Vickers hardheidsmetingen

Citation for published version (APA):Pouwels, A. S. W. C. (1990). Vickers hardheidsmetingen. (TH Eindhoven. Afd. Werktuigbouwkunde, VakgroepProduktietechnologie : WPB; Vol. WPA0885). Eindhoven: Technische Universiteit Eindhoven.

Document status and date:Gepubliceerd: 01/01/1990

Document Version:Uitgevers PDF, ook bekend als Version of Record

Please check the document version of this publication:

• A submitted manuscript is the version of the article upon submission and before peer-review. There can beimportant differences between the submitted version and the official published version of record. Peopleinterested in the research are advised to contact the author for the final version of the publication, or visit theDOI to the publisher's website.• The final author version and the galley proof are versions of the publication after peer review.• The final published version features the final layout of the paper including the volume, issue and pagenumbers.Link to publication

General rightsCopyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright ownersand it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights.

• Users may download and print one copy of any publication from the public portal for the purpose of private study or research. • You may not further distribute the material or use it for any profit-making activity or commercial gain • You may freely distribute the URL identifying the publication in the public portal.

If the publication is distributed under the terms of Article 25fa of the Dutch Copyright Act, indicated by the “Taverne” license above, pleasefollow below link for the End User Agreement:www.tue.nl/taverne

Take down policyIf you believe that this document breaches copyright please contact us at:openaccess@tue.nlproviding details and we will investigate your claim.

Download date: 28. Mar. 2020

Vickers hardheldsm~tingen

HS - Venlo stageverslag idoor A.S.W.C. Pouwels

april 1990

VF code: C2 WPA nr: 0885

INHOUDSOPGAVE

Samenvatting

Summary

51 Inleiding

§ 1.1 Macro-Vickers

§ 1.2 Micro-Vickers

§ 1.2.1 Het micro-Vickers toestel

52 Een wiskundige benadering van de Vickers hardheidsmethode

52.1 Bepaling n-waarde

52.2 Interpretatie van de logF-logd en de logHv-logd grafieken

53 De relatle tussen de proefkracht en de gemeten hardheid

54 Het meten aan proefstaven

54.1 Het inbedden van proefstukken

54.2 Hardheidsmetingen aan de drie doorsneden

55 ConcIusie

Literatuurlijst

B1jlagen: - figuren

- tabellen

- grafieken

pagina:

3

4

5

7

8

9

10

12

13

15

16

17

18

19

20

3

SAMENVA TTING

Een van de meest gebrulkte hardheldsmethoden is de methode volgens Vickers. De

Vickers methode kan uitgevoerd worden met een breed scala aan proefkrachten. De

metingen met de kleine proefkrachten, de micro-Vickers methode, maakt het mogel1jk

hardheidsmetingen te verrlchten op zeer klelne opppervlakken.

Als toepassing wordt het hardheidsverloop over diverse doorsneden van een

proefstaaf bepaald.

4

SUMMARY

A generally used hardness measuring method is de Vickers method. The Vickers method

can be executed with wide varying forces. The measurements with small forces, the

micro-Vickers method, creates the possib1l1ty to execute many measurements on a

very small surface.

As an application the hardness changes in different sections of a test bar wlll be

determined.

5

§ 1 INLEIDING

Bij metal en kan de hardheid door koudversteviging binnen brede grenzen worden

veranderd. Omgekeerd kunnen op grond van de hardheid bepaalde conclusies worden

getrokken over de versteviging van het materiaal.

In de jaren 1900-1930 zijn achtereenvolgens drie methoden van statische hardheids­

meting ontwikkeld, die ook heden nog naast elkaar worden toegepast omdat elke

methode zijn eigen toepassingsgebied heeft. Deze hardheidsmethoden zijn: Brinell,

Rockwell en Vickers. Bij aIle methoden wordt een indringlichaam met een bepaalde

kracht in het proefstuk gedrukt. Aan de indrukking die hierbij ontstaat, wordt een

meetwaarde afgelezen, waaruit de hardheid wordt berekend. De Vickers hardheids­

meting is de nauwkeurigste van de drie en heeft het meest uitgebreide meetgebied.

De Vickersmeting wordt uitgevoerd met een pyramidevormige diamant als indruk­

lichaam. waarvan de tegenoverliggende zijden onderling een hoek van 1360 maken.

Deze diamant wordt met een bepaalde kracht in het te onderzoeken materiaal gedrukt,

zodat er een blijvende indrukking ontstaat. De indrukkingskracht loopt in 5 sec. op

tot een maximaIe waarde, die dan 10-15 sec. wordt gehandhaafd. Deze kracht kan

varieren van 5gf tot 50kgf.

De Vickershardheid is gedefinieerd als de kracht gedeeld door het oppervlak van de

achtergebleven indrukking; als eenheid wordt kgf/mm2 gehanteerd.

6

In formulevorm: Hv = 2-cos 22° -F/d2 (1)

Hv = Vickershardheld

F =proefkracht

d = diagonaallengte van de indrukking

De metlngen z1jn onder te verdelen naar de grootte van de proefkracht in micro- en

macro-hardheidsmetlngen. De macro-hardheidsmetingen betreffen de metingen met

de grote proefkrachten (vanaf 1 kgf.); metingen met kleinere proefkrachten vallen

onder het micro-bereik. Voor de uitvoering van micro-hardheldsmetingen Is andere

apparatuur nodig als voor macro-hardheidsmetlngen.

7

§ 1.1 MACRO-VICKERS

Macro-Vickers metingen worden uitgevoerd met een toestel zoals weergegeven in

figuur I.Het macro-Vickers toestelis uitgerustmet een meetoculairom de indrukklng­

en in de proefstukken te meten. Met deze hardheidsmeter worden metlngen verricht

volgens de volgende reeks van proefkrachten: 5kgf,lOkgf,15kgf,20kgf,30kgf,40kgf­

.50kgf.

Met het meetoculair wordt de gemiddelde lengte van beide diagonalen bepaald; de

hardheid kan dan worden afgelezen uit de tabel behorende bij de gebruikte kracht (zie

tabellen 1 tim 5).

N.b.: de resultaten van de I5kgf metingen z1jn berekend met formule (I) omdat er voor

deze proefbelasting geen tabel was.

Op een proefstuk van staal C45 is de bovengenoemde reeks metingen verricht; de

gemeten hardheid is uitgezet tegen de proefkracht in grafiek 1. Elke meetwaarde

vertegenwoordigt het gemiddelde van drie meetpunten. De meetwaarde bl1jkt blj de

macro-Vickers methode onafhankelllk te zlln van de proefkracht.

8

§ 1.2 MICRO-VICKERS

De micro-Vickers methode is principieel niet anders dan de macro-methode, toch

treden er blj kleine proefkrachten versch1llende verschljnselen op welke blj de macro­

methode niet van invloed zljn.

Er zljn blj de micro-Vickers methode diverse foutenbronnen welke hun uitwerking

hebben op de uiteindelljk gemeten hardheidswaarde. We onderschelden "echte" en

"schijnbare" foutenbronnen.

"Echte" fouten hangen samen met de kleinheid van de indrukkingen:

- polljstfouten,

- proefkrachtfouten.

- trillingsfouten,

- apparaatfouten.

- afleesfouten,

"Sch1jnbare" fouten z1jn niet beinvloedbaar en hangen samen met de materiaaleigen­

schappen. Deze worden blj C45 veroorzaakt door de opbouw uit ferriet (zacht) en

perl1et (hard). De afzonderlljke indrukklngen vinden dan namelljk plaats grotendeels

In het ferriet of grotendeels in het perl1et, wat een grote spreiding in de gemeten

hardheidswaarden tot gevolg heeft.

De invloeden van deze foutenbronnen veroorzaken een toenemende gemeten hardheid

blj afnemende proefkracht.

51.2.1

9

HET MICRO-VICKERS TOESTEL

Als micro-Vickers hardheldsmeter wordt de Leitz Durimet IC gebruikt (figuur 2). De

Durlmet IC is ultgerust met een Indrukmechanisme. een meetmicroscoop en een

kruistafel. Met het meetmicroscoop Is het bij een vergroting van 500 X mogelijk de

lengte van de indrukkings-diagonalen tot op 0.5 pm af te lezen en tot op 0.1 pm

nauwkeurig te schatten. Een tweede objectief zorgt voor een vergroting van 100 X en

maakt een totaaloverzicht van de indrukklngen mogelijk.

De indrukklng door de dlamant wordt gestart met een druk op de knop. het opbrengen

van de kracht en het constant houden van de kracht gedurende =20 sec. gebeurt

verder automatisch. Signalering door drie controlelampjes geeft de status van de

ultvoerlng aan.

De verplaatslng van de krulstafelis op 0.01 mm nauwkeurig in te stellen zodat een

reeks metingen op onderllng gelijke atstand gedaan kunnen worden. Dit wordt tijdens

het verdere verloop van het onderzoek gebruikt om het verloop van de hardheld over

doorsneden van proefstukken te bepalen.

Met het micro-Vickers toestel zijn metingen bij verschlllende proetkrachten verrlcht:

5gf.lOgf.15gf.50gf,lOOgf en 500gf.

150· gf.175* gf.200gf.225* gf.

•=massa's samengesteld; hardheden berekend met tormule (1).

Na het meten van de Indrukkingsdiagonalen is de hardheid at te lezen uit de bij de

gebruikte proefkracht behorende tabel (tabellen 6 tim 11). De proet Is ultgevoerd op

staal C45. de gemeten hardheid Is in grafiek 2 uitgezet tegen de proetkracht waarblj

elk meetpunt het gemlddelde weergeeft van drie metingen. Hleruit blijkt dat blj een

kleinere proetkracht een grotere hardheld gemeten wordt.

10

52 EEN WISKUNDIGE BENADERING VAN DE

VICKERS HARDHEIDSMETHODE

Uit de eerder genoemde formule: Hv=2acos220aF/d2 0)

voIgt dat er een evenredigheld bestaat tussen d2 en F als Hv = constant.

Oftewel: F = a ad2 (2)

De proportlonal1teltsfactor "a" Is een constante welke karakterlserend Is voor de

hardheld van het materlaal.

Hv = 2acos 22° aa = 1,854aa

De factor 2acos 22° voIgt ult de 136° tophoek van de vickers diamant:

'-

Geometrie Vickers dlamant

. ... - ,.',;. /::. :'. :.: ,.

. ,,)" "

... --~ :: "~'-. ~ .~-.. ~

,.. ,,',

Het buitenoppervlak van de dlamant Is: A = %d2/cos Q

Bij een tophoek van 1360 : Q = 220

Hv F/A = F/C~d2/COS 220) = 2acos 220aF/d2

De formule voor de berekenlng van de Vickershardheld is gebaseerd op de wet van

Kick: "de ruimtelijke inhoud van het verdrongen materiaalis proportloneel met de voor

de deformatle benodlgde arbeid, mits de volumina en de spanningsvelden gelijk

blijven" Ca). Bij de Vickers-meting, met pyramldevormige diamant, wordt aan deze

voorwaarden voldaan.

(a) cltaat uit: MikroharteprO.fung ... Buckle O1t. (1)).

11

Later is uit proefnemingen gebleken dat blj afnemende proefkrachten de wet van Kick

zljn geldigheid verl1est. De verhouding tussen proefkracht en indrukklngsdiagonaal­

lengte is dan niet meer kwadratisch. maar voldoet aan de wet van Meyer:

F = a'dD (3)

- n = 2 wet van Kick

- n <2 wet van Meyer

12

52.1 BEPALING N-WAARDE

De waarde van n is te achterhalen door de resultaten van de proetnemingen uit te

zetten is een log F - log d diagram.

F=a'dD (3)

log F =log a + n log d

Wanneer F en d dUbbellogaritmisch uitgezet worden voIgt daaruit een rechte. Zie

gratiek 4 voor de macro-Vickers resultaten en grafiek 5 voor de micro-Vickers

resultaten. Hiermee is de geldigheid van de formules (2) en (3) te controleren en

tevens is de waarde van n afte lezen. De n-waarde is de stJjging van de logaritmische

rechte log F = f(log d).

Het programma GRAPHER waarmee de grafieken getekend zJjn geeft ook de wiskundige

vergelijking van de lijn:

voor macro-Vickers: 0.11 • 2.0 x : n = 2.0 (grafiek 4)

voor micro-Vickers: 0.14 • 1.9 x : n =1.9 (grafiek 5)

Hiermee Is aangetoond dat de wet van Kick zJjn geldigheid verllest bJj kleiner

wordende proefkrachten. De verhoudingtussen proefkracht en indrukkingsdlagonaal­

lengte is niet meer kwadratisch (formule 2) maar de exponent wordt kleiner dan 2

(tormule 3).

Gratiek 6 is een samenvoeging van grafiek 4 en grafiek 5 ,door de logaritmische

verdeling van de d-as kan het hele bereik omvat worden.

Grafiek 61aat zien dat de IJjn door de macro-meetpunten steUer verloopt (grotere n­

waarde) dan de lijn door de micro-meetpunten (kleinere n-waarde).

13

52.2 INTERPRETATIE VAN DE logF-logd EN

DE logHv-logd GRAFIEKEN

Door de proetkracht F en de gemeten hardheid Hv beiden uit te zetten tegen de

indrukkingsdiagonaallengte Un Mm grafiek), kunnen er conclusies getrokken worden

ten aanzien van de nauwkeurigheid van de metingen.

Uit de formules (l) en (3) voIgt:

- Hv uitgezet tegen d: Hv = 2°cos 220 °a °d< 0-2) = COd< 0-2)

log Hv = log C+(n-2Hog d

- F uitgezet tegen d: F =aOdo

log F = log a + n log d

Hieruit blijkt dat 10gHv-Iogd en 10gF-Iogd llneaire functies zijn met als rlchtlngs­

coefficient respectievelljk: n-2 en n.

Formule (1) Is om te schrijven tot: d2 = 1.854 F/Hv. Ais de F- en Hv-as een gelijke

schaaiverdeling hebben dan voIgt hieruit dat de grafieken van 10gF-Iogd en 10gHv­

logd elkaar snijden in het punt waarvoor geldt: d=f1854 = 43.111m.

Dlt punt is het theoretische snijpunt van de beide lijnen voor het geval dat er zlch

geen fouten bevlnden in de in formule (l) ingevulde parameters.

De fouten die gemaakt kunnen worden bij de bepallng van de Vickershardheid volgens

formule (1) zljn:

- afwUkingen in de dlamantvorm (2°cos 22°),

- afwUkingen in de proetkracht (F),

- afwijkingen in de gemeten diagonaallengte (d).

Het programma GRAPHER geert de formules van de functles:

MICRO (grafiek 7):

10gF-logd: 10gF = 10gO.IS + 1.9341 logd

10gHv-Iogd: logHv = log271.36 +0.0683 logd

MACRO (grafiek 8):

logF-Iogd: logF = logO. 11 + 1.9958logd

10gHv-logd: logHv = log196.83 + 0.0031 logd

14

Door logF en logHv analytisch aan elkaar gelijk te stellen is het snijpunt van de

functies te berekenen. Afwijkingen t.O.V. de theoretische waarde van het snijpunt (

d=43.1 pm) wijzen op een fout in de gemeten diagonaallengte. Hierbij wordt aange­

nomen dat er geen afwijkingen zijn in de diamantvorm en in de grootte van de

proefkracht.

De analytische oplossing levert :

Snijpunt micro-grafiek: d = 56.2 lim : fout 30% (t.o.v. theoretische waarde)

Snijpunt macro-grafiek: d = 42.5 lim : fout 1.4% (t.o.v. theoretische waarde)

Hieruit blijkt dat bij de diagonaallengtemeting bij de micro-methode een :::20x grotere

fout wordt gemaakt dan bij de macro-methode.

16

53 DE RELATIE TUSSEN PROEFKRACHT EN

GEMETEN HARDHEID

Om een indruk te krijgen van de invloed van de proefkracht op de gemeten hardheid

is het hele krachtenscala van 5gf tot 60kgf doorlopen met behulp van een micro­

Vlckers- en een macro-Vickers toestel.

Elke meetwaarde kwam tot stand door het gemiddelde te nemen van drie metlngen per

proefkracht.

De meetresultaten van de proeven op een proefstuk van staal C46 staan weergegeven

in tabel 12 en in de grafieken 1,2 en 3.

Hieruit blljkt dat de gemeten hardheid sterk toeneemt blj afnemende kracht.

Door de kracht-as een logaritmische verdeling te geven, kan deze het heIe krachten­

scala omvatten (grafiek 3). Hierln toont het snijpunt van de lijnen het omslagpunt in

de meetresultaten.

Hieruit voIgt dat de proefkracht van 500gf de kleinste proefkracht is welke nog een

hardheidswaarde oplevert die overeenstemt met de macro-Vickers resultaten. De

resultaten van de macro-Vickers methode worden als referentie gekozen omdat hierbij

weinig stoorlnvloeden de meetresultaten beinvloeden. Blj proefkrachten kleiner dan

500gf gaan aUerlei Invloedsfactoren een rol spelen welke een toenemende gemeten

hardheidswaarde tot gevolg hebben (zle § 1.2).

16

54 HET METEN AAN PROEFSTAVEN

Het doel van deze orienterende proeven is een hardheidsmethode te vlnden waarmee

het hardheldsverloop over een proefstaaf met een diameter van 7 mm te bepalen is.

Dit stelt bljzondere eisen aan de meetmethode. te weten:

1. kleine indrukkingen zodat mlnimaal 10 metingen over de doorsnede mogelUk zljn.

2. de metingen mogen elkaar niet beinvloeden door b.v. koudverstevlging.

3. de metlngen moeten betrouwbare en dus redelijk constante waarden opleveren.

ad.I) In principe kan de Vickers-hardheidsmeting hiervoor gebruikt worden.

ad.2) De indrukkingen moeten erg klein zijn want de versteviglngsinvloed door de

Indrukking is ongeveer drie keer zo breed als de indrukking zelf; dus een erg klelne

proefkracht..~:7777/////77777.//77777.h':;~";;~;:=•.\ •.~ ."1 ;J7~777/7ml:m, .-, ~ ... ,~,;,.,~.. .,'" .~... - 11.5

.' - 16.5--..,-~ .....---- 14.3

-'~~"';:::~F~-~~":---t2

'.17.55.5

3.52,

Verloop van de versteviging door een Vickers-lndrukklng

ad.3) De proefkracht mag niet te klein zjjn omdat de spreiding van de meetwaarden

hierblj te sterk zal toenemen.

Het doel van de proeven 15 de klelnste proefkracht te vlnden welke een indrukking

achter laat die klein genoeg is voor een tlental metingen op een afstand van 7 mm. Het

resultaat van de metlngen moet betrouwbaar zljn.

17

§4.1 HET INBEDDEN VAN PROEFSTUKKEN

De proefstaven welke blj deze proefnem1ngen gebru1kt worden zijn van staal C45. Uit

een trekstaaf zijn drle proefstukken gehaald zodat er dr1e vIakken ontstaan waarop

het hardhe1dsverloop gemeten kan worden.

Omdat de ax1ale doorsnede en de radiale doorsnede onder 450 niet zonder meer

gebru1kt kunnen worden voor hardheidsmetingen, zuBen de proefstukken ingebed

moeten worden.

Normallter worden soortgelijke proefstukken Ingebed in bakel1et. Voor deze proeven

zou dit problemen geven omdat er metingen verricht gaan worden aan sterk

voorvervormde proefstukken, welke ook lngebed zuBen gaan worden (deze proeven

komen In dit verslag nog niet aan de orde).

Bij het lnbedden in bakel1et gebeurt bij ± 2000 C gedurende 5 mIn., dlt zou voor de

voorvervormde staven een warrntebehandel1ng betekenen.

Als alternatief voor bakellet zou glethars gebruikt kunnen worden: dlt hardt ult bij

± 1000 C. Of deze temperatuur weI laag genoeg 1s om geen lnvloed te hebben op de

proefstukken is nlet te voorspeBen.

Daarom werd er gekozen voor polyester glethars dat ulthardt bij kamertemperatuur

zonder verdere warmte effecten. De uithardlng echter duurt enkele dagen. Polyester

glethars is een twee componenten hars die gebrulkt wordt voor het ing1eten van b.v.

lnsecten.

18

54.2 HARDHEIDSMETINGEN AAN DE DRIE

DOORSNEDEN

De hardheldsmetlngen aan de drle verschlllende doorsnedes van de onvervormde staaf

zouden een gelljke hardheid moeten opleveren met een gelUkmatlge hardheldsverde­

ling over de doorsnede, omdat het uitgangsmateriaal onvervormd Is en als homogeen

mag worden aangenomen.

De resultaten van de hardheidsmetlngen aan de doorsnedes staan vermeld in de

tabellen

13 tim 16, de grafieken 9 tim 12 z1jn de graflsche weergave van de meetwaarden.

Uit de resultaten voIgt dat de hardheidswaarden over de drie doorsnedes elkaar niet

veel ontlopen en ze voldoen aan de eerder gemeten hardheld, gemeten aan een

onvervormd, nlet Ingebed proefstuk met een proefkracht van 500gf; Hv =202 s.d. =4.6.

De spreidlng van de hardheden over de doorsnedes kan gezlen worden als een

wlliekeurige verdellng.

19

§ 5 CONCLUSIE

De Vlckers-hardheidsmethode omvateen groot aantal hardheidsmeetmethoden die elk,

afhankeUJk van de grootte van de proefkracht. een versch11lend toepassingsgebied

hebben.

De gemeten hardheid blj de macro-methode blljkt onafhankelljk te zljn van de kracht.

Blj de micro-methode neemt de gemeten hardheid toe blj afnemende proefkracht. dit

kan verklaard worden door de invloed van foutenbronnen. De invloed van deze

foutenbronnen neemt toe blj afnemende diagonaallengte. Blj de macro-methode zljn

deze foutenbronnen ook van invloed. maar de uitwerklng is hier erg klein en constant.

Gezien de hardheidsverdel1ng over de ingebedde proefstukken niet verschilt t.o.V.

niet-ingebedde proefstukken. kan aangenomen worden dat inbedden in kunsthars een

goed alternatief is voor het inbedden in bakel1et.

Dat de macro-metingen nauwkeuriger zljn dan de micro-metingen blijkt uit de

beschouwing van de logF-logd en de logHv-Iogd gratieken.

De proefkracht-afhankel1jkheid van de micro-Vickers meetresultaten maakt het

noodzakelijk om de gemeten hardheid te voorzien van een index met betrekking tot de

gebruikte proefkracht: b.v. Hvo. Utgf : meting met een proetkracht van O.2kgf.

20

LITERATUURL,IJST

(l) Mikroh&rteprilfung und ihre Anwendung

H. Biickle HLR 66 BUE

1965

[2) Materialenkennis en materiaalbeproeving

w. Weissbach ISBN 9063760094

1981

[3) Mikroharte und Struktur

VDI-Berichte Nr.160 1972

Dr.lng. H. Blickle ARK 20 VDI

(4) Technische metaalkunde A

T.U. Eindhoven

diktaat Nr.4.490b

-----------------------------------------------------------BIJLAGEN

FIGUUR 1

.-,~' ;;...'"- .

,_:, : i

'-

.,~..,'. ~

•

. '. "/ .., r,

'·re

'... ,.

"

FIGUUR 2

~----25

24

'--------23

1

2

3

4

56 ~:~:17

9

10

12

15

161314

17 26

18

19

21, 20

22

Instelknop 10

Voorbeeld en

Gemeten waarde0,038

Fig. 26

FIGUUR 3

Gemeten waarde:

0,321

oL()N

o~N

o ooN

GRAFIEK 1

ooooLO

oooo-;:j-

o04­00>ot")

-+-'..r.:uo.......

02:oU)0 00 .......N

CL

oooo

oo(j)

GRAFIEK 2

oo

oon_

en

-+-'LUoI-~­ll>oL

00­oN

oo~

ooIf)

ooN

000n N ..-N N N~ww/J6>j I\H

o-.::tN

~r-T""T""""'''''''''T'"T""'1r-T""T'''''''''''''''''T'"T""'1r-T""T'''''''''''T"'T'"T'"T""'1r-T""T'''''''''''''''''~r-T""T"''T'T'"T''T"T''''/''''Ir-T""T"'T'T'''''''''T'T"1r-T""T.,..-j-O

oOJ

oIf)N

*

*

..

..

GRAFIEK 3

o

o

o

4-

OJ

o

o

oL()N

000~ I"') NN N N

lWW/j6>1

oN

ooN

o(j)

GRAFIEK 4

o o o

GRAFIEK 5

E~o

o o o

GRAFIEK 6

oD::::()«:2

o

o

o

o o o o o

o.....-

o.....-

o.....-

GRAFIEK 7

u...I-J~--L..-~--L--_U-L-J.....I.-J..-l-...l-..L..--_L...L...L..I....L.....l.......l--...l....--->------+-O

.....-

lL. >I

~-------------+- ~~~

EO~.....-

o.....-

o.....-

o

GRAFIEK 8

o~I")

~......I---L----l....-.....L...-..---l--_...J....L...I-..L-l-...J-..I----.i-~_...L-L-J,......L.-.....L.-"---'------'-------'---_---+- 0~

>I

E~~o..--

rr-r-,.............,-.-~---.-- ......................-r-,.-..,.-~~--rT""'T~-.--r--..,---.---+- 0..--

o..--

o..--

oS

GRAFIEK 9

<D,

*Q) * L()

""0Q)

C

*(f)I....

0

E0"'0 * VQ) ~- ~

0

*X0

Q)

*U

""0 I"')

I....Q)

>0

OJC

N-Q)

"'0I....Q)

>(f)

"'0<J)

..c""0I....

0

*..c

0

O~l Sal OOl S6~ 06~ S8~

I\H

GRAFIEK 10

<l>UQ)

c:(f)L.

aa

*-0 L()

<l>-0

*.--00

EL.

* '¢Q)

E-0

L.(I)

>aCJ'I *

"Dc: I")

Q)

"'0

*L.<l>>(J)

-0N

<l>£UL.

*0£

..---

06lOOl £6l/\H

£Ol...---.---.,....--r-~.----r--.,....-r-"'T""""""'1,........,...---.--r--~---r---.--r-.,-.,---.----r--r-~O

£8lOll

GRAFIEK 11

hardheidsverdeling over de radiale doorsnede over 45 graden: breedterichting

o....--N

L()oN * *ooN

>I

L()(Jl....--

L* >L-* _

* ***

o(Jl....--

o~

>"Ij.....t".J::-::...l\:I

864

d mm2

~ Iii' iii iii iii iii iii iii iii iii' iii iii iii iii

""--0

L •.•

---------------------Vickers HV 5

.......__..'.-. _.TABEL 1

F = 49,02N Q 5kp

DI_gonl'_ 0 1 2 3 4 5 8 7 8 9mm

0,06 2194 2128 2065 2008 19480.07 1892 1839 1789 1740 1693 1648 1605 1564 1524 14880.08 1449 1413 1379 1346 1314 1283 1253 1225 1197 11710.09 1145 1120 1095 1072 1049 1027 1006 988 968 04e0,10 927 90~ 891 874 857 841 825 810 795 781

0.11 768 752 739 726 713 701 689 877 888 8550.12 844 833 823 813 603 593 564 575 568 558 .0,13 549 540 532 524 516 509 602 494 487 4800,14 473 488 460 454 447 441 435 429 423 4180,15 412 407 401 396 391 386 361 378 371 3870,18 362 358 353 349 345 341 336 332 329 325

0.17 3~1 317 313 310 306 303 299 296 293 2890,18 c86 283 280 277 274 271 ~ 265 282 2800.19 257 254 251 249 246 244 241 239 ~ 2340,20 232 229 227 225 223 221 219 218 214 212

0.21 210 208 206 204 203 201 199 197 195 1930.22 192 190 188 187 185 183 182 180 178 1770,23 175 174 172 171 169 168 167 165 1&4 162

0.24 161.0 159.6 158.3 157.0 155.7 154.5 153.2 152,0 150.8 149,50.2!\ 148.3 147.1 146.0 144.9 143,7 142,6 141,5 140.4 139,3 138,20,26 137.2 136.1 135,1 134.0 133.0 132,0 131.0 130.1 129,1 128,1

0.27 127.2 126.3 125.4 124.4 123.5 122.6 121,7 120,8 120.0 119,10.28 118.3 117,4 116.6 115.8 115.0 114.2 113,4 112,6 111.8 111.0

: O.~g 110.3 109.5 108,8 108,0 107.3 106,6 105,8 105,1 104.4 103.7

t,30 103,0 102.3 101.8 101,0 100.3 99,7 99,0 98,4 97.8 97.1

0.31 96,S 95,9 '95.3 94.6 9-1,0 93.4 92.9 92,3 91.7 91.10.3? 90.6 90,0 89,4 88.9 88.3 87.8 87.2 86,7 86,2 85.70.33 85.2 84.6 84.1 63.6 83.1 82.6 82.1 81,8 81.2 80,7

0.34 80.2 79.7 79,3 7El.B 78,4 77,9 77.5 77,0 76,8 76,10,35 75.7 75.3 74,9 74.4 74.0 73.6 73.2 72,8 72,4 72.00.30

I71.6 71.2 70,6 70.4 70.0 69,6 69.2 68,8 68,S 88,1

0.37 87,7 67.4 67,0 66.6 66.3 66,0 65.6 65.2 64.9 64,80.38 &4.2 63.9 63.8 63.2 62.9 62,6 62,3 61,9 61,6 61,30,39 61,0 60,7 60,3 60.0 59.7 59,4 59,1 58.8 58.5 58.3

0.40 58,0 57,7 57.4 57,1 56.a 56,S 56.3 58,0 55.7 55.4

0.41 55.2 54.9 54,8 54.4 54,1 53,9 53.8 53,3 53.1 52.80.42 52,8 52.3 52,1 51.8 51.6 51,3 51,1 60.9 50.6 50,40.43 50,2 49.9 49,7 49,S 49,2 49.0 4a,8 48,8 48,3 48.1

0.44 47,9 47,7 47.5 47.3 47.0 46,8 48.6 46.4 46,2 46,00.45 45.8 45.6 45.4 45.2 45.0 44,8 4-4.8 "4,4 44.2 44.00.48 43,8 43.6 43,4 43,3 43.1 42.9 42,7 42,5 42.3 42.20,4;' 42,0 41.8 41.8 41.4 41.3 41,1 40.9 40.8 40,8 40,"0.48 40.2 40.1 39,9 39,7 39,6 39,4 39,3 39,1 38.9 3B,80.49 38,6 38,S 36.3 38.2 38.0 37,8 37,7 37,S 37," 37,3

0,50 37,1 37,0 38,11 38,7 36,S 38.4 36,2 36,1 35,9 35.8

0.51 35.6 35,S 35.3 35,2 35.1 35,0 34.8 34.7 34.8 34,"O.5~ 34.3 34.2 34.0 33.9 33.6 33.8 33,S 33,4 33.3 33.10.53 33.0 32.9 32,8 32.8 32.5 32.4 32,3 32.2 32.0 31.90.54 31.8 31.7 31,6 • 31.5 31,3 31.2 31,1 31.0 30.9 30.80.55 30.7 30.5 30.4 • 30.3 30.2 30.1 30.0 29,9 29,8 29.70.56 29.6 29,5 29.4 29.3 29.2 29.1 28,9 28.8 28.7 28.8

0.57 28.5 28,4 26.3 28.2 28.1 28.0 28,0 27.9 27.8 27.70.58 27.6 27.5 27.4 27.3 27.2 27,1 27,0 26.9 26.8 28.70.59 26,6 26,6 28,5 26,4 26,3 26,2 26,1 26,0 25,9 25,8

0,80 25,6 25.7 25,8 25.5 25.4 25,3 25,3 25,2 25,1 25.0

0.81 24.9 24.8 2.4,8 24.7 24.6 2.4.5 24.4 24.4 24,3 24,20.82 24.1 24.0 24.0 23.9 23.8 23,8 23.7 23.6 23.S 23.40,63 23,4 23.3 23,2 23,1 23,1 23,0 22,9 22,9 22.8 22,7

0.64 22.6 22.6 22,5 22,4 22.4 22.3 22,2 22,2 22.1 22,00,65 22.0 21.9 21,8 21,7 21.7 21.6 21.6 21,5 21,4 21,40,66 21.3 21,2 21.1 21.1 21.0 21.0 20.9 20,8 20.8 20,7

0.6i 20.7 20.6 20.5 20.5 20.4 20.3 20.3 20.2 20.2 20,10.68 20.1 20.0 19,9 19.9 19.8 19,8 19,7 19,7 19.6 19,50,69 19,5 19.4 19.4 19.3 19.3 19.? 19,1 19,1 19,0 19,0

0.70 18.9 18.9 16,6 18.8 lB,7 18.7 18.6 16,6 18,5 18,4

0.71 18.4 18.3 18.3 18.2 18.2 18.1 18,1 18.0 1e.o 17,90.72 17.9 17,8 17,8 17.7 17,7 17.6 17.6 17,5 17,5 17,50,73 17,4 17,4 17.3 17,3 17,2 17,2 17,1 17,1 17,0 17,0

.'

.'

..Vlck@rs HV 10 F = 98,04 N A 10 kp.

TABEL 2

DII'gonal' 0 1 2 3 4 5 6. 7 8 D,"m

O.to 111!!4 18111 1783 1748 1714) 1602 1650 1620 1690 16810.11 1533 1505 1478 1452 1427 1402 1378 1354 1332 13100,12 1268 1267 1246 1226 1206

11187 1166 1150 1132 1115

0.13 1097 1081 1064 1048 103

11018 1003 988 974 960

0.14 946 "33 920 907 89 882 870 858 847 8350,15 624 813 803 792 78 772 762 752 743 7340.18 724 ,715 707 698 690 681 873 685 857 8490,17 642 634 627 620 813 606 599 592 585 6790.18 572 566 560 554 548 542 536 530 525 5190.19 514 508 503 498 493 488 483 478 473 468

0.20 464 459'- 455 450 446 442 437 433 429 425.0.21 421 417 413 409 405 401 397 394 390 3870,22 383 380 376 373 370 3~6 363 360 357 3540.23 351 348 345 342 339 336. 333 330 327 3250,24 322 319 317, 314 312 309 306, 304

.,302 299

0,25 297 294 292 289 287 285 283 ' 281 279 " 278,'0,28 . 274 2n 270 268 266 2601 ~2 260 258 2560.21 254 253 251 249 247 245 243 242 240 2380.28 236 235 233 232 230 228 227 225 224 2220.29 221 219 218 216 215 213 212 21~ 209 207

0,36 206 205 203 202 201 199 198 197 196 194

',31 193 192 191 18!) 188 187 le6 185 183 182-41.32 181 180 179 178 177 HG 175 173 172 1710,33 170 169 lG8 167 16G • 165 164 183 162 161.

O.:H 160 160 159 158 157 156 155 154 153 1520,3& 151.4 ' '150.5 149,7 148.8 ''''8,0. 147.1 146,3 145.5 144,7 143.90.3 143.1 142.3 141.5 140.7 140,0 139.2 138.4 137.7 136.9 136.2

0.31' 135.5.

134,7 134.0 133,3 132,6 131,9 131.2 130.5 129,8 129.10.38 128,4 127,7 127.1 126.4 125,8 125.1 1201,S 123,8 123,2 122,60,3'9' ~21.9 . ~ .... 1~1.3 120,7 120.1 119.5 118.9 118,3 117.7 117,1 116.5

0.40 115.9 115.3 114.8 I 114,2 113.6 113,1 112.~ 111,9 111;4 110,9/

0.41 110,3 109.6 109,3 • 108,7 108,2 107,7 107.~ 106,6 10G.1 105.80,42 105.1 104,6 104,1 103,6 103,1 102,7 102,2 101,7 101.2 100,60,43 100,3 99,8 99,4 98,9 98.5 98,0 97.6 97,1 96,7 96,2

0.44 98,8.

95,3 94,9 94,5 94,1 93,6 93.2 92,8 92,4 92,00.45 91,8 91,2 90,8 90,4 90,0 89,6 89,2 88.8 88.4 88,00.48 87.8 87,3 e6,9 86,5 e8.1 85,8 85.4 85,0 84,7 84,3

0.41 84.G 83,8 83,2 82,9 82,S 82,2 81,8 81.5 81,2 BO.8o,4d 80,S 80,2 79.8 79,S 79,2 78.8 78.5 78.2 77.9 77,60.49 77,2 76,9 76.6 76,3 76,0 75,7 75,4 75,1 74,8 74,S

0.50 74,2 73,9 73.8 73,3 73,0 72.7 72.4 72,1 71,9 71.80,51 71.3 71,0 70,7 70.5 70.2 69,9 89,6 69,4 89,1 88,80,52 68,8 68.3 68,1 67.8 67.5 67,3 67,0 66.8 68.5 86,30,53 68.0 65,8 65.5 65.3 65,0 64.8 84,S 64,3 64,1 63,8

0.54 83,8 83,4 63,1 62,9 62,7 62,4 62,2 62,0 81.7 81.50,55 81.3 81.1 60,9 60.6 60,4 60,2 60,0 59,8 59,6 59.30,511 59,1 56,9 58.7 5A.5 58.3 58.1 57.9 57,7 57,S 57,3

0,57 57,1 58.9 56.7 56,5 56,3 58.1 55,9 55.7 55.5 55,30,58 55.1 54,9 54,7 54,6 64,4 54.2 54,0 53,8 53,8 53,40.59 53,3 53,1 52.9 ~2,7 52,8 52,4 52,2 52,0 51,9 51,7

0,80 51,S 51,3 51.2 61.0 SO.8 SO,7 50,S 50.3 SO.2 60,0

0,61 49.8 49.7 '9,5 "'9,4 49.2 49,0 'S,9 48,7 48.8 "S.40.82 48,2 48,1 47.9 47,8 47,6 47.5 47,3 47,2 47.0 4e,90.83 <C6,7 46,6 46.4 46,3 46,1 "'6,0 45,S 45,7 45.8 45.4

0.84 45.3 45,1 45,0 44,8 44,7 44,6 44,4 44.3 44.2 44,00,85 43,9 43.8 43,6 43,S 43,4 43,2 43,1 43,0 42.8 42,7

.0.68 42,6 42,4 42,3 42.2 42,1 41,9 41,8 41,7 41,8 41,4

0,67 41,3 41.2 41,1 40,9 1\0,6 40.7 40,6 40,5 40,3 40,20,68 40.1 40,0 39,9 39.6 39,8 39.5 39,4 39.3 39.2 39,10,89 39.0 38,8 38.7 38.6 38,S 38,4 38,3 38,2 38,1 38.0

0.70 37.8 37,7 37.6 37,S 37,4 37,3 37,2 37,1 37.0 38,9

0.71 36.8 36,7 36,8 36.5 36,4 36,3 36.2 36,1 38.0 35,90,72 35,8 35,7 35,6 35.5 35.... 35,3 35.2 35,1 35,0 34,90,73 34,8 34,7 34,6 3<1.5 34,4 34,3 34,2 34,1 34,0 34,0

0.7" 33.9 33,8 33.7 33,6 33.5 33,4 33.3 33.2 33,1 33,10,75 33.0 32.9 32,6 32,7 32,6 32.5 32.4 32,4 32.3 32,20.76 32,1 32.0 31,9 31,e 31,8 31,7 31,6 31,5 31,4 31.4

o,n 31,3 31.2 31,1 31,0 30,9 30.9 30.8 30.7 30.7 3o.e0,78 30.5 30,4 30.3 30.3 30.2 30,1 30.0 29.9 29.9 29,80,79 29.7 29,6 29,6 29.5 29.4. 29.3 29,3 29,2 29,1 29,1

"

Vickers HV 20 F ~ 196,1 N A 20 kp

TABEL 3

OI."on~l. 0 1 2 3 4 5 6 7 8 9mm

0,13 2194 2160 2128 2096 2066 2036 2006 1976 1946 19200,14 1892 1866 lMO 18t4 1780 17G4 1740 17t6 1694 16700,15 1&19 1627 1605 1564 1564 1544 1524 1505 1486 14670,16 1449 1431 1413 1396 1379 1362 1346 1330 1314 12990,17 1283 1208 1254 1239 1225 1211 1197 1184 1171 11580,18 1145 11:12 1120 1107 1095 1064 1072 1061 1049 10360.19 1027 1017 1006 996 985 975 965 956 946 9370,20 927 918 909 9')0 891 883 874 866 857 849.0,21 841 833 8?5 818 810 802 795 788 780 7730,22 766 759 753 746 739 733 720 720 713 707O,?3 701 6% 669 063 677 672 660 OGO 655 6490,24 &14 639 633 628 023 618 613 608 803 5980,25 593 5138 564 579 575 571 566 562 557 5530,26 549 544 540 536 532 528 524 520 516 5130.27 509 505 502 498 494 490 487 483 480 4760,28 473 470 4GO 463 4(i0 457 453 450 447 4440.29 441 438 435 432 429 426 423 420 4\8 4150,30 412 409 407 404 401 399 396 394 391 3880,31 306 303 381 379 370 374 371 309 307 3650,32 362 360 356 350 3!)3 351 349 347 345 3430,33 341 339 337 335 333 331 329 327 325 3230,34 32\ 319 3\7 315 3\3 312 3\0 308 308 3050,35 303 30\ 300 298 296 294 293 291 289 2880,36 286 285 284 282 280 278 277 275 274 2730,37 271 269 268 267 205 204 202 201 200 2580,38 257 256 254 253 2~)2 250 249 248 2"6 2450.39 244 243 0'''1 2"0 239 238 0'37 235 234 2330.40 232 23\ 230 228 227 226 225 224 223 2220,41 221 220 218 217 216 215 2\4 213 212 2110,42 2\0 209 208 207 206 205 204 203 203 2020,43 201 200 199 198 197 196 195 194 193 192

0.44 191 191 190 189 188 187 187 186 185 1840.45 183 182 182 181 1130 179 178 178 177 1760.46 175 175 174 173 172 172 171 170 169 1690.47 168 167 166 166 lG5 16-1 164 163 162 1620.48 161 160 150 159 156 158 157 156 156 1550.49 155 154 153 153 152 15\ 151 150 150 149

0.50 148 148 147 147 146 145 145 144 143 143

0,51 143 142 142 141 140 140 139 139 138 1380.52 137 137 136 136 135 135 134 134 133 1330,53 132 132 131 131 130 130 129 129 128 1280,54 127 127 126 126 1;>5 125 124 124 124 1230,55 123 122 122 122 121 120 120 120 119 1190.56 118 116 117 117 \17 116 116 115 115 115

0.57 114 114 113 113 113 112 112 111 111 1110,58 110 110 110 109 109 106 1011 108 107 1070,59 107 106 lOG 106 105 105 104 104 104 103

0.60 103 103 102 102 102 101 101 101 100 1000,61 100 99,3 99,0 90.7 90,4 98.0 97,7 97,4 97,1 96.80,62 96,S 96,2 95,9 9~.5 95,3 94,9 94,6 94,3 94,0 93,70,63 93,4 93,2 92,9 92,6 92.3 92.0 91.7 91,4 91.1 90.80.64 90,6 90,3 90,0 89,7 89,4 89,2 88,9 88,6 88,3 88,10.65 87,8 87,5 87,2 87,0 86,7 86,5 86,2 85,9 85,7 85,40.66 85,1 84,9 84,6 84,4 84,1 83,9 83,6 83,4 83,1 82,9

0,67 82,6 82,4 82.1 81,9 81,6 81.4 81,2 80,9 80,7 80,40,68 80,2 60,0 79.8 79,5 79.3 79,0 78,8 78,6 78,4 78,10.69 77.9 77,7 77,S 77,2 77,0 76,6 76,6 76.3 76,1 75,9O,;\) 75.7 75,5 75,3 75,0 74,8 74.6 74,4 74,2 74,0 73,8

0.71 73.6 73,4 73,2 73,0 72,8 72,5 72,3 72.1 71,9 71,70,72 71.5 71,3 71,2 71.0 70,8 70,6 70.4 70,2 70,0 69,80,73 69,6 69,4 69,2 69,0 68,8 68.7 68,5 68,3 68.1 67,9

0,74 67,7 67.5 67.4 67.2 67.0 66,8 66,6 66,5 66.3 66,10.75 65,9 65,8 65,6 65,4 65,2 65,1 64.9 64.7 64,6 64.40,76 64,2 64.0 63.9 63,7 63.5 63.4 63,2 63,0 62,9 62,7

0.77 62,6 62,4 62,2 62,0 61,9 61,8 61,6 61,4 61,3 61,10,76 61.0 60,8 60.7 60,5 60,3 60,2 60,0 59,9 59,7 59,60,79 59,4 59,3 59,1 59.0 58,8 58,7 58,S 58,4 58,2 58.1

--. .Vlckerg HV 40 r ~'l;J.? ~J . , Ill) kp

TABEL 4

OI~gon~l.. 9 1 2 3 4 5 6 7 8 Qmm

0.19 ~55 2033 ~012 Hl'll 1970 lClr;1 1911 1!'111 In'12 18730.20 lA54 1836 1618 1000 1782 1765 lHB 1731 1715 16'l1l0.21 1682 161;0 1650 1635 lG:'O IGOr; 15')0 1575 I 1561 15H0.'2 1533 1519 1505 ,,,'};> '''10 '''fiS '''52 '''''0 ''':>7 ''''''0.23 1"02 1390 1378 13(';6 13';5 1343 1331 1321 1310 13no0.24 1288 1277 1267 1256 124fj 1236 1226 1216 120G 11!'11)0.25 1187 1177 1160 1159 1150 1'''1 1132 1123 1114 11060.20 1097 1089 1081 1072 1064 105G 101\8 10"1 1033 10;>50.27 1018 . 1010 1003 9')5 980 9nl 974 966 960 9530.28 946 939 933 926 920 913 907 901 89" 8880.29 AIl2 876 870 IllH 1l5fl 0';2 81\7 n", 835 11300.30 824 819 813 808 803 797 792 787 782 7770.31 772 767 762 757 752 747 743 738 734 7290.32 724 720 715 711 707 702 . 690 li94 690 61150,33 -t 681 677 673 669 6G5 6Gl 657 653 649 6450.34· 642 638 634 630 627 623 620 616 613 6100.35 60G 602 599 595 592 5n9 5115 5112 579 5760.36 572 569 566 563 5(';0 557 55" 551 MB 5450.37 542 539 530 533 530 5:>7 525 5n 519 5160.38 514 511 500 506 503 500 498 495 493 4900,39 4A8 4R5 401 4flO 470 "75 473 471 4nll 4560.40 4164 461 4159 4157 454 452 4150 4148 446 "430.41 4141 439 437 435 433 431 4129 427 425 4230.42 421 419 417 415 413 411 409 407 405 4030.43 401 399 397 396 394 392 390 3118 387 3850.44 383 381 380 378 376 375 373 371 370 3680.45 366 '364 363 362 360 351l 35, 355 354 3520.4/\ 351 349 348 3"(\ 345 343 342 340 3:\q 3370.47 336 334 333 332 330 329 327 326 325 3230.48 322 321 319 310 317 315 314 313 312 3100.49 309 308 300 305 304 303 302 300 299 2980.!'i0 297 2!lf\ 2M '93 '92 291 290 288 :'117 2R60.51 285 264 283 ;l02 201 280 279 278 276 2750.52 274 273 272 271 270 2G9 2GB 2G7 2GO 2650.53 264 '1,3 262 261 260 259 258 257 256 2550.54 254 253 253 252 251 250 249 248 247 2<160.55 245 244 243 243 242 241 240 239 238 2370,58 '37 238 235 234 233 232 232 231 230 2290.57 228 228 227 226 225 2~4 224 223 222 2210.58 221 220 219 211\ 210 217 216 215 214 2140,59 213 212 212 :;>11 2\0 209 209 2011 207 2070.1'0 200 205 ~O5 20-1 201 203 202 201 201 :'00061 199 199 198 HI7 197 196 195 195 194 1940.62 193 192 192 191 191 190 109 189 108 1870.f\3 187 1A6 11\6 185 105 184 1113 183 182 ln20.64 181 1Rl 1110 179 17'1 179 171l 177 177 1760.65 176 175 174 174 173 173 172 172 171 1710,66 170 170 169 1(j9 160 168 167 167 166 1M0.67 HiS 165 164 164 161 161 1G2 162 161 1610.68 160 159,9 159.5 159.Q 1~,n.5 150.0 I 157.r, 157.2 156.7 151;.30.89 155.8 155.4 154.9 154.5 • 154.0 153.6 153.1 152.7 152.3 151.80.70 151.4 151.0 150.5 150.0 14').6 149,2 148.n 148.4 148.0 147.60.71 147.1 146,7 146.3 145.9 145':' 145.1 144.7 144.3 143.9 143.50.72 143.1 142,7 142.3 141.9 141.5 , 41,1 140.7 140.3 140,0 139.60.73 139.2 138,8 138.4 138.1 137.7 137.3 13G.91 136.6 136.2 135.80.74 135,5 135.1 134,7 134.4 13".0 130.6 133.1 132.9 132.6 132.20.75 131.9 131.5 131.2 130.8 130.5 130.1 129.r. 128,4 129.1 1:'8.C0.76 128.4 128.1 127.7 127.4 127.1 l~('.R 12(;,4 , 126.1 125.0 125.40.77 125.1 124.8 124.5 124.1 123.11 123.5 123.2 122.'1 122.5 122.20,78 121.9 121,6 121.3 121.0 120.7 120.4 120.1 119,8 119.5 11!',20.7~ 1111.ft 118.6 1111.2 11A.0 117.7 117.4 117,1 110.n 116,5 111l.20,flO 115,9 115.6 115.3 115.0 114,7 114.5 114.2 113.9 113.6 113.30.81 113.1 112.8 112.5 112.2 111.9 111.7 111.4 111.1 110.9 110.60.82 110.3 110.1 109.0 109.5 109.2 109.0 100.7 108.5 108.2 107.90.A3 107,7 107.4 107,2 100.9 100.6 1(lfj.4 106.1 lOS.!! 105.6 105.40.84 105,1 1M.9 104.6 104.4 104.1 101.9 103.6 103.4 103.2 102.90.85 102.7 102.4 102.2 101.9 101.7 101.5 101.2 101.0 100.8 100.50.P6 100.3 100.0 99.1\ 99.6 9!'1.4 99.1 98.9 98.7 98.5 98.2

-.

Vickers HV 50 F = 490,2 N Q, 50 kp

TABEL 5

Dlloonlr. I 0 1 2 3 .. I 5 I 6 I 7 I 8 I 9 Imm

0.21 2103 2083 2063 2044 2025 2006 19B7 1969 1951 19330.22 1916 1898 1881 1865 1848 1832 1815 1799 1784 17680.23 1753 1738 1723 1708 1693 1679 1665 1651 1637 16240.24 1610 1596 1563 1570 15S7 1545 1532 1520 1508 14950.25 1484 1472 1460 1449 1437 1426 1415 1404 1393 13820,26 1372 1361 1351 1341 1330 1320 1310 1301 1291 12810.27 1272 1263 1253 1244 1235 1226 1217 1208 1200 11910.28 1183 1174 1166 1158 1150 1142 1134 1126 1118 11100,29 1103 1095 1087 1080 1073 1065 1058 1051 1044 1037

0.30 1030 1023 1017 1010 1003 997 990 984 977 9710,31 905 959 953 91\G 91\0 934 929 923 917 9110.32 905 900 01)4 809 (1£13 878 872 8G7 8G2 8570,33 851 846 841 036 831 026 821 816 812 8070.34 802 797 793 788 784 779 775 770 766 7620.35 757 753 7118 744 740 736 732 728 724 7190.36 715 711 708 704 700 GD6 692 600 685 6810.31 677 671\ 670 GG6 GG3 659 656 65? 6119 MG0.38 642 639 635 G32 G;>9 6?G 6;>;> 619 GIG 6130,39 610 601 603 600 5~l7 591\ 591 580 50S 5620,40 500 577 574 571 5G8 SG5 563 5GO 557 5540.41 552 549 546 541\ 5-11 538 536 533 531 5280,42 526 523 521 518 516 513 511 509 506 5040.43 502 "99 4197 .,95 4CJ3 .,90 488 4811 403 41810.44 479 .,71 475 473 470 4GO 466 4(;4 4G2 .,600.45 458 456 454 4S2 "';0 JlIIO JlII6 444 442 4400.46 438 0436 "34 433 431 429 427 425 423 4220.41 420 0418 416 "'4 413 4,. 409 400 406 40"0,48 402 401 399 397 396 394 393 391 36'1 3880,49 386 385 38" 382 380 378 377 375 374 372

0,50 371 369 368 367 365 364 362 361 360 3580.51 357 355 354 352 351 350 348 347 348 3440.52 343 342 340 339 338 336 335 334 333 3310,53 330 329 328 326 325 324 323 322 320 3190,54 316 317 316 315 313 312 311 310 309 3060.55 307 305 304 303 302 301 300 299 298 2970.56 296 295 294 293 292 290 289 286 287 286

0.57 285 284 283 282 201 280 279 279 278 2770.58 276 275 274 273 272 271 270 269 266 2670.59 266 266 265 264 263 262 261 260 259 258

0.60 258 257 256 255 250t 253 253 252 251 2500,61 249 248 2~8 247 2ot6 2~5 244 241\ 243 2420.62 241 240 240 239 238 237 237 236 235 2340,63 234 233 232 231 231 230 229 229 228 227

0,64 226 2:>6 225 224 224 223 222 221 221 2200.65 220 219 218 217 217 216 216 215 214 2140,66 213 212 212 211 210 210 209 208 208 207

0.67 207 206 205 205 204 204 203 202 202 2010.68 201 200 199 199 198 198 197 196 196 1950,69 195 1!lot 1P~ ,193 193 192 191 191 190 1900.10 189 189 160 188 167 187 166 186 185 1850.71 184 183 183 182 182 181 181 180 160 1790.72 179 178 178 177 liT 176 176 175 175 1740.73 174 174 173 173 172 172 171 171 170 1700.74 169 169 168 168 168 167 167 166 166 1650,75 165 164 164 164 163 163 162 162 161 1610,76 161 160 159,7 159,3 158,8 158,4 158.0 157.6 157,2 156,80.77 156,4 156,0 155,6 155,2 15~.8 154.4 154.0 153,6 153.2 152,80.78 152,4 152.0 151,6 151.2 150,8 150.4 150.0 149,7 149.3 149.00.79 148.6 1046.2 147,8 147,4 1~7.0 146,7 146,3 146,0 145,6 145,2

0.80 144.9 144.5 144,2 143,8 143,4 143,1 142,7 142,4 142.0 141.70.81 141.3 141.0 140.6 140,2 139.9 139,6 139.2 136,9 138,8 138.20.82 137,9 137,8 137,2 136,9 1313.6 136.2 135.9 135.6 135,2 134.90.83 134,6 134,3 133.9 133,6 133,3 133,0 132,7 132,4 132.0 131.70.84 131.4 131.1 130,8 130.5 130.2 129.9 129.6 129,3 126,9 12860,85 128,3 128.0 127.7 121,4 127,1 126,8 126.5 12(;,2 126,0 125,70.86 125.4 125.1 124.8 124.5 12~,2 123,9 123,6 123,4 123.1 122,80.87 122,5 122,2 121.9 121,7 121,4 121,1 120,8 120.6 120,3 12000.88 119.7 119.5 119,2 116,9 118,7 118,4 118.1 117,9 117.5 117.30.89 117.1 116.8 116.5 116.3 116,0 115,8 115,5 115.2 115,0 114,7

Prufkraft P = 5 'pr 1 V1ckll"Ihiirh Rv (kp/..2)III

~:. 0 2 3 4 5 6 7 8 9

2 231e 2102 1916 1753 1600 1484 1372 1272 1183 11023 10)0 965 905 851 e02 757 715 677 642 6104 580 552 526 501 479 458 438 420 402 3865 371 356 }43 3)0 318 'YJ7 296 285 276 266

6 258 249 241 2}4 226 219 213 207 201 1957 189 184 179 174 169 165 161 156 152 1498 145 141 1)8 135 1)1 128 It'S 122 1~'0 1179 115 112 110 107 105 103 101 98,S 96,5 94,6

10 92,7 90,9 8;>,1 87,4 85.7 84,1 82,S 81,a 79,S 78,0

11 76,6 75,2 73,9 72,6 71,) 70,1 68,9 67,7 66,6 65,512 64 ,4 63,3 62,3 61,3 60,3 59,3 58,4 57,5 56,6 55,7'3 54,9 54,0 53,2 52,4 5',6 50,9 50,1 49,4 48,7 48,014 47,3 46,6 46.0 45,) 44,7 44,1 43.5 42,9 42,3 41,815 41,2 40.7 40, I 39,6 )9,1 38,6 38,1 37.6 37,1 36,7

16 )6,2 35,8 35.3 }4 .9 }C,5 }C,O 33,6 33,2 32,9 )2,517 )2,1 )1,7 )1.' )1,0 'YJ ,6 )0,) 29,9 29,6 29,3 28.918 28,6 28,) 28,0 27.7 27,4 27,1 26,8 26,S .6,2 26.019 25,7 25. 4 25,1 24,9 24,6 24,4 24,1 23,9 23,6 23,420 23,2 22,9 22,7 22,5 22 ,) 22,1 21,8 21,6 21,4 21,2

21 21,0 20,6 20.2 19.9 '9,522 '9.2 18,8 18,5 18,2 '7,82) 17 .5 17,2 16,9 16,6 16,424 16,1 '5.8 15.6 '5,3 15,125 14,8 14,6 14,4 14,1 13.9

26 1),7 1),5 1),3 1).' 12,927 12,7 12,5 12,4 12,2 12,028 11,8 11,7 11,5 11,3 11,229 11,0 10,9 10,7 10.6 10,4~ 10,3 10,2 10.0 9,9 9,8

TABEL 6

Pri..ifkroft p:: 10p

d I Yicker&hv" Hy (kD/..' )iD I.lUI 0 1 2 3 4 5 6 7 8 9

3 2060 1937 1813 1704 1604 1512 1427 1353 1282 12204 "59 1104 104B 1000 9SB 916 876 839 799 7735 742 713 £86 660 635 613 591 571 551 533

6 515 4,e 4B2 467 453 4)9 426 41) 401 Jl97 ]78 J£8 3SB )48 3J9 3)0 )'" J1J )05 2978 290 283 276 269 263 257 251 245 2)9 2J49 228 224 219 214 210 205 201 196 193 189

10 185 181 178 174 171 ,68 165 16, 1SB 156

" 15J 150 147 145 142 140 1)7 135 133 13112 128 126 124 122 120 119 117 "5 113 11113 110 108 ,06 '05 '03 102 100 9B,e 97,4 96,014 94,6 93.3 92,0 90,7 89,4 88,2 e7,o 85,B 84,7 83,515 82,4 el.3 80.3 79,2 78,2 77,i 76" 75,i 74,3 73,4

16 77,4 71,S 70,7 69,8 68,9 68,1 67,3 66,s 65,7 64 ,917 64 ,2 63,4 62,7 62,0 61,2 60,6 59,9 59,2 SB.5 57,918 57,2 56,6 56,0 55,4 54,8 54,2 53,6 53,0 52,5 51,~

19 5',4 50,8 50,3 49,8 49,3 48,8 4B,3 47,8 47,3 46,B20 46,4 45,9 45,4 45,0 44,6 44,' 43.7 43,3 4i,9 42,S

2' 4i,O 41,7 41,3 40,9 40,S 40,1 39,7 39,4 39,0 38,722 38,3 38,0 37,6 37,3 37,0 36,6 36,3 36,0 35,7 35,423 35,1 )4 ,8 )4 ,5 )4,2 D,9 33,6 33,3 33,0 )2,7 3i,524 )2,i )',9 )1,7 )',4 3',1 30,~ )0,6 30,4 30.2 29.925 29,7 29,4 i9,2 29,0 28,7 2B,5 2B,3 2E,' 27,9 n,6

26 27,4 27,2 27,0 26,8 26,6 26,4 26,2 26,0 25,B i5,627 25,4 25,3 25,1 24,9 24,7 24,S i4,3 i4, i 24,0 23,e28 23,7 i3,5 i3,) n,i 23,0 22,8 n.7 22,S 22 ,4 n,i29 22,1 21,9 71,7 2f ,6 71,S 21,3 2',i 2' ,0 iO,9 20,7JO 20,6 20,5 2O,) 20,2 20,1 19,~ 19,B '9,7 '9,5 '9,4

31 '9,3 19,0 lB,8 lB,6 le,332 '8,1 17,9 17,7 17,4 l?,i33 17,0 16,8 16,6 16,. 16,iJ4 16,0 15,9 '5,7 15,5 '5,)35 '5,1 '5,0 14,8 14,6 14 ,5

)6 14,3 '14,2 14,0 13,8 13,7]7 '3,5 '3,4 '3,3 '3,1 '3,0J8 12,8 12,7 12,6 12,4 12,339 12,2 12,' ",9 11,8 11,740 ",6 ",5 11,4 11,2 11,1

41 11,0 10,842 10,5 10,34) 10,0 9,8

TABEL 7

Priifkraft P = 1S 9d I VlclPnhll,t. HVinI' I 0 1 2 3 • 5 6 7 8 9

4 1739 1654 1578 1505 1437 1374 1315 1259 120B 11595 1113 1069 10~8 990 953 919 887 856 B~7 7986 773 748 724 701 679 658 638 620 602 5847 568 552 537 522 50B 494 4B2 469 457 4468 435 4~4 414 404 394 3B5 376 36B 359 3519 344 336 329 322 315 308 302 296 290 ~84

10 278 273 268 262 257 252 248 243 238 23411 230 226 222 218 214 210 207 203 200 19712 193 190 187 184 181 178 175 172 170 16713 165 162 160 157 155 153 150 148 146 14414 142 140 138 136 134 132 130 129 127 12515 124 122 120 119 117 116 114 113 111 11016 109 107 106 105 103 102 101 99,7 98,6 97,417 96,2 95,1 94,0 92,9 91,9 90,8 89,8 88,B 87,8 86,818 85,9 84,9 84,0 83,1 82,2 81.3 80,4 79,5 78,7 77,919 77,1 76,2 75,5 74,7 73,9 73,2 72,4 71,7 71,0 70.220 69,5 68.8 68,2 67,5 66,8 66.2 65,5 64,9 64,3 63.721 63,1 62,5 61,9 61,3 60,7 60,2 59,6 59,1 5B,5 5B,O22 57,S 57,0 56.4 55,9 55,4 54,9 54.5 54,0 53.5 53.023 52,6 52,1 51,7 51,2 50,8 50.4 49,9 49,5 49,1 48,724 48,3 47,9 47,5 47,1 46,7 46,3 46,0 45,6 45,3 44,925 44,S 44.2 43.8 43.5 43,1 42,8 42,4 42,1 41,8 41,S26 41,2 40,9 40,S 40.2 39,9 39.6 39.3 39,0 38,7 3B.427 38,2 37,9 37,6 37,3 37,0 36,8 36,5 36,3 36,0 35,728 35.5 35,3 35.0 34,7 34.5 34,3 34,0 33,8 33,6 33,329 33,1 32,9 32,6 32,4 32,2 32,0 31,8 31,6 31,4 31,1

PrOfkraft P = 2S 9

;~ 1 V_i_c~_.,,_h_6'_,._H_v ,

_" 0.__' __2__3. •__5__6__7 8 __9__ I

TABEL 8

678

91011121314

151617

181920

212223

242526

272829

1288946724

572464383322274237206181160

143128116

10595,887,6

80,574,268,6

63,659,155,1

1246920707

560454376317270233203179159

142127115

10494.986,9

79,873,668,1

63,158.7504.7

1206894689

5484A6370311266

·230201177157

140126114

10394.186,1

79,273,067,S

62,758,354,4

1168870673

536437363306262221198174155

138124112

10293,285,478,S72.467,0

62,257,954,0

1132847657

525429357 ­302258224

195172153

137123111

10192,484,7

77,971,966,5

61,857,S53,6

1097824642514420351297254220

193170151

135122110

10091:683,9

77,271,366,0

61,357,153,3

1064803627

503413345

292251217

190168150134121109

99.490,883,2

76,670,765,S

60,956,752,9

1033782612493405339287247215188166148

133119lOB98,S90,082,5

76,070,265,0

60,456,352,6

1003762599

483397333283243212186164146

131118107

97,689,281,8

75,469,664,S

60,055,952,2

974743585<173390327279240209

183162145

13011710696)88,481,2

74,869,164,1

59.655,S51,9

Prufkroft p = 50 9d

I 0

Vid~'5horle HVin

/' I 2 3 4 ~ 6 7 B 9

9 1145 11:20 1095 1072 1049 1027 1006 985 965 94610 927 909 891 874 857 841 625 810 795 78011 766 752 739 . 726 713 701 689 677 666 65512 644 633 623 613 603 593 584 575 566 55713 549 540 532 524 516 509 501 494 487 48014 473 466 460 453 447 441 435 429 423 41815 412 407 401 396 391 386 381 376 371 36716 362 358 353 349 345 340 336 332 329 32517 321 317 313 310 306 303 299 296 293 28918 286 283 280 277 274 271 268 265 262 26019 257 254 251 249 246 244 241 239 236 23420 232 229 227 225 223 221 218 216 214 21221 210 208 206 204 202 201 199 197 195 19322 192 190 188 186 185 183 162 180 178 17723 175 174 172 171 169 168 166 165 164 162

Prufkroft P = 100 9

d I Vichrsh6rf. HVin

I/' 0 1 2 3 4 5 6 7 8 9

13 1097 1081 1064 1048 1033 1018 1003 988 974 96014 946 933 920 907 894 882 870 858 847 83515 824 813 803 792 782 772 762 752 743 73416 724 715 707 698 689 681 673 665 657 64917 642 634 627 620 612 606 599 592. 585 57918 572 S66 560 554 548 542 536 530 525 51919 514 508 503 498 493 488 483 478 473 46820 464 459 454 450 446 441 437 433 429 42521 420 417 413 409 405 401 397 394 390 38722 383 380 376 373 370 366 363 360 357 35423 351 348 345 342 339 336 333 330 327 32524 322 319 317 314 311 309 306 304 302 29925 297 294 292 290 287 285 283 281 279 27626 274 272 270 268 266 264 262 260 258 25627 254 253 251 249 247 245 243 242 240 23828 237 235 233 232 230 228 227 225 224 22229 221 219 217 216 215 213 212 210 209 20730 206 205 203 202 201 199 198 197 195 19431 193 192 190 189 188 187 186 185 183 18232 181 180 179 178 177 176 174 173 172 17133 170 169 168 167 166 165 164 163 162 1"134 160 159 159 158. 157 156 155 154 153 15235 151 151 150 149 148 147 146 146 145 14436 143 142 142 141 140 139 138 138 137 13637 135 135 134 133 133 132 131 130 130 12938 128 128 127 126 126 125 124 124 123 12339 122 121 121 120 119 119 118 118 117 11640 116 115 115 114 114 113 112 112 111 11141 110 110 109 109 108 108 107 107 106 10642 105 105 104 104 103 103 102 102 101 10143 100 99.8 99,4 98,9 98.5 98,0 97.6 97,1 96,7 96,244 95,8 95.3 94,9 94.5 94,1 93,6 93.2 92.8 92.4 92,0-45 91.6 91.2 90,8 90.4 90,0 89.6 89,2 88.8 88.4 88,046 87.6 87,2 86.9 86.5 86,1 85,8 85.4 85.0 84,7 84.347 83,9 83.6 83.2 82.9 82.5 82.2 81,8 81,5 81.2 80,8"8 80,5 80.2 79,8 79.5 79,2 78.8 78,5 78.2 77,9 77.649 77.2 76.9 76.6 ]6.3 76.0 75.7 75,4 75,1 74.8 74.550 74.2 73,9 73.6 73,3 73,0 72.7 72,4 72.1 71,9 71.651 71.3 71,0 70,7 70,5 70.'2 69.9 69.6 69,4 69,1 68.852 68,6 68.3 68,0 67.8 67.5 67,3 67,0 66,8 66.5 66,353 66.0 65.8 65.5 65,3 65.0 64.8 64,5 64.3 64.1 63.854 63,6 63.3 63.1 62.9 6'2.6 62,4 62,2 62,0 61,7 61.5

TABEL 9

,

Prufkraft P = 200 9

TABEL 10

Yf Videuhdrle HV

0 1 2 3 4 5 6 7 8 9

19 1027 1017 1006 996 985 975 965 955 946 93720 927 918 909 900 891 883 874 866 857 84921 841 833 825 817 810 802 795 788 780 77322 766 759 753 746 739 733 726 720 713 70723 701 695 689 683 677 672 666 660, 655 64924 640\ 639 633 628 623 618 613 608 603 59825 593 589 584 579 575 570 566 562 557 55326 549 544 540 536 532 528 524 520 516 51227 509 505 501 498 494 490 487 483 480 47628 473 470 466 463 460 457 453 450 447 44429 441 438 435 432 429 426 423 420 418 41530 412 409 407 404 401 399 396 394 391 38831 386 383 3Bl 379 376 374 371 369 367 364

"32 362-· 360 358 355 353 351 349 347 345 34333 341 339 336 334 332 330 "'329 327 325 32334 321 319 317 315 313 312 310 30B 306 30435 303 301 299 298 296 294 293 "291 289 28836 286 285 283 281 280 278 277 27.5 274 27237 271 269 268 267 I 265 264 262 261 260 258

". "38 257 255 254 253 252 250 249 248 246 24539 244 243 241 240 239 238 237 235 234 23340 " 7.32 231 229 228 227 ·226 225 224 223 222-41 221 220 218 217 216 215 214 213 212 21142 210 209 208 207 206 205 ~04 203 202 20243 201 200 199 19B 197 196 195 194 193 19244 192 191 190 189 188 187 186 186 185 18445 183 182 182 181 180 179 178 178 177 17646 175 175 174 173 172 172 171 170 169 16947 . 168 167 166 166 165 164 164 163 162 16248 161 160 160 159 158 158 157 156 156 15549 154 154 153 153 152 151 151 150 150 14950 148 148 147 147 146 145 145 144 144 14351 143 142 141 141 140 140 139 139 138 13852 137 137 136 136 135 135 134 134 133 13353 132 132 131 131 130 130 129 129 128 12854 127 127 126 126 125 125 124 124 124 1235S 123 122 122 121 121 120 120 120 119 11956 118 118 117 117 117 116 116 115 115 11557 114 114 113 113 113 112 112 111 111 11158 110 110 109 109 109 108 108 108 107 10759 107 106 106 105 105 • 105 '104 104 104 10360 103 103 102 102 102 101 101 101 100 100

. .'--

Prufkraft P = 500 9

d IVichrs· d IViCk... ·1 d IViCk.... 'd , Vickers· d IVicker,.

in ha,te in h6rte in harte in h6rle in hc.'rte

" HV " HV /I HV " HV " HV

51 356 70.5 187 109 78.0 148 42.3 187 26.551.5 350 71 184 110 76.7 149 41.8 188 26.252 343 72 179 III 75.3 150 41,2 189 26.052.5 336 73 174 112 73.9 151 40,7 190 25,753 330 74 169 113 72.6 152 40,1 191 25.453.5 324 75 165 114 71,4 153 39.6 192 25,254 318 76 161 115 70.1 154 39.1 193 24.954,5 312 77 156 116 68.9 155 38,6 194 24.655 307 78 152 117 67,7 156 38,1 195 24,455.5 301 79 149 118 66.6 157 37.6 196 24,156 296 80 145 119 65.5 158 37.1 197 23.956.5 290 81 141 120 64,4 159 36) 198 23,757 285 82 138 121 63,3 160 36,2 199 23,457.5 280 83 135 122 62,3 161 35.8 200 23.258 276 84 131 123 61.3 162 35,3 201 22.958.5 271 85 128 124 60,3 163 34,9 202 22,759 266 86 125 125 59,3 164 34,5 203 22,559,S 262 87 122 126 58,4 165 34,1 204 22,360 258 88 120 127 57,5 166 33,6 205 22.160.5 253 89 117 128 56.6 167 33.2 206 21,861 249 90 114 129 55,7 168 32.9 207 21.661,S 245 91 112 130 54,9 169 32,5 208 21,462 241 92 110 131 54.0 170 32.1 209 21,262.5 237 93 107 132 53.2 171 31,7 210 21.063 234 94 105 133 52.4 172 31.3 211 20,863,5 230 95 103 134 51.6 173 31.0 212 20.664 226 96 101 135 50.9 174 30,6 213 20,4

64.5 223 97 98,5 136 50.1 175 303 214 20,265 219 98 96.5 137 49,4 176 29.9 215 20.165.5 216 99 94,6 138 48) 177 29.6 216 19,9

66 213 100 92.7 139 48.0 178 29.3 217 19,766.5 210 101 90,8 140 47,3 179 28,9 218 19.567 207 102 89,2 141 46,6 180 28,6 219 19,3

67.5 204 103 87.4 142 46.0 181 28.3 220 19.268 201 104 85,7 143 45,3 182 28.0 221 19.068,5 198 105 84;1 144 44,7 183 27,7 222 18,869 195 106 82.5 145 44.1 184 27,4 223 18,669,S 192 107 81.0 146 43.5 185 27.1 224 18.570 189 108 79,S 147 42,9 186 26,8 225 18.3

TABEL 11

TABEL 12

MEETPUNTEN MICRO/MACRO VICKERS

Proefkracht [gf) Gemeten hardheid [kgf/mm 2 ) gemeten diameter [lim)

MACRO

50000 200 684 679 681

40000 200 606 613 609

30000 200 525 527 626

20000 201 430 430 431

15000 203 369 372 370

10000 203 302 304 301

5000 198 216 217 217

MICRO

500 202 67.2 68.1 68.6

225 212 44.9 43.9 44.3

200 212 40.6 42.2 42.9

175 215 38.4 39.4 38.8

100 213 29.3 29.6 29.7

50 224 19.7 20.7 20.7

15 230 10.8 10.9 11.3

10 225 9.1 9.0 9.1

5 246 6.1 6.1 6.2

RADIALE DOORSNEDE

Gemeten hardheid {kgf/mmZ ]

195

195

198

195

201

198

195

187

198

192

gem.= 195.4 s.d.= 3.9

AXIALE DOORSNEDE

Gemeten hardheld {kgf/mrnZI

192

198

198

198

198

204

204

192

195

204

195

gem.= 198.0 s.d.= 4.4

TABEL 13

RADIALE DOORSNEDE OVER 45 GRADEN:

LENGTERICHTING

Gemeten hardheld (kgf/mm 2 ]

204

192

196

200

204

210

206

204

201

207

197

201

209

204

203

gem.= 202.5 s.d.= 4.9

TABEL 14

RADIALE DOORSNEDE OVER 45 GRADEN:

BREEDTERICHTING

Gemeten hardheld [kgf/mm 2 )

198

201

201

194

198

206

206

196

201

201

gem.=200.2 s.d.=3.9

TABEL 15