NO.5601 10-P-0053_E (1/7)
Super thin double-coated adhesive tape
No.5601
Outline
Nitto Denko No. 5601 is 0.01mm thick double-coated adhesive tape. The tape has a #2 polyester film as a base coated on both sides with acrylic adhesive and offers superior bonding performance to plastic films and moldings. The tape facilitates thinner electronic equipment, as tape thickness is 0.01mm. Also, it is has an excellent converting and working performance by using #2 polyester film.
Structure
Features
●Tape thickness is 0.01mm. Can be used for bonding in limited spaces or clearances.
●Excellent thickness uniformity by using polyester film.
●Uses thin #2 polyester film for superior conversion prior to use and offers less blocking and oozing.
●Excellent bonding performance to plastic material.
●The tape minimizes dust emission by using polyester release liner and plastic core.
●The six hazardous materials restricted by the RoHS directive are not compounded. Applications
●Fixing of reflective sheets and optical waveguide films used for LCD backlight modules such as
digital camera and cellular phone.
●Fixing of film for compact electronics.
●Fixing of thin layered films, splicing and fixing for metal foil end. Standards size
Tape thickness (mm) Widths (mm) Length (m)
0.01 50, 100, 230 50
For more information, please contact us.
Acrylic adhesive
Polyester film (#2) Acrylic adhesive
Release liner (Polyester film)
No.5601 【Tape thickness: 0.01 ㎜】
Plastic core
No.20131024092056-41536
NO.5601 10-P-0053_E (2/7)
Properties
●180 peeling adhesion by substrate
Substrate No.5601
ABS plate 7.0
Polystyrene plate 8.5
Acrylic plate 8.0
Polycarbonate 9.0
Polyester film 7.8
Stainless steel plate 8.3
Aluminum plate 6.6
Glass plate 7.8
(Unit: N/20 mm) Backing: PET#25
Peeling speed: 300 mm/min
Peeling angle: 180 Pressure application condition: *1pass back and forth with 2kg
Substrate: Stainless steel plate
〈Test method〉
PET#25
Substrate
No.5601
180° peeling adhesion by substrate
Adh
esio
n [
N/2
0mm
]
Substrate
ABS Polystyrene Acrylic Polycarbonate Polyester Stainless steel
Aluminum Glass
No.20131024092056-41536
NO.5601 10-P-0053_E (3/7)
Properties
●180°peeling adhesion by temperature
●Holding power
Temperature No.5601
10℃ 7.0
23℃ 8.3
40℃ 7.8
60℃ 6.2
80℃ 6.1
Temperature No.5601
40℃ 0.3
80℃ 0.6
(Unit: N/20 mm) Backing: PET#25
Peeling speed: 300 mm/min
Peeling angle: 180 Measurement temperature: 10C, 23C, 40C, 60C, 80C,
*Application under various temperatures
→Measurement under various temperatures
Substrate: Stainless steel plate
(Unit:mm/hr) Measurement temperature: 40, 80℃
Tape area: 10mmx20mm
Load: 4.9N(500g)
Substrate: Bakelite plate
No.5601
PET#25
w
Bakelite plate
〈Test method〉
180° peeling adhesion by temperature
Adh
esio
n [
N/2
0mm
]
Temperature
No.20131024092056-41536
NO.5601 10-P-0053_E (4/7)
Properties
●Shear strength
●180°Peeling adhesion by pressure
Temperature No.5601
23℃ 450
Pressure No.5601
0.1kg 4.6
0.5kg 7.0
2kg 8.3
5kg 8.4
(Unit:N/20mm) Backing: PET#25
Peeling speed: 300mm/min
Peeling speed: 180°
Measurement condition: 23℃x50%RH
Pressure application condition *1 pass back with forth with 0.1 kg、0.5kg、2kg、5kg
(Unit: N/20 mm x 20mm) Substrate:Acrylic plate / Acrylic plate
Tape area: 20mm x 20mm
Peeling speed: 50 mm/min
Measurement condition: 23C x 50%RH
Measurement method:
A specimen is prepared and shear strength is
measured after allowing it to set 30 minutes.
No.5601
Peeling speed
50mm/min
Acrylic plate
〈Test method〉
Acrylic plate
Adhesive adhesion by pressure
Adh
esio
n [
N/2
0mm
]
Pressure
No.20131024092056-41536
NO.5601 10-P-0053_E (5/7)
Properties
●180°Peeling adhesion after application(increase)
●180°peeling adhesion(change after application)
Temperature Time No.5601
23℃
0.5hrs 8.3
4hrs 8.3
12hrs 8.4
24hrs 8.5
48hrs 8.9
72hrs 8.9
Temperature Time No.5601
23℃
1 day 8.5
14 days 9.2
30 days 9.4
40℃92%RH
1 day 8.5
14 days 9.5
30 days 9.8
50℃
1 day 8.8
14 days 10.1
30 days 10.4
70℃
1 day 9.2
14 days 11.5
30 days 11.4
(Unit:N/20mm) Backing: PET#25
Peeling speed: 300mm/min
Peeling angle: 180°
Measurement condition: 23℃x50%RH
Substrate: stainless steel plate
180 peeling adhesion after application (increase)
(Unit:N/20mm) Backing: PET#25
Peeling speed: 300mm/min
Peeling angle: 180°
Measurement condition: 23℃x50%RH
Substrate: stainless steel plate
Time
Adh
esio
n [
N/2
0mm
]
No.20131024092056-41536
NO.5601 10-P-0053_E (6/7)
Properties
●Unevenness (Observe the unevenness on applied metal foil)
*Super thin, No.5601 does not stand out the unevenness where the tape applied.
〈Test method〉 ・Metal foil : Rolled cooper foil #35
・Substrate: Acrylic plate
・Size: 50mm×70mm
・Tape area:20mm width x 70mm
Metal foil
Tape
Acrylic plate
〈No.5601〉 〈0.10mm-thick double coated tape〉
Tape mark Tape mark
Tape mark Tape mark
No.20131024092056-41536
NO.5601 10-P-0053_E (7/7)
Precautions when using
●Remove all oil, moisture and dirt from the surface of the substrate before applying.
●The tape employs pressure-sensitive adhesive. Be sure to apply pressure with a roller or press when applying. Failure to do so could affect properties or appearance.
●The tape may not adhere well to significantly uneven or distorted surfaces. Level off the surface as much as possible before applying.
●Because it is very thin, you should avoid applying large loads for at least several hours following application.
Precautions when storing
●Be sure to keep the tape in its box when not using. ●Keep in a cool dark place not exposed to direct sunlight.
Safety precautions
●Make sure the product is suitable for the application (objective and conditions) before attempting to
use. The tape may come off depending on the substrate to which it is applied or conditions under
which it is applied.
●Use in combination with another method of joining if there is possibility of an accident.
Published in October 2013
! WARNING
No.20131024092056-41536
No.5603,No.5603BN 10-P-0170_E (1/6)
Double-coated adhesive tape
No.5603, No.5603BN Outline
Nitto Denko No. 5603 and No. 5603BN are 0.03mm thickness double-coated adhesive tapes. The tapes have a #4 polyester film as a base coated on both sides with acrylic adhesive, and offer superior bonding to plastic films and moldings. A mere 0.03-mm thick, the tape facilitates thinner electronic equipment. The double-coated adhesive tapes also offer superior adhesion to rough surfaces.
Structure
Features
●Tape thickness is 0.03 mm. Can be used for bonding in limited spaces or clearances.
●Uses thin #4 polyester film for superior conversion prior to use.
●Offers strong bonding to PC housing, optical waveguide plates and reflective sheets used for LCD backlight modules.
●Halogen-free type. (We do not use chloride compounds on purpose for this product.)
●The six hazardous materials restricted by the RoHS directive are not compounded.
Applications
●Fixing of reflective sheets used for LCD backlight modules for digital cameras and cellular telephones.
●Fixing of parts for compact home appliances
Standards Size
Tape thickness (mm) Widths (mm) Length (m)
0.03 50, 70 50
For more information, please contact us.
No.5603, No.5603BN* 【Tape thickness: 0.03mm】
Acrylic adhesive Polyester film (#4) Acrylic adhesive Release liner (Polyester film)
Plastic core *No. 5603BN is the black version of No. 5603.
Uses black polyester film.
No.20131024092147-41537
No.5603,No.5603BN 10-P-0170_E (2/6)
Properties
●180 peeling adhesion by substrate
<Test method>
被着体別180°引き剥がし粘着力
0.0
2.0
4.0
6.0
8.0
10.0
12.0
14.0
ABS ポリスチレン アクリル ポリカーボネート ポリエステル ステンレス アルミ ガラス
被着体
粘着
力[N
/20m
m]
Substrate No.5603,No.5603BN
ABS plate 10.0
Polystyrene plate 10.8
Acrylic plate 11.0
Polycarbonate plate 10.1
Polyester film 11.4
Stainless steel plate 10.4
Aluminum plate 9.7
Glass plate 9.6
(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement condition: 23℃, 50%RH Pressure application conditions
* 1 pass back and forth with 2-kg roller
PET#25
Substrate
Tape
180° peeling adhesion by substrate
Adh
esio
n [
N/2
0mm
]
Substrate
ABS Polystyrene Acrylic Polycarbonate Polyester Stainless steel Aluminum Glass
No.20131024092147-41537
No.5603,No.5603BN 10-P-0170_E (3/6)
Properties
●180 peeling adhesion by temperature
温度別180°引き剥がし粘着力の変化
0.0
2.0
4.0
6.0
8.0
10.0
12.0
14.0
16.0
0℃ 10℃ 23℃ 40℃ 60℃ 80℃
温度
粘着
力[N
/20m
m]
●180 peeling adhesion at low temperatures (applied at 23C and measured at 0C and -10C)
Substrate Temperature No.5603,No.5603BN
Stainless steel plate 0℃ 12.4
-10℃ 12.0
Polyester film 0℃ 8.3
-10℃ 6.6
Temperature No.5603,No.5603BN
0℃ 12.1
10℃ 10.9
23℃ 10.4
40℃ 9.1
60℃ 7.4
80℃ 6.6
(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement temperature: 0℃, 10℃, 23℃, 40℃, 60℃, 80℃
Application under various temperatures →Measurement under various temperatures Substrate: Stainless steel plate
(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180°
Measurement temperature: 0℃, -10℃
*Applied at 23c, 50% RH and measured at 0C and -10C
Substrate: Stainless steel plate
Polyester film
Adh
esio
n [
N/2
0mm
]
Temperature
180° peeling adhesion by temperature
No.20131024092147-41537
No.5603,No.5603BN 10-P-0170_E (4/6)
Properties
●Holding power
●Shear strength
●180 peeling adhesion by pressure
圧着力別粘着力
0.0
2.0
4.0
6.0
8.0
10.0
12.0
14.0
0.1kg 0.5kg 2kg 5kg
圧着力
粘着
力[N
/20m
m]
Temperature No.5603,No.5603BN
40℃ 0.3
80℃ 0.6
Temperature No.5603,No.5603BN
23℃ 600
Pressure No.5603,No.5603BN
0.1 kg 9.3
0.5 kg 9.9
2 kg 10.4
5 kg 10.6
(Unit: mm/hr) Measurement temperature: 40, 80℃ Application area: 10mmx20mm Load: 4.9N (500g) Substrate: Phenol resin plate
Tape
PET#25
w
Phenol plate
<Test method>
(Unit: N/20mmx20mm) Substrate: Acrylic plate / acrylic plate Tape area: 20mm×20mm Peeling speed: 50mm/min Measurement temperature: 23℃, 50%RH Measurement method: A specimen is prepared and shear strength
is measured after allowing it to set 30 minutes.
<Test method>
Acrylic plate
Tape
Acrylic plate
Peeling speed
50mm/min
(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement condition: 23℃, 50%RH Pressure application conditions:
* 0.1kg, 0.5kg, 2kg, 5kg 1 pass back and forth with 2-kg roller
Adhesive adhesion by pressure
Adh
esio
n [N
/20m
m]
Pressure
No.20131024092147-41537
No.5603,No.5603BN 10-P-0170_E (5/6)
Properties
●180 peeling adhesion after application (increase)
貼付け後の180°引き剥がし粘着力-上昇性
0.0
2.0
4.0
6.0
8.0
10.0
12.0
14.0
0.5hrs 4hrs 12hrs 24hrs 48hrs 72hrs
時間
粘着
力[N
/20m
m]
●180 peeling adhesion (change after application)
No.5603,No.5603BN
23 ℃
0.5 hrs 10.4
4 hrs 10.5
12 hrs 11.0
24 hrs 11.4
48 hrs 11.9
72 hrs 11.9
Temperature Time No.5603,No.5603BN
23℃
1 day 11.4
14 days 11.9
30 days 12.7
40℃, 92%RH
1 day 11.5
14 days 12.4
30 days 13.2
50℃
1 day 11.7
14 days 12.8
30 days 13.6
70℃
1 day 12.0
14 days 13.8
30 days 15.0
(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Measurement condition: 23℃, 50%RH
Substrate: Stainless steel plate
(Unit: N/20mm) Backing: PET#25 Peeling speed: 300mm/min Peeling angle: 180° Storage conditions: 23℃, 40℃×92%RH
50℃, 70℃ Measurement condition: 23℃, 50%RH Substrate: Stainless steel plate
180 peeling adhesion after application (increase)
Adh
esiv
e ad
hesi
on [N
/20m
m]
Time
No.20131024092147-41537
No.5603,No.5603BN 10-P-0170_E (6/6)
Precautions when using
●Remove all oil, moisture and dirt from the surface of the substrate before applying.
●The tape employs pressure-sensitive adhesive. Be sure to apply pressure with a roller or press when applying.
Failure to do so could affect properties or appearance. ●The tape may not adhere well to significantly uneven or distorted surfaces. Level off the surface as much as
possible before applying.
●Because it is very thin, you should avoid applying large loads for at least several hours following application. Precautions when storing
●Be sure to keep the tape in its box when not using. ●Keep in a cool dark place not exposed to direct sunlight.
Safety precautions
●Make sure the product is suitable for the application (objective and conditions) before attempting to use. The tape
may come off depending on the substrate to which it is applied or conditions under which it is applied.
●Use in combination with another method of joining if there is possibility of an accident.
Published in October 2013
! WARNING
No.20131024092147-41537