Sheet, Plate & Rollformed Aluminium
Rolled Aluminium Products, Sheet Metal, Plate Metal and Rollformed Metal
Mechanical Properties: Sheet and Plate
Sheet and Plate: Alloy 5182 - 8011
Alloy and
Temper Thickness5(mm) Tensile Strength (MPa)
Over Up ToUltimate
Min.
Ultimate
Max.
Yield
Min.
Yield
Max.
Elongation (% min in
50mm or 5.653)
5182 - H14 0.15 0.50 325 385 5
5182 - H19 0.15 0.50 385 2
Alloy & Temper Thickness5(mm) Tensile Strength (MPa)
Over Up ToUltimate
Min.
Ultimate
Max.
Yield
Min.
Yield
Max.
Elongation (%
min in 50mm or
5.653)
6061 - O11 0.25 0.50 150 85 14
0.50 3.25 150 85 16
3.25 12.00 150 85 18
12.00 25.00 150 16
6061 - T4 0.25 0.50 205 115 14
0.50 6.00 205 115 16
6.00 25.00 205 115 16
6061 - T4212 0.25 0.50 205 95 14
0.50 6.00 205 95 16
6.00 25.00 205 95 16
6061 - T6 &
T6212
0.25 0.50 290 240 8
0.50 12.00 290 240 10
12.00 25.00 290 240 7
Alloy and
Temper Thickness5(mm) Tensile Strength (MPa)
Over Up To
Ultimate
Min.
Ultimate
Max.
Yield
Min.
Yield
Max.
Elongation (% min in
50mm or 5.65 >3)
8011 - O 0.15 0.30 75 105 16
0.30 0.80 75 105 20
0.80 1.30 75 105 25
1.30 5.00 75 105 30
8011 - H12 0.20 0.50 100 135 3
0.50 0.80 100 135 4
0.80 1.30 100 135 6
chanical Properties of Alloys 5182 - 80116 from Ullrich Aluminium http://www.ullrich.co.nz/rolled/rpmech11.php
2 01-May-2013 6:49 PM
7/28/2019 Mechanical Properties of Alloys 5182 - 80116
2/2
1.30 3.00 100 135 8
3.00 6.00 100 135 9
8011 - H14 0.20 0.50 115 150 2
0.50 0.80 115 150 3
0.80 1.30 115 150 4
1.30 3.00 115 150 5
3.00 6.00 115 150 7
8011 - H16 0.20 0.50 140 170 1
0.50 0.80 140 170 2
0.80 1.30 140 170 3
1.30 3.00 140 170 4
3.00 6.00 140 170 5
8011 - H18 0.20 0.50 160 1
0.50 0.80 160 2
0.80 1.30 160 3
1.30 3.00 160 4
Footnotes:
1. Mechanical test specimens are taken as detailed under Sampling and Testing.
3. A = Cross-sectional area of specimen.
5. These yield strengths are not determined or guaranteed unless specifically requested.
11. Annealed (O temper) material shall, upon heat treatment or heat treatment and ageing, be capable of
developing the mechanical properties applicable to T42 or T62 temper material respectively.
12. Material heat-treated (T42) or heat-treated and aged (T62), from any temper by the user, should attain themechanical properties applicable to these tempers.
New Zealand / International Sales
Visit our Sales Centres
Visit www.ullrich.co.nz
Phone: 0800 500 338 (Within NZ)
Email: general enquiry form
Orders: order form
Australia
Visit our Sales Centres
Visit www.ullrich.com.au
Phone: 1300 650 075 (Within AU)
Email: general enquiry form
Orders: order form
Ullrich Aluminium Company Ltd, New Zealand
Aluminium Castings - Aluminium Extrusions - Aluminium Finishes - Aluminium Ladders, Commercial - Building ProductsDivision - Cladding, Wintec UlltraClad- Decorative Metals - Download Brochures - Extruded Aluminium Bends -Fabricated Aluminium - Fasteners - Machinery, Tekna - Marine Products - Sheet, Plate & Rollformed Aluminium - WeldingProducts - Wintec UlltraClad Cladding -
Company Profile - Contact Details - Sales Centres - News - Specials - Interesting Links - Home - TOP
chanical Properties of Alloys 5182 - 80116 from Ullrich Aluminium http://www.ullrich.co.nz/rolled/rpmech11.php
2 01-May-2013 6:49 PM