.10
15.2
755
39.2
—
—
Zinc-Aluminum- Copper Alloy
0.26 7.21 — 0.12 15.31 58 1050 18 — C.D.C. Manganese
Alloy 772
A L U M I N U M A N D A L L O Y S
0.098
—
2.71
—
1215
—
0.23
—
13.11
—
1540
5
1510
5
17
18
10.0
10.0
3.75
3.75
Aluminum 1100
0.101
—
2.79
—
1185
—
0.23
—
12.71
—
1190
5
840
5
23
35
10.5
10.5
4.0
4.0
Aluminum Alloy 2017
0.100
—
2.77
—
1180
—
0.23
—
12.61
—
1340
5
840
5
21
35
10.6
10.6
3.75
4.0
Aluminum Alloy Alclad 1024
0.099
—
2.73
—
1210
—
0.23
—
12.91
—
1340
5
1070
5
21
26
10.0
10.0
3.75
3.75
Aluminum Alloy 3003
0.097
—
2.68
—
1200
—
0.23
—
13.21
—
960
5
960
5
30
30
10.2
10.2
3.75
3.75
Aluminum Alloy 5052
0.098
—
2.70
—
1205
—
0.23
—
13.01
—
1190
5
1070
5
23
26
10.0
10.0
3.75
3.75
Aluminum Alloy 6061
0.101
—
2.80
—
1175
—
0.23
—
12.91
—
—
840
5
—
35
10.4
10.4
3.9
3.9
Aluminum Alloy 7075
0.096 2.65 1080 0.23 11.51 870
5 34 10.3 3.85 Cast Aluminum
Alloy 413.0
1 = 68 to 212°F 5 = at 77°F
14
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
A L U M I N U M A N D A L L O Y S ( c o n t i n u e d )
Cast Aluminum Alloy B443.0 (UNS A24430) Castings—ASTM B 108
AI —bal Si —5
Permanent Mold Casting
As Cast 9 23 10 45
Cast Aluminum Alloy A380.0 (UNS A13800) Castings—ASTM B 85 Grade SC84A
AI —bal Cu —3.5 Si —8.5
Die Casting
As Cast 24 48 3 —
Cast Aluminum Alloy. 295.0 (UNS A02950) Castings—ASTM B 26
AI —bal Cu —4.5 Si —1.1
Sand Casting
Heat Treated 24 36 5 —
Cast Aluminum Alloy 514.0 (UNS A05140) Castings—ASTM B 26 & B 618
AI —bal Mg —4
Sand Casting
As Cast 12 25 9 50
Cast Aluminum Alloy 510.0 (UNS A05200) Castings—ASTM B 26
AI —bal Mg —10
Sand Casting
Solution Heat Treated 26 48 16 75
Cast Aluminum Alloy 336.0 (UNS A03360) Castings—ASTM B 108
AI —bal Si —12 Mg — 1 Ni — 2.5 Cu — 1
Permanent Mold Casting Heat Treated Plus 340°F
43 47 0.5 125
Cast Aluminum Alloy 242.0 (UNS A02420) Castings—ASTM B 26, B 108 & B 618
AI —bal Mg —1.5 Ni —2 Cu —4
Sand Casting Heat Treated Plus 650°F
30
32
0.5
85
M A G N E S I U M A L L O Y S
Magnesium Alloy AZ 31B (UNS M11311) Plate & Sheet—ASTM B 90 Forgings—ASTM B 91 Bar, Tube & Wire—ASTM B 107
Mg —bal AI —3 Zn —1 Mn —0.2 min
Sheet Annealed
Hard Sheet
22
32
37
42
21
15
56
73
Magnesium Alloy AZ 80A (UNS M11800) Forgings—ASTM B 91 Bar, Tube & Wire—ASTM B 107 Castings—ASTM B 80, B 199 & B 403
Mg —bal AI —8.5 Zn —0.5 Mn —0.12 min
As Forged
Forged and Aged
33
36
48
50
11
6
69
72
Magnesium Alloy AZ 91B (UNS M11912) Castings—ASTM B 94
Mg —bal All —9 Zn —0.7 Mn —0.15 min
Die Cast
22
33
3
63
Cast Magnesium Alloy AZ 91C (UNS Ml 1914) Castings—ASTM B 199 (Permanent) & ASTM B 80 (Sand)
Mg —bal AI —8.7 Zn —0.7 Mn —0.13 min
As Cast
Solution Treated and Aged
14
19
24
40
2.5
5
60
70
Magnesium Alloy AZ 92A (UNS M11920) Castings—ASTM B 199 (Permanent) & ASTM B 80 (Sand)
Mg —bal AI —9 Zn —2 Mn —0.10 min
As Cast
Solution Treated
Solution Treated and Aged
14
14
22
25
40
40
2
10
3
65
63
81
Magnesium Alloy EZ 33A (UNS M12330) Castings—ASTM B 199 (Permanent) & ASTM B 80 (Sand)
Mg —bal Zn —2.6 Zr —0.7 Rare earth metal—3
Aged Castings
16
23
3
50
Magnesium Alloy HK 31A (UNS M13310) Plate & Sheet—ASTM B 90 Castings—ASTM B 199 (Permanent)
Mg —bal Th —3.25 Zr —0.7
Strain Hardened Partially—Sheet Annealed
Castings—Heat Treated
29
15
37
32
8
8
68
RB66
PROPERTIES OF SOME METALS AND ALLOYS
15
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
A L U M I N U M A N D A L L O Y S ( c o n t i n u e d )
0.097 2.69 1170 0.23 12.31 9905 28 10.3 3.85 Cast Aluminum
Alloy B443.0
0.098 2.72 1100 0.23 11.61 6705 45 10.3 3.85 Cast Aluminum
Alloy A380.0
0.102 2.81 1190 0.23 12.71 9605 30 10.0 3.75 Cast Aluminum
Alloy 295.0
0.096 2.65 1185 0.23 13.41 9645 30 10.3 3.85 Cast Aluminum
Alloy 514.0
0.093 2.57 1120 0.23 13.71 6105 50 9.5 3.55 Cast Aluminum
Alloy 520.0
0.098 2.72 1050 0.23 11.01 8105 36 10.6 4.35
Cast Aluminum Alloy 336.0
0.102
2.81
1175
0.23
12.61
9305
31
10.3
3.85
Cast Aluminum Alloy 242.0
M A G N E S I U M A L L O Y S
0.064
—
1.77
—
1170
—
0.245
—
14.51
—
6576
—
55
—
6.5
—
2.4
—
Magnesium AlloyAZ 31B
0.065
—
1.80
—
1130
—
0.25
—
14.51
—
5222
—
87
—
6.5
—
2.4
—
Magnesium AlloyAZ 80A
0.065
1.80
1105
0.25
14.51
4932
102
6.5
2.4
Magnesium AlloyAZ 91B
0.065
—
1.81
—
1105
—
0.25
—
14.51
—
4932
—
90
91
6.5
—
2.4
—
Cast Magnesium Alloy AZ 91C
0.066
—
—
1.82
—
—
1100
—
—
0.25
—
—
14.01
—
—
4932
—
—
84
99
84
6.5
—
—
2.4
—
—
Magnesium AlloyAZ 92A
0.066
1.83
1189
0.25
14.51
6966
42
6.5
2.4
Magnesium AlloyEZ 33A
0.065
—
1.79
—
1204
—
0.24
—
—
—
7846
6396
37
46
6.5
6.5
2.4
2.4
Magnesium AlloyHK 31A
1 = 68 to 212°F 2 = 68 to 572°F 5 =at 77°F 6 = Near room temperature
16
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
M A G N E S I U M A L L O Y S ( c o n t i n u e d )
Magnesium Alloy HZ 32A (UNS M13320) Castings—ASTM B 80 (Sand)
Mg —bal Th —3.25 Zn —2.1 Zr —0.7
Solution Treated and Aged Castings
13
27
4
55
Magnesium Alloy ZK 60A (UNS M16000) Extrusions—ASTM B 107 Forgings—ASTM B 91
Mg —bal Zn —5.5 Zr —0.45 min.
As Extruded
Aged
38
44
49
53
14
11
75
82
T I T A N I U M A L L O Y S
Titanium Ti-35A (UNS R50250) Forgings—ASTM B 381 Sheet, Strip & Plate—ASTM B 265 Pipe—ASTM B 337 Tubes—ASTM B 338 Bars—ASTM B 348 Castings—ASTM B 367
Ti —bal C —0.08 max. Fe —0.12 max N —0.03 max H —0.015 max O —0.18
Sheet Annealed
30
40
30
135
Titanium Ti-50A (UNS R50400) Forgings—ASTM B 381 Sheet, Strip & Plate—ASTM B 265 Pipe—ASTM B 337 Tubes—ASTM B 338 Bars—ASTM B 348 Castings—ASTM B 367
Ti —bal C —0.08 max. Fe —0.20 max N —0.03 max H —0.015 max O —0.25 max
Sheet Annealed
45
55
25
215
Titanium Ti-75A (UNS R50700) Forgings—ASTM B 381 Sheet, Strip & Plate—ASTM B 265 Bar—ASTM B 348 Castings—ASTM B 367
Ti —bal C —0.08 max Fe —0.30 max N —0.05 max H —0.015 max O —0.40 max
Sheet Annealed
75
85
18
265
Ti-0.2 Pd Alloy (UNS R52400) Sheet, Strip & Plate—ASTM B—265 Pipe—ASTM B 337 Tube—ASTM B 338 Bars—ASTM B 348 Forgings—ASTM B 381 Castings—ASTM B 367
Ti —bal Pd —0.15 C —0.08 Fe —0.20 max N —0.03 max H —0.015 max O —0.25 max
Sheet Annealed 45 55 25 215
Ti-5 AI-2.5 Sn Alloy (UNS R54520) Sheet, Strip & Plate—ASTM B 265 Bar—ASTM B 348 Forgings—ASTM B 381 Castings—ASTM B 367
Ti —bal AI —5 Sn —2.5 C —0.08 max Fe —0.50 max N —0.05 max H —0.0175 max O —0.20 max
Annealed 125 135 13 RC39
Ti-8 AI-1 Mo-1 V Alloy (UNS R54810) Plate, Sheet & Strip—AMS 4915 & 4916 Bar—AMS 4972 Forgings—AMS 4973
Ti —bal AI —8 Mo —1 V —1 C —0.08 max Fe —0.30 max N —0.05 max H —0.015 max O —0.12 max
Sheet Annealed
130
140
13
RC39
PROPERTIES OF SOME METALS AND ALLOYS
17
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
M A G N E S I U M A L L O Y S ( c o n t i n u e d )
0.066
1.83
1198
0.23
14.84
7556
39
6.5
2.4
Magnesium Alloy HZ 32A
0.066
—
1.83
—
1175
—
0.24
—
14.51
—
8156
8456
36
—
6.5
—
2.4
—
Magnesium Alloy ZK 60A
T I T A N I U M A L L O Y S
0.163
4.50
3063
0.124
4.8
1083
336
14.9
6.5
Titanium Ti-35A
0.163
4.50
3100
0.125
4.8
1143
336
14.9
6.5
Titanium Ti-50A
0.164
4.53
3038
0.129
4.8
1183
360
15.1
6.5
Titanium Ti-75A
0.163 4.50 3100 0.125 4.8 1143 340 14.9 6.5
Ti-0.2 Pd Alloy
0.162
4.47
3002
0.125
5.2
543
1092
16
7.0
Ti-5 AI-2.5 So Alloy
0.158
4.36
—
—
4.7
—
1192
17.5
—
Ti-8 AI-1 Mo 1V Alloy
1 = 68 to 212°F 3 = at 68°F 4 = 68 to 392°F 6 = near room temperature
18
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
T I T A N I U M A L L O Y S ( c o n t i n u e d )
TI-6 AI-2 Sn-4 Zr-2 Mo Alloy (UNS 854620) Bar—AMS 4975 Forgings—AMS 4976
Ti —bal AI —6 Sn —2 Zr —4 Mo —2 C —0.04 max Fe —0.15 max N —0.04 max H —0.015 max O —0.12 max
Bar Annealed
130
140
15
RC39
Ti-6 AI-6 V-2 Sn Alloy (UNS 856620) Sheet, Strip & Plate—AMS 4918 Bars & Forgings—AMS 4971, 4978 & 4979 Extrusions—AMS 4936
Ti —bal AI —5.5 V —5.5 Sn —2 Cu —0.7 Fe —0.7 C —0.05 max N —0.04 max H —0.015 max O —0.20 max
Sheet Annealed
155
165
12
RC41
Ti-6 AI-4 V Alloy (UNS 856400) Sheet, Strip, Plate—ASTM B 265 Bar—ASTM B 348 Forgings—ASTM B 381 Castings—ASTM B 367
Ti —bal AI —6.3 V —4 C —0.08 max Fe —0.25 max N —0.05 max H —0.015 max O —0.20 max
Sheet Annealed
Heat Treated
130
165
140
175
13
12
RC39
—
Ti-6 AI-2 Sn-4 Zr-6 Mo Alloy (UNS 856260) Bars & Forgings—AMS 4981
Ti —bal AI —6 Sn —2 Zr —4 Mo —6 C —0.04 max Fe —0.15 max N —0.02 max H —0.015 max O —0.12 max
Sheet Annealed
150
160
12
RC42
Ti-13 V-11 Cr-3 All Alloy (UNS 858010) Plate, Sheet & Strip—AMS 4917 Wire—AMS 4959
Ti —bal V —13.5 Cr —11 AI —3 C —0.05 max Fe —0.35 max N —0.05 max H —0.025 max O —0.17 max
Sheet Annealed
Heat Treated
130
170
135
180
13
6
RC37
—
Ti Code 12 Sheet, Strip & Plate—ASTM B 265 Pipe & Tube—ASTM B 337 & B 338 Bars—ASTM B 348 Forgings—ASTM B 381 Fittings—ASTM B 363
Ti —bal Ni —0.8 Mo —0.3 C —0.08 max Fe —0.30 max N —0.03 max H —0.015 max O —0.25 max
Annealed
62
82
20
240
PROPERTIES OF SOME METALS AND ALLOYS
19
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
T I T A N I U M A L L O Y S ( c o n t i n u e d )
0.164
4.53
3000
—
—
—
—
16.5
—
Ti-6 AI-2 Sn- 4 Zr-2 Mo Alloy
0.164
4.53
3100
0.155
5.0
503
942
16.5
—
Ti-6 AI-6 V- 2 Sn Alloy
0.160
—
4.42
—
3000
—
0.135
—
4.9
—
503
—
1026
—
16.5
—
6.1
—
Ti-6 AI-4 V Alloy
0.168
4.64
3050
—
5.2
493
—
16.5
—
Ti-6 AI-2 Sn-4 Zr-6 Mo Alloy
0.175
—
4.83
—
—
—
0.120
—
5.44
—
483
—
918
—
15
—
62
—
Ti-13 V-11 Cr- 3 AI Alloy
0.163
4.51
—
0.13
5.328
132
31236
15
6.2
Ti Code 12
3 = at 68°F 4 = 68 to 392°F 28 = 32 to 600°F 35 = at 75°F
20
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
T I T A N I U M A L L O Y S ( c o n t i n u e d )
Ti-10 V-2 Fe-3 AI Alloy
Ti —bal V —10 Fe — 2 AI — 3 C — 0.05 max N — 0.05 max H — 0.015 max O — 0.13 max
Forgings Solution
Treated and (1) Aged (2) Overaged
166
135
176
145
12
20
—
—
R E S I S T A N C E H E A T I N G A L L O Y S
80 Ni-20 Cr Alloy (UNS N06003) ASTM B 344
Ni —80 Cr —20
Annealed
60
100
30
RB88
60 Ni-15 Cr-bal Fe Alloy (UNS N06004) ASTM B 344
Ni —60 Cr —15 Fe —bal
Annealed 50 105 30 200
35 Ni-20 Cr-bal Fe Alloy ASTM B 344
Fe —bal Ni —35 Cr —20
Annealed 55 102 30 RB83
Ni-Cr AlloyA
Ni —bal Cr —20 AI — 3 Fe —3
Annealed
65
140
35
—
Fe-Cr-Al AlloyB (UNS K92400)
Fe —bal Cr —23 AI — 5 Co —May be present
Annealed
80
100
25
215
M A G N E T I C A L L O Y S
80 Ni-4 Mo Alloy (Magnetically Soft) ASTM A 753, Alloy 4
Ni —80 Mo — 4 Fe —bal
Magnetic Annealed 22 79 64 RB62
Mu Metal (Magnetically Soft) ASTM A 753, Alloy 3
Ni —77 Cu — 5 Cr — 2.5 Fe —bal
Strip Mill Annealed
Hydrogen Annealed
38
18
90
64
35
27
—
RB60
48 Ni-bal Fe Alloy (Magnetically Soft) ASTM A 753, Alloy 2
Ni —48 Fe —bal
Strip Mill Annealed
Hydrogen Annealed
40
—
80
—
33
—
—
—
Alnico II (Permanent Magnet Alloy)
Fe —bal AI —10 Ni —18 Co —13 Cu — 6
Cast Annealed
Sintered
—
—
3
65
—
—
RC45
RC43
A Developed for applications requiring a negli- B Marketed, with minor chemical variations, gibIe temperature coefficient of resistance in under the following trademarks: *See page 84 for list of trademarks the temperature range of –60 to 480°F KANTHAL* 200 ALLOY* ALCHROME* Marketed, with minor chemical variations, under the following trademarks: KARMA* EVANOHM* NIKROTHAL*
PROPERTIES OF SOME METALS AND ALLOYS
21
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
T I T A N I U M A L L O Y S ( c o n t i n u e d )
0.168
—
4.65
—
—
—
—
—
5.443
—
—
—
—
—
16
—
—
—
Ti-10 V-2 Fe- 3 AI Alloy
R E S I S T A N C E H E A T I N G A L L O Y S
0.304
8.41
2550
0.104
7.3 9.615
10410
650
31
—
80 Ni-20 Cr
Alloy
0.298 8.25 2460 0.112
7.6 9.416
9310 675 29 — 60 Ni-15 Cr-
bal Fe Alloy
0.287 7.95 2515 0.098 8.816 14810 610 27 — 35 Ni-20 Cr-
bal Fe Alloy
0.293
8.11
2550
0.104
7.4
88
800
—
—
Ni-Cr AlloyA
0.262
7.25
2750
—
9.316
—
812
—
—
Fe-Cr-AI AlloyB
M A G N E T I C A L L O Y S
0.315 8.7 2600 0.12 6.41 232 350 33.3 6.6 80 Ni-4 Mo Alloy
—
0.307
—
8.5
—
—
—
—
—
6.91
—
—
—
337
30
25
—
—
Mu Metal
—
0.296
—
8.2
—
—
—
—
—
4.71
—
—
—
270
—
—
—
—
48 Ni-bal Fe Alloy
0.256
0.243
7.09
6.73
—
—
—
—
6.92
6.92
—
—
3905
4085
—
—
—
—
Alnico II
1 = 68 to 212°F 2 = 68 to 572°F 3 = at 77°F 10 = at 212°F 15 = 68 to 1832°F 16 = 68 to 937°F 43 = 32 to 800°F
22
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
M A G N E T I C A L L O Y S ( c o n t i n u e d )
Alnico III (Permanent Magnet Alloy)
Fe —bal AI —12 Ni —26 Cu — 3
Cast Annealed
—
12
—
RC45
Alnico IV (Permanent Magnet Alloy)
Fe —bal AI —12 Ni —28 Cc — 5
Cast Annealed
Sintered
—
—
9.1
60
—
—
RC45
RC42
Alnico V** (Permanent Magnet Alloy)
Fe —bal AI — 8 Ni —15 Co —24 Cu — 3
Cast Cooled in Magnetic Field
Sintered
—
—
5.4
50
—
—
RC50
RC44
Alnico VI** (Permanent Magnet Alloy)
Fe —bal AI — 8 Ni —16 Co —24 Cu — 3 Ti — 1.25
Cast Cooled in Magnetic Field
Sintered
—
—
23
—
—
—
RC50
RC44
Alnico VII** (Permanent Magnet Alloy)
Fe —bal Al — 8.5 Ni —18 Co —24 Cu — 3.25 Ti — 5
Cast Cooled in Magnetic Field
—
—
—
RC60
Alnico Vill** (Permanent Magnet Alloy)
Fe —bal AI — 7 Ni —15 Co —35 Cu — 4 Ti — 5
Cast Cooled in Magnetic Field
—
—
—
RC57
Cunico (Permanent Magnet Alloy)
Cu —50 Ni —21 Co —29
Strip Cold Rolled Heat Treated
— 100 — RB95
Cunife (Permanent Magnet Alloy)
Cu —60 Ni —20 Fe —20
Strip Cold Rolled Heat Treated
— 100 — RB73
Permalloy 49
Fe —bal Ni —48.5
Strip Cold Rolled Round & Flat Wire 1175°F Slow Cool
— — — —
Moly Permalloy 4/79
Ni —80 Mo — 4 Fe —bal
Strip Cold Rolled Round & Flat Wire
1175°F Controlled Cool — — — —
** = Properties depend on cooling rate
PROPERTIES OF SOME METALS AND ALLOYS
23
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
M A G N E T I C A L L O Y S ( c o n t i n u e d )
0.249
6.89
—
—
7.22
—
3605
—
—
Alnico III
0.253
0.232
7.00
6.42
—
—
—
—
7.32
7.32
—
—
4505
4085
—
—
—
—
Alnico IV
0.265
0.241
7.34
6.67
—
—
—
—
6.32
6.32
—
—
2825
3005
—
—
—
—
Alnico V**
0.268
0.241
7.42
6.67
—
—
—
—
6.32
6.32
—
—
3005
3185
—
—
—
—
Alnico VI**
0.259
7.17
—
—
6.12
—
3485
—
—
Alnico VII**
0.265
7.34
—
—
—
—
3005
—
—
Alnico VIII**
0.300 8.30 — — 7.82 — 1445 — — Cunico
0.311 8.61 — — 7.82 — 1085 — — Cunife
— — — — — — 2895 — — Permalloy
49
— — — — — — 3495 — — Moly Permalloy
4/79
2 = 68 to 572°F 5 = at 77°F
24
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C O N T R O L L E D E X P A N S I O N A N D C O N S T A N T - M O D U L U S A L L O Y S
INVAR* (UNS K93600) ASTM B 388
Ni —36 Fe —bal
Annealed
40
71
43
132
Super-Invar
Ni —31 Fe —bal Co — 5.2 Mo — 0.5 max Si — 0.15 max C — 0.05 max
Bar, Sheet, Etc. 1525°F Water Quench
600°F Air Cool 212°F Air Cool
44
70
38
RB77
42 Ni-Iron Alloy (UNS K94200) ASTM F 30 & B 388
Ni —42 Fe —bal
—
35
68
45
138
50 Ni-Iron Alloy (UNS K95000) ASTM F 30 & B 388
Ni —50 Fe —bal
Annealed
33
77
45
144
Iron-Nickel Temperature Compensating Alloys
Ni —29.5 Fe —bal___ Ni —31 Fe —bal___ Ni —32.5 Fe —bal
Annealed
—
65
—
125
Ni-Fe-Co AlloyC
Fe —bal Ni —29 Co —17
Annealed 35 85 40 —
ELINVAR*
Fe —bal Ni —33 Cr — 5 W —2 Mn — 0.6 Si — 0.5 C — 0.5
Annealed
45
80
30
150
38 Ni-7 Cr Alloy
Ni —38 Fe —bal Cr — 7 Mn — 0.45 max Si — 0.30 max C — 0.12
Annealed
29
73
44
RB67
NI-SPAN-C* Alloy 902 (UNS N09902)
Ni —42.2 Mn — 0.4 Fe —48.5 Cr — 5.3 Ti — 2.6 AI — 0.6
Annealed
Aged
Cold Rolled 50%
Cold Rolled and Aged 1200°F
35
110
126
176
90
175
131
192
40
25
6
9
125
305
265
365
ISO-ELASTIC*
Ni —36.85 Fe —54.25 Mn — 0.55 Cr — 7.10 Mo — 0.45
Annealed
Cold Worked
35
135
85
155
30
10
135
305
INCOLOY* Alloy 903
Ni —38 Co —15 AI — 0.7 Ti — 1.4 Cb — 3 Fe —bal
Aged
160
190
14
—
*See page 84 for list of trademarks C Also available, with minor chemical varia- tions, under the following trademarks: THERLO* RODAR* KOVAR*
PROPERTIES OF SOME METALS AND ALLOYS
25
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C O N T R O L L E D E X P A N S I O N A N D C O N S T A N T - M O D U L U S A L L O Y S
0.293
8.11
2600
0.12
0.8
72.6
494
21
8.1
INVAR*
0.294
8.14
—
—
Near zero
—
—
22
—
Super-Invar
0.294
8.14
2600
0.12
2.9
106
405
22
8.5
42 Ni-Iron Alloy
0.297
8.22
2600
0.12
4.9
124
270
24
9.3
50 Ni-Iron Alloy
0.295 to 0.292
8.17 to 8.08
—
0.12
6.0 to 3.0
80
480
22
—
Iron-Nickel Temperature Compensating Alloys
0.303 8.39 2650 0.123 3.3 98 294 — — Ni-Fe-Co AlloyC
0.295
8.17
—
0.12
3 Plus
—
—
22
9
ELINVAR*
0.292
8.08
—
—
3.317
—
570
—
—
38 Ni-7 Cr Alloy
0.293
—
—
—
8.11
—
—
—
2700
—
—
—
0.12 —
—
—
4.519
—
—
—
95
—
—
—
611
—
—
—
24-29
—
—
—
9-10
—
—
—
NI-SPAN-C* Alloy 902
0.292
—
8.08
—
—
—
—
—
4 Plus
—
—
—
528
—
25
—
9.2
—
ISO-ELASTIC*
0.294
8.14
2539
0.105
4.0
11744
37944
21.344
8.644
INCOLOY* Alloy 903
17 = 70 to 200°F 19 = at 500°F 44 = at 100°F
26
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
N I C K E L A N D A L L O Y S
Nickel 211 ASTM F 290
Ni —95 Mn — 4.9 C — 0.1
Annealed 35 75 40 140
Nickel 210 Castings—ASTM A 494
Ni —95.6 Cu — 0.5 Fe — 0.5 Mn — 0.8 Si — 1.5 C — 0.8
As Cast
25a
57
22
110
Nickel 200 (UNS N02200) Plate, Sheet, Strip—ASTM B 162 Bar—ASTM B 160 Pipe & Tube—ASTM B 161 & B 163
Ni —99.5 Mn — 0.2 Fe — 0.2 C — 0.08
Rod Hot Rolled Annealed
21.5
67
47
100
Nickel 201 (UNS N02101) Plate, Sheet, Strip—ASTM B 162 Bar—ASTM B 160 Pipe & Tube—ASTM B 161 & B 163
Ni —99.5 Mn — 0.2 Fe — 0.2 C — 0.01
Rod Hot Rolled Annealed
18
55
55
90
Nickel 205 (UNS N02205) ASTM F 1, F 2 & F 3
Ni —99.5 Mn — 0.2 Fe — 0.1 Ti — 0.03 Mg — 0.01 C — 0.08
Rod Hot Rolled Annealed
21
67
47
100
Nickel 270 (UNS N02270) Electronic Sleeves—ASTM F 239 ASTM F 1, F 2 & F 3
Ni —99.98
Strip Annealed
16
50
50
RB80
PERMANICKEL* Alloy 300
Ni —98.5 Mn— 0.2 Ti — 0.4 Mg — 0.4 C — 0.2
Rod Annealed
Annealed and Aged
45
140
121
176
41
16
160
325
DURANICKEL* Alloy 301
Ni —94 AI — 4.4 Si — 0.5 Ti — 0.6 Mn — 0.2 Fe — 0.3 C — 0.2
Hot Rolled and Aged 132 185 28 330
Nickel Beryllium 440 (Wrought)
Ni —bal Be — 1.95 Ti — 0.5
Strip Annealed
Annealed
45
150
105
215
40
15
RB70
RC47
Nickel Beryllium M 220C (Cast)
Ni —bal Be — 2.15 C — 0.4 max
Casting Annealed
Annealed and Aged
60
180
110
190
10
2
RC28
RC51
Nickel Beryllium CR—1 (Cast)
Ni —bal Be — 2.7 Cr — 0.7 C — 0.1
As Cast
Annealed and Aged at 950°F
70
180
125
195
2
0
285
328
WAUKESHA METAL* No. 23 (Non-Galling Alloy)
Ni —78 Pb — 3.5 Sn — 8 Zn — 7.5 Mn — 2
As Cast 55 75 10 160
*See page 84 for list of trademarks a = 0.5 % extension under load
PROPERTIES OF SOME METALS AND ALLOYS
27
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
N I C K E L A N D A L L O Y S
0.315 8.73 2600 0.11 7.417 3063 102 30 12 Nickel 211
0.301
8.34
2550
0.13
8.85
410
125
21.5
—
Nickel 210 (Cast)
0.321
8.89
2635
0.11
7.417
5203
57
30
12
Nickel 200
0.321
8.89
2635
0.11
7.4
5503
46
30
11
Nickel 201
0.321
8.89
2635
0.11
7.417
5203
57
30
12
Nickel 205
0.321
8.89
2650
0.11
7.417
595
45
30
—
Nickel 270
0.316
—
8.75
—
2620
—
0.106
—
6.817
—
4003
—
100
95
30
—
11
—
PERMANICKEL* Alloy 300
0.298 8.25 2620 0.104 7.2 1653 255 30 11
DURANICKEL* Alloy 301
0.318
—
8.84
—
—
—
—
—
8.018
—
2203
—
143
—
28.5
—
—
—
Nickel Beryllium 440
0.29
—
8.10
—
2310
—
—
—
7.74
—
2153
—
—
—
27
—
—
—
Nickel Beryllium M 220C
0.287
—
7.95
—
2310
—
—
—
—
—
—
—
345 to 172
—
25 to 28
—
—
—
Nickel Beryllium CR-1
0.32 8.86 — — 7.4831 19232 — 22 —
WAUKESHA METAL* No. 23
3 =at 68°F 4 = 68 to 392°F 17 = 70 to 200°F 18 = at 500°F 31 = 32 to 500°F 32 = 70 to 1100°F
28
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
N I C K E L A N D A L L O Y S ( c o n t i n u e d )
WAUKESHA METAL* No. 88 (Non-Galling Alloy)
Ni —bal Fe — 5 Cr —12.5 Mo — 3 Bi — 4 Sn —4 Mn — 0.8
As Cast 38 45 7 150
TINEL* Alloy A (Nitinol Memory Alloy)
Ni —50 Ti —50
Proprietary 62 125 20 RA60
M O N E L * N I C K E L - C O P P E R A L L O Y S
MONEL* Alloy 400 (UNS N04400) Rod & Bar—ASTM B 164 Class A Plate, Sheet, Strip—ASTM B 127 Tube—ASTM B 165 & B 513 Forgings —ASTM B 564
Ni —66 Cu —31.5 Fe — 1.1 Mn — 1 Si — 0.2 C — 0.2
Rod Hot Rolled Annealed
30
79
48
125
MONEL* Alloy 401
Ni —42.5 Cu —55 Mn — 1.6 Fe — 0.4
Rod Hot Rolled Annealed
25
63
48
100
MONEL* Alloy 404 (UNS N04404) ASTM F 96
Ni —54.5 Cu —45 Mn — 0.05 Fe — 0.2 C — 0.08
Rod Hot Rolled
Strip Annealed
31
22
69
64
45
43
RB67
RB54
MONEL* Alloy R-405 (UNS N04405) Rod & Bar—ASTM B 164 Class B
Ni —66 Cu —31 Fe — 1.2 Mn — 1 Si — 0.2 C — 0.2 S — 0.04
Hot Rolled
Cold Drawn
45
75
85
100
35
25
145
200
MONEL* Alloy K-500 (UNS N05500) Bar & Forgings—AMS 4676
Ni —65.5 Cu —29.5 AI — 2.7 Ti — 0.6 Fe — 1 Mn — 0.8 C — 0.1 Si — 0.2
Rod As Hot Rolled
Hot Rolled Aged
49
111
97
160
44
23.5
155
300
Nickel-Copper Alloy 410 (Cast)
Ni —66 Cu —30.5 Fe — 1 Mn — 0.8 Si — 1.6 C — 0.15
As Cast
35
75
40
150
Nickel-Copper Alloy 411 (Cast)
Ni —66 Cu —32.5 Fe — 1.5 Mn — 0.8 Si — 1.6 Cb + Ta—2.0
As Cast
35
75
40
150
Nickel-Copper Alloy 505 (Cast) (S MONEL*)
Ni —64 Cu —29 Fe —2 Mn — 0.8 Si — 4
Casting Annealed
As Cast or Annealed and Aged
—
—
—
—
—
—
225
340
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
29
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
N I C K E L A N D A L L O Y S ( c o n t i n u e d )
0.31 8.58 — — 8.031 200" 67531 27 —
WAUKESHA METAL* No.18
0.23 6.5 2370 — 6.11 1253 600 11 — TINEL* Alloy A
(Nitinal Memory Alloy)
M O N E L * N I C K E L - C O P P E R - A L L O Y S
0.319
8.84
2460
0.102
7.717
151
3
307
26
10
MONEL* Alloy 400
0.321 8.88 — — 7.617 — 294 — —
MONEL* Alloy 401
0.321
—
8.88
—
—
—
0.099
—
7.417
—
—
—
300
—
25
—
9.4
—
MONEL* Alloy 404
0.319
—
8.84
—
2460
—
0.102
—
7.717
—
151
3
—
307
—
26
—
9.5
—
MONEL* Alloy R-405
0.306
—
8.46
—
2460
—
0.100
—
7.617
—
121
3
136
20
370
—
26
—
9.5
—
MONEL* Alloy K-500
0.312
8.63
2450
0.13
9.232
186
1
320
23
—
Nickel-Copper Alloy 140 (Cast)
0.312
8.63
2450
0.13
9.232
186
1
320
23
—
Nickel-Copper Alloy 411 (Cast)
0.302
8.36
2350
0.13
8.932
136
1
380
24
—
Nickel-Copper Alloy 505 (Cast) (S MONEL*)
1 = 68 to 212°F 3 = at 68°F 14 = Dynamic Modulus 17 = 70 to 200°F 20 = at 200°F 31 = 32 to 500°F 32 = 70 to 1100°F 33 = 68 to 1500°F
30
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
I N C O L O Y * N I C K E L - I R O N - C H R O M I U M A L L O Y S
INCOLOY* Alloy 800 (UNS N08800) Plate, Sheet, Strip—ASTM B 409 Rod & Bar—ASTM B 408 Pipe & Tube—ASTM B 163 & B 407 Forgings—ASTM B 564
Ni —32.5 Cr —21 Fe —45.5 C — 0.05 Ti — 0.4 AI — 0.4
Rod Hot Rolled Annealed
42
87
44
150
INCOLOY* Alloy 801 (UNS N08801) Plate, Sheet & Strip—AMS 5552 Bar, Rod & Forging Stock—AMS 5742
Ni —32 Cr —20.5 Fe —44.5 C — 0.05 Ti — 1.1
Strip Annealed
Strip Annealed and Aged
34
56
92
114
44
30
RB76
RB93
INCOLOY* Alloy 802
Ni —32.5 Cr —21 Fe —46 C — 0.4
Rod Hot Rolled Annealed
46
102
44
160
INCOLOY* Alloy 825 (UNS N08825) Plate, Sheet, Strip—ASTM B 424 Rod & Bar—ASTM B 425 Pipe—ASTM B 423
Ni —42 Cr —21.5 Fe —30 Cu — 2.2 Mo — 3 Ti — 0.9 AI — 0.1 C — 0.03
Rod Annealed
44
100
43
150
I N C O N E L * N I C K E L - C H R O M I U M - I R O N A L L O Y S
INCONEL* Alloy 600 (UNS N06600) Plate, Sheet, Strip—ASTM B 168 Rod & Bar—ASTM B 166 Pipe & Tube—ASTM B 163, B 167, B 516 & B 517 Forgings—ASTM B 564
Ni —76 Cr —15 Fe — 8 Mn — 0.5 Si — 0.2 C — 0.08 Cu — 0.2
Rod Hot Rolled Annealed 41 96 45 150
INCONEL* Alloy 601 (UNS N06601) Bars & Forging Stock—AMS 5715 Sheet, Strip & Plate—AMS 5870
Ni —60.5 Cr —23 Fe —14 AI — 1.4 Mn — 0.5 Si — 0.2 C — 0.05 Cu — 0.5
Rod Hot Rolled Annealed
66
112
41
RB79
Cast Alloy 611
Ni —bal Cr —15.5 Fe — 9 Cb — 2 Si — 1.6 Mn — 0.9 Cu — 0.5 C — 0.2
As Cast
41a
78
15
175
INCONEL* Alloy 617
Ni —52 Cr —22 Co —12.5 Mo — 9 AI — 1.2 Fe — 1.5 Mn — 0.5 Si — 0.5 Ti — 0.3 C — 0.07
Rod Hot Rolled Annealed
52
112
56
172
*See page 84 for list of trademarks a = 0.5% extension under load
PROPERTIES OF SOME METALS AND ALLOYS
31
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
I N C O L O Y * N I C K E L - I R O N - C H R O M I U M A L L O Y S
0.287
7.94
2525
0.11
7.917
803
595
28
11
INCOLOY* Alloy 800
0.287
—
7.94
—
2525
—
0.1085
—
7.817
—
865
—
6095
—
30
—
11
—
INCOLOY* Alloy 801
0.283
7.83
2500
0.11
7.817
825
6695
29.7
—
INCOLOY* Alloy 802
0.294
8.14
2550
—
7.817
773
678
28
—
INCOLOY* Alloy 825
I N C O N E L * N I C K E L - C H R O M I U M - I R O N A L L O Y S
0.304 8.43 2575 0.106 7.417 1033 620 30 11
INCONEL* Alloy 600
0.293 8.11 2494 0.1073 7.617 783 710 30 11.8
INCONEL* Alloy 601
0.300
8.30
2950
0.1141
8.947
1041
700
23
—
Cast Alloy 611
0.302
8.36
2510
0.100
6.43
94
736
36.6
11.8
INCONEL* Alloy 617
1 = 68 to 212°F 3 = at 68°F 5 = at 77°F 17 = 70 to 1500°F 46 = 80 to 750°F 47 = 70 to 1400°F
32
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
I N C O N E L * N I C K E L - C H R O M I U M - I R O N A L L O Y S ( c o n t i n u e d )
INCONEL* Alloy 625 (UNS N06625) Plate, Sheet & Strip—ASTM B 443 Pipe & Tube—ASTM B 444 Rod & Bar—ASTM B 446
Ni —61 Cr —21.5 Fe — 4 Cb — 3.6 Mo — 9 Mn — 0.2 Si — 0.2 C — 0.05
Rod Hot Rolled Annealed
70
140
50
180
Cast Alloy 625
Ni —bal Cr —21.5 Mo — 9 Cb — 4 Fe —3 Mn — 0.5 Si — 0.6 C — 0.06 max
Casting Annealed
40
70
20
—
INCONEL* Alloy 690
Ni —61 Cr —29 Fe —9 Mn — 0.2 Si — 0.2 C — 0.02 Cu — 0.2
Rod Hot Rolled Annealed 51 104 47 RB90
INCONEL* Alloy 718 (UNS N07718) Plate, Sheet, Strip —AMS 5597 & ASTM B 670 Bar—AMS 5664 Bars & Forgings—ASTM A 637
Ni —52.5 Cr —19 Fe —18.5 AI — 0.5 Ti — 0.9 Cb — 5.1 Mo — 3.0 Mn — 0.2 Si — 0.2 C — 0.04
Rod Hot Rolled, Annealed and Aged
180
208
20
RC45
INCONEL* Alloy X—750 (UNS N01150) Bars & Forgings—ASTM A 637
Ni —73 Cr —15.5 Fe — 7 AI — 0.7 Ti — 2.5 Cb — 1 Mn — 0.5 Si — 0.2 C — 0.04
Rod Hot Rolled, 1625°F and Aged
Sheet Annealed and Aged
126
122
184
177
25
27
RC36
RC36
INCONEL* Alloy 751
Ni —72.5 Cr —15.5 Fe — 7 AI —1.2 Ti — 2.3 Cb — 1 Mn — 0.5 Si — 0.2 C — 0.05
Annealed
Annealed and Aged
75
142
125
175
50
20
176
337
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
33
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
I N C O N E L * N I C K E L - C H R O M I U M - I R O N A L L O Y S ( c o n t i n u e d )
0.305
8.44
2460
0.098
7.117
683
776
30.1
11.8
INCONEL* Alloy 625
—
—
—
—
—
—
—
—
—
Cast Alloy 625
0.296 8.19 2510 0.1073 7.817 9320 691 30.6 —
INCONEL* Alloy 690
0.296
8.19
2437
0.104
7.217
793
725
29
11.2
INCONEL* Alloy 718
0.298
—
8.25
—
2600
—
0.103
—
7.017
—
833
—
731
—
31
—
11
—
INCONEL* Alloy X-750
0.298
—
8.25
—
2600
—
—
—
—
—
—
—
743
—
31
—
11
—
INCONEL* Alloy 751
3 = at 68°F 17 = 70 to 200°F 20 = at 200°F
34
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
N I M O N I C * N I C K E L - C H R O M I U M A L L O Y S
NIMONIC* Alloy 75
Ni —77.4 Cr —20.5 AI — 0.15 Ti — 0.35 Fe — 0.5 C — 0.10
Bar Hot Rolled Annealed
51
116
44
RB87
NIMONIC* Alloy 80A (UNS N07080) Bars & Forgings—ASTM A 637
Ni —74.5 Cr —20.5 AI — 1.25 Ti — 2.4 Fe — 0.5 C — 0.05
1975°F, Air Cool plus 1300°F
90
154
39
RC34
NIMONIC* Alloy 90 (UNS N07090) AMS 5829
Ni —57 Cr —20.5 Co —17 AI — 1.6 Ti — 2.6 Fe — 0.5 C — 0.05
1975°F, Air Cool plus 1300°F 116 179 33 RC38
NIMONIC* Alloy 115
Ni —bal Cr —15 Co —15 Mo — 3.5 Ti — 4 AI — 5
2175°F, Air Cool plus 2010°F
125
180
27
RC37
H A S T E L L O Y * A L L O Y S
HASTELLOY* Alloy B-2 (UNS N10665) Sheet, Plate & Strip—ASTM B 333 Rod—ASTM B 335 Pipe & Tube—ASTM B 619, B 622 & B 626 Fittings—ASTM B 366
Ni —bal Mo —28 Fe — 2 max Co — 1 max Cr — 1 max Mn — 1 max Si — 0.10 max C —0.02 max
Sheet Solution Heat Treated
76
138
53
RC22
HASTELLOY* C-276 (UNS N10216) Plate, Sheet & Strip—ASTM B 575 Rod—ASTM B 574 Pipe & Tube—ASTM B 619, B 622 & B 626 Fittings—ASTM B 366
Ni —bal Mo —16 Cr —15.5 Fe — 5 W — 4 Co — 2.5 max Mn — 1 max V — 0.35 max Si — 0.08 max C — 0.02 max
Sheet Solution Heat Treated
52
115
61
RB90
HASTELLOY* Alloy C-4 (UNS N06455) Plate, Sheet & Strip—ASTM B 575 Rod—ASTM B 574 Pipe & Tube—ASTM B 619, B 622 & B 626 Fittings—ASTM B 366
Ni —bal Cr —16 Mo —15.5 Fe — 3 max Co — 2 max Mn — 1 max Ti — 0.70 max Si — 0.08 max C — 0.015 max
Sheet Solution Heat Treated
60
111
52
RB90
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
35
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
N I M O N I C * N I C K E L - C H R O M I U M A L L O Y S
0.302
8.37
2515
0.11
6.1
79 10
655
10
32.0
—
NIMONIC* Alloy 75
0.297
8.22
2500
0.103
6.2
70 10
732
10
32.114
—
NIMONIC* Alloy 80A
0.296 8.19 2500 0.11 6.4 75 10 708
10 32.814 —
NIMONIC* Alloy 90
0.284
7.85
2400 0.11 6.2
—
803
10
31.314
—
NIMONIC* Alloy 115
H A S T E L L O Y * A L L O Y S
0.333 9.22 — 0.093 10 6.245 85
10 829 10 31.414 —
HASTELLOY* Alloy B-2
0.321
8.89
2500
0.102
6.217
78 10
779
29.814
—
HASTELLOY* Alloy C-276
0.312
8.64
—
0.102 10
6.017
79 10
748
30.814
—
HASTELLOY* Alloy C-4
10 = at 212°F 14 = Dynamic Modulus 17 = 70 to 200°F 45 = 68 to 600°F
36
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
H A S T E L L O Y * A L L O Y S ( c o n t i n u e d )
HASTELLOY* Alloy 6 (UNS N06007) Sheet, Plate & Strip—ASTM B 582 Rod—ASTM B 581 Pipe & Tube—ASTM B 619, B 622 & B 626 Fittings—ASTM B 366
Ni —bal Cr —22 Fe —19.5 Mo — 6.5 Cb + Ta—2 Cu — 2 Co — 2.5 max Mn — 1.5 Si — 1 max W — 1 max C — 0.05 max
Sheet Solution Heat Treated
46
102
62
RB84
HASTELLOY* Alloy 6-3 (UNS N06985) Sheet, Plate & Strip—ASTM B 582 Rod—ASTM B 581 Pipe & Tube—ASTM B 619, B 622 & B 626 Fittings—ASTM B 366
Ni —bal Cr —22 Fe —19.5 Mo — 7 Co — 5 max Cu — 1.9 W — 1.5 max Mn — 0.8 Si — 0.4 Cb + Ta—0.3 C — 0.015 max
Sheet Solution Heat Treated
47
100
50
RB79
HASTELLOY* Alloy N (UNS N10003) Sheet & Plate—ASTM B 434 Rod—ASTM B 573 Fittings—ASTM B 366
Ni —bal Cr — 7 Mo —16.5 Fe — 5 max Mn — 0.8 max Si — 1 max AI + Ti — 0.5 max W — 0.5 max Cu — 0.35 max Co — 0.2 max B — 0.01 max C — 0.06
Sheet Solution Heat Treated
45
115
51
RB96
HASTELLOY* Alloy S Bars & Forgings—AMS 5711 Sheet, Plate & Strip—AMS 5873 Wire—AMS 5838
Ni —bal Cr —16 Mo —15 Mn — 0.5 Si — 0.4 AI — 0.2 La — 0.02 B — 0.015 max C — 0.02 max Fe — 3 max Co — 2 max W — 1 max
Sheet Solution Heat Treated
72
129
51
RB93
HASTELLOY* Alloy W (UNS N10004) Wire—AMS 5786 Bar & Forgings—AMS 5755
Ni —bal Cr — 5 Mo —24 Fe —6 Co — 2.5 max Mn — 1 max Si — 1 max V — 0.6 max C — 0.12 max
Sheet Solution Heat Treated 53 123 55 —
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
37
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
H A S T E L L O Y * A L L O Y S ( c o n t i n u e d )
0.300
8.31
2450
0.10910
7.517
705
—
27.814
—
HASTELLOY* Alloy G
0.300
8.31
—
—
—
—
—
—
—
HASTELLOY* Alloy G-3
0.320
8.93
2550
0.10010
7.045
79
10
725
31.714
—
HASTELLOY* Alloy N
0.316
8.75
2516
0.10210
6.417
97 42
770 5
30.814
—
HASTELLOY* Alloy S
0.325 9.03 2400 — 7.038 — — — —
HASTELLOY* Alloy W
1 = 68 to 212°F 5 = at 77°F 10 = at 212°F 14 = Dynamic Modulus 17 = 70 to 200°F 38 = 70 to 600°F 42 = at 392°F 45 = 68 to 600°F
38
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
H A S T E L L O Y * A L L O Y S ( c o n t i n u e d )
HASTELLOY* Alloy X (UNS N06002) (AISI No. 680) Sheet & Plate—ASTM B 435 Rod—ASTM B 572 Pipe & Tube—ASTM B 619, B 622 & B 626 Fittings—ASTM B 366
Ni —bal Cr —22 Fe —18.5 Mo — 9 Co — 1.5 Mn —1 max Si — 1 max W — 0.6 C — 0.10
Sheet Solution Heat Treated 52 114 43 RB90
C H L O R I M E T * A L L O Y S
CHLORIMET* 2 Gen. Applications—ASTM A 744 Castings—ASTM A 494
Ni —bal Mo —31.5 Fe — 3 max Cr — 1 max Mn — 1 max Si — 1 max C — 0.07 max
2100°F, Water Quenched
46
76
20
230
CHLORIMET* 3 Gen. Applications—ASTM A 744 Castings—ASTM A 494
Ni —bal Cr —18.5 Mo —18.5 Fe —3 max Mn — 1 max Si — 1 max C — 0.07 max
2100°F, Water Quenched
46
72
25
220
I L L I U M * A L L O Y S ( N I C K E L B A S E )
ILLIUM* B
Ni —bal Cr —28 Mo — 8.5 Cu — 5.5 Si — 3.5 C — 0.05
Castings 2100°F, Air Cooled
58
60
1
221-420
ILLIUM* G
Ni —bal Cr —22.5 Mo — 6.4 Cu — 6.5 Fe — 6.5 Mn — 1.25 max Si — 0.2 C — 0.2
Castings 2125°F, Water Quenched
35
60
5
159
ILLIUM* 98
Ni —ball Cr —28 Mo — 8.5 Cu — 5.5 Fe — 1 Mn — 1.25 max Si — 0.2 C — 0.05
Castings 2125°F, Water Quenched
41
54
18
143
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S
GMR 235D Alloy
Ni —bal Cr —15.5 Mo — 5 Fe — 4.5 Ti — 2.5 AI — 3.5 B — 0.05
Casting As Cast 103 112 3.5 —
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
39
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
H A S T E L L O Y * A L L O Y S ( c o n t i n u e d )
0.297 8.22 2470 0.116 7.7017 63 37 712 28.514 —
HASTELLOY* Alloy X
C H L O R I M E T * A L L O Y S
0.33
9.2
2400
—
6.438
—
—
27
—
CHLORIMET* 2
0.32
9.0
2400
—
7.138
—
—
24
—
CHLORIMET* 3
I L L I U M * A L L O Y S
0.310
8.57
—
—
—
—
—
—
—
ILLIUM* B
0.300
8.31
—
0.105
7.171
84
37
741
24.3
—
ILLIUM* G
0.302
8.36
—
—
—
—
—
—
—
ILLIUM* 98
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S
0.291 8.05 — — — — — 28.7`° —
GMR 235D Alloy
1 = 68 to 212°F 3 = at 68°F 14 = Dynamic Modulus 17 = 70 to 200°F 37 = at 70°F 38 = 70 to 600°F
40
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
Alloy 713C (UNS N07713) Castings—ASTM A 567, AMS 5377 & 5391
Ni —bal Cr —12.5 Mo — 4.2 Cb — 2 Ti — 0.8 AI — 6.1 B — 0.012 Zr — 0.1 C — 0.12
Casting As Cast 107 123 7.9 RC34
Alloy 713LC
Ni —bal Cr —12 Mo — 4.5 Cb — 2 Ti — 0.6 AI — 5.9 B — 0.01 Zr — 0.1 C — 0.05
Casting As Cast 109 130 15 RC39
Alloy 901 (UNS N09901) (AISI No. 682) Bar & Forgings—AMS 5660 & 5661
Ni —42.5 Cr —12.5 Mo — 5.7 Fe —bal Ti — 2.8 AI — 0.2 B — 0.015
Bar 2000°F W.Q. plus 1460°F A.C., plus 1225°F A.C.
Sheet 1950°F A.C., plus 1325°F A.C.
130
107
175
166
14
23
—
—
HAYNES* Alloy 556
Fe —bal Cr —22 Ni —20 Co —20 Mo — 3 W — 2.5 Mn — 1 Cb + Ta— 1 La — 0.02 C — 0.1 N — 0.2 Si — 0.4 AI — 0.2 Zr — 0.02
Sheet Solution Heat Treated
58
118
58
RB90
Alloy A-286 (UNS K66286) (AISI No. 660) Bars & Forgings—ASTM A 638 Bolting Material—ASTM A 453
Ni —26 Cr —15 Mo — 1.3 Fe —bal Ti — 2 AI — 0.2 B — 0.015
Bar 1800°F O.Q. plus 1325°F A.C.
105 146 25 RC28
IN-100 Alloy (UNS N13100) Castings—AMS 5397
Ni —bal Cr —10 Co —15 Mo — 3 Ti — 4.7 AI — 5.5 B — 0.014 V — 1 Zr — 0.06
Cast 123 147 9 —
IN-102 Alloy (UNS N06102) Plate, Sheet & Strip—ASTM B 519 Rod & Bar—ASTM B 518 Pipe & Tube—ASTM B 445
Ni —bal Cr —15 Mo — 3 W — 3 Cb — 3 Fe —7 Ti — 0.6 AI — 0.4 B — 0.005 Zr — 0.03
Bar 1800°F A.C.
73
139
47
215
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
41
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
0.286 7.91 2350 — 5.9217 146 20 — 29.9114 —
Alloy 713C
0.289 8.00 2410 — 5.9217 146 20 — 28.614 —
Alloy 713LC
0.297
—
8.22
—
—
—
—
—
7.7517
—
97
20
—
—
—
29.914
—
—
—
Alloy 901
0.297
8.23
—
—
—
—
—
29.514
—
HAYNES* Alloy 556
0.286 7.91 2550 0.10 9.1717 100 20 546 29.114 10.4
Alloy A-286
0.280 7.75 2435 — 7.2017 — — 31.214 —
IN-100 Alloy
0.309
8.55
2530
—
7.3217
86 20
—
29.114
—
IN-102 Alloy
14 = Dynamic Modulus 17 = 70 to 200°F 20 = at 200°F
42
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
IN-738 Alloy
Ni —bal Cr —16 Co — 8.5 AI — 3.4 Ti — 3.4 W — 2.6 Mo — 1.7 Ta —1.7 Cb — 0.9 C — 0.17 Zr — 0.1 B — 0.01
Casting 2050°F, A.C. plus 1550°F, A.C. (A.C.=Air Cooled)
138
159
5.5
—
IN-792 Alloy
Ni —bal Cr —12.4 Co — 9 AI — 3.1 Ti — 4.5 W — 3.8 Mo — 1.9 Ta — 3.9 C — 0.12 Zr — 0.1 B — 0.02
Casting 2050°F, A.C. plus 1550°F, A.C: (A.C.=Air Cooled)
154
170
4
—
Ni-939 Alloy
Ni —bal Cr —22.5 Co —19 Ti — 3.7 AI — 1.9 W — 2.0 Ta — 1.4 Cb — 1.0 C — 0.15 Zr — 0.1 B — 0.01
Casting 2120°F, A.C. plus 1560°F, A.C. (A.C.=Air Cooled)
101
147
7.1
—
1-605 Alloy, HAYNES* Alloy 25 (UNS R30605) (AISI No. 670) Bar & Forgings—AMS 5759 Sheet—AMS 5537
Co —bal Ni —10 Cr —20 W —15 Fe — 3 max Mn — 1.5 Si — 1 max C — 0.10
Sheet Solution Heat Treated
67
146
59
RC24
HAYNES* Alloy 188 (UNS R30188) Bars & Forgings—AMS 5772 Sheet, Plate & Strip—AMS 5608
Co —bal Cr —22 Ni —22 W —14 Fe — 3 max Mn — 1.25 max Si — 0.35 La — 0.04 C — 0.10
Sheet 2150°F, W.Q.
70
139
56
RB96
MAR-M* 246 Alloy
Ni —bal Cr — 9 Co —10 Mo — 2.5 W —10 Ti — 1.5 AI — 5.5 B — 0.015 Ta — 1.5 Zr — 0.05 C — 0.15
Cast
125
140
5
RC39
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
43
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
0.293
8.11
2250-2400
0.1051
6.4517
88 18
—
29.214
11.314
IN-738 Alloy
0.298
8.25
—
—
—
—
—
—
—
IN-792 Alloy
0.295
8.16
2255-2444
0.1011
6.61
83 1
736
28.9
—
IN-939 Alloy
0.330
9.13
2570
0.0921
6.817
75 20
—
32.614
L-605 Alloy, HAYNES* Alloy25
0.324
8.97
2425
0.10110
6.617
84 20
554
33.614
—
HAYNES* Alloy 188
0.307
8.5
2475
—
—
—
—
33
—
MAR-M* 246 Alloy
1 = 68 to 212°F 10 = at 212°F 14 = Dynamic Modulus 17 = 70 to 200°F 18 = at 500°F 20 = at 200°F
44
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
M-252 Alloy (UNS N07252) (AISI No. 689) Bars & Forgings—ASTM 637 Sheet & Strip—AMS 5551
Ni —bal Cr —20 Co —10 Mo —10 Ti — 2.6 AI —1 B — 0.005
Bar 1900°F A.C. plus 1400°F A.C.
122 180 16 RC39
RENÉ 41* (UNS N07041) (AISI No. 683) Bar & Forgings—AMS 5712 & 5713 Sheet, Strip & Plate—AMS 5545 Castings—AMS 5399
Ni —bal Cr —19 Co —11 Mo —10 Fe — 2 Ti — 3.1 AI — 1.5 B — 0.005
Bar 1950°F A.C. plus 1400°F A.C.
154
206
14
—
RA 333* Alloy (UNS N06333) Sheet, Strip & Plate—AMS 5593 Bars & Forgings—AMS 5717
Ni —bal Cr —25.5 Fe —14.5 Mo — 3.8 W — 3.8 Co — 3.8 Si — 1.1 Mn — 2 max C — 0.08 max
Bar Annealed
55
105
55
RB90
S-616 Alloy (UNS N30816) (AISI No. 671) Bars & Forgings—ASTM A 639 & AMS 5765Sheet & Strip—AMS 5765
Ni —20 Cr —20 Co —bal Mo — 4 W —4 Cb — 4 Fe —4
Bar 2150°F A.C. plus 1400°F A.C.
67 140 35 —
TD Nickel
Ni —bal ThO2—2.2
Bar 1800°F A.C.
90
100
25
—
UDIMET* Alloy 500 (UNS N07500) (AISI No. 684) Bars & Forgings—ASTM A 637 & AMS 5751Castings—ASTM A 567 & AMS 5384
Ni —bal Cr —18 Co —18.5 Mo — 4 Ti — 2.9 Al — 2.9 Zr — 0.05 B — 0.006
Bar 1975°F A.C. plus 1550°F A.C. plus 1400°F A.C.
110
176
16
—
UDIMET* Alloy 700 (AISI No. 687)
Ni —bal Cr —15 Co —18.5 Mo — 5.2 Ti — 3.5 AI — 4.3 B — 0.03
Bar 2150°F A.C. plus 1975°F A.C. plus 1550°F A.C. plus 1400°F A.C.
140 204 17 —
WI-52 Alloy
Co —bal Cr —21 W —11 Cb — 2 Fe —2 C — 0.45
Cast
85
125
5
380
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
45
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
0.298 8.25 2500 — 5.917 90 20 — 29.814 —
M-252 Alloy
0.298
8.25
2500
0.11
6.6317
62 20
—
31.914
—
RENÉ 41* Alloy
0.298
8.25
—
—
8.6733
—
—
31
—
RA 333* Alloy
0.313 8.65 2450 — 7.3817 86 20 — 34.914 13.6
S-816 Alloy
0.322
8.90
2650
0.106
6.017
572 20
45
22.014
—
TD Nickel
0.290
8.02
2540
—
6.7517
77 20
—
32.114
—
UDIMET* Alloy 500
0.286 7.91 2550 — 7.7421 136 20 — 32.414 —
UDIMET* Alloy 700
0.321
8.87
2450
0.11
8.021
172 20
—
—
—
WI-52 Alloy
14 = Dynamic Modulus 17 = 70 to 200°F 20 = at 200°F 21 = 70 to 1000°F 33 = 68 to 1500°F
46
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
Waspaloy (UNS N07001) (AISI No. 685) Bars & Forgings—ASTM A 637 Sheet, Strip & Plate—AMS 5544 Tube—AMS 5586
Ni —bal Cr —19.5 Co —13.5 Mo — 4.3 Ti — 3 AI — 1.3 B — 0.006 Zr — 0.04
Bar 1975°F A.C. plus 1550°F A.C. plus 1400°F A.C.
115
185
25
—
B-1900 Alloy
Ni —bal Cr — 8 Co —10 Mo — 6 Ti — 1 AI — 6 Ta — 4 B — 0.015 Zr — 0.10
Casting As Cast 120 141 8 —
D-979 Alloy (UNS N09979) (AISI No. 664) Bar & Forgings—AMS 5746 Sheet & Strip—AMS 5509
Ni —bal Cr —15 Mo — 4 W — 4 Fe —27 Ti — 3 AI —1 B — 0.01
Bar 1900°F O.Q. plus 1550°F A.C. plus 1300°F A.C.
146
204
15
—
X-40 Alloy (UNS R30031) Castings—ASTM A 567 Grade 2 & AMS 5382Wire—AMS 5789
Co —bal Ni —10.5 Cr —25.5 W — 7.5
Casting As Cast
76
108
9
—
N-155 Alloy, MULTIMET* Alloy (UNS R30155) (AISI No. 661) Bars & Forgings—ASTM A 639 & AMS 5769 Sheet, Strip & Plate—AMS 5532 Wire—AMS 5794
Fe —bal Ni —20 Cr —21 Co —20 Mo — 3 W — 2.5 Cb + Ta— 1 Mn — 1.5 Si — 1 max C — 0.10 N — 0.15
Sheet Solution Heat Treated
58
118
49
RB92
DISCALOY* (UNS K66220) (AISI No, 662) Bars & Forgings—ASTM A 638
Fe —bal Ni —26 Cr —13.5 Mo — 2.7 Ti — 1.7 AI — 0.1 B — 0.005
Bar 1850°F O.Q. plus 1500°F A.C. plus 1200°F A.C.
106 145 19 300
I R O N A N D S T E E L A L L O Y S
Ingot Iron
Fe —99.9 plus Hot Rolled
Annealed
29
19
45
38
26
45
90
67
Wrought Iron
Fe —bal Slag— 2.5
Hot Rolled
30
48
30
100
Carbon Steel—SAE 1020 (UNS 610200) Plates—ASTM A 285
Fe —bal C — 0.20 Mn — 0.45 Si — 0.25
Annealed
Quenched and Tempered at 1000°F
38
62
65
90
30
25
130
179
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
47
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
H I G H - T E M P E R A T U R E H I G H - S T R E N G T H A L L O Y S ( c o n t i n u e d )
0.296 8.19 2475 — 6.817 74 20 — 30.914 —
Waspaloy
0.297 8.22 2375 — 6.5017 71 20 — 31.014 —
B-1900 Alloy
0.296
8.19
2550
—
7.6017
92 20
—
30.014
11.6
D-919 Alloy
0.311
8.60
—
—
8.3921
82 20
—
32.814
—
X-40 Alloy
0.296
8.20
2470
—
7.91
101 42
559
29.314
—
N-155 Alloy, MULTIMET* Alloy
0.288
7.97
2665
0.113
8.5017
97 20
—
28.414
—
DISCALOY*
I R O N A N D S T E E L A L L O Y S
0.284
—
7.86
—
2795
—
0.108
—
6.8
—
490
—
57
—
30.1
—
11.8
—
Ingot Iron
0.278 7.70 2750 0.11 6.35 418 70 29 — Wrought Iron
0.284
—
7.86
—
2760
—
0.107
—
6.7
—
360
—
60
—
30
—
—
—
Carbon Steel— SAE 1020
1 = 68 to 212°F 14 = Dynamic Modulus 17 = 70 to 200°F 20 = at 200°F 21 = 70 to 1000°F 42 = at 392°F
48
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
I R O N A N D S T E E L A L L O Y S ( c o n t i n u e d )
300M Alloy Steel (UNS K44315) Bar, Forgings & Tubing—AMS 6416, 6417 & 6419
Fe —bal C — 0.43 Mn — 0.80 Si — 1.60 Ni — 1.85 Cr — 0.85 Mo — 0.40 Y — 0.08 C — 0.43
Bar Hardened and Tempered at 600°F
240
290
10
550
AISI 4340 Alloy Steel (UNS No. 643400) Bars—ASTM A 322 & A 331 Sheet & Strip—ASTM A 505 Tubing—ASTM A 519 Wire—ASTM A 547
Fe —bal C — 0.40 Mn — 0.70 Si — 0.28 Ni — 1.85 Cr — 0.80 Mo — 0.25
Annealed Oil Quenched &
Tempered at 1100°F
80
130
120
140
18
13
250
290
AISI 4620 Alloy Steel (UNS No. 646200) Bars—ASTM A 322 & A 331 Sheet & Strip—ASTM A 505 Tubing—ASTM A 519
Fe —bal C — 0.20 Mn — 0.55 Si — 0.28 Ni — 1.80 Mo — 0.25
Annealed O.Q. & Tempered 300°F
Oil Quenched & Temperedat 1100°F
56† 105†
80†
80 135
95
30 17
—
160 287
218
AISI 4820 Alloy Steel (UNS No. 648200) Bars—ASTM A 322 & A 331 Sheet & Strip—ASTM A 505 Tubing—ASTM A 519
Fe —bal C — 0.20 Mn — 0.60 Si — 0.28 Ni — 3.50 Mo — 0.25
Annealed O.Q. & Tempered 300°F
Oil Quenched & Temperedat 1100°F
66† 126
82
100 170
102
25 15
26
200 —
205
AISI 8620 Alloy Steel (UNS No. 686200) Bars—ASTM A 322 & A 331 Sheet & Strip—ASTM A 505 Tubing—ASTM A 519
Fe —bal C — 0.20 Mn — 0.80 Si — 0.28 Ni — 0.55 Cr — 0.50 Mo — 0.20
Annealed
Oil Quenched & Tempered
at 300°F
51†
112
76
142
32
17
157
284
9310 Alloy Steel (UNS 693106) Bars, Forgings & Tubing—AMS 6263, 6265
& 6267
Fe —bal C — 0.10 Mn — 0.55 Si — 0.28 Ni — 3.25 Cr — 1.20 Mo — 0.12
Annealed
Oil Quenched & Temperedat 300°F
80†
123
100
159
25
16
200
321
NITRALLOY* N Alloy Steel (UNS K52355) Bars, Forgings & Tubing—AMS 6475
Fe —bal C — 0.24 Mn — 0.55 Si — 0.30 Ni — 3.50 Cr — 1.15 Mo — 0.25 AI — 1.25
Quenched & Tempered at 1200°F
Before Nitriding
Core after Nitriding at 975°F
115
170
132
180
22
16
275
370
3 1/2% Nickel Steel Plate—ASTM A 203 Pipe & Tubing—ASTM A 333 & A 334 Forgings—ASTM A 350 & A 336
Fe —bal C — 0.20 Mn — 0.50 Si — 0.25 Ni — 3.50
Plate Normalized 45 78 23 160
*See page 84 for list of trademarks † Yield Point
PROPERTIES OF SOME METALS AND ALLOYS
49
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
I R O N A N D S T E E L A L L O Y S ( c o n t i n u e d )
0.283
7.84
2740
0.107
6.7
360
60
30
11.6
300M Alloy Steel
0.283
—
7.84
—
2740
—
0.117
—
6.317
—
264
—
148
—
29
—
—
—
AISI 4340 Alloy Steel
0.283 —
—
7.83 —
—
— —
—
0.11 —
—
6.317 —
—
290 3
—
—
149 —
—
29 —
—
— —
—
AISI 4620 Alloy Steel
0.284
—
—
7.86
—
—
— —
—
0.115
—
—
6.4
—
—
255
3 —
—
158
—
—
29 —
—
12 —
—
AISI 4820 Alloy Steel
0.283
—
7.85
—
—
—
0.11
—
6.21
—
260
26
—
180
—
29
—
12
—
AISI 8620 Alloy Steel
0.283
—
7.83
—
—
—
0.115
—
6.5
—
238
—
168
—
29
—
—
—
9310 Alloy Steel
0.283
—
7.83
—
—
—
0.115
—
6.5
—
240
—
166
—
29
—
—
—
NITRALLOY* N Alloy Steel
0.284 7.85 — 0.1521 6.1548 253 3 — 30 —
3 1/2% Nickel Steel
1 = 68 to 212°F 3 = at 68°F 17 = 70 to 200°F 26 = at 120°F 48 = 0 to 200°F
50
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
I R O N A N D S T E E L A L L O Y S ( c o n t i n u e d )
9% Nickel Steel Plate—ASTM A 353 & A 553 Pipe & Tube—ASTM A 333 & A 334 Forgings —ASTM A 522
Fe —bal C — 0.13 max Mn — 0.60 Si — 0.25 Ni —9
Plate Quenched and Tempered at 1175°F
Plate Double Normalized and Tempered at 1175°F
93 88
110 110
25 26
RC23 RC23
IN-787 Alloy Steel ASTM A 710 Plate—ASTM A 736 Flanges—ASTM A 707
Fe —bal C — 0.05 Mn — 0.55 Si — 0.25 Ni — 0.85 Cr — 0.75 Mo — 0.2 Cu — 1.15 Cb — 0.04
Hot Rolled & Aged Normalized & Aged
Water Quenched & Aged
95 73 90
108 89
104
36 28 25
195 150 185
High-Yield-Strength Alloy Steels (Quenched and Tempered) Plate—ASTM A 514 & A 517 Forgings—ASTM A 592
Fe —bal C — 0.16 Mn — 0.85 Si — 0.35 Ni — 1.50 max Cr — 2.00 max Mo — 0.35 V — 0.08 max Ti — 0.10 max Zr — 0.15 max Cu — 0.50 max B — 0.003
Plate Quenched and Tempered 1150°F min
110
125
19
255
2 1/2% Nickel Cast Steel Castings—ASTM A 352
Fe —bal C — 0.21 Mn — 0.75 Si — 0.25 Ni — 2.3
Castings Normalized
and Tempered (Heavy Sections are Liquid Quenched)
42 75 25 156
3 1/2% Nickel Cast Steel Castings —ASTM A 352
Fe —bal C — 0.13 Mn — 0.75 Si — 0.25 Ni — 3.5
Castings Normalized
and Tempered (Heavy Sections are Liquid Quenched)
42 75 26 157
Maraging Steel 18-200 (UNS K92810) Plate—ASTM A 538
Fe —bal Ni —18 Mo — 4.2 Ti — 0.2 AI — 0.1 C — 0.03 max Co — 7.8
Annealed
Aged at 900°F
117
200
145
215
17
12
RC27
RC46
Maraging Steel 18-250 (UNS K92890) Plate—ASTM A 538
Fe —bal Ni —18 Mo — 4.8 Ti — 0.4 AI — 0.1 C — 0.03 max Co — 7.8
Annealed
Aged at 900°F
116
250
146
260
19
10
RC29
RC49
Maraging Steel 18-300 (UNS K93120) Plate—ASTM A 538
Fe —bal Ni —18.5 Mo — 4.8 Ti — 0.65 AI — 0.1 C — 0.03 max Co — 8.8
Annealed
Aged at 900°F
115
280
147
290
17
8
RC32
RC53
PROPERTIES OF SOME METALS AND ALLOYS
51
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
I R O N A N D S T E E L A L L O Y S ( c o n t i n u e d )
0.284
—
7.86
—
2730
—
0.08822
—
4.922
—
9123
—
203
—
3023
—
—
—
9% Nickel Steel
0.283 — —
7.84 — —
— — —
0.12 — —
6.417 — —
— — —
— — —
29 — —
12 — —
IN-787 Alloy Steel
0.283
7.83
—
0.11
6.6
264
148
29
12
High-Yield-StrengthAlloy Steels
0.283 7.83 — 0.11 6.4 2783 132 29 12
2 1/2% Nickel Cast Steel
0.284 7.84 — 0.11 6.3 2543 144 30 12
3 1/2% Nickel Cast Steel
—
0.289
—
8.00
—
2650
—
0.107
—
5.624
2033
1363
—
300 to 420
273
26.2
—
—
Maraging Steel 18-200
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
27.0
—
—
Maraging Steel 18-250
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
27.5
—
—
Maraging Steel 18-300
3 = at 68°F 17 = 70 to 200°F 22 = –320 to 70°F 23 = at –32°F 24 = 70 to 900°F
52
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T I R O N A L L O Y S
Cast Gray Iron (UNS F12101) Castings—ASTM A 48 Class 30 &
A 278 Class 30
C — 3.4 Si — 1.8 Mn — 0.8 Fe —bal
As Cast
—
32
—
190
Malleable Iron (UNS F22200) Castings—ASTM A 47 Grade 32510
C — 2.5 Si — 1 Mn — 0.55 max Fe —bal
Annealed
33
52
12
130
Ductile Iron (UNS F32800) (Nickel Containing) Grade 60-40-18
Castings—ASTM A 536 & A 395
Fe —bal C — 3.6 Si — 2.3 Mn — 0.5 Ni — 0.75
Annealed 47 65 24 160
Ductile Iron (UNS F33100) (Nickel Containing) Grade 65-45-12
Castings—ASTM A 536
Fe —bal C — 3.6 Si — 2.3 Mn — 0.5 Ni — 0.75
Annealed or As Cast 52 72 13 174
Ductile Iron (UNS F33800) (Nickel Containing) Grade 80-55-06
Castings—ASTM A 536
Fe —bal C — 3.6 Si — 2.3 Mn — 0.5 Ni — 0.75
As Cast 65 90 8 228
Ductile Iron (UNS F34800) (Nickel Containing) Grade 100-70-03
Castings—ASTM A 536
Fe —bal C — 3.6 Si — 2.3 Mn — 0.5 Ni — 0.75
Normalized and Tempered 80 110 6 260
Ductile Iron (UNS F36200) (Nickel Containing) Grade 120-90-02
Castings—ASTM A 536
Fe —bal C —3.6 Si —2.3 Mn —0.5 Ni —0.75
Oil Quenched and Tempered 120 140 4 325
Ni-Resist Type 1 (UNS F41000) ASTM A 436
Fe —bal Ni —15.5 Si — 2 Mn — 1.25 Cu — 6.5 Cr — 2 C — 3 max
As Cast — 27 — 150
Ni-Resist Type 2 (UNS F41002) ASTM A 436
Fe —bal Ni —20 Si — 2 Mn — 1.25 Cr — 2 C — 3 max
As Cast
—
27
—
145
Ni-Resist Type 5 (UNS F41006) ASTM A 436
Fe —bal Ni —35 Si — 1.5 Mn — 0.6 C — 2.4 max
As Cast — 22 — 110
Ductile Ni-Resist Type D-2 (UNS F43000) Castings—ASTM A 439
Fe —bal Ni —20 Si — 2.25 Cr — 2.25 C — 3 max
As Cast 32 59 14 170
PROPERTIES OF SOME METALS AND ALLOYS
53
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T I R O N A L L O Y S
0.260
7.20
2150
—
6.7
310
400
14
—
Cast Gray Iron
0.264
7.32
2250
0.122
6.6
—
180
25
—
Malleable Iron
0.250 7.1 2150 — 6.21 276 10 399 11 24.5 9.3
Ductile Iron
0.250 7.1 2150 — 6.21 276 10 399 11 24.5 9.3
Ductile Iron
0.252 7.2 2150 — 5.91 218 10 408 11 24.5 9.3
Ductile Iron
0.252 7.2 2150 — 5.91 218 10 408 11 24.5 9.3
Ductile Iron
0.252 7.2 2150 — 5.91 218 10 408 11 24.5 9.3
Ductile Iron
0.264 7.3 2250 0.116 10.44 276 1020 15.6 4.5
Ni-Resist Type 1
0.264 7.3 2250 0.116 10.44 276 1020 15.6 4.5
Ni-Resist Type 2
0.268 7.41 2250 — 2.84 273 — 10.5 4.5
Ni-Resist Type 5
0.268 7.41 2250 — 10.44 93 612 17.5 —
Ductile NI-Resist Type D-2
1 = 68 to 212°F 4 = 68 to 392°F 10 = at 212°F 11 = at 72°F
54
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T I R O N A L L O Y S ( c o n t i n u e d )
Ductile Ni-Resist Type D-5 (UNS F43006) Castings—ASTM A 439
Fe —bal Ni —35 Si — 2 C — 2.4 max
As Cast 32 58 30 155
Ductile Ni-Resist Type D-5S
Fe —bal Ni —36 Si — 5.3 Mn — 0.5 Cr — 2.0 C — 2.0
As Cast
36
63
20
160
Ni-Hard Type 1 (UNS F45000) Castings—ASTM A 532 Class IA
Fe —bal Ni —4.5 Cr —2.1 C —3.3 Si —0.5 Mn —0.6
Sand Cast
Chill Cast
—
—
60
90
—
—
600
650
Ni-Hard Type 2 (UNS F45001) Castings—ASTM A 532 Class IB
Fe —bal Ni —4.5 Cr —2.1 C —2.8 Si —0.5 Mn —0.6
Sand Cast
Chill Cast
—
—
60
100
—
—
575
625
Ni-Hard Type 4 (UNS F45003) Castings—ASTM A 532 Class ID
Fe —bal Ni —6 Cr —8.5 C —3 Si —1.5 Mn —0.6
Sand Cast
Chill Cast
—
—
80
110
—
—
600
650
DURIRON* (Cast) Iron-Silicon Alloy
Fe —bal Si —14.5 C — 0.85
As Cast — 16 — 520
DURICHLOR* (Cast) Iron-Silicon-Molybdenum Alloy
Fe —bal Si —14.5 Ma — 3 C — 0.85
As Cast
—
16
—
520
W R O U G H T S T A I N L E S S S T E E L
Type 201 Stainless Steel (UNS S20100) Plate, Sheet & Strip—ASTM A 412 & A 666 Bar—ASTM A 276
Fe —bal Cr —17 Ni — 4.5 Mn — 6.5 N — 0.25 max C — 0.15 max
Strip Annealed
55
115
60
RB90
Type 202 Stainless Steel (UNS S20200) Sheet, Plate & Strip—ASTM A 412 & A 666 Bar—ASTM A 314 & A 276 Forgings—ASTM A 473
Fe —bal Cr —18 Ni — 5 Mn — 9 N — 0.25 max C — 0.15
Strip Annealed
55
105
55
RB90
Type 301 Stainless Steel (UNS S30100) Plate, Sheet & Strip—ASTM A 167, A 177
& A 666 Tube—ASTM A 554
Fe —bal Cr —17 Ni — 7 C — 0.15 max
Strip Annealed
Cold Rolled
40 up to 165
110 up to 200
60
8
RB85 up to RC41
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
55
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T I R O N A L L O Y S ( c o n t i n u e d )
0.278
7.68
2250
—
—
—
—
18
—
Ductile Ni-Resist Type D-5
0.266
7.37
2160-2232
—
5.417
—
—
16
—
Ductile Ni-Resist Type D-5S
0.278
—
7.70
—
—
—
—
—
4.725
—
99 26
—
480 5
—
25
—
—
—
Ni-Hard Type 1
0.278
—
7.70
—
—
—
—
—
4.725
—
99 26
—
480 5
—
25
—
—
—
Ni-Hard Type 2
0.278
—
7.70
—
—
—
—
—
6.425
—
99 26
—
540 5
—
25
—
—
—
Ni-Hard Type 4
0.255 7.0 2300 0.13 7.421 — — 23 — DURIRON*
0.255
7.0
2300
0.13
7.2
—
—
23
—
DURICHLOR*
W R O U G H T S T A I N L E S S S T E E L
0.283
7.86
—
—
8.727
—
423
28.6
—
Type 201 Stainless Steel
0.282
7.83
—
—
10.228
—
427
—
—
Type 202 Stainless Steel
0.29
—
7.9
—
2590
—
0.12
—
9.4
—
113 10
—
432
—
28
—
12.5
—
Type 301 Stainless Steel
5 = at 77°F 10 = at 212°F 17 = 70 to 200°F 21 = 70 to 1000°F 25 = 50 to 200°F 26 = at 120°F 27 = 32 to 700°F 28 = 32 to 600°F
56
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
Type 302 Stainless Steel (UNS S30200) Plate, Sheet & Strip—ASTM A 167, A 240
& A 666 Bar—ASTM A 276, A 314 & A 479 Wire—ASTM A 313, A 478 & A 492 Forgings—ASTM A 473 Tube—ASTM A 511 & A 554
Fe —bal Cr —18 Ni — 9, C — 0.15 max
Sheet Annealed
Cold Rolled
40 up to 165
90 up to 190
50
5
RB85 up to RC40
Type 303 & 303 Se Stainless Steel (UNS S30300) Bar—ASTM A 276, A 314, A 320 & A 582 Forgings—ASTM A 473 Wire—ASTM A 581
Fe —bal Cr —18 Ni — 9 S — 0.15 min or Se — 0.15 min C — 0.15 max
Bar Annealed
35
90
50
160
Type 304 Stainless Steel (UNS S30400) Plate, Sheet & Strip—ASTM A 167, A 240
& A 666 Tube—ASTM A 213, A 249 & A 632 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 313, A 49,2 & A 580
Fe —bal Cr —18.5 Ni — 9.5 C — 0.08 max
Sheet Annealed
Cold Rolled
35 up to 160
85 up to 185
50
4
RB80 up to RC40
Type 304L Stainless Steel (UNS 530403) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 213, A 249 & A 632 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 478 & A 580
Fe —bal Cr —18.5 Ni —10 C — 0.03 max
Sheet Annealed
28
75
50
RB70
Type 304 plus Boron Stainless Steel
Fe —bal Cr —18 Ni —10 B —2
Sheet Annealed
53
96
12
RB95
Type 305 Stainless Steel (UNS S30500) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 249, A 511 & A 554 Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Wire—ASTM A 313, A 492 & A 580
Fe —bal Cr —18 Ni —12 C — 0.12 max
Sheet Annealed
38
85
50
RB80
Type 309 Stainless Steel (UNS S30900) Plate, Sheet & Strip—ASTM A 167 Tube—ASTM A 249, A 312 & A 511 Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —23 Ni —13.5 C — 0.20 max
Sheet Annealed
45
90
45
RB85
Type 310 Stainless Steel (UNS S31000) Plate, Sheet & Strip—ASTM A 167 Tube—ASTM A 213, A 249 & A 312 Bar—ASTM A 276 & A 314 Forgings—ASTM A 473
Fe —bal Cr —25 Ni —20 C — 0.25 max
Sheet Annealed 45 95 45 RB85
Type 314 Stainless Steel (UNS S31400) Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —25 Ni —20 Si — 2.5 C — 0.25 max
Bar Annealed 50 100 45 180
PROPERTIES OF SOME METALS AND ALLOYS
57
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.29
—
7.9
—
2590
—
0.12
—
9.6
—
113 10
—
432
—
28
—
12.5
—
Type 302 Stainless Steel
0.29
7.9
2590
0.12
9.6
113 10
432
28
—
Type 303 & 303 Se Stainless Steel
0.29
—
7.9
—
2650
—
0.12
—
9.6
—
113 10
—
432
—
28
—
12.5
—
Type 304 Stainless Steel
0.29
7.9
2650
0.12
9.6
113 10
432
28
12.5
Type 304 L Stainless Steel
0.29
7.9
—
0.12
10.529
—
445
—
—
Type 304 plus Boron Stainless Steel
0.29
7.9
2650
0.12
9.6
113 10
432
28
12.5
Type 305 Stainless Steel
0.29
7.9
2650
0.12
8.3
96 10
468
29
—
Type 309 Stainless Steel
0.29 7.9 2650 0.12 8.0 96 10 468 30 —
Type 310 Stainless Steel
0.279 7.72 — 0.12 8.428 121 10 462 29 —
Type 314 Stainless Steel
10 = at 212°F 28 = 32 to 600°F 29 = 32 to 1200°F
58
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
Type 316 Stainless Steel (UNS S31600) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 213, A 249 & A 269 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 313
Fe —bal Cr —17 Ni —12 Mo — 2.25 C — 0.08 max
Sheet Annealed
40
90
50
RB85
Type 316L Stainless Steel (UNS S31603) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 213, A 249, A 269 & A 688 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 478 & A 580
Fe —bal Cr —17 Ni —13 Mo — 2.25 C — 0.03 max
Sheet Annealed
32
75
50
RB72
Type 317 Stainless Steel (UNS S31700) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 249, A 269 & A 594 Bar—ASTM A 314 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —19 Ni —13 Mo — 3.5 C — 0.08 max
Sheet Annealed
—
—
—
—
Type 317 LM* Stainless Steel
Fe —Bal Cr —19 Ni —14 Mo — 4.25 Si — 1.0 max C — 0.03 max
Annealed
44
91
42
RB85
JESSOP* Type 317L Plus Stainless Steel
Fe —bal Cr —19 Ni —14 Mo — 4.3 Si — 0.7 C — 0.02
Annealed
45
90
40
RB84
Type 321 Stainless Steel (UNS S32100) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 213, A 249 & A 269 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473
Fe —bal Cr —18 Ni —11 Ti — 5×C min C — 0.08 max
Sheet Annealed 35 90 50 RB80
Type 329 Stainless Steel (UNS S32900) Tube—ASTM A 268 & A 511
Fe —bal Cr —27.5 Ni — 4.75 Mo — 1.5 C — 0.15
Annealed 1775°F, water quenched
Aged 1400°F, 8 hr Aged 1400°F, 40 hr
80 — —
105 — —
25 — —
RC22 RC45 RC50
Type 330 Stainless Steel (UNS N08330) Plate, Sheet & Strip—AMS 5592
& ASTM B 536 Bar—AMS 5716, ASTM B 511 & B 512 Pipe—ASTM B 535 & B 546
Fe —bal Cr —19 Ni —35 Si — 1.25 C — 0.08 max
Hot Rolled
Annealed
55
39
100
85
35
50
200
150
Type 347 Stainless Steel (UNS S34100) Plate, Sheet & Strip—ASTM A 167 & A 240 Tube—ASTM A 213, A 269 & A 571 Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —18 Ni —11 Cb + Ta—10×C min C — 0.08 max
Sheet Annealed
40
95
45
RB85
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
59
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.29 7.9 2550 0.12 8.9 113
10
444
28
—
Type 316 Stainless Steel
0.29
7.9
2550
0.12
8.9
113
10
444
28
—
Type 316L Stainless Steel
0.29
7.9
2550
0.12
7.9
113
10
444
28
—
Type 317 Stainless Steel
0.29
7.9
2500-2550
0.12
8.0
112
10
444
28
—
Type 317LM* Stainless Steel
0.29
7.9
2500-2550
0.12
8.1
105
440
28
—
JESSOP* Type 317L Plus Stainless Steel
0.29 7.9 2600 0.12 9.3 112
10 432 28 —
Type 321 Stainless Steel
0.28 — —
7.75 — —
— — —
0.11 — —
8.033 — —
— — —
450 — —
— — —
— — —
Type 329 Stainless Steel
—
0.289
—
8.0
2550
—
0.11
—
—
8.317
—
86
—
610
—
28.5
—
—
Type 330 Stainless Steel
0.29
8.03
2600
0.12
9.3
112
10
438
28
—
Type 347 Stainless Steel
10 = at 212°F 17 = 70 to 200°F 33 = 68 to 1500°F
60
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
CARPENTER* No. 10 Stainless Steel (UNS S38400)
Bar & Wire—ASTM A 493
Fe —bal Cr —16 Ni —18 C — 0.08 max
Annealed
35
75
55
126
CARPENTER 20Cb-3* Stainless Steel
Fe —bal Ni —34 Cr —20 Mo — 2.5 Cu — 3.5 Cb + Ta—8xC min C — 0.06 max
Bar Annealed
43
90
39
183
AL-6X* Stainless Steel
Fe —bal Cr —20 Ni —24 Mo — 6.3 Mn — 1.5 Si — 0.5 C — 0.025
Strip Annealed
Cold Reduced 20%
Cold Reduced 50%
40
115
151
90
127
162
45
14
4.5
—
—
—
JESSOP JS700* Stainless Steel (UNS N08700) Plate, Sheet & Strip—ASTM B 599
Fe —bal Cr —21 Ni —25 Mo — 4.5 Cb — 0.4 Cu — 0.4 C — 0.04 max
Annealed
35 min
80 min
30 min
212 max
JESSOP JS777* Stainless Steel
Fe —bal Cr —21 Ni —25 Mo — 4.5 Cb — 0.3 Cu — 2.0 C — 0.04 max
Annealed
35 min
80 min
30 min
212 max
904 L Stainless Steel (UNS N08904) Plate, Sheet & Strip—ASTM B 625 Bar & Wire—ASTM B 649 Pipe & Tube—ASTM B 673, B 674 & B 677
Fe —bal Cr —20 Ni —25 Mo — 4.5 Cu — 1.5 Mn — 1.7 Si — 0.4 C — 0.02 max
Annealed 2012°F, Water Quenched
36
85
50
140
HASTELLOY* Alloy M-531 (UNS N08310) Sheet, Strip & Plate—ASTM B 620 Rod—ASTM B 621 Pipe & Tube—ASTM B 619, B 622 & B 626
Fe —bal Cr —22 Ni —26 Mn — 2.5 max Mo — 5 Si — 1.0 max Ti — 4xC min C — 0.05 max
Sheet Solution Heat Treated
44
84
42
RB83
FERRALIUM* Alloy 255
Fe —bal Cr —26 Ni — 5.5 Mo — 3 Mn — 0.8 Si — 0.45 Cu — 1.7 N — 0.17 C — 0.04 max
Sheet Solution Heat Treated
Hardened at 950°F
94
102
124
131
25
24
RC21
—
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
61
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.29
8.03
—
0.12
9.5
—
476
—
—
CARPENTER* No.10 Stainless Steel
0.291
8.05
—
0.12
8.311
84.626
625
28
11
CARPENTER 20Cb-3* Stainless Steel
0.293
—
—
8.1
—
—
2500
—
—
—
—
—
8.51
—
—
95
1
—
—
570
—
—
29
—
—
—
—
—
AL 6X* Stainless Steel
0.29
8.0
—
—
9.15
102
—
—
—
JESSOP J5700* Stainless Steel
0.29
8.0
—
—
9.15
102
—
—
—
JESSOP J5717* Stainless Steel
0.285
7.90
—
0.123
5.81
126
480
28
—
904 L Stainless Steel
0.297
8.22
—
—
—
—
—
—
—
HASTELLOY* Alloy M-532
0.282
—
7.81
—
—
—
—
—
6.745
—
105 3
—
473
—
30.514
—
—
—
FERRALIUM* Alloy 255
1 = 68 to 212°F 3 = at 68°F 14 = Dynamic Modulus 26 = at 120°F 45 = 68 to 600°F
62
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
NITRONIC* 20 Stainless Steel
Fe —bal Cr —23 Ni — 8 Mn — 2.5 Si — 0.8 N — 0.35 C — 0.33
2150°F, Water Quenched
Aged 1400°F, Air Cooled
75
84
138
142
46
29
RC24
RC36
NITRONIC* 32 Stainless Steel (UNS 24100) Bars—ASTM A 479 Wire—ASTM A 580 Spring Wire—ASTM A 313
Fe —bal Cr —18 Ni — 1.6 Mn —12 Si — 0.5 N — 0.3 C — 0.10
Annealed
Cold Reduced 20%
Cold Reduced 50%
60
135
204
115
172
238
55
28
10
RB96
RC28
RC40
NITRONIC* 33 Stainless Steel (UNS 24000) Bars & Shapes—ASTM A 276 & A 479 Plate, Sheet & Strip—ASTM A 240 & A 412 Tube—ASTM A 269 Pipe—ASTM A 312 Wire—ASTM A 580 Spring Wire—ASTM A 313
Fe —bal Cr —18 Ni — 3 Mn — 13 Si — 1.0 max N — 0.3 C — 0.08 max
Sheet Annealed
Cold Reduced 20%
Cold Reduced 50%
68
140
191
115
160
210
50
18
6
RB95
RC37
RC44
NITRONIC* 40 Stainless Steel (UNS S21900) Plate, Sheet & Strip—ASTM A 412 & AMS 5595 Bars & Shapes—ASTM A 276 Wire—ASTM A 580 Bar, Wire, Etc.—AMS 5656
C is also available
Fe —bal Cr —20 Mn — 9 Ni — 6.5 Si — 1 max N — 0.3 C — 0.08 max
at 0.04 max in UNS S21904
Sheet Annealed
Cold Reduced 20%
Cold Reduced 50%
65
132
175
108
148
192
43
18
7
RB92
RC31
RC39
NITRONIC* 50 Stainless Steel (UNS 520910) Bars & Shapes—ASTM A 276 & A 479 Plate, Sheet & Strip—ASTM A 240 & A 412 Tube—ASTM A 269 Pipe—ASTM A 312 & A 403 Wire—ASTM A 580 AMS 5764 & 5861
Fe —bal Cr —22 Ni —12.5 Mn — 5 Mo — 2.25 Si — 1.0 max N — 0.3 Cb — 0.2 V — 0.2 C — 0.06 max
Bar Annealed 1950°F
Cold Drawn 30%
Cold Drawn 60%
65
174
216
125
194
234
45
15
9
RC23
—
—
NITRONIC* 60 Stainless Steel (UNS S21800) Bars & Shapes—ASTM A 276 & A 479 Wire—ASTM A 580
Fe —bal Cr —17 Ni — 8.5 Mn — 8 Si — 4 N — 0.13 C — 0.10 max
Bar Annealed
Cold Drawn 20%
Cold Drawn 50%
60
112
174
103
140
217
64
35
15
RB95
RC31
RC41
18-9 LW* Stainless Steel (UNS S30430) Bar & Wire—ASTM A 493
Fe —bal Cr —18 Ni —9 Cu — 3.5
Annealed
30
78
65
150
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
63
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.279
—
7.73
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
NITRONIC* 20 Stainless Steel
0.281
—
—
7.78
—
—
—
—
—
—
—
—
9.01
—
—
—
—
—
421
—
—
29
—
—
11
—
—
NITRONIC* 32 Stainless Steel
0.280
—
—
7.76
—
—
—
—
—
—
—
—
8.917
—
—
110 10
—
—
444 5
—
—
—
—
—
—
—
—
NITRONIC* 33 Stainless Steel
0.283
—
—
7.83
—
—
—
—
—
—
—
—
9.341
—
—
96 20
—
—
438
—
—
28
—
—
—
—
—
NITRONIC* 40 Stainless Steel
0.285
—
—
7.88
—
—
—
—
—
—
—
—
9.017
—
—
108 34
—
—
492
—
—
28
—
—
10
—
—
NITRONIC* 50 Stainless Steel
0.275
—
—
7.62
—
—
—
—
—
—
—
—
8.81
—
—
—
—
—
589
—
—
26
—
—
—
—
—
NITRONIC* 60 Stainless Steel
—
—
—
—
—
—
—
—
—
18-9 LW* Stainless Steel
1 = 68 to 212°F 5 = at 77°F 10 = at 212°F 17 = 70 to 200°F 20 = at 200°F 34 = at 300°F 41 = at 300°F
64
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
17-7 PH* Stainless Steel (UNS S17700) (AISI No. 631)
Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 579 & A 705 Wire—ASTM A 313
Fe —bal Cr —17 Ni — 7 AI — 1.1
Sheet Solution Treated
Hardened
40
220
130
235
35
6
RB85
RC48
17-4 PH* Stainless Steel (UNS S17400) (AISI No. 630)
Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 705
Fe —bal Cr —16.5 Ni — 4 Cu — 4 Cb + Ta—0.3
Bar Solution Treated
Hardened
110
185
150
200
12
14
RC32
RC44
15-5 PH* Stainless Steel (UNS S15500) Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 705
Fe —bal Cr —15 Ni — 5 Cu — 4
Bar Solution Treated
Hardened
110
185
150
200
12
14
RC32
RC44
PH 15-7 Mo* Stainless Steel (UNS S15700) (AISI No. 632)
Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 705
Fe —bal Cr —15 Ni — 7 Mo — 2.5 AI — 1.1
Solution Treated
Hardened
55
225
130
240
35
6
RB88
RC48
PH 14-8 Mo* Stainless Steel (UNS S14800) AMS 5601 & AMS 5603
Fe —bal Cr —14 Ni —8 Mo — 2.5 AI — 1.1
Sheet Solution Treated
Hardened
55
220
125
235
25
5
RB88
RC49
PH 13-8 Mo* Stainless Steel (UNS S13800) Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 705
Fe —bal Cr —13 Ni — 8 Mo — 2.2 AI —1
Bar Solution Treated
Hardened
100
200
160
225
15
13
RC30
RC48
Stainless “W”* (UNS S17600) (AISI No. 635)
Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 705
Fe —bal Cr —17 Ni — 7 Ti — 0.7 Al — 0.2 C — 0.07
Annealed
Hardened at 1000°F
98
190
135
200
15
11
RC26
RC44
AM 350* Stainless Steel (UNS S35000) (AISI No. 633)
Sheet & Strip—AMS 5546 Tube—AMS 5554 Forgings—ASTM A 579
Fe —bal Cr —17 Ni — 4 Mo — 3 C — 0.08
Annealed
Hardened
60
173
145
206
40
13.5
290
410
AM 355* Stainless Steel (UNS S35500) (AISI No. 634)
Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 579 & A 705
Fe —bal Cr —15.5 Ni — 4.5 Mo — 3
Annealed
Hardened
57
174
160
210
26
14
310
415
CUSTOM 455* Stainless Steel (UNS S45500) (Maraging)
Bar—ASTM A 564 Plate, Sheet & Strip—ASTM A 693 Forgings—ASTM A 705
Fe —bal Cr —11.75 Ni — 9 Cu — 2.25 Ti — 1.2 Cb — 0.3 C — 0.03 max
Annealed
Hardened
115
220
140
230
12
10
280
500
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
65
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.282
0.276
7.81
7.65
—
—
—
—
8.517
5.717
—
128 18
480
498
—
29
—
11
17-7 PH* Stainless Steel
0.280
0.282
7.74
7.80
—
—
0.11
0.10
6.017
6.017
—
135 18
588
462
—
28.5
—
12.7
17-4 PH* Stainless Steel
0.280
0.282
7.74
7.80
—
—
0.11
0.10
6.017
6.017
—
135 18
588
462
28.5
—
11.2
—
15-5 PH* Stainless Steel
0.282
0.277
7.80
7.68
—
—
—
—
8.017
5.017
—
112 20
480
498
—
29
—
11.4
PH 15-7 Mo* Stainless Steel
0.283
0.278
7.83
7.71
—
—
—
—
—
5.317
—
—
—
—
—
—
—
—
PH 14-8 Mo* Stainless Steel
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
—
PH 13-8 Mo* Stainless Steel
0.28
0.28
7.7
7.7
—
—
—
—
5.5
—
130 10
145 10
600
510
28
28
—
11.3
Stainless “W”*
0.286
0.282
7.92
7.81
2550
—
—
—
—
6.3
—
100
—
475
—
29.4
—
11.3
AM 350* Stainless Steel
0.286
0.282
7.92
7.81
2550
—
—
—
—
6.4
—
105
—
455
—
29.3
—
11.4
AM 355* Stainless Steel
0.280
—
7.74
—
—
—
—
—
5.9
—
—
—
—
—
29
—
11
—
CUSTOM 455* Stainless Steel
10 = at 212°F 17 = 70 to 200°F 18 = at 500°F 20 = at 200°F
66
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
17-14 Cu Mo Stainless Steel (AISI No. 653)
Fe —bal Cr —17 Ni —14 Cu — 3 Mo — 2.5 Ti — 0.25 Cb — 0.5
Annealed and Aged
Hot Cold Worked 20%
42
93
86
114
45
20
170
255
19-9 DL Alloy (UNS K63198) (AISI No. 651)
Plate, Sheet & Strip—ASTM A 457 Bar—ASTM A 458 Forgings—ASTM A 477
Fe —bal Cr —19 Ni — 9 Mo — 1 W — 1.25 Cb + Ta—0.4 Ti —0.25 C —0.30
Hot Rolled and Stress Relieved
Cold Worked
and Stress Relieved
41
88
74
98
30
13
216
321
Greek Ascoloy Stainless Steel (UNS S41800) (AISI No. 615)
AMS 5508, 5616 & 5817 Bars & Forgings—ASTM A 565
Fe —bal Cr —12 W — 3 Ni — 2
Bar Hardened
150
170
13
340
Type 405 Stainless Steel (UNS S40500) Plate, Sheet & Strip—ASTM A 176 & A 240 Tube—ASTM A 268 & A 511 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —12.5 C — 0.08 max Al — 0.2
Sheet Annealed
40
65
25
RB75
Type 409 Stainless Steel (UNS S40900) Plate, Sheet & Strip—ASTM A 176 Tube—ASTM A 268 & A 651
Fe —bal Cr —11 Mn — 1.0 max Si — 1.0 max Ti — 0.75 max (6×C min) C — 0.08
Annealed
38
68
25
RB75
Type 410 Stainless Steel (UNS S41000) Plate, Sheet & Strip—ASTM A 176 & A 240 Tube—ASTM A 268 & A 511 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —12 C — 0.15 max
Sheet Annealed
Heat Treated
45
140
70
180
25
15
RB80
RC39
Type 414 Stainless Steel (UNS S41400) Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Tube—ASTM A 511 Wire—ASTM A 580
Fe —bal Cr —12.5 Ni — 2 C — 0.15 max
Sheet Annealed
Bar Heat Treated
105
150
120
200
15
15
RB98
RC43
Type 420 Stainless Steel (UNS S42000) Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —13 C —over 0.15
Bar Annealed
Heat Treated
50
195
95
230
25
8
RB92
500
Type 430 Stainless Steel (UNS S43000) Plate, Sheet & Strip—ASTM A 176 & A 240 Tube—ASTM A 268, A 511, A 554 & A 651 Bar—ASTM A 276, A 314 & A 479 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —17 C — 0.12 max
Sheet Annealed
Cold Rolled
45 up to
95
75 up to 110
25
10
RB80 up to 225
Type 431 Stainless Steel (UNS 543100) Forgings—ASTM A 473 Bar—ASTM A 276 & A 314 Wire—ASTM A 580
Fe —bal Cr —16 Ni — 1.75 C — 0.20 max
Bar Annealed
Hardened
95
150
125
195
25
15
260
400
PROPERTIES OF SOME METALS AND ALLOYS
67
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.287
—
7.94
—
—
—
—
—
8.23
—
98
—
—
—
28
—
—
—
17-14 Cu Me Stainless Steel
0.287
—
7.94
—
2615
—
0.10
—
8.5
—
9.4
—
—
—
29.5
—
—
—
19-9 DL Alloy
0.284
7.86
2670
0.11
5.3
—
—
29
—
Greek Ascoloy Stainless Steel
0.28
7.7
2790
0.11
6.0
—
360
29
—
Type 405 Stainless Steel
0.278
7.68
2600-2750
— 6.5 —
—
—
—
Type 409 Stainless Steel
0.28
—
7.7
—
2790
—
0.11
—
6.1
—
173 10
—
342
—
29
—
—
—
Type 410 Stainless Steel
0.28
—
7.7
—
—
—
0.11
—
5.8
—
173 10
—
420
—
—
—
—
—
Type 414 Stainless Steel
.28
—
7.7
—
—
—
0.11
—
5.7
—
173 10
—
330
—
29
—
—
—
Type 420 Stainless Steel
0.280
—
7.75
—
2750
—
0.11
—
5.8
—
181 10
—
360
—
29
—
—
—
Type 430 Stainless Steel
0.280
—
7.75
—
2700
—
0.11
—
6.5
—
140 10
—
432
—
29
—
—
—
Type 431 Stainless Steel
10 = at 212°F
68
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
Type 440C Stainless Steel (UNS S44004) Forgings—ASTM A 473 Bar—ASTM A 276 & A 314 Wire—ASTM A 580
Fe —bal Cr —17 C — 1.10
Bar Annealed
Quenched and Tempered 600°F
65
275
110
285
14
2
230
RC57
Type 446 Stainless Steel (UNS S44600) Plate, Sheet & Strip—ASTM A 176 Tube—ASTM A 268 & A 511 Bar—ASTM A 276 & A 314 Forgings—ASTM A 473 Wire—ASTM A 580
Fe —bal Cr —25 N — 0.25 max C — 0.20 max
Sheet Annealed
50
80
20
RB83
E-BRITE* 26-1 Stainless Steel (UNS S44627) Bar—ASTM A 276, A 314 & A 479 Tube—ASTM A 268 Plate, Sheet & Strip—ASTM A 176 & A 240
Fe —bal Cr —26 Mo — 1 Mn — 0.05 Si — 0.2 N — 0.01 C — 0.002
Annealed
50
70
30
RB82
29-4 Stainless Steel (UNS S44700) Tube—ASTM A 268 Plate, Sheet & Strip—ASTM A 176 & A 240 Bar—ASTM A 276 & A 479
Fe —bal Cr —29 Mo — 4 Mn — 0.3 max Si — 0.2 max N — 0.02 max C — 0.01 max
Annealed
75
90
25
RB95
29-4-2 Stainless Steel (UNS S44800) Tube—ASTM A 268 Plate, Sheet & Strip—ASTM A 176 & A 240 Bar—ASTM A 276 & A 479
Fe —bal Cr —29 Mo — 4 Ni — 2 Mn — 0.3 max Si — 0.2 max N — 0.02 max C — 0.01 max
Annealed
85
95
22
RB97
SEA-CURE* Stainless Steel (UNS S44660) Sheet & Strip—ASTM A 240 Tube—ASTM A 268
Fe —bal Cr —26 Mo — 3 Ni — 2.5 C — 0.025 max
Annealed
75
90
32
RB95
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S
CA-15 Cast Stainless Steel (UNS 191150) Gen. Applications—ASTM A 743 Valves, Fittings—ASTM A 217 & A 487
Fe —bal Cr —12 C — 0.15 max
1800°F, Air Cooled, Tempered at 600°F
Tempered at 1400°F
150
75
200
100
7
20
390
200
CA-40 Cast Stainless Steel (UNS 191153) Gen. Applications—ASTM A 743
Fe —bal Cr —12 C — 0.30
1800°F, Air Cooled, Tempered at 600°F
Tempered at 1400°F
165
67
220
110
1
18
470
212
CA-611M Cast Stainless Steel (UNS 191540) Gen. Applications—ASTM A 743 Valves, Fittings—ASTM A 487
Fe —bal Cr —12 Ni — 4 Mo — 0.7 C — 0.06 max
1750°F, Air cooled, Tempered at 1100-
1150°F
100
120
24
269
CB-7Cu-1 (11-4PH) Cast Stainless Steel Castings—ASTM A 747
Fe —bal Cr —17 Ni — 4 Cu — 3 Cb — 0.3 (Optional)C — 0.07 max
1925°F, Air Cooled, Aged at 900°F
Aged at 1100°F
161
132
187
145
10
15
412
315
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
69
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
W R O U G H T S T A I N L E S S S T E E L ( c o n t i n u e d )
0.280
—
7.75
—
2700
—
0.11
—
5.6
—
168 10
—
360
—
29
—
—
—
Type 440C Stainless Steel
0.270
7.45
2750
0.012
5.8
145 10
402
29
—
Type 446 Stainless Steel
0.277
7.66
—
0.100
5.936
136 10
332
—
—
E-BRITE* 26-1 Stainless Steel
0.278
7.69
2750
—
5.2'
—
—
29
—
29-4 Stainless Steel
0.276
7.64
2735
—
5.2'
—
—
—
—
29-4-2 Stainless Steel
—
—
—
—
—
—
—
—
—
SEA-CURE* Stainless Steel
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S
0.275
—
7.61
—
2750
—
0.11
—
5.51 6.421
—
174 10
—
468
—
29
—
—
—
CA-15 Cast Stainless Steel
0.275
—
7.61
—
2725
—
0.11
—
5.51 6.421
—
174 10
—
456
—
29
—
—
—
CA-40 Cast Stainless Steel
0.278
7.70
2750
0.11
6.01 7.021
174 10
469
29
—
CA-6NM Cast Stainless Steel
0.280
—
7.76
—
2750
—
0.1137
—
6.017
6.617
119 10
—
46437
—
28.5
—
—
—
CB-7Cu-1 (17-4 PH) Cast Stainless Steel
1 = 68 to 212°F 10 = at 212°F 17 = 70 to 200°F 21 = 70 to 1000°F 36 = 91 to 223°F 37 = at 70°F
70
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
CB-7Cu-2 (15-5 PH) Cast Stainless Steel Castings—ASTM A 747
Fe —bal Cr —15 Ni — 5 Cu — 3 Cb — 0.3 (Optional) C — 0.07 max
1925°F, Air Cooled, Aged at 900°F
Aged at 1100°F
161
132
187
145
10
15
412
315
CB-30 Cast Stainless Steel (UNS J91803) Gen. Applications—ASTM A 743
Fe —bal Cr —20 Ni — 2 max C — 0.30 max
Annealed
60
95
15
195
CC-50 Cast Stainless Steel (UNS J92615) Gen. Applications—ASTM A 743
Fe —bal Cr —28 Ni — 4 max C — 0.50 max
As Cast
1900°F, Air Cooled
60
65
95
97
15
18
193
210
CE-30 Cast Stainless Steel (UNS J93423) Gen. Applications—ASTM A 743
Fe —bal Cr —28 Ni — 9
As Cast
2000°F, Water Quenched
60
63
95
97
15
18
170
170
CF-3 Cast Stainless Steel (UNS J92500) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351
Fe —bal Cr —19 Ni —10 C — 0.03 max
2000°F, Water Quenched
32
72
55
133
CF-8 Cast Stainless Steel (UNS J92600) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351 Centrifugal Pipe—ASTM A 451
Fe —bal Cr —19 Ni — 9 C — 0.08 max
2000°F, Water Quenched
32
77
55
140
CF-3M Cast Stainless Steel (UNS J92800) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351
Fe —bal Cr —19 Ni —11 Mo — 2.5 C — 0.03 max
2000°F, Water Quenched 40 83 50 —
CF-8M Cast Stainless Steel (UNS J92900) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351 Centrifugal Pipe—ASTM A 451
Fe —bal Cr —19 Ni —10 Mo — 2.5 C — 0.08 max
2000°F, Water Quenched 42 80 50 163
CF-8C Cast Stainless Steel (UNS J92110) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351 Centrifugal Pipe—ASTM A 451
Fe —bal Cr —19 Ni —10 C — 0.08 max Cb — 8xC min or Cb + Ta—10×C min
2000°F, Water Quenched 38 77 39 149
CF-16F Cast Stainless Steel (UNS J92701) Gen. Applications—ASTM A 743
Fe —bal Cr —19 Ni —10 S — 0.3 Mo — 0.6 C — 0.16 max
2000°F, Water Quenched
40
77
52
150
CF-20 Cast Stainless Steel (UNS J92602) Gen. Applications—ASTM A 743
Fe —bal Cr —19 Ni —9 C — 0.20 max
2000°F, Water Quenched
36
77
50
163
PROPERTIES OF SOME METALS AND ALLOYS
71
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
0.280
—
7.76
—
2750
—
0.1137
—
6.017
6.617
119
10
—
464 37
464 37
28.5
—
—
—
CB-7Cu-2 (15-5 PH) Cast Stainless Steel
0.272
1.53
2725
0.11
5.71 6.521
154
10
456
29
—
CB-30 Cast Stainless Steel
0.272
—
7.53
—
2725
—
0.12
—
5.91 6.421
—
151
10
—
462
—
29
—
—
—
CC-50 Cast Stainless Steel
0.277
—
7.67
—
2650
—
0.14
—
9.621
—
—
—
510
—
25
—
—
—
CE-30 Cast Stainless Steel
0.280
7.75
2600
0.12
9.01 10.021
110
10
457
—
—
CF-3 Cast Stainless Steel
0.280
7.75
2600
0.12
9.01 10.021
110
10
457
28
—
CF-8 Cast Stainless Steel
0.280
7.75
2550
0.12
8.91 9.721
113
10
492
—
—
CF-3M Cast Stainless Steel
0.280 7.75 2550 0.12
8.91 9.721
113
10 492 28 —
CF-8M Cast Stainless Steel
0.280 7.75 2600 0.12
9.31 10.321
112
10 426 28 —
CF-8C Cast Stainless Steel
0.280
7.75
2550
0.12
9.01 9.921
113
10
432
28
—
CF-16F Cast Stainless Steel
0.280
7.75
2575
0.12
9.61 10.421
110
10
468
28
—
CF-20 Cast Stainless Steel
1 = 68 to 212°F 10 = at 212°F 17 = 70 to 200°F 21 = 70 to 1000°F 37 = at 70°F
72
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
CG-8M Cast Stainless Steel (UNS 193000) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744
Fe —bal Cr —19 Ni —11 Mo — 3.5 C — 0.08 max
2000°F, Water Quenched 40 83 50 —
CH-20 Cast Stainless Steel (UNS J93402) Gen. Applications—ASTM A 743 Valves, Fittings—ASTM A 351 Centrifugal Pipe—ASTM A 451
Fe —bal Cr —24 Ni —13 C — 0.20 max
2000°F, Water Quenched
50
88
38
190
CK-20 Cast Stainless Steel (UNS J94202) Gen. Applications—ASTM A 743 Valves, Fittings—ASTM A 351 Centrifugal Pipe—ASTM A 451
Fe —bal Cr —25 Ni —20 C — 0.20 max
2100°F, Water Quenched
38
76
37
144
CN-1M Cast Stainless Steel (UNS J95150) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351
Fe —bal Cr —20 Ni —29 Mo — 2 Cu — 3 min C — 0.07 max
2050°F, Water Quenched
31.5
69
48
130
CD-4MCu Cast Stainless Steel Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, Fittings—ASTM A 351
Fe —bal Cr —26 Ni — 5.5 Mo — 2.5 Cu — 3.0
2050°F, Water Quenched 80 110 20 240
CW-12M-1 Cast Stainless Steel Gen. Applications—ASTM A 743 Severe Service—ASTM A 744
Ni —bal Cr —16.5 Mo —17 Fe — 6 V — 0.3 Mn — 1.0 max Si — 1.0 max C — 0.12 max
2150°F min, Water Quenched
46
min
72
min
4
min
—
CW-12M-2 Cast Stainless Steel General Applications—ASTM A 743 Severe Service—ASTM A 744
Ni —bal Cr —18.5 Mo —18.5 Fe — 3 max V — 0.3 Mn — 1.0 max Si — 1.0 max C — 0.07 max
2150°F min, Water Quenched
46 min
72 min
25 min
—
N-12M-1 Cast Stainless Steel Gen. Applications—ASTM A 743 Severe Service—ASTM A 744
Ni —bal Cr — 1.0 max Mo —28 Fe — 5 V — 0.3 Mn — 1.0 max Si — 1.0 max C — 0.12 max
As Agreed
46 min
76 min
6 min
—
N-12M-2 Cast Stainless Steel Gen. Applications—ASTM A 743 Severe Service—ASTM A 744
Ni —bal Cr — 1.0 max Mo —31.5 Fe — 3 max Mn — 1.0 max Si — 1.0 max C — 0.07 max
As Agreed
46 min
76 min
20 min
—
PROPERTIES OF SOME METALS AND ALLOYS
73
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
0.280 7.75 2550 0.12
8.91 9.721
113
10 492 — —
CG-8M Cast Stainless Steel
0.279
7.72
2600
0.12
8.31 9.621
98
10
504
28
—
CH-20 Cast Stainless Steel
0.280
7.75
2600
0.12
8.01 9.221
98
10
540
29
—
CK-20 Cast Stainless Steel
0.289
8.00
2650
0.11
8.61 9.721
145
10
538
24
—
CN-7M Cast Stainless Steel
— — — —
6.51 7.121
— — — —
CD-4MCu Cast Stainless Steel
0.336 9.30 (Calculated)
—
—
—
—
—
—
—
CW-12M-1 Cast Stainless Steel
— — — — — — — — —
CW-12M-2 Cast Stainless Steel
0.334 9.24 (Calculated)
—
—
—
—
—
—
—
N-12M-1 Cast StainlessSteel
—
—
—
—
—
—
—
—
—
N-12M-2 Cast StainlessSteel
1 = 68 to 212°F 10 = at 212°F 21 = 70 to 1000°F
74
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
ALOYCO* 20 Cast Stainless Steel (UNS J95150) Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves Fittings—ASTM A 351
Fe —bal Cr —20.5 Ni —28.8 Mo — 2.5 Cu — 3.5 Mn — 1.5 max Si — 1.5 max C — 0.07 max
Castings Annealed (2150°F, Water Quenched)
32
69
48
130
DURIMET* 20 Cast Stainless Steel (UNS J95150)Gen. Applications—ASTM A 743 Severe Service—ASTM A 744 Valves, fittings—ASTM A 351
Fe —bal Cr —20.5 Ni —29 Cu — 3.5 Mo — 2.5 Mn — 1.5 max Si — 1.5 max C — 0.07 max
2050°F, Water Quenched
25 min
62 min
35 min
130
ILLIUM* P Cast Stainless Steel
Fe —bal Cr —28 Ni — 8 Cu — 3 Mo — 2 Mn — 0.75 Si — 0.75 C — 0.20
Castings 1975°F, Water Quenched
72
100
18
235
IN-849 Cast Stainless Steel
Fe —bal Cr —26 Ni — 6.8 Mn — 0.7 Si — 1.0 C — 0.03
Castings, 2050°F, Water Quenched
67
84
26
228
SANDUSKY* Alloy 75
Fe —bal Cr —26 Ni — 6.8 Mn — 0.8 Si — 0.7 C — 0.03
Casting, Proprietary Heat Treatment
62
113
20
235
IN-862 Cast Stainless Steel
Fe —bal Cr —21 Ni —24 Mo — 5 Mn — 0.5 Si — 0.8 C — 0.07 max
2150°F, Water Quenched 25 60 20 —
HA Cast Heat Resistant Alloy Valves, Fittings—ASTM A 217 Grade C12
Fe —bal Cr — 9 Mo — 1 C — 0.20 max
Annealed 1825°F and
Aged at 1400°F
65
81
95
107
23
21
180
220
HC Cast Heat Resistant Alloy (UNS J92605) Gen. Applications—ASTM A 297
Fe —bal Cr —28 Ni — 4 max C — 0.50 max
As Cast
Aged at 1400°F
65
80
70
115
2
18
190
230
HD Cast Heat Resistant Alloy (UNS J93005) Gen. Applications—ASTM A 297
Fe —bal Cr —28 Ni — 5.5 C — 0.50 max
As Cast
48
85
16
190
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
75
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
0.289
8.02
2650
0.11
8.61
145 3
538
24
—
ALOYCO* 20 Cast Stainless Steel
0.289
8.02
2650
0.113
8.61
145 10
538
24
—
DURIMET* 20 Cast Stainless Steel
0.275
7.61
—
—
—
—
—
—
—
ILLIUM* P Cast Stainless Steel
0.274
7.58
2680
—
7.01
—
—
29
—
IN-849 Cast Stainless Steel
0.274
7.58
2680
—
7.01
—
—
29
—
SANDUSKY* Alloy 75
— — — — — — — — —
IN-862 Cast Stainless Steel
0.279
—
7.72
—
2750
—
0.11
—
6.11
7.121 —
182 10
—
420
—
29
—
—
—
HA Cast Heat Resistant Alloy
0.272
—
7.53
—
2725
—
0.12
—
6.321
—
151
—
462
—
29
—
—
—
HC Cast Heat Resistant Alloy
0.274
7.58
2700
0.12
7.721
151 10
486
27
—
HD Cast Heat Resistant Alloy
1 = 68 to 212°F 3 = at 68°F 10 = at 212°F 21 = 70 to 1000°F
76
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
HE Cast Heat Resistant Alloy (UNS J93403) Gen. Applications—ASTM A 297
Fe —bal Cr —28 Ni — 9 C — 0.35
As Cast
Aged at 1400°F
45
55
95
90
20
10
200
270
HF Cast Heat Resistant Alloy (UNS J92603) Gen. Applications—ASTM A 297
Fe —bal Cr —21 Ni — 9 C — 0.30
As Cast
Aged at 1400°F
45
50
85
100
35
25
165
190
HH Cast Heat Resistant Alloy (UNS J93503) Gen. Applications—ASTM A 297 Structural Parts—ASTM A 447
Fe —bal Cr —26 Ni —12 C — 0.35
As Cast
Aged at 1400°F
50
55
80
86
25
11
185
200
HI Cast Heat Resistant Alloy (UNS J94003) Gen. Applications—ASTM A 297
Fe —bal Cr —28 Ni —16 C — 0.35
As Cast
Aged at 1400°F
45
65
80
90
12
6
180
200
HK Cast Heat Resistant Alloy (UNS J94224) Gen. Applications—ASTM A 297
Fe —bal Cr —26 Ni —20 C — 0.40
As Cast
Aged at 1400°F
50
50
75
85
17
10
170
190
HL Cast Heat Resistant Alloy (UNS J94604) Gen. Applications—ASTM A 297
Fe —bal Cr —30 Ni —20 C — 0.40
As Cast
52
82
19
192
HN Cast Heat Resistant Alloy (UNS J94213) Gen. Applications—ASTM A 297
Fe —bal Cr —21 Ni —25 C — 0.35
As Cast
38
68
17
160
HP Cast Heat Resistant Alloy (UNS J95705) Gen. Applications—ASTM A 297
Fe —bal Cr —26 Ni —35 C — 0.53
As Cast
40
71
11.5
—
HP50-WZ Cast Heat Resistant Alloy
Fe —bal Cr —26 Ni —35 W —5 Zr — 0.6 C — 0.50
As Cast
40
71
11.5
—
HT Cast Heat Resistant Alloy (UNS J94605) Gen. Applications—ASTM A 297
Fe —bal Cr —17 Ni —35 C — 0.55
As Cast
Aged at 1400°F
40
45
70
75
10
5
180
200
HU Cast Heat Resistant Alloy (UNS J95405) Gen. Applications—ASTM A 297
Fe —bal Cr —18 Ni —39 C — 0.55
As Cast
Aged at 1800°F
40
43
70
73
9
5
170
190
IN-657 Cast Heat Resistant Alloy
Ni —bal Cr —50 Cb — 1.5 Fe — 0.5 Mn — 0.2 Si — 0.3 Ni — 0.08 C — 0.10 max
As Cast
54
87
28
—
PROPERTIES OF SOME METALS AND ALLOYS
77
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
0.277
—
7.67
—
2650
—
0.14
—
9.621
—
120
30
—
510
—
25
—
—
—
HE Cast Heat Resistant Alloy
0.280
—
7.75
—
2550
—
0.12
—
8.91
9.921
108
10
—
480
—
28
—
—
—
HF Cast Heat Resistant Alloy
0.279
—
7.72
—
2500
—
0.12
—
9.421
—
98
10
—
480
—
27
—
—
—
HH Cast Heat Resistant Alloy
0.279
—
7.72
—
2550
—
0.12
—
9.921
—
98
10
—
—
—
27
—
—
—
HI Cast Heat Resistant Alloy
0.280
—
7.75
—
2550
—
0.12
—
9.221
—
98
10
—
540
—
29
—
—
—
HK Cast Heat Resistant Alloy
0.279
7.72
2600
0.12
9.221
98
10
564
29
—
HL Cast Heat Resistant Alloy
0.283
7.83
2500
0.11
—
—
—
27
—
HN Cast Heat Resistant Alloy
0.284
7.86
2450
0.11
9.221
90
10
614
27
—
HP Cast Heat Resistant Alloy
0.284
7.87
2450
0.1137
9.221
90
10
612
37
27
—
HP50-WZ Cast Heat Resistant Alloy
0.286
—
7.96
—
2450
—
0.11
—
8.521
—
91
10
—
601
—
27
—
—
—
HT Cast Heat Resistant Alloy
0.290
—
8.03
—
2450
—
0.11
—
8.821
—
107
10
—
631
—
27
—
—
—
HU Cast Heat Resistant Alloy
0.287
7.96
2397
0.1101
5.91
88
35
589
35
30
—
IN-657 Cast Heat Resistant Alloy
1 = 68 to 212°F 10 = at 212°F 21 = 70 to 1000°F 31 = at 1500°F 35 = at 75°F 37 = at 70°F
78
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
HW Cast Heat Resistant Alloy Gen. Applications—ASTM A 297
Fe —bal Cr —12 Ni —60 C — 0.55
As Cast
Aged at 1800°F
36
52
68
84
4
4
185
205
HX Cast Heat Resistant Alloy Gen. Applications—ASTM A 297
Fe —bal Cr —17 Ni —66 C — 0.55
As Cast
Aged at 1800°F
36
44
65
73
9
9
176
185
IN-519 Cast Heat Resistant Alloy
Fe —bal Cr —24 Ni —24 Cb — 1.6 Mn — 1.0 max Si — 1.0 max C — 0.30
As Cast 35 75 25 —
R E F R A C T O R Y M E T A L S A N D A L L O Y S
Columbium (UNS R04210) Rod, Bar, Wire—ASTM B 392 Sheet, Strip, Foil—ASTM B 393 Tube—ASTM B 394
Cb —99.6 min
Sheet Annealed
Cold Rolled (97%)
37
—
53
84
26
5
80
160
Columbium-Tantalum-Tungsten Alloy
Cb —bal Ta —28 W —11 Zr — 0.85
Sheet, Stress Relieved
90
105
14
225
Columbium-Vanadium Alloy
Cb —bal V —5
Recrystallized at 2000°F
56
78
32
RB82
Columbium-Zirconium Alloy (UNS R04261) Sheet, Strip, Foil—ASTM B 393 Rod, Bar, Wire—ASTM B 392 Tube—ASTM B 394
Cb —98.5 min Zr — 1
Annealed
As Rolled
22
60
38
62
25
3
—
—
Molybdenum (UNS R03600) Forgings—ASTM B 384 Sheet, Strip, Foil—ASTM B 386 Bar, Rod, Wire—ASTM B 387
Mo —99.9 plus
As Rolled
Recrystallized
75
50
100
70
30
45
250
190
0.5% Titanium-Molybdenum Alloy (UNS R03620) Forgings—ASTM B 384 Sheet, Strip, fail—ASTM B 386 Bar, Rod, Wire—ASTM A 397
Mo —bal Ti — 0.5
As Rolled
Recrystallized
90
60
120
80
30
40
290
200
Tungsten-Nickel-Copper Alloy (UNS R07030) ASTM B 459 Grade 4
W —97.5 Ni + Cu—2.4
Sintered Powder Shapes 80 100 3 —
Tungsten-Nickel-Copper Alloy (UNS R07100) ASTM B 459 Grade 1
W —bal Ni — 7.5 Cu — 2.5
Forged from Sintered Powder 85 120 17 285
Tantalum (UNS R05400) Rod & Wire—ASTM B 365 Flat Products—ASTM B 364
Ta —99.8 plus Sheet Annealed
Cold Rolled
—
100
50
110
40
3
45
123
Tungsten (UNS R07004) Bars, Rods, Billets—ASTM B 410
W —99.95 min Sheet Hard Cold Rolled
Annealed
360 —
400 270
— —
— —
Tungsten-Rhenium Alloy
W —75 Re —25
Wire Wrought
Recrystallized
—
—
310
190
—
15
—
450d
d = Vickers hardness number
PROPERTIES OF SOME METALS AND ALLOYS
79
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
C A S T C O R R O S I O N A N D H E A T R E S I S T A N T A L L O Y S ( c o n t i n u e d )
0.294
—
8.14
—
2350
—
0.11
—
7.821
—
91
10
—
673
—
25
—
—
—
HW Cast Heat Resistant Alloy
0.294
—
8.14
—
2350
—
0.11
—
7.821
—
—
—
—
—
25
—
—
—
HX Cast Heat Resistant Alloy
0.286 7.92 2490 0.1083 7.21 98
10 582'5 23 —
IN-519 Cast Heat Resistant Alloy
R E F R A C T O R Y M E T A L S A N D A L L O Y S
0.310
—
8.57
—
4475
—
—
—
4.3821
—
306
3
—
105
—
15
—
5.4
—
Columbium
0.390
10.8
4695
—
—
—
—
20
—
Columbium- Tantalum- Tungsten Alloy
0.306
8.47
4310
0.065
4.1530
377
3
131
15.8
—
Columbium-
Vanadium Alloy
0.311
—
8.6
—
4350
—
0.065
—
—
—
364
3
—
—
—
12
—
—
—
Columbium- Zirconium Alloy
0.369
—
10.20
—
4730
—
0.061
—
2.71
—
900
3
—
31.1
—
46
—
17.4
—
Molybdenum
0.369
—
10.22
—
4730
—
0.061
—
3.061
—
816
3
—
31.3
—
46
—
17.4
—
0.5% Titanium- Molybdenum Alloy
0.67 18.5 — — — — — 52 — Tungsten-
Nickel-Copper Alloy
0.61 17.0 — — 3.77 500
8 — 45 — Tungsten-
Nickel-Copper Alloy
0.600
—
16.65
—
5425
—
0.034
—
3.61
—
377
3
—
74.6
—
27
—
10
—
Tantalum
0.697 —
19.30 —
6100 —
0.033 —
2.41
—
— —
33.2 —
50 —
19.6 —
Tungsten
0.71
—
19.65
—
5612
—
—
—
—
—
—
—
168
—
57
—
—
—
Tungsten- Rhenium Alloy
1 = 68 to 212°F 3 = at 68°F 7 = 100 to 1200°F 8 = at 32°F 10 = at 212°F 21 = 70 to 1000°F 30 = 30 at 1500°F 35 = at 75°F
80
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
R E F R A C T O R Y M E T A L S A N D A L L O Y S ( c o n t i n u e d )
Tungsten-Rhenium Alloy
W —50 Re —50
Sintered Powder, Wrought
Recrystallized
210
123
240
150
—
18
600d
350d
Uranium Castings—ASTM B 419 Melting Stock—ASTM B 420
U —99.8 plus Cast 28 56 4 —
Zirconium (UNS R60001) Ingots—ASTM B 350 Sheet, Strip, Plate—ASTM B 352 Bar, Rod, Wire—ASTM B 351 Tube—ASTM B 353
Zr —99.8 plus
Annealed
16
36
31
77
Zirconium-Hafnium Alloy (UNS R60102) Sheet, Strip & Plate—ASTM B 551 Bar & Wire—ASTM B 550 Tube—ASTM B 523
Zr —bal Hf — 3 Cr-Fe— 0.2 max
Annealed
50
64
23
RB89
P R E C I O U S M E T A L S A N D A L L O Y S
Gold (UNS P00010) ASTM B 562
Au —99.995 min Cold Rolled, 60%
Annealed
30
Nil
32
19
4
45
58
25
18K White Gold
Au —75 Ni —18.5 Zn — 5.25 Cu — 1.25
Annealed
Hard
93
—
115
178
25
—
211
323
W.E. No. 1 (UNS P00691) ASTM B 522
Au —69 Ag —25 Pt — 6
Annealed
Hard
16.3
—
39
70
33
—
74
132
Fine Silver (UNS P07020) Cast Bar—ASTM B 413 Grade 99.90
Ag —99.90 min
Annealed
Hard
7.9
38
18.2
43
54
6
27
90
Sterling Silver
Ag —92.5 Cu —bal
Annealed
Hard
20
50
41
64
26
4
65
125
Coin Silver
Ag —90 Cu —bal
Annealed
Hard
23
53
42
65
26
4
70
125
EASY-FLO* Silver Brazing Alloy (UNS P07500) AMS 4769 AWS A 5.8 (B Ag-1)
Ag —50 Cd —18 Zn —16.5 Cu —15.5
Annealed
Cold Rolled
—
—
67
89
29
11
120
160
R-T Silver Brazing Alloy
Ag —60 Cu —25 Zn —15
Annealed
Cold Drawn
45
75
58
89
38
9
110
160
Platinum Pt (Commercial) Annealed — 18 38 39
Palladium Pd (Commercial) Annealed — 25 27 38
Iridium Ir —100 Annealed 34 155 — 220
Rhodium Rh —100 Annealed — 100 — 120
Platinum-Iridium
Pt —90 Ir —10
Annealed
Hard
—
—
55
90
—
—
130
185
*See page 84 for list of trademarks
PROPERTIES OF SOME METALS AND ALLOYS
81
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan-sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
R E F R A C T O R Y M E T A L S A N D A L L O Y S ( c o n t i n u e d )
0.496
—
13.76
—
4622
—
—
—
—
—
257
6
—
116
—
52.3
—
—
—
Tungsten- Rhenium Alloy
0.689 19.07 2070 — 7.7 — — 24 — Uranium
0.245
6.5
3380
0.118
2.9
—
246
11
—
Zirconium
0.237
6.55
—
—
3.2
145
—
—
—
Zirconium Hafnium Alloy
P R E C I O U S M E T A L S A N D A L L O Y S
0.698
—
19.32
—
1945
—
0.0319
—
7.9
1
—
2060
8
—
14.1
—
10.8
—
—
—
Gold
0.53
—
14.61
—
1886
—
—
—
—
—
—
—
210.3
—
16.6
—
—
—
18K White Gold
0.58
—
16.0
—
—
—
—
—
—
—
—
—
95
—
13.0
—
—
—
W.E. No. 1
0.379
—
10.49
—
1761
—
0.056
—
9.4412
—
2900
—
9.6
—
10.5
—
3.9
—
Fine Silver
—
—
—
—
—
—
—
—
10.5
—
2510
—
12.08
—
—
—
—
—
Sterling Silver
—
—
—
—
—
—
—
—
10.5
—
2490
—
12.13
—
—
—
—
—
Coin Silver
0.342
—
9.49
—
1175
—
—
—
—
—
—
—
42
—
—
—
—
—
EASY FLO* Silver Brazing Alloy
0.344
—
9.52
—
1325
—
—
—
—
—
—
—
50
—
13
—
—
—
R-T Silver Brazing Alloy
0.775 21.45 3256 0.0318 4.9
1 485 64 24.8 — Platinum
0.434 12.02 2826 0.0588 6.5
1 494
1 65 16.8 — Palladium
0.813 22.65 4429 0.031 3.78
1 406
1 32 75 — Iridium
0.447 12.41 3560 0.059 4.6
1 610
13 27 46 — Rhodium
0.778
—
21.53
—
3240
—
—
—
—
—
—
—
150
—
—
—
—
—
Platinum- Iridium
1 = 68 to 212°F 6 = Near room temperature 8 = at 32°F 9 = at 64°F 12 = 32 to 1652°F 13 = at 63°F
82
Typical Mechanical Properties
Material
Nominal Composition %
Form and Condition
Yield Strength
(0.2% offset), 1000 psi
Tensile
Strength, 1000 psi
Elongation
in 2 in., %
Hardness, Brinell or Rockwell
P R E C I O U S M E T A L S A N D A L L O Y S ( c o n t i n u e d )
Platinum-Rhodium
Pt —90 Rh —10
Annealed
Cold Worked, 75%
—
—
45
90
35
2
90
165
Platinum-Ruthenium
Pt —90 Ru —10
Annealed
Hard
—
—
83
150
31
2
190
280
Palladium-Ruthenium
Pd —95.5 Ru — 4.5
Annealed
Hard
—
—
51
—
—
—
152
286
Palladium-Silver
Pd —60 Ag —40
Annealed
Hard
—
—
55
100
—
—
180
260
Palladium Alloy No 934
Pd —35 Pt —10 Au —10 Ag —30 Cu —15
Annealed
Heat Treated
61
125
96
146
24
10
180
280
Ruthenium Ru —100 Annealed — 78 — 250 to 450
PROPERTIES OF SOME METALS AND ALLOYS
83
Typical Physical Properties
Density, Ib/cu in.
Specific Gravity
Melting Point, °F
Specific Heat (32 to 212°F),
Btu / Ib / °F
Thermal Expan- sion Coefficient
(32 to 212°F), in 10–6
in. / in. / °F
Thermal Conductivity (32 to 212°F),
Btu / sq ft /hr / °F / in.
Electrical
Resistivity, (68°F) ohms
/cir mil ft
Tensile
Modulus of Elasticity,
in 106 psi
Torsional Modulus
of Elasticity, × 106 psi
Material
P R E C I O U S M E T A L S A N D A L L O Y S ( c o n t i n u e d )
0.722
—
19.97
—
—
—
—
—
—
—
—
—
115
—
—
—
—
—
Platinum- Rhodium
0.720
—
19.94
—
3000
—
—
—
—
—
—
—
258
—
—
—
—
—
Platinum- Ruthenium
0.436
—
12.07
—
2900
—
—
—
—
—
—
—
145
—
20.0
—
—
—
Palladium- Ruthenium
—
—
—
—
2440
—
—
—
—
—
—
—
252
—
—
—
—
—
Palladium Silver
0.430
—
11.9
—
1985
—
—
—
—
—
—
—
215
—
—
—
—
—
Palladium Alloy No. 934
0.450 12.45 4190 — — — 41
8 60 — Ruthenium
8 = at 32°F
84
TRADEMARKED PRODUCTSTrademarks Product of ALCHROME............................................................................................................. AMAX Inc. ALOYCO .................................................................................................................Aloyco,Inc. AL-6X................................................................................. Allegheny Ludlum Industries, Inc. AM 350 .............................................................................. Allegheny Ludlum Industries, Inc. AM 355 .............................................................................. Allegheny Ludlum Industries, Inc. CARPENTER 20Cb-3.........................................................Carpenter Technology Corporation CHLORIMET ..................................................................................The Duriron Company, Inc. CUSTOM 455 ....................................................................Carpenter Technology Corporation DISCALOY.........................................................................Westinghouse Electric Corporation DURANICKEL ....................................................................................Inco family of companies DURICHLOR ..................................................................................The Duriron Company, Inc. DURIMET ......................................................................................The Duriron Company, Inc. DURIRON ......................................................................................The Duriron Company, Inc. EASY-FLOW .............................................................................................. Handy and Harman E-BRITE .............................................................................. Allegheny Ludlum Industries, Inc. ELINVAR......................................................................................................... Metalimphy,Inc. EVANOHM............................................................................................................... AMAX Inc. FERRALIUM .................................................................................... Bonar Langley Alloys Ltd. HASTELLOY ................................................................................................Cabot Corporation HAYNES .....................................................................................................Cabot Corporation ILLIUM ......................................................................... Stainless Foundry & Engineering, Inc. INCOLOY ..........................................................................................Inco family of companies INCONEL ..........................................................................................Inco family of companies INVAR............................................................................................................. Metalimphy,Inc. ISO-ELASTIC ................................................................................. John Chatillon & Sons, Inc. JESSOP .............................................................................................. Jessop Steel Company KANTHAL.......................................................................................... The Kanthal Corporation KARMA............................................................................................... Driver-Harris Company KOVAR .............................................................................Carpenter Technology Corporation MAR-M......................................................................................... Martin Marietta Corporation MONEL .............................................................................................Inco family of companies MULTIMET...................................................................................................Cabot Corporation NIKROTHAL ...................................................................................... The Kanthal Corporation NIMONIC ...........................................................................................Inco family of companies NITRONIC................................................................................................................ Armco Inc. NI-SPAN-C.........................................................................................Inco family of companies NITRALLOY ............................................................................. Joseph T. Ryerson & Son, Inc. PERMANICKEL ..................................................................................Inco family of companies RA 333 .......................................................................................................Rolled Alloys, Inc. RENÉ 41.........................................................................................................Teledyne Allvac RODAR ................................................................................................................... AMAX Inc. SANDUSKY ..............................................................Sandusky Foundry & Machine Company SEA-CURE ........................................................................................................ Colt Industries STAINLESS “W”......................................................................United States Steel Corporation THERLO.............................................................................................. Driver-Harris Company TINEL ................................................................................................... Raychem Corporation UDIMET ........................................................................................ Special Metals Corporation WAUKESHA METAL....................................................................Waukesha Foundry Company YORCORON ..............................................................................IMI Yorkshire Imperial Limited ZILLOY ..................................................................................The New Jersey Zinc Company 15-5 PH ................................................................................................................. Armco Inc. 17-4 PH ................................................................................................................. Armco Inc. 17-7 PH ................................................................................................................. Armco Inc. 18-9 LW................................................................................................................. Armco Inc. PH 15-7 Mo ........................................................................................................... Armco Inc. PH 14-8 Mo ........................................................................................................... Armco Inc. PH 13-8 Mo ........................................................................................................... Armco Inc. 200 Alloy.......................................................................................... Driver-Harris Company 317LM ...............................................................................Eastern Stainless Steel Company
85
SOURCES OF ADDITIONAL INFORMATION (Properties and Specifications)
“Alloy Digest,” Engineering Alloys Digest, Inc. P.O. Box 823, Upper Montclair, NJ 07043
American Institute of Mining, Metallurgical and Petroleum Engineers
345 East 47th Street, New York, NY 10017 American Iron and Steel Institute
1000 Sixteenth Street, N.W., Washington, DC 20036 American National Standards Institute
1430 Broadway, New York, NY 10018 American Powder Metallurgy Institute
P.O. Box 2054, Princeton, NJ 08540 American Society of Mechanical Engineers
345 East 47th Street, New York, NY 10017 American Society for Metals
Metals Park, OH 44073 American Society for Testing and Materials
1916 Race Street, Philadelphia, PA 19103 American Welding Society
2501 N.W. 7th Street, Miami, FL 33125 Brass and Bronze Ingot Institute
33 North LaSalle Street, Room 3500, Chicago, IL 60602 Cast Bronze Bearing Institute
221 North LaSalle Street, Suite 2026, Chicago, IL 60601 Copper Development Association
405 Lexington Avenue, New York, NY 10017 Ductile Iron Society
615 Sherwood Parkway, Mountainside, NJ 07092 Gray and Ductile Iron Founders’ Society
20611 Center Ridge Road, Rocky River, OH 44116 Investment Casting Institute
8521 Clover Meadow, Dallas, TX 75243 Metal Powder Industries Federation
P.O. Box 2054, Princeton, NJ 08540 National Association of Corrosion Engineers
2400 West Loop South, Houston, TX 77027 Society of Automotive Engineers
400 Commonwealth Drive, Warrendale, PA 15096 Steel Founders’ Society of America
455 State Street, Des Plaines, IL 60016 “Unified Numbering System for Metals and Alloys,” 2nd ed., American Society for Testing and Materials
1916 Race Street, Philadelphia, PA 19103 United States Government Specifications
Superintendent of Documents, U.S. Government Printing Office Washington, DC 20402 Department of the Air Force, Air Research & Development Command Wright Air Development Center, Wright-Patterson Air Force Base, OH 45433
“Woldman’s Engineering Alloys,” 6th ad., American Society for Metals
Metals Park, OH 44073