The Application of High-Current Low-Energy Electron Beam r Diffusion Welding and Brazing of Material Abstract – The structure and strength of the surface coating layers of iron, stainless steel and heat-resistant alloy treated by high-current low-energy electron beam have been considered. The microstructure and properties of diffusion bonded and brazed joints have been studied. Peremogi ave., Kyiv, 03056, Ukraine, Ph.: +38 044 4890164, E-mail: [email protected] *Institute of High Current Electronics SB RAS, 2/3., Akademichesky ave., Tomsk, 634055, Russia **The E.O. Paton electric Welding Institute of the NAS of Ukraine, 11, Bozhenkastr., Kyiv, 03680, Ukraine ***Admiral Makarov National University of Shipbuilding, 9, Geroev Stalingrada ave., Mykolaiv, 54025, Ukraine, Ph.: +38 0512 431174, F.: +38 0512 421081, E- mail: [email protected] V.V. Kvasnytskyy, N.N. Koval*, Yu.F. Ivanov*, L.I. Markashova**, V.D. Kuznetsov, V.F. Kvasnytskyy***

The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Embed Size (px)

Citation preview

Page 1: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

The Application of High-Current Low-Energy Electron Beam

for Diffusion Welding and Brazing of Materials.

Abstract – The structure and strength of the surface coating layers of iron, stainless steel and heat-resistant alloy treated by high-current low-energy electron beam have been considered. The microstructure and properties of diffusion bonded and brazed

joints have been studied.

National Technical University of Ukraine – Kyiv Polytechnic Institute, 37, Peremogi ave., Kyiv, 03056, Ukraine, Ph.: +38 044 4890164, E-mail: [email protected]

*Institute of High Current Electronics SB RAS, 2/3., Akademichesky ave., Tomsk, 634055, Russia**The E.O. Paton electric Welding Institute of the NAS of Ukraine, 11, Bozhenkastr., Kyiv, 03680, Ukraine***Admiral Makarov National University of Shipbuilding, 9, Geroev Stalingrada ave., Mykolaiv, 54025,

Ukraine, Ph.: +38 0512 431174, F.: +38 0512 421081, E-mail: [email protected]

V.V. Kvasnytskyy, N.N. Koval*, Yu.F. Ivanov*, L.I. Markashova**, V.D. Kuznetsov, V.F. Kvasnytskyy***

Page 2: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Diffusion welding (DW) is the effective method of bond of materials and belongs to method of welding with pressure. In pressure welding a very important issue is surface condition. Presence on the surface of adsorbed gases and oxide films requires that surfaces be activated in order to form bonds between atoms of materials being joint. To activate surfaces there were proposed: cyclic loading, use of ultra dispersed powders, intermediate gaskets (may be fusible and infusible) and many other methods that do not always prove to be effective. Often solders are used as fusible gaskets, which requires placing of solders and complicates assembly of articles. There are also problems in manufacture of modern solders. Therefore, search of new diffusion welding and brazing technologies is vital.

Purpose of this work is to study impact of surfaces, modified with high-current low-energy electron beams, on formation of joints in diffusion welding of iron with stainless steel and heat-resistant alloys and brazing of heat-resistant nickel alloys.

Page 3: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 1 Microstructure of welded joint during traditional DW of alloyЧС88У-ВИ, ×800

Page 4: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

a b

Fig. 2. Microstructure of modified layer of steel grade 10895 (a, ×250) and its fine structure (b, ×28000).

Page 5: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

a b

Fig. 3. Fine structure of modified layer of steel grade 12Х18Н10Т (a, ×20000) and nickel - base alloy ЧС88У-ВИ (b, ×30000).

Page 6: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Condition of metal

Microhardness, MPa

Steel of

10 895

Steel of 12Х18Н10Т

Alloy

ЧС88У-ВИ

Parent metal

(condition

of delivery)

Modified

1210

1240...1180

1810

19201610...

3320

34103290...

2100

22901950...

1980

21001820...2660

28302440...

Page 7: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 4. Microstructure of modified layer of steel grade 10895 × 250

Dз~1,5 мкмDз~15 мкм

7

Page 8: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 5. Microstructure of welded joint of steel grades12Х18Н10Т and 10895 with modified surfaces: ×400

Page 9: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

9

а

b, х20 000

c, х37 000

Fig. 6. Microstructure of DW joint of alloy ЧС88У-ВИ with modified surfaces: (a×400), fine structure (b, c)

Page 10: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

a, х 20 000 b, х 37 000

10

Fig. 7. Fine structure of DW joint with modified layer of steel grade 10895 and 12Х18Н10Т.

Page 11: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig.8. Change of TKLD by heating at a speed of 28 °С/с (1, 2), 2 °С/с (4,5), 1 °С/с (3) alloy of ЧС88У‑ВИ, driving complete heat treatment

(1,3,4) and driving hardening in water (2,5) 11

Page 12: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 9. Epures of plastic deformation εx (а), εy (b), εху (c) and ε ecv (d) at the temperature of 1050°С (1), 1075°С (2), 1100°С (3), 1125°С (4) and 1150°С (5)

a

c

b

d

12

Page 13: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 10. Fields of plastic deformation εy (а), εxy (b) and εecv (c) at heating of DW bond of alloy ЧС88 in different structural conditions: at a temperature 1050 °С (1), 1075 °С (2), 1100 °С (3),

1125 °С (4) и 1150 °С (5) (above – heat-treated, down is the hardened metal)

, %0 ,4 00 ,3 50 ,3 00 ,2 50 ,2 00 ,1 50 ,1 00 ,0 50

1 2 3 4 5

y , %

0 51 01 52 023 0

0-0 ,-0 ,-0 ,-0 ,-0 , 5-0 ,

1 2 3 4 5

, %0 ,4 00 ,3 50 ,3 00 ,2 50 ,2 00 ,1 50 ,1 00 ,0 50

э к в

1 2 3 3 5

а b

c

13

Page 14: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 11. Surface of sample (a) and spectrum on the elements of the

alloyed (b) and covered (c) surfaces layer on the alloy of ЧС88У-ВИ

а

b

c14

Page 15: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 12. Morphology of cross-sectional (a, b, c) and distribution of Zr (d) in a alloy of ЧС88У-ВИ after alloying of Zr (10 imp. at density of energies 25 J/sm2 and depths of the

alloyed bench of 4 micrometer 15

Никелевый сплав (ЧС-88) (образец №8/25) Напыляли поверхность - Zr

Обработка электронным пучком косой шлиф

а ×600 б ×1550

в ×3100 г

h3,5…4мкм

1

7

a b

c d

Distance , micrometerCon

cent

rati

on o

f Z

r, %

mas

s

Page 16: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

16

№8/25) Напыляли поверхность - Zr

Обработка электронным пучком

косой шлиф

а ×600 б ×1550 в ×3100 г Рис.3

h10мкм

1

7

a b

c d

Distance , micrometerCon

cent

rati

on o

f Z

r, %

mas

s

Fig. 13. Morphology of cross-sectional (a, b, c) and distribution of Zr (d) in a alloy of ЧС88У-ВИ after alloying of Zr (10 imp. at density of energies 25 J/sm2 and depths of the

alloyed bench of 8 micrometer

Page 17: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 14.Surface of heatproof alloys of ЧС88У-ВИ (a), Inconel 718 (b), brazing (c, d)17

а

b

c

d

Page 18: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Fig. 15. Microstructure of bond of alloy of ЧС88У-ВИ by alloying of Zr δ=1,0 micrometer: (a, b) - alloyed two of bond surface, (c, d) - alloyed one of bond surface

18

а b

c d

Page 19: The Application of High-Current Low-Energy Electron Beam for Diffusion Welding and Brazing of Materials. Abstract – The structure and strength of the surface

Conclusions:

1. Comparison of diffusion welding of steel grades 10 895 and 12Х18Н10Т with different preparation of surfaces showed, that formation of bonded joint is most effectively conduced by modification of both surfaces to be joint. If only one surface is to be modified, it should be surface of α-iron, whose energy of crystalline structure defects is much greater than that of γ-Fe.

2. Positive effect of surface modification of dispersion-strengthened nickel alloy is caused by both modification effect (highly dispersive structure, dislocations density, etc.) and build up of high level of strains in contact of modified (hardened) layer and alloy with excessive phase producing plastic deformations in their contact zone, which is confirmed by deformation strips in the butt joint area. At this, more preferable is bonded joint of modified and non-modified surfaces.

3. It was established for the first time that impact of HCLEEB permits to braze surface of heat-resistant alloys with elements reducing melting temperature of surface layer, specifically with Zr, Hf, Nb, with bringing of introduced element concentration close to concentration in solders by changing thickness of its previously applied layer, energy density in electron beam, duration and number of pulses.

4. Brazed layer functions not only as solder but conduces to development of plastic deformations and formation of common grains in the joint.

5. Modification of surface layer of materials to be fused by change of its structure, level of structural strains, 3-d category strains, brazing with elements reducing welding temperature, is an effective means to raise quality and simplify technology of diffusion welding.