October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
1
Effects of cement components and
contaminants on dehydrogenase activity
in a mixed contaminated soi l
Reginald B. Kogbara1,2
1Department of Engineering, University of Cambridge, Trumpington Street, Cambridge CB2 1PZ, UK.
2Present Address: Mechanical Engineering Program, Texas A&M University at Qatar,
P.O. Box 23874, Education City, Doha, Qatar.
Email: [email protected]
Summary
Microbiological findings from investigations aimed at encouraging biodegradation of organics
within cement-stabilized contaminated soils revealed that magnesium phosphate cement could
resuscitate and sustain microbial activity in a heavily polluted soil. Microbial activity in soil
contaminated with lead nitrate, zinc chloride and 2-chlorobenzoic acid and treated with
magnesium phosphate cement formulations was monitored using dehydrogenase assay. Low
levels of the contaminants stimulated soil dehydrogenase activity. There was a total inhibition of
soil dehydrogenase activity at co-contamination levels above 1500 mg/kg. Magnesium oxide is
identified as a stimulant, triple super phosphate an inhibitor, of dehydrogenase activity. The
implications of these findings would be useful in improving the robustness of biological clean-up
Some of the findings in this report have been published as part of a wider study in the paper,
Kogbara et al. (2011), Water Air Soil Pollut. 216: 411–427, DOI: 10.1007/s11270-010-0541-7.
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
2
of polluted sites, as well as in fertiliser management practices for agricultural productivity.
Introduction
Co-contamination with organics and heavy metals is a common feature of polluted soils. This
has led to concerted efforts to develop remediation techniques that could deal with a wide range
of contamination. One such technique is the incorporation of a biodegradative mechanism
within a soil treated with stabilization/solidification (S/S) binders. Stabilization/solidification
basically involves chemical fixation and physical encapsulation of contaminants by the addition
of binders, mainly Portland cement-(PC) based (Kogbara et al., 2011a; Kogbara et al., 2012). It
is effective and widely used for treatment of heavy metals but not very effective with organics.
Details of the techniques and processes of the technology can be found elsewhere (Conner and
Hoeffner, 1998).
Successful incorporation of a biodegradative mechanism within stabilized/solidified soils
requires a cementititious system with pH lower than that of PC (12 – 13) since the high alkalinity
of PC is unsuitable for biological activity. This led to research into magnesium phosphate
cements (MPCs). MPCs like other phosphate based cements are formed at room temperature by
rapid acid-base reaction between dead burned magnesia and an acid phosphate source. A
comprehensive d e s c r ip t io n o f t he cem en t has b een docum ented ( Wagh, 2 0 0 4 ). A
m a j o r advantage of MPCs beneficial to biological activity is its potential to form mixes with
different pH ranges, depending on the magnesia and phosphate contents. The MPCs
employed in this study had triple super phosphate (TSP, supplied by RS Minerals, UK) as acid
phosphate source and dead burned magnesia (MgO, Richard Baker Harrison, UK) as base
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
3
source. TSP is a common fertilizer; it is composed mainly of calcium dihydrogen phosphate,
and also contains some gypsum (Iyengar and Al-Tabbaa, 2008). The chemical constituents of
dead burned magnesia have been reported (Harbottle and Al-Tabbaa 2008; Kogbara et al.,
2011b).
Harbottle and Al-Tabbaa (2006) investigated enhancing microbial activity in cementitious
systems using different additives like compost, nutrients, oxygen releasing compounds, water
retaining compounds and carbon sources. The study demonstrated the effectiveness of compost
in this regard as it provides a nutrient and microbe source as well as enhances the porosity of the
final S/S treated soil. Compost has also been found to enhance biodegradation of
recalcitrant hydrocarbons in hazardous wastes (Ayotamuno et al., 2010). The above
cited works set the stage for the present study which sought to encourage microbial activity
within a co-contaminated soil amended with compost and treated with magnesium phosphate
cement formulations. It is thought that successful maintenance of microbial life within an S/S
system would bring about a sustainable remediation technique where heavy metals are stabilized
and organics biodegraded over time. Thus, it was the aim of this study to investigate the
possibility of encouraging microbial activity in a co-contaminated soil with relatively high
concentration of contaminants, treated with an S/S binder.
In the experiments described, a model silty sand soil was prepared using Fraction-D Leighton
Buzzard sand (D50 ~150-300µm, David Ball Ltd., UK) and silt (silica flour, D50< 150µm, David Ball
Ltd, UK). Eco-compost (sieved past 2mm; Scotsdales Ltd, Cambridge, UK) was added as organic
matter to provide a microbial inoculum as well as a source of nutrients and to enhance the porosity of
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
4
the soil/cement system. A model soil was used in place of real site soil so that the exact chemical
composition of the soil would be known and any effect on microbial assay test result by soil elements
isolated. The soil was composed of 70% sand, 20% silt and 10% compost. It had 15% moisture
content, dry weight. The effect of increased compost content on microbial activity was examined by
using a soil composed of 60% sand, 15% silt and 25% compost. The soil was contaminated with 2-
chlorobenzoic acid, lead nitrate and zinc chloride as organic and metallic contaminants and treated
with magnesium phosphate cement formulations.
Microbial activity was monitored using dehydrogenase assay following the combined methods of
Casida et al. (1964) and Harbottle and Al-Tabbaa (2008). The assay is indicative of the total
metabolic activity of soil microorganisms and has been used in several works (Weaver et al.,
1994). It has been shown to be very sensitive for evaluating the toxicity of anthropogenic
pollutants in soil (Gong et al., 1997). The test involved 6g of soil or crushed soil-cement and 3.5
ml of 0.75% 2,3,5-Triphenyltetrazolium chloride (TTC) solution containing 50mM Trizma
hydrochloride. Incubation was done for 24 hours at 37 C. Extraction of 2,3,5-
triphenyltetrazolium formazan (TPF—a water-insoluble red dye) was done with ethanol and the
concentration measured with a UV/VIS Spectrophotometer at a wavelength of 485 nm.
Results and discussion
Contamination of the soil with 3000 mg/kg each of lead nitrate, zinc chloride and 2-
chlorobenzoic acid caused a total inhibition of dehydrogenase activity, but the uncontaminated
soil with 10% and 25% compost had 3.582 µg TPF/ml and 6.270 µg TPF/ml respectively. Soil
contamination with 3000 mg/kg of only 2CBA and simultaneous addition of 3000 mg/kg of all
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
5
three contaminants to compost only, further demonstrated that dehydrogenase activity was
inhibited by the high concentration of contaminants (Table 1, section A). Previous studies have
reported significant inhibition of soil microbial activity by heavy metals. Marzadori et al. (1996)
reported significant decrease in dehydrogenase activity with the addition of 5000 mg/kg lead,
while Salminen et al. (2001) reported that microbial biomass and activity were clearly reduced at
a zinc concentration of 1000 mg/kg. Compared with single pollutants, combined pollution is
obviously much more complex. Results obtained from combined pollution are generally more
difficult to interpret because of large number of factors and interactions between factors (Gong et
al., 1997). This led to investigations on the concentrations of the contaminants that can be
tolerated.
Five levels of co-contamination were arbitrarily chosen to investigate the range of concentration
at which dehydrogenase activity can occur in the soil. Section B of Table 1 shows that at levels
of contamination up to 187.5 mg/kg there was a stimulation of soil dehydrogenase activity as the
amount of TPF produced was more than that of the uncontaminated soil. Significant stimulation
of dehydrogenase activity has previously been observed on contaminated soil with poplar but
was thought to be influenced by the covering plant (Gong et al., 1997). The data shows that at
lower contaminant concentrations the contaminants may be useful to soil microbes as nutrients
thereby stimulating microbial activity. This is similar to the findings of previous studies where
microbial numbers increased in the aftermath of hydrocarbon contamination (Ayotamuno et al.,
2006; Kogbara 2008). However, at 750 mg/kg co-contamination, dehydrogenase activity was
reduced. At co-contamination levels ≥1,500 mg/kg there was a total inhibition of microbial
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
6
activity.
Table 1. Dehydrogenase activity measurements on soil
Section Treatment Dehydrogenase activity
(µg TPF/ml)
A Model soil with 10% compost, contaminated with
3000 mg/kg each of 2CBA, Pb(NO3)2 and ZnCl2
0.000
Uncontaminated model soil with 10% compost content 3.582 + 1.476
Uncontaminated model soil with 25% compost content 6.270 + 0.138
Compost only, with 3000 mg/kg co-contamination 0.000
Model soil with 10% compost, contaminated with
3000 mg/kg of only 2CBA
0.000
B Simultaneous addition of 2CBA,
Pb(NO3)2 and ZnCl2 to model soil
with 10% compost content at the
following concentrations
0 mg/kg 3.582 + 1.476
93.75 mg/kg 7.602 + 1.080
187.5 mg/kg 5.724 + 1.230
750 mg/kg 3.000 + 0.792
1,500 mg/kg 0.000
2,250 mg/kg 0.000
Results represent mean + standard deviation of three replicates
After the contaminated soil was treated with two MPC formulations, it was observed that one
formulation resuscitated dehydrogenase activity while the other did not. The two cement
formulations used had the base materials mixed in the ratio, TSP:MgO = 8:1 for the lower pH
end (~6.5) and TSP:MgO = 1:2 for the higher pH end (~10). The soil:cement ratio was 2:1 for
both formulations. De-ionised water was used to produce the wet grout in which the
cement:water ratio was 2:1. Contaminated soil samples treated with TSP:MgO = 1:2 showed
evidence of microbial activity after 14 days of treatment but those treated with TSP:MgO = 8:1
did not. To investigate this, dehydrogenase activity test was carried out on crushed soil-cement
samples without any contamination, five days after treatment, and it was observed that samples
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
7
treated with TSP:MgO=1:2 had evidence of dehydrogenase activity (3.408 µg TPF/ml) while
those treated with TSP:MgO=8:1 did not show any trace of dehydrogenase activity (Table 2). At
this stage, it was hypothesized that the influence of pH noted by Mahmoud and Ghaly (2004),
whereby high pH environments (9.5 < pH < 13) can lead to non-enzymatic production of TPF in
the TTC dehydrogenase assay may be responsible for the dehydrogenase activity observed in
samples with the higher pH. However, tests on the cement constituents only, showed that this
was not the case as the cement formulations at pH extremes, 6.5 and 10 exhibited abiotic
dehydrogenase activities of 2.562 and 3.300 µg TPF/ml respectively (Table 2).
Further tests were carried out on the base materials, MgO and TSP, and the results demonstrated
that the abiotic dehydrogenase activity observed was due to the effect of dead burned magnesia.
The material induces the same coloration (pink to reddish) ascribed to the action of
dehydrogenase enzymes in the assay. With TSP alone there was no trace of abiotic
dehydrogenase activity which shows that the abiotic dehydrogenase activity observed in the
mixtures of cement constituents only was due to MgO stimulation. Although the mixture of
cement constituents only with TSP:MgO=8:1 exhibited abiotic dehydrogenase activity,
surprisingly when it was used for S/S treatment of the contaminated soil there was no trace of
dehydrogenase activity. The said cement formulation was projected to be favorable for microbial
activity due to its near neutral pH.
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
8
Table 2. Dehydrogenase activity measurements on soil-cement components
Treatment Dehydrogenase activity
(µg TPF/ml)
Uncontaminated soil with 10% compost content treated
with TSP:MgO = 8:1 cement (after 5 days)
Uncontaminated soil with 10% compost content treated
with TSP:MgO = 1:2 cement (after 5days)
0.000
3.408 + 0.318
Cement constituents only, TSP:MgO = 8:1 (pH~6.5) 2.562 + 0.000 (abiotic)
Cement constituents only, TSP:MgO = 1:2 (pH~10) 3.300 + 0.018 (abiotic)
Triple Super Phosphate (TSP) only 0.000
Dead burned magnesia (MgO) only 2.526 + 0.054 (abiotic)
2.5%, 5%, 10%, 20% and 30% of TSP in a mixture of
compost and TSP, without any contamination
0.000
Results represent mean + standard deviation of three replicates
The above findings led to the hypothesis that TSP might inhibit dehydrogenase activity. To test
the hypothesis, different amounts of TSP was added to uncontaminated compost such that the
amount of TSP in the mixture of compost and TSP ranged from 2.5% - 30% (Table 2). There
was no trace of dehydrogenase activity even with the lowest amount of TSP in the mixture. This
demonstrated that TSP is an inhibitor of dehydrogenase activity. This is surprising as the
literature has it that phosphates stimulate soil microbial activity. A number of substances that
could stimulate or inhibit dehydrogenase activity have been documented but neither MgO nor
TSP was listed (Weaver et al., 1994). Similar findings in this direction previously reported
include: magnesium stimulation of catalytic activity of horse liver aldehyde dehydrogenase
(Takahashi and Weiner, 1980), superphosphate reduction of bacterial populations (Kelly and
Henderson, 1978) and inhibitory effects of TSP on microbial respiration and substrate induced
respiration (Thirukkumaran and Parkinson, 2000).
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
9
Noteworthy is the fact that although TSP inhibits microbial activity, the cement constituents
with TSP:MgO = 8:1 and TSP:MgO =1:2 had evidence of abiotic dehydrogenase activity. This
was due to MgO stimulation as the amount of TPF produced in the former was less than that in
the latter. Moreover, it is likely that the reaction product of the mixture, Ca-Struvite could also
enhance the stimulation as reports by Takahashi and Weiner (1980) have it that catalytic activity
of horse liver aldehyde dehydrogenase was also activated by the presence of Ca2+
. The absence
of dehydrogenase activity in contaminated soil samples treated with TSP:MgO=8:1 cement
formulation could be ascribed to limiting amount of MgO in the whole mixture thus giving way
to inhibition by TSP.
These results suggests that the dehydrogenase activity observed in contaminated soil samples
treated with TSP:MgO =1:2 cement formulation had a biotic and an abiotic component. The
biotic component was evaluated by using three kinds of treatment: soil with 10% compost
contaminated with all three contaminants (3000 mg/kg each), same with only 2CBA, and soil
with 25% compost contaminated with all three contaminants. The dehydrogenase activity results
after 14 and 28 days are shown in Figure 1. The error bars represent the standard deviation of
three replicates. Much of the hydration of typical cements is achieved in 28 days hence the test
was carried out at the set periods. Overall, the results show that the amount of TPF produced was
generally higher than that associated with abiotic dehydrogenase activity. Moreover,
the presence of heavy metal contaminants and increased amounts of compost caused different
trends in microbial activity with time. Samples with 10% compost (C) and only 2CBA, and 25%
compost content with all contaminants had higher dehydrogenase activities than those with 10%
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
10
compost and all contaminants at 14 and 28 days. The results demonstrate that the application of
the cement formulation to a heavily polluted soil where microbial activity was inhibited could
resuscitate and sustain it for a period. Chemical fixation of contaminants thus reducing their
toxicity to soil microbes coupled with magnesium oxide stimulation of microbial activity may
well be the mechanisms responsible.
10% C, all contam. 10% C, 2CBA only 25% C, all contam.
Figure 1. Dehydrogenase activity measurements in TSP:MgO=1:2 soil-cement samples
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
11
Conclusions
The findings of this study has shown that the application of magnesium phosphate cement
formulation with the appropriate magnesia content to a heavily polluted soil where microbial
activity is inhibited could resuscitate and sustain it for a period of time. This knowledge would
be useful in improving the robustness of S/S technology as it would facilitate the incorporation
of a biodegradation mechanism thus leading to a more sustainable remediation technology. A
useful implication of these findings is that magnesium oxide may be effective in stimulating
microbial activity in a heavily polluted soil where it is limiting. The inhibition of microbial
activity by triple super phosphate observed in the study informs the need to review fertilizer
management practices, especially its effect on the contribution of soil biota to agricultural
productivity.
Acknowledgements
The provision of financial support for this work by the Cambridge Commonwealth Trust is
gratefully acknowledged.
References
Ayotamuno, J.M., Kogbara, R.B., Ogaji, S.O.T., and Probert, S.D. (2006). Bioremediation of a
crude-oil polluted agricultural-soil at Port Harcourt, Nigeria. Applied Energy, 83 (11), 1249 –
1257.
Ayotamuno, J.M., Kogbara, R.B., Agele, E.A., and Agoro, O.S. (2010). Composting and
phytoremediation treatment of petroleum sludge. Soil and Sediment Contamination, 19 (6), 686 –
695.
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
12
Cassida, L.E. Jr., Klein, D.A., and Santoro, T. (1964). Soil dehydrogenase activity. Soil Science,
98, 371 – 376.
Conner, J.R., and Hoeffner, S.L. (1998). A critical review of stabilization/solidification
technology. Critical Reviews in Environmental Science & Technology, 28 (4), 397 – 462.
Gong P., Sun, T-H., Beudert, G., and Hahn, H.H. (1997). Ecological effects of combined organic
or inorganic pollution on soil microbial activities. Water, Air, & Soil Pollution, 96, 133 – 143.
Harbottle, M., and Al-Tabbaa, A. (2006). Combining stabilisation / solidification with
biodegradation to enhance long-term remediation performance. In Proceedings of the second
IASTED International Conference on Advanced Technology in the Environmental Field. Ubetini,
L. (ed). Lanzarote, Spain: Acta Press, pp. 222 – 227.
Harbottle, M.J., and Al-Tabbaa, A. (2008). Degradation of 2-chlorobenzoic acid in
stabilised/solidified soil systems. International Biodeterioration & Biodegradation, 61, 173 -
181.
Iyengar, S., and Al-Tabbaa, A. (2008). Application of two novel magnesia-based cements in
stabilisation/solidification of contaminated soils. In Proceedings of GeoCongress: Geotechnics
of waste management and remediation. Khire, M.V., Alshawabkeh, A.N., and Reddy, K.R. (eds).
New Orleans: American Society of Civil Engineers, pp. 716 - 723.
Kelly, J.M., and Henderson, G.S. (1978). Effects of nitrogen and phosphorus additions on
deciduous litter decomposition. Soil Science Society of America Journal, 42, 972 – 976.
Kogbara, R.B. (2008). Ranking agro-technical methods and environmental parameters in the
biodegradation of petroleum-contaminated soils in Nigeria. Electronic Journal of
Biotechnology, 11 (1), 113 – 125.
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
13
Kogbara, R.B., Yi, Y., and Al-Tabbaa, A. (2011). Process envelopes for
stabilisation/solidification of contaminated soil using lime–slag blend. Environmental Science
and Pollution Research, 18 (8), 1286 – 1296.
Kogbara, R.B., Al-Tabbaa, A., and Iyengar, S.R. (2011). Utilisation of magnesium phosphate
cements to facilitate biodegradation within a stabilised/solidified contaminated soil. Water, Air,
& Soil Pollution, 216 (1-4), 411 – 427.
Kogbara, R.B., Al-Tabbaa, A., Yi, Y., and Stegemann, J.A. (2012). pH-dependent leaching
behaviour and other performance properties of cement-treated mixed contaminated soil. Journal
of Environmental Sciences, 24 (9), 1630 – 1638.
Mahmoud, N.S., and Ghaly, A.E. (2004). Influence of temperature and pH on the nonenzymatic
reduction of triphenyltetrazolium chloride. Biotechnology Progress, 20, 346 – 353.
Marzadori, C., Ciavatta, C., Montecchio, D., and Gessa, C. (1996). Effects of lead pollution on
different soil enzyme activities. Biology & Fertility of Soils, 22, 53 – 58.
Salminem, J., Anh, B.T., and Van Gestel, C.A.M. (2001). Enchytraeids and microbes in Zn
polluted soil: No link between organic level stress responses and ecosystem functioning.
Ecotoxicology, 10, 351 – 361.
Takahashi, K., and Weiner, H. (1980). Magnesium stimulation of catalytic activity of horse liver
aldehyde dehydrogenase. Journal of Biological Chemistry, 255(17), 8206 – 8209.
Thirukkumaran, C.M., and Parkinson, D. (2000). Microbial respiration, biomass, metabolic
quotient and litter decomposition in a lodgepole pine forest floor amended with nitrogen and
phosphorous fertilizers. Soil Biology & Biochemistry, 32, 59 – 66.
October 2012
Laboratory Report on Dehydrogenase Assay Experiments in Soil-Cement Systems
14
Wagh, A.S. (2004). Chemically bonded phosphate ceramics, 1st edn. Oxford: Elsevier.
Weaver, R.W., Angle, J.S., and Bottomley, P.S. (eds). (1994). Methods of soil analysis, Part 2
– microbiological and biological and biochemical properties. Madison: Soil Science Society of
America Book series, No. 5.