Performance Rubber & Additives - Kuttnerkuttner.ru/download/biesterfeld.pdf · Performance Rubber & Additives Polymers Portfolio Lucene POE ... NBR / PVC Polyblend Copolymers EPM

Performance Rubber & Additives

PortfolioPolymersLucene POE Carbon BlackFillersProcessing AidsAccelerators / Curing Agents / Retarder Polymerbound preparationsAntioxidants / AntiozonantsMagnesium OxideMoisture AbsorbentsBlowing AgentsBatch-Off-Release Agents

2 3

Content

Polymers 5

Acrylonitrile Butadiene Rubber (NBR) 5 Ethylene-Propylene Rubber (EPR) 5 FKM-Co-Polymer Raw Gum, for bisphenolic curing 6 FKM-Ter-Polymer Raw Gum, for bisphenolic curing 6 FKM-Co-Polymer integrated, bisphenol 7 FKM-Ter-Polymer integrated, bisphenol 8 FKM-Ter-Polymere, for peroxide curing 8 Hydrogenated Butadiene Acrylonitrile Co-Polymer (HNBR) 9 Isobutene-Isopropene Rubber (IIR) 9 Butadien Rubber (BR) 9 Epichlorohydrin Rubber (CO), Homopolymer 9 Epichlorohydrin Rubber (ECO), Copolymer 10 Epichlorohydrin Rubber (GECO), Terpolymer 10 Terpolymer PECO 10 Styrene Butadiene Rubber (SBR) 10 Chlorosulfonated Polyethylene (CSM) 11 Chlorinated Polyethylene (CPE/CM) 11 Silicone Rubber & Compounds 11 Silicone Rubber Color Masterbatches 11 Silicone Rubber Additives 12

Lucene POE 12

Ethylene-Octene-Copolymer 12Ethylene-Butene-Copolymer 12

Carbon Black 13

Reinforcing Grades 13Semi Reinforcing Grades 13Conductive Grades 13 Class A Grades 14 Low PAH Grades 14

Processing Aids 14

Homogenizer and Tackifier 14 Flow Improver 15 Lubricants 15 Peptizer 15Plasticizer, Tackifier, Extender 15 Flame Retardants + Smoke Suppressants 16

Blowing Agents 16

Accelerators / Curing Agents / Retarder 17

Sulfenamides 17Thiazoles 17 Dithiocarbamates 17 Guanidines 17 Dithiophosphate 17 Thiurams 17 Thioureas 17

Polymerbound preparations 18

Sulfenamides 18 Thiazoles 18 Dithiocarbamates 18 Guanidines 18 Thiurams 18 Thioureas 18

Antioxidants / Antiozonants 19

Magnesium Oxide 19

Moisture Absorbents 19

CaO 19 Co-Agents 19

Batch-Off-Release Agents 20

Liquids 20 Dispersions 20 Powders 20

4 5

Our principals Polymers

Acrylonitrile Butadiene Rubber (NBR)

Ethylene-Propylene Rubber (EPR)

Low ACN

Medium-Low ACN

Standard ACN

Standard ACN, fast curing

High ACN

NBR / PVC Polyblend

Copolymers EPM

EPDM

EPDM (Bimodal)

EPDM (Metallocene)

ACN Content

Ethylen Content

Mooney Viscosity, ML (1+4) 100°C


2255 (FDA)7150 (FDA)7150 (L) (FDA)7150 (H) (FDA)287562306240625062606280 (FDA)6830 (FDA)6840 (FDA)6850 (FDA)3250328070307030L7030H

Vistalon 404Vistalon 703Vistalon 706Vistalon 722Vistalon 785Vistalon 805Vistalon 1703 PVistalon 2504 NVistalon 3666Vistalon 7500Vistalon 8600Vistalon 8700Vistalon 8800Vistalon 2502Vistalon 5601Vistalon 6602Vistalon 7001Vistalon 7602Vistalon 9301

22%28%28%28%28%34%34%34%34%34%34%34%34%41%41%34%28%40%

44,5%72,5%65,0%72,0%49,0%78,0%76,8%55,5%64,0%55,5%57,5%63,0%53,5%50,0%68,5%55,0%73,0%55,0%69,0%

55 (50-60)51 (47-57)44 (40-47)60 (55-63)7533 (29-37)41 (38-47)55 (48-54)60 (50-65)80 (75-85)30 (26-35)40 (35-45)50 (45-50)55 (49-59)80 (74-86)576060-80

282142173033252552 (x)82817873 (x)257280606567

low oil resistancefair oil resistancefair oil resistancefair oil resistancefair oil resistancegood oil resistancegood oil resistancegood oil resistancegood oil resistancegood oil resistancegood oil resistancegood oil resistancegood oil resistancehigh oil resistancehigh oil resistancegood oil resistancefair oil resistancehigh oil resistance

------0,9% *3,8%4,5%5,7%8,9%8,0%10,0%4,5%5,0%5,2%5,0%7,5%2,8%

very high cold flexibilityhigh cold flexibilityhigh cold flexibilityhigh cold flexibilityhigh cold flexibilitygood cold flexibilitygood cold flexibilitygood cold flexibilitygood cold flexibilitygood cold flexibilityanti fouling compoundanti fouling compoundanti fouling compoundlow cold flexibilitylow cold flexibility70% NBR 30% PVC70% NBR 30% PVC 70% NBR 30% PVC

very widenarrowbimodalnarrownarrownarrowvery widewidemediumbimodalbimodalbimodalbimodalwidetailoredwidetailored-narrow

high temp. applicationhigh green strengthhigh flex crack resistanceelectr. prop., green strengthhoses, beltsvery high green strengthgreen strength, surfaceelectr. prop., brake padssoft parts, blendsfast curing, good CSvery fast curing, excellent CSvery fast curing, excellent CSvery fast curing, excellent CSblending, moulded foamsgreen strength, high perform.blends, easy processingrapid extrusion, inj.-mouldingfast curing, hot/cold flexibleroofing and sheeting

Capability

Diene Content

Properties

MWD Application information

(x) - contains process oil: Vistalon 8800: 15phr / Vistalon 3666: 75phr * - VNBPlease check that a specific supplier or brand is available in your region.

6 7

FKM-Co-Polymer Raw Gum, for bisphenolic curing FKM-Co-Polymer integrated, bisphenol

FKM-Ter-Polymer Raw Gum, for bisphenolic curing

FKM MLF2-11 I

FKM MLF2-12 II

FKM MLF2-12 III

FKM MLF2-13 I

FKM MLF2-13 II

FKM MLF2-13 III

FKM MLF2-13 IV

FKM MLF2-13W I

FKM MLF2-13W II

FKM MLF2-13W III

BDF 201P *

BDF 275P

BDF 25P

BDF 30P

BDF 302A

BDF 331P

BDF 361P

BDF 362P

BDF 401P

BDF 402P

BDF 403P

BDF 401HP

BDF 60C

BDF 45P

BDF 601P

FKM MLF3-11 I

FKM MLF3-12 I

FKM MLF3-12 II

FKM MLF3-13 I

FKM MLF3-13 II

FKM MLF3-13 III

FKM MLF3-13 IV

FKM MLF3-14 I

higher viscosities available

* P: precompound; A: adhesive promoter incorporated; CP: for compression molding mainly; IP: for injection mainly; EP: for extrusion mainly; HP: high viscosity (copolymers), high fluorine content (terpolymers)

higher viscosities available

Density (g/cm3)

Specific Gravity (g/cm3)

Density (g/cm3)

Fluorine Content (%)




Nominal Viscosity, ML (1+10) 121°C


65-66

65-66

65-66

65-66

65-66

65-66

65-66

65-66

65-66

65-66

66

66

66

66

66

66

66

66

66

66

66

66

66

66

66

68

68

68

68

68

68

68

68

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,82±0,02

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,81

1,86±0,02

1,86±0,02

1,86±0,02

1,86±0,02

1,86±0,02

1,86±0,02

1,86±0,02

1,86±0,02

20-30

31-40

41-50

51-60

61-70

71-80

81-90

61-70

71-80

81-90

20

20

25

30

30

30

30

30

40

40

40

42

43

45

60

20-30

31-40

41-50

51-60

61-70

71-80

81-90

91-100

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

4%

4%

4%

4%

4%

4%

4%

4%

4%

4%

4%

4%

4%

4%

4%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

≤ 0.05%

Co-polymer of Vinylidenfluoride, Hexafluoropropylene

Co-polymer of Vinylidenfluoride, Hexaflu-oropropylene






Co-polymer of Vinylidenfluoride, Hexa-fluoropro-propylene - broad molecular weight distribution



Excellent mold flow, improve mold release and good compression set

Excellent injection behavior, good scorch safety and lack of mould fouling

Excellent mold flow, improve hot tear strength

Excellent flow, excellent mold release and good compression set

With adhesive promoter incorporated, it can be applied by conventional technology for coating

High Elongation grade, good mold flow and hot tear strength

Excellent mold flow, hot tear resistance, improve bonding adhesion

A modified version of BDF 361P specially for electronic application

Excellent processability and low compression set

A modified version of BDF 401P specially for electronic application

A modified version of BDF 401P specially for food contact application

Excellent mechanical properties and low compression set

Excellent compression molding behavior, very low compression set

Higher viscosity version of BDF 25P

Higher viscosity version of BDF 401P, optimized compression set

Ter-polymer of Vinylidenfluoride, Tetra-fluoroethylene, Hexafluoropropylene








Moisture (%)Vol. Change Fuel C / 70h@23°C

Moisture (%)

Chemical description Description

Chemical description

8 9

FKM-Ter-Polymer integrated, bisphenol Hydrogenated Butadiene Acrylonitrile Co-Polymer (HNBR)

Isobutene-Isopropene Rubber (IIR)

FKM-Ter-Polymere, for peroxide curing

Epichlorohydrin Rubber (CO), Homopolymer

Butadien Rubber (BR)

BDT 2461E

BDT 40CP

BDT 235P

BDT 435P

BDT 40P

BDT 246-2CP

BDT 246-1EP

BDT 246-2EP

BDT 246-3EP

BDT 601P

BDT 351P

BDT 651P

BDT 501HP

BDTL 30P

BDP 435

BDP 235

CO 3604 CO 3605 CO 3606

CHIMEI Kibipol

Specific Gravity (g/cm3)

Density (g/cm3)




Density g/cm³



Chlorine content

68

68

68

68

68

69

69

69

69

68

68

68

70

66

70

70

1.30 ± 0.101.30 ± 0.101.30 ± 0.10

PR-255PR-040

1,85

1,85

1,85

1,85

1,85

1,86

1,86

1,86

1,86

1,85

1,85

1,85

1,89

1,80

1,90

1,90

40 ± 550 ± 560 ± 5

low cis BR (<35%)high cis BR (>97%)

35

40

25

40

40

46

23

34

25

60

35

60

53

30

45

25

36 ~ 3836 ~ 3836 ~ 38

MV 1+4: 54MV 1+4: 45

3%

3%

3%

3%

3%

2%

2%

2%

2%

3%

3%

3%

2%

4%

29%

29%

Li-catalyzedNd-catalyzed

Excellent extrusion behavior, low die swelling, good chemical resistance


Low viscosity version of BDT 435P, excellent mold flow, hot tear resistance, improve bonding adhesion

Excellent mold flow, hot tear resistance, improve bonding adhesion


Excellent mold flow, improve mold release and very good chemical resistance

Good processability, metal bonding properties and superior fluid resistance

Good processability, metal bonding properties and superior fluid resistance

Good processability, improved bonding properties and superior fluid resistance

Excellent balance of resistance to compression set and fluid

Low viscosity version of BDT 651P, good hot tear resistance, mould flow and metal bonding properties

Good hot tear resistance, mould flow and metal bonding properties

Good mold flow, superior fluid resistance better than standard FKM terpolymers

Slightly improved low temperature flexibility

Ter-polymer of Vinylidenfluoride, Tetrafluoropropylene, Hexaflouropropylene

Ter-polymer of Vinylidenfluoride, Tetrafluoropropylene, Hexaflouropropylene

Epichlorohydrin rubber CO homopolymerized by epichlorohydrinEpichlorohydrin rubber CO homopolymerized by epichlorohydrinEpichlorohydrin rubber CO homopolymerized by epichlorohydrin

colorless, odorlesswhite, modern tyre quality

Vol. Change Fuel C / 70h@23°C

Compression Set 70h@200°C

Description

Chemical description

Typical application

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Zhanber

Exxon Chlorobutyl CIIR

Exxon Bromobutyl BIIR

Exxpro

Butyl

Density (g/cm3)

Density (g/cm3)



ZN28255ZN350512ZN35053ZN35056ZN35058ZN35156ZN35158ZN35256ZN35258ZN35355ZN39057ZN43056ZN43058ZN43156

10662211222222442255303534333745065S268S365S

0,950,960,960,960,960,960,960,960,970,950,960,970,960,97

0,920,930,930,930,930,930,930,930,920,920,92

50±7125±730±765±785±760±780±760±780±750±770±765±785±7 65±7

38 ± 432 ± 432 ± 446 ± 546 ± 545 ± 535 ± 545 ± 529 - 3546 - 5630 - 36

≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5≤0,5

0,02%0,02%0,02%0,02%0,02%

0,03%0,03%0,03%

28±1,536±1,536±1,536±1,536±1,536±1,536±1,534±1,534±1,536±1,539±1,543±1,542±1,5 43±1,5

non stainingnon stainingnon stainingnon stainingnon staining

non stainingnon stainingnon staining

28±45±44-105±45±412±412±428±428±452-604-105±44-10 12±4

1,26±0,081,08±0,151,03±0,301,08±0,151,03±0,300,47±0,050,75±0,071,10±0,100,85 - 1,251,50 - 1,902,00 - 2,60

w-% Chlorinemol-% Brominemol-% Brominemol-% Brominemol-% Brominemol-% Brominemol-% Brominemol-% Brominemol-% Unsaturationmol-% Unsaturationmol-% Unsaturation

Volatile matter (%)

Antioxydant Content

ACN content (%)

Iodine value (mg / 100mg)

Functional Content

10 11

Epichlorohydrin Rubber (ECO), Copolymer

Epichlorohydrin Rubber (GECO), Terpolymer

Terpolymer PECO

Chlorosulfonated Polyethylene (CSM)

Chlorinated Polyethylene (CPE/CM)

Silicone Rubber Color Masterbatches

Silicone Rubber & Compounds

Styrene Butadiene Rubber (SBR)

ECO 2404

ECO 2405

ECO 2406

GECO 1204

GECO 1205

GECO 1206

PECO 1204

PECO 1205

PECO 1206

CSM 40

CM 3660 T

CM 3690

CM 3685

CM 3675

CM 3665

CM 3660

CM 3655

CM 3650

CM 4085

CM 3055

CPE 135 A

MF 1032

HCR

LSR

HCR

LSR

FSR

F-LSR

RTV

Additives

ESBR

LG Chem Eco grades

CHIMEI Kibipol SSBR





MooneyViscosity ML (1+4) 125°C


Density g/cm³

Density g/cm³

Density g/cm³

Type

Chlorine Content (%)

Chlorine content

Chlorine content

Chlorine content

Chlorine content

Shore A

Styrene content

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

1.20 ± 0.10

33043305330633073308

35 - 3735 - 3735 - 3735 - 3735 - 3735 - 3735 - 3735 - 3739 - 4129 - 3135 - 37 31 - 33

Pigments dispersion in silicone polymer for solid silicone, HTV-HCRPigments dispersion in fluids and resins for liquid silicone, LSR-RTV

High Consistency RubberLiquid Silicone RubberFluoro Silicone RubberFluoro Liquid Silicone Rubber Room Temperature Vulkanizing

1500 stabilized1502 stabilized1712 oil extended1721 oil extended1723 low PCA oil ext.1778 oil extendedPR-1205 Li catalyzed

40 ± 5

50 ± 5

60 ± 5

40 ± 5

50 ± 5

60 ± 5

40 ± 5

50 ± 5

60 ± 5

41-5051-6061-7071-8081-90

60 - 75 85 - 95 80 - 90 70 - 80 60 - 70 55 - 65 50 - 60 45 - 55 80 - 100 50 - 60 80 - 100 50 - 60

525244-5444-5440-4841-5147

24 ~ 27

24 ~ 27

24 ~ 27

12 ~ 18

12 ~ 18

12 ~ 18

12 ~ 18

12 ~ 18

12 ~ 18

35 ± 2%35 ± 2%35 ± 2%35 ± 2%35 ± 2%

≤ 60≤ 60≤ 60≤ 55≤ 55≤ 55≤ 55≤ 55≤ 55≤ 65≤ 60≤ 65

23,5%23,5%23,5%40,0%23,5%23,5%18,0%

stainingnon stainingstainingstainingstainingnon stainingnon staining

Epichlorohydrin rubber ECO copolymerized by epichlorohydrin, ethylene oxide



Epichlorohydrin rubber GECO; polymerized by epichlorohydrin, epoxy ethane and allyl glycidyl ether



Hyperoxide epichloryhydrin rubber PECO copolymerized by epichlorohydrin, epoxy ethane and epoxy propane



Excellent processing performance, higher breaking strengt and elongation, good weather resistance, oil resistance, flame retardancy and electrical insulating properties. Particularly suitable for processing all kinds of rubber products, such as rubber hose, wire and cable sheath, etc.

Wire&Cable, hoses Rubber Compounding Rubber Compounding Wire&Cable, hoses W&C, hoses, clean surface, high extr. Speed W&C, hoses, clean surface, high extr. Speed Cable jacketing Cable jacketing High level flame and oil restance Suitable for magnetic materials PVC impact modifier Impact modifier for ABS and PU.

Mesgo Iride ColorsMesgo Iride Colors

Dow Corning / Xiameter

dark brown, tyre qualitypale, industrial qualitydark brown, industrial purposedark brown, industrial purposedark brown, industrial purposepale, industrial purposewhite (for EC label tyres)

Typical application

Typical application

Typical application

Typical application

Typical application

Typical application

12 13

Silicone Rubber Additives

High Temperature additives

Flame Retardant additives

Anti-blooming addtives

Polymer Modifier additives

Release Agent additives

Coefficient of Friction additives

Marker additives

Silicone Rubber Platinum additives

HTA FRA ABA PMA RAA CFA MA RCA

Mesgo Iride Colors

Lucene POE

Carbon Black

Ethylene-Octene-Copolymer

Reinforcing Grades

Semi Reinforcing Grades

Conductive Grades

Ethylene-Butene-Copolymer

LC 160

LC 170

LC 180

LC 100

LF 100

LC 370

LC 670

LC 760

VULCAN 10HD

VULCAN 9

VULCAN 9H

VULCAN 6

VULCAN 7H

REGAL 300

VULCAN 3

VULCAN M

VULCAN 3H

VULCAN J

VULCAN 1345

VULCAN 1391

STERLING SO-1

STERLING SO

STERLING V

STERLING 105

STERLING VH

REGAL SRF

SPHERON 4000

VULCAN P

VULCAN XC-72

BLACK PEARLS 2000

LC 165

LC 175

LC 168

LC 305

LC 565

Density (g/cm³)

STSA (m²/mg)

STSA (m²/mg)

STSA(m²/mg)

Density (g/cm³)

MI (g/10min)

Type ASTM-D1765

Type ASTM-D1765

Type ASTM-D1765

MI (g/10min)

Melting Temp. (°C)

Iodine (mg/g)

Iodine (mg/g)

Iodine (mg/g)

Specific Surface

Specific Surface

Specific Surface

Structure

Structure

Structure

Melting Temp. (°C)

0,51,11,21,21,23,05,013,0

N134N115/SAFN121N220/SAFN234N326/HAF-LSN330/HAFN339N347/HAF-HSN375n.a.n.a.

N539/FEF-LSN550/FEFN660/GPFN683/APFN650/GPF-HSN772/SRF-LM-NS

N294/SCFN472/ECFn.a.

0,51,11,23,05,0

0,8630,870,8850,9020,9030,8700,8700,863

1291231141041137876878291122157

39403636353129

961271500

0,8620,8700,8620,9030,865

5658739696575841

1421601211211208282909090124202

43433635363032

172253n.a.

3052329036

36232023231394

979611198101688810097969499

82847387825748

97120n.a.

322220128

5771828888707048

10111313211412572102120124114110134

111121901331226552

116174330

132123119115124111104110104115128145

58596055565754

10487164

4370469054

Mooney Viscosity MU

crushed OAN (ml/100g)

crushed OAN (ml/100g)

crushed DBP (ml/100g)

Mooney Viscosity MU

Hardness Shore A

OAN (ml/100g)

OAN (ml/100g)

DBP (ml/100g)

Tint strength % ITRB



Hardness Shore A

14 15

Class A Grades

Low PAH Grades

SPHERON 6400A

SPHERON 6000A

SPHERON 5000A

SPHERON SO-1A

SPHERON SOA

SPHERON SO-LP

SPHERON 4000-LP

VULCAN 6-LP

STSA (m²/mg)

Benzo(a)- pyrene(max value)

Type ASTM-D1765

Type ASTM-D1765

Iodine (mg/g)

Specific Surface Structure

PAH content* (ppm)

n.a.n.a.n.a.N539/FEF-LSN550/FEF

N550/FEFn.a.N220/SAF

1821273840

111

1620274343

7170808284

111

9592120111121

202020

3437455760

crushed DBP (ml/100g)

For each of 8 PAH included in EU list (max value)

DBP (ml/100g)

For sum of 18 PAH included in GS Mark list (max value)


* Cabot internal test method requires 48 hours toluene extraction (Soxhlet)* STSA, Iodine and OAN is the same as for normal carbon black grades without low PAH

Processing Aids

Homogenizer and Tackifier

Flow Improver

Lubricants

Peptizer

Plasticizer, Tackifier, Extender

MA-B20

MA-B40

MA-B50

MA-B60

MA-F44

MA-F50

MA-F60

MA-F60T

MA-F70S

MA-F84

MA-L16

MA-L20

MA-L22

MA-L25

MA-L33

MA-L42

MA-L88

MA-P60

MA-P66

MA-P168

INDOPOL

pastille colour

pastille colour

pastille colour

pastille colour

Extra benefits besides of major function




Alkylphenol formaldehyde resin

Mixture of aromatic hydrocarbon resins

Mixture of aromatic hydrocarbon resins

Mixture of aliphatic hydrocarbon resins

Reacted blend of fatty acid derivatives

Zinc soaps of unsaturated, high molecular weight fatty acids

Blend of zinc soaps of high molecular weight fatty acids

Structure of fatty acid soaps and amides

Blend of zinc soaps of unsaturated, high molecular weight fatty acids

Zinc soaps of unsaturated, high molecular weight fatty acids

Structure of fatty acid soaps and amides

Fatty acid ester derivative

High molecular weight, aliphatic fatty acid ester

Fatty acid ester derivative

Structure of high molecular weight esters and fatty acid soaps

Blend of fatty acid derivative

Mixture of fatty acid Soaps

Blend of Di-benzamido-diphenyl-disulphide and metal soaps

Blend of organo metal complexes, fatty acid derivatives and peptising agents

Blend of Di-benzamide-diphenyl-di-sulphide (DBD) on low-melt carrier

Polybutene

dark brown

dark brown

yellow

yellow

pale yellow

beige

yellowish

beige

beige

pale yellow

pale yellow

white

white

white

beige

beige/ white

beige/ brown

beige/ brown

bluish/ greenish

bluish

Synthetic Hydrocarbon polymer made by polymerization of Isobutene + N-Butene

Very effective tackifier for synthetic rubbers

Tackifier, flow improver for dark compounds, also for different polarity/viscosity blends

Tackifier, flow improver for light dark compounds, also for different polarity/viscosity blends. Prevents mill bagging

Tackifier, flow improver for white/pale compounds, also for different polarity/viscosity blends

For high mineral/silica filled NR and synthetic rubbers. Cell structure improver for EVA foams

Very effective for physical NR and synthetic rubber peptisation, enhances carbon black dispersion.

Dedicated for low temperature mixing, improves NR physical peptisation

Improves NR physical peptisation, enhances calandering and extrusion, provides smooth surface and higher tear strength

Very effective for white fillers, especially for high loaded Silica compounds, prevents blooming

SBR, BR, NR sulphur curing activator, NR mastication viscosity reducer, may replace stearic acid or other activators

For practically all elastomers, reduces sticking on metal surfaces, enhances injection moulding.

General purpose, works with most fillers and cureatives. Enhances mould release.

High temperature capable, very effective in polar polymers. Improves filler incorporation.

General purpose, works with most fillers and cureatives. Improves mould filling

Prevents filler agglomeration in high filled compounds. Im-proves filler incorporation in open and closed mixing systems.

Special recommendation for EPM and EPDM. Enhances mould flow.

Economical lubricant for low cost NR/SBR/BR compounds.

Mild early stage NR mastication agent, enhances filler dispersion, extrusion, mould flow.

Improves pre-mastication of NR. Peptizer and processing agent for low dosage. General purpose capable.

Multifunctional peptizer without premastication. Very effective, low dosage. Easy incorporation at lower temperatures.

Clear and bright viscous liquid polymers ( molecular weights between 180 - 6000) plasticizing and tackifying numerous natural and synthetic elastomers

16 17

Flame Retardants + Smoke Suppressants

Firemaster 2100R

Reofos + Kronitex

ZB-467

Decabromodiphenylethane Isopropylated TriarylPhosphates + Phosphoric Acid Esters

Zinc Borate

Bromine-based Flame RetardantPlasticizing Phosphorus-Based Flame Retardants

Smoke Suppressant

Blowing Agents

Cellcom CAP

Cellcom H

Cellcom KE

Cellcom OBSH, EPOB/75, 80 Paste

Kycerol Series

Cellcom AC activated

Cellcom A80

Cellcom AC ACMP Series Cellcom AC7D80 Paste

Cellcom PTSS, TSS

Cellcom 5PT

Type Process Temp.

Micro-Capsules

TSH

OBSH

NaHCO3

ADC activ.

DNPT

ADC

TSSC

5PT

high pressurized gases (e.g. butene), enclosed in polymeric shells which break off

p-Toluenesulfonyl hydrazide

p-Toluenesulfonyl Acetone Hydrazon (Cellcom KE)

P,P‘-Oxybis Benzene Sulfonyl Hydrazide

Sodium-Bicarbonate, Sodium-Hydrogencarbonate

Azodicarbonamide, with or without activating substances

DiNitrosopenta methylen Tetramin

p-Toluenesulfonyl Semicarbazide

5-Phenyl Tetrazol

80-140°C

100-155°C

170-180°C

155-165°C

150-190°C

150-210°C

175-200°C

200-210°C

227-235°C

234-245°C

Suitable for most polymers. Shell residue may suffer the pureness of the blown product

Elastomer foaming for high hygienic (medical) purposes: NR, SBR, IIR, CR, EPDM, EVA.

Cellcom KE provides finer foam structure

Fine foam structure, no odoir, no colou-ring. Applicable for food and medical products. PVC, EVA, EPDM, CR, NR, SBR, NBR, NBR/PVC, PE-LD, PU

No odor, non-toxic, endothermic decom-position. LD-PE, HD-PE, PS, PP, PVC-U, ABS, PA, PC, TPE

X-LDPE, EVA, PE, PVC, PS, ABS, TPE, all foamable elastomers (e.g. SBR, NBR, CR, NBR/PVC, EPDM)

Typical Blowing Agent for elastomer foaming. Applicable to some plastics and ceramics. Restricted usability due to emis-sions. NR, SBR, BR, CR, HI-PS, PVC-P

Chemical blowing agent, available in various types. Any PVC, HD-PE, LD-PE, PP, PS, HI-PS, EVA, ABS, PPO, TPE and various elastomers basing on EPDM, CR

High process temperatures, fulfils whiteness requirements. ABS, PP, HI-PS, HD-PE, PVC, PPO, PA

Highest process temperatures, only Nitrogen emission. PC, PA, PET, ABS, Fluoropolymers and Fluoroelastomers

Application Details

Accelerators / Curing Agents / Retarder

Sulfenamides

Thiazoles

Thioureas

Dithiocarbamates

Thiurams

Guanidines

Dithiophosphate

CBS

TBBS

MBS

DCBS

MBT

MBTS

ZMBT

ETU

DETU

DPTU

ZDBC

ZDEC

ZDMC

TDEC

ZEPC

DPTT

TBzTD

TETD

TiBTD

TMTD

TMTM

DPG

DOTG

ZDTP

Active Ingredient Colour

N-cyclohexyl-2 benzothiazole sulphenamideN-tert-butyl-2-benzothiazyl sulfenamideBenzothiazyl-2-sulphenmorpholideN,N-dicyclohexyl-2-benzothiazole sulphenamide

2-Mercaptobenzothiazole Dibenzothiazyldisulphide Zinc salt of 2-mercaptobenzothiazole

N-N‘-Ethylenethiourea N-N‘-Diethylthiourea N-N‘-Diphenylthiourea

Zinc dibutyl dithiocarbamate Zinc diethyl dithiocarbamate Zinc dimethyl dithiocarbamate Tellurium diethyldithiocarbamate Zinc ethylphenyl dithiocarbamate

Dipentamethylene thiuram tetrasulphide Tetrabenzylthiuram disulphide Tetraethylthiuram disulphide Tetraisobutylthiuram disulphide tetramethylthiuram disulphide Tetramethylthiuram monosulphide

Diphenylguanidine Di-o-tolylguanidine

Zinc dialkyl dithiophosphate

off-white/greyishoff-white/greyishyellowlight brown

light yellowyellowlight yellow

whitewhitewhite

whitewhitewhiteorange and yellowwhite

white to light yellowwhitelight yellowwhitewhiteyellow

off-white/greyish off-white/greyish

yellowish

granules/oil coated powder granules/oil coated powder grains granules/oil coated powder

granules/oil coated powder granules/oil coated powder granules/oil coated powder

granules/oil coated powder granules/oil coated powder granules/oil coated powder

granules/oil coated powder granules/oil coated powder granules/oil coated powder granules/oil coated powder granules/oil coated powder

granules/oil coated powder granules/oil coated powder granules/oil coated powder granules/oil coated powder granules/oil coated powder granules/oil coated powder

granules/oil coated powder granules/oil coated powder

vicous liquid

Appearance

This shows only a selection of chemicals, further are available.

18 19

Polymerbound preparations

Moisture Absorbents

Antioxidants / Antiozonants

Magnesium Oxide

Sulfenamides

Co-Agents

CaO

Thiazoles

Dithiocarbamates

Thiurams

Guanidines

Thioureas

Actmix CBS-80GE F140

Actmix MBS-80GE F200

Actmix TBBS-80GE F140

TAC

Biesterfeld TAC 70E

TAIC

TAIC 70

ANFOGEN #200

ANFOGEN #600

ANFOGEN #600H

IPPD

6PPD

TMQ standard

Actmix MBT-80GE F140

Actmix MBTS-75GE F140

Actmix ZMBT-80GE F140

Actmix ZDBC-80GE F140

Actmix ZDEC-75GE F140

Actmix ZDMC-80GE F140

Actmix ZBEC-70GE F100

Actmix DPTT-70GE F140

Actmix TBzTD-75GE F140

Actmix TMTD-80GE F140

Actmix TMTM-80GE F500

Actmix DPG-80GE F140

Actmix DOTG-75GE F140

Actmix ETU-80GE F140

Active Ingredient

Chemical composition

Chemical composition

Active IngredientCarrier

Consistency

Content (% m/m)

Conc.

Meltin Point, onset (°C)

N-cyclohexyl-2 benzothiazole sulphenamide Benzothiazyl-2-sulphenmorpholide

N-tert butyl-2-benzothiazyl-sulphenamide

Triallylcyanurat Triallylcyanurat Triallylisocyanurat Triallylisocyanurat

Calcium oxide with special oil Coated CaO with fatty acid Coated CaO with fatty acid fine particle size

N-isopropyl-N‘-phenyl-p-phenylendiamineN-(1,3-dimethyl-butyl)-N‘-phenyl-p-phenylendiamine polymeric 2,2,4-trimethyl-1,2-dihydrochinoline

2-Mercaptobenzothiazole Dibenzothiazyldisulphide Zinc salt of 2-mercaptobenzothiazole

Zinc dibutyl dithiocarbamate Zinc diethyl dithiocarbamate Zinc dimethyl dithiocarbamate Zinc dibenzyldithiocarbamate

Dipentamethylene thiuram tetrasulphide Tetrabenzylthiuram disulphide Tetramethylthiuram disulphide Tetramethylthiuram monosulphide

Diphenylguanidine Di-o-tolylguanidine

N-N‘-Ethylenethiourea

EPDM / EVAEPDM / EVAEPDM / EVA

liquiddry liquidliquiddry liquid

EPDM / EVAEPDM / EVAEPDM / EVA

EPDM / EVAEPDM / EVAEPDM / EVAEPDM / EVA

EPDM / EVAEPDM / EVAEPDM / EVAEPDM / EVA

EPDM / EVAEPDM / EVA

EPDM / EVA

808080

100%70%100%70%

755080

807580

80808070

70758080

8075

70

granulesgranules granules

Extrusion, Injection for rubber & plasticRubber, PVC, Sealants, AdhesivesBreathable film, Biodegradable film

dark granulesdark granulesamber coloured granules

granules granules granules

granulesgranulesgranulesgranules

granulesgranulesgranulesgranules

granulesgranules

granules

Appearance

Application

Appearance

Magnesia 291

Magnesia 295

Magnesia 2923

Magnesia 2933

Actmix MgO-75GE F140

Bulk Density g/l

Activity CMA-Seconds

Surface Aream²/g

9 350500380380

45185110150

99,599,89999

3-8

55

98,29998,298,275

Particle Size >45µm %

Median Particle Size µm

MgO Content %

This shows only a selection of preparations, further preparations are available and also other carriers.

20 21

Liquids

Dispersions

Powders

Active

Active

Active

Batch-Off-Release Agents

Alkon 7315

Alkon 7610

Alkon 3531

Alkon 6500

Alkon 6280

Alkon 6240

Alkon 9370

Alkon 9180

Alkon 9520

Alkon 9310AA

Alkon 9420

Alkon 9195L

Alkon 9580

Alkon 9420CR1

28%16%35%

30%35%26%

100%100%100%100%100%100%100%100%

Easy dispersed in waterUniform coatings on rubber compounds

Supperior release propertiesCustomized formulations available

Ready-made dispersions Excellent release on the treated compound

Superior low and high visibility coatingsCustomised complex dispersions

Easy dispersed in waterUniform coatings on rubber compounds

Minimum foaming or sedimentationExcellent release propertiesVery strong and rigid coating

Notes

22 23

Notes

Imprint Published by: Biesterfeld Performance Rubber GmbHFerdinandstrasse 4120095 HamburgGermanyPhone: +49 40 [email protected]

Registered Office: Hamburg, Commercial Register: Hamburg, HRB 8492, VAT ID DE811186167Managing Directors: Sascha Hennig, Peter Wilkes

Our raw material information, data and graphics was obtained from the records of our raw material suppliers.Local availability of products might differ from country to country.

Disclaimer:We shall not be liable for the suitability of the goods for the purpose intended by Customer, unless the achievement of a certain outcome of the utilisation was expressly incorporated into the contract. Our advice, information or recommendations regarding application shall be provided to the best of our knowledge. As the actual application is beyond our scope of influence, and as the circumstances of such application are not completely foreseeable, written and verbal indications, suggestions etc. can only be provided on a non-binding basis. They shall in particular not release Customer from the obligation to examine our products and goods for their suitability with regard to the intended processes and purposes.

Biesterfeld Performance Rubber GmbHWerkstraße 1 67354 Römerberg Tel.: +49 6232 60049-0Fax: +49 6232 60049-99rubber@biesterfeld.comwww.biesterfeld-performancerubber.com

Documents

Performance Rubber & Additives - Kuttnerkuttner.ru/download/biesterfeld.pdf · Performance Rubber & Additives Polymers Portfolio Lucene POE ... NBR / PVC Polyblend Copolymers EPM