CATIONICNANO INK TECHNOLOGY
®
Highbrow Trading International Pvt. Ltd., New Delhi, INDIAArt Store, Istanbul, Turkey
CATIONICNANO INK TECHNOLOGY
® SS-200
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-200
SS-200
SS-200
CATIONIC
SS-200
SS-100
CATIONICNANO INK TECHNOLOGY
® SS-400
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-400
CATIONIC
SS-400
SS-420
Water Based PU Elastic White
CATIONICNANO INK TECHNOLOGY
® SS-420
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-420
CATIONIC
SS-420
Water Based PU Elastic Clear
CATIONICNANO INK TECHNOLOGY
® SS-500
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-500
CATIONIC
SS-500
SS-500
SS-100
CATIONICNANO INK TECHNOLOGY
® SS-620Clear Base
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-620
CATIONIC
CATIONIC
CATIONICNANO INK TECHNOLOGY
® SS-700
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-700
CATIONIC
SS-100
CATIONICNANO INK TECHNOLOGY
® SS-720
CATIONIC
H
CATIONIC
NANO INK TECHNOLOGY
®
SS-720
CATIONIC
SS-720
SS-100
SS-800 Self Cure White
SS-800
SS-800 is special polymer hi-breed white for printing on 100% Dyed Polyester Active wearsand heat sensitive fabrics that needs to be cured at low temperature to avoid shrinkage.
No cure option in conjunction with cool-fix cross linker to avoid dye sublimation on 100% polyster.
CATIONIC
NANO INK TECHNOLOGY
®
Recommended formulation for elastic fabrics :
SS 800 elastic self cure white 750-900g
SS 820 elastic self cure flash base 250-100 g
1 Kg (1000g)
Cool fix cross linker to be added 3% by weight in flash
base as well as white to avoid.
Inter-coat adhesion problem
Should be low cured at 135-150C for 2 mins.
For self cure at room temperature for at least 48 hours before wash.
CATIONIC
CATIONIC
CATIONICNANO INK TECHNOLOGY
®
SS-820 Self Cure Flash Base
SS-820 is special polymer hi-breed flash cure base for printing on 100% Dyed Polyester Active wearsand heat sensitive fabrics that needs to be cured at low temperature to avoid shrinkage.
No cure option in conjunction with cool-fix cross linker to avoid dye sublimation on 100% polyster.
CATIONIC
NANO INK TECHNOLOGY
®
Recommended formulation for elastic fabrics :
SS 800 elastic self cure white 750-900g
SS 820 elastic self cure flash base 250-100 g
1 Kg (1000g)
Cool fix cross linker to be added 3% by weight in flash
base as well as white to avoid.
Inter-coat adhesion problem
Should be low cured at 135-150C for 2 mins.
For self cure at room temperature for at least 48 hours before wash.
CATIONIC
CATIONIC
SS 820 is an elastic low cure clear used to achieve an extra soft handfeel without losing elasticity in textile printing.
CATIONICNANO INK TECHNOLOGY
®
SS-900 Super Stretch Athletic White
SS-900 is special polymer hi-breed white for printing on Cotton / Spandex / Blended active wears and heat sensitive fabrics that needs to be cured at low temperature to avoid shrinkage.
Self cure ability in conjunction with cool-fix cross linker to avoid dye sublimation on 100% polyester.
CATIONIC
NANO INK TECHNOLOGY
®
Recommended formulation for elastic fabrics :
SS 900 elastic self cure white 750-900g
SS 920 elastic self cure flash base 250-100 g
1 Kg (1000g)
Cool fix cross linker to be added 3% by weight in flash
base as well as white to avoid.
Inter-coat adhesion problem
Should be low cured at 135-150C for 2 mins.
For self cure at room temperature for at least 48 hours before wash.
CATIONIC
CATIONIC
SS 900 is an elastic low cure white used to achieve an extra soft handfeel without losing elasticity in textile printing.
CATIONICNANO INK TECHNOLOGY
®
SS-920 Super Stretch Athletic Clear
SS-920 is special polymer hi-breed clear for printing on Cotton / Spandex / Blended active wears and heat sensitive fabrics that needs to be cured at low temperature to avoid shrinkage.
Self cure ability in conjunction with cool-fix cross linker to avoid dye sublimation on 100% polyester.
CATIONIC
NANO INK TECHNOLOGY
®
Recommended formulation for elastic fabrics :
SS 900 elastic self cure white 750-900g
SS 920 elastic self cure flash base 250-100 g
1 Kg (1000g)
Cool fix cross linker to be added 3% by weight in flash
base as well as white to avoid.
Inter-coat adhesion problem
Should be low cured at 135-150C for 2 mins.
For self cure at room temperature for at least 48 hours before wash.
CATIONIC
CATIONIC
SS 920 is an elastic low cure clear used to achieve an extra soft handfeel without losing elasticity in textile printing.
CATIONICNANO INK TECHNOLOGY
®
CATIONICNANO INK TECHNOLOGY
® SS-100
CATIONIC
CATIONIC
CATIONIC
NANO INK TECHNOLOGY
®
SS-100
SS-100
SS-100
SS-100
METALLICS BRIGHT GOLDCATIONICNANO INK TECHNOLOGY
®
CATIONIC METTALIC GOLD
Cationic Inks, Mahmutbey Mah. Atlas Cad. No:30Kat: 1-2-3 Bagcilar / ISTANBUL
0212 477 85 14, Fax : 0212 477 82 96
METALLICS BRIGHT SILVERCATIONICNANO INK TECHNOLOGY
®
CATIONIC METTALIC SILVER
Cationic Inks, Mahmutbey Mah. Atlas Cad. No:30Kat: 1-2-3 Bagcilar / ISTANBUL
0212 477 85 14, Fax : 0212 477 82 96
SS-630 Elastic Flock AdhesiveCATIONICNANO INK TECHNOLOGY
®
SS 100
CationicCationic
SS-100
CATIONIC
NANO INK TECHNOLOGY
®
SS-640 Elastic Foil AdhesiveCATIONICNANO INK TECHNOLOGY
®
CationicCationic
SS-100
CATIONIC
NANO INK TECHNOLOGY
®
CationicCationic
SS-580
SS-580 Pull
SS-580 Thermo-Cracking Mixing Base
CATIONICNANO INK TECHNOLOGY
®
CATIONIC
NANO INK TECHNOLOGY
®
SS-590 Thermo-Cracking WhiteCATIONICNANO INK TECHNOLOGY
®
CationicCationic
CATIONIC
NANO INK TECHNOLOGY
®
Pull
SS DasConsultant Director - Global Sales, Cationic Range Product Development and Customer CareContact : +91-9810342899Email : [email protected] Delhi, INDIA
Kerim GulerDirector and Managing PartnerContact : +90 542 740 25 93Email : [email protected] Mah. Atlas Cad. No. 30 Kat: 1-2-3 Bagcilar / Istanbul, Turkey
1. Elastic Flock Adhesive
2. Elastic Foil Adhesive
3. Burn Out
4. Iridescent Metallics & Glitters
5. Thermo Cracking White & Clear
6. Water base Denim Print White & Clear
7. Water base Nylon White & Clear
8. HD Series of water base inks
9. Cold Catalyst
10. PU Thickner, Softner and Binders
CATIONICNANO INK TECHNOLOGY
®
Offers ....Speciality Range on Request
Recommended