Olefinic PolymersTechnical Data Sheet
PGPCOwww.pgpc-ir.comPGPCOwww.pgpc-ir.com
and Compounds
Unit 4, No 202, A�er Yarmohammadi St, Dolat St, Pasdaran St, Tehran, Iran
+98-21-22583822 +98-21-26471511
@pgpco PGPCO persian gulf polymer Co
C O N T E N T SABOUT US / 2Our Vision & Mission / 4Linear Low Density Polyethylene (LLDPE) / 6Low Density Polyethylene (LDPE) / 18High Density Polyethylene (HDPE) / 40Polypropylene (PP) / 78Polyvinyl Chloride (PVC) / 106Polycarbonate (PC) / 112Masterbatches,Compounds and blends / 114
About UsPersian Gulf Polymer Pouya Tejarat Novin (PGPCO)
Better Decision for better Production. 3
P ersian Gulf Polymer Pouya Tejarat Novin (PGPCO), estab-lished in 2016, is a reputed, professionally managed busi-
ness company active in the field of oil, gas, chemical and petro-chemical products. The company’s focus is on supplying virgin and recycled polymers in global markets, but there are also sub-stantial activities in supplying chemicals and oil derivatives, which handled by related departments. Although the company seems young, however all staff and managers are well experi-enced with more than 10 years in this industry. The company benefits from powerful relationships with petrochemical plants, also we have a worldwide network for the marketing of petro-chemical products.
PGPCO is concentrating on just-in-time deliveries of a variety of top quality plastic, petrochemical and oil-refineries products with competitive prices. In addition, we are in the deal with many refineries, petrochemical and plastic recycling and compound-ing plants, which allow us to serve our clients quickly and effec-tively. Our ability for quick and effective services make business so quickly and effectively making the company so strong with a good reputation in the market and building market shares in-creasingly; we provide fast, on time solutions to the immediate orders of clients as well as building lasting relationships based on trust and mutual understanding.
Together with an ecological attitude, PGPCO meets the market demands by working together with customers and suppliers closely.
4 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Our Vision & Mission
Better Decision for better Production. 5
• To be the world leader in the market by meeting customer de-
mands in a timely, responsible, reliable and efficient business
behavior.
• In an ever-changing world, we aim to be an indispensable part
of our customers’ lives.
• Develop our business, build strong lasting partnerships and
create an innovative industry leading trade & supply experienc-
es.
• We seek to generate value in products’ and to deliver superior
service to our customers and manufacturers by understanding
their specific market needs in terms of quality, cost, financial
advice, and environmental friendly distribution.
• Our mission is to exceed the expectations of every client by
offering them outstanding customer’s service.
• PGPCO produces intelligent solutions that are based on in-
novative and tailor-made products and services. Integrated
with its reputable and reliable partnerships, PGPCO becomes
a long-term solution partner for its customers and suppliers
and this aspect also creates achievement opportunities for its
shareholders. In meeting the requirements of international cus-
tomers in plastics raw material, PGPCO adopts a management
approach that is focused on continuous improvement, most
effective and efficient use of its resources to create added value
for the honorable customers.
6 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Linear Low Density PolyethyleneLLDPE
Better Decision for better Production. 7
8 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“LL 0209KJ” is a LLDPE copolymer with butane-1as a co
monomer which contains antioxidant, Slip and antiblock additives. It gives film of high slip which is easily separable.
It is recommended for general purpose applications. It is suit-
able for blending with conventional LDPE. Film made from
pure LL 0209 KJ has the following advantages over conven-
tional LDPE:
• Easier sealing
• Greater drawdown capability
• Higher tensile strength
• Higher puncture resistance.
Application:• Food Grade
• Refuse sacks.
• Produce bags, Carrier bags.
LL0209KJ
Better Decision for better Production. 9
High Slip/ Antiblock Grade
Additive Silica Talc
Neutralizer Calcium Stearate Calcium Stearate
Antioxidant Irganox1010 , Irgafos168 Irganox1010 , Irgafos168
Antiblock Siloblock47 250 Talc ABT
Slip Erucamide Erucamide
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 2.16kg) 0.9 g/10 min ISO 1133
Density 921 Kg/m³ ISO 1183
Tensile Strength at Yield MD/TD 10/11 MPa ISO 527
Tensile Strength at Break MD/TD 41/32 MPa ISO 527
Elongation at Break MD/TD 620/840 % ISO 527
Tear Strength MD/TD 145/370 g/25µ ASTM D 1922
Dart Drop Impact 150 g ASTM D 1709
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
10 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“LL 0209AA” is a LLDPE copolymer with 1-butene as a
co-monomer which contains antioxidant. It is recommended
for general purpose applications. It is suitable for blending
with conventional LDPE. The film made from pure LL0209-AA
has the following advantages over conventional LDPE: Better
sealing, higher puncture resistance, Greater drawdown capa-
bility, and higher tensile strength.
Neutralizer: Calcium Stearate
Antioxidant: Irganox1010, Irganox168
Application:• Food Grade
• Heavy duty sacks, Agricultural films, liners
• Produce bags, Stretch film
LL0209AA
Better Decision for better Production. 11
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C/ 2.16kg) 0.9 g/10 min ISO 1133
Density 920 Kg/m³ ISO 1183
Tensile Strength at Yield MD/TD 10/11 MPa ISO 527
Tensile Strength at Break MD/TD 41/32 MPa ISO 527
Elongation at Break MD/TD 620/840 % ISO 527
Tear Strength MD/TD 145/370 g/25µ ASTM D 1922
Dart Drop Impact 130 g ASTM D 1709
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
12 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:Product Description: 22501 is a LLDPE blown film grade de-signed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications.
Application:• Blown film grade• General Purpose applications
Features:• High stiffness• Good optical properties• Low extrusion temperature• Ease of processing• Low gels• Suited for blending with LDPE
Additives:• Thermal Antioxidant (Process Stabilizer)• Antiblock Agent• Slip Agent • Catalyst neutralizer (acid scavenger, lubricant)
22501KJ
Better Decision for better Production. 13
PROPERTY VALUE UNIT TEST METHOD
Density 0.9220 g/ml ASTM D 1505
MFR(190°C/2.16kg) 0.95 g/10min ASTM D 1238
Dart Impact 80 g ASTM D 1709
Elmendorf Tear MD/TD 105/460 g ASTM D 1922
Tensile strength at yield MD/TD 13/12.5 MPa ASTM D 882
Tensile strength at Break MD/TD 45/30 MPa ASTM D 882
Ultimate Elongation MD/TD 680/780 % ASTM D 882
2% Secant modulus MD/TD 200/240 MPa ASTM D 882
Haze 21 % ASTM D 1003
Gloss 45° 38 % ASTM D 2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
Recommended processing conditions
Melt Temperature °C 190-230
Blown up ration 2.0-3.0
Dip Gap mm 2.0-2.5
Thickness micron 15-150
@ 25 micron film obtained on Collin 25, B.u.R. 2.5: I, Temp. Profile 155 → 190°C.
14 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:22501 is a LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion tem-perature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications.
Application:• Blown film grade• General Purpose applications
Features:• High stiffness• good optical properties• low extrusion temperature• ease of processing• low gels• suited for blending with LDPE
Additives:• Thermal Antioxidant (Process Stabilizer)• Catalyst neutralizer (acid scavenger, lubricant)
22501AA
Better Decision for better Production. 15
PROPERTY VALUE UNIT TEST METHOD
Density 0.9220 g/ml ASTM D 1505
MFR(190°C/2.16kg) 0.95 g/10min ASTM D 1238
Dart Impact 80 g ASTM D 1709
Elmendorf Tear MD/TD 105/460 g ASTM D 1922
Tensile strength at yield MD/TD 13/12.5 MPa ASTM D 882
Tensile strength at Break MD/TD 45/30 MPa ASTM D 882
Ultimate Elongation MD/TD 680/780 % ASTM D 882
2% Secant modulus MD/TD 200/240 MPa ASTM D 882
Haze 21 % ASTM D 1003
Gloss 45° 38 % ASTM D 2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
Recommended processing conditions
Melt Temperature °C 190-230
Blown up ration 2.0-3.0
Dip Gap mm 2.0-2.5
Thickness micron 15-150
at 25 micron film obtained on Collin 25, B.u.R. 2.5: I, Temp. Profile 155 → 190°C.
16 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:22B01 is a LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion tem-perature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications.
Application:• High stiffness Blown film• Blending• Lamination
Features:• High stiffness Blown film• Blending• Lamination
Additives:• Thermal Antioxidant (Process Stabilizer)• Anti-block agent• Processing aid
LL22B01AA
Better Decision for better Production. 17
PROPERTY VALUE UNIT TEST METHOD
Density 0.920-0.924
g/ml ASTM D 1505
MFR (190°C/2.16kg) 0.8-1.2 g/10min ASTM D 1238
Dart Impact 75 g ASTM D 1709
Elmendorf Tear MD/TD 120/400 g ASTM D 1922
Tensile strength at Break MD/TD 49/43 MPa ASTM D 882
Ultimate Elongation MD/TD 800/900 % ASTM D 882
2% Secant modulus MD/TD 150/180 MPa ASTM D 882
Haze 25 % ASTM D 1003
Gloss 45° 35 % ASTM D 2457
Fish Eyes 60 Gels/m² MTM 17108
Ti content 2 Ppm wt MTM 15636
Yellowness Index 0.5 - ASTM D1925
F/E Ratio <30 - ASTM D1238
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
18 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Low Density PolyethyleneLDPE
Better Decision for better Production. 19
20 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:Lupolen 2420D is a non – additive, low density Polyethylene. It is delivered in pellet form.
Application:• Bags & Pouches • Bottles for Consumer Goods • Shrink Film • Blown Film • Film
Features:• Good Processability• Good Tear strength• Good Toughness
Processing Method:• Blown Film• Injection Moulding• Extrusion Blow Moulding
LD2420D
Better Decision for better Production. 21
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C/ 2.16kg) 0.25 g/10 min ISO 1133
Density 0.923 Kg/m³ ISO 1183
Tensile Modulus 240 MPa ISO 527-1, -2
Tensile Strength at Yield 10 MPa ISO 527-1, -2
Tensile Strength at Break MD/TD 27/20 MPa ISO 527-1, -3
Tensile Strain at Break MD/TD 200/500 % ISO 527-1, -3
Dart Drop Impact (50 blown film) 250 g ASTM D 1709
Vicat softening temp (50ºC/h 10N)
94 °C ISO 306
Haze (50) < 14 % ASTM D1003
Gloss (60º ,50) > 50 ASTM D2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
22 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:LFI 2130 can be used for general packaging applications, par-ticularly those requiring a measure of shrink.
Features:It has excellent toughness and outstanding biaxial shrink properties. The material contains only antioxidant and has very low energy consumption during processing.
Processing Conditions:• Extruder temperature profile: 150-170 °C• Frost line height: 5-7 times die diameter• Blow Up Ratio: 2-3• Recommended film thickness: 25 to 50 µm.
LFI2130
Please note that, these processing conditions are recommended by producer only for 100% LFI2130 resin (not in the case of blending with any other compat-ible material), but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.
Better Decision for better Production. 23
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190 °C/ 2 .16 Kg ) 0.3 dg/min ISO 1133
Density 921 Kg/m³ ISO 1183 (A)
Impact strength 31 KJ/m ASTM D 4272
Tear strength TD/MD 45/20 KN/m ISO 6383-2
Yield stress TD/MD 10/11 MPa ISO 527
Tensile Strength at Break TD/MD
24/22 MPa ISO 527
Tensile Strain at Break TD/MD >500/350 % ISO 527
Modulus of Elasticity TD/MD 150/140 MPa ISO 527
Coefficient of friction 0.7 G ASTM D 1894
Blocking <5 G SABTEC Method
Re-blocking 20 G SABTEC Method
Haze 12 % ASTM D1003A
Gloss (45º) 55 % ASTM D 2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
24 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:Lupolen 2420F is a non – additivated, low density Polyeth-ylene. It is delivered in pellet form.
Application:• Bags & Pouches • Blow Moulding Application • Shrink Film • Blown Film • Film
Processing Method:• Blown Film• Injection Moulding• Extrusion Blow Moulding
Features:• Good Heat Seat• Optical• Good Processability• Good Melt Strength
LD2420F
Better Decision for better Production. 25
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C / 2.16kg) 0.75 g/10 min ISO 1133
Density 0.923 Kg/m³ ISO 1183
Tensile Modulus 260 MPa ISO 527-1, -2
Tensile Strength at Yield 11 MPa ISO 527-1, -2
Tensile Strength at Break MD/TD 26/20 MPa ISO 527-1, -3
Tensile Strain at Break MD/TD 300/600 % ISO 527-1, -3
Dart Drop Impact (50 blown film) 150 g ASTM D 1709
Vicat softening temp (50ºC/h 10N) 96 °C ISO 306
Haze (50) < 0.8 % ASTM D1003
Gloss (60º ,50) > 90 ASTM D2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
26 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:LH0075 is a high molecular weight low-density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. The film made from LH0075 exhibits high dart impact combined with excellent yield and tensile strength and high stiffness. It can be processed on au-tomatic machines. It possesses good dimensional stability. LH0075 is chiefly recommended for extrusion of blown film. It is suitable for shrink film having a high resistance to the hole formation and high degree of shrinkage on cooling. LH0075 contains antioxidant.
Processing conditions:LH0075 can be easily processed in all types of extruders. The temperature of the polymer at the die output should be in the range of 180-210˚C. In order to preserve the excellent me-chanical properties, it is advisable to limit the predominant orientation of the film along the machine direction by work-ing with a blowup ratio of 2. The film temperature at the nip rollers and haul–off should be kept as close as possible to the ambient temperature.
LH0075
Better Decision for better Production. 27
PROPERTY VALUE UNIT TEST METHOD
Mass density 0.921 gr/ml * TSTM 209 B
Melt Flow Rate (190 ˚C/2.16 kg) 0.75 g/10min ASTM D 1238
Vicat softening point 94 °C ASTM D 1525
Elongation at break (MD) 300 Min % ASTM D 882
Elongation at break (TD) 450 Min % ASTM D 882
Tensile at break (MD) 170 Min Kg/cm² ASTM D 882
HDT 33 °C ASTM D 648
Dart impact 120 Min gr ASTM D 1709
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
TSTM = Toyo Soda Standard Test Method.
Application:• Carrier bags • Shrink film • Industrial film • Dust bin liners • Large bottles • Blow moulding of small containers • Packaging of pharmaceutical products
28 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:LFI 2119 is a low density polyethylene, with excellent optical properties. This grade offers a high output and excellent draw down and specially designed for general purpose thin films.
Application:LFI 2119 is recommended for blown film extrusion. This prod-uct is suitable for manufacture of general purpose LDPE film packaging and general lamination films. Pharmaceutical Ap-plications and food packaging.
Additive:• Antioxidant
Processing Conditions:• Extruder temperature profile: 160-185°C• Frost line height: 5-7 times die diameter.• Blow Up Ratio: 2-3• Recommended film thickness: 20 to 50 µm.
LFI2119
Please note that, these processing conditions are recommended by producer only for 100% LFI2119 resin (not in the case of blending with any other compat-ible material), but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.
Better Decision for better Production. 29
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190 °C /2 .16 Kg ) 1.9 dg/min ISO 1133
Density 921 Kg/m³ ISO 1183 (A)
Impact strength 26 KJ/m ASTM D 4272
Tear strength TD/MD 25/60 KN/m ISO 6383-2
Yield stress TD/MD 11/13 MPa ISO 527
Tensile Strength at Break TD/MD 20/35 MPa ISO 527
Tensile Strain at Break TD/MD >500/150 % ISO 527
Modulus of Elasticity TD/MD 200/190 MPa ISO 527
Coefficient of friction > 1 g ASTM D 1894
Blocking 20 g SABTEC Method
Re-blocking 100 g SABTEC Method
Haze 9 % ASTM D1003A
Gloss (45º) 55 % ASTM D 2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
30 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:Lupolen 2420H is a non – additive, low density Polyethylene. It is delivered in pellet form.
Application:• Bags & Pouches • Food Grade• Cast Film• Shrink Film • Blown Film
Processing Method:• Blown Film• Cast Film
Features:• Good Heat Seat• Optical• Good Processability
LD2420H
Better Decision for better Production. 31
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°/ 2.16kg) 1.9 g/10 min ISO 1133
Density 924 Kg/m³ ISO 1183
Tensile Modulus 260 MPa ISO 527-1, -2
Tensile Strength at Yield 11 MPa ISO 527-1, -2
Tensile Strength at Break MD/TD 26/18 MPa ISO 527-1, -3
Tensile Strain at Break MD/TD 250/600 % ISO 527-1, -3
Dart Drop Impact (50 blown film) 110 g ASTM D 1709
Vicat softening temp (50ºC/h 10N) 94 ºC ISO 306
Haze (50) < 8.0 % ASTM D1003
Gloss (60º ,50) > 100 ASTM D2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
32 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:LF0200 is a high molecular weight low-density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. The film made from LF0200 exhibits high dart impact combined with excellent yield and tensile strength and high stiffness. Its toughness bears even in cold temperatures. The film can be sealed on all types of machines. The film possesses good dimensional stability and is resistant to tearing and breaking. LF0200 contains antiox-idant.
Processing conditions:LF0200 can be easily processed in all types of extruders. The temperature of the polymer at the die output should be in the range of 160-180 o C. Minimum blow-up ratio should be about 2 in order to keep a good balance of mechanical properties. To avoid blocking and shrinkage in the reel, the film tempera-ture at the nip rollers and haul off should be kept as close as possible to the ambient temperature.
LF0200
Better Decision for better Production. 33
PROPERTY VALUE UNIT TEST METHOD
Mass density 0.921 gr/ml * TSTM 209 B
Melt Flow Rate (190 ˚C/2.16 kg) 2 g/10min ASTM D 1238
Vicat softening point 94 C° ASTM D 1525
Haze 15 Max % ASTM D 1003
Gloss at 60 60 Min Gu ASTM D 523
Elongation at break (MD) 330 Min % ASTM D 882
Elongation at break (TD) 660 Min % ASTM D 882
Tensile at break (MD) 160 Min Kg/cm² ASTM D 882
Dart impact 100 Min gr ASTM D 1709
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
TSTM = Toyo Soda Standard Test Method.
Application:• General purpose bags • Packaging of mechanical parts Industrial film • Carrier bags large bottles • Coextruded milk bags • Low tension power cables insulation and industrial in-jection mouldings.
34 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:LFI 2125A is suitable for packaging films and is especial suit-able when ultimate down gauging is required. It is suitable for Pharmaceutical applications and food packaging.
Feature:LFI 2125A is a grade with a very high level of anti-block and a high level of slip agent (Erucamide) the grade has an excellent draw down ability. The films produced from this grade are stiff, have excellent optical properties, low COF and no blocking.
• Additive:• Antioxidant
• Slip agent
• Anti block agent
LFI2125A
Better Decision for better Production. 35
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C/ 2 .16 Kg) 2.5 dg/min ISO 1133
Density 921 Kg/m³ ISO 1183 (A)
Impact strength 23 KJ/m ASTM D 4272
Tear strength TD/MD 25/70 KN/m ISO 6383-2
Yield stress TD/MD 11/13 MPa ISO 527
Tensile Strength at Break TD/MD 19/30 MPa ISO 527
Tensile Strain at Break TD/MD >500/100 % ISO 527
Modulus of Elasticity TD/MD 180/190 MPa ISO 527
Coefficient of friction 0.2 g ASTM D 1894
Blocking < 5 g SABTEC Method
Re-blocking 0 g SABTEC Method
Haze 9 % ASTM D1003A
Gloss (45º) 60 % ASTM D 2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
36 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:Lupolen 2420K is a non – additive, low density Polyethylene. It is delivered in pellet form.
Application:• Coatings
• Protective
• Surface Protection Film
• Shrink Film
Processing Method:• Blown Film
• Cast Film
• Extrusion Coating
• Injection Molding
Feature:• Good Heat Seal
• Good Optical Properties
• Good Processability
LD2420K
Better Decision for better Production. 37
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C/ 2.16kg) 4 g/10 min ISO 1133
Density 924 Kg/m³ ISO 1183
Tensile Modulus 260 MPa ISO 527-1, -2
Tensile Strength at Yield 11 MPa ISO 527-1, -2
Tensile Strength at Break MD/TD 22/17 MPa ISO 527-1, -3
Tensile Strain at Break MD/TD 300/600 % ISO 527-1, -3
Dart Drop Impact (50 blown film) 100 g ASTM D 1709
Vicat softening temp (50ºC/h 10N) 92 ºC ISO 306
Haze (50) < 8.0 % ASTM D1003
Gloss (60º ,50) > 105 ASTM D2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
38 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:LFI2047A is a low density polyethylene, with good toughness and good optical properties. This product contains a medium level of anti-block and slip agent (Erucamide), has low energy consumption during processing and a good draw down abili-ty. It typically exhibits low friction and low blocking.
Application:LFI2047A is recommended for blown film extrusion. This product is very suitable for high clarity laundry bags, textile wrapping films and zip lock bags. This grade enables high speed converting without sticking and is suitable for Pharma-ceutical application and food packaging.
Processing Conditions:• Extruder temperature profile: 145-160°C
• Frost line height: 5-7 times die diameter.
• Blow Up Ratio: 2-3
• Recommended film thickness: 25 to 50 µm.
LFI2047A
Please note that, these processing conditions are recommended by producer only for 100% LFI2119 resin (not in the case of blending with any other compat-ible material), but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.
Better Decision for better Production. 39
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C /2 .16 Kg ) 4.7 dg/min ISO 1133
Density 920 Kg/m³ ISO 1183 (A)
Impact strength 15 KJ/m ASTM D 4272
Tear strength TD/MD 25/80 KN/m ISO 6383-2
Yield stress TD/MD 11/12 MPa ISO 527
Tensile Strength at Break TD/MD 15/27 MPa ISO 527
Tensile Strain at Break TD/MD >500/100 % ISO 527
Modulus of Elasticity TD/MD 200/200 MPa ISO 527
Coefficient of friction 0.2 g ASTM D 1894
Blocking 20 g SABTEC Method
Re-blocking 10 g SABTEC Method
Haze 9 % ASTM D1003A
Gloss (45º) 55 % ASTM D 2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
40 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
High Density Polyethylene HDPE
Better Decision for better Production. 41
42 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HD-5000S is a HDPE grade specially designed for monofila-ment applications, which combines good processability with high tenacity. This grade has good balance of mechanical strength and high production rates. HD-5000S is also well suited for multiply applications, like ropes and stretched fil-aments.
Application:• Fishing net
• Rope
• Agricultural net
• Tarpaulin
• Woven sack
Processing Conditions:Recommended barrel temperatures range is between 160°C and 190°C.
HD5000S
Better Decision for better Production. 43
PROPERTY VALUE UNIT TEST METHOD
Density 0.954 g/ml ASTM D 1505
MFR(190°C/2.16kg) 0.8 g/10min ASTM D 1238
Vicat Softening Point 125 º C ASTM D 1525
Flexural Modulus 1100 MPa ASTM D 790
Tensile Strength at Yield 24 MPa ASTM D 638
Tensile Strength at Break 39 MPa ASTM D 638
HDT 75 °C ASTM D 648
Notched Izod Impact at 23 °C 400 J/m ASTM D 256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
44 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HD 7000F is high density polyethylene copolymer (with Bu-tene-1 as co monomer) which well known for the high quality film applications. It has Bi-model design of molecular com-position and thon offers both excellent process ability and superior mechanical properties.
Application:• ultra-thin film -Shirt bags.
Processing Conditions:Recommended melt temperature: 200 – 220 °C
Processing Conditions:The product is supplied in palletized 25-kg bags. HD7000F should be stored dry and away from sources of heat and light.
HD7000F
Better Decision for better Production. 45
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190°C/ 2.16Kg) 0.04 g/10 min ISO 1133
Density 0.952 Kg/m³ ISO 1183
Stress at Yield 250 Kg/cm² ASTM D638
Stress at Break 390 Kg/cm² ASTM D638
Elongation at Break Above 500 % ASTM D63
Stiffness 10000 Kg/cm² ASTM D747
Izod Impact Strength 30 Kg.cm/cm ASTM D256
Hardness Shore D 64 D scale ASTM D2240
Stress cracking resistance Above 500 hr ASTM D1693
Melting Point 131 C° ASTM D2117
Vicat Softening Temperature 124 C° ASTM D1525
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
46 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HM-9450F (EX5) is blown film grade resin which is manufac-tured by suspension polymerization of ethylene monomer. HM-9450F (EX5) is a bi-model high density polyethylene with 1-Butene as co monomer.
Application:• For blown films with paper-like quality, suitable for counter bags, carrier bags and wrapping films, excellent processing.
Features:• High molar mass film grade
• Good stiffness and tenacity
Additives:• Antioxidant/Process stabilizer
• Lubricant/ acid scavenger
HM-9450F(EX5)
Better Decision for better Production. 47
PROPERTY VALUE UNIT TEST METHOD
Density 0.949 g/cm³ ISO 1183
FRR (21.6/ 5) 29
MFR (190°C/ 21.6 Kg) 8 g/10 min ISO 1133
MFR (190°C/ 5 Kg) 0.28 g/10 min ISO 1133
Fish Eye Note ≤3 note Internal
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. (Test specimen from compression moulded sheet at 23°C | FRR values are statistical and calcu-lated by dividing MFR values | Notch Impact Test specimen from compressed moulded sheet 23°C)
48 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Please note that, these processing conditions are recommended by producer only for 100% HFI5110 resin (not in the case of blending with any other compat-ible material), but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.
Product Description:HFI5110 is a high molecular weight, high density polyeth-ylene, which has a broad molecular weight distribution and high melt strength. This product specially designed for pro-ducing thin films with excellent strength and rigidity.
Typical Applications:HFI5110 is recommended for blown film extrusion. This prod-uct is suitable for manufacture of high strength grocery sacks, shopping bags and high quality thin films for uni/multi-wall packaging. Films produced with this product can be readily treated and printed to give high quality graphics.
Additive:• Antioxidant• Heat stabilizer Zinc Stearate
Processing Conditions:• Extruder temperature profile: 200-235°C • Frost line height: 6-8 times die diameter. • Blow Up Ratio: 3-5 • Recommended film thickness: 15 to 50 µm
HFI5110
Better Decision for better Production. 49
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate (190 °C / 2 .16 Kg ) 10 dg/min ISO 1133
Density (23 °C) 951 Kg/m³ ISO 1183
Tensile Modulus of elasticity 1050 MPa ISO527-1;2
Tear strength TD/MD 55/55 MPa ISO 527-1;3
Tensile Strain at Break (MD) 580 % ISO 527-1
Tensile Strain at Break (TD) 620 % ISO 527-1
Tensile stress at Yield 26 MPa ISO 527-1
Tensile strain at Yield 10 % ISO 527-1
Elmendorf tear strength(MD) 250 mN ISO 6383-2
Elmendorf tear strength(TD) 800 mN ISO 6383-2
Melting Point 132 °C ISO 3146
Vicat Temperature 127 °C ISO 306
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. Properties are based on 20 µm blown film produced at a melt temperature of 220°C and 4 BUR using 100% HFI5110.
50 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HM-CRP100 N is a high density polyethylene with 1-Butene as co monomer. It is natural, outstanding ESCR, high impact strength, outstanding hydrostatic strength for PE 100 class.
Applications:Pipe extrusion PE 100 class, industrial and pressure pipe, gas pipe, drinking water pipe, relining, and fittings.
Additive:• Antioxidant/Process stabilizer• Lubricant/ acid scavenger
Processing Conditions:• Extruder temperature profile: 200-235°C • Frost line height: 6-8 times die diameter. • Blow Up Ratio: 3-5 • Recommended film thickness: 15 to 50 µm
HM-CRP100 - Natural
Better Decision for better Production. 51
PROPERTY VALUE UNIT TEST METHOD
Density 0.948 g/cm³ ISO 1183
FRR (21.6/5) 28
MFR (190°C/ 2.16 Kg) 6.2 g/10 min ISO 1133
MFR (190°C/ 5 Kg) 0.22 g/10 min ISO 1133
Notched Impact (23°c) 24 mj/mm² ISO179/1eA
Hydrostatic Strength (80 ºC) (4.5 N/mm²) 5000 H ISO 1167
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. (Test specimen from compression moulded sheet at 23°C | FRR values are statistical and cal-culated by dividing MFR values |Notch Impact Test specimen from compressed moulded sheet 23°C)
52 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HM-CRP100 Black is a black pipe grade resin (PE100) which is manufactured by suspension polymerization of ethylene monomer. HM-CRP100 Black is a bi-model high density poly-ethylene with 1-Butene as co monomer.
Applications:Top quality PE100 pressure pipes for gas and water transpor-tation at higher pressures or with thinner walls as PE80.
Additive:• Antioxidant/Process stabilizer• Lubricant/ acid scavenger• Carbon Black
HM-CRP100 - Black
Better Decision for better Production. 53
PROPERTY VALUE UNIT TEST METHOD
Density 0.955 – 0.960 g/cm³ ISO 1183
FRR 21.6/5 28
MFR (190°C/ 2.16 Kg) 6.2 g/10 min ISO 1133
MFR (190°C/ 5 Kg) 0.22 g/10 min ISO 1133
Notched Impact (23°c) 24 mj/mm² ISO179/1eA
Hydrostatic Strength (80 ºC) (4.5 N/mm²) 5000 h ISO 1167
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. (Test specimen from compression moulded sheet at 23°C |FRR values are statistical and calculated by dividing MFR values |Test specimen from compressed moulded sheet 23 C sheet 23 ºC)
54 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:EX3 is a high density polyethylene with 1-Butene as co mono-mer. It is high density and stuffiness, good ESCR, high rigidity, good flow ability and impact strength.
Applications:For container with capacities ranging from a few ml up to 10 liters, also for production of sheets for thermoforming
Features:• High density and Stiffness• good flowability and impact Strength• good Stress Cracking resistance
Additive:• Antioxidant/Process stabilizer• Lubricant/ acid scavenger
Processing Conditions:Recommended barrel temperatures range is between 160 °C and 190 °C.
HM-5010T2N (EX3 – PE80)
Better Decision for better Production. 55
PROPERTY VALUE UNIT TEST METHOD
Density 0.954+0.002 g/cm3 ISO 1183
FRR (21.6/5) 19+3
MFR (190°C/ 21.6 Kg) 23+4 g/10 min ISO 1133
MFR (190°C/ 5 Kg) 1.2+0/3 g/10 min ISO 1133
Notched Impact (23°c) > 9 mj/mm2 ISO179/1eA
Hydrostatic Strength (80 ºC) (4.5 N/mm²) 5000 h ISO 1167
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
56 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HB0035 is a high molecular weight high density polyethylene blow moulding grade combining blow moulding extrusion be-havior and superior mechanical properties. Blow moulded items made from HB0035 exhibit high impact strength and good stress cracking resistance and high stiffness. HB 0035 contains antioxi-dant to protect the polymer from degradation during processing. HB 0035 is a highly crystalline, non-polar thermoplastic and has excellent chemical resistance and superb impact resistance at ambient conditions and even at cold temperatures.
Applications:HB0035 is well suited for wide range of blow moulding applica-tions due to its unique properties. These range from bottles for bleach, motor oil, toiletries, mild and distilled water. This grade is also used to make small containers (from 10 cc to 20 lit.).
Processing ConditionsHB0035 can be processed in most types of blow moulding equipment including HDPE or LDPE extruders. It is suitable for producing hollow article in extrusion blow moulding process. A single screw extruder with a barrel of 25D to 30D long, smooth walled grooved feed section and/ or with decompression, mix-ing and shearing sections with 20D to 25Dscrew length are typi-cal extruders for blow moulding of containers. This arrangement minimizes thermal degradation of melt and provides a high
HB0035
Better Decision for better Production. 57
PROPERTY VALUE UNIT TEST METHOD
MFI (190°C/ 2.16kg) 0.35 g/m10min ASTM D 1238
Density 0.959 g/cm3 ASTM D1505
Izod Impact at 23 °C 25 min Kg.cm/cm ASTM D 256
Yellow Index -5 max. - ASTM D1925
ASH Content 0.06 max Wt% ASTM D1063
Volatile matter 0.05 max Wt% ASTM D 1960
Tensile Strength at Break 290 min g/cm3 ASTM D 638
Elongation at Break 900 min % ASTM D 638
Melting point 130 ºC ASTM D2117
Vicat Softening Point 126 ºC ASTM D 1525
Flexural Modulus 1100 MPa ASTM D 790
ESCR 15 Hr ASTM D1693
HDT 75 °C ASTM D 648
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests.
plasticizing capacity coupled with good extrudate quality.
Food Contact:The composition of products complies with the EC Directive 90/128/EEC for use in food contact application.
Packaging: This product is packed in 25 Kg PE bags.
58 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HM-8355(BL4) is a high density polyethylene with 1-Butene as co monomer with general purpose grade for large con-tainers. It is a high molar mass, easily processable, high stiff-ness strength, good stress cracking resistance and very good molding surface finish grade resin.
Applications:• Jerry can• General purpose grade for large container (volume ap-prox. 1-500 lit)
Features:• High molar mass• easily processable high stiffness strength• good stress Cracking resistance and very good molding surface finish
Additive:• Antioxidant/Process stabilizer• Lubricant/ acid scavenger
Processing Conditions:Recommended barrel temperatures range is between 160 °C and 190 °C.
HM-8355 (BL4)
Better Decision for better Production. 59
PROPERTY VALUE UNIT TEST METHOD
Melt Index(21.6) 9.5 g/10 min ISO 1113
Melt Index(5) 0.35 g/10 min ISO 1113
FRR (21.6/5) 27
Density 0.951 g/cm³ ISO 1183
Swell Ratio 110 %
Notched Impact at 23 °C 10 mJ/mm² ISO 179/ 1 eA
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
60 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:BL3” is a high density polyethylene with 1-Butene as co monomer. It is high density and stuffiness, good ESCR, high rigidity, good flow ability and impact strength.
Applications:For container with capacities ranging from a few ml up to 10 liters, also for production of sheets for thermoforming
Features:• High density and Stiffness• good flowability and impact Strength• good Stress Cracking resistance
Additive:• Antioxidant/Process stabilizer• Lubricant/ acid scavenger
Processing Conditions:Recommended barrel temperatures range is between 160 °C and 190 °C.
HF4760 (BL3)
Better Decision for better Production. 61
PROPERTY VALUE UNIT TEST METHOD
Density 0.954+0.002 g/cm3 ISO 1183
MFR (190°C / 21.6 Kg) 23+4 g/10 min ISO 1133
MFR (190°C/ 5 Kg) 1.2+0/3 g/10 min ISO 1133
FRR (21.6/5) 19±3 -
Notched Impact (23°C) > 9 mj/mm2 ISO179/1eA
Notched Impact at 23 °C 10 mJ/mm² ISO 179/ 1 eA
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
62 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:CC52502 is a Narrow MWD HDPE specially designed for miner-al water bottles and beverage caps. This grade has excellent organoleptic properties which prevent unpleasant odor and taste from cap or closure to transfer to water. It has good gas permeability characteristics, superior process ability and ex-cellent mechanical strength. HDPE CC52502 does not contain slip agent.
Applications:• Caps and closures for mineral water bottles• Caps for sparkling water and carbonated soft drinks• beverage caps.
Features:• Narrow MWD HDPE• excellent organoleptic property• superior processability and excellent mechanical strength• good gas permeability characteristics
Additive:• Antioxidant/acid scavenger
CC52502
Better Decision for better Production. 63
PROPERTY VALUE UNIT TEST METHOD
Density (g/ml) 0.952 ASTM D 1505
MFR (190°C/2.16kg) (g/10min) 2 ASTM D 1238
Vicat Softening Point º C 124 ASTM D 1525
Flexural Modulus MPa 1000 ASTM D 790
Tensile Strength at Yield MPa 25 ASTM D 638
Tensile Strength at Break MPa 38 ASTM D 638
HDT °C 78 ASTM D 648
Notched Izod Impact at 23 °C J/m 180 ASTM D
256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
Processing Conditions:Recommended barrel temperatures range is between 160 °C and 190 °C.
64 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:CC52502 is a Narrow MWD HDPE specially designed for miner-al water bottles and beverage caps. This grade has excellent organoleptic properties which prevent unpleasant odor and taste from cap or closure to transfer to water. It has good gas permeability characteristics, superior processability and ex-cellent mechanical strength. HDPE CC52502SU does contain slip agent and stabilized against UV light.
Applications:• Caps and closures for mineral water bottles• Caps for sparkling water and carbonated soft drinks• beverage caps.
Features:• Narrow MWD HDPE• excellent organoleptic property• superior processability and excellent mechanical strength• good gas permeability characteristics
Additive:• Antioxidant/acid scavenger• UV stabilizer/Slip agent
CC52502SU
Better Decision for better Production. 65
PROPERTY VALUE UNIT TEST METHOD
Density 0.952 (g/ml) ASTM D 1505
MFR (190°C/2.16kg) 2 (g/10min) ASTM D 1238
Vicat Softening Point 124 º C ASTM D 1525
Flexural Modulus 1000 MPa ASTM D 790
Tensile Strength at Yield 25 MPa ASTM D 638
Tensile Strength at Break 38 MPa ASTM D 638
HDT 78 °C ASTM D 648
Notched Izod Impact at 23 °C 180 J/m ASTM D
256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
Processing Conditions:Recommended barrel temperatures range is between 160 °C and 190 °C.
66 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:52511 is a HDPE copolymer injection molding grade for appli-cations requiring a good balance between physical properties and flowability, like housewares and toys.
Applications:• Injection molding grade • Housewarer
Features:• Good balance between physical properties andflowability.
Additive:• Thermal Antioxidant
Processing Conditions:Recommended barrel temperatures range is between 190 and 280°C.
HD52511
Better Decision for better Production. 67
PROPERTY VALUE UNIT TEST METHOD
Density 0.952 (g/ml) ASTM D 1505
Melt Index(190°C/2.16kg) 11 (g/10min) ASTM D 1238
Flexural Modulus 1320 MPa ASTM D 790
Notched Izod Impact at 23 °C 32 J/m ASTM D 256/A
Vicat Softening Point 122 ºC ASTM D 1525
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
68 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:52505 is a HDPE copolymer which is manufactured in gas phase process. This grade is an injection molding grade for applications requiring a good physical property even at low temperatures, like pails, containers and technical moldings.
Applications:• Containers
Features:• Good physical property even at low temperatures.
Additive:• Thermal Antioxidant
Processing Conditions:Recommended barrel temperatures range is between 190 and 280°C.
HD52505
Better Decision for better Production. 69
PROPERTY VALUE UNIT TEST METHOD
Density 0.952 g/ml ASTM D 1505
MFR(190°C/2.16kg) 4 – 6 g/10min ASTM D 1238
Vicat Softening Point 124 º C ASTM D 1525
Flexural Modulus 1200 MPa ASTM D 790
Tensile Strength at Yield 27 MPa ASTM D 638
Tensile Strength at Break 18 MPa ASTM D 638
H.D.T 82 º C ASTM D 648
Notched Izod Impact at 23 °C 55 J/m ASTM D 256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
70 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:52505UV is a HDPE copolymer which is manufactured in gas phase process. This grade is an injection molding grade for applications requiring a good physical property even at low temperatures, like pails, containers and technical moldings.
Applications:• Containers
Features:• Good physical property even at low temperatures.
Additive:• Thermal Antioxidant UV Stabilizer
Processing Conditions:Recommended barrel temperatures range is between 190 and 280°C.
HD52505UV
Better Decision for better Production. 71
PROPERTY VALUE UNIT TEST METHOD
Density 0.952 g/ml ASTM D 1505
MFR(190°C/2.16kg) 4 – 6 g/10min ASTM D 1238
Vicat Softening Point 124 º C ASTM D 1525
Flexural Modulus 1200 MPa ASTM D 790
Tensile Strength at Yield 27 MPa ASTM D 638
Tensile Strength at Break 18 MPa ASTM D 638
H.D.T 82 º C ASTM D 648
Notched Izod Impact at 23 °C 55 J/m ASTM D 256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
72 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:60505 is a HDPE injection molding grade which combines high stiffness with good physical properties. This resin is well suited for crates and toys applications
Applications:• Injection Molding Grade• Crates• Toys applications
Features:• High stiffness with good physical properties
Additive:• HD-60505: Thermal Antioxidant • HD-60505UV: Thermal Antioxidant UV Stabilizer
Processing Conditions:Recommended barrel temperatures range is between 190 and 280°C.
HD60505
Better Decision for better Production. 73
PROPERTY VALUE UNIT TEST METHOD
Density 0.9570 g/ml ASTM D 1505
MFR(190°C/2.16kg) 5.5 g/10min ASTM D 1238
Vicat Softening Point 127 º C ASTM D 1525
Flexural Modulus 1480 MPa ASTM D 790
Tensile Strength at Yield 30 MPa ASTM D 638
Tensile Strength at Break 16 MPa ASTM D 638
H.D.T 78 º C ASTM D 648
Notched Izod Impact at 23 °C 46 J/m ASTM D 256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
74 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:60507 is a HDPE homopolymer which is manufactured in gas phase process for injection molding grade which combines good flowability with balanced physical properties. This resin is well suited for general purpose application requiring high stiffness.
Applications:• Injection Molding Grade• Crates
Features:• Good flowability with balanced physical properties
Additive:• HD-60507:
• Thermal Antioxidant (Process Stabilizer)• Catalyst neutralizer (acid scavenger, lubricant)
• HD-60507UV: • Thermal Antioxidant (Process Stabilizer) • Catalyst neutralizer (acid scavenger, lubricant)• UV Stabilizer
Processing Conditions:Recommended barrel temperatures range is between 190 and 280°C.
HD60507UV
Better Decision for better Production. 75
PROPERTY VALUE UNIT TEST METHOD
Density 0.958 g/ml ASTM D 1505
MFR(190°C/2.16kg) 7.5 g/10min ASTM D 1238
Vicat Softening Point 127 º C ASTM D 1525
Flexural Modulus 1500 MPa ASTM D 790
Tensile Strength at Yield 30 MPa ASTM D 638
Tensile Strength at Break 13 MPa ASTM D 638
Ultimate Elongation 350 % ASTM D 638
Notched Izod Impact at 23 °C 36 J/m ASTM D 256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
76 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:HD-52518 is a HDPE copolymer which manufactured by gas phase process. This grade is LLDPE Injection Moulding, Extru-sion Coating & Rotomoulding. Injection molding for applica-tion requiring a good balance between easy of process ability and flowability and mechanical properties are the special peruse of this grade.
Applications:• High fluidity • Houseware
Features:• Good balance between physical properties and flowability
Additive:• Thermal Antioxidant (Process Stabilizer) • Catalyst neutralizer (acid scavenger, lubricant)
Processing Conditions:Recommended barrel temperatures range is between 190 and 280°C.
HD-52518
Better Decision for better Production. 77
PROPERTY VALUE UNIT TEST METHOD
Density 0.9520 g/ml ASTM D 1505
MFR (190°C/ 2.16kg) 18 g/10min ASTM D 1238
Vicat Softening Point 122 º C ASTM D 1525
Flexural Modulus 1350 MPa ASTM D 790
Notched Izod Impact at 23 °C 25 J/m ASTM D 256/A
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
78 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Polypropylene PP
Better Decision for better Production. 79
80 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“HP525J” is a medium flow homopolymer with bimodal molecular weight distribution and good clarity intended for BOPP films. The product is suitable for metallizable film, both as monolayer and in coextruded structures. It contains a stan-dard processing stabilisation but does not contain any slip, antiblocking agents and is Calcium Stearate free. “ HP525J” offers good optical properties, easy processing and very sta-ble film profile. Typical applications are BOPP packing films and Solid Phase Thermoforming sheets. “HP525J” is suitable for food contact.
Applications:• High quality packaging film for food, Lamination to oth-er films, Metalizing Film• Medical packaging, Thermoformed food containers
Features:• Medium Flow• Good processability• Good Transparency and Gloss
Processing Method:• BOPP Film• Thermoforming
HP525J (Homo Polymer)
Better Decision for better Production. 81
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 3.0 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 35 MPa ASTM D638
Tensile Elongation at Yield 12 % ASTM D638
Izod Impact Strength (notched) at 23 °C 55 J/m ASTM D256
Rockwell Hardness 105 R Scale ASTM D785
Vicat softening point (10N) 159 °C ASTM D1525
H.D.T. (0.46 Mpa) 94 °C ASTM D648
Accelerated oven ageing in air at 150 °C 500 hours ASTM D3012
Haze (20 µm) 0.5 % ASTM D1003
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
82 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“HP550J” is a polypropylene homopolymer particularly suit-able for the extrusion of sheet for thermoforming, film yarn and monofilament. This grade combines outstanding pro-cessability with good mechanical properties. “HP550J” is de-signed for the production of films that can be converted into stretched tapes for weaving applications. Textile film yarns with a denier count of not more than 1100 to 1200 and are used for the production of carpet backing, bags, industrial fabrics, mats and artificial grass. Film yarn with a denier count ranging from 3000 to 28000 is used for baler twines, packaging twines and ropes. “HP550J” is suitable for food contact.
Applications:• Shift sheet for High quality thermoformings such as vending cups, packaging dairy products and trays for fruit, biscuits and chocolates• Raffia, tapes, strapping, mats and artificial grass, brush and broom filling and technical applications, nets for var-ious purposes
Processing Method:• Extrusion (film yarn, monofilament, sheet)• Thermoforming
Features:
HP550J (Homo Polymer)
Better Decision for better Production. 83
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
• Good mechanical properties• Good processability• Homopolymer
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 3.2 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 35 MPa ASTM D638
Tensile Elongation at Yield 12 % ASTM D638
Izod Impact Strength (notched) at 23 °C 55 J/m ASTM D256
Rockwell Hardness 102 R Scale ASTM D785
Vicat softening point (10N) 156 °C ASTM D1525
H.D.T. (0.46 Mpa) 94 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 hours ASTM D3012
84 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Index 6 Dg/min ISO 1133
Density 0.9 g/cm³ ISO 1183
Flexural Modulus 1500 N/mm² ISO 178
Tensile 34 N/mm² ISO R527
Elongation at yield 13 % ISO R527
Izod Impact Strength (notched) at 23 °C 4 Kj/m² ISO 180
Rockwell Hardness 71 point ISO 868
Vicat softening point (9.8 N) 155 °C ISO 306/A
H.D.T. (0.46 Mpa) 119 °C ISO 75/B
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
Product Description:C30S is a polypropylene homopolymer with a good flow properties and is particularly suitable for the extrusion of film yarn, monofilament, cast film and sheet. C30S combines out-standing process ability with good mechanical properties.
Applications:• Baler twines, packaging twines and ropes.• Brush and broom filling and technical applications.
C30S (Homo Polymer)
Better Decision for better Production. 85
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Index 16 Dg/min ISO 1133
Density 0.9 g/cm³ ISO 1183
Flexural Modulus 1550 N/mm² ISO 178
Tensile 30 N/mm² ISO R527
Elongation at yield 12 % ISO R527
Vicat softening point (9.8 N) 154 °C ISO 306/A
H.D.T. (0.46 Mpa) 95 °C ISO 75/B
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
Product Description:V 30 S is a high fluidity PP for the production of staple fibers with improved thermo bonding ability for non-woven fabrics.
Applications:The typical applications of this grade are cover stock for dia-pers, feminine care product and wipes, filters and fabrics for the clothing and furniture industry.
V30S (Homo Polymer)
86 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:Moplen Z 30S is a high melt flow homopolymer for the pro-duction of low denier BCF, CF, and staple fibres at medium to high spinning speeds.Moplen Z30S offers a high homogeneity, stable extrusion and excellent process ability on both short and long spinning lines. This grade allows a high stretch ratio and gives tough and resilient fibres.
Applications:• Moplen Z30S is widely used for the production of bulked continuous filament for carpet face yarns.• Another major application is the production of high te-nacity continuous filament for straps for backpacks, han-dles for big bags and safety belts. • Continuous filament with medium tenacity is used for upholstery, sportswear and heavy duty clothing.
• Moplen Z 30S is al also suitable for the production of low denier staple fibres for thermobonding
• Moplen Z 30 S is suitable for food contact.
Z30S (Homo Polymer)
Better Decision for better Production. 87
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Index 25 Dg/min ISO 1133
Density 0.9 g/cm³ ISO 1183
Flexural Modulus 1550 N/mm² ISO 178
Tensile 35 N/mm² ISO R527
Elongation at yield 13 % ISO R527
Izod Impact Strength (notched) at 23 °C 3 Kj/m² ISO 180
Rockwell Hardness 72 Point ISO 868
Vicat softening point (9.8 N) 155 °C ISO 306/A
H.D.T. (0.46 Mpa) 118 °C ISO 75/B
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
88 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“HP552R” is a HIGH MELT FLOW HOMOPOLYMER FOR THE PRODUCTION OF Cf, BCF and fine denier staple fibres at me-dium to high spinning speeds and exhibits excellent antigas-fading properties. “HP552R” is suitable for nonwoven fabrics for diapers, medical-sanitry applications and wipes. Another typical application is high tenacity is used for upholstery and sportswear. “HP552R” is also suited for the production of bulked continuous filament for carpets. “HP552R” is suitable for food contact.
Processing Method:• Fiber Extrusion (CF, BCF, staple)
Features:• High melt flow• excellent antigasfading properties• Good process ability properties
Typical Applications:• Medical-sanitary applications, Wipes and tissues, straps for backpacks, sport bags, bulk bagsand for safety belts• Upholstery and sportswear, Bulk continuous filament for carpets• Hygiene nonwoven
HP552R (Homo Polymer)
Better Decision for better Production. 89
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 25 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 32 MPa ASTM D638
Tensile Elongation at Yield 13 % ASTM D638
Izod Impact Strength (notched) at 23 °C 30 J/m ASTM D256
Rockwell Hardness 100 R Scale ASTM D785
Vicat softening point (10N) 152 °C ASTM D1525
H.D.T. (0.46 Mpa) 94 °C ASTM D648
Accelerated oven ageing in air at 150 °C 150 hours ASTM D3012
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
90 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:″EP440G″ is a nucleated heterophasic copolymer especially developed for extrusion applications. ″EP440G″ exhibits high stiffness, very high impact properties at room and sub-zero temperatures, good dimensional stability and excellent creep and deforming resistance. The main applications of ″EP440G″ are thermoforming, corrugated board and extrusion blow molding.
Processing Method:• Thermoforming, Extrusion blow molding
Features:• Very high impact resistance• High stiffness• Good dimensional stability
Applications:• Crates• Panels & Profiles• Corrugated Sheet• Conduit pipes and fittings for electrical distribution and cable protection• Blow molded bottles and containers
EP440G (Copolymer)
Better Decision for better Production. 91
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 1.3 g/10 min ISO 1133
Density 0.9 Kg/m³ ISO 1183
Flexural Modulus 1450 MPa ISO 527-1, -2
Tensile Strength at Yield 27 MPa ISO 527-1, -2
Tensile Elongation at Break > 50 % ISO 527-1, -2
Tensile Elongation at Yield 8 % ISO 527-1, -2
Charpy impact strength (Notch A)
23°C0°C
409
KJ/m²KJ/m²
ISO 179
Gloss (60°) 65 ----- DIN 67530
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
92 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“EP440L″ is a medium flow heterophasic polypropylene copolymer with improved mechanical properties balance. The product features high stiffness and outstanding impact strength at low temperatures and is specifically designed for injection molding applications. In comparison with con-ventional copolymers with the same MFR and same rigidity, ″EP440L″, exhibits 35 % higher toughness. ″EP440L″ is suit-able for a wide range of applications in the packaging, auto-motive and consumer goods industries.
Processing Method:• Injection molding
Features:• High Impact strength• excellent transparency
Applications:• Packaging, automotive and consumer goods industries• Luggage, paint pails, buckets, containers, crates, batter-ies and large toys
EP440L (Copolymer)
Better Decision for better Production. 93
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 6.0 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1400 MPa ASTM D790
Tensile Strength at Yield 26 MPa ASTM D638
Tensile Elongation at Yield 9 % ASTM D638
Izod Impact Strength (notched) at 23 °C 170 J/m ASTM D256
Izod Impact Strength (notched) at -20 °C 70 R Scale ASTM D256
Shore Hardness (Shore D) 68 ----- ISO 868
Vicat softening point (10N) 152 °C ASTM D1525
H.D.T. (0.46 Mpa) 95 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 hours ASTM D3012
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
94 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:″EP3130UV″ is a non-filled polypropylene copolymer for in-jection molding with very high impact strength. The product has good U.V. resistance designed for outdoor applications. This grade is used for production of automotive parts, such as bumpers, and compounding.
Processing Method:• Injection molding, Compounding
Features:• Very high impact strength especially at low tempera-tures• Good U.V. resistance• Good processability• Heterophasic copolymer
Applications:• Automotive parts• Outdoor applications• Technical articles
PP-EP3130UV (Copolymer)
Better Decision for better Production. 95
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 10 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 850 MPa ASTM D790
Tensile Strength at Yield 18 MPa ASTM D638
Tensile Elongation at Break 60 % ASTM D638
Izod Impact Strength (notched) at 23 °C 500 J/m ASTM D256
Izod Impact Strength (notched) at -20 °C 100 J/m ASTM D256
Shore Hardness (Shore D) 68 ----- ISO 868
Vicat softening point (10N) 135 °C ASTM D1525
H.D.T. (0.46 Mpa) 75 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 hours ASTM D3012
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
96 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“EP548R” is a nucleated, antistatic formulated, high fluidity heterophasic copolymer used for thin-walled injection mold-ing. Items made with “EP548R” exhibit high stiffness. Rela-tively good impact resistance and excellent antistatic prop-erties. Due to its excellent moldability and short cycle items, “EP548R” allows high productivity rates. The finished items show good mechanical properties, high dimensional stability. “EP548R” is very well suited for the production of thin walled articles or articles with long flow paths such as flower pots, containers, housewares, filters, filters housings and appliance components. “EP548R” is suitable for food contact.
Processing Method:• Injection molding
Features:• Good Impact strength• excellent antistatic properties• excellent moldability• short cycle time
Applications:• Housewares, filters, filters housing and appliance com-ponents • Sport, leisure and toys
EP548R (Copolymer)
Better Decision for better Production. 97
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C, 2.16 kg) 21 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 27 MPa ASTM D638
Tensile Elongation at Yield 7 % ASTM D638
Izod Impact Strength (notched) at 23 °C 85 J/m ASTM D256
Izod Impact Strength (notched) at -20 °C 50 R Scale ASTM D256
Rockwell Hardness 98 R Scale ASTM D785
Vicat softening point (10N) 149 °C ASTM D1525
H.D.T. (0.46 Mpa) 110 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 Hours ASTM D3012
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
98 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“EP548T” is a high melt flow rate, nucleated heterophasic co-polymer with a special antistatic additivation used for thin-walled injection molding. IML and houseware applications. The product features improved balance of mechanical prop-erties. The product features improved balance of mechanical properties. The use of “EP548T” allows high productivity due to the easy mold filling and short cycle times. In compari-son with conventional copolymers with the same MFR and the same toughness,”EP548T” exhibits 15% higher rigidity. “EP548T” is suitable for food contact.
Processing Method:• Injection molding
Features:• High fluidity• Easy mold filling and short cycle times• Desirable impact/ stiffness balance• Unspecified antistatic properties• heterophasic copolymer
Applications:• TWIM/IML food containers (Margarine tubs, yoghurt pots, pots for soft cheese, pudding) • Housewares, Caps and closures, Flower pots and cool boxes, Sport, leisure and toys.
EP548T (Copolymer)
Better Decision for better Production. 99
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C, 2.16 kg) 50 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 28 MPa ASTM D638
Tensile Elongation at Yield 5 % ASTM D638
Izod Impact Strength (notched) at 23 °C 60 J/m ASTM D256
Izod Impact Strength (notched) at -20 °C 30 R Scale ASTM D256
Rockwell Hardness 100 R Scale ASTM D785
Vicat softening point (10N) 151 °C ASTM D1525
H.D.T. (0.46 Mpa) 95 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 Hours ASTM D3012
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
100 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:“RP340N” is a polypropylene random copolymer which fea-tures extremely high flow properties, excellent transparency, high gloss and exhibits good antistatic properties. “RP340N” is mainly designed for transparent house wares and quality packaging applications. It is an outstanding grade for injec-tion molded containers and thin-walled packaging where clarity is of utmost importance. In many of these applications, “RP340N” can replace PS since it can match the optical prop-erties whilst adding low weight, low odor transfer, chemical resistance and impact strength.
Processing Method:• Injection molding• Extrusion (sheet)
Features:• High flow properties• excellent transparency• High gloss• Good antistatic properties
Applications:• Clear containers, Household articles, packaging for foods, cosmetics and pharmaceutical• Products lids, caps and closures Coextrusion with other
RP340N (Random Copolymer)
Better Decision for better Production. 101
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C, 2.16 kg) 11 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1050 MPa ASTM D790
Tensile Strength at Yield 28 MPa ASTM D638
Tensile Elongation at Yield 12 % ASTM D638
Izod Impact Strength (notched) at 23 °C 85 J/m ASTM D256
Rockwell Hardness 94 R Scale ASTM D785
Vicat softening point (10N) 128 °C ASTM D1525
H.D.T. (0.46 Mpa) 83 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 Hours ASTM D3012
Haze (1mm) 9 % ASTM D1003
Gloss (60˚) 85 --- ASTM D2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
polypropylene resins to produce• Multilayer sheet for thermoforming trays for fresh pasta and bakery products
102 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:″PP RP340R″ is a nucleated polypropylene random copoly-mer with medium fluidity and outstanding transparency and gloss and is designed for injection molding applications.″RP340R″ is the material of choice for applications where transparency is a primary requirement. This grade is also suitable for injection stretch blow molded containers and bottles. This product combines good see through clarity and excellent moisture barrier properties with hot fallibility. There-fore, ″RP340R″ offers an effective alternative for PET and PVC for the packaging of non-oxygen sensitive products such as confectionary, herbs, toiletries and cosmetics.
Processing Method:• Injection molding• Injection stretch blow molding
Features:• High melt flow• excellent transparency• High gloss• Random copolymer
Applications:• Household containers, housewares - Packaging for food, cosmetics and pharmaceutical products
RP340R (Random Copolymer)
Better Decision for better Production. 103
• Clear tubs and pots for ice cream, yoghurt and other desserts -Medical sector such as syringes, test tubes and vials - Lids, caps and closures - CD and DVD boxes - Sports, Leisure and toys
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C, 2.16 kg) 25 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Flexural Modulus 1050 MPa ASTM D790
Tensile Strength at Yield 28 MPa ASTM D638
Tensile Elongation at Yield 12 % ASTM D638
Izod Impact Strength (notched) at 23 °C 65 J/m ASTM D256
Rockwell Hardness 94 R Scale ASTM D785
Vicat softening point (10N) 127 °C ASTM D1525
H.D.T. (0.46 Mpa) 83 °C ASTM D648
Accelerated oven ageing in air at 150 °C 360 Hours ASTM D3012
Haze (1mm) 22 % ASTM D1003
Gloss (60˚) 73 --- ASTM D2457
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
104 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:″RPX-348S″ is a Polypropylene random copolymer with high fluidity and outstanding transparency and optical properties. This grade is designed for injection molding and injection starch blow molding (ISBM) applications. Thanks to its high fluidity, one can experience reduced cycle times and ener-gy savings compared to conventional grades. “RPX-345S″ is suitable for the packaging of non-oxygen sensitive products (e.g. Confectionary, herbs, toiletries and cosmetics) hcncc, it counts as an effective alternative for the PVC and PET in ISBM.
Processing Method:• Injection molding• Injection stretch blow molding
Features:• High melt flow• Excellent Optical properties• Good antistatic properties• excellent process ability • reduced cycle times Random Copolymer
Applications:• Household containers, housewares, Packaging for food, cosmetics and pharmaceutical products TWIM, Lids, caps and closures, Medical sector such as syringes, test tubes
RPX-345S (Random Copolymer)
Better Decision for better Production. 105
and vials, Sports, leisure and toys. CD and DVD boxes, Bot-tles and containers produced with ISBM.
PROPERTY VALUE UNIT TEST METHOD
Melt Flow Rate ( 230 °C/ 2.16 kg) 38 g/10 min ASTM D1238
Density 0.9 Kg/m³ ASTM D1505
Tensile Modulus 1150 MPa ASTM D790
Tensile Strength at Yield 28 MPa ASTM D638
Tensile Elongation at Yield 11 % ASTM D638
Izod Impact Strength (notched) at 23°C 55 J/m ASTM D785
Rockwell Hardness 94 R-Scale ASTM D785
Accelerated oven ageing in air at 150 °C 360 Hours ASTM D3012
Haze (1mm) 12 % ASTM D1003
Vicat softening point (10N) 128 °C ASTM D1525
H.D.T. B (0.45 MPa) 70 °C ASTM D648
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
106 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Polyvinyl Chloride PVC
Better Decision for better Production. 107
108 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:PVC E6834 is a fine-particle, paste-making emulsion ho-mopolymer giving low-viscosity plastisols.Pastes with a medium plasticizer content show almost New-tonian flow properties. PVC E6834 is suitable for chemically blown foams with a low plasticizer content. The main appli-cation areas are relatively rigid foams for flooring and leather cloth.
Applications:Pastes based on E68 can be applied by all the usual proce-dures. E6834 is well suited for the production of foams having a fine cell structure. It is characterized by the following prop-
erties:• Low initial viscosity• Good chemical foam ability, regular cell structure• Good viscosity stability, particularly at storage tempera-tures of about 40° C• Excellent release properties from heated metal surfaces (punch process).• It has also proved suitable for mechanically frothed foams containing silicone based foaming aids.
Processing:Pastes based on E68 can be applied by all the usual proce-dures.
E-6834 (Emulsion)
Better Decision for better Production. 109
PROPERTY VALUE UNIT TEST METHOD
K-Value 67 ~ 69 ISO 1628-2
Sieve Analysis > 63µm ≤ 2 % ISO 565
Volatile Matter ≤ 0.3 wt% ISO 1269
Methanol extract ≤ 2.5 wt% ISO 6427
Residual VCM ≤1 (ppm) ISO 6401
Thermostability (min) Mathiss drying oven > 15 Min Vinnolit
THMA 180
Paste viscosity After 1 h (Pas) ≤ 6 (Pas) ISO 11468
Part of Quality ≥ 98 % DIN EN 11468
All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests
110 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Product Description:PVC contains approximately 56% by weight of chlorine. This polymer possesses thermoplastic properties.Grade S65 has low porosity & high bulk density.
Applications:• Pipe and fitting• Injection moulding
S-65 (Suspension)
Better Decision for better Production. 111
PROPERTY VALUE UNIT TEST METHOD
K-Value 65 ± 1 ISO 1628-2 /4.4.2.1
Viscosity Number 105 ISO 1682-2 /4.4.2.1
Bulk Density 550 - 610 Gr/Lit ISO 60 /4.4.2.2
Sieve Analysis > 63µm 95 ~ 100 % ISO 4610 /4.4.2.3A
Sieve Analysis > 250 µm 0 ~ 5 % ISO 4610 /4.4.2.3A
Retained on 0.4 mm Sieve < 1 % ISO 4610 /4.4.2.3B
Porosity (Plasticizer absorption) 19 ~ 25 % ISO 4608 /4.4.2.4
Volatile Matter < 0.3 wt% ISO 1269 /4.4.2.5
Flow ability (S/150 g) (10 mm Nozzle) ≤ 25 ISO 6186 /4.4.2.6
Residual VCM ≤ 1 ppm ISO 6401/5.4.2.9
Dark Resin Particles ≤ 20 In Powder
Fish Eyes ≤ 20 Felttest per 25 cm²/4.4.2.8
Sulfate ASH < 0.1 wt% ISO 34511/4.4.2.9- All above mentioned data are typical values and not to be construed as real
specifications. Users should confirm results by their own tests
112 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
PolycarbonatePC
Better Decision for better Production. 113
PROPERTY VALUE UNIT TEST METHOD
MFI (300°C/ 1.2 Kg) 7.1 – 10 g/10 min ASTM D1238
Density 1.2 g/cm³ ASTM D792
Tensile Strength at yield ≥ 60 Mpa ASTM D638
Modulus of Elasticity 2000 – 2400 Mpa ASTM D638
Elongation at Break > 85 % ASTM D638
Dielectric Strength at 50 Hz ≥ 20 Kv/mm ASTM D149
Charpy Impact Strength (Notched) ≥ 25 Kj/m² ASTM D6110
Vicat Soft. Temp. 142 – 146 C ASTM D1525
Transmittance (Thickness 2mm) ≥ 80 % ASTM D1003
Solvent Content Max. 1500 ppm GC (int-st)
Yellow Index Max. 6 --- ASTM D1925 All above mentioned data are typical values and not to be construed as real
specifications. Users should confirm results by their own tests
Processing Method: • Suitable for Molding and Sheet
Application:• Optical, Business Machines, Packaging, Sports, Appli-ances, Electrical, Lighting, Wire & Cable, Automotive
114 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Masterbatches,Compounds and blendsAll kinds of compounds and masterbatches can be produced in one-pack and customized according to customer demand. One-packs are tailor-made and well-balanced additive masterbatches that cover a wide range of customer demands. These are the mixture of two or more additives and present solutions for specific applications.
All kinds of compounds and masterbatches can be produced in one-pack and customized according to customer demand. One-packs are tailor-made and well-balanced additive masterbatches that cover a wide range of customer demands. These are the mixture of two or more additives and present solutions for specific applications.
Better Decision for better Production. 115
116 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Adding color and functionality to plastics, accelerating prod-uct design and development, building brand power in diverse markets. In each of these areas, our products, technology, and service deliver major advantages and cement long-term customer relationships.
• Colored Masterbatches (White, Black, etc.) • Anti-Slip Masterbatches • Antistatic Masterbatches• Antiblock Masterbatches• Calcium Carbonate Masterbatches • Antioxidant Masterbatches• Anti-UV Masterbatches • Anti-fog masterbatches
Masterbatches
Better Decision for better Production. 117
PA based compound:• Polyamide 6 and Polyamide 66 compounds reinforced with glass fiber (10%-40%).• Polyamide 6 and Polyamide 66 compounds reinforced with mineral fillers (10%-40%).• Impact modified PA6 and PA66.
PP based compounds:This class of materials are widely used in automotive indus-tries such as interior and exterior, also engine parts including air conditioning joints, radiator fan and etc.
• Polypropylene compounds reinforced with talc (10%-70%)• Polypropylene compounds reinforced with calcium car-bonate (10%-70%)• Polypropylene compounds reinforced with glass fiber (10%-40%)• Polypropylene compounds reinforced with talc and glass• Polypropylene compounds toughened with elastomers
PC based compounds:Polycarbonate is an amorphous material with properties like
Engineering Plastic Compounds and blends
118 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
high transparency, impact resistance and highdimensional stability. Among the disadvantages of pure poly-carbonate, low tension failure and fluidity can bementioned. Using alloys PC/ABS and PC/PBT are eliminated these defects.
Featured properties of PC based compounds• Impact resistance, tensile strength and excellent rigidity• Extraordinary fluidity and dimensional stability• Good Heat-resistant• High surface brightness and the ability to re-taking pro-cess
Better Decision for better Production. 119
PC and ABS Blends | PC/ABS*Grades MFI
(220°C/ 10Kg) Application Typical Application
220 12 Injection Automobile interior parts
250 8 General Purpose
Automobile interior parts, electrical casing
265 6General
Purpose, High Impact
Automobile interior parts, electrical casing
265 FR 12Injection,
Flame Retar-dant
Automobile parts, Electrical parts
120 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
ExportdestinationsEast price, West quality
Better Decision for better Production. 121
122 PGPCo | Olefinic Polymers and Compounds Technical Data Sheet
Olefinic PolymersTechnical Data Sheet
PGPCOwww.pgpc-ir.comPGPCOwww.pgpc-ir.com
and Compounds
Unit 4, No 202, A�er Yarmohammadi St, Dolat St, Pasdaran St, Tehran, Iran