Teacher : Cheng-Ho Chen. 南台化材. Outline. Introduction Materials Experimental Results and discussion Conclusions. 南台化材. Introduction (1). During the last twenty years, not only in the academia but also in the industry clay polymer nanocomposites (CPN) have attracted significant interest. - PowerPoint PPT Presentation
Citation preview
Teacher: Cheng-Ho Chen
1南台化材
IntroductionMaterialsExperimentalResults and discussionConclusions
2南台化材
During the last twenty years, not only in the academia but also in the industry clay polymer nanocomposites (CPN) have attracted significant interest.
Nanocomposites provide a significant improvement in polymer properties such as modulus,strength, and heat resistance, when compared to conventional composites.
Montmorillonite can significantly improve thermal stability and mechanical properties when dispersed in a polymer matrix with a low content. In general, there are two nanostructures in Mt/PP nanocomposites.
3南台化材
They intercalated octadecyl amine ethoxylate ether (A), which has two poly(ethylene oxide) segments, into the interlayer space of Mt, and the modified Mt was used to prepare Mt/PP nanocomposites by a melt blending technique with and without maleic anhydride grafted polypropylene (PPg).
南台化材4
Polypropylene, PP [-CH2CH(CH3)-]n
Ca2+-montmorillonite , Ca2+-Mt
Octadecyl trimethylammonium chloride
Octadecyl amine ethoxylate ether
南台化材5
南台化材 6
The surfactant A (50 g) was first dissolved in water till a limpid solution was obtained and then Ca2+-Mt (50 g) were added to this surfactant solution.
The AMt dispersion was heated at 60 °C under vigorous stirring.
The A/Ca2+-Mt (AMt) hybrids were dried in a 60 °C oven for several days and then pulverized. The power was sieved by passing though a 200-mesh stainless steel sifter.
A/OMt (AOMt) hybrids were prepared in the same way.
AMt or AOMt hybrids were added with 1–5 parts per hundred parts of PP (phr) by weight, then extruded by a general three-section twin-screw extruder (D=20 mm, L/D=40).
Screw speed was set at 200 rpm and the temperatures were 175 °C, 190 °C, and 190 °C for each section of the barrel and 185 °C for the die.
南台化材7
Before analysis by FTIR and TGA, all samples were extracted by boiling xylene for 72 h in order to get rid of free octadecyl amine ethoxylate ether component.
Results and discussion
南台化材 8
2923cm-1 、 2851cm-1
:C-H
9南台化材
10南台化材
N-H…O
11南台化材
12南台化材
Fig. 4. TEM micrographs of Mt/PP nanocomposites: (a) and (b), PP/AMt (100/5); (c) and (d),
PP/PPg/AMt (90/10/5); (e) and (f), PP/AOMt (100/5); (g) and (h), PP/PPg/AOMt (90/10/5).
PP/AMt (100/5)
PP/PPg/AMt (90/10/5)
PP/AOMt (100/5)
PP/PPg/AOMt (90/10/5)
1.83nm
1.83nm 3.73nm4.21nm
1.80nm 1.80nm 3.88nm 4.28nm
13南台化材
14南台化材
PP/AMt (100/5)
PP/PPg/AMt (90/10/5)
PP/AOMt (100/5)
PP/PPg/AOMt (90/10/5)
15南台化材
16南台化材
南台化材17
PP/AMt
PP/PPg/AOMtPP/PPg/AMt
PP/AOMt
南台化材
18
As observed by XRD and TEM analysis, Mt/PP nanocomposites were successfully prepared by melt blending technique using different contents of Mt modified by polyether with and without compatibilizer PPg.
The modified Mt polyether in PP matrix led to a significant reduction of melt viscosity and enhancement in Izod-notched impact strength and elongation at break.
The Izod-notched impact strength and elongation at break of Mt/PP nanocomposites were 1.95 and 2.77 times as high as those of pure PP. The tensile strength was also improved in the presence of PPg.