Download pdf - Cellulosic Electrodes

Lincoln Cellulosic Electrodes.

Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and canonly be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

www.lincolnelectric.eu

SM

AW

Fleetweld® 5P+Cellulosic electrode

ClassificationAWS A5.1 : E6010ISO 2560-A : E 42 3 C 25

General descriptionCellulosic coated electrode for pipe and general weldingGives high ductility root weldsVery deep penetration ensures sound root passEasy striking, easy slag releaseHigh volume of generated gas eliminates porosityReduces problems from dirt and oil on surface

Welding positions

ISO/ASME PF/5Gup PG/5Gdown

Current typeDC +

ApprovalsLR TÜV3 +

Chemical composition (w%), typical, all weld metal C Mn Si

0.15 0.50 0.25

Mechanical properties, all weld metalCondition Yield strength Tensile strength Elongation Impact ISO-V(J)

(N/mm2) (N/mm2) (%) -20°C -29°C -30°C

Required: AWS A5.1 min. 331 min. 414 min. 22 27ISO 2560-A min. 420 500-640 min. 20 47

Typical values AW 440 520 26 70 65

Packaging and available sizesDiameter (mm) 2.5 3.2 4.0 5.0Length (mm) 350 350 350 350

Unit: metal can Pieces / unit 325 205 130 83Net weight/unit (kg) 5.0 5.2 5.1 5.1

Identification Imprint: 6010-FW5P+ Tip Color: none Fleetweld® 5P+: rev. EN 22

66

SM

AW

Fleetweld® 5P+

Materials to be weldedSteel grades/Code Type

Pipe materialEN 10208-1 L 210, L 240EN 10208-2 L 240 , L 290, L 360EN 10216-1 / 10217-1 P 235, P 275, P 355API 5LX X42, X46, X52Gaz de France X42, X46, X52

Calculation dataSizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/

Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal(mm) (A) (s)* E(kJ) H(kg/h) (kg) B 1/N

2.5x350 40-70 DC+ 15.83.2x350 65-130 DC+ 26.24.0x350 90-175 DC+ 40.05.0x350 140-225 DC+ 61.5

Welding parameters, optimum fill passesWelding positions PF/5G up PG/5G downDiameter (mm)

2.5 55A 65A3.2 90A 110A4.0 130A 150A5.0 150A 165A

Remarks/ Application advicePreheating pipe material L360 (X52) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root pass

67

Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and can

only be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request


SMAW

Shield Arc® 70+

High strength cellulosic electrode

Classification

AWS A5.5 : E8010-GISO 2560-A : E 46 4 1Ni C 25

General description

Cellulosic coated electrode for vertical down pipe welding

Suitable for pipe with strengths in the range of X56 - X70

Can be used for root, fill and capping passes

Low susceptibility to wagon tracks, windows and pinholes

Good impact values

Can be used for silicon-killed steels

Welding positions

ISO/ASME PG/5Gdown

Current type

DC +

Approvals

TÜV+

Chemical composition (w%), typical, all weld metal

C Mn Si Ni Cr V P S0.12 0.90 0.20 0.85 0.10 0.03 0.012 0.013

Mechanical properties, all weld metal

Condition 0.2% Proof strength Tensile strength Elongation Impact ISO-V(J)(N/mm2) (N/mm2) (%) -20°C -40°C

Required: AWS A5.5 min. 460 min. 550 min. 19 not requiredISO 2560-A min. 460 530-680 min. 20 min. 47

Typical values AW 510 570 24 75

Packaging and available sizes

Diameter (mm) 3.2 4.0 5.0Length (mm) 350 350 350

Unit: Metal can Pieces / unit 320 195 125Net weight/unit (kg) 8.3 7.7 7.8

Identification Imprint: 8010-G SA70+ Tip Color: none Shield Arc® 70+: rev. EN 21

126

SMAW

Shield Arc® 70+

Materials to be welded

Steel grades/Code Type

Pipe material

EN 10208-2 L 360, L 415, L 445, L 480

EN 10216-1 / 10217-1 P 355

API 5LX X 56, X60, X65, X70

Gaz de France X52, X63

Calculation data

Sizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal

(mm) A) (s)* E(kJ) H(kg/h) (kg) B 1/N

3.2 x 350 75 - 130 DC+ 25.84.0 x 350 90 - 185 DC+ 39.55.0 x 350 140 - 225 DC+ 62.3

Welding parameters, optimum fill passes

Welding positions PG/5G downDiameter (mm)

3.2 110A4.0 150A5.0 165A

Remarks/ Application advice

Preheating pipe material from L360 to L480 (X56 to X70) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root passUse electrodes directly from metal cansUse Fleetweld 5P+ for lower hardness in the root pass

127



SM

AW

Shield Arc® 6P+Cellulosic electrode

ClassificationAWS A5.1 : E6010ISO 2560-A : E 42 3 C 25

General descriptionCellulosic electrode for pipe weldingSmooth arcSoft and ductile root weldsSuitable for root, fill and cap passes up to X52 grades

Welding positions

ISO/ASME PF/5Gup PG/5Gdown

Current typeDC + / -

Chemical composition (w%), typical, all weld metal C Mn Si P S

0.11 0.55 0.18 0.009 0.009


(N/mm2) (N/mm2) (%) -29°C -30°C

Required: AWS A5.1 min. 331 min. 414 min. 22 27ISO 2560-A min. 420 500-640 min. 20 47

Typical values AW 420-524 503-594 24-33 51-85

Packaging and available sizesDiameter (mm) 3.2 4.0Length (mm) 350 350

Unit: metal can Pieces / unit 205 130Net weight/unit (kg) 5.2 5.1

Identification Imprint: 6010 Shield Arc 6P+ Tip Color: none Shield Arc® 6P+: rev. EN 02

130



SM

AW

Shield Arc® 6P+


Pipe materialAPI 5LX X42, X46, X52



3.2x350 65-130 DC+/- 46 25.34.0x350 90-175 DC+/- 52 39.2

Welding parameters, optimum fill passesWelding positions 5G up 5G downDiameter (mm)

3.2 90A 110A4.0 130A 150A

Remarks/ Application advicePreheating pipe material L360 (X52) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root passUse electrodes directly from metal cans

131



SM

AW

Shield Arc® 7P+High strength Cellulosic electrode

ClassificationAWS A5.5 E7010-P1/E7010-GISO 2560-A : E 42 3 Z C 25

General descriptionCellulosic electrode for pipe weldingSuitable for root, fill and cap passes up to X65 gradesHigh resistance to porosityEasy welding puddle controlHigh stacking efficiency: fill joints in fewer passesMicro-alloyed to ensure consistent mechanical properties

Welding positions

ISO/ASME PG/5Gdown

Current typeDC + (Also DC- for dia.4mm)

Chemical composition (w%), typical, all weld metal C Mn Si Ni Mo P S

0.12-0.23 0.5-0.9 0.14-0.32 0.62-0.95 0.12-0.3 0.015 0.015


(N/mm2) (N/mm2) (%) -20°C -29°C -40°C

Required: AWS A5.1 min.414 min480 min. 22 min.27ISO 2560-A min. 420 500-640 min. 20 47

Typical values AW 427-520 496-635 23-30 34-102 27-85



Identification Imprint: 7010-P1 Shield Arc 7P+ Tip Color: none Shield Arc® 7P+: rev. EN 02

132



SM

AW

Shield Arc® 7P+


Pipe materialAPI 5LX X42, X46, X52, X56, X60, X65



4.0x350 90-175 DC+/- 39.15.0x350 130-210 DC+ 62.5

Welding parameters, optimum fill passesWelding positions 5G downDiameter (mm)

4.0 150A5.0 165A

Remarks/ Application advicePreheating pipe material from L360 to L450 (X52 to X65) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root passUse electrodes directly from metal cans

133



SM

AW

Shield Arc® 8P+High strength cellulosic electrode

ClassificationAWS A5.5 E8010-P1ISO 2560-A : E 46 4 1Ni C 25

General descriptionCellulosic electrode for pipe weldingSuitable for root, fill and cap passes up to X70 gradesHigh resistance to porosityEasy welding puddle controlHigh stacking efficiency: fill joints in fewer passesMicro-alloyed to ensure consistent mechanical properties

Welding positions

ISO/ASME PG/5Gdown

Current typeDC + (Also DC- for dia.4mm)

ApprovalsDNV TÜV

+ +

Chemical composition (w%), typical, all weld metal C Mn Si Ni Cr Mo P S

0.17 0.7 0.25 0.8 0.2 0.2 0.01 0.01

Mechanical properties, all weld metalCondition 0.2% Proof strength Tensile strength Elongation Impact ISO-V(J)

(N/mm2) (N/mm2) (%) -29°C -40°C -46°C

Required: AWS A5.5 min. 460 min. 550 min. 19 27ISO 2560-A min. 460 530-680 min. 20 min. 40

Typical values AW 460-559 550-676 20-27 62-99 46-84



Identification Imprint: 8010-P1 Shield Arc 8P+ Tip Color: none Shield Arc® 8P+: rev. EN 02

134



SM

AW

Shield Arc® 8P+


Pipe materialAPI 5LX X56, X60, X65, X70


Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal(mm) A) (s)* E(kJ) H(kg/h) (kg) B 1/N

4.0 x 350 90 - 185 DC+/- 39.15.0 x 350 140 - 225 DC+ 62.5

Welding parameters, optimum fill passesWelding positions 5G downDiameter (mm)

4.0 150A5.0 165A

Remarks/ Application advicePreheating pipe material from L360 to L480 (X56 to X70) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root passUse electrodes directly from metal cansUse PIPELINER 6P+ for lower hardness in the root pass when required

135


www.lincolnelectriceurope.com

SM

AW

Shield Arc® HYPHigh strength cellulosic electrode

ClassificationAWS A5.5-96 : E7010-G EN 499-94 : E 42 2 Mo C 25

General descriptionCellulosic coated electrode for vertical down pipe weldingSuitable for pipe with strengths X52 trough X65Popular with weldersEasy operabilityLow susceptibility to wagon tracks, windows and pinholes

Welding positions

ISO/ASME PG/5Gdown

Current typeDC electr. +

ApprovalsLR TÜV

3,3Y +

Chemical composition (w%). typical. all weld metal C Mn Si Mo V

0.12 0.35 0.12 0.35 0.02

Mechanical properties, all weld metal Condition 0.2% Proof strength Tensile strength Elongation Impact ISO-V(J)

(N/mm2) (N/mm2) (%) -20°C -30°C

Required: AWS A5.5-96 min. 390 min. 480 min. 22 not required EN 499-94 min. 420 500-640 min. 20 min. 47

Typical values AW 430 520 26 75 50

Packaging, available sizes and identification Diameter (mm) 2.5 3.2 4.0 5.0Length (mm) 350 350 350 350

Unit: Metal can Pieces / unit (nominal) 440 325 195 130Net weight/unit (kg) 6.9 8.4 7.8 8.1

Identification Imprint: 7010-G SAHYP Tip colour: none Shield Arc® HYP: rev. EN 15

76

SM

AW

Shield Arc® HYP

Materials to be weldedSteel Code Type

Pipe material EN 10208-2 L 360, L 415EN 10216-1 / 10217-1 P 355API 5LX X52, X 56, X60, X65Gaz de France X52, X63

Calculation DataSizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/

Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal

(mm) A) (s)* E(kJ) H(kg/h) (kg) B 1/N

2.5x350 40-70 DC+ 15.73.2x350 75-130 DC+ 26.04.0x350 90-185 DC+ 40.05.0x350 140-225 DC+ 62.3

* stub end = 35 mm

Welding parameters, optimum fill passesWelding position: PG/5G downDiameter (mm) Current (A)

2.5 653.2 1104.0 1505.0 165

Application AdvicePreheating pipe material L360 and L415 (X56 t/m X65) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding”hot pass” immediately (within 5 min.) after root pass. Use electrode directly from metalcans.Use Fleetweld 5P for lower hardness in the root passUse electrode directly from metal cans.Use Fleetweld 5P for lower hardness in the root pass

77