USA 791 Westport Pkwy., Fort Worth, TX, 76177 - Phone: 817 335-1826 [email protected] www.socomore.com Hexavalent Chrome Alternatives for aluminium surface treatment SOCOGEL HCP SOCOGEL UV CURED SOCOSURF TCS/PACS Socosurf TCS - T rivalent C onversion and Sealing Socosurf PACS - Passivation After C onversion and Sealing Heat cured anti-corrosion sol-gel Format Curing Dry film thickness Conductivity SST w/o paint SST with paint Paint adhesion Chem. resistance 2 step process 0.20-0.25 μm (0.008-0.01 mil) 30 mg/ft² Before 168 hrs SST 2040 μΩ/inch² After 168 hrs SST: 5220 μΩ/inch² 336 hrs Cr paint systems Non-Cr paint systems 3000 hrs Cr paint systems Non-Cr paint systems SOL-GEL Format Curing Dry film thickness Conductivity SST w/o paint SST with paint Filiform corrosion Paint adhesion Chem. resistance * Depending on paint system UV cured anti-corrosion hybrid sol-gel SOL-GEL NB : Rinse baths not shown Anodizing Sealing Conversion Deoxidizing or desmutter after alkaline etching Spray gun or robotic application Integration of the new process in the aluminium alloys surface treatment line 1 component (1K) Ready to use – Automated UV cured (H-lamp), RT 20-25 μm (0.8-1.0 mil) No 3000 hrs (bare Aluminium) > 3000 hrs 1000 hrs* Cr paint systems Non-Cr paint systems Water, humidity, skydrol, organic solvent, kerosene, de-icing fluid, synt. lubricant 3 component (3K) 30 min @ 230°F (110°C) 3-7 μm (0.12-.027 mil) No 336 hrs (unclad Aluminium) 1000 hrs (clad Aluminum) 3000 hrs Cr paint systems Non-Cr paint systems Skydrol, organic solvent, synt. lubricant Format Film thickness Coating weight Conductivity SST w/o paint Paint adhesion SST w/o paint Paint adhesion Conversion Sealing after anodizing Historical system New sol-gel UV cured Cr pre -treatment + Chromated or Cr free paint system Cr free pre - treatment + Cr free paint system

SOL-GEL SOCOSURF TCS/PACS · 2 step process 0.20-0.25 µm (0.008-0.01 mil) 30 mg/ft² Before 168 hrs SST 2040 µ˜/inch² After 168 hrs SST: 5220 µ˜/inch² 336 hrs Cr paint systems

Download PDF Report

Upload
others
View
0
Download
0

Embed Size (px)

Citation preview

Page 1: SOL-GEL SOCOSURF TCS/PACS · 2 step process 0.20-0.25 µm (0.008-0.01 mil) 30 mg/ft² Before 168 hrs SST 2040 µ˜/inch² After 168 hrs SST: 5220 µ˜/inch² 336 hrs Cr paint systems

USA 791 Westport Pkwy., Fort Worth, TX, 76177 - Phone: 817 335-1826 [email protected] www.socomore.com

Hexavalent Chrome Alternatives for aluminium surface treatment

SOCOGEL HCP SOCOGEL UV CURED

SOCOSURF TCS/PACS

Socosurf TCS - Trivalent Conversion and SealingSocosurf PACS - Passivation After Conversion and Sealing

Heat cured anti-corrosion sol-gel

Format Curing Dry film thickness

Conductivity SST w/o paint SST with paint Paint adhesion Chem. resistance

2 step process

0.20-0.25 µm (0.008-0.01 mil)30 mg/ft²Before 168 hrs SST 2040 µΩ/inch² After 168 hrs SST: 5220 µΩ/inch² 336 hrs Cr paint systemsNon-Cr paint systems

3000 hrsCr paint systemsNon-Cr paint systems

SOL-GEL

Format Curing Dry film thickness Conductivity SST w/o paint SST with paint Filiform corrosion Paint adhesion Chem. resistance

* Depending on paint system

UV cured anti-corrosion hybrid sol-gel

SOL-GEL

Integration of the new process in the aluminium alloys surface treatment line

ASETSDefense 1

NB : Rinse baths not shown Anodizing

Sealing

Conversion

Deoxidizing or desmutter after alkaline etching

Spray gun or robotic application

Integration of the new process �in the aluminium alloys surface treatment line

1 component (1K)Ready to use – AutomatedUV cured (H-lamp), RT20-25 µm (0.8-1.0 mil) No3000 hrs (bare Aluminium)> 3000 hrs1000 hrs*Cr paint systemsNon-Cr paint systemsWater, humidity, skydrol, organic solvent, kerosene, de-icing fluid, synt. lubricant

3 component (3K)30 min @ 230°F (110°C)3-7 µm (0.12-.027 mil)No336 hrs (unclad Aluminium)1000 hrs (clad Aluminum)3000 hrs Cr paint systems Non-Cr paint systemsSkydrol, organic solvent, synt. lubricant

Format

Film thickness Coating weightConductivity SST w/o paint Paint adhesion

SST w/o paintPaint adhesion

Conversion

Sealing after anodizing

UV - cured hybrid sol - gel

Paint Shop Process for Mankiewicz 1

Historical system

New sol-gel UV cured

Cr pre -treatment + Chromated or Cr free paint system

Cr free pre - treatment + Cr free paint system

� Developed to: