COMPOSITESSCIENCE AND
Composites Science and Technology 64 (2004) 2031–2038
TECHNOLOGY
www.elsevier.com/locate/compscitech
Comparison of short carbon fibre surface treatments onepoxy composites
II. Enhancement of the wear resistance
Hui Zhang, Zhong Zhang *
Institute for Composite Materials, University of Kaiserslautern, Erwin Schr€odinger Str. 58, 67663 Kaiserslautern, Germany
Received 7 August 2003; accepted 22 February 2004
Available online 9 April 2004
Abstract
In this study, pitch-based short carbon fibres were treated by both an air oxidation and a cryogenic treatment, thereafter these
fibres were incorporated into epoxy matrix for wear investigations. It was found that under an appropriate air oxidative condition,
the wear resistance of carbon fibre reinforced epoxy was significantly improved at low contact pressure, whereas that was reduced at
high pressures which may due to the damage of fibre mechanical properties after oxidation. On the contrary, carbon fibres pre-
formed better at high sliding pressure after cryogenic treatment. Correlated wear mechanisms were discussed.
� 2004 Elsevier Ltd. All rights reserved.
Keywords: Wear resistance; Short carbon fibre; Fibre treatment; Air oxidation; Cryogenic treatment; Epoxy matrix
1. Introduction
Possessing of excellent mechanical and tribological
properties, carbon fibre reinforced plastics (CFRP) are
increasingly being used for many different applications.
More and more industrial components, e.g., bushings,
cams, gears, rollers, wheels, brakes, conveyors, andsliding shoes, etc., are manufactured from short/con-
tinuous carbon fibres reinforced composites, where
friction and wear are key parameters to be taken into
consideration. In the past years, many researchers have
focused on the tribological behaviours of CFRP in
various directions. Lancaster co-workers [1–5] found
that the wear performance of CFRP under lubricated
conditions was influenced by the types of carbon fibreand matrix materials, the counterface and its surface
roughness, the experimental temperature, and the for-
mation of transferred film as well. Voss and Friedrich
* Corresponding author. Tel.: +49-631-201-7213; fax: +49-631-201-
7196.
E-mail address: [email protected] (Z. Zhang).
0266-3538/$ - see front matter � 2004 Elsevier Ltd. All rights reserved.
doi:10.1016/j.compscitech.2004.02.010
[6] reported that, compared to glass fibres, short carbon
fibres show better potential to an enhanced wear re-
sistance for PEEK matrix at different pv-factors
(product of contact pressure and sliding velocity). The
effect on friction and wear of carbon fibre orientation
and surface temperatures of unidirectional fibre com-
posites were also investigated in detail by Tripathy andFurey [7]. Lu and Friedrich [8,9] studied systematically
the influence of carbon fibre volume fraction of their
composites on friction and wear, and declared that an
optimum range for short carbon fibre in PEEK matrix
is 15–25 vol% according to the improved specific wear
rate.
In the theoretical analysis, Voss and Friedrich [6] also
developed a semi-empirical formula for sliding wear ofshort fibre composites as following
WsC ¼ 1
ð1� VFÞW �1sM þ 0:5ð1þ V c
F ÞVFW �1sFs
þ 0:5ð1� V cF ÞVFWsFci; ð1Þ
where WsC is the total wear rate of composites, WsM is the
wear rate of the unfilled matrix, WsFs is the wear rate of
Table 1
Details of specimens and treatment conditions
Treatment
approach
Sample no. CF volume
content
Treatment
details
– CF_0 15% As-received
Oxidation (in air) CF_450 15% 450 �C/1 h
CF_500 15% 500 �C/1 h
CF_550_1 15% 550 �C/1 h
CF_550_2 15% 550 �C/2 h
CF_600 15% 600 �C/1 h
Cryogenic treatment CF_1 15% 1 min
(in liquid nitrogen) CF_5 15% 5 min
CF_10 15% 10 min
CF_20 15% 20 min
Block Specimen
Normal Force Dead Weight
Ring: Counterpart Steel 100Cr6 (DIN) Polished
Fig. 1. A schematic diagram of a block-on-ring test apparatus.
2032 H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038
the fibre, WsFci accounts for fibre cracking and sub-
sequent processes of fibre–matrix separation at the in-
terface, VF is the fibre volume fraction, and c determines
how fast the transition from one process to another
occurs once VF is altered. In this equation, the totalvolume wear rate, WsC, is composed by two items. The
first item reflects the contribution of fibre and matrix to
the wear rate, whereas the second item reflects the in-
fluence of fibre–matrix interface due to the fibre crack-
ing, the subsequent fibre–matrix debonding and
separation at the interface. According to Eq. (1), it is
clear that the enhancement of the fibre–matrix interfa-
cial bonding is expected to be beneficial to an improvedwear resistance of composites, which will be concen-
trated on the present paper.
It is well known that treatment and modification of
carbon fibre surface are, generally speaking, of help to
enhance the interfacial bonding between fibre and ma-
trix. In the first part of this paper [10], two different
kinds of surface treatments, i.e. air oxidation and
cryogenic treatment, were concentrated on short carbonfibres (CF), which effectively improved the mechanical
properties of CF/epoxy composites due to the en-
hancement on fibre–matrix interfacial bonding. In the
present study, the wear performance of untreated and
treated CF/EP composites under various nominal con-
tact pressures were compared using a block-on-ring test
apparatus. The worn surfaces were observed by SEM,
and wear mechanisms were discussed.
2. Experimental
2.1. Materials
The matrix used was a bisphenol-A type resin
(DER331, Dow) hardened by an amine curing agent(HY2954, Dow). Pitch-based short carbon fibres with-
out any treatments were supplied by Kureha Co.
(M-2007S). Details of fibre surface treatments by hot air
or liquid nitrogen, as well as the preparation procedures
of epoxy composites, were given in the first part of this
paper [10] (represented in Table 1 as well).
2.2. Wear test
Unlubricated sliding wear tests were carried out on a
block-on-ring apparatus designed and constructed at the
IVW (Fig. 1). A hardened and polished carbon steel ring
(German Standard 100Cr6) with a diameter of 60 mm
and initial surface roughness of Ra ¼ 0:1 lm served as
counterpart. The sliding velocity was kept constant at
1 m/s, while the contact pressure was adjusted in a rangebetween 0.5 and 5 MPa. The test duration was set to
20 h. All measurements were performed at room tem-
perature. The specimen�s weight loss after experiments,
Dm, was measured by an analytical balance with a pre-
cision of 0.01 mg. Finally, the specific wear rate Ws andthe time-related depth wear rate Wt were calculated ac-
cording to the following equations
Ws ¼DmqFNL
ðmm3=N mÞ; ð2Þ
Wt ¼ k� � pv ðm=sÞ; ð3Þwhere q is the density of the specimen, FN is the normal
load applied on the specimen during sliding, L is the
total sliding distance, p is the nominal contact pressure
on the specimen and v is the sliding velocity of the ring.
k� is often referred in literatures as the ‘‘wear factor’’,which is equal to Ws numerically. k� is a factor depended
on the properties of the two materials in contact and the
dominant wear mechanisms. In the case of moderate pv
product, k� should be constant, however k� value may
significantly increase at higher pv-factor, in which severe
wear occurs correlated to different wear mechanisms
[11]. At least six specimens of each composition were
measured, and an average value was reported with anerror scatter of the maximum absolute error.
2.3. SEM worn surface observation
After wear test, the worn surfaces were investigated
by both a scanning electron microscopy (SEM) and a
laser profilometry. The roughness of worn surface was
H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038 2033
calculated by software supplied by UBM Messtechnik
Company.
3. Results and discussion
3.1. Neat matrix and untreated-CF/epoxy at a pv-factor
of 1 MPa m/s
Measured by a block-on-ring apparatus after a test
duration of 20 h at a pv-factor of 1 MPa m/s, the specific
Fig. 3. Worn surfaces of untreated CF/EP composites (p ¼ 1 MPa, v ¼ 1 m/s)
fibre thinning; (b) fibre broken; and (c) fibre peeling off.
Fig. 2. Worn surface of (a) neat epoxy, and (b) untrea
wear rates of neat epoxy and untreated short-CF/EP
composites were 6.92� 10�6 and 1.48� 10�6 mm3/N m,
respectively. It is clear that the addition of 15 vol% of
untreated short-CF could significantly improve the wear
resistance of epoxy, which was also reported for otherpolymers [1,2,6,8,12].
In order to understand the corresponding wear
mechanisms, worn surfaces of epoxy and its composite
were observed by SEM (as show in Fig. 2). Regarding
to neat epoxy, it is clear that the fatigue wear is the
dominative wear mechanism which was caused by the
, which demonstrate the three sequential stages during sliding wear: (a)
ted CF/EP composites (p ¼ 1 MPa, v ¼ 1 m/s).
2034 H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038
repeated very high local stresses in the course of sliding.
Many fatigue wear particles can be recognized on the
worn surface of neat epoxy in Fig. 2(a). In this case,
wear is mainly determined by the crack initiation, crack
growth and facture, which are relatively poor of neatepoxy. Regarding to untreated CF/EP, the worn surface
given in Fig. 2(b) is smoother than that of the neat ep-
oxy. Even the major wear mechanism is still fatigue
1.160.47 0.61
6.92
1.030.751.48
0
2
4
6
8
10
Neat
CF_0
CF_450
CF_500
550_
1
550_
2
CF_600
Ws
[10-6
mm
3 /Nm
]
Fig. 4. Influence of air treatment conditions on the enhancement of
wear resistance of short carbon fibre reinforced epoxy composites
(p ¼ 1 MPa, v ¼ 1 m/s).
Fig. 5. Worn surfaces of air-treated CF/EP composites at different treatmen
wear, short carbon fibre thinning, broken, and peeling
off become dominant [12–14]. As shown in Fig. 3(a)–(c)
of the three sequential stages of fibre wear mentioned
above, it can be found that carbon fibres were exposed
on the sliding surface, supported mainly the sliding loadapplied, and protected matrix material to avoid being
ploughed and torn during wear process [12].
3.2. Oxidative-treated CF/EP at a pv-factor of 1 MPa m/s
Fig. 4 illustrates the effect of air treatment conditions
on the specific wear rate of CF/EP composites. Experi-
ments were performed at room temperature under acontact pressure of 1 MPa and a sliding velocity of 1 m/s.
All oxidative-treated samples more or less exhibited an
improved wear resistance, although the tendency was not
very clear. This also implied that the wear mechanisms
might be controlled by several factors. When the treat-
ment temperature was between 450 and 500 �C, the
variation of Ws was indistinct. Under a treatment con-
dition of 550 �C for 1 h (CF_550_1), a lowest Ws wasachieved, i.e., 0.47� 10�6 mm3/N m, which is less than
one-third of that of untreated ones. When continually
t conditions: (a,b) 550 �C/1 h, (c) 600 �C/1 h (p ¼ 1 MPa, v ¼ 1 m/s).
Table 2
Wear factors and roughness of worn surface of untreated and treated
CF/EP composites
No. k� (10�6 mm3/N m) Fitted scope
of pressure
(MPa)
Roughness of
worn surface at
1 MPa m/s (lm)
CF_0 3.16 0.5–5 0.80
CF_550_1 1.31 0.5–2 0.71
CF_20 2.25 0.5–5 0.87
30 CF_0
H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038 2035
increasing the treatment temperature or time, Ws, how-
ever, increased again.
Carbon fibre surface treatment is usually accompa-
nied with the change of the fibre�s mechanical properties
(cf. [10]), which may consequently affect the wear rate ofcomposites. Therefore, the wear rate of composites is
considered to be governed by two essential causes, i.e.,
fibre–matrix interfacial bonding and fibre mechanical
properties. In the case of oxidative treatment, the first
item in Eq. (1) can be considered as constant since a
constant VF was applied. For the second item in Eq. (1),
due to the enhanced fibre–matrix interfacial adhesion,
few fibres debonding occurred and the broken fibres weremaintained in the matrix. As a result, the value of the
second item of Eq. (1) was reduced, accordingly reduced
the wear rate of composites. On the worn surface
of oxidative-treated specimen (CF_550_1) given in
Fig. 5(a), less groove and fibre peeling-off can be de-
tected, comparing to that of untreated one in Fig. 2(b).
The high magnification micrograph of Fig. 5(b) illus-
trates that the oxidative treatment improved the fibre–
1.160.47 0.61
6.92
1.030.751.48
0
2
4
6
8
10
Neat
CF_0
CF_450
CF_500
CF_550
_1
CF_550
_2
CF_600
Ws
[10-6
mm
3 /Nm
]
Fig. 6. Influence of cryogenic treatment conditions on the enhancement
of wear resistance of short carbon fibre reinforced epoxy composites
(p ¼ 1 MPa, v ¼ 1 m/s).
Fig. 7. Worn surfaces of cryo-treated composites (a,b) (p ¼ 1 MPa, v ¼ 1 m
matrix interface significantly when compared to the un-
treated ones in Fig. 3(a)–(c) at the same sliding condition.
However, over oxidative etching was also unfavour-
able to improve the wear resistance of composites. Since
the fibres were probably damaged by an excessiveoxidation, fibre broken may easily occur, which will
/s). The treatment condition: immersed in liquid nitrogen for 20 min.
0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.00
5
10
15
20
25
Wt [
10-9 m
/s]
pv-Factors [MPa m/s]
CF_550_1 CF_20
Fig. 8. Influence of pv-factor on the depth wear rate, Wt, of untreated
and treated CF/EP composites. The treatment condition: for air-
treatment: 550 �C/1 h; for cryo-treatment: 20 min.
2036 H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038
contribute negatively to the wear resistance of compos-
ites. Under a treatment condition of 550 �C/1 h, the wornsurface (Fig. 5(a)) is relatively smooth with very small
debris. However, when the treatment temperature in-
creased to 600 �C for the same treatment time, largenumber and size debris can be observed, even with a piece
of broken fibre (marked by white arrow in Fig. 5(c)). It
can, therefore, be concluded that an appropriate oxida-
tive treatment could improve the wear resistance of CF/
EP composites due to the enhanced interfacial bonding,
however, over treatment should be avoided.
Fig. 9. Worn surfaces of (a,b) untreated, (c,d) air-treated (550 �C/1 h), and (e
contact pressure of sliding (p ¼ 3 MPa, v ¼ 1 m/s).
3.3. Cryo-treated CF/EP at a pv-factor of 1 MPa m/s
Fig. 6 illustrates the effect of cryogenic treatment on
the Ws of CF/EP composites under a pv-factor of 1 MPa
m/s. Although it was believed that the fibre–matrix in-terfacial bonding increased after treatment in our pre-
vious work [10], the Ws of all treated samples increased
lightly compared to that of untreated one, which indi-
cates that cryogenic treatment shows somehow negative
effect to an enhanced wear resistance, at least at the
present pv-factor condition.
,f) cryo-treated (20 min in liquid nitrogen) CF/EP composites at higher
H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038 2037
Fig. 7 demonstrates the worn surface of cryo-treated
CF/EP composite, in which short-CF were treated in
nitrogen for 20 min (CF_20). As shown in Fig. 7(a), the
worn surface of cryo-treated sample was much rougher
in comparing with untreated (Fig. 2(b)) and oxidative-treated composites (Fig. 5(a)). This observation was also
confirmed by the roughness of worn surface of these
three samples measured by laser profilometer (as given
in Table 2). A high magnification micrograph as shown
in Fig. 7(b) shows that cryo-treated carbon fibres were
not easy to be thinned, probably due to the fibre
strengthening effect [15]. Therefore, a poor wear resis-
tance of its composites was observed. Further investi-gations are still needed to fully understand the
mechanism behind.
3.4. At higher pv-factor
In order to understand the wear behaviour of un-
treated and treated carbon fibre composites at higher
pv-factor, the depth wear rate, Wt, as a function of pv-factors were plotted in Fig. 8, where v was kept as
constant of 1 m/s and only p was varied from 0.5 to
5 MPa. The oxidative-treated condition is 550 �C/1 h
(CF_550_1), and cryo-treated one is 20 min in liquid
nitrogen (CF_20), as optimised from the previous study.
A high pv value leads to high depth wear rates of
materials generally. In the range of pv values applied,
the Wt of both untreated and cryo-treated specimensperformed almost linear dependences according to
Eq. (3), but the situation was different for the oxidative-
treated one. Fitted wear factors, k�, were summarized in
Table 1, determined by the slope of each case. For ox-
idative-treated one, only a rang of 0–2 MPa m/s of
pv-factor was applicable. It is clear that the oxidative-
treated one is very sensitive to the contact pressure,
p. At lower p condition, the oxidative-treated fibrepreformed the lowest wear factor in all three cases.
However, once p was higher than 2 MPa, the depth
wear rate increased sharply. This result confirms again
that the oxidative treatment may damage the fibre in
some degree, which leads to more fibre broken and
peeling-off at high pressure. The cryogenic treatment
performed a satisfied improvement of wear resistance at
high pressure, which may due to the less damage andeven an increased strength of fibres after this treatment.
To conclude, following causes may contribute to an
improved wear resistance of composites at high pres-
sure: (i) improved strength of both composites and fi-
bres [10]; (ii) a reduction of interface debonding and
fibre peeling-off due to the improved interface strength;
(iii) carbon fibres can still be thinned at higher pressure
applied, which is of help to reduce the frictional coeffi-cient during sliding.
The worn surfaces of these three cases measured at a
pv-factor of 3 MPa m/s are given in Fig. 9. To compare
the low magnification micrographs of Fig. 9(a), (c) and
(e), it can be seen that there are many grooves in the
oxidative-treated case of Fig. 9(c), which indicates that
fibre peeling-off can easily take place at higher pressure.
However, for the cryo-treated one in Fig. 9(e), the wornsurface is relatively smooth. The high magnification
micrographs given in Fig. 9(b), (d) and (f) show more
details about these effects, which confirm the wear
mechanisms discussed above.
4. Conclusions
Based on this work devoted to studying the effect of
surface treatment on wear resistance of short carbon
fibre reinforced epoxy composites, the following con-
clusions can be drawn:
1. Wear resistance of polymer composites can be en-
hanced by an improved fibre–matrix interface of car-
bon fibre surface treatments.2. Optimised oxidative treatment may significantly im-
prove the wear resistance at low pv-factor, e.g.
1 MPa m/s. However, negative effect occurred at
higher pv values, e.g. P 3 MPa m/s, which may due
to the fibre damage after treatment.
3. Cryogenic treatment performed very low wear rate at
high sliding pressure, even they were not as good as
untreated one at lower pressure. The improved fibrestrength and interface strength may contribute to this
effect.
Acknowledgements
Z. Zhang is grateful to the Alexander von Hum-boldt Foundation for his Sofja Kovalevskaja Award,
financed by the German Federal Ministry of Educa-
tion and Research (BMBF) within the German Gov-
ernment’s ‘‘ZIP’’ program for investment in the
future. The authors appreciate Prof. Dr.-Ing. Dr.
h.c.K. Friedrich, IVW, for his valuable discussions
during the course of this work and the preparation of
this paper.
References
[1] Lancaster JK. The effect of carbon fiber reinforcement on the
friction and wear of polymers. J Appl Phys 1968;1:549–59.
[2] Giltrow JP, Lancaster JK. The role of the counterface in the
friction and wear of carbon fiber reinforced thermosetting resins.
Wear 1970;16:359.
[3] Hollander AE, Lancaster JK. An application of topographical
analysis to the wear of polymer. Wear 1973;25.
[4] Birkett A, Lancaster JK. Counterface effects on the wear of a
composite dry-bearing liner. Wear 1986;110:345–57.
[5] Lancaster JK. Dry bearings: a survey of materials and factors
affecting their performance. Tribology 1973;12:219–51.
2038 H. Zhang, Z. Zhang / Composites Science and Technology 64 (2004) 2031–2038
[6] Voss H, Friedrich K. On the wear behaviour of short-fiber-
reinforced PEEK composites. Wear 1987:1–18.
[7] Tripathy BS, Furey MJ. Tribological behaviour of unidirectional
graphite-epoxy and carbon-PEEK composites. Wear 1993;162–
164:385–96.
[8] Lu ZP, Friedrich K. On sliding friction and wear of PEEK and its
composites. Wear 1995;181–183:624–31.
[9] Friedrich K, Karger-Kocsis J, Lu ZP. Effects of counterpart
roughness and temperature on friction and wear of PEEK
composites. Wear 1991;148:235–47.
[10] Zhang H, Zhang Z, Breidt C. Comparison of short carbon fibre
surface treatments on epoxy composites: I. Enhancement of
mechanical properties. Compos Sci Technol 2004 doi:10.1016/
j.compscitech.2004.02.009.
[11] Friedrich K. Chapter 8: Wear of reinforced polymer by different
abrasive counterparts. In: Friedrich K, editor. Friction and wear
of polymer composites. Amsterdam, The Netherlands: Elsevier;
1988. p. 240–1.
[12] Fl€ock J, Friedrich K. On the friction and wear behaviour of PAN-
and pitch-fiber reinforced PEEK composites. Wear 1999;225–
229:304–11.
[13] Tsukizoe T, Ohmae N. Chapter 7: Friction and wear performance
of unidirectionally oriented glass, carbon, aramid and stainless
steel fiber reinforced plastics. In: Friedrich K, editor. Friction and
wear of polymer composites. Amsterdam, The Netherlands:
Elsevier; 1988. p. 219–21.
[14] Zhang Z, Breidt C, Chang L, Haupert F, Friedrich K. Enhance-
ment of the wear resistance of epoxy: short carbon fibre, graphite,
PTFE and nano-TiO2. Composites A 2004. [to be published].
[15] Rashkovan IA, Korabelnikov YG. The effect of fiber surface
treatment on its strength and adhesion to the matrix. Compos Sci
Technol 1997;57:1017–22.