USNASReg. No. 256/1-028
INSTITUT ZA VARILSTVOWel d in g I n s tit ute
Institutzavarilstvod.o.o.,Ptujska19,SI-1000Ljubljana Sheet lil
INSPECTION BODY - WELDING PROCEDURES
Welding procedure approval (WPAR) in accordance with 51ST EN ISO15614-1 + GL2000
No.: 33922/11 (E) Ljubljana, 09 Sept., 2011
Client 1 BIMONT d.o.o., Senčna ulica 19, 6310 Izola
Date of welding 1 Sveti Anton, 12 July, 2011 I DN: 1_6_8_98 _
The test pieces were produced on steel mat. no: W.Nr.:1.0570 (S355J2+N) and fulfil following' requirements:Tensile test Rmin ranqe 490-630 N/mmL Hardness HV10: <380HVBend angle 180° Imperfect shape - permitted for quality level C in accordance
with EN ISO 5817Impact toughnes: <':27Jpri T= -20°C Internal imperfections - permitted for quality level B in
accordance with EN ISO 5817
Range of approval:
Weldinq process MAG (136)Type ofweld Butt weld BW ssMaterial and group (SIST-TP CEN ISOfTR 15608) steel with nominal elastic limit Re:5355N/mm2 (gruppe1.1,
1.2)Thickness (mm) from 3,0 to 24,0Outer diameter (mm) above 0500,0Filler material EN ISO 17632-A: T 46 4 C/M1 H5Type of current DC (+)Welding position PFWelding process Shielding gas: CO2 (in acc. to SIST EN ISO 14175: C1)
Shieldinq root: ceramic backinq
I The approval of the welding procedure is based on the test results stated in Report no.: 33922/11 (E).
It is certified herewith that the test welds were prepared, welded and tested in accordance with therequirements of the test specifications and standards indicated above.
""$" .1 -'
.,;r-' ;;"il'"~ ,.,,.<. ~•..
Thedocumentmaybecopiesonlyasawhole!Obr.: OP-s; rev. 11, Priloga 3
USNAS
INSTITUT ZA VARILSTVOW el d i n g I n s tit ute
Institut za varilstvo d.o.o., Ptujska 19, SI-1000 Ljubljana
Reg. No. 256/1-028
Sheet lil
INSPECTION BODY - WELDING PROCEDURES
Welding procedure approval (WPAR) in accordance with 51ST EN ISO15614-1 + GL2000
No: 33923/11 (E) Ljubljana, 09 Sept., 2011
Client I BIMONT d.o.o., Senčna ulica 19, 6310 Izola
Date ofwelding I Sveti Anton, 12 July, 2011 ION: 1-=6...:...c89:....:.8 _
The test pieces were produced on steel mat.no.: W.Nr.:1.0570 (S355J2+N) and fulfil following requirementsfor fillet weld:Hardbess HV 10: < 380HV Imperfect shape - permitted for quality level C in accordance
with EN ISO 5817High of weld (mm): <': 6,0 (Muiti pass) Internal imperfections - permitted for quality level B in
accordance with EN ISO 5817
Range of approval:
Welding process MAG (136)Type ofweld Fillet weld FWMaterial and group (SIST-TP CEN ISOlTR 15608) steel with nominal elastic limit Re:5 355 N/mm2 (gruppe.:
1.1, 1.2)Thickness (mm) From 7,5 mm to 14,4 mmOuter diameter (mm) /
Throat thickness (mm) IFiller material EN ISO 17632-A: T 46 4 C/M1 H5Type of current DC (+)Weldinq position PFWelding process Shielding gas: CO2 (in acc. to SIST EN ISO 14175: C1)
I The approval of the welding procedure is based on the test results sta ted in Report no.: 33923/11 (E).
It is certified herewith that the test welds were prepared, welded and tested in accordance with there uirements of the test specifications and standards indicated above.
Slamp:
The document may be copies only as a whole!Obr.: OP-5; rev. 11, Priloga 3
VSNASReg. No. 256/1-028
INSTITUT ZA VARILSTVOW el d in g I n s tit ute
Institutzavarilstvod.o.o.,Ptujska19,SI-1000Ljubljana Sheet 111
INSPECTION BODY - WELDING PROCEDURES
Welding procedure approval (WPAR) in accordance with 51ST EN ISO15614-1 + GL2000
33924/11 (E)No: Ljubljana, 09 Sept., 2011
Client I BIMONT d.o.o., Senčna ulica 19, 6310 Izola
Date of we Idin9 I Sveti Anton, 14 July, 2011 ION: 16898
The test pieces were produced on steel mat. no: W.Nr.: 1.0570 (S355J2+N) and fulfil foliowinq requirements:Tensile test Rmin range 490-630 Nzmrn" Hardness HV10: <380HVBend angle 180° Imperfect shape - permitted for quality level C in accordance
with EN ISO 5817Impact toughnes: ~27J pri T= -20°C Internal imperfections - permitted for quality level B in
accordance with EN ISO 5817
Range of approval:
Weldinq process E (111)Type ofweld Butt weld BW ss nbMaterial and group (SIST-TP CEN ISOlTR 15608) steel with nominal elastic limit Res355N/mm2 (gruppe1.1,
1.2)Thickness (mm) from 3,0 to 24,0Outer diameter (mm) above 0500,0Filler material EN ISO 2560-A: E 42 4 B 32 H5Tvpe of current De (+)Weldinq position PEWeldinq process /
I The approval of the welding procedure is based on the test results stated in Report no.: 33924/11 (E).
It is certified herewith that the test welds were prepared, welded and tested in accordance with there uirements of the test s ecifications and standards indicated above.
Thedocumentmaybecopiesonlyasawhole!Obr.: DP-5; rev. 11, Priloga 3
USNASReg. No. 256/1-028
INSTITUT ZA VARILSTVOW el d i n g I n s tit ute
Institut za varilstvo d.o.o., Ptujska 19, SI-1000 Ljubljana Sheet 111
INSPECTION BODY - WELDING PROCEDURES
Welding procedure approval (WPAR) in accordance with 51ST EN ISO15614-1 + GL2000
33925/11 (E)No: Ljubljana, 09 Sept., 2011
Client I BIMONT d.o.o., Senčna ulica 19, 6310 Izola
Date of welding I Sveti Anton, 14 July, 2011 ION: 1_6_89_8 _
The test pieces were produced on steel mat. no.; W.Nr.:1.0570 (S355J2+N) and fulfil following requirementsfor fillet weld:Hardness HV 10: < 380HV Imperfect shape - permitted for quality level C in accordance
with EN ISO 5817High of weld (mm): ~ 10,0 (Muiti pass) Internal imperfections - permitted for quality level B in
accordance with EN ISO 5817
Range of approval:
Welding process E (111)Type ofweld Fillet weld FWMaterial and group (SIST-TP CEN ISOfTR 15608) steel with nominal elastic limit Re::; 355 N/mm2 (gruppe:
1.1, 1.2)Thickness (mm) From 10,0 mm to 24,0 mmOuter diameter (mm) 1Throat thickness (mm) /Filler material EN ISO 2560-A: E 42 4 B 32 H5Type of current De (+)Welding position POWelding process /
I The approval of the welding procedure is based on the test results stated in Report no.: 33925/11 (E).
It is certified herewith that the test welds were prepared, welded and tested in accordance with there uirements of the test s ecifications and standards indicated above.
The document may be copies only as a whole!Obr.: OP-5; rev. 11, Priloga 3
USNASReg. No. 256/1-028
INSTITUT ZA VARILSTVOW el d i n g In s tit ute
Institutzavarilstvod.o.o.,Ptujska19,SI-1000Ljubljana Sheef 111
INSPECTION BODY - WELDING PROCEDURES
Welding procedure approval (WPAR) in accordance with 51ST EN ISO15614-1 + GL2000
33926/11 (E)No.: Ljubljana, 09 Sept., 2011
Client I BIMONT d.o.o., Senčna ulica 19, 6310 Izola
Date of welding I Sveti Anton, 13 July, 2011 ION: 16898
The test pieces were produced on steel mat. no: W.Nr.:1.0570 (S355J2+N) and fulfil followinq requirements:Tensile test Rmin range 490-630 N/mm" Hardness HV10: <380HVBend angle 180° Imperfect shape - permitted for quality level C in accordance
with EN ISO 5817Impact toughnes: ~27J pri T= -20°C Internal imperfections - permitted for quality level B in
accordance with EN ISO 5817
Range of approval:
Weldinq process TIG(141)Type ofweld Butt weld BW ss nbMaterial and group (SIST-TP CEN ISOlTR 15608) steel with nominal elastic limit Re:S355N/mm2 (gruppe1.1,
1.2)Thickness (mm) from 3,0 to 12,6Outer diameter (mm) Above 025,5Filler material EN ISO 14341: G2 MoTvpe of current DG (-)Weldinq position HL045Welding process Shielding gas: Ar (in acc. to SIST EN ISO 14175: 11)
I The approval of the welding procedure is based on the test results stated in Report no.: 33922/11 (E).
It is certified herewith that the test welds were prepared, welded and tested in accordance with there uirements of the test s ecifications and standards indicated above.
Sfamp:
Thedocumentmaybecopiesonlyasawhole!Obr.: DP-5; rev. 11, Priloga 3
INSTITUT ZA VARILSTVOW el d in g I n s tit ute
Institut za varilstvo d.o.o., Ptujska 19, SI-1000 Ljubljana
USNASReg. No. 256/1-028
Sheet lil
INSPECTION BODY - WELDING PROCEDURES
Welding procedure approval (WPAR) in accordance with 51ST EN ISO15614-1
No.: 33345/11 (E) Ljubljana, 23 June, 2011
Client 1 BIMONT d.o.o., Senčna ulica 19, 6310 Izola
Date of welding 1 Sveti Anton, 10 June, 2011 ION: 1---'.6--=--85'--'-0 ---'
The test pieces were produced on steel mat.: tube - W.Nr.:1.0345 (P235GH) and plate - W.Nr.: 1.0425(P265GH) and fulfil foliowinq requirements:Hardness HV 10: < 380HV Imperfect shape - permitted for quality level C in accordance
with EN ISO 5817Internal imperfections - permitted for quality level B inaccordance with EN ISO 5817
Range of approval:
Welding process TIG(141)Type ofweld BW T - joint (tube on flanqe)Material and group (SIST-TP CEN ISOfTR 15608) steel with nominal elasticlimit Re:5265N/mm2 (gruppe 1.1)
Thickness (mm) tube: from 3,0 to 7,2 I plate: from 11,0 to 44,0Outer diameter (mm) above 038,0Filier material EN ISO 14341: G2 MoType of current De (-)Welding position PBOther informations Shielding gas: Ar (in ace. to SIST EN ISO 14175: 11)
Obr.: OP-S; rev. 11, Priloga 3
1 The approval of the welding procedure is based on the test results stated in Report no.: 33345/11 (E).
It is certified herewith that the test welds were prepared, welded and tested in accordance with there uirements of the test s ecifieations and standard indieated above.
Head of inspection body:d~J~ZO~1:;