Page 1 of 2 Fastenal Product Standard REV-01
Date: May 19, 2017
TRS.HWSL.IN.Z
Thread Rolling Screw, Hex Washer Slotted, Indented, Zinc The information below lists the required dimensional, chemical and physical characteristics of the products in this purchase order. If
the order received does not meet these requirements, it may result in a supplier corrective action request, which could jeopardize your
status as an approved vendor. Unless otherwise specified, all referenced consensus standards must be adhered to in their entirety.
Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min.
#4 .188 .181 .060 .049 .243 .225 .019 .011 .039 .031 .042 .025
#6 .250 .244 .093 .080 .328 .302 .025 .015 .048 .039 .053 .033
#8 .250 .244 .110 .096 .348 .322 .031 .019 .054 .045 .074 .052
#10 .312 .305 .120 .105 .414 .384 .031 .019 .060 .050 .072 .057
#12 .312 .305 .155 .139 .432 .398 .039 .022 .067 .056 .103 .077
1/4 .375 .367 .190 .172 .520 .480 .050 .030 .075 .064 .101 .083
5/16 .500 .489 .230 .208 .676 .624 .055 .035 .084 .072 .134 .100
3/8 .562 .551 .295 .270 .780 .720 .063 .037 .094 .081 .168 .131
1/2 .750 .735 .400 .367 1.040 .960 .085 .050 .106 .091 .190 .165
Size
A
Width Across
Flats
H
Head Height
B
Washer
Diameter
U
Washer
Thickness
J
Slot Width
T
Slot Depth
Page 2 of 2 Fastenal Product Standard REV-01
Date: May 19, 2017
TRS.HWSL.IN.Z
P C
Point
Diameter
Diameter of
Circumscribing
Circle (Thread)
Max. Max. Max.
#4 40 0.1120 0.0900 0.1145
#6 32 0.1380 0.1110 0.1410
#8 32 0.1640 0.1370 0.1670
#10 24 0.1900 0.1530 0.1940
#10 32 0.1900 0.1630 0.1930
#12 24 0.2120 0.1790 0.2200
1/4 20 0.2500 0.2060 0.2550
5/16 18 0.3125 0.2640 0.3180
3/8 16 0.3750 0.3200 0.3810
1/2 13 0.5000 0.4160 0.5080
Nominal
Screw Size
Basic
Screw
Diameter
Thread
per Inch
Specification Requirements:
• Dimension, Material &
Performance: ASME B18.6.3
• Drive Style: Indented Hex Washer Slotted Head
• Finish: Fe/Zn 3AN per ASTM F1941/F1941M and waxed
• Hydrogen Embrittlement: Baking to relieve internal hydrogen embrittlement is
mandatory and shall be performed after electroplating
prior to the application of conversion finish where baking
temperatures can damage the conversion film. Baking may be
allowed after conversion finish provided temperature does not
alter performance. Part temperature shall reach 375°F to
400°F (190°C to 204°C) for a minimum of 4 hours, as soon as
practical after plating.
Hydrogen Embrittlement test results shall be maintained and
supplied to Fastenal upon request.