nanomaterials
Review
Lyotropic Liquid Crystal Phases fromAnisotropic Nanomaterials
Ingo Dierking 1,* and Shakhawan Al-Zangana 2 ID
1 School of Physics and Astronomy, University of Manchester, Oxford Road, Manchester M13 9PL, UK2 College of Education, University of Garmian, Kalar 46021, Iraq; [email protected]* Correspondence: [email protected]
Received: 11 August 2017; Accepted: 14 September 2017; Published: 1 October 2017
Abstract: Liquid crystals are an integral part of a mature display technology, also establishingthemselves in other applications, such as spatial light modulators, telecommunication technology,photonics, or sensors, just to name a few of the non-display applications. In recent years, there hasbeen an increasing trend to add various nanomaterials to liquid crystals, which is motivated byseveral aspects of materials development. (i) addition of nanomaterials can change and thus tune theproperties of the liquid crystal; (ii) novel functionalities can be added to the liquid crystal; and (iii) theself-organization of the liquid crystalline state can be exploited to template ordered structures or totransfer order onto dispersed nanomaterials. Much of the research effort has been concentrated onthermotropic systems, which change order as a function of temperature. Here we review the otherside of the medal, the formation and properties of ordered, anisotropic fluid phases, liquid crystals,by addition of shape-anisotropic nanomaterials to isotropic liquids. Several classes of materials willbe discussed, inorganic and mineral liquid crystals, viruses, nanotubes and nanorods, as well asgraphene oxide.
Keywords: liquid crystal; lyotropic; inorganic nanoparticle; clay; tobacco mosaic virus (TMV);Deoxyribonucleic acid (DNA); cellulose nanocrystal; nanotube; nanowire; nanorod; graphene;graphene oxide
1. Introduction
Liquid crystals (LC) are a state of matter which is thermodynamically located between theisotropic liquid and the crystalline phase [1,2]. They exhibit flow properties like a liquid and at thesame time partially retain the order of a crystal. For this reason, they possess anisotropic physicalproperties such as their refractive index, dielectric constant, elastic behaviour, or viscosity, just to namea few. But while being partially ordered, LCs also exhibit flow properties like a liquid; they are thusanisotropic fluids. The liquid crystalline state can be brought about via two fundamentally differentways, leading to the two basic classes of LC, thermotropic phases and lyotropic phases. The former isachieved by varying an intensive variable of state, such as temperature or pressure, while the latter isformed through a variation of the concentration of a dopant in an isotropic solvent, often water.
1.1. Thermotropic Liquid Crystals
Thermotropic LCs [3–5] are the ones which are widely known due to their applicational impactin flat screen televisions, laptop and tablet displays, or mobile phones [6]. All these applications relyon the fact that LCs exhibit elastic behaviour and can be addressed via electric or magnetic fields,which changes the orientation of the optic axis, and thus the birefringence. Thermotropic LCs arefurther distinguished by their degree of order, showing further phase transitions within the temperatureregime of the liquid crystalline state. The phase generally observed below the isotropic liquid is called
Nanomaterials 2017, 7, 305; doi:10.3390/nano7100305 www.mdpi.com/journal/nanomaterials
Nanomaterials 2017, 7, 305 2 of 28
nematic, N, and exhibits solely orientational order of the long axis of rod-like molecules, while disk-likemolecules, so called discotic, can show nematic phases as well. The spatial and temporal averageof this long axis is called the director, n. At lower temperatures smectic phases are also observed,which, in addition to orientational order, also exhibit one- or two-dimensional positional order of themolecules centres of mass. Depending on the degree and nature of order, a whole range of differentsmectic phases can be distinguished, with the simplest being the smectic A phase with one-dimensionalpositional order and the director in direction of the smectic layer normal. If the director, which at thesame time is the optic axis of the system, is inclined to the layer normal, one speaks of the smectic Cphase (see Figure 1).
Nanomaterials 2017, 7, 305 2 of 28
temperature regime of the liquid crystalline state. The phase generally observed below the isotropic
liquid is called nematic, N, and exhibits solely orientational order of the long axis of rod‐like
molecules, while disk‐like molecules, so called discotic, can show nematic phases as well. The spatial
and temporal average of this long axis is called the director, n. At lower temperatures smectic phases
are also observed, which, in addition to orientational order, also exhibit one‐ or two‐dimensional
positional order of the molecules centres of mass. Depending on the degree and nature of order, a
whole range of different smectic phases can be distinguished, with the simplest being the smectic A
phase with one‐dimensional positional order and the director in direction of the smectic layer normal.
If the director, which at the same time is the optic axis of the system, is inclined to the layer normal,
one speaks of the smectic C phase (see Figure 1).
Figure 1. Schematic illustration of different liquid crystal (LC) phases observed on heating from the
crystalline state. At first, positional ordering is partially maintained in the smectic phases, SmC and
SmA, together with orientational order of the long molecular axis of often rod‐shaped molecules. On
further heating, positional order is lost at the transition to the nematic phase, which solely exhibits
orientational order. Eventually, at the clearing point, all liquid crystalline order is lost and the
isotropic liquid is reached. For simplicity, only rod‐like molecules are depicted in the figure, but other
molecular shapes exist as well, such as disc‐like or bent‐core materials, which exhibit liquid crystalline
behavior.
These phases are called the fluid smectic phases, with hexatic phases and higher ordered phases
to follow at even lower temperature [7]. The order thus increases with decreasing temperature, while
the symmetry is reduced. An important parameter in the description of LC phases is the orientational
order parameter, S2, which in its simplest description takes the form:
S ⟨ ⟩ ⟨3 1
2⟩ (1)
where P2 is the second Legendre polynomial and ϑ the angle between the long axis of an individual
molecule and the director. The order parameter changes as a function of temperature, a dependence
which is schematically shown in Figure 2.
Figure 1. Schematic illustration of different liquid crystal (LC) phases observed on heating from thecrystalline state. At first, positional ordering is partially maintained in the smectic phases, SmC andSmA, together with orientational order of the long molecular axis of often rod-shaped molecules.On further heating, positional order is lost at the transition to the nematic phase, which solely exhibitsorientational order. Eventually, at the clearing point, all liquid crystalline order is lost and the isotropicliquid is reached. For simplicity, only rod-like molecules are depicted in the figure, but other molecularshapes exist as well, such as disc-like or bent-core materials, which exhibit liquid crystalline behavior.
These phases are called the fluid smectic phases, with hexatic phases and higher ordered phases tofollow at even lower temperature [7]. The order thus increases with decreasing temperature, while thesymmetry is reduced. An important parameter in the description of LC phases is the orientationalorder parameter, S2, which in its simplest description takes the form:
S2 = 〈P2(cosϑ)〉 = 〈3cos2ϑ− 12
〉 (1)
where P2 is the second Legendre polynomial and ϑ the angle between the long axis of an individualmolecule and the director. The order parameter changes as a function of temperature, a dependencewhich is schematically shown in Figure 2.
1.2. Lyotropic Liquid Crystals
Lyotropic LCs [8,9] on the other hand are observed when changing the concentration of a shape-or property anisotropic dispersant in an isotropic solvent. Often, lyotropic phases are observed asa function of concentration of amphiphilic molecules in water or other solvents, as schematicallyshown in Figure 3. Below the critical micelle concentration, cmc, the amphiphiles are molecularlydispersed in the solvent, but at larger concentrations form micelles, which can be of the spherical, diskor rod-like type, depending on the molecular shape. At even higher concentrations, these micellesaggregate to ordered structures and can form hexagonal, cubic or lamellar phases, also of the inverse
Nanomaterials 2017, 7, 305 3 of 28
type. The observed phase diagrams can be quite complex, as they depend largely on concentration,but also on temperature.Nanomaterials 2017, 7, 305 3 of 28
Figure 2. Schematic temperature dependence of the scalar orientational order parameter S. At
elevated temperatures in the isotropic phase, it is S = 0. At the clearing temperature TN‐I, a first order
transition into the nematic phase is observed, accompanied by a discontinuous jump of the order
parameter, generally to S ≈ 0.45, which then increases with decreasing temperature to value of about
S ≈ 0.6–0.7. Further increases in orientational order are observed at the transitions into smectic phases,
albeit much smaller than those between the nematic and the isotropic phase.
1.2. Lyotropic Liquid Crystals
Lyotropic LCs [8,9] on the other hand are observed when changing the concentration of a shape‐
or property anisotropic dispersant in an isotropic solvent. Often, lyotropic phases are observed as a
function of concentration of amphiphilic molecules in water or other solvents, as schematically shown
in Figure 3. Below the critical micelle concentration, cmc, the amphiphiles are molecularly dispersed
in the solvent, but at larger concentrations form micelles, which can be of the spherical, disk or rod‐
like type, depending on the molecular shape. At even higher concentrations, these micelles aggregate
to ordered structures and can form hexagonal, cubic or lamellar phases, also of the inverse type. The
observed phase diagrams can be quite complex, as they depend largely on concentration, but also on
temperature.
Figure 2. Schematic temperature dependence of the scalar orientational order parameter S. At elevatedtemperatures in the isotropic phase, it is S = 0. At the clearing temperature TN-I, a first order transitioninto the nematic phase is observed, accompanied by a discontinuous jump of the order parameter,generally to S ≈ 0.45, which then increases with decreasing temperature to value of about S ≈ 0.6–0.7.Further increases in orientational order are observed at the transitions into smectic phases, albeit muchsmaller than those between the nematic and the isotropic phase.
Nanomaterials 2017, 7, 305 3 of 28
Figure 2. Schematic temperature dependence of the scalar orientational order parameter S. At
elevated temperatures in the isotropic phase, it is S = 0. At the clearing temperature TN‐I, a first order
transition into the nematic phase is observed, accompanied by a discontinuous jump of the order
parameter, generally to S ≈ 0.45, which then increases with decreasing temperature to value of about
S ≈ 0.6–0.7. Further increases in orientational order are observed at the transitions into smectic phases,
albeit much smaller than those between the nematic and the isotropic phase.
1.2. Lyotropic Liquid Crystals
Lyotropic LCs [8,9] on the other hand are observed when changing the concentration of a shape‐
or property anisotropic dispersant in an isotropic solvent. Often, lyotropic phases are observed as a
function of concentration of amphiphilic molecules in water or other solvents, as schematically shown
in Figure 3. Below the critical micelle concentration, cmc, the amphiphiles are molecularly dispersed
in the solvent, but at larger concentrations form micelles, which can be of the spherical, disk or rod‐
like type, depending on the molecular shape. At even higher concentrations, these micelles aggregate
to ordered structures and can form hexagonal, cubic or lamellar phases, also of the inverse type. The
observed phase diagrams can be quite complex, as they depend largely on concentration, but also on
temperature.
Figure 3. Schematic illustration of the phase diagram of an amphiphilic surfactant in an isotropicsolvent, forming lyotropic phases. Crossing the critical micelle concentration, cmc, spherical orcylindrical micelles are formed. At higher surfactant concentrations, these can aggregate to liquidcrystalline phases, namely the hexagonal and the lamellar phase, for increasing concentration.Cubic phases, which are not shown in this figure, can occur at different regimes of the phase diagram.
Similarly, dispersions of shape-anisotropic nanoparticles, like nanorods or nanoplates, in isotropicsolvents can lead to the formation of often nematic lyotropic LC phases. Spontaneous self-organizationis observed, such that the dispersed particles order roughly parallel. The structure is very muchreminiscent of its two-dimensional analogue of floating trees on the surface of a lake. Figure 4 showsone of the first photographs of Spirit Lake after the eruption of the volcano Mt. St. Helens in 1980,
Nanomaterials 2017, 7, 305 4 of 28
taken by Col. David K. Wendt, USAF Reserves, one day after the explosive eruption. Whole forestswere washed into the lake, where the logs collected to form a “nematic” structure with the logs locallypointing approximately in the same direction, minimizing the free volume. This average directionwould then be defined as the director, n, in the case of Figure 4 approximately along the diagonal frombottom left to top right.
Nanomaterials 2017, 7, 305 4 of 28
Figure 3. Schematic illustration of the phase diagram of an amphiphilic surfactant in an isotropic
solvent, forming lyotropic phases. Crossing the critical micelle concentration, cmc, spherical or
cylindrical micelles are formed. At higher surfactant concentrations, these can aggregate to liquid
crystalline phases, namely the hexagonal and the lamellar phase, for increasing concentration. Cubic
phases, which are not shown in this figure, can occur at different regimes of the phase diagram.
Similarly, dispersions of shape‐anisotropic nanoparticles, like nanorods or nanoplates, in
isotropic solvents can lead to the formation of often nematic lyotropic LC phases. Spontaneous self‐
organization is observed, such that the dispersed particles order roughly parallel. The structure is
very much reminiscent of its two‐dimensional analogue of floating trees on the surface of a lake.
Figure 4 shows one of the first photographs of Spirit Lake after the eruption of the volcano Mt. St.
Helens in 1980, taken by Col. David K. Wendt, USAF Reserves, one day after the explosive eruption.
Whole forests were washed into the lake, where the logs collected to form a “nematic” structure with
the logs locally pointing approximately in the same direction, minimizing the free volume. This
average direction would then be defined as the director, n, in the case of Figure 4 approximately along
the diagonal from bottom left to top right.
Figure 4. Logs washed into the Spirit Lake after the eruption of the volcano St. Helens in 1980. The
photograph was taken from a helicopter by Col. David K. Wendt, USAF Reserves, who was one of
the first arriving with a rescue team, one day after the eruption. The logs exhibit the nematic ordering
of rigid rods, as proposed by Lars Onsager. (The length of the picture is estimated to approximately
50 m).
In general, the colloidal suspensions of geometrically anisotropic particles can be observed to
produce a LC phase above a critical concentration. Orientational order arises from particle anisotropy
for an associated critical volume fraction Vcrit depending on the aspect ratio, AR = W/L, of the particle
as Vcrit ≈ 4/AR = 4 L/W, where L is the length and W the width of the nanoparticle. This first theoretical
description was reported by Onsager [10]. His theory is based on the fact that when the concentration
of particles reaches a certain level, the freedom of the particles is constrained and as a result, the
entropy decreases due to overlapping excluded volume of the particles. To compensate for the
entropy decrease, the particles start to acquire orientational order. Thus, above a critical concentration
orientation order is achieved and a nematic LC phase is formed. First experimental reports go back
even further when liquid crystalline behaviour was described for tobacco and tomato mosaic virus
(TMV) [11] and vanadium pentoxide (V2O5) [12] in the early 20th century. Decades later Mourchid et
al., studied colloidal plate‐like charged particles and clay particles to report liquid crystalline
behaviour[13]. In this review, we will try to summarize some of the most interesting experimental
systems and properties of liquid crystalline behaviour from shape‐anisotropic nanoparticles, such as
Figure 4. Logs washed into the Spirit Lake after the eruption of the volcano St. Helens in 1980.The photograph was taken from a helicopter by Col. David K. Wendt, USAF Reserves, who was one ofthe first arriving with a rescue team, one day after the eruption. The logs exhibit the nematic orderingof rigid rods, as proposed by Lars Onsager. (The length of the picture is estimated to approximately50 m).
In general, the colloidal suspensions of geometrically anisotropic particles can be observed toproduce a LC phase above a critical concentration. Orientational order arises from particle anisotropyfor an associated critical volume fraction Vcrit depending on the aspect ratio, AR = W/L, of the particleas Vcrit ≈ 4/AR = 4 L/W, where L is the length and W the width of the nanoparticle. This first theoreticaldescription was reported by Onsager [10]. His theory is based on the fact that when the concentrationof particles reaches a certain level, the freedom of the particles is constrained and as a result, the entropydecreases due to overlapping excluded volume of the particles. To compensate for the entropy decrease,the particles start to acquire orientational order. Thus, above a critical concentration orientation orderis achieved and a nematic LC phase is formed. First experimental reports go back even further whenliquid crystalline behaviour was described for tobacco and tomato mosaic virus (TMV) [11] andvanadium pentoxide (V2O5) [12] in the early 20th century. Decades later Mourchid et al., studiedcolloidal plate-like charged particles and clay particles to report liquid crystalline behaviour [13].In this review, we will try to summarize some of the most interesting experimental systems andproperties of liquid crystalline behaviour from shape-anisotropic nanoparticles, such as inorganicand mineral materials, clays, biological nanoparticles, such as TMV, DNA and cellulose nanocrystals,nanotubes and nanorods, as well as nanoplates and two-dimensional materials, such as graphene,graphene oxide, and reduced graphene oxide.
1.3. Isotropic to Nematic Transition: Maier-Saupe vs. Onsager
Thermotropic LCs are generally described by the Maier-Saupe theory [14–16] , which is basedexclusively on attractive interactions of the van der Waals type, thus induced dipole-induced dipoleinteractions. This works very well, because the rigid, polarizable cores of respective mesogens aremainly of the aromatic type, and steric repulsion can largely be ignored. Through a self-consistentfield equation, which has to be solved numerically, the Maier-Saupe theory predicts the temperature
Nanomaterials 2017, 7, 305 5 of 28
dependence of the (scalar) order parameter S2. At a certain temperature a discontinuous, first ordertransition is observed, at which the order parameter takes a value of S2 = 0.43, continuously increasingwith decreasing temperature, to values of the order of S2 = 0.7–0.8 for rather low temperatures.The Maier-Saupe approach does not yield a satisfactory description of lyotropic LCs though, especiallythose based on colloidal particles as they are discussed in this publication.
Already a decade before the work of Maier and Saupe, Onsager [10] formulated a theory whichwas able to describe the occurrence of a nematic state in colloidal suspensions, and which was largelythe opposite of the approach that Maier and Saupe took later on. Onsager’s theory starts from theassumption that no two particles can occupy the same space, all interactions between suspendedcolloids are in fact repulsive, ignoring any attractive van der Waals forces. Repulsive interactionscan be steric, thus based on excluded volume, or they can be of electrostatic nature. Onsager in factaccounted for electrostatic repulsion as approximating it through an increase in particle size, which waslater detailed more correctly [17,18]. Further simplifications that were made in the first instance, butrelaxed later on (see [18] and references therein), were monodispersity and the use of rigid rod particlesof length L and diameter D. Thus, the aspect ratio D/L plays a paramount role in Onsager’s approach.The description is purely based on maximizing the entropy. The phase behaviour of such a colloidalsuspension is found by the minimization of the free energy F = U − TS, where the internal energyU = 0 for pure steric repulsion, T is the temperature and S the entropy. There are two competingeffects: decreasing the excluded volume increases the free volume and thus the translational entropyof the particles. This on the other hand implies a reduction of the mixing entropy. When the particleconcentration is small the mixing entropy term dominates the phase behaviour and the isotropic phaseis maintained. According to Onsager this is the case for particle volume fractions of Ψiso < 3.3 D/L.At this corresponding particle concentration, a first order transition is observed into the two-phaseregion of coexisting isotropic and nematic phase. This two-phase region terminates into the nematicphase at a particle volume fraction of Ψn > 4.5 D/L. A complete phase diagram for rigid rod cylindersfrom computer simulation by Bolhuis and Frenkel [19] is depicted in Figure 5, which includes not onlythe isotropic and the nematic phase, but also smectic ordering and colloidal crystals.Nanomaterials 2017, 7, 305 6 of 28
Figure 5. Predicted phase diagram from computer simulations of a rigid rod system, showing the
isotropic phase at low aspect ratios and low concentrations, then an Iso + N biphasic region, before a
nematic phase is established. Eventually, also smectic and crystalline phases are observed.
(Reproduced by permission from ref. [19]).
The Onsager model leads to very high values of the orientational order parameter of S2 ≈ 0.8 at
the beginning of the transition into the nematic state, to S2 ≈ 0.95 at larger nanoparticle concentrations.
These values are much larger than those predicted for thermotropic nematic phases by the Maier‐
Saupe theory, but are indeed observed for lyotropic phases from anisotropic colloidal particles, as we
will see below in an example of the TMV. It is believed that the Maier‐Saupe model is more applicable
to systems that are only slightly compressible, thus only show a small change of density at the
transition and smaller orientational order parameters, while the Onsager model is most appropriately
applied to dilute suspensions of particles, showing large changes in density and orientational order
parameter at the transition to the liquid crystalline state.
2. Lyotropic Phases from Nanomaterials
Much effort has been invested into the study of nanoparticles dispersed in LCs. These systems
are mainly studied for their possibility to tune the liquid crystalline properties, such as threshold
voltage Vth, response times τ, viscosity η, dielectric anisotropy Δε, refractive index n, or the
birefringence Δn, which are of importance for applications, especially in the area of LC displays
(LCDs). Nanoparticles employed in such dispersions are often based on inorganic or mineral
materials [20,21] such as dielectric and ferroelectric particles like TiO2 [22] and Sn2P2S6 [23] or BaTiO3
[24,25], gold nanoparticles [26] or carbon based nanotubes [27,28] and graphene oxide [29]. However,
also other nanotubes, like ZnO [30] or semiconducting CdSe [31] have been employed to add
additional functionality to the LC matrix. Not surprisingly, many of the shape‐anisotropic dopants
can also form LC phases by themselves, through dispersion in isotropic solvents. The shape‐
anisotropy may be provided through the nanoparticles being rod‐ or tube‐like, disk‐like or existing
as sheet‐like materials. These are then representing lyotropic LC phases, similar to the ones formed
by amphiphilic molecules dispersed at relatively large concentrations above the cmc in a solvent,
often water.
Having shortly outlined above the main predictions and descriptions expected from the theory
first devised by Lars Onsager in 1949 [10], we can step back in time for a few decades to discuss the
first experimentally observed liquid crystalline systems of this kind.
Figure 5. Predicted phase diagram from computer simulations of a rigid rod system, showingthe isotropic phase at low aspect ratios and low concentrations, then an Iso + N biphasic region,before a nematic phase is established. Eventually, also smectic and crystalline phases are observed.(Reproduced by permission from ref. [19]).
The Onsager model leads to very high values of the orientational order parameter of S2 ≈ 0.8 atthe beginning of the transition into the nematic state, to S2 ≈ 0.95 at larger nanoparticle concentrations.These values are much larger than those predicted for thermotropic nematic phases by the Maier-Saupetheory, but are indeed observed for lyotropic phases from anisotropic colloidal particles, as we will
Nanomaterials 2017, 7, 305 6 of 28
see below in an example of the TMV. It is believed that the Maier-Saupe model is more applicable tosystems that are only slightly compressible, thus only show a small change of density at the transitionand smaller orientational order parameters, while the Onsager model is most appropriately applied todilute suspensions of particles, showing large changes in density and orientational order parameter atthe transition to the liquid crystalline state.
2. Lyotropic Phases from Nanomaterials
Much effort has been invested into the study of nanoparticles dispersed in LCs. These systemsare mainly studied for their possibility to tune the liquid crystalline properties, such as thresholdvoltage Vth, response times τ, viscosity η, dielectric anisotropy ∆ε, refractive index n, or thebirefringence ∆n, which are of importance for applications, especially in the area of LC displays (LCDs).Nanoparticles employed in such dispersions are often based on inorganic or mineral materials [20,21]such as dielectric and ferroelectric particles like TiO2 [22] and Sn2P2S6 [23] or BaTiO3 [24,25], goldnanoparticles [26] or carbon based nanotubes [27,28] and graphene oxide [29]. However, also othernanotubes, like ZnO [30] or semiconducting CdSe [31] have been employed to add additionalfunctionality to the LC matrix. Not surprisingly, many of the shape-anisotropic dopants can also formLC phases by themselves, through dispersion in isotropic solvents. The shape-anisotropy may beprovided through the nanoparticles being rod- or tube-like, disk-like or existing as sheet-like materials.These are then representing lyotropic LC phases, similar to the ones formed by amphiphilic moleculesdispersed at relatively large concentrations above the cmc in a solvent, often water.
Having shortly outlined above the main predictions and descriptions expected from the theoryfirst devised by Lars Onsager in 1949 [10], we can step back in time for a few decades to discuss thefirst experimentally observed liquid crystalline systems of this kind.
2.1. Inorganic and Mineral Liquid Crystals
LC phases from anisotropic, inorganic or mineral crystallites in a solvent, often water, represent asol with particles of colloidal size, i.e., particles with at least one dimension smaller than approximatelyone micrometer. The first studies of such materials go back to 1902 when sols of FeOOH were shown tobecome birefringent under the application of a magnetic field, today known as the Majorana effect [32].A few years later, in 1915–1916, Freundlich [12,33] demonstrated on colloidal dispersions of vanadiumpentoxide, V2O5, the occurrence of birefringence induced by flow alignment of anisotropic crystallites,as well as by applied electric field, and concluded that the mechanism of both effects was the same;application of a force to align the long axis of the anisotropic particles leads to an induced birefringence.Removal of the external stimuli causes a thermal relaxation back to an isotropic distribution of particleswithout any birefringence.
It has been reported repeatedly that freshly prepared V2O5 sols show no birefringence at earlytimes, while only later on, after days, sometimes weeks, anisotropic, birefringent regions develop inthe form of tactoids [34]. These are domains with orientationally ordered rod-like particles as shownschematically in Figure 6a. Their shape is clearly different from the circular domains of thermotropicnematics forming at the isotropic to nematic transition, which exhibits round domains due to theminimization of surface tension. Tactoids, which are shown in microscopic observation in Figure 6b forV2O5, on the other hand exhibit two tips which may be rounded off if flow or electric and magnetic fieldapplication is involved. The growth of tactoids has also been reported for other inorganic sols [20] likeH2WO4 and FeOOH, but also for other systems, like chromonic LCs [35,36] or TMV [37]. For inorganicor mineral sols, nematic liquid crystalline behaviour with purely orientational order has been observed,but also smectic type phases with additional ordering in layers can be found.
Nanomaterials 2017, 7, 305 7 of 28
Nanomaterials 2017, 7, 305 7 of 28
2.1. Inorganic and Mineral Liquid Crystals
LC phases from anisotropic, inorganic or mineral crystallites in a solvent, often water, represent
a sol with particles of colloidal size, i.e., particles with at least one dimension smaller than
approximately one micrometer. The first studies of such materials go back to 1902 when sols of
FeOOH were shown to become birefringent under the application of a magnetic field, today known
as the Majorana effect [32]. A few years later, in 1915–1916, Freundlich [12,33] demonstrated on
colloidal dispersions of vanadium pentoxide, V2O5, the occurrence of birefringence induced by flow
alignment of anisotropic crystallites, as well as by applied electric field, and concluded that the
mechanism of both effects was the same; application of a force to align the long axis of the anisotropic
particles leads to an induced birefringence. Removal of the external stimuli causes a thermal
relaxation back to an isotropic distribution of particles without any birefringence.
It has been reported repeatedly that freshly prepared V2O5 sols show no birefringence at early
times, while only later on, after days, sometimes weeks, anisotropic, birefringent regions develop in
the form of tactoids [34]. These are domains with orientationally ordered rod‐like particles as shown
schematically in Figure 6a. Their shape is clearly different from the circular domains of thermotropic
nematics forming at the isotropic to nematic transition, which exhibits round domains due to the
minimization of surface tension. Tactoids, which are shown in microscopic observation in Figure 6b
for V2O5, on the other hand exhibit two tips which may be rounded off if flow or electric and magnetic
field application is involved. The growth of tactoids has also been reported for other inorganic sols
[20] like H2WO4 and FeOOH, but also for other systems, like chromonic LCs [35,36] or TMV [37]. For
inorganic or mineral sols, nematic liquid crystalline behaviour with purely orientational order has
been observed, but also smectic type phases with additional ordering in layers can be found.
Figure 6. (a) schematic illustration of the director/particle field within a nematic tactoid; and (b)
microscopic photograph of the same for the inorganic LC vanadium pentoxide, V2O5. (Reproduced
by permission from ref. [34]).
The classic inorganic LC is vanadium pentoxide V2O5, which forms a nematic lyotropic phase.
The phase formation is strongly dependent on the preparation conditions of V2O5, which shows small
elongated crystallites or fibre like ribbons. This is related to the aging of virgin preparations over time
periods of hours or even days, depending on temperature, concentration and electrolyte addition.
The aging process, thus the formation process of a nematic phase from the sol, increases in speed for
large crystallite concentrations, higher temperatures, and increased electrolyte addition. The particle
length then increases at practically constant width of approximately 10 nm from several nanometers
to a few micrometers, which is accompanied by a sol‐gel transition [38]. Electric field experiments in
the nematic phase indicate a negative dielectric anisotropy, Δε < 0. A respective temperature‐
concentration stability diagram is shown for V2O5 in Figure 7.
Figure 6. (a) schematic illustration of the director/particle field within a nematic tactoid; and (b) microscopicphotograph of the same for the inorganic LC vanadium pentoxide, V2O5. (Reproduced by permission fromref. [34]).
The classic inorganic LC is vanadium pentoxide V2O5, which forms a nematic lyotropic phase.The phase formation is strongly dependent on the preparation conditions of V2O5, which shows smallelongated crystallites or fibre like ribbons. This is related to the aging of virgin preparations over timeperiods of hours or even days, depending on temperature, concentration and electrolyte addition.The aging process, thus the formation process of a nematic phase from the sol, increases in speed forlarge crystallite concentrations, higher temperatures, and increased electrolyte addition. The particlelength then increases at practically constant width of approximately 10 nm from several nanometers toa few micrometers, which is accompanied by a sol-gel transition [38]. Electric field experiments in thenematic phase indicate a negative dielectric anisotropy, ∆ε < 0. A respective temperature-concentrationstability diagram is shown for V2O5 in Figure 7.Nanomaterials 2017, 7, 305 8 of 28
Figure 7. Summary of the phase behaviour of V2O5 in dependence on the volume fraction of the
dispersed inorganic crystallites, as determined by Nuclear Magnetic Resonance, NMR. (Reproduced
by permission from ref. [39]).
Similar behaviour as for vanadium pentoxide is observed for aluminium oxyhydroxide, AlOOH,
with tactoids of nematic order forming. When these tactoids join, a Schlieren texture with typical
disclinations is developed, as shown in Figure 8a [40]. Another nanomaterial to mention is uranyl
fluoride UO2F2. This exhibits a nematic phase in a solution of acetone and heavy water, as
demonstrated by nuclear magnetic resonance (NMR) experiments [41].
Figure 8. (a) Nematic Schlieren texture of AlOOH (reproduced by permission from ref. [40]); and (b)
nematic thread‐like texture of Li2Mo6Se6 (reproduced by permission from ref. [42]), scale unknown.
A general class of inorganic nematic LCs is M2Mo6X6 with the metal M = Li, Na, K from the
alkalimetal group 1, and X = Se, Te from the chalcogens group 16. Also here we observe crystallite
lengths of a few micrometers and the formation of Schlieren textures or thread‐like textures [42], as
shown in Figure 8b, clearly identifying nematic behaviour, in this case with N‐methylformamide as
solvent. The phase separation into a nematic and an isotropic component is observed after several
hours to months.
As mentioned above, also the formation of smectic phases can be observed. This has been
demonstrated for example for FeOOH by the microscopic observation of step textures indicating
smectic layering [43], and for tungstic acid H2WO4 (WO3∙H2O). A detailed overview about
preparation methods and conditions of elongated inorganic particles and their LC structures and
phases can be found in a review article by Sonin [20].
0.5 0.7 1.5 4 Φ %
Isot
ropi
c
Bip
hasi
c
Nem
atic
(uni
axia
l)
Nem
atic
(uni
axia
l)
Nem
atic
(bia
xial
)
fluid suspensions gels
T (K)
350
300
Figure 7. Summary of the phase behaviour of V2O5 in dependence on the volume fraction of thedispersed inorganic crystallites, as determined by Nuclear Magnetic Resonance, NMR. (Reproduced bypermission from ref. [39]).
Similar behaviour as for vanadium pentoxide is observed for aluminium oxyhydroxide, AlOOH,with tactoids of nematic order forming. When these tactoids join, a Schlieren texture with typical
Nanomaterials 2017, 7, 305 8 of 28
disclinations is developed, as shown in Figure 8a [40]. Another nanomaterial to mention isuranyl fluoride UO2F2. This exhibits a nematic phase in a solution of acetone and heavy water,as demonstrated by nuclear magnetic resonance (NMR) experiments [41].
Nanomaterials 2017, 7, 305 8 of 28
Figure 7. Summary of the phase behaviour of V2O5 in dependence on the volume fraction of the
dispersed inorganic crystallites, as determined by Nuclear Magnetic Resonance, NMR. (Reproduced
by permission from ref. [39]).
Similar behaviour as for vanadium pentoxide is observed for aluminium oxyhydroxide, AlOOH,
with tactoids of nematic order forming. When these tactoids join, a Schlieren texture with typical
disclinations is developed, as shown in Figure 8a [40]. Another nanomaterial to mention is uranyl
fluoride UO2F2. This exhibits a nematic phase in a solution of acetone and heavy water, as
demonstrated by nuclear magnetic resonance (NMR) experiments [41].
Figure 8. (a) Nematic Schlieren texture of AlOOH (reproduced by permission from ref. [40]); and (b)
nematic thread‐like texture of Li2Mo6Se6 (reproduced by permission from ref. [42]), scale unknown.
A general class of inorganic nematic LCs is M2Mo6X6 with the metal M = Li, Na, K from the
alkalimetal group 1, and X = Se, Te from the chalcogens group 16. Also here we observe crystallite
lengths of a few micrometers and the formation of Schlieren textures or thread‐like textures [42], as
shown in Figure 8b, clearly identifying nematic behaviour, in this case with N‐methylformamide as
solvent. The phase separation into a nematic and an isotropic component is observed after several
hours to months.
As mentioned above, also the formation of smectic phases can be observed. This has been
demonstrated for example for FeOOH by the microscopic observation of step textures indicating
smectic layering [43], and for tungstic acid H2WO4 (WO3∙H2O). A detailed overview about
preparation methods and conditions of elongated inorganic particles and their LC structures and
phases can be found in a review article by Sonin [20].
0.5 0.7 1.5 4 Φ %
Isot
ropi
c
Bip
hasi
c
Nem
atic
(uni
axia
l)
Nem
atic
(uni
axia
l)
Nem
atic
(bia
xial
)
fluid suspensions gels
T (K)
350
300
Figure 8. (a) Nematic Schlieren texture of AlOOH (reproduced by permission from ref. [40]);and (b) nematic thread-like texture of Li2Mo6Se6 (reproduced by permission from ref. [42]),scale unknown.
A general class of inorganic nematic LCs is M2Mo6X6 with the metal M = Li, Na, K from thealkalimetal group 1, and X = Se, Te from the chalcogens group 16. Also here we observe crystallitelengths of a few micrometers and the formation of Schlieren textures or thread-like textures [42],as shown in Figure 8b, clearly identifying nematic behaviour, in this case with N-methylformamide assolvent. The phase separation into a nematic and an isotropic component is observed after severalhours to months.
As mentioned above, also the formation of smectic phases can be observed. This has beendemonstrated for example for FeOOH by the microscopic observation of step textures indicatingsmectic layering [43], and for tungstic acid H2WO4 (WO3·H2O). A detailed overview about preparationmethods and conditions of elongated inorganic particles and their LC structures and phases can befound in a review article by Sonin [20].
2.2. Clay Based Liquid Crystals
Clays are obviously a very closely related topic, as they are aluminosilicates, rock-formingminerals. They generally exist in powder form with layered structures made of plates or platelets.This structure is also the reason why they easily swell in the presence of water or other isotropicsolvents [44], which are situated between the sheets. Similar to the hard-rod model of Onsager andits later variants, such a model can also be formulated for hard disks, and computer simulations byVeerman and Frenkel indicate a stable nematic and a columnar phase [45].
2.2.1. Bentonite
Already Langmuir [46] in 1938 observed that a bentonite clay suspension phase separates into anisotropic region and an anisotropic, birefringent region, which in fact turns out to be a gel. Only muchlater it was realized that at very low concentrations a real LC phase and not a gel could be produced.Bentonite clay is used in a number of diverse applications from food additives to cosmetics, facialmasks, and nutritional products, all the way to cat litter and drilling mud. The general application ofthe liquid crystalline phase may be found in the ordering of inorganic nanosheets for possible futureapplications in sensors or energy storage. Hybrids with dyes could be used for photosensitization, orin optical materials for plasmonic nanostructures.
Nanomaterials 2017, 7, 305 9 of 28
2.2.2. Laponite
Laponite, a synthetic clay used in personal care products to modify rheological properties, or asgelator in construction work and artware, also exhibits a similar behaviour. Some exemplary texturesof concentrated solutions are shown in Figure 9 for both materials [47]. These are typical nematictextures from disk-like platelets.
Nanomaterials 2017, 7, 305 9 of 28
2.2. Clay Based Liquid Crystals
Clays are obviously a very closely related topic, as they are aluminosilicates, rock‐forming
minerals. They generally exist in powder form with layered structures made of plates or platelets.
This structure is also the reason why they easily swell in the presence of water or other isotropic
solvents [44], which are situated between the sheets. Similar to the hard‐rod model of Onsager and
its later variants, such a model can also be formulated for hard disks, and computer simulations by
Veerman and Frenkel indicate a stable nematic and a columnar phase [45].
2.2.1. Bentonite
Already Langmuir [46] in 1938 observed that a bentonite clay suspension phase separates into
an isotropic region and an anisotropic, birefringent region, which in fact turns out to be a gel. Only
much later it was realized that at very low concentrations a real LC phase and not a gel could be
produced. Bentonite clay is used in a number of diverse applications from food additives to cosmetics,
facial masks, and nutritional products, all the way to cat litter and drilling mud. The general
application of the liquid crystalline phase may be found in the ordering of inorganic nanosheets for
possible future applications in sensors or energy storage. Hybrids with dyes could be used for
photosensitization, or in optical materials for plasmonic nanostructures.
2.2.2. Laponite
Laponite, a synthetic clay used in personal care products to modify rheological properties, or as
gelator in construction work and artware, also exhibits a similar behaviour. Some exemplary textures
of concentrated solutions are shown in Figure 9 for both materials [47]. These are typical nematic
textures from disk‐like platelets.
Figure 9. Nematic texture of different clays, (a) bentonite and (b) laponite (reproduced by permission
from ref. [47]). The image width is approximately 1 mm for (a) and 500 μm for (b).
Applications of the liquid crystalline phase could again be found in the ordering of inorganic
nanosheets by templating LC order for sensors and optical materiuals, or in the application of
cosmetics.
2.2.3. Imogolite
Imogolite is a natural hydrated aluminium silicate found in volcanic ash, which can be dispersed
in water under acidic conditions. The observed phase separation between isotropic and anisotropic,
birefringent liquid is practically temperature independent [48,49]. Imogolite forms a tubular structure
and exhibits a texture reminiscent of a cholesteric fingerprint organisation, demonstrated in Figure
10.
Figure 9. Nematic texture of different clays, (a) bentonite and (b) laponite (reproduced by permissionfrom ref. [47]). The image width is approximately 1 mm for (a) and 500 µm for (b).
Applications of the liquid crystalline phase could again be found in the ordering of inorganicnanosheets by templating LC order for sensors and optical materiuals, or in the application of cosmetics.
2.2.3. Imogolite
Imogolite is a natural hydrated aluminium silicate found in volcanic ash, which can be dispersedin water under acidic conditions. The observed phase separation between isotropic and anisotropic,birefringent liquid is practically temperature independent [48,49]. Imogolite forms a tubular structureand exhibits a texture reminiscent of a cholesteric fingerprint organisation, demonstrated in Figure 10.Nanomaterials 2017, 7, 305 10 of 28
Figure 10. So‐called “fingerprint” texture of imogolite, exhibiting an equidistant line pattern, which
is somewhat reminiscent of a cholesteric fingerprint texture. Nevertheless, imogolite does not exhibit
any chiral constituents, so that the stripe pattern is not indicative of a cholesteric phase. (Reproduced
by permission from ref. [49]).
It does not seem to be quite clear why a chiral texture is observed, while the tubes do not seem
to exhibit any chirality. Also, the equidistant striped pattern disappears for increasing concentrations
of imogolite. Possibly, the texture is related to a banded texture, as it can also be observed for some
nematic gels formed from molecular ribbons.
2.3. Biological Nanoparticles
Biological or natural fibres, in fact all biological anisotropic nanoparticles, are potential
candidates for exhibiting lyotropic liquid crystalline behaviour. For example, cellulose and its
derivatives shows cholesteric lyotropic phases in many isotropic solvents [50], and so do cellulose
nanocrystals in water [51]. Fibrous or filamentous proteins for example of the collagen family, or
muscle proteins like actin can for LC phases. The variety of liquid crystalline behaviour of nucleic
acidsDeoxyribonucleic acid (DNA) or ribonuceic acid (RNA) is multiple, and also related rod‐like
structures, such as the TMV, has long been shown to exhibit mesophases.
2.3.1. Tobacco Mosaic Virus (TMV)
The TMV, is a single‐stranded RNA virus which affects mainly tobacco plants, but also various
other plants, visible by a discolouration of the leaves in a mosaic like pattern. Back in the 1930s it was
presumably the first ever virus to be discovered. The TMV can be seen as a natural prototype of a
ridged rod. It is very straight and rod‐like in structure with a constant diameter of approximately 18
nm and an often uniform length of about 300 nm, thus an aspect ratio of the order of D/L ≈ 15 (see
Figure 11a). It is thus ideally suited as a test system for the Onsager theory.
Figure 10. So-called “fingerprint” texture of imogolite, exhibiting an equidistant line pattern, which issomewhat reminiscent of a cholesteric fingerprint texture. Nevertheless, imogolite does not exhibit anychiral constituents, so that the stripe pattern is not indicative of a cholesteric phase. (Reproduced bypermission from ref. [49]).
Nanomaterials 2017, 7, 305 10 of 28
It does not seem to be quite clear why a chiral texture is observed, while the tubes do not seem toexhibit any chirality. Also, the equidistant striped pattern disappears for increasing concentrationsof imogolite. Possibly, the texture is related to a banded texture, as it can also be observed for somenematic gels formed from molecular ribbons.
2.3. Biological Nanoparticles
Biological or natural fibres, in fact all biological anisotropic nanoparticles, are potential candidatesfor exhibiting lyotropic liquid crystalline behaviour. For example, cellulose and its derivatives showscholesteric lyotropic phases in many isotropic solvents [50], and so do cellulose nanocrystals inwater [51]. Fibrous or filamentous proteins for example of the collagen family, or muscle proteins likeactin can for LC phases. The variety of liquid crystalline behaviour of nucleic acidsDeoxyribonucleicacid (DNA) or ribonuceic acid (RNA) is multiple, and also related rod-like structures, such as the TMV,has long been shown to exhibit mesophases.
2.3.1. Tobacco Mosaic Virus (TMV)
The TMV, is a single-stranded RNA virus which affects mainly tobacco plants, but also variousother plants, visible by a discolouration of the leaves in a mosaic like pattern. Back in the 1930s it waspresumably the first ever virus to be discovered. The TMV can be seen as a natural prototype of a ridgedrod. It is very straight and rod-like in structure with a constant diameter of approximately 18 nm andan often uniform length of about 300 nm, thus an aspect ratio of the order of D/L ≈ 15 (see Figure 11a).It is thus ideally suited as a test system for the Onsager theory.Nanomaterials 2017, 7, 305 11 of 28
Figure 11. (a) Electron microscopic photograph of tobacco mosaic viruses, TMV, indicating an aspect
ratio of approximately 15, and a relatively monodisperse length distribution. The scale bar indicates
0.2 μm. Part (b) depicts the concentration dependence of the orientational order parameter S, as
determined by small angle x‐ray scattering, SAXS. The order parameter is zero in the isotropic liquid,
and increases from about S ≈ 0.7 to S ≈ 0.95 through the biphasic region and into the regime of the
nematic phase at large concentrations. (part (a) is reproduced from wikimedia commons, with no
author name supplied, while part (b) is reproduced by permission from ref. [52]).
And indeed, in 1936 a first publication [11] reported liquid crystalline behaviour for TMVs at
certain concentrations, through the growth of tactoids and with corresponding x‐ray investigations
(figure with textures). Most likely independently derived, a similar result was reported by Rischkov
and Smirnova [53] about five years later. More detailed small angle X‐ray scattering (SAXS)
experiments were carried out by Oldenbourg and co‐workers [52] who produced a small angle
diffraction pattern for a magnetic field aligned nematic phase, which allowed the determination of
the orientational order distribution function, and thus the scalar order parameter S. The latter
indicated a transition from isotropic through a two‐phase region into a nematic phase with increasing
TMV concentration. The order parameter in the nematic phase changed from about S = 0.75 at the
transition to S = 0.95 for high concentrations, which is in accordance with Onsager’s predictions
(Figure 11b).
Fraden and co‐workers [54] performed a thorough investigation of TMV solutions, measuring
the birefringence as a function of concentration, temperature, ionic strength and polydispersity. They
observed the appearance of spatial and angular local order for increasing concentration until an
isotropic to nematic phase transition is accomplished via an Iso‐N two‐phase regime. From their
measurements, together with a modified Onsager approach, they concluded that the nematic phase
stability of TMV suspensions is mainly caused by electrostatic repulsion, rather than attractive (van
der Waals) forces between the TMV rods. This indicates a transition due to excluded volume effects
as generally predicted by Onsager, whose theory ignores attractive forces all together and is purely
based on (steric) repulsion interactions. The complete phase diagram of the tobacco mosaic virus was
later predicted from theory and simulations by Graf and Löwen [55], who did not only describe the
isotropic to nematic transition with its two‐phase region, but also further transitions into smectic
phases and colloidal crystal phases.
Tobacco mosaic viruses in the nematic state have also been suggested for the design of silica‐
TMV mesostructures and nanoparticles, i.e., using the TMV as a template in the synthesis of inorganic
frameworks with ordered porosity in order to produce more complicated structures. Fowler et al. [56]
describe a method where ordered TMVs in the nematic arrangement are silicated and then thermally
removed via biodegradation. This led to silica structures with hexagonally ordered nano‐channels of
a diameter of approximately 20 nm. The authors also synthesized silica nanoparticles with radially
arranged nano‐channels. A range of further approaches to use TMV LCs as templates for the
controlled synthesis of ordered structures have since been pointed out (see references [57,58] and
Figure 11. (a) Electron microscopic photograph of tobacco mosaic viruses, TMV, indicating anaspect ratio of approximately 15, and a relatively monodisperse length distribution. The scale barindicates 0.2 µm. Part (b) depicts the concentration dependence of the orientational order parameterS, as determined by small angle x-ray scattering, SAXS. The order parameter is zero in the isotropicliquid, and increases from about S ≈ 0.7 to S ≈ 0.95 through the biphasic region and into the regime ofthe nematic phase at large concentrations. (part (a) is reproduced from wikimedia commons, with noauthor name supplied, while part (b) is reproduced by permission from ref. [52]).
And indeed, in 1936 a first publication [11] reported liquid crystalline behaviour for TMVs atcertain concentrations, through the growth of tactoids and with corresponding x-ray investigations(figure with textures). Most likely independently derived, a similar result was reported by Rischkov andSmirnova [53] about five years later. More detailed small angle X-ray scattering (SAXS) experimentswere carried out by Oldenbourg and co-workers [52] who produced a small angle diffraction patternfor a magnetic field aligned nematic phase, which allowed the determination of the orientationalorder distribution function, and thus the scalar order parameter S. The latter indicated a transitionfrom isotropic through a two-phase region into a nematic phase with increasing TMV concentration.
Nanomaterials 2017, 7, 305 11 of 28
The order parameter in the nematic phase changed from about S = 0.75 at the transition to S = 0.95 forhigh concentrations, which is in accordance with Onsager’s predictions (Figure 11b).
Fraden and co-workers [54] performed a thorough investigation of TMV solutions, measuringthe birefringence as a function of concentration, temperature, ionic strength and polydispersity.They observed the appearance of spatial and angular local order for increasing concentration untilan isotropic to nematic phase transition is accomplished via an Iso-N two-phase regime. From theirmeasurements, together with a modified Onsager approach, they concluded that the nematic phasestability of TMV suspensions is mainly caused by electrostatic repulsion, rather than attractive (vander Waals) forces between the TMV rods. This indicates a transition due to excluded volume effectsas generally predicted by Onsager, whose theory ignores attractive forces all together and is purelybased on (steric) repulsion interactions. The complete phase diagram of the tobacco mosaic viruswas later predicted from theory and simulations by Graf and Löwen [55], who did not only describethe isotropic to nematic transition with its two-phase region, but also further transitions into smecticphases and colloidal crystal phases.
Tobacco mosaic viruses in the nematic state have also been suggested for the design of silica-TMVmesostructures and nanoparticles, i.e., using the TMV as a template in the synthesis of inorganicframeworks with ordered porosity in order to produce more complicated structures. Fowler et al. [56]describe a method where ordered TMVs in the nematic arrangement are silicated and then thermallyremoved via biodegradation. This led to silica structures with hexagonally ordered nano-channels ofa diameter of approximately 20 nm. The authors also synthesized silica nanoparticles with radiallyarranged nano-channels. A range of further approaches to use TMV LCs as templates for the controlledsynthesis of ordered structures have since been pointed out (see references [57,58] and referencestherein). It is worth noting, that while the TMV produces nematic ordering, also cholesteric [59] andsmectic phases [60] have been observed for different virus suspensions.
2.3.2. DNA
Since the identification of the double helix structure of DNA by Watson and Crick in 1953, basedon the X-ray information provided by Gosling and Franklin, this biopolymer has attracted muchinterest, not only as the carrier of genetic information, but also as a molecule to probe elasticity, as acomponent in hybrid materials or in bio-nanotechnology. The DNA structure is composed of twohelical biopolymers coiled around each other, bound together by hydrogen bonds. Along its length,the structure of DNA is quite flexible and dynamic. The double helix is about 2 nm wide and has apitch of 3.4 nm, while a DNA molecule can contain millions of base pairs and can have a length in theorder of millimetres, and even tens of millimetres.
The fact that DNA can exhibit liquid crystalline phases has been realized quite some time ago,and there has been an excellent review article of the earlier work until about twenty years ago byLivolant and Leforestier [61]. In 1988, Strzelecka et al. [62] reported on the multiple LC phases of DNAat higher concentrations. Through NMR line width experiments on solutions of DNA fragments ofapproximately 50 nm in average length, corresponding to 146 base pairs, the isotropic, cholesteric andsmectic-like phases, together with their respective two-phase regions iso + chol and chol + smectic wereidentified as a function of increasing DNA concentration. Furthermore, typical textures were shown,similar to the ones of Figure 12. Already one year later, it was shown by Livolant et al. [63] that the highconcentration phase is of the columnar type, and later, by the same authors, it was further demonstratedby electron microscopy of typical double twist cylinders, that the often called “pre-cholesteric” phasewas in fact a Blue Phase [64]. The structure and evolution of the liquid crystalline phases of DNA wasalso confirmed by polarization sensitive two-photon fluorescence microscopy on respectively labelledDNA molecules.
Nanomaterials 2017, 7, 305 12 of 28
Nanomaterials 2017, 7, 305 12 of 28
references therein). It is worth noting, that while the TMV produces nematic ordering, also cholesteric
[59] and smectic phases [60] have been observed for different virus suspensions.
2.3.2. DNA
Since the identification of the double helix structure of DNA by Watson and Crick in 1953, based
on the X‐ray information provided by Gosling and Franklin, this biopolymer has attracted much
interest, not only as the carrier of genetic information, but also as a molecule to probe elasticity, as a
component in hybrid materials or in bio‐nanotechnology. The DNA structure is composed of two
helical biopolymers coiled around each other, bound together by hydrogen bonds. Along its length,
the structure of DNA is quite flexible and dynamic. The double helix is about 2 nm wide and has a
pitch of 3.4 nm, while a DNA molecule can contain millions of base pairs and can have a length in
the order of millimetres, and even tens of millimetres.
The fact that DNA can exhibit liquid crystalline phases has been realized quite some time ago,
and there has been an excellent review article of the earlier work until about twenty years ago by
Livolant and Leforestier [61]. In 1988, Strzelecka et al. [62] reported on the multiple LC phases of
DNA at higher concentrations. Through NMR line width experiments on solutions of DNA fragments
of approximately 50 nm in average length, corresponding to 146 base pairs, the isotropic, cholesteric
and smectic‐like phases, together with their respective two‐phase regions iso + chol and chol + smectic
were identified as a function of increasing DNA concentration. Furthermore, typical textures were
shown, similar to the ones of Figure 12. Already one year later, it was shown by Livolant et al. [63]
that the high concentration phase is of the columnar type, and later, by the same authors, it was
further demonstrated by electron microscopy of typical double twist cylinders, that the often called
“pre‐cholesteric” phase was in fact a Blue Phase [64]. The structure and evolution of the liquid
crystalline phases of DNA was also confirmed by polarization sensitive two‐photon fluorescence
microscopy on respectively labelled DNA molecules.
Figure 12. Typical textures observed for the lyotropic phases of relatively long DNA with increasing
concentration. (a) Cholesteric fingerprint texture with equidistant line pattern due to the helical
superstructure of the phase. The distance between two dark lines is equal to identity period of half
the pitch, P/2; (b) At the transition from the cholesteric to the columnar hexagonal phase; and (c)
within the fully developed columnar hexagonal phase. The scale bars are 10 μm. (Reproduced by
permission from ref. [61]).
In recent years, the attention of LC forming DNA has slightly shifted towards rather short, more
controllable and defined molecules. According to Onsager theory only volume fractions of Ψ > ΨIso‐
N ≈ 4D/L should be able to exhibit a nematic phase. Molecules with aspect ratios L/D < 4 should not
show LC phase formation for any concentrations. Nonetheless, Nakata et al. [65] have demonstrated
the 6–20 base pair DNA can in fact exhibit cholesteric and columnar phases via end‐to‐end adhesion
and stacking of oligomers into polydisperse, rod‐shaped, semi‐rigid aggregates, which then act like
colloidal particles forming LC phases. This mechanism of self‐assembly of short DNA duplexes to
form building blocks for cholesteric LCs was detailed later on in subsequent publications [66]. In the
Figure 12. Typical textures observed for the lyotropic phases of relatively long DNA with increasingconcentration. (a) Cholesteric fingerprint texture with equidistant line pattern due to the helicalsuperstructure of the phase. The distance between two dark lines is equal to identity period of half thepitch, P/2; (b) At the transition from the cholesteric to the columnar hexagonal phase; and (c) withinthe fully developed columnar hexagonal phase. The scale bars are 10 µm. (Reproduced by permissionfrom ref. [61]).
In recent years, the attention of LC forming DNA has slightly shifted towards rather short,more controllable and defined molecules. According to Onsager theory only volume fractions ofΨ > ΨIso-N ≈ 4D/L should be able to exhibit a nematic phase. Molecules with aspect ratios L/D < 4should not show LC phase formation for any concentrations. Nonetheless, Nakata et al. [65] havedemonstrated the 6–20 base pair DNA can in fact exhibit cholesteric and columnar phases viaend-to-end adhesion and stacking of oligomers into polydisperse, rod-shaped, semi-rigid aggregates,which then act like colloidal particles forming LC phases. This mechanism of self-assembly of shortDNA duplexes to form building blocks for cholesteric LCs was detailed later on in subsequentpublications [66]. In the original work on short DNA molecules, fully complimentary sequences wereemployed, which was then extended by Zanchetta et al. [66,67] to partially overlapping sequencesand even to LC ordering in systems with a large amount of randomness provided by random DNAsequences, when Bellini et al. [68] discussed liquid crystalline behaviour observed between the isotropicphase of short oligomers and isotropic gels of long random DNA strands. Very recently, this work onvery short DNA has been extended to systems with only four base pairs to still show liquid crystallinebehaviour via aggregation [69]. An interesting effect for short DNA LCs has been observed for varyingconcentration, as right handed DNA macromolecules can produce left handed cholesteric structures atlow concentration and right handed ones at larger concentrations, passing a structurally non-chiralnematic state as a function of concentration [70]. This is very similar to the temperature inducedtwist inversion phenomena observed in thermotropic LCs [71–76] where in the lyotropic systems theconcentrations mimics the role of temperature as the variable of state.
DNA finds its applications in LC research and possible future technology for example in theuse as chiral dopants to control the pitch of cholesteric phases [77], as biosensors [78] and even asalignment layers for LC applications [79].
2.3.3. Cellulose Nanocrystals
Cellulose is composed of polysaccharides, linear chains of hundreds to thousands of sugar units.It is a natural polymer which occurs in abundance in nature and has one of the most inexhaustiblesupplies. Its attractiveness for materials and composites lies in the fact that cellulose is regenerative,easily biodegradable, and optical properties have been studied in great detail. It has long been knownthat cellulose derivatives in suitable solvents form lyotropic LCs, often with a rather short pitch in thevisible range of the spectrum [50,80]. Their phase behaviour and optical properties have been studies
Nanomaterials 2017, 7, 305 13 of 28
in great detail, also with respect to cellulose-based derivatives. Cellulose nanocrystals as hard rodsystems seem to have attracted increasing interest only over recent years.
Like many of the other hard-rod nano-materials we have discussed above, also cellulosenanocrystals form lyotropic LCs in accordance with the predictions of Onsager’s model. Also inthis case tactoids may be observed in microscopy of cellulose nanocrystal/water systems. Only here,we are dealing with chiral constituent molecules, such that a chiral nematic or cholesteric phase isobserved in contrast to the nematic phases. The cellulose nanocrystals have an average dimension ofabout 100 nm in length, 25 nm in width and approximately 10 nm in height (Figure 13a). They canthus be seen as lath-like nanoparticles [81]. In the lyotropic cholesteric phase, these nanocrystalsorient with their long axis parallel to an average direction, which changes with a continuous twistwhen proceeding in the direction of the short axis, perpendicular to the long axis. Thus a helicalsuperstructure is formed. For increasing concentration of cellulose nanocrystals, the volume fractionof the anisotropic phase increases, as expected (Figure 13b,d). The observed pitch is generally of theorder of 10–20 µm, decreasing with increasing cellulose nanocrystal concentration and increasing withnanocrystal length or aspect ratio [82]. The helical superstructure and pitch is clearly manifested alsoin the observed textures between crossed polarizers, as an equidistant pattern of dark lines, called afingerprint texture (Figure 13c).Nanomaterials 2017, 7, 305 14 of 28
Figure 13. Summary of the basic lyotropic liquid crystalline behaviour of cellulose nanocrystals. (a)
The nanocrystals of cellulose are composed of chiral polymers and exhibit a length of about 100 nm
and lateral dimensions between 10–20 nm, thus aspect ratios in the order of 10; (b) For concentration
up to about 3% the isotropic phase is observed, which changes to a biphasic region in which the liquid
crystalline volume fraction increases with increasing concentration until at about 10–14% a
completely anisotropic phase is observed; (c) Since the building blocks are chiral, cellulose
nanocrystal LCs exhibit a cholesteric phase, as demonstrated by the fingerprint texture. The helical
pitch is in the order of 10–20 μm; (d) Volume fraction of the anisotropic phase as a concentration of
cellulose nanocrystals. (The different parts of the figure were reproduced by permission from ref. [83]).
The general phase behaviour of cellulose nanocrystals in water has been discussed on several
occasions [84–88] and results appear to be non‐contradictory: below about 3 vol % the solution is
completely isotropic. It is followed by a two‐phase region of isotropic + LC in the regime of 3–10 vol %
nanocrystalline cellulose, and reaches a completely liquid crystalline state at 10–14 vol %. Above 14
vol % a gel is formed [84]. In the two‐phase region the anisotropic volume fraction increases with
increasing cellulose nanocrystal concentration.
One of the most prominent material parameters of lyotropic cellulose nanocrystal dispersions is
the viscosity, which generally increases for increasing concentration and aspect ratio [89]. Also
studies relating to the ionic strength have been reported [90], and further the influences of
temperature and humidity [91] for dried cellulose nanocrystal films obtained from lyotropic LCs.
Such materials are produced as multifunctional thin films for applications, for example in
varying the wavelength of selective reflection across the film diameter, a property which is due to a
varying concentration of cellulose nanocrystals [92]. Also the production of plasmonic films of
cellulose nanocrystal cholesterics incorporating gold [93,94] or silver [95] nano‐rods has been
reported. Such composite films display tuneable chiroptic properties.
Figure 13. Summary of the basic lyotropic liquid crystalline behaviour of cellulose nanocrystals.(a) The nanocrystals of cellulose are composed of chiral polymers and exhibit a length of about 100 nmand lateral dimensions between 10–20 nm, thus aspect ratios in the order of 10; (b) For concentrationup to about 3% the isotropic phase is observed, which changes to a biphasic region in which the liquidcrystalline volume fraction increases with increasing concentration until at about 10–14% a completelyanisotropic phase is observed; (c) Since the building blocks are chiral, cellulose nanocrystal LCs exhibita cholesteric phase, as demonstrated by the fingerprint texture. The helical pitch is in the order of10–20 µm; (d) Volume fraction of the anisotropic phase as a concentration of cellulose nanocrystals.(The different parts of the figure were reproduced by permission from ref. [83]).
Nanomaterials 2017, 7, 305 14 of 28
The general phase behaviour of cellulose nanocrystals in water has been discussed on severaloccasions [84–88] and results appear to be non-contradictory: below about 3 vol % the solutionis completely isotropic. It is followed by a two-phase region of isotropic + LC in the regime of3–10 vol % nanocrystalline cellulose, and reaches a completely liquid crystalline state at 10–14 vol %.Above 14 vol % a gel is formed [84]. In the two-phase region the anisotropic volume fraction increaseswith increasing cellulose nanocrystal concentration.
One of the most prominent material parameters of lyotropic cellulose nanocrystal dispersions isthe viscosity, which generally increases for increasing concentration and aspect ratio [89]. Also studiesrelating to the ionic strength have been reported [90], and further the influences of temperature andhumidity [91] for dried cellulose nanocrystal films obtained from lyotropic LCs.
Such materials are produced as multifunctional thin films for applications, for example invarying the wavelength of selective reflection across the film diameter, a property which is dueto a varying concentration of cellulose nanocrystals [92]. Also the production of plasmonic films ofcellulose nanocrystal cholesterics incorporating gold [93,94] or silver [95] nano-rods has been reported.Such composite films display tuneable chiroptic properties.
2.3.4. Active Liquid Crystals
At this point it is worthwhile to also mention active LCs as an emerging topic of pronouncedinterest. In general, active matter [96,97] resembles a system composed of many active constituents,each of which consumes energy or converts one form of energy to motion or the exertion of a mechanicalforce. They are therefore intrinsically non-equilibrium systems. Examples are found in a wide varietyof soft matter and biological systems, such as swarms of insects, flocks of birds, school of fish, or closerto the topic of this review, bacteria or microtubules. Systems are often of biological origin, but morelately also synthetically derived. They generally show dynamic self-organization and self-propellation.Active LCs have recently become a topic of much increasing interest [98].
In addition, as liquid crystalline systems, active matter is a non-equilibrium system, like cellsfor example, assemblies of many molecular units working cooperatively to undergo processes likemotion, cell division or replication. These systems are actively driven, thus consume energy, which hasto be provided from the surrounding. They can thus not be described by equilibrium statistics.The group of Dogic [99] have demonstrated an interesting example of active matter by the use ofstretchable microtubule bundles. They showed that active matter can be hierarchically assembled tomimic LCs, but also polymer gels and emulsions by forming an active percolation network at not toosmall microtubule concentrations. The demonstrated active LCs form the typical s = ±1/2 defects,indicating nematic order with defects that show spatiotemporal dynamics. If one balances the ratesof defect creation and defect annihilation, one can achieve steady-state streaming dynamics, whichcontinues over prolonged time scales. This is a behaviour qualitatively different from non-activenematics, as for the latter the defect dynamics follows particular scaling laws for creation [100] andannihilation [101,102] of topological defects. The group of Lavrentovich [103] used a somewhatdifferent active liquid crystal medium. They dispersed motile bacteria, bacillus subtilis, in a liquidcrystalline host and demonstrated that the nematic topological defects can be used to commandactive matter. By employing a variety of different director fields, they showed that the bacteriasenses differences in director field deformation. It was observed, that for pure splay and pure benddeformations the bacteria motion is bipolar, with an equal probability distribution for motion along thedirector field in either direction. This was different for mixed splay-bend regions, where the motionbecomes unipolar, directed towards the positive defects and avoiding negative ones. Lavrentovich et al.thus directed the motion of bacteria by the use of defect patterns, and therefore exerting a directinginfluence on the otherwise chaotic motion. It is very likely that active liquid crystalline systems willbecome a direction of research where many interesting fundamental aspects are to be discovered,with a high likeliness of future applications in the areas of biotechnology and medicine.
Nanomaterials 2017, 7, 305 15 of 28
2.4. Liquid Crystals from Nanotubes and Nanorods
The largest part of the literature and thus experimental investigations, are related to the dispersionof nanotubes within an already existing LC phase [104–106]. This host phase can be nematic, cholestericor smectic, and already possess a physical functionality, as for example in the form of SmC* ferroelectricliquid crystals (FLC). The aim is to transfer the anisotropic order of the LC onto the dispersedanisotropic particles, the LC acting as a template [27,107]. Due to the properties of the dispersednanotubes or nanorods, this adds functionality to the dispersion, for example in the form of a switchableconductivity [28]. Orientation of nanotubes and changes of physical properties can also be observed inferroelectric LCs [108], discotics [109,110], and lyotropic phases [111–114]. Nevertheless, here we willconcentrate on the opposite phenomena, the formation of lyotropic LC phases through the addition ofnanotubes and nanorods to an isotropic solvent [115–117].
2.4.1. Nanotubes
The possible occurrence of liquid crystalline order was first predicted by Somoza et al. [118]who analysed two limiting approaches theoretically: (i) purely attractive van der Waals interactionsbetween the nanotubes, which led to the formation of nematic and columnar phases for increasingconcentration of nanotubes; (ii) solely hard-core repulsion, which led to the formation of nematic andsmectic A phases for increasing concentration. The isotropic to nematic transition was found to dependon the length of the nanotubes; increasing with increasing nanotube length. Experimentally, it appearsthat ultra-sonication is of vital importance to de-bundle the nanotubes, increase tube solubility andlead to the observation of lyotropic behaviour. The nematic phase grows in the form of tactoids withan order parameter increasing from about S ~0.3 to S ~0.5 which increases with increasing time ofsonication [119,120], as depicted in Figure 14. It should also be noted that a predicted smectic A phasehas not been observed experimentally so far, which can most likely be attributed to the polydispersityof the nanotubes. All in all, the nanotube lyotropic phase formation is quite similar to that of TMVsor DNA.
Nanomaterials 2017, 7, 305 16 of 28
concentration of nanotubes; (ii) solely hard‐core repulsion, which led to the formation of nematic and
smectic A phases for increasing concentration. The isotropic to nematic transition was found to
depend on the length of the nanotubes; increasing with increasing nanotube length. Experimentally,
it appears that ultra‐sonication is of vital importance to de‐bundle the nanotubes, increase tube
solubility and lead to the observation of lyotropic behaviour. The nematic phase grows in the form
of tactoids with an order parameter increasing from about S ~ 0.3 to S ~ 0.5 which increases with
increasing time of sonication [119,120], as depicted in Figure 14. It should also be noted that a
predicted smectic A phase has not been observed experimentally so far, which can most likely be
attributed to the polydispersity of the nanotubes. All in all, the nanotube lyotropic phase formation
is quite similar to that of TMVs or DNA.
Figure 14. (a–d) formation of the lyotropic nematic phase of multiwall nanotubes, multiwall
nanotubes (MWNT), in water, for increasing concentration through the biphasic region. At
approximately 5% by volume, the nematic phase is fully developed as evidenced by a typical
Schlieren texture. (Reproduced by permission from ref. [117]); (e) Similar results are obtained for
DNA functionalized nanotubes. (Reproduced by permission from ref. [121]).
First experimental evidence for lyotropic nanotube LCs was presented shortly after their
prediction, by Song et al. [116,117] for a multiwall nanotube (MWNT) in water system. To enhance
the solubility without the need for employing a surfactant, the nanotubes were functionallized with
COOH before dispersion in water. The transition from isotropic to the nematic state was observed at
a nanotube loading of approximately 1 vol %, with a two‐phase region between 1–4 vol %. Above
this concentration, a purely nematic state was found [115]. The two‐phase region is somewhat wider
than that predicted by Onsager, which again can be attributed to the large polydispersity of the
MWNTs. Windle and co‐workers [122] demonstrated that the longer, straighter nanotubes
accumulate in the nematic phase of the dispersion, while impurities, which are always present in
nanotube systems, as well as short tubes, accumulate in the isotropic liquid. Badaire followed a
similar approach for single‐wall nanotubes (SWNT), but instead of covalent functionalization,
denatured DNA was adsorbed on the walls of the tubes [115]. The dispersion in water is then
facilitated via electrostatic repulsion, as the denatured DNA is charged. This is used to compensate
the attractive van der Waals interactions between the nanotubes, and implies that below a certain
coating concentration the dispersion remains isotropic. Above the critical coating concentration, a
nematic phase is observed above 4 wt % SWNTs, with a two‐phase region between 2–4 wt % (see
Figure 14e). Electrostatic repulsion to disperse the single‐wall nanotubes was also used by Rai et al.
[121] for nanotube LCs without the functionalization with chemical groups or decoration with DNA.
Figure 14. (a–d) formation of the lyotropic nematic phase of multiwall nanotubes, multiwall nanotubes(MWNT), in water, for increasing concentration through the biphasic region. At approximately5% by volume, the nematic phase is fully developed as evidenced by a typical Schlieren texture.(Reproduced by permission from ref. [117]); (e) Similar results are obtained for DNA functionalizednanotubes. (Reproduced by permission from ref. [121]).
First experimental evidence for lyotropic nanotube LCs was presented shortly after theirprediction, by Song et al. [116,117] for a multiwall nanotube (MWNT) in water system. To enhance
Nanomaterials 2017, 7, 305 16 of 28
the solubility without the need for employing a surfactant, the nanotubes were functionallizedwith COOH before dispersion in water. The transition from isotropic to the nematic state wasobserved at a nanotube loading of approximately 1 vol %, with a two-phase region between 1–4 vol %.Above this concentration, a purely nematic state was found [115]. The two-phase region is somewhatwider than that predicted by Onsager, which again can be attributed to the large polydispersityof the MWNTs. Windle and co-workers [122] demonstrated that the longer, straighter nanotubesaccumulate in the nematic phase of the dispersion, while impurities, which are always presentin nanotube systems, as well as short tubes, accumulate in the isotropic liquid. Badaire followeda similar approach for single-wall nanotubes (SWNT), but instead of covalent functionalization,denatured DNA was adsorbed on the walls of the tubes [115]. The dispersion in water is thenfacilitated via electrostatic repulsion, as the denatured DNA is charged. This is used to compensate theattractive van der Waals interactions between the nanotubes, and implies that below a certain coatingconcentration the dispersion remains isotropic. Above the critical coating concentration, a nematicphase is observed above 4 wt % SWNTs, with a two-phase region between 2–4 wt % (see Figure 14e).Electrostatic repulsion to disperse the single-wall nanotubes was also used by Rai et al. [121] fornanotube LCs without the functionalization with chemical groups or decoration with DNA. In thiscase though, a strong acid had to be chosen as the isotropic solvent, which led to protonation of thetube walls and thus electrostatic repulsion and better tube dispersion.
2.4.2. Nanorods and Nanowires
It appears that it is generally hard to obtain large scale uniformly oriented samples of nanotubebased lyotropic LCs. This is probably closely related to the largely unavoidable polydispersityof the systems under investigation. It is likely that a more successful approach may be found inthe use of nanorods, which can be produced with a much better monodispersity and where thenanoparticles are straight and less flexible, i.e., behave more like an ideal system in terms of theOnsager description. Systems with dispersed nanorods have been investigated, but again, mainly withrespect to dispersions in an already existing (thermotropic) LC. Here the self-organization of the LC isexploited to self-assemble nanorods, to provide added functionality or tuning of physical properties.An example are gold nanorods, LC modified gold particles and gold nanorod LCs [26,123–126],which enhance the anisotropy of the conductivity, the dielectric constant, and the elastic behaviour.
Nanorods of ZnO
Zinc oxide, ZnO, is generally produced as a white powder for the use in many materials andapplications, such as paints, plastics, glass, ceramics, food products and mainly in the rubber industry,where it is employed in the vulcanization process of rubber. It is a wide band-gap semiconductor ofthe II-VI group and its uses in the electronics industry are in thin-film transistors, light emitting diodes,and as transparent electrodes for liquid crystal displays.
Mostly, ZnO nanoparticles, and other metallic and metal oxide nanoparticles, are incorporatedinto already existing thermotropic or lyotropic phases, rather than being used to generate the LCbehaviour [30]. Lamellar, cubic and hexagonal lyotropic phases have also been reported to be used asa reaction medium in which nanoparticles are synthesised [127]. Reports on the formation of lyotropicLCs from ZnO nanoparticles are comparatively scarce.
In the form of single crystal semiconductor nanowires ZnO assembles into lyotropic nematicphases in organic and aqueous solvents. The formation of the LC phase follows that predictedby Onsager, and outlined above, where below certain ZnO nanowire concentrations an isotropicphase is formed, which at higher concentrations becomes a two-phase region and eventuallyat another, still higher concentration, transforms into a lyotropic nematic phase [128]. For thedemonstration of such liquid crystalline behaviour, high aspect ratio nanowires were employed,suitably surface-functionalised by molecules containing sulphur, an alkyl spacer and headgroups suchas H or COOH. In the nematic state a nicely developed Schlieren texture can be observed, as shown in
Nanomaterials 2017, 7, 305 17 of 28
Figure 15. On drying thin films from the lyotropic phase, the ZnO nanowires may act like a templateof the director field [128], imaging typical s = ±1 and s = ±1/2 defects of the lyotropic nematic phase,similar to polymer stabilized LCs with thermotropic nematic phases [129] (see Figure 15).
Nanomaterials 2017, 7, 305 17 of 28
In this case though, a strong acid had to be chosen as the isotropic solvent, which led to protonation
of the tube walls and thus electrostatic repulsion and better tube dispersion.
2.4.2. Nanorods and Nanowires
It appears that it is generally hard to obtain large scale uniformly oriented samples of nanotube
based lyotropic LCs. This is probably closely related to the largely unavoidable polydispersity of the
systems under investigation. It is likely that a more successful approach may be found in the use of
nanorods, which can be produced with a much better monodispersity and where the nanoparticles
are straight and less flexible, i.e., behave more like an ideal system in terms of the Onsager description.
Systems with dispersed nanorods have been investigated, but again, mainly with respect to
dispersions in an already existing (thermotropic) LC. Here the self‐organization of the LC is exploited
to self‐assemble nanorods, to provide added functionality or tuning of physical properties. An
example are gold nanorods, LC modified gold particles and gold nanorod LCs [26,123–126], which
enhance the anisotropy of the conductivity, the dielectric constant, and the elastic behaviour.
Nanorods of ZnO
Zinc oxide, ZnO, is generally produced as a white powder for the use in many materials and
applications, such as paints, plastics, glass, ceramics, food products and mainly in the rubber industry,
where it is employed in the vulcanization process of rubber. It is a wide band‐gap semiconductor of
the II‐VI group and its uses in the electronics industry are in thin‐film transistors, light emitting
diodes, and as transparent electrodes for liquid crystal displays.
Mostly, ZnO nanoparticles, and other metallic and metal oxide nanoparticles, are incorporated
into already existing thermotropic or lyotropic phases, rather than being used to generate the LC
behaviour [30]. Lamellar, cubic and hexagonal lyotropic phases have also been reported to be used
as a reaction medium in which nanoparticles are synthesised [127]. Reports on the formation of
lyotropic LCs from ZnO nanoparticles are comparatively scarce.
In the form of single crystal semiconductor nanowires ZnO assembles into lyotropic nematic
phases in organic and aqueous solvents. The formation of the LC phase follows that predicted by
Onsager, and outlined above, where below certain ZnO nanowire concentrations an isotropic phase
is formed, which at higher concentrations becomes a two‐phase region and eventually at another,
still higher concentration, transforms into a lyotropic nematic phase [128]. For the demonstration of
such liquid crystalline behaviour, high aspect ratio nanowires were employed, suitably surface‐
functionalised by molecules containing sulphur, an alkyl spacer and headgroups such as H or COOH.
In the nematic state a nicely developed Schlieren texture can be observed, as shown in Figure 15. On
drying thin films from the lyotropic phase, the ZnO nanowires may act like a template of the director
field [128], imaging typical s = ±1 and s = ±1/2 defects of the lyotropic nematic phase, similar to
polymer stabilized LCs with thermotropic nematic phases [129] (see Figure 15).
Figure 15. Dried films of ZnO lyotropic nematic phases can be used to image defects of strength (a) s
= +1/2 and (b) s = −1/2; Part (c) shows a Schlieren texture of a fully developed lyotropic nematic phase
from ZnO nanowires. (Reproduced by permission from ref. [128]).
Figure 15. Dried films of ZnO lyotropic nematic phases can be used to image defects of strength(a) s = +1/2 and (b) s = −1/2; Part (c) shows a Schlieren texture of a fully developed lyotropic nematicphase from ZnO nanowires. (Reproduced by permission from ref. [128]).
The same group of authors also went one step further in the functionalization of ZnO nanowires,by doping with cobalt Co and manganese Mn, to introduce magnetic properties [130]. Also here, highaspect ratio, surface functionalized nanowires were used, and magnetic reorientations of the ZnOdirector field demonstrated.
Nanorods of TiO2
Titanium oxide finds its applications in the food industry, as sunscreen, and especially as a whitepigment in paper, plastics and paints. In nature it is known as rutile, anastase and brookite, differingin their crystal structure. TiO2 nanorods and nanowires are generally produced through a conversionof anastase. Also for TiO2 there are reports where lyotropic LC phases are used in the synthesis ofnanomaterials, where self-assembled lamellar, spherical and rod-like structures may be observed [131].Reports of TiO2 nanowires being used to generate lyotropic phases are scarce [132]. One such reportdescribes a two-stage assembly process in the formation of a lyotropic nematic phase, by first forminga primary structure, such as ribbons, which then in a second self-assembly step through an increase inconcentration may form a nematic and lamellar lyotropic LC.
CdSe Semiconductor Nanorods
Cadmium selenide nanorods are semiconductors, typically of length ~40 nm and width ~6 nm.This means they have an aspect ratio for which one can well expect the formation of orientationalorder as it is observed for nematic phases [133]. Due to the fact that these nanoparticles can also beproduced with an excellent monodispersity, one even has the opportunity to possibly detect smecticordering, i.e., the formation of at least one dimensional positional order [134].
Nanomaterials 2017, 7, 305 18 of 28
Nanomaterials 2017, 7, 305 18 of 28
The same group of authors also went one step further in the functionalization of ZnO nanowires,
by doping with cobalt Co and manganese Mn, to introduce magnetic properties [130]. Also here, high
aspect ratio, surface functionalized nanowires were used, and magnetic reorientations of the ZnO
director field demonstrated.
Nanorods of TiO2
Titanium oxide finds its applications in the food industry, as sunscreen, and especially as a white
pigment in paper, plastics and paints. In nature it is known as rutile, anastase and brookite, differing
in their crystal structure. TiO2 nanorods and nanowires are generally produced through a conversion
of anastase. Also for TiO2 there are reports where lyotropic LC phases are used in the synthesis of
nanomaterials, where self‐assembled lamellar, spherical and rod‐like structures may be observed
[131]. Reports of TiO2 nanowires being used to generate lyotropic phases are scarce [132]. One such
report describes a two‐stage assembly process in the formation of a lyotropic nematic phase, by first
forming a primary structure, such as ribbons, which then in a second self‐assembly step through an
increase in concentration may form a nematic and lamellar lyotropic LC.
CdSe Semiconductor Nanorods
Cadmium selenide nanorods are semiconductors, typically of length ~40 nm and width ~6 nm.
This means they have an aspect ratio for which one can well expect the formation of orientational
order as it is observed for nematic phases [133]. Due to the fact that these nanoparticles can also be
produced with an excellent monodispersity, one even has the opportunity to possibly detect smectic
ordering, i.e., the formation of at least one dimensional positional order [134].
Figure 16. CdSe nanorods exhibit typical nematic Schlieren textures, as shown in part (a) of the figure
(reproduced by permission from ref. [133]). The electron micrographs of parts (b) and (c) indicate
nematic and smectic ordering, thus orientational and additional one‐dimensional positional order,
respectively. The insets show the corresponding Fourier transforms. (Reproduced by permission from
Figure 16. CdSe nanorods exhibit typical nematic Schlieren textures, as shown in part (a) of the figure(reproduced by permission from ref. [133]). The electron micrographs of parts (b) and (c) indicatenematic and smectic ordering, thus orientational and additional one-dimensional positional order,respectively. The insets show the corresponding Fourier transforms. (Reproduced by permission fromref. [135]); (d) depicts the SAXS picture of the nematic phase, which also clearly evidences orientationalorder. (Reproduced by permission from ref. [134]).
CdSe nanorods show indeed a pronounced appearance of lyotropic nematic phases in thepresence of organic solvents [134], as shown in the distinct Schlieren textures of Figure 16a, wheres = 1/2 and s = 1 disclinations are observable. Also small angle X-ray experiments on orientedsamples nicely present evidence for nematic ordering (Figure 16d), while transmission electronmicroscopy (TEM) reveals not only a nematic structure of nanorods, but also positional order forhigher concentrations (Figure 16b,c). Liquid crystalline self-assembly of nanorods has been reviewedrecently by Thorkelsson et al. [136]. Not only have semiconducting nanorods been investigated for theformation of lyotropic LCs, but also within LC templates [31].
2.5. Liquid Crystals from Nanoplates
Just like the disk-like colloidal structures of for example clay particles, also other materials ofthat shape can exhibit very stable lyotropic LC phases as a function of particle concentration. One ofthe most prominent examples are the derivatives of graphene [137–141]. Graphene has attractedmuch attention over the recent years due to its promising properties in terms of elastic modulus andconductivity while only exhibiting flakes of the nanometer to micrometer size which are only a carbonmonomolecular thick.
2.5.1. Graphene
In terms of liquid crystalline behaviour graphene itself is actually not the material of choice, due toits poor solubility and dispensability in isotropic solvents. This has been tested for a large variety of
Nanomaterials 2017, 7, 305 19 of 28
solvents with varying polarity [142] and it appears that solubility is slightly increased for increasingdielectric constant. Nevertheless, overall the solubility of graphene in any solvent is very small andconcentrations to observe lyotropic liquid crystalline behaviour are not easily achieved, not even withprolonged ultrasonication to avoid aggregation and coagulation.
A possible way forward are protonated graphenes. The formation of a lyotropic liquid crystallinephase formed by graphene in chlorosulphonic acid was first reported by Pasquali and co-workers [143]in 2010. A nematic texture was observed to indicate liquid crystallinity. The structure of the nematicphase is similar to that of a discotic nematic phase, with the director being normal to the plane of thegraphene sheets. Despite the principle demonstration of liquid crystalline behaviour, processing ofthese systems is obviously not desirable, and systems with more environmentally friendly solventsand better solubility need to be found.
2.5.2. Graphene Oxide
This is the case with graphene oxide (GO), which represents a form of graphene decorated withhydroxyl, carboxyl and epoxide groups. This makes it easily dissolvable in water and other solvents.A further advantage of graphene oxide is the fact that in contrast to graphene, it is readily available inlarge quantities at a very reasonable price. As first demonstrated by Kim and co-workers [144] andXu and Gao [145] in 2011, GO in water or organic solvents forms a nematic phase above a certainthreshold concentration, with typical textures observed, as shown in Figure 17a for increasing GOconcentration. As common, a two-phase behaviour is observed as demonstrated also in Figure 17b forthree different graphene oxide sources. The formed phase is very stable with respect to temperature,up until the boiling point of the solvent.Nanomaterials 2017, 7, 305 20 of 28
Figure 17. (a) Qualitative illustration of the increasing LC volume fraction for increasing graphene
oxide, GO, concentration; Part (b) quantifies this behaviour for three graphene oxide samples from
different sources. The difference in quantitative behaviour as the biphasic concentration regime is
passed, is due to a variation of polydispersity and graphene flake size among other influences; (c)
Application of magnetic fields can be used to uniformly orient the lyotropic nematic phase of
graphene oxide, which is evidenced by rotation of the sample between crossed polarizers; (d) Also
with small angle X‐ray diffraction one can demonstrate orientational order of the director, obtained
in capillaries. (Parts (a–c) are reproduced by permission from ref. [144], while part (d) is reproduced
by permission from ref. [145]).
Xu and Gao [145] actually claim that the phase they observe can be described by the model of
the twist grain boundary (TGB) phase, where blocks of smectic layers are rotated with respect to each
other, while the grain boundaries between blocks are arrays of screw dislocations. The rotation of the
blocks will eventually lead to a helical superstructure, which can be commensurate or
incommensurate. They attribute their interpretation to the observed weak layering by small angle X‐
ray scattering (Figure 17d) in combination with LC texture observation and cryo‐Scanning Electron
Microscopy. This appears to be a point of controversy, because the formation of a TGB‐like phase
requires the presence of chirality, which is absent in the studied system, as neither the graphene oxide,
nor the solvent are chiral. The observed textures also appear different than the common fingerprint
textures observed for chiral nematic or cholesteric LCs, without a clear periodicity, appearing more
like textures observed in shear banding. In addition, the fact that the graphene oxide sheets exhibit a
large polydispersity makes it less likely to form a TGB structure. At this point the detailed structure
of the observed phase does not seem to be quite clear, and possibly further investigations will be
needed. Nevertheless, it is without doubt that the observed aqueous graphene oxide suspensions
exhibit liquid crystalline behaviour.
It should further be pointed out, that the actual phase appearance or in fact possibly the diagram
slightly depends on the average size of the GO flakes, the polydispersity, the dielectric constant of
the solvent and confinement conditions [146]. The liquid crystalline phase is formed at lower
concentrations for larger GO flake sizes, it is observed more easily for solvents with an increased
Figure 17. (a) Qualitative illustration of the increasing LC volume fraction for increasing grapheneoxide, GO, concentration; Part (b) quantifies this behaviour for three graphene oxide samples fromdifferent sources. The difference in quantitative behaviour as the biphasic concentration regimeis passed, is due to a variation of polydispersity and graphene flake size among other influences;(c) Application of magnetic fields can be used to uniformly orient the lyotropic nematic phase ofgraphene oxide, which is evidenced by rotation of the sample between crossed polarizers; (d) Alsowith small angle X-ray diffraction one can demonstrate orientational order of the director, obtained incapillaries. (Parts (a–c) are reproduced by permission from ref. [144], while part (d) is reproduced bypermission from ref. [145]).
Nanomaterials 2017, 7, 305 20 of 28
Xu and Gao [145] actually claim that the phase they observe can be described by the model ofthe twist grain boundary (TGB) phase, where blocks of smectic layers are rotated with respect to eachother, while the grain boundaries between blocks are arrays of screw dislocations. The rotation of theblocks will eventually lead to a helical superstructure, which can be commensurate or incommensurate.They attribute their interpretation to the observed weak layering by small angle X-ray scattering(Figure 17d) in combination with LC texture observation and cryo-Scanning Electron Microscopy.This appears to be a point of controversy, because the formation of a TGB-like phase requires thepresence of chirality, which is absent in the studied system, as neither the graphene oxide, nor thesolvent are chiral. The observed textures also appear different than the common fingerprint texturesobserved for chiral nematic or cholesteric LCs, without a clear periodicity, appearing more liketextures observed in shear banding. In addition, the fact that the graphene oxide sheets exhibit a largepolydispersity makes it less likely to form a TGB structure. At this point the detailed structure of theobserved phase does not seem to be quite clear, and possibly further investigations will be needed.Nevertheless, it is without doubt that the observed aqueous graphene oxide suspensions exhibit liquidcrystalline behaviour.
It should further be pointed out, that the actual phase appearance or in fact possibly the diagramslightly depends on the average size of the GO flakes, the polydispersity, the dielectric constantof the solvent and confinement conditions [146]. The liquid crystalline phase is formed at lowerconcentrations for larger GO flake sizes, it is observed more easily for solvents with an increaseddielectric constant, such as water, and it is somewhat suppressed or not observable for more confinedgeometries. This is most likely due to the very strong planar anchoring of the graphene oxide sheetsto the bounding glass substrates, which produces pseudo-isotropic behaviour. The fact that liquidcrystalline behaviour of GO can be observed at much lower concentrations if the flakes exhibit a largersize was also observed by Dan et al. [147]. Furthermore, the LC formation in dependence of differentorganic solvents has been discussed by Jalili et al. [148]. At last, an interesting scenario can be observedif dispersing graphene oxide in a thermotropic nematic. Increasing the temperature above the clearingpoint, converts the host LC into an isotropic phase, which can then in combination with the GO actas a solvent to form a lyotropic nematic phase [29]. One can thus observe the transition between athermotropic and a lyotropic nematic phase, which can be shown by dielectric spectroscopy, but is notobservable in differential scanning calorimetry, thus apparently not connected to a latent heat [149].
Graphene oxide LCs can be oriented by magnetic field application, as shown in Figure 17c withthe corresponding small angle X-ray scattering image showing the typical pattern of orientationalorder (Figure 17d). Under the confinement of LC sandwich cells, graphene oxide nematic can beoriented between untreated glass plates or in channels, such that the GO plane lies parallel to thesubstrates [146]. The director therefore is oriented normal to the substrate plane, and the sample canbe rotated between well oriented bright and dark states between crossed polarizers (see Figure 18).
Nanomaterials 2017, 7, 305 21 of 28
dielectric constant, such as water, and it is somewhat suppressed or not observable for more confined
geometries. This is most likely due to the very strong planar anchoring of the graphene oxide sheets
to the bounding glass substrates, which produces pseudo‐isotropic behaviour. The fact that liquid
crystalline behaviour of GO can be observed at much lower concentrations if the flakes exhibit a
larger size was also observed by Dan et al. [147]. Furthermore, the LC formation in dependence of
different organic solvents has been discussed by Jalili et al. [148]. At last, an interesting scenario can
be observed if dispersing graphene oxide in a thermotropic nematic. Increasing the temperature
above the clearing point, converts the host LC into an isotropic phase, which can then in combination
with the GO act as a solvent to form a lyotropic nematic phase [29]. One can thus observe the
transition between a thermotropic and a lyotropic nematic phase, which can be shown by dielectric
spectroscopy, but is not observable in differential scanning calorimetry, thus apparently not
connected to a latent heat [149].
Graphene oxide LCs can be oriented by magnetic field application, as shown in Figure 17c with
the corresponding small angle X‐ray scattering image showing the typical pattern of orientational
order (Figure 17d). Under the confinement of LC sandwich cells, graphene oxide nematic can be
oriented between untreated glass plates or in channels, such that the GO plane lies parallel to the
substrates [146]. The director therefore is oriented normal to the substrate plane, and the sample can
be rotated between well oriented bright and dark states between crossed polarizers (see Figure 18).
Figure 18. Confinement in channels of plain, untreated glass, can also provide a simple mechanism
of orientation for the lyotropic nematic phase of graphene oxide. The transmission of the LC changes
with a periodicity of 90° when rotated between crossed polarizes. It is brightest when the director is
oriented at 45° to either of the polarizers (a) and darkest, when it is parallel to either polarizer A or P
(d); In between, the transmission continuously varies (b,c). (Reproduced by permission from ref.
[146]).
Song et al. [150] have demonstrated that application of an AC electric field to a lyotropic
graphene oxide nematic LC can result in electro‐optic switching, based on the Kerr effect, with a very
large Kerr coefficient. This effect can also be used to orient graphene oxide sheets [151].
2.5.3. Reduced Graphene Oxide
Heating graphene oxide above approximately 165 °C thermally reduced GO to rGO, which
results in a partial recovery of graphene properties, especially the electronic ones, but at the cost of
solubility, which in turn increases the tendency for aggregation and coagulation, making it more
difficult to obtain liquid crystalline behaviour. This can be compensated by employing surfactants to
stabilize the rGO flakes, as demonstrated by Poulin et al. [152]. One may thus partially maintain the
favourable electronic properties of graphene, while additionally being able to exploit the self‐
organization due to liquid crystallinity.
2.5.4. Other 2D Materials
One could expect that other two‐dimensional materials similar to graphene, graphene oxide or
reduced graphene oxide, such as boron nitride, indium selenide or gallium selenide, MoS2, NbSe2,
WO3 or WS3 can also exhibit lyotropic LC phases at certain concentrations in suitable solvents,
Figure 18. Confinement in channels of plain, untreated glass, can also provide a simple mechanism oforientation for the lyotropic nematic phase of graphene oxide. The transmission of the LC changeswith a periodicity of 90◦ when rotated between crossed polarizes. It is brightest when the director isoriented at 45◦ to either of the polarizers (a) and darkest, when it is parallel to either polarizer A or P(d); In between, the transmission continuously varies (b,c). (Reproduced by permission from ref. [146]).
Nanomaterials 2017, 7, 305 21 of 28
Song et al. [150] have demonstrated that application of an AC electric field to a lyotropic grapheneoxide nematic LC can result in electro-optic switching, based on the Kerr effect, with a very large Kerrcoefficient. This effect can also be used to orient graphene oxide sheets [151].
2.5.3. Reduced Graphene Oxide
Heating graphene oxide above approximately 165 ◦C thermally reduced GO to rGO, which resultsin a partial recovery of graphene properties, especially the electronic ones, but at the cost of solubility,which in turn increases the tendency for aggregation and coagulation, making it more difficult toobtain liquid crystalline behaviour. This can be compensated by employing surfactants to stabilize therGO flakes, as demonstrated by Poulin et al. [152]. One may thus partially maintain the favourableelectronic properties of graphene, while additionally being able to exploit the self-organization due toliquid crystallinity.
2.5.4. Other 2D Materials
One could expect that other two-dimensional materials similar to graphene, graphene oxide orreduced graphene oxide, such as boron nitride, indium selenide or gallium selenide, MoS2, NbSe2, WO3
or WS3 can also exhibit lyotropic LC phases at certain concentrations in suitable solvents, especially ifthese materials occur in single layers. This will then most likely have strong parallels to inorganic LCsand clays.
3. Summary and Outlook
The topic of LCs and nanomaterials has attracted increasing attention over the last years, not onlywithin the LC community, but also more broadly as soft materials in general and model anisotropiccolloid systems. An extensive summary of up-to-date knowledge can be found in the two-volumebook by Lagerwall and Scalia [153–155]. The three main reasons for this increased interest are (i)nanomaterials in thermotropic LCs can be used to add functionality and tune the properties ofthe liquid crystalline system; (ii) Phases, especially those of the frustrated type, can be stabilized,and novel materials with anisotropic properties can be created, which spontaneously align shapeanisotropic nanoparticles. This can be achieved either through templating liquid crystalline order fromthermotropic, as well as lyotropic phases, as well as the formation of lyotropic phases themselves,by nanoparticles ordering in an isotropic solvent; (iii) LC—nanoparticle composites, may these be ofthe thermotropic or the lyotropic type, allow for the construction of nanotechnology devices in manydiverse areas, such as displays, sensors, biological engineering, or even functional clothing. In thisreview, we have tried to give a broad overview of different lyotropic liquid crystalline systems, basedon a variety of anisotropic particles in the colloidal size range. These can be one- or two-dimensionalnanomaterials. In both cases, initial investigations on inorganic materials go back for about a century,although they have by far not attracted the attention of their organic, thermotropic counterparts,which is mainly due to the success of the latter in electro-optic and display devices. One of theclassic examples of inorganic LCs [20] is vanadium pentoxide, V2O5, which dates back to about 1915.While many inorganic LCs are formed by one-dimensional nanoparticles, mineral and clay LCs [44,46]are mostly obtained from plate like, thus two-dimensional particles. The classic examples of biologicallyotropic LCs are the TMVs [11] (and other similar viruses), as well as DNA [61]. One materialwhich is located at the borderline between biological one- to two-dimensional crystals, are cellulosenanocrystals [86]. An increasing amount of literature on recent further lyotropic LCs can be found forcarbon nanotubes [106,116] (as well as similar nanotubes and nanowires), and graphene oxide [154].
All of the above discussed lyotropic liquid crystalline systems from rods or plates have one featurein common: they all obey the theoretical description initially formulated by Onsager in the 1940s,at least to a large extent, and often even quantitatively. This has also been demonstrated by a variety ofcomputer simulations and experimental work summarized in references [18,19,155].
Nanomaterials 2017, 7, 305 22 of 28
Given the synthesis and development of ever new nanomaterials, and the rapid advancementof nanotechnology, it seems to be out of question that lyotropic, anisotropic particle based LCs willplay an increasing role of importance in the future. This is mainly due to the fact that many of thefunctionalities observed and exploited in thermotropic LCs, like electric and magnetic reorientation,and with it a change of birefringence, ferroelectricity or magnetic properties, can now also be observedin lyotropic LCs. The properties of self-assembly, self-organisation, and spontaneous alignment willbe beneficial for nanotechnological applications, and the fact that for many of the lyotropic systems,water can be used as a solvent, favours environmentally friendly production mechanisms, which areclearly the way forward for future applications.
Author Contributions: I.D. conceived and wrote this review. S.A.Z. helped with the figures, reproductionpermissions, and discussions.
Conflicts of Interest: The authors declare no conflict of interest.
References
1. Collings, P.J. Liquid Crystals: Nature’s Delicate Phase of Matter; Princeton University Press: Princeton, NJ,USA, 1990.
2. Collings, P.J.; Hird, M. Introduction to Liquid Crystals Chemistry and Physics; Taylor & Francis: London, UK;Bristol, PA, USA, 1997.
3. Chandrasekhar, S. Liquid Crystals, 2nd ed.; Cambridge University Press: Cambridge, UK, 1992.4. Singh, S. Liquid Crystals: Fundamentals; World Scientific: Hackensack, NJ, USA, 2002.5. De Gennes, P.G.; Prost, J. The Physics of Liquid Crystals, 2nd ed.; Oxford University Press: Oxford, UK;
New York, NY, USA, 1993.6. Lueder, E. Liquid Crystal Displays: Addressing Schemes and Electro-Optical Effects; John Wiley & Sons: Chichester,
UK, 2001.7. Dierking, I. Textures of Liquid Crystals; Wiley-VCH: Weinheim, Germany, 2003.8. Petrov, A.G. The Lyotropic State of Matter: Molecular Physics and Living Matter Physics; Taylor & Francis:
London, UK, 1999.9. Figueiredo Neto, A.M.; Salinas, S.R.A. The Physics of Lyotropic Liquid Crystals: Phase Transitions and Structural
Properties; Oxford University Press: New York, NY, USA, 2005.10. Onsager, L. The effects of shape on the interaction of colloidal particles. Ann. N. Y. Acad. Sci. 1949, 51, 627–659.
[CrossRef]11. Bawden, F.C.; Pirie, N.W.; Bernal, J.D.; Fankuchen, I. Liquid Crystalline Substances from Virus-infected
Plants. Nature 1936, 138, 1051–1052. [CrossRef]12. Diesselhorst, H.; Freundlich, H. On the double refraction of vanadine pentoxydsol. Phys. Z. 1915, 16, 419–425.13. Mourchid, A.; Delville, A.; Lambard, J.; LeColier, E.; Levitz, P. Phase Diagram of Colloidal Dispersions of
Anisotropic Charged Particles: Equilibrium Properties, Structure, and Rheology of Laponite Suspensions.Langmuir 1995, 11, 1942–1950. [CrossRef]
14. Maier, W.; Saupe, A. Eine einfache molekulare Theorie des nematischen kristallinflüssigen Zustandes.Zeitschrift für Naturforsch. A 1958, 13, 564–566. [CrossRef]
15. Maier, W.; Saupe, A. Eine einfache molekular-statistische Theorie der nematischen kristallinflüssigen Phase.Teil l1. Zeitschrift für Naturforsch. A 1959, 14, 882. [CrossRef]
16. Maier, W.; Saupe, A. Eine einfache molekular-statistische Theorie der nematischen kristallinflüssigen Phase.Teil II. Zeitschrift für Naturforsch. A 1960, 15, 287. [CrossRef]
17. Stroobants, A.; Lekkerkerker, H.N.W.; Odijk, T. Effect of electrostatic interaction on the liquid crystal phasetransition in solutions of rodlike polyelectrolytes. Macromolecules 1986, 19, 2232–2238. [CrossRef]
18. Vroege, G.J.; Lekkerkerker, H.N.W. Phase transitions in lyotropic colloidal and polymer liquid crystals.Rep. Fmg. Phys. 1992, 55, 1241–1309. [CrossRef]
19. Bolhuis, P.; Frenkel, D. Tracing the phase boundaries of hard spherocylinders. J. Chem. Phys. 1997,106, 666–687. [CrossRef]
20. Sonin, A.S. Inorganic lyotropic liquid crystals. J. Mater. Chem. 1998, 8, 2557–2574. [CrossRef]
Nanomaterials 2017, 7, 305 23 of 28
21. Gabriel, J.-C.P.; Davidson, P. Mineral Liquid Crystals from Self-Assembly of Anisotropic Nanosystems.Top. Curr. Chem. 2003, 226, 119–172.
22. Chen, W.-T.; Chen, P.-S.; Chao, C.-Y. Effect of Doped Insulating Nanoparticles on the Electro-OpticalCharacteristics of Nematic Liquid Crystals. Jpn. J. Appl. Phys. 2009, 48, 15006. [CrossRef]
23. Reznikov, Y.; Buchnev, O.; Tereshchenko, O.; Reshetnyak, V.; Glushchenko, A.; West, J. Ferroelectric nematicsuspension. Appl. Phys. Lett. 2003, 82, 1917. [CrossRef]
24. Singh, U.B.; Dhar, R.; Dabrowski, R.; Pandey, M.B. Enhanced electro-optical properties of a nematic liquidcrystals in presence of BaTiO3 nanoparticles. Liq. Cryst. 2014, 41, 953–959. [CrossRef]
25. Al-Zangana, S.; Turner, M.; Dierking, I. A comparison between size dependent paraelectric and ferroelectricBaTiO3 nanoparticle doped nematic and ferroelectric liquid crystals. J. Appl. Phys. 2017, 121, 85105.[CrossRef]
26. Hegmann, T.; Qi, H.; Marx, V.M. Nanoparticles in Liquid Crystals: Synthesis, Self-Assembly, DefectFormation and Potential Applications. J. Inorg. Organomet. Polym. Mater. 2007, 17, 483–508. [CrossRef]
27. Dierking, I.; Scalia, G.; Morales, P.; LeClere, D. Aligning and Reorienting Carbon Nanotubes with NematicLiquid Crystals. Adv. Mater. 2004, 16, 865–869. [CrossRef]
28. Dierking, I.; Scalia, G.; Morales, P. Liquid crystal–carbon nanotube dispersions. J. Appl. Phys. 2005, 97, 44309.[CrossRef]
29. Al-Zangana, S.; Iliut, M.; Turner, M.; Vijayaraghavan, A.; Dierking, I. Properties of a Thermotropic NematicLiquid Crystal Doped with Graphene Oxide. Adv. Opt. Mater. 2016, 4, 1541–1548. [CrossRef]
30. Saliba, S.; Mingotaud, C.; Kahn, M.L.; Marty, J.-D. Liquid crystalline thermotropic and lyotropic nanohybrids.Nanoscale 2013, 5, 6641. [CrossRef] [PubMed]
31. Mukhina, M.V.; Danilov, V.V.; Orlova, A.O.; Fedorov, M.V.; Artemyev, M.V.; Baranov, A.V. Electrically controlledpolarized photoluminescence of CdSe/ZnS nanorods embedded in a liquid crystal template. Nanotechnology2012, 23, 325201. [CrossRef] [PubMed]
32. Majorana, Q. Sur la biréfringence magnétique. C. R. Acad. Sci. 1902, 135, 159–161.33. Freundlich, H. Die Doppelbrechung des Vanadinpentoxydsols. Berichte der Bunsengesellschaft für Phys. Chem.
1916, 22, 27–33.34. Zocher, H. Spontaneous structure formation in sols; a new kind of anisotropic liquid media. Anorg. Allg. Chem.
1925, 147, 91–110. [CrossRef]35. Yi, Y.; Clark, N.A. Orientation of chromonic liquid crystals by topographic linear channels: Multi-stable
alignment and tactoid structure. Liq. Cryst. 2013, 40, 1736–1747. [CrossRef]36. Kim, Y.-K.; Shiyanovskii, S.V.; Lavrentovich, O.D. Morphogenesis of defects and tactoids during
isotropic–nematic phase transition in self-assembled lyotropic chromonic liquid crystals. J. Phys. Condens. Matter2013, 25, 404202. [CrossRef] [PubMed]
37. Bernal, J.D.; Fankuchen, I. X-ray and crystallographic studies of plant virus preparations: I. Introduction andpreparation of specimens; II. Modes of aggregation of the virus particles. J. Gen. Physiol. 1941, 25, 111–146.[CrossRef] [PubMed]
38. Davidson, P.; Garreau, A.; Livage, J. Nematic colloidal suspensions of V2O5 in water—Or Zocher phasesrevisited. Liq. Cryst. 1994, 16, 905–910. [CrossRef]
39. Pelletier, O.; Sotta, P.; Davidson, P. Deuterium Nuclear Magnetic Resonance Study of the Nematic Phase ofVanadium Pentoxide Aqueous Suspensions. J. Phys. Chem. B 1999, 103, 5427–5433. [CrossRef]
40. Zocher, H.; Török, C. Neuere Beiträge zur Kenntnis der Taktosole. Kolloid-Zeitschrift 1960, 173, 1–7. [CrossRef]41. Michaelev, V.A.; Tcherbakov, V.A. Zh. Obs. Khim. 1985, 55, 1223.42. Davidson, P.; Gabriel, J.C.; Levelut, A.M.; Batail, P. A New Nematic Suspension Based on All-Inorganic
Polymer Rods. Europhys. Lett. 1993, 21, 317–322. [CrossRef]43. Zocher, H.; Török, C. Crystals of higher order and their relation to other superphases. Acta Crystallogr. 1967,
22, 751–755. [CrossRef]44. Gabriel, J.-C.P.; Davidson, P. New Trends in Colloidal Liquid Crystals Based on Mineral Moieties. Adv. Mater.
2000, 12, 9–20. [CrossRef]45. Veerman, J.A.C.; Frenkel, D. Phase behavior of disklike hard-core mesogens. Phys. Rev. A 1992, 45, 5632–5648.
[CrossRef] [PubMed]46. Langmuir, I. The Role of Attractive and Repulsive Forces in the Formation of Tactoids, Thixotropic Gels,
Protein Crystals and Coacervates. J. Chem. Phys. 1938, 6, 873–896. [CrossRef]
Nanomaterials 2017, 7, 305 24 of 28
47. Gabriel, J.-C.P.; Sanchez, C.; Davidson, P. Observation of Nematic Liquid-Crystal Textures in Aqueous Gelsof Smectite Clays. J. Phys. Chem. 1996, 100, 11139–11143. [CrossRef]
48. Kajiwara, K.; Donkai, N.; Hiragi, Y.; Inagaki, H. Lyotropic mesophase of imogolite, 1. Effect of polydispersityon phase diagram. Makromol. Chem. 1986, 187, 2883–2893. [CrossRef]
49. Kajiwara, K.; Donkai, N.; Fujiyoshi, Y.; Inagaki, H. Lyotropic mesophase of imogolite, 2. Microscopicobservation of imogolite mesophase. Makromol. Chemie 1986, 187, 2895–2907. [CrossRef]
50. Zugenmaier, P. Crystalline Cellulose and Cellulose Derivatives; Springer: Berlin, Germany, 2010.51. Lin, N.; Huang, J.; Dufresne, A. Preparation, properties and applications of polysaccharide nanocrystals in
advanced functional nanomaterials: A review. Nanoscale 2012, 4, 3274. [CrossRef] [PubMed]52. Oldenbourg, R.; Wen, X.; Meyer, R.B.; Caspar, D.L.D. Orientational Distribution Function in Nematic
Tobacco-Mosaic-Virus Liquid Crystals Measured by X-Ray Diffraction. Phys. Rev. Lett. 1988, 61, 1851–1854.[CrossRef] [PubMed]
53. Rischkov, V.L.; Smirnova, V.A. Liquid Crystals of the Virus of the Tobacco Mosaic (Nicotiana virus 1).Comptes Rendus l’Academie Sci. l’URSS 1941, 31, 930.
54. Fraden, S.; Maret, G.; Caspar, D.L.D. Angular correlations and the isotropic-nematic phase transition insuspensions of tobacco mosaic virus. Phys. Rev. E 1993, 48, 2816–2837. [CrossRef]
55. Graf, H.; Löwen, H. Phase diagram of tobacco mosaic virus solutions. Phys. Rev. E 1999, 59, 1932–1942.[CrossRef]
56. Fowler, C.E.; Shenton, W.; Stubbs, G.; Mann, S. Tobacco Mosaic Virus Liquid Crystals as Templates for theInterior Design of Silica Mesophases and Nanoparticles. Adv. Mater. 2001, 13, 1266–1269. [CrossRef]
57. Flynn, C.E.; Lee, S.-W.; Peelle, B.R.; Belcher, A.M. Viruses as vehicles for growth, organization and assemblyof materials. Acta Mater. 2003, 51, 5867–5880. [CrossRef]
58. Dogic, Z.; Fraden, S. Ordered phases of filamentous viruses. Curr. Opin. Colloid Interface Sci. 2006, 11, 47–55.[CrossRef]
59. Dogic, Z.; Fraden, S. Cholesteric Phase in Virus Suspensions. Langmuir 2000, 16, 7820–7824. [CrossRef]60. Dogic, Z.; Fraden, S. Smectic Phase in a Colloidal Suspension of Semiflexible Virus Particles. Phys. Rev. Lett.
1997, 78, 2417–2420. [CrossRef]61. Livolant, F.; Leforestier, A. Condensed phases of DNA: Structures and phase transitions. Prog. Polym. Sci.
1996, 21, 1115–1164. [CrossRef]62. Strzelecka, T.E.; Davidson, M.W.; Rill, R.L. Multiple liquid crystal phases of DNA at high concentrations.
Nature 1988, 331, 457–460. [CrossRef] [PubMed]63. Livolant, F.; Levelut, A.M.; Doucet, J.; Benoit, J.P. The highly concentrated liquid-crystalline phase of DNA is
columnar hexagonal. Nature 1989, 339, 724–726. [CrossRef] [PubMed]64. Leforstier, A.; Livolant, F. DNA liquid crystalline blue phases. Electron microscopy evidence and biological
implications. Liq. Cryst. 1994, 17, 651–658. [CrossRef]65. Nakata, M.; Zanchetta, G.; Chapman, B.D.; Jones, C.D.; Cross, J.O.; Pindak, R.; Bellini, T.; Clark, N.A.
End-to-End Stacking and Liquid Crystal Condensation of 6- to 20-Base Pair DNA Duplexes. Science 2007,318, 1276–1279.
66. Zanchetta, G.; Nakata, M.; Buscaglia, M.; Clark, N.A.; Bellini, T. Liquid crystal ordering of DNA and RNAoligomers with partially overlapping sequences. J. Phys. Condens. Matter 2008, 20, 494214. [CrossRef]
67. Zanchetta, G.; Nakata, M.; Buscaglia, M.; Bellini, T.; Clark, N.A. Phase separation and liquid crystallizationof complementary sequences in mixtures of nanoDNA oligomers. Proc. Natl. Acad. Sci. USA 2008,105, 1111–1117. [CrossRef] [PubMed]
68. Bellini, T.; Zanchetta, G.; Fraccia, T.P.; Cerbino, R.; Tsai, E.; Smith, G.P.; Moran, M.J.; Walba, D.M.; Clark, N.A.Liquid crystal self-assembly of random-sequence DNA oligomers. Proc. Natl. Acad. Sci. USA 2012,109, 1110–1115. [CrossRef] [PubMed]
69. Fraccia, T.P.; Smith, G.P.; Bethge, L.; Zanchetta, G.; Nava, G.; Klussmann, S.; Clark, N.A.; Bellini, T. LiquidCrystal Ordering and Isotropic Gelation in Solutions of Four-Base-Long DNA Oligomers. ACS Nano 2016,10, 8508–8516. [CrossRef] [PubMed]
70. Zanchetta, G.; Giavazzi, F.; Nakata, M.; Buscaglia, M.; Cerbino, R.; Clark, N.A.; Bellini, T. Right-handeddouble-helix ultrashort DNA yields chiral nematic phases with both right- and left-handed director twist.Proc. Natl. Acad. Sci. USA 2010, 107, 17497–17502. [CrossRef] [PubMed]
Nanomaterials 2017, 7, 305 25 of 28
71. Stegemeyer, H.; Siemensmeyer, K.; Sucrow, W.; Appel, L. Liquid Crystalline Norcholesterylesters: Influenceof the Axial Methylgroups on the Phase Transitions and the Cholesteric Helix. Zeitschrift für Naturforsch. A1989, 44, 1127–1130. [CrossRef]
72. Slaney, A.J.; Nishiyama, I.; Styring, P.; Goodby, J.W. Twist inversion in a cholesteric material containing asingle chiral centre. J. Mater. Chem. 1992, 2, 805–810. [CrossRef]
73. Dierking, I.; Gieβelmann, F.; Zugenmaier, P.; Kuczynskit, W.; Lagerwall, S.T.; Stebler, B. Investigations ofthe structure of a cholesteric phase with a temperature induced helix inversion and of the succeeding SmC*phase in thin liquid crystal cells. Liq. Cryst. 1993, 13, 45–55. [CrossRef]
74. Styring, P.; Vuijk, J.D.; Nishiyama, I.; Slaney, A.J.; Goodby, J.W. Inversion of chirality-dependent propertiesin optically active liquid crystals. J. Mater. Chem. 1993, 3, 399–405. [CrossRef]
75. Dierking, I.; Gießelmann, F.; Zugenmaier, P.; Mohr, K.; Zaschke, H.; Kuczynski, W. The Origin of theHelical Twist Inversion in Single Component Cholesteric Liquid Crystals. Zeitschrift für Naturforsch. A 1994,49, 1081–1086. [CrossRef]
76. Dierking, I.; Gieβelmann, F.; Zugenmaier, P.; Mohr, K.; Zaschke, H.; Kuczynski, W. New diastereomericcompound with cholesteric twist inversion. Liq. Cryst. 1995, 18, 443–449. [CrossRef]
77. De Michele, C.; Zanchetta, G.; Bellini, T.; Frezza, E.; Ferrarini, A. Hierarchical Propagation of Chiralitythrough Reversible Polymerization: The Cholesteric Phase of DNA Oligomers. ACS Macro Lett. 2016,5, 208–212. [CrossRef]
78. Tan, H.; Yang, S.; Shen, G.; Yu, R.; Wu, Z. Signal-Enhanced Liquid-Crystal DNA Biosensors Based onEnzymatic Metal Deposition. Angew. Chem. Int. Ed. 2010, 49, 8608–8611. [CrossRef] [PubMed]
79. Nakata, M.; Zanchetta, G.; Buscaglia, M.; Bellini, T.; Clark, N.A. Liquid Crystal Alignment on a Chiral Surface:Interfacial Interaction with Sheared DNA Films. Langmuir 2008, 24, 10390–10394. [CrossRef] [PubMed]
80. Rojas, O.J. Cellulose Chemistry and Properties: Fibers, Nanocelluloses and Advanced Materials; Springer: Cham,Switzerland, 2016.
81. George, J.; Sabapathi, S.N. Cellulose nanocrystals: Synthesis, functional properties, and applications.Nanotechnol. Sci. Appl. 2015, 8, 45–54. [CrossRef] [PubMed]
82. Gray, D.; Mu, X. Chiral Nematic Structure of Cellulose Nanocrystal Suspensions and Films; Polarized Lightand Atomic Force Microscopy. Materials (Basel). 2015, 8, 7873–7888. [CrossRef] [PubMed]
83. Dong, X.M.; Kimura, T.; Revol, J.-F.; Gray, D.G. Effects of Ionic Strength on the Isotropic–Chiral NematicPhase Transition of Suspensions of Cellulose Crystallites. Langmuir 1996, 12, 2076–2082. [CrossRef]
84. Beck-Candanedo, S.; Roman, M.; Gray, D.G. Effect of Reaction Conditions on the Properties and Behavior ofWood Cellulose Nanocrystal Suspensions. Biomacromolecules 2005, 6, 1048–1054. [CrossRef] [PubMed]
85. Ureña-Benavides, E.E.; Ao, G.; Davis, V.A.; Kitchens, C.L. Rheology and Phase Behavior of LyotropicCellulose Nanocrystal Suspensions. Macromolecules 2011, 44, 8990–8998. [CrossRef]
86. Lagerwall, J.P.F.; Schütz, C.; Salajkova, M.; Noh, J.; Hyun Park, J.; Scalia, G.; Bergström, L.Cellulose nanocrystal-based materials: From liquid crystal self-assembly and glass formation tomultifunctional thin films. NPG Asia Mater. 2014, 6, e80. [CrossRef]
87. Honorato-Rios, C.; Kuhnhold, A.; Bruckner, J.R.; Dannert, R.; Schilling, T.; Lagerwall, J.P.F.Equilibrium Liquid Crystal Phase Diagrams and Detection of Kinetic Arrest in Cellulose NanocrystalSuspensions. Front. Mater. 2016, 3, 21. [CrossRef]
88. Gray, D. Recent Advances in Chiral Nematic Structure and Iridescent Color of Cellulose Nanocrystal Films.Nanomaterials 2016, 6, 213. [CrossRef] [PubMed]
89. Wu, Q.; Meng, Y.; Wang, S.; Li, Y.; Fu, S.; Ma, L.; Harper, D. Rheological behavior of cellulose nanocrystalsuspension: Influence of concentration and aspect ratio. J. Appl. Polym. Sci. 2014, 131, 40525. [CrossRef]
90. Shafiei-Sabet, S.; Hamad, W.Y.; Hatzikiriakos, S.G. Ionic strength effects on the microstructure and shearrheology of cellulose nanocrystal suspensions. Cellulose 2014, 21, 3347–3359. [CrossRef]
91. Wu, Q.; Meng, Y.; Concha, K.; Wang, S.; Li, Y.; Ma, L.; Fu, S. Influence of temperature and humidity onnano-mechanical properties of cellulose nanocrystal films made from switchgrass and cotton. Ind. Crops Prod.2013, 48, 28–35. [CrossRef]
92. Park, J.H.; Noh, J.; Schütz, C.; Salazar-Alvarez, G.; Scalia, G.; Bergström, L.; Lagerwall, J.P.F.Macroscopic Control of Helix Orientation in Films Dried from Cholesteric Liquid-Crystalline CelluloseNanocrystal Suspensions. ChemPhysChem 2014, 15, 1477–1484. [CrossRef] [PubMed]
Nanomaterials 2017, 7, 305 26 of 28
93. Querejeta-Fernández, A.; Chauve, G.; Methot, M.; Bouchard, J.; Kumacheva, E. Chiral Plasmonic FilmsFormed by Gold Nanorods and Cellulose Nanocrystals. J. Am. Chem. Soc. 2014, 136, 4788–4793. [CrossRef][PubMed]
94. Liu, Q.; Campbell, M.G.; Evans, J.S.; Smalyukh, I.I. Orientationally Ordered Colloidal Co-Dispersions ofGold Nanorods and Cellulose Nanocrystals. Adv. Mater. 2014, 26, 7178–7184. [CrossRef] [PubMed]
95. Chu, G.; Wang, X.; Chen, T.; Gao, J.; Gai, F.; Wang, Y.; Xu, Y. Optically Tunable Chiral Plasmonic Guest–HostCellulose Films Weaved with Long-range Ordered Silver Nanowires. ACS Appl. Mater. Interfaces 2015,7, 11863–11870. [CrossRef] [PubMed]
96. Menzel, A.M. Tuned, driven, and active soft matter. Phys. Rep. 2015, 554, 1–45. [CrossRef]97. Ramaswamy, S. Active matter. J. Stat. Mech. Theory Exp. 2017, 2017, 54002. [CrossRef]98. Bukusoglu, E.; Bedolla Pantoja, M.; Mushenheim, P.C.; Wang, X.; Abbott, N.L. Design of Responsive and
Active (Soft) Materials Using Liquid Crystals. Annu. Rev. Chem. Biomol. Eng. 2016, 7, 163–196. [CrossRef][PubMed]
99. Sanchez, T.; Chen, D.T.N.; DeCamp, S.J.; Heymann, M.; Dogic, Z. Spontaneous motion in hierarchicallyassembled active matter. Nature 2012, 491, 431–434. [CrossRef] [PubMed]
100. Fowler, N.; Dierking, D.I. Kibble-Zurek Scaling during Defect Formation in a Nematic Liquid Crystal.ChemPhysChem 2017, 18, 812–816. [CrossRef] [PubMed]
101. Dierking, I.; Marshall, O.; Wright, J.; Bulleid, N. Annihilation dynamics of umbilical defects in nematic liquidcrystals under applied electric fields. Phys. Rev. E 2005, 71, 61709. [CrossRef] [PubMed]
102. Dierking, I.; Ravnik, M.; Lark, E.; Healey, J.; Alexander, G.P.; Yeomans, J.M. Anisotropy in the annihilationdynamics of umbilic defects in nematic liquid crystals. Phys. Rev. E 2012, 85, 21703. [CrossRef] [PubMed]
103. Peng, C.; Turiv, T.; Guo, Y.; Wei, Q.-H.; Lavrentovich, O.D. Command of active matter by topological defectsand patterns. Science 2016, 354, 882–885. [CrossRef] [PubMed]
104. Zakri, C. Carbon nanotubes and liquid crystalline phases. Liq. Cryst. Today 2007, 16, 1–11. [CrossRef]105. Lagerwall, J.P.F.; Scalia, G. Carbon nanotubes in liquid crystals. J. Mater. Chem. 2008, 18, 2890–2898.
[CrossRef]106. Yadav, S.P.; Singh, S. Carbon nanotube dispersion in nematic liquid crystals: An overview. Prog. Mater. Sci.
2016, 80, 38–76. [CrossRef]107. Lynch, M.D.; Patrick, D.L. Organizing Carbon Nanotubes with Liquid Crystals. Nano Lett. 2002, 2, 1197–1201.
[CrossRef]108. Yakemseva, M.; Dierking, I.; Kapernaum, N.; Usoltseva, N.; Giesselmann, F. Dispersions of multi-wall carbon
nanotubes in ferroelectric liquid crystals. Eur. Phys. J. E 2014, 37, 7. [CrossRef] [PubMed]109. Kumar, S.; Bisoyi, H.K. Aligned Carbon Nanotubes in the Supramolecular Order of Discotic Liquid Crystals.
Angew. Chem. Int. Ed. 2007, 46, 1501–1503. [CrossRef] [PubMed]110. Bisoyi, H.K.; Kumar, S. Carbon nanotubes in triphenylene and rufigallol-based room temperature monomeric
and polymeric discotic liquid crystals. J. Mater. Chem. 2008, 18, 3032. [CrossRef]111. Lagerwall, J.P.F.; Scalia, G.; Haluska, M.; Dettlaff-Weglikowska, U.; Giesselmann, F.; Roth, S.
Simultaneous alignment and dispersion of carbon nanotubes with lyotropic liquid crystals. Phys. Status Solidi2006, 243, 3046–3049. [CrossRef]
112. Lagerwall, J.; Scalia, G.; Haluska, M.; Dettlaff-Weglikowska, U.; Roth, S.; Giesselmann, F. Nanotube AlignmentUsing Lyotropic Liquid Crystals. Adv. Mater. 2007, 19, 359–364. [CrossRef]
113. Jiang, W.; Yu, B.; Liu, W.; Hao, J. Carbon Nanotubes Incorporated within Lyotropic Hexagonal Liquid CrystalFormed in Room-Temperature Ionic Liquids. Langmuir 2007, 23, 8549–8553. [CrossRef] [PubMed]
114. Scalia, G.; von Bühler, C.; Hägele, C.; Roth, S.; Giesselmann, F.; Lagerwall, J.P.F. Spontaneous macroscopiccarbon nanotube alignment via colloidal suspension in hexagonal columnar lyotropic liquid crystals.Soft Matter 2008, 4, 570–576. [CrossRef]
115. Badaire, S.; Zakri, C.; Maugey, M.; Derré, A.; Barisci, J.N.; Wallace, G.; Poulin, P. Liquid Crystals ofDNA-Stabilized Carbon Nanotubes. Adv. Mater. 2005, 17, 1673–1676. [CrossRef]
116. Song, W. Nematic Liquid Crystallinity of Multiwall Carbon Nanotubes. Science 2003, 302, 1363. [CrossRef][PubMed]
117. Song, W.; Windle, A.H. Isotropic–Nematic Phase Transition of Dispersions of Multiwall Carbon Nanotubes.Macromolecules 2005, 38, 6181–6188. [CrossRef]
Nanomaterials 2017, 7, 305 27 of 28
118. Somoza, A.M.; Sagui, C.; Roland, C. Liquid-crystal phases of capped carbon nanotubes. Phys. Rev. B 2001,63, 81403. [CrossRef]
119. Puech, N.; Blanc, C.; Grelet, E.; Zamora-Ledezma, C.; Maugey, M.; Zakri, C.; Anglaret, E.; Poulin, P.Highly Ordered Carbon Nanotube Nematic Liquid Crystals. J. Phys. Chem. C 2011, 115, 3272–3278. [CrossRef]
120. Zakri, C.; Blanc, C.; Grelet, E.; Zamora-Ledezma, C.; Puech, N.; Anglaret, E.; Poulin, P. Liquid crystals ofcarbon nanotubes and graphene. Philos. Trans. R. Soc. A Math. Phys. Eng. Sci. 2013, 371, 20120499. [CrossRef][PubMed]
121. Rai, P.K.; Pinnick, R.A.; Parra-Vasquez, A.N.G.; Davis, V.A.; Schmidt, H.K.; Hauge, R.H.; Smalley, R.E.;Pasquali, M. Isotropic–Nematic Phase Transition of Single-Walled Carbon Nanotubes in Strong Acids. J. Am.Chem. Soc. 2006, 128, 591–595. [CrossRef] [PubMed]
122. Song, W.; Windle, A.H. Size-Dependence and Elasticity of Liquid-Crystalline Multiwalled Carbon Nanotubes.Adv. Mater. 2008, 20, 3149–3154. [CrossRef]
123. Sharma, V.; Park, K.; Srinivasarao, M. Colloidal dispersion of gold nanorods: Historical background, opticalproperties, seed-mediated synthesis, shape separation and self-assembly. Mater. Sci. Eng. R Rep. 2009,65, 1–38. [CrossRef]
124. Stamatoiu, O.; Mirzaei, J.; Feng, X.; Hegmann, T. Nanoparticles in Liquid Crystals and Liquid CrystallineNanoparticles. Top. Curr. Chem. 2012, 318, 331–393. [PubMed]
125. Liu, Q.; Cui, Y.; Gardner, D.; Li, X.; He, S.; Smalyukh, I.I. Self-Alignment of Plasmonic Gold Nanorodsin Reconfigurable Anisotropic Fluids for Tunable Bulk Metamaterial Applications. Nano Lett. 2010,10, 1347–1353. [CrossRef] [PubMed]
126. Umadevi, S.; Feng, X.; Hegmann, T. Large Area Self-Assembly of Nematic Liquid-Crystal-FunctionalizedGold Nanorods. Adv. Funct. Mater. 2013, 23, 1393–1403. [CrossRef]
127. Saliba, S.; Davidson, P.; Impéror-Clerc, M.; Mingotaud, C.; Kahn, M.L.; Marty, J.-D. Facile direct synthesisof ZnO nanoparticles within lyotropic liquid crystals: towards organized hybrid materials. J. Mater. Chem.2011, 21, 18191. [CrossRef]
128. Zhang, S.; Majewski, P.W.; Keskar, G.; Pfefferle, L.D.; Osuji, C.O. Lyotropic Self-Assembly ofHigh-Aspect-Ratio Semiconductor Nanowires of Single-Crystal ZnO. Langmuir 2011, 27, 11616–11621.[CrossRef] [PubMed]
129. Dierking, I.; Archer, P. Imaging liquid crystal defects. RSC Adv. 2013, 3, 26433–26437. [CrossRef]130. Zhang, S.; Pelligra, C.I.; Keskar, G.; Majewski, P.W.; Ren, F.; Pfefferle, L.D.; Osuji, C.O. Liquid Crystalline
Order and Magnetocrystalline Anisotropy in Magnetically Doped Semiconducting ZnO Nanowires.ACS Nano 2011, 5, 8357–8364. [CrossRef] [PubMed]
131. Liu, L.H.; Bai, Y.; Wang, F.M.; Liu, N. Fabrication and Characterizes of TiO2 Nanomaterials Templated byLyotropic Liquid Crystal. Adv. Mater. Res. 2012, 399–401, 532–537. [CrossRef]
132. Ren, Z.; Chen, C.; Hu, R.; Mai, K.; Qian, G.; Wang, Z. Two-Step Self-Assembly and Lyotropic Liquid CrystalBehavior of TiO2 Nanorods. J. Nanomater. 2012, 2012, 180989. [CrossRef]
133. Li, L.; Walda, J.; Manna, L.; Alivisatos, A.P. Semiconductor Nanorod Liquid Crystals. Nano Lett. 2002,2, 557–560. [CrossRef]
134. Li, L.-S.; Alivisatos, A.P. Semiconductor Nanorod Liquid Crystals and Their Assembly on a Substrate.Adv. Mater. 2003, 15, 408–411. [CrossRef]
135. Kim, F.; Kwan, S.; Akana, J.; Yang, P. Langmuir–Blodgett Nanorod Assembly. J. Am. Chem. Soc. 2001,123, 4360–4361. [CrossRef] [PubMed]
136. Thorkelsson, K.; Bai, P.; Xu, T. Self-assembly and applications of anisotropic nanomaterials: A review.Nano Today 2015, 10, 48–66. [CrossRef]
137. Georgakilas, V.; Otyepka, M.; Bourlinos, A.B.; Chandra, V.; Kim, N.; Kemp, K.C.; Hobza, P.; Zboril, R.;Kim, K.S. Functionalization of Graphene: Covalent and Non-Covalent Approaches, Derivatives andApplications. Chem. Rev. 2012, 112, 6156–6214. [CrossRef] [PubMed]
138. Rezapour, M.R.; Myung, C.W.; Yun, J.; Ghassami, A.; Li, N.; Yu, S.U.; Hajibabaei, A.; Park, Y.; Kim, K.S.Graphene and Graphene Analogs toward Optical, Electronic, Spintronic, Green-Chemical, Energy-Material,Sensing, and Medical Applications. ACS Appl. Mater. Interfaces 2017, 9, 24393–24406. [CrossRef] [PubMed]
139. Huang, X.; Yin, Z.; Wu, S.; Qi, X.; He, Q.; Zhang, Q.; Yan, Q.; Boey, F.; Zhang, H. Graphene-Based Materials:Synthesis, Characterization, Properties, and Applications. Small 2011, 7, 1876–1902. [CrossRef] [PubMed]
Nanomaterials 2017, 7, 305 28 of 28
140. Singh, V.; Joung, D.; Zhai, L.; Das, S.; Khondaker, S.I.; Seal, S. Graphene based materials: Past, present andfuture. Prog. Mater. Sci. 2011, 56, 1178–1271. [CrossRef]
141. Huang, X.; Qi, X.; Boey, F.; Zhang, H. Graphene-based composites. Chem. Soc. Rev. 2012, 41, 666–686.[CrossRef] [PubMed]
142. Brimicombe, P.D.; Gleeson, H.F. Private communication, 2008.143. Behabtu, N.; Lomeda, J.R.; Green, M.J.; Higginbotham, A.L.; Sinitskii, A.; Kosynkin, D.V.; Tsentalovich, D.;
Parra-Vasquez, A.N.G.; Schmidt, J.; Kesselman, E.; et al. Spontaneous high-concentration dispersions andliquid crystals of graphene. Nat. Nanotechnol. 2010, 5, 406–411. [CrossRef] [PubMed]
144. Kim, J.E.; Han, T.H.; Lee, S.H.; Kim, J.Y.; Ahn, C.W.; Yun, J.M.; Kim, S.O. Graphene Oxide Liquid Crystals.Angew. Chem. Int. Ed. 2011, 50, 3043–3047. [CrossRef] [PubMed]
145. Xu, Z.; Gao, C. Graphene chiral liquid crystals and macroscopic assembled fibres. Nat. Commun. 2011, 2, 571.[CrossRef] [PubMed]
146. Al-Zangana, S.; Iliut, M.; Turner, M.; Vijayaraghavan, A.; Dierking, I. Confinement effects on lyotropicnematic liquid crystal phases of graphene oxide dispersions. 2D Mater. 2017, 4, 41004. [CrossRef]
147. Dan, B.; Behabtu, N.; Martinez, A.; Evans, J.S.; Kosynkin, D.V.; Tour, J.M.; Pasquali, M.; Smalyukh, I.I.Liquid crystals of aqueous, giant graphene oxide flakes. Soft Matter 2011, 7, 11154–11159. [CrossRef]
148. Jalili, R.; Aboutalebi, S.H.; Esrafilzadeh, D.; Shepherd, R.L.; Chen, J.; Aminorroaya-Yamini, S.;Konstantinov, K.; Minett, A.I.; Razal, J.M.; Wallace, G.G. Scalable One-Step Wet-Spinning of GrapheneFibers and Yarns from Liquid Crystalline Dispersions of Graphene Oxide: Towards Multifunctional Textiles.Adv. Funct. Mater. 2013, 23, 5345–5354. [CrossRef]
149. Al-Zangana, S.; Iliut, M.; Boran, G.; Turner, M.; Vijayaraghavan, A.; Dierking, I. Dielectric spectroscopy ofisotropic liquids and liquid crystal phases with dispersed graphene oxide. Sci. Rep. 2016, 6, 31885. [CrossRef][PubMed]
150. Shen, T.-Z.; Hong, S.-H.; Song, J.-K. Electro-optical switching of graphene oxide liquid crystals with anextremely large Kerr coefficient. Nat. Mater. 2014, 13, 394–399. [CrossRef] [PubMed]
151. Kim, J.Y.; Kim, S.O. Liquid crystals: Electric fields line up graphene oxide. Nat. Mater. 2014, 13, 325–326.[CrossRef] [PubMed]
152. Zamora-Ledezma, C.; Puech, N.; Zakri, C.; Grelet, E.; Moulton, S.E.; Wallace, G.G.; Gambhir, S.; Blanc, C.;Anglaret, E.; Poulin, P. Liquid Crystallinity and Dimensions of Surfactant-Stabilized Sheets of ReducedGraphene Oxide. J. Phys. Chem. Lett. 2012, 3, 2425–2430. [CrossRef] [PubMed]
153. Lagerwall, J.P.F.; Scalia, G. Liquid Crystals with Nano and Microparticles; World Scientific: Singapore, 2017.154. Narayan, R.; Kim, J.E.; Kim, J.Y.; Lee, K.E.; Kim, S.O. Graphene Oxide Liquid Crystals: Discovery, Evolution
and Applications. Adv. Mater. 2016, 28, 3045–3068. [CrossRef] [PubMed]155. Lekkerkerker, H.N.W.; Vroege, G.J. Liquid crystal phase transitions in suspensions of mineral colloids:
New life from old roots. Philos. Trans. A Math. Phys. Eng. Sci. 2013, 371, 20120263. [CrossRef] [PubMed]
© 2017 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open accessarticle distributed under the terms and conditions of the Creative Commons Attribution(CC BY) license (http://creativecommons.org/licenses/by/4.0/).