S T R U C T U R A L S T E E L S
C O N T E N T SRS 025 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3
RS 031 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5
RS 045 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7
RS 059 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9
RS 062 . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 11
→ CHEMICAL COMPOSITION (W%) → PROPERTIES
→ APPLICATION
S T R U C T U R A L S T E E L S
QU
ALIT
Y
Parts which require greater toughness in the automotive and aerospace industries, such as; drive shafts, axles, connecting rods, crankshafts, pins, bolts, etc .
Cr, Mo and Mn low-alloy steel known for its good toughness and torsional strength . The steel has good machining properties .
soft annealing cooling hardness (HB)680-720 °C furnace <241hardening quenching hardness (HRC)820-860 °C oil, water
→ HEAT TREATMENT
C Si Mn Cr Mo Ni0.41 0.20 0.75 1.05 0.23 -
→ W.NR.: 1.7225 (EN ISO 4957)
→ EN / DIN: 42CrMo4
→ AISI: 4142
RS 025
→ DELIVERY CONDITION:
quenched and tempered at 750-1300 N/mm2 depending on the diameter of the bar≤ Φ16mm 1100-1300 N/mm2
≥ Φ17≤40 mm 1000-1200 N/mm2
≥ Φ41≤100 mm 900-1100 N/mm2
≥ Φ101≤160 mm 800-950 N/mm2
≥ Φ161≤250mm 750-900 N/mm2
→ PROCESS: conventional
S T R U C T U R A L S T E E L S
↘ cct↘ tt
DISCLAIMERThe information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
1 10 1000100 10000 100000
100010010
10
1
1
Time in minutes
Time in hours
Time in seconds
Marks:A - AusteniteK - CarbideP - PerliteM - MartensiteB - Bainite
Tem
pera
ture
in (˚
C)
0
100
200
300
400
500
600
700
800
900
1000
1100
1200
632HV
627HV
572HV
493HV
340HV
245HV
231HV
207HV
V� T = 52,5 °C/sekV� T = 36,2 °C/sek
V� T = 10 °C/sek
V� T = 2,7 °C/sekV� T = 1,3 °C/sek
V� T = 0,17 °C/sekV� T =0,089 °C/sek
V� T = 0,044 °C/sek
AF+P
MsM
B
Ac₁ = 735 °C
Ar₁ = 665 °C
Ac₃ = 800 °C
Ar₃ = 730 °C
Tempering temperature [°C]
Tens
ile st
reng
th a
nd 0
,2%
pro
of st
ress
[N/m
m2 ]
Redu
ction
of a
rea
and
elon
gatio
n [%
]
0 100 200 300 400 500 600 7000 0
200
400
600
800
1000
1200
1400
1600
1800
2000
10
20
30
40
50
60
70
80
90
100
Tensile strength0,2 % proff stressReduction of areaElongation
RS 025
→ CHEMICAL COMPOSITION (W%) → PROPERTIES
→ APPLICATION
S T R U C T U R A L S T E E L S
QU
ALIT
Y
Steel suitable for carburising, cold shrinking . Suitable for the manufacture of gears, shafts, universal joints, etc .
Alloy, special carbon steel.
soft annealing cooling hardness (HB)650-700 °C furnace <207hardening quenching hardness (HRC)860-980 °C oil, water, warm bath
→ HEAT TREATMENT
→ DELIVERY CONDITION: soft annealed with a hardness of <207 HB
→ PROCESS: conventional
C Si Mn Cr Mo Ni0.16 Max 0.40 1.15 0.95 - -
→ W.NR.: 1.7131 (EN ISO 4957)
→ EN / DIN: 16MnCr5
→ AISI: 5115, 5117
RS 031
S T R U C T U R A L S T E E L S
DISCLAIMERThe information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
RS 031
↘ cct↘ tt
→ CHEMICAL COMPOSITION (W%) → PROPERTIES
→ APPLICATION
S T R U C T U R A L S T E E L S
QU
ALIT
Y
For all types of base plates, tools for plastic processing, cold and hot applications . Hand tools such as knives, axes, hammers, etc.
Suitable for work at higher temperatures . Hardening achieves a harder surface and a tough core.
soft annealing cooling hardness (HB)680-710 °C furnace <207hardening quenching hardness (HRC)820-860 °C oil, water
→ HEAT TREATMENT
→ DELIVERY CONDITION: soft annealed with a hardness of <207 HB
→ PROCESS: conventional
C Si Mn Cr Mo Ni0.45 Max 0.40 0.65 Max. 0.40 Max. 0.10 Max. 0.40
→ W.NR.: 1.1730 (EN ISO 4957)
→ EN / DIN: C45 W
→ AISI:
RS 045
S T R U C T U R A L S T E E L S
↘ cct↘ tt
DISCLAIMERThe information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
1 10 1000100 10000 100000
100010010
10
1
1
Time in minutes
Time in hours
Time in seconds
Marks:A - AusteniteK - CarbideP - PerliteM - MartensiteB - Bainite
Tem
pera
ture
in (˚
C)
0
100
200
300
400
500
600
700
800
900
1000
1100
1200
509HV
497HV
332HV
258HV
251HV
240HV
234HV
V� T = 42,5 °C/sekV� T = 29,5 °C/sek
V� T = 7,8 °C/sekV� T = 2,1 °C/sek
V� T = 1 °C/sek
V� T =0,14 °C/sek
V� T = 0,042 °C/sek
A
FP
MsM
B
Ac₁ = 720 °CAr₁ = 670 °C
Ac₃ = 790 °C
Ar₃ = 740 °C
Tempering temperature [°C]1000 200 300 400 500 600 700
Hard
ness
in H
RC
40
55
50
60
45
35
30
65
70
RS 045
→ CHEMICAL COMPOSITION (W%) → PROPERTIES
→ APPLICATION
S T R U C T U R A L S T E E L S
QU
ALIT
Y
For springs . Can be quenched and surface hardened . Highly-burdened parts for cars, machines, etc.
Spring steel. Low-alloy, special structural Cr-V steel.
soft annealing cooling hardness (HB)640-720 °C furnace <217hardening quenching hardness (HRC)
820-860 °C oil, water see the scale of discounts
→ HEAT TREATMENT
→ DELIVERY CONDITION: soft annealed with a hardness of <248 HB
→ PROCESS: conventional
C Si Mn Cr V Mo0.51 Max 0.40 0.90 1.05 0.18 -
→ W.NR.: 1.8159 (EN ISO 4957)
→ EN / DIN: 50CrV4
→ AISI: 6145/6150
RS 059
S T R U C T U R A L S T E E L S
↘ cct↘ tt
DISCLAIMERThe information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
1 10 1000100 10000 100000
100010010
10
1
1
Time in minutes
Time in hours
Time in seconds
Marks:A - AusteniteK - CarbideP - PerliteM - MartensiteB - Bainite
Tem
pera
ture
in (˚
C)
0
100
200
300
400
500
600
700
800
900
1000
1100
1200
724HV
702HV
682HV
404HV
362HV
270HV 260
HV
254HV
V� T = 38,8 °C/sekV� T = 30,4 °C/sek
V� T = 8,3 °C/sekV� T =2,5 °C/sek
V� T = 1,1 °C/sek
V� T =0,15 °C/sekV� T =0,088 °C/sek
V� T = 0,043 °C/sek
A
P
MsM
B
Ac₁ = 728 °C
20 100
100 100 97 40 30
100 100
5060
3
Ar₁ = 660 °C
Ac₃ = 780 °C
Ar₃ = 700 °C
Mikrotrdota HV 0,1
Distance from quenched end in mm0 10 20 30 40 50 60
Hard
ness
in H
RC
20
50
40
60
30
10
0
70
RS 059
→ CHEMICAL COMPOSITION (W%) → PROPERTIES
→ APPLICATION
S T R U C T U R A L S T E E L S
QU
ALIT
Y
For cold application, for tools for plastics . Suitable for polishing, with a tough core and wear-resistant surface .
Case hardening special tool steel . Suitable for carburising . Good polishability .
soft annealing cooling hardness (HB)670-710 °C furnace <217hardening quenching hardness (HRC)850-880 °C oil, water, warm bath
→ HEAT TREATMENT
→ DELIVERY CONDITION: soft annealed with a hardness of <217 HB
→ PROCESS: conventional
C Si Mn Cr Mo Ni0.19 Max 0.40 1.25 1.15 - -
→ W.NR.: 1.2162 (EN ISO 4957)
→ EN / DIN: 21MnCr5
→ AISI: 5120
RS 062
S T R U C T U R A L S T E E L S
↘ cct↘ tt
DISCLAIMERThe information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
1 10 1000100 10000 100000
100010010
10
1
1
Time in minutes
Time in hours
Time in seconds
Marks:A - AusteniteK - CarbideP - PerliteM - MartensiteB - Bainite
Tem
pera
ture
in (˚
C)
0
100
200
300
400
500
600
700
800
900
1000
1100
1200
396HV
311HV
289HV
251HV
724HV
724HV
724HV
724HV
724HV
724HV
V� T =78 °C/sekV� T = 41 °C/sek
V� T = 34,1 °C/sek
V� T = 8,7 °C/sek
V� T = 2,2 °C/sek
V� T = 0,69 °C/sek
V� T = 0,15 °C/sekV� T = 0,081 °C/sek
V� T = 0,040 °C/sek
V� T = 1,2 °C/sek
A
MsM
B
FAc₁ = 740 °C
50
50
50
40 4040
4040
4040
30
305
60 6070
5520
60 60 60 60
Hardness HV 0,1
P
Ac₃ = 835 °C
Tempering temperature [°C]1000 200 300 400 500 600 700
Hard
ness
in H
RC
40
55
50
60
45
35
30
65
70
RS 062