INTRODUCTION
Rev. Jun 2019 valid until next revision
Chemicals Business, SCG is one of the largest integrated petrochemical companies in Thai land and a key industry leader in Asia. We of fer a fu l l array of petrochemical products ranging from upstream product ions of o lef ins to downstream product ions of three main plast ics resins: polyethylene (PE), polypropylene (PP) and polyvinyl chlor ide (PVC). Widely recognized for super ior product qual i ty as wel l as for wor ld-class operat ion ef f ic iency, we have jo int ventures wi th a number of the wor ld’s leading chemical companies, including The Dow Chemical , Mitsui Chemicals and Mitsubishi Chemical Corporat ion.
We are commit ted to developing new high value-added products (HVA) and service solut ions that inspire our customers and partners.
PASSION FOR BETTER
OUR PRODUCTION CAPACITY (AS OF 2019)
TOTAL CAPACITY : 2,878 KTA(PE / PP / PVC)
POLYOLEFINTotal : 1,912 (KTA)
PVCTotal : 966 (KTA)
PVC Resin 850 KTA
PVC Compound 80 KTA
PVC Paste Resin 36 KTA
HDPE 920 KTA
PP 720 KTA
LLDPE 120 KTA
LDPE 152 KTA
2
With Siloplast Process Technology, we provide several grades of XLPE for low-to-medium voltage power cable (up to 25 kv). Our products are carefully customized to satisfy customer requirements, such as fast curing, conductor color change prevention, excellent surface appearance with low shrinkage and great processability.
SCG™ XLPE
Integrated Solutions for Safety and Reliability
3
WIRE & CABLE SOLUTIONS
"Passion for Better" is the business pract ice to which SCG has been str ict ly adhered when working with our stakeholders in order to ensure cont inuous improvement in al l aspects throughout the value chain. We truly understand the demands for enhanced performance in the energy and data t ransmission industry, as wel l as taking into account the r is ing requirements for safety and rel iabi l i ty in accordance with the global t rends of rapid urbanizat ion. We are always open to new requirements f rom customers and str ive only for the best. This is why customers can be sure that we del iver state-of- the-art products and services that ul t imately lead to sustainable solut ions.
With the avai labi l i ty of polyolef in and polyvinyl, SCG offers a ful l range of products exclusively customized for Power Cable and Telecommunicat ions Cable businesses with strong focus on safety and rel iabi l i ty . We develop custom-made products that del iver the highest qual i ty and consistency to match your requirements in terms of funct ional i ty and processabi l i ty . More important ly, our products also meet both local and internat ional regulatory standards, such as ASTM, TIS, JIS, IEC, AS/NZS.
With more than 50 years of extensive experience, SCG is undoubtedly one of the leading providers of PVC Resin and PVC compound for wire & cable business. Available for both insulation and jacketing, our PVC products cover a broad array of applications, ranging from building wires, communication wires, electrical appliances, electrical plugs, cable adhesive tapes, to special cables, such as high flame retardant and low smoke low halogen cables.
SCG™ HDPE / SCG™ MDPEBlack HDPE Compound/ Black MDPE Compound/ Natural HDPEWith Bi-modal Process Technology from Mitsui Chemicals of Japan and Excellent compounding system, we are highly capable of providing outstanding properties of SCG wire & cable products. Its mechanical, electrical, and thermal properties, as well as processability and surface appearance meet special requirements for both jacketing and insulation applications of power and telecommunications cables.
SCG™ PVCPVC Resin and PVC Compound
Crosslinkable Polyethylene Compound
TELECOMMUNICATION CABLE
POWER CABLE
4
Component
Jacketing
Bedding
Insulation
Recommended Material Grade
PVC
FR-PVC
HDPE Compound
MDPE Compound
PVC
FR-PVC
HDPE Compound
MDPE Compound
XLPELS210NTA
LS243NTA
C2905BKA
C69XXXX
H2001WC
M545WC
C2905BKA
C69XXXX
H2001WC
M545WC
WIRE & CABLE SOLUTIONS
Component
Jacketing
Filler Rods
Recommended Material Grade
HDPE Compound
HDPE
MDPE Compound
HDPE
H2001WC
H520W*
M545WC
H520W
Remark: *H520W: The color str ip and natural or colorable jacket ing compound for outdoor cable appl icat ion requires adding up a proper UV stabi l izer to exhibi t UV resistance.
Power Cable
Fiber Optic Cable
Component
Jacketing
Filler Spacer
Insulation
Recommended Material Grade
FR-PVC
HDPE
HDPE H520W
H511W
C69XXXX
LAN Cable
Component
Jacketing
Bedding
Insulation
Recommended Material Grade
FR-PVC
LSHF
FR-PVC
LSHF
XLPE
LSHF
C69502NTA
21901NTA
C69502NTA
21901NTA
LS220NTA
21901NTA
SPECIALTY PRODUCTS
Fiber Resistance andFlame Retardant Cable
5
SCG™ HDPEBLACK HDPE COMPOUND
- Jacketing of Power Cable- Jacketing of Fiber Optic Cable
0.40
0.963
20
>700
>70
0.15
0.96
34
>800
>70
GRADE
Recommended Application
Tensile Strength at Break[MPa]
ASTM D 638 @ Crosshead Speed 50 mm/min
Key Characteristic
MFR[g/10min]
ASTM D 1238 @ 190°C, 2.16 kg
Density[g/cm3]
ASTM D 1505
Elongation at Break[%]
ASTM D 638 @ Crosshead Speed 50 mm/min
OIT @200°C[min]
ASTM D 3895 @ 200°C
H2001WC H678WC
- Excellent Environmental Stress Crack Resistance (ESCR)- High toughness with superior mechanical properties for jacketing
- Jacketing of Fiber Optic Cable
- Suitable for high speed productivity- Provide good surface appearance
6
SCG™ HDPENATURAL HDPE RESIN
- Insulation of communication cables; local area network (LAN), telephone and signal cable
0.80
0.950
34
>400
>100
0.90
0.949
34
>600
>100
GRADE
Recommended Application
Tensile Strength at Break[MPa]
ASTM D 638 @ Crosshead Speed 50 mm/min
Key Characteristic
MFR[g/10min]
ASTM D 1238 @ 190°C, 2.16 kg
Density[g/cm3]
ASTM D 1505
Elongation at Break[%]
ASTM D 638 @ Crosshead Speed 50 mm/min
OIT @200°C[min]
ASTM D 3895 @ 200°C
H511W H520W
- High-speed insulation materials- Excellent stabilized system that contains metal deactivator which provide good balance of physical and electrical properties performance.
- Natural, colorable* HDPE resin for jacketing- Filler rod- Color strip
- Suitable for high speed productivity- Provide good surface appearance- Contains appropriate level of additives for sufficient product performance
7
Remark: *For outdoor cable application requires adding up a proper UV stabilizer to exhibit UV resistance
8
SCG™ MDPEBLACK MDPE COMPOUND
GRADE
Recommended Application
Tensile Strength at Break[MPa]
ASTM D 638 @ Crosshead Speed50 mm/min
Key Characteristic
MFR[g/10min]
ASTM D 1238 @ 190°C, 2.16 kg
Density[g/cm3]
ASTM D 1505
Elongation at Break[%]
ASTM D 638 @ Crosshead Speed50 mm/min
OIT @210°C[min]
ASTM D 3895 @ 200°C
M545WC
- Jacketing of Power Cable- Jacketing of Fiber Optic Cable
- Suitable for high speed productivity- Provide good flexibility and surface appearance - Superior mechanical properties for jacketing
0.70
0.946
28
>800
>40
SCG™ HDPEBLACK FLAME RETARDANT HDPE COMPOUND
GRADE
FR500WC 2.00 1.10 >15 >300 >60- Lightweight Black Flame Retardant HDPE Compound for Jacketing of Fiber Optic Cable- Good flame retradant performance with lightweight compound products
Tensile strengthat break[MPa]
ASTM D 638 @ Crosshead
Speed 50 mm/min
Elongationat break
[%]ASTM D 638
@ Crosshead Speed 50 mm/min
Recommended Application
MFR[g/10min]
ASTM D 1238 @ 190°C, 2.16 kg
Density[g/cm3]
ASTM D 1505
OIT @200°C[min]
ASTM D 3895 @ 200°C
SCG™ PVCPVC COMPOUND FOR FLAME RETARDANT CABLE
GRADE
C69XX 85 - 97 100°C/7 Days min 12.5 min 150 min 1 - Flame Retardant cable
Tensile Strength[MPa]
JIS K 6723
Elongation[%]
JIS K 6723Recommended Application
HardnessShore A
ASTM D 2240
Aging ConditionTemperature
[°C]/DaysJIS K 6723
VolumeResistivity
[x1013 Ohm-cm]JIS K 6723
SPECIALTY PRODUCTSFLAME RETARDANT PRODUCTS
9
With main focus on safety and rel iabi l i ty , SCG is strongly commit ted to developing several F lame Retardant products, whi le aiming to work closely wi th customers to arr ive at the opt imal solut ions.
SCG™ XLPE
GRADE
Recommended Application
Key Characteristic
Tensile Strength[MPa]
IEC 60811-1-1
MFR[g/10min]
ASTM D 1238 @ 190°C, 2.16 kg
Hot Set Test200°C, 0.2 Mpa, 15 min
Hot Elongation/Set Elongation [%]IEC 60811-2-1
Elongation[%]
IEC 60811-1-1
Volume Resistivity[x1017 Ohm-cm]
IEC 60093
LS 203 NTB
- Medium voltage insulation up to 24KV
- Crosslinking by immerse in hot water (90°C) 8-12 hrs.- Low processing temperature 140 to 180 °C- Good crosslinking property
2.8
35/-10
18
500
3.6
LS 243 NTA
- Medium voltage insulation up to 24KV- Fast curing time
- Crosslinking by immerse in hot water (90°C) 10-30 hrs.- Good surface/ low shrinkage
2.0
25/-8
21
480
2.7
LS 210 NTA
- Low voltage insulation - Improved surface- Suitable for small wire up and wall thickness up to 1.4 mm
- Crosslinking by immerse in hot water (90°C) 4-5 hrs.- Good surface/ low shrinkage
2.0
60/-6
20
560
2.2
CROSSLINKABLE POLYETHYLENE COMPOUND
10
11
LS 220 NTA LS 206 NTA LS 121 NTA
- Low voltage insulation - Contains metal deactivator
- Low voltage insulation - Provide good crosslinking
- Low voltage insulation - One step grade
- Crosslinking by immerse in hot water (90°C) 4-5 hrs.- Good surface/ low shrinkage- Contains metal deactivator
- Crosslinking by immerse in hot water (90°C) 4-5 hrs.- Good surface/ low shrinkage- Good crosslinking property and easy to process
- Crosslinking by immerse in hot water (90°C) 2-3 hrs or ambient cure 5 days for thickness 1 mm- Good surface/ low shrinkage
2.0
LS 240 NTA
- Low voltage insulation - Fast curing and suitable for wall thickness up to 2.8 mm
- Very short crosslinking time by immerse in hot water (90°C) 0.5-3 hrs.- Good surface/ low shrinkage
2.0
25/-10
22.9
465
1.9
75/-7
18
580
1.9
2.0
85/-5
20
580
2.8
2.8
25/-5
21
470
2.0
LS 211 NTA
- Low voltage insulation - Meet NFC 33-209 standard
- Crosslinking by immerse in hot water (90°C) 4-5 hrs.- Good surface/ low shrinkage- Meet NFC 33-209 STD
2.0
50/-6.5
19.5
510
2.7
SCG™ PVC
GRADE
Recommended Application
K-Value[-]
ISO 1628-2
Sleve Analysis, Retained on 75 microns [%]
ASTM D 1921
Apparent Bulk Density[Apparent Bulk]
ISO 60
Sleve Analysis, Retained on 250 microns [%]
ASTM D 1921
Impurity and Foreign Matter[Points/100g]
ISO/R 1265
Residual Vinyl Chloride Monomer
[ppm]
Volume Resistivity[x1013 Ohm-cm]
SG660
- Electrical wire and cable
0.55
66.0
0.1
98.1
1
0.3
SG710
- Electrical wire and cable- Wire harness
0.49
71.3
0.1
98.2
3
0.3
0.1 0.1
3.6 4.0
PVC RESIN FOR CABLES
12
SG760
- High strength and thermal stability product such as wire and cable, wire harness, and electrical tape, etc.
0.47
76.8
0.1
0.1
97.2
3
0.2
4.2
Volatile Malter [%]
ISO 1269
SG71ZSG71J
- Electrical tape- Electrical wire and cable- Wire harness
- Electrical tape- Electrical wire and cable- Wire harness
0.49
71.5
0.1
96.9
3
0.3
SG730
- High strength and thermal stability product such as wire and cable, wire harness, and electrical tape, etc.
0.48
73.7
0.1
95.9
2
0.3
SG840
- High strength and thermal stability product such as wire and cable, wire harness, electrical tape, etc.
0.48
85.2
0.1
0.1 0.1 0.1
97.7
2
0.2
4.1
0.49
71.2
0.1
98.3
3
0.3
0.1
4.0 3.8 4.2
13
SCG™ PVC
GRADE
Recommended Application
Hardness Shore AASTM D 2240
Elongation[%]
JIS K 6723
Aging ConditionTemperature [oC]/Days
JIS K 6723
Tensile Strength[MPa]
JIS K 6723
Volume Resistivity [x 1013 Ohm-cm]
JIS K 6723
C39XX C08XX C27XX - C29XX C37XX - C39XX
Drop wire JacketingJacketing,insulation
Jacketing,insulation
40 - 50 76 - 82 76 - 82 70 - 99
min 50 min 0.1 min 0.1 min 0.1
120oC/7 Days 100oC/7 Days100oC/7 Days 80oC/7 Days
min 12.5 min 13.5 min 13.5 min 9.5
min 150 min 150min 250 min 250
PVC COMPOUND FOR TELECOMMUNICATION CABLE
14
(Shore D)
15
C76XX - C79XX C87XX - C89XX C56XX C58XX C26XX C28XX C29XX
58 - 99
80oC/7 Days 80oC/7 Days 136oC/7 Days 120oC/5 Days 100oC/5 Days 100oC/5 Days 80oC/7 Days
min 5.5 min 5.5 min 11.5 min 19.5 min 14.5 min 21.0 min 12.5
min 150 min 200 min 250 min 250 min 200 min 200 min 125
min 0.1 min 0.1 min 0.5 min 0.5 min 0.1 min 1 min 1
70 - 99 55 - 65 75 - 85 72 - 82 82 - 92 86 - 95
Jacketing,insulation
Jacketing,insulation
Insulation,non migration
Insulation,non migration
Electrical tape Electrical tapeElectrical
componants
C48XX - C49XX
Jacketing,insulation
78 - 99
min 0.1
120oC/7 Days
min 14.5
min 250
VIETNAMSCG Plastics Co., Ltd. (Ho Chi Minh Office)10th Floor, An Phu Plaza 117-119 Ly Chinh Thang P7, Q3 Ho Chi Minh City, VietnamTel.+84 988 804 672
SCG Plastics Co., Ltd. (Hanoi office)19th Floor, VCCI tower, No.9 Dao Duy Anh Street, Dong Da District, Hanoi city, VietnamTel. +84 988 804 672
TPC Vina Plastic & Chemicals Corporation Co., Ltd.(Ho Chi Minh Office)U.091-9th Floor, Habor View Tower30 Nguyen Hue Street District 1,Ho Chi Minh City, VietnamTel. +84 838 234 730 AUSTRALIA
SCG Trading Australia Pty Ltd. (Australia Office)Suite 404, Level 4, 1 Chandos Street, St. Leonards NSW 2065, AustraliaTel. +61 411 022 231
CHINAMYANMARSCG Plastics Co., Ltd.2nd Floor N. 136/137, Pyay Road, Saw BeaGyi Gone, Yangon, MyanmarTel. +95 951 946 41
INDONESIA
SCG Plastics (China) Co., Ltd. (Shanghai Office)RM 1012 Huarong Building No.1271 South of Pudong Road, Pudong New Area, Shanghai, China, 200122Tel.+86 182 170 743 69
SCG Plastics (China) Co., Ltd. (Guangzhou Office)Unit 3207, Block B, China Shine Plaza, No.9Lin He Xi Road, Tianhe, Guangzhou, China, 510610Tel. +86 139 030 579 29
PT. TPC Indo Plastic and Chemicals (Surabaya Office)Lt.5, Unit S 508-509, Kompleks Graha Festival KAV.3 Mayjend, Yono Soewoyo, Graha Family, Surabaya, Indonesia, 60226Tel. +62 319 900 120 56
1 Siam Cement Road, Bangsue, Bangkok 10800, ThailandTel: +662 586 6294 Fax:+662 586 3676
E-mail: wire&[email protected]
SCG CHEMICALS CO., LTD.
The applications specified for reference only. It is customer’s responsibilities to inspect and test the product for suitability of the customer’s own use and purpose. The customer is responsible for appropriate, safe, legal use, processing and handling of the product. To the best of our knowledge, the information contained herein is accurate and reliable as of the date of publication. We however do not assume any liability whatsoever for the accuracy and completeness of the information contained herein. We make no warranties which extend beyond the description herein. Nothing herein shall constitute any implied warranty of merchantability or fitness for a particular purpose. No liability can be accepted in respect for the use of the product in conjunction with other materials. The information contained herein relates exclusively to the product when it is not used in conjunction with any third party’s materials.