PREPARATION AND CHARACTERIZATION OF PZT/PVDF COMPOSITES
FILMS FABRICATED BY ELECTROSPINNING METHOD
Do Phuong Anh1,*, Do Viet On1, Dao Anh Quang2, Nguyen Van Thinh3, Nguyen Thi Anh Tuyet4,
Vo Thanh Tung1 and Truong Van Chuong1
1University of Sciences, Hue University, Vietnam2Institute of Reasearch and Development, Duy Tan University, Danang, Vietnam3University of Technology and Education, University of Danang, Vietnam4Faculty of Natural Sciences, Quy Nhon University, Binhdinh, Vietnam
E-mail: [email protected]; [email protected]
Abstract
In this paper, we present some properties of Lead Zirconate Titanate/Poly(Vinylidene Fluoride)
(PZT/PVDF) composites. The obtained results indicate that 0.9÷1.8 µm PZT/PVDF fibers involved
films were achieved using electrospinning method. In other hand, the effect of grain size, content and
other factors under the purview of Young’s modulus and ferroelectric properties.
Keywords: PVDF, PZT, composites, electrospinning, ferroelectric, piezoelectric, nanofiber.
1. Introduction
The use of ceramic nanoparticles in various organic polymers may provide performance and
multifunctional materials with applications in many technological fields such as actuators, sensors,
solar cells, optoelectronic devices, etc.
Polyvinylidene fluoride (PVDF) is a fluorinated polymer with excellent mechanical and electric
properties, which it was chosen as matrix due to their applications in a wide range of industrial fields.
Research in the field of material science and engineering has been devoted to the development of
innovative materials known as ceramic-polymer composites [2, 3, 8, 9, 13, 15, 16, 19-23, 25, 38]
Poly(vinylidene fluoride) (PVDF) is one of the semicrystalline polymers with at least five
crystalline phases, its can form a different crystal depending on the condition of the crystallization.
The different crystal structures are nonpolar α-phase, polar β -, γ -, δ- phase and ε – phase [4, 9, 12,
14-16, 18, 21, 25, 27-30, 35, 37, 39 ]. The β - phase crystal has all trans conformation that results in
the most polar phase among other crystals, being used extensively in piezoelectric, pyroelectric and
ferroelectric applications, because its piezoelectric activity is based on the dipole orientation within
the crystalline phase.
A variety of experimental techniques have been developed to induce β-phase formation in PVDF.
For example, Matsushige and Takemura showed that crystallization from the melt at pressures which
exceed 350 MPa led to the formation of the β-form of PVDF. Uniaxial or biaxial drawing of PVDF
mailto:[email protected]
films has also been shown to induce an α-β transition. In addition, a number of reports also indicate
that nanoclays, carbon nanotubes, graphene oxides and metal oxides can induce the β-crystal
formation in PVDF nanocomposites prepared via melt processing or solution processing. Besides,
electrospinning also produces pre-dominantly the β-phase.
Ceramic-polymer composites are studied regarding possible preparation procedures, their
ferroelectric properties and their tensile behavior. Furthermore, different arrangements of functional
ingredients are investigated such as 1-3, 2-2 and 0-3 composites [1-6, 11, 18-21, 26, 29, 31- 34, 38,
40].
Especially composites with ceramic fillers randomly dispersed in a polymer matrix are broadly
studied because of good preparation opportunities in order to vary the filler content, the filler and the
matrix materials. Such composites are called 0-3 composites according to Newnham’s connectivity
notation. Then, the PZT ceramic particles with excellent piezoelectric properties were evenly
dispersed in a three-dimensional connected flexible polymer matrix. This type of composite has
excellent comprehensive properties
The influence of preparation processes on the structure and electrical properties of piezoelectric lead
zirconate titanate/poly(vinylidene fluoride) composites was investigated. Electrospinning method can
enhance obviously the ferroelectric, dielectric and piezoelectric properties of PZT/PVDF composites
by reducing the void in piezoelectric composites and decreasing the interface defect between ceramic
phase and polymer phase [4, 5, 8, 10, 36, 40].
2. Experimental section
2.1 Materials
The PVDF used was Aldrich chemistry (France), average Mw~534,000. The solvents used were N,N-
dimethylformamide (DMF, Merck 99.5%) and acetone (Merck, 99.7%). The PZT ceramic (d33 = 317
pC/N, ɛr = 1800), which was prepared via the conventional solid-state reaction method, PZT powers
are prepared with a mortar and pestle, the mean particle size of the PZT powders is about 200 – 500
nm (Figure 1).
Figure 1. SEM images of particle size of the PZT before and after grinding
2.2 Devices
The crystalline structure analysis was performed at room temperature using an X-ray diffraction
system (XRD, Bruker D8 Advance, Germany) with Cu Kα radiation (λ= 0.154 nm) and Fourier
transform infrared (FTIR, Prestige 21 Shimadzu, Japan, Department of Chemical, Hue University of
Education) spectroscopy, respectively. The surface morphology was examined using a scanning
electron microscopy (SEM, Nova NanoSEM 450-FEI) operated at an accelerating voltage of 10–20
kV), the Raman spectra was recorded by a Micro Raman Spectrophotometer (JASCO Raman NRS-
3000) using 633 nm excited laser at room temperature. The polarization-electric field (P−E) hysteresis
loops were measured with a HIOKI 3532 (Radiant Technologies) which testing unit connected with
a high-voltage interface. The electrospinning apparatus was assembled by Hue University of Science
(Vietnam); it consisted of a high-voltage power supply, an automated syringe pump (KDS101, KD
Scientific, USA) with speed from 1mL/h to 999 mL/h and a 10-mL syringe with a 25-gauge diameter
of needle (~0.5 mm); The high electric potential (EG = 0 ÷ 30 kV) and the stretching force (FG) applied
during electrospinning, a steel rotating (E-HUSC-01, Hue University of Science, Vietnam) with 1500
rpm mandrel was used as the collector
2.3. Process
Preparation of the PVDF sol solution: The PVDF precursor solutions 16 wt% were prepared by
dissolving the PVDF powder in 3:1 DMF/acetone solution. The solution was heated at 65oC in silicon
oil bath for 30 min to completely dissolve the polymer.
Table 1. Samples of PZT/PVDF
Samples Composite
compound ratio
ρ (g/cm3)
No. Name of
products
F16 PVDF 16 wt% + 0wt% PZT 1.7
F-P5 PVDF 16 wt% + 5wt% PZT 1.8
F-P10 PVDF 16 wt% + 10wt% PZT 2.1
F-P15 PVDF 16 wt% + 15wt% PZT 2.4
F-P20 PVDF 16 wt% + 20wt% PZT 2.8
F-P25 PVDF 16 wt% + 25wt% PZT 3.1
Fabrication of the PZT/PVDF composite films by electrospinning: The PZT, which was added to
the PVDF solutions at concentration of 5, 10, 15, 20, and 25wt%, respectively (Table 1).
Solubilization was carried out at 65℃ under ultrasound for 1 hour.
The solution flow rate was precisely maintained at 1.5 mL/h using the syringe pump. A 12-cm
distance and an applied voltage of 14 kV were maintained between the needle and the collector [19].
The PZT/PVDF thin films were deposited by spin coating the solution after 4 h on the silver
substrates at room temperature. The wet films were annealed at 135 °C for different durations in an
oven.
Besides on, these composite films was found that the number of particles increases with the
increase in the PZT volume fraction. There is a non-uniformity observed in particle size of the
samples due to the presence of different particle sizes of PZT. The SEM micrographs also reveals
that there is an increase in the reinforcement of PZT particles in the PVDF matrix which indicates
that there is a change in volume fraction, Fig 2 [18].
3. Results and discussion
3.1 Crystalline phase analysis
3.1.1 Surface morphology
Figure 2a show the SEM micrographs of bare PVDF and PVDF with different wt% PZT. Smooth and
bead-free solid fibres were obtained for all the samples. In order to estimate fibre size, the
nanostructural photos of the composites were analyzed using Lince software. The fibre size located
between 0.45 µm and 1.8 µm and gathered round the top of Gauss fitting plot.
The electrospinning parameters can be adjusted to control final PVDF fiber characteristics. One of
the important parameters to consider is molecular weight of PZT. Figure 2 (a-m) shows the SEM
micrographs and fiber diameter distribution of the various PVDF fibers at different PZT contents.
During this sintering process, PZT/PVDF nanofibers become less flexible. At a higher voltage, the
jet draws away more solution, which requires a higher flow rate to create a stable Taylor cone. Too
low of a flow rate creates a break in the jet as more solution collects on the tip causes excess solution
to fall to the ground.
Figure 2. SEM images and grain size distribution for PZT/PVDF composites with different PZT:
(a-b) 0 wt%, (c-d) 5 wt%, (e-f) 10 wt%, (g-h) 15 wt%, (i-k) 20 wt%, (l-m) 25 wt%.
Figure 2 shows, these structures were morphologically analyzed by scanning electron microscopy
(SEM) with 900÷1800 nm diameter of PZT/PVDF, these process were achieved by maximum PZT
the concentration (sign: F-P25), the spraying technique is not possible with higher PZT concentrations
of 25wt% .
The effect of the PZT content on the morphology and average diameters of the PZT/PVDF
nanofibers is shown in Fig. 2. To further understand the impact of PZT on PVDF, it had an average
diameter of 450 nm (see in Figure 5(a-b)). However, an increase in the PZT content resulted in the
formation of the gradual diameter of nanofibers increases. The diameter of nanofibers was
significantly larger than mean difficult in spray coating on thin film [11, 22]. The PZT doping will
significantly benefits the β-phase crystallization of PVDF composites and remnant polarization,
however, if the PZT-doping concentration is too high, will damage the film quality, increase the
thickness of film spin-coating, make the PZT/PVDF film break up [2]. A complete film can be
achieved with 25 wt% PZT contents. On other hand, PZT can effectively improve the piezoelectric
properties of PVDF.
3.1.2 FTIR, XRAY and RAMAN, Crystalline structure
Figure 3a shows the FTIR spectra of aligned electrospun PVDF fibers with different PZT contents
(0–25 wt%); here the enhancement of β phase (infrared band at 478, 510, 840, 1072, 1274, and 1404
cm-1) with increasing PZT content can be observed [6].
The FTIR spectrums of the nanofilms (Figure 3a), the absorption peaks at 1274, 1072 and 840 cm-
1 are typical vibration characteristics of crystalline β phase. It is notable that doping PZT into PVDF
has a distinctive effect of both enhancing the crystalline β phase and weakening the crystalline α
phase. This effect is closely related to the concentration of PZT. For the spectrum of higher PZT
concentrations doped PVDF, the crystalline β phase absorption bands at 1274, 1072 and 840 cm-1
improve compared with lower concentrations [1, 6, 9-14, 20, 22, 24-31, 37, 40].
In order to confirm the crystalline phase of the samples and the influence of PZT ceramic particles
in the polymer matrix an X-ray diffraction analysis was carried out in the range 10° to 70° as shown
in Fig. 3b. The PZT powder sample exhibits characteristic peaks observed at 2θ = 21.3°, 31.1°, 38.4°,
44.5°, 50.2°, 55.3°, and 64.7° corresponding to the planes with Miller indices of (001), (110), (111),
(200), (201), (211), (022). For PVDF films, the shoulder peak at the 2θ value of about 17.2° corresponds
to (020) and (110) planes of crystalline α phase and peak at 20.4° indicates the PVDF β-phase [1, 5,
6, 7, 11, 12, 16, 17, 20-31, 40].
Figure 3. FTIR spectra and XRD curves of the PZT/PVDF composite film with different wt% PZT
By comparing the PZT powder with of the PZT-PVDF composites, it is found that there is no
additional evidence of structural change, XRD analysis is in good agreement with FTIR analysis.
Figure 4. Raman spectrum of PVDF 16%wt with different contant of PZT
We prepared the 0-3 composites of pure PVDF and doped them with PZT the concentration (5-25
wt%). The PZT content was done to increase the conductivity of the matrix as this increased
conductivity will enhance the poling of ceramic at a later stage.
Figure 4 shows that the Raman spectra of the PZT-PVDF film are completely dominated by the
PZT material. The peaks with wave numbers of 130, 185, 374, 545 and 573 cm-1 were assigned to the
tetragonal PZT phase. These peaks are identified as A1(1TO), E(2TO), A1(2TO), E(3TO), and
A1(3TO) modes, respectively [6, 7, 12, 25, 26, 30, 40]. It has also been shown that when the PZT
increases several times, it is shown that the peak intensities are from 600 cm-1 to 1000 cm-1, most of
the PZT crystals have been trapped in the PVDF matrix during crystallization. This is clearly seen
through the SEM image of the composite.
Figure 5. Tensile stress-strain properties of PZT/PVDF nanofiber composite films prepared with
different levels of PZT content. The inset shows the results of Young’s modulus for PZT/PVDF
nanofiber composite films.
Figure 5 shows the typical stress/strain curves of all samples. The Young’s moduli of the
PZT/PVDF composite nanofibres were much higher than that of the bare PVDF nanofibre, especially
for the 15 wt% samples. A slight decline in mechanical properties for the 25 wt% sample may have
been due to its low crystallinity, as confirmed by the XRD and Raman spectrum results.
PZT doping will significantly benefits the β-phase crystallization of PVDF nanocomposites and
remnant polarization, however, if the PZT-doping concentration is too high, will damage the film
quality, increase the thickness of film spin-coating, make the film less transparent, warp the substrate,
and in the worst case, make the PZT/PVDF film peel off. This may have been due to the addition of
PZT hindering the movement of the PVDF molecular chain, which reduced the elasticity and the
elongation of the composite [9, 12, 17, 24, 39].
PZT can effectively improve the piezoelectric properties of PVDF, although excessive PZT doping
will limit the flexibility of composite film as it sustains less elongation just before failure. However,
it had been found that high doping concentrations will increased remnant polarization because there
will be a significant increase in the dielectric constant and thus the piezoelectric signal will increase
[12, 23].
3.2 Ferroelectric properties of the PZT/PVDF films
A series of P–E hysteresis loops for PZT/PVDF composite measured at room temperature were
shown in Fig. 6. The results showed that the composites with PZT volume fraction 5 to 25 wt%
exhibited non-saturated P–E hysteresis loop.
Figure 6. The P−E hysteresis loops for F16(a) and F16-x%PZT films with different concentrations
of PZT, x= 5 (b), 10 (c), 15 (d), 20 (e), 25 (f) wt%
It is also be noted that when increasing the PZT content to beyond, values of remnant polarization
increases and coercive field decreases to a finite value as shown in table 2. The results thus suggested
that distribution of PZT granules in PVDF matrix played a significant role in controlling of
ferroelectric behavior. The ferroelectric properties of the PZT/PVDF films with different
concentrations of PZT between 5 and 25 wt% were investigated.
Table 2. Ferroelectric properties of the PZT/GO/PVDF films
Samples Composite
compound
ratio
Remnant
Polariation
(Pr) µC/cm2
Coercive
field
(EC) kV/cmNo. Name of
products
F16 0 2.1 9.3
F-P5 5 4.3 7.2
F-P10 10 4.8 6.1
F-P15 15 5.3 6.1
F-P20 20 5.9 5.7
F-P25 25 6.2 4.8
The gradual increase of Pr is caused by the crystallinity enhancement of polar β-phase with
increasing of doped PZT and annealed techniques. The correlation between the amorphous phase
contents and ferroelectric properties of PZT thin films was further discussed from the viewpoint of
local chemical structures, Fig.6 [7, 17-21, 34, 35, 40].
A remnant polarization increasing from 2,1 to 6.2 mC/m2 were achieved by optimizing the concentration of 25 wt% of PZT, while simultaneously reducing the coercive field at the same time.
The modification of the physical properties can be explained by alterations in PVDF fiber due to
drawing and poling and to the presence of PZT (Table 2), [10, 36].
4. Conclusion
In this study, PZT-PVDF composites with 0–3 connectivity was successfully fabricated from a
series of PZT volume fractions from 5 to 25 by electrospinning method. With the increase of the PZT
content, an enhancement of the β phase was observed. The PZT-PVDF composites open new
opportunities to develop a large scale manufacturing of flexible devices, piezoelectric devices,
sensors, force transducer, and so on with technological applications.
Experimental density values of the composites were found to be harmonized with calculated
density values. SEM observations revealed a homogeneous mixture of PZT-PVDF phases. The values
of stress - strain coefficient and ferroelectric character obtained in this work revealed that it may be
more suitable for widely future applications.
Acknowledgements
This work was carried out in the framework of the National Project in Physics Program until 2020
under No. ÐTÐLCN.10/18.
References
[1] Zak, A. K., Gan, W. C., Majid, W. H. A., Darroudi, M., & Velayutham, T. S. (2011). Experimental and
theoretical dielectric studies of PVDF/PZT nanocomposite thin films, Ceramics International, 37(5),
1653–1660, doi:10.1016/j.ceramint.2011.01.037
[2] K. Arlt and M. Wegener (2010). Piezoelectric PZT/PVDF-copolymer 0-3 Composites: Aspects
on Film Preparation and Electrical Poling, IEEE Transactions on Dielectrics and Electrical
Insulation, vol. 17, no. 4.
[3] Y. Zhang, Y. Zhang, X. C. Cui, B. He, Y. Nie, P. D. and Z. L. Wang, (2014). PVDF–PZT
nanocomposite film based self-charging power cell, IOP Publishing Ltd, Nanotechnology, 105401
(7pp)
[4] S. F. Mendes, C.M. Costa, V. Sencadas, J. S. Nunes, P. Costa, R. Gregorio Jr, S. L. Méndez
(2009). Effect of the ceramic grain size and concentration on the dynamical mechanical and
dielectric behavior of poly(vinilidene fluoride)/Pb(Zr0.53Ti0.47)O3 composites, Appl Phys A, 96:
899–908, doi 10.1007/s00339-009-5141-2
[5] Greeshma T., Balaji R., & Jayakumar S (2013). PVDF Phase Formation and Its Influence on
Electrical and Structural Properties of PZT-PVDF Composites. Ferroelectrics Letters Section,
40(1-3), 41–55. doi:10.1080/07315171.2013.814460
[6] Singh P., Borkar H., Singh B. P., Singh V. N., & Kumar A (2015). Electro-mechanical properties
of free standing micro- and nano-scale polymer-ceramic composites for energy density capacitors.
Journal of Alloys and Compounds, 648, 698–705. doi:10.1016/j.jallcom.2015.06.272
[7] Hu X.-P., Duan D.-W., Zhang K., Zhang Y.-C., Chu S.-Q., Zhang J., … Cao J.-L
(2013). Influences of the Amorphous Phase on Local Structures and Properties of Ferroelectric
Thin Films. Ferroelectrics, 453(1), 149–155, doi: 10.1080/00150193.2013.842443
[8] D. Guo, G. Xie and J. Luo (2014). Mechanical properties of nanoparticles: basics and applications,
J. Phys. D: Appl. Phys. 47 013001 (25pp)
[9] C.M. Costa, S. Firmino Mendes, V. Sencadas, A. Ferreira, R. Gregorio Jr, J.L. Gómez Ribelles,
S. Lanceros-Méndez (2010). Influence of processing parameters on the polymer phase,
microstructure and macroscopic properties of poly(vinilidene fluoride)/Pb(Zr0.53Ti0.47)O3
composites, Journal of Non-Crystalline Solids, 356 (2010) 2127–2133
[10] Jaitanong N, et al (2014). Piezoelectric properties of cement based/PVDF/PZT composites,
Materials Letters, doi:10.1016/j.matlet.2014.05.040i
[11] B. Luo, X. Wang, Y. Wang and L. Li (2014). Fabrication, characterization, properties and
theoretical analysis of ceramic/PVDF composite flexible films with high dielectric constant and
low dielectric loss, J. Mater. Chem. A, 2, 510–519.
[12] P. Singh, H. Borkar, B. P. Singh, V. N. Singh, and A. Kumar (2014). Ferroelectric polymer-
ceramic composite thick films for energy storage applications, AIP ADVANCES 4, 087117.
[13] R. Li, L. Zhang, Z. Shi and J. Pei (2016). Effects of Coupling Agents on the Structure and
Electrical Properties of PZT-Poly (Vinylidene Fluoride) Composites, Appl. Sci. 2016, 6, 282.
[14] X. Cai, T. Lei, D. Sun and L. Lin (2017). A critical analysis of the α, β and γ phases in
poly(vinylidene fluoride) using FTIR, RSC Adv., 2017, 7, 15382.
[15] Ch. Wan and Ch. R. Bowen (2017). Multiscale-structuring of polyvinylidene fluoride for energy
harvesting: the impact of molecular-, micro- and macro-structure, J. Mater. Chem. A, 2017, 5,
3091.
[16] V. Tiwari & G. Srivastava (2014). Effect of thermal processing conditions on the structure and
dielectric properties of PVDF films, Polym Res 21:587, doi 10.1007/s10965-014-0587-0
[17] J. S. Yun1, C. K. Park, Y. H. Jeong, J. H. Cho, J. H Paik, S. H. Yoon and K. R. Hwang (2016).
The Fabrication and Characterization of Piezoelectric PZT/PVDF Electrospun Nanofiber
Composites, Nanomater Nanotechnol, 6:20, doi: 10.5772/62433
[18] P. Gowdhaman, V. Annamalai & O.P. Thakur (2016). Piezo, ferro and dielectric properties of
ceramic-polymer composites of 0-3 connectivity, Ferroelectrics, 493:1, 120-129, doi:
10.1080/00150193.2016.1134028
[19] C. Chen, P. Hu, J. Yang, Z. Liu, (2016). Synthesis of PVDF/SBT composite thin films by spin
coating technology and their ferroelectric properties, Materials Science-Poland, 34(3), 2016, pp.
650-654
[20] J. Chang, Y. Shen, X. Chu, X. Zhang, Y. Song, Y. Lin, C. Nan and L. Li, (2015). Large d33 and
Enhanced Ferroelectric/ Dielectric Properties of Poly(vinylidene fluoride)-based Composites
Filled with Pb(Zr0.52Ti0.48)O3 Nanofibers, RSC Advances, page 1 of 6, issue 63, 2015.
[21] A. Jain, P. K. J., A. Kr. Sharma, A. Jain, Rashmi P.N (2015). Dielectric and Piezoelectric
Properties of PVDF/PZT Composites: A Review, Polymer Engineering and Science, doi:
10.1002/pen.24088.
[22] A. Matei, V. Ţucureanu, P. Vlăzan, I. Cernica, M. Popescu, and C. Romaniţan (2017). Study of
piezoelectric filler on the properties of PZT-PVDF composites, AIP Conference Proceedings
1916, 030006, doi: 10.1063/1.5017439
[23] J. Pei, Z. Zhao, X. Li, H. Liu, and R. Li (2017). Effect of preparation techniques on structural
and electrical properties of PZT/PVDF composites, Mater. Express, vol. 7, no. 3.
[24] R. Li, J. Zhou, H. Liu and J. Pei (2017). Effect of Polymer Matrix on the Structure and Electric
Properties of Piezoelectric Lead Zirconatetitanate/Polymer Composites, Materials Article, 10,
945; doi:10.3390/ma10080945.
http://dx.doi.org/10.1016/j.matlet.2014.05.040ihttps://doi.org/10.1063/1.5017439
[25] Rajamanickam, N., Jayakumar, K., & Ramachandran, K. (2017). Structural, morphological and
Raman studies on hybridized PVDF/BaTiO3 nanocomposites, AIP Conference Proceedings,
doi:10.1063/1.4980462
[26] Pradhan, S. K., Kumar, A., Sinha, A. N., Kour, P., Pandey, R., Kumar, P., & Kar, M.
(2017). Study of ferroelectric properties on PVDF-PZT nanocomposite. Ferroelectrics, 516(1),
18–27, doi:10.1080/00150193.2017.1362243
[27] R. Naika and S. Rao (2019). Preparation and Characterization of flexible PVDF based polymer
film for energy harvesting applications, ICMPC-2019, Materials Today: Proceedings, 18 (2019)
5107–5113
[28] M. Selvaraj, R. Senthilkumar, S. Selvasekarapandian, R. Balaji, and T. G. Manivasagam (2019).
Influence of graphene oxide and reduced graphene oxide on dielectric properties of PZT/PVDF
composite films, AIP Conference Proceedings 2162, 020056; doi:10.1063/1.5130266
[29] S. Revathi, L. John Kennedy, S. K. Khadheer Basha, and R. Padmanabhan (2018). Synthesis,
Structural, Optical and Dielectric Properties of Nanostructured 0–3 PZT/PVDF Composite Films,
Journal of Nanoscience and Nanotechnology, vol. 18, 4953–4962, 2018.
[30] M. G. Garnica-Romo, A. Páez-Sánchez, L. García-González, I. Domínguez-López, L. L. Díaz-
Flores & M. Villicaña- Mendez, (2015). Nanoparticles of lead zirconate titanate (PZT) used as
ferroelectric ceramics produced by sol–gel acetic-acid route, J Sol-Gel Sci Technol, 74:425–431,
doi:10.1007/s10971-015-3617-4
[31] S. K. Pradhan, Amit Kumar, P. Kour, Rabichandra Pandey, Pawan Kumar, Manoranjan Kar, A.
N. Sinha, (2018). Tuning of dielectric and impedance properties of PVDF by incorporation of Mg
doped PZT, Journal of Materials Science: Materials in Electronics, doi:10.1007/s10854-018-
9779-4.
[32] R. L. B. de Freitas , W. K. Sakamoto, L. P. S. Freitas, F. Castro, A. P. L. Filho, C. Kitano, and
A. A. de Carvalho, (2018). Characterization of PZT/PVDF Composite Film as Functional
Material, Ieee Sensors Journal, Vol. 18, No. 12.
[33] Yang H., Pei J., Cui S., Guo Q., & Li R. (2018). Performance analysis of fiber reinforced
piezoelectric lead zirconate titanate/poly(vinylidene fluoride) composites. Materials Express, 8(6),
511–520, doi:10.1166/mex.2018.1459
[34] J. Tang, J. Liu And H. Huang (2019). Dielectric, Piezoelectric and Ferroelectric Properties of
Flexible 0–3 Type PZT/PVDF Composites Doped with Graphene, Journal of Materials Science:
Materials in Electronics, doi:10.1007/s10854-018-9779-4
[35] J. D. Bobić, G. F. Teixeira, R. Grigalaitis, S. Gyergyek, …, B. D. Stojanovic (2019). PZT–
NZF/CF ferrite flexible thick films: Structural, dielectric, ferroelectric, and magnetic
characterization, Journal of Advanced Ceramics, 8(4): 545–554, doi:10.1007/s40145-019-0337-1
[36] Liu T., Pei J., Xu J., Guo Q., & Li R. (2019). Analysis of PZT/PVDF composites performance
reinforced by aramid fibers. Materials Research Express, 6(6), 066303, doi:10.1088/2053-
1591/ab0869.
https://doi.org/10.1063/1.5130266
[37] E. Brunengo, M. Castellano, L. Conzatti, G. Canu, V. Buscaglia, P. Stagnaro (2020). PVDF-
based composites containing PZT particles: How processing affects the final properties, J. Appl.
Polym. Sci., doi: 10.1002/APP.48871
[38] W. Zhou , J. Fan , Z. Xin and G. You, (2020). Micro-Structure Modelling and Electrical
Properties Analysis of PZT Matrix Ferroelectric Composites, Materials, 13, 448;
doi:10.3390/ma13020448
[39] F. Kong, M. Chang and Z. Wang (2020). Comprehensive Analysis of Mechanical Properties of
CB/SiO2/PVDF Composites, Polymers, 12, 146, doi:10.3390/polym12010146
[40] Arul K. T., & Rao M. S. R. (2020). Ferroelectric properties of flexible PZT composite films.
Journal of Physics and Chemistry of Solids, 109371, doi:10.1016/j.jpcs.2020.109371.