Measurement of the mode II intralaminar fracture toughness and R-curve of polymer composites using a modified Iosipescu specimenand the size effect lawCatalanotti, G., & Xavier, J. (2015). Measurement of the mode II intralaminar fracture toughness and R-curve ofpolymer composites using a modified Iosipescu specimen and the size effect law. Engineering FractureMechanics, 138, 202-214. https://doi.org/10.1016/j.engfracmech.2015.03.005
Published in:Engineering Fracture Mechanics
Document Version:Peer reviewed version
Queen's University Belfast - Research Portal:Link to publication record in Queen's University Belfast Research Portal
Publisher rightsCopyright 2015 Elsevier.This manuscript version is made available under the CC-BY-NC-ND 4.0 license (http://creativecommons.org/licenses/by-nc-nd/4.0/), whichpermits distribution and reproduction for non-commercial purposes, provided the author and source are cited.
General rightsCopyright for the publications made accessible via the Queen's University Belfast Research Portal is retained by the author(s) and / or othercopyright owners and it is a condition of accessing these publications that users recognise and abide by the legal requirements associatedwith these rights.
Take down policyThe Research Portal is Queen's institutional repository that provides access to Queen's research output. Every effort has been made toensure that content in the Research Portal does not infringe any person's rights, or applicable UK laws. If you discover content in theResearch Portal that you believe breaches copyright or violates any law, please contact [email protected].
Download date:01. Sep. 2021
Measurement of the mode II intralaminar
fracture toughness and R-curve of polymer
composites using a modified Iosipescu
specimen and the size effect law
G. Catalanotti a,∗, J. Xavier baDEMec, Faculdade de Engenharia, Universidade do Porto, Rua Dr. Roberto
Frias, 4200-465, Porto, Portugal.
bOptics and Experimental Mechanics Laboratory, INEGI, Campus da FEUP, Rua
Dr. Roberto Frias 4200-465 Porto, Portugal.
Abstract
A modified Iosipescu specimen is proposed to measure the mode II intralaminarfracture toughness and the corresponding crack resistance curve of fibre reinforcedcomposites. Due to the impossibility of scaling the specimen, a modification of theclassical size effect method is proposed. The classical Iosipescu shear feature wasused and tests were coupled with digital image correlation to support the proposedapproach. Experiments were performed on IM7/8552 material system and the R-curve was obtained. The steady–state value of the fracture toughness of the ply isfound to be equal to R0ss = 34.4 kJ/m2.
Key words:
A. Polymer-matrix composites (PMCs), B. Fracture toughness, C. Analyticalmodelling, D. Mechanical testing
1 Introduction1
The intralaminar fracture toughness is a key parameter used to screen and to2
qualify material systems, and is an input parameter for strength analysis mod-3
els. Some of those, as recent progressive damage models, use softening laws4
∗ Corresponding authorEmail address: [email protected] (G. Catalanotti).
Preprint submitted to Eng Fract Mech 30 January 2015
that can be completely defined once the R-curve of the material is known [1–5
4]. Others, as Finite Fracture Mechanics (FFMs) models [5–8], require the6
fracture toughness (together with the strength of the laminate) as input pa-7
rameters.8
Despite the importance of knowing the intra-laminar fracture toughness of9
composite laminates, very few tests methods were developed in the recent10
past. Generally the R-curve is measured using Compact Tension or Compact11
Compression specimens [9], the last if the R-curve associated with the propa-12
gation of a kink band is required. Several difficulties arise in the execution of13
the experimental tests, in particular the measurement of the crack extension14
and the computation of the J-Integral around the crack tip [10]. Moreover, the15
orthotropy of the material complicates the tests and the data post-processing.16
Those difficulties drastically increase when measuring the R-curve in mode17
II. In this case no tests method exists and, to the authors’ best knowledge,18
no relevant work has been done using fibre-reinforced plastics. However, the19
measurement of the R-curve in mode II could be very valuable because it20
would enable the generalization of several analysis models developed for mode21
I propagation (e.g., FFMs and progressive damage models).22
The authors recently proposed the use of the size-effect methods developed23
by Bazant (mainly for rocks and ceramics) to measure the R-curve of fibre re-24
inforced composites [11,12]. It was demonstrated that size effect method can25
be effectively used to measure the R-curve of a laminate (or a ply), drasti-26
cally simplifying the experimental tests. Indeed, using the size effect law it is27
not required to measure the crack extension, a parameter whose experimental28
measurement is quite difficult when using heterogeneous materials, particu-29
larly under compression, under shear, and in the presence of bridging effects.30
In this paper the size effect method is applied to a modified Iosipescu speci-31
men. This experimental method is commonly used to measure the elastic and32
strength parameters of fibre–reinforced plastic in shear and its ability to ap-33
ply a uniform shear stress field in the gauge section of the specimen has been34
demonstrated [13]. The details of the method are given in [14]. Therefore, the35
Iosipescu test method was chosen to apply the shear stress to a cracked spec-36
imen. The main inconvenient of this method is that the experimental device37
is standardized and it is not possible to scale specimens of the same geometry38
to use the classical size effects method [15]. To overcome this limitation, a39
modification of the size effects method is proposed. Digital image correlation40
was coupled to the Iospiescu tests to provide the strain field at the centre of41
the specimens.42
2
2 Analytical Model43
2.1 Linear-elastic material44
Let x1 and x2 be the material axes of a two-dimensional orthotropic solid.45
The energy release rate in mode II for a crack propagating in the x1 direction46
reads:47
GII =1
EK2
II (1)
where E is the equivalent modulus and KII is the stress intensity factor in48
mode II. The equivalent modulus reads [16]:49
E =(
s11 s221 + ρ
2
)−1/2
λ−1/4 (2)
where slm are components of the compliance tensor computed in the x1-x250
coordinate system, and λ and ρ are two dimensionless elastic parameters given51
as [16]:52
λ =s11s22
ρ =2 s12 + s662√s11s22
(3)
The measurement of the ply fracture toughness is based on balanced cross ply53
laminates [9]. The plies that are perpendicular to the direction of the crack54
propagation (0◦ plies) have a fracture toughness that is two or three orders55
of magnitude higher than that of the plies parallel to the crack propagation56
(90◦ plies). This is due to the fact that the former plies experience a fibre57
dominated failure whilst the latter experience a matrix dominated failure.58
Neglecting the possible small interactions between these two different failure59
modes, an energy balance shows that the fracture toughness of the laminate60
along the x1 direction is simply one half of the fracture toughness of the 0◦61
ply for the same direction.62
If a balanced cross ply is used (λ = 1), equation (2) yields:63
E = E(
1 + ρ
2
)−1/2
(4)
where E is the Young’s modulus along a preferred direction of the material.64
3
Consider now a modified Iosipescu specimen as shown in Figure 1. The width65
of the specimen is 2W = 20mm while the length is 80mm. The specimen66
has a gauge section of width 2w, created with two symmetric notches, and67
two symmetric cracks on the gauge section of length a. Two dimensionless68
parameters are defined: (i) the ratio between the crack length and the width69
of the gauge section, α = a/w; and (ii) the ratio between the width of the70
gauge section and the width of the specimen, β = w/W . Figures 1(a) and 1(b)71
shows the specimen when 0 < β < 1 and β = 1, respectively.72
[Fig. 1 about here.]73
The stress intensity factor of equation (1) depends on the dimension of the74
specimen (a characteristic size, w), on the geometry (α and β), and on the75
remote applied load P or stress τ :76
KII = τ√wφ (α, ρ, β) =
P
2 t√wφ (α, ρ, β) (5)
where τ = P/ (2wt).77
Since β = w/W , the previous equation can be rewritten as:78
KII = τ√
β Wφ (α, ρ, β) (6)
Using (1), the energy release rate reads:79
GII =W
Eβ τ 2 φ2 (α, ρ, β) . (7)
Equation (7) yields the energy release rate for a given applied stress τ . At the80
peak load, when the maximum stress is τu, the energy release rate equals the81
mode II fracture toughness of the material:82
R (∆a) =W
Eβ τ 2u φ
2
(
α0 +∆a
β W, ρ, β
)
(8)
where ∆a is the crack increment and α0 = a0/w, where a0 is the initial crack83
length. The R-curve is a material parameter that does not depend on the84
shape or dimension of the specimen. In particular it does not depend on the85
parameter β. Therefore, taking the derivative of R with respect to β, it follows86
that ∂βR = 0. Deriving equation (8) with respect to β and imposing ∂βR = 087
yields:88
4
∂βR =W
E∂β(
β τ 2 φ2)
= 0. (9)
If τ = τ (β) (for a given W ) is known and under the hypothesis that α0 is89
a constant, equation (9) can be solved for β = β (∆a). Substituting β (∆a)90
in equation (8) yields the R-curve for 0 < β < 1 or, in other words, for91
0 < w < W .92
It should be noted that the procedure described enables the determination93
of part of the R-curve (in the range 0 < β < 1) but not the entire R-curve.94
This is due to the fact that it is not possible to extrapolate the region of95
the R-curve when w → +∞ because 0 < w < W . To obtain the entire R-96
curve the size effect law must be obtained with a characteristic length that97
ranges in the interval [0,+∞). In the impossibility of scaling the specimens,98
the size effect law can be obtained by mapping the part of the R-curve already99
defined. Consider a specimen with a constant β, for example β = 1 as shown100
in Figure 2.101
[Fig. 2 about here.]102
The crack driving force for this specimen reads:103
GII =1
Ew τ 2 ψ2 (10)
where ψ = φ|β=1. At the peak load the following system of equations is satis-104
fied:105
GII = R∂∆aGII ≥ ∂∆aR
(11)
where ∂∆aGII = ∂∆aR represents the condition for unstable crack propagation.106
Equation (11) represents the tangency condition between the crack driving107
force and the R-curve, as shown in Figure 3. Therefore, for a given w⋆, the108
value of τ ⋆ tangent to the R-curve can be found. The strategy used here is quite109
simple: for a given characteristic dimension w⋆ the stress τ for which there is110
just an intersection point (⋆ in Figure 3) is the stress τ ⋆. This is illustrated111
in Figure 3 in which, for a given point of the R-curve (indicated with ⋆), only112
two crack-driving force curves are defined (assuming a0 constant). The known113
portion of the R-curve (in red in Figure 3) extends between two points that114
are tangent to the driving forces curve identified with βmin and βmax.115
5
βmin and βmax are the limiting values of β. Since the numerical model described116
in the following section is defined for β ∈ [0.2, 1.0], βmin and βmax are taken117
as 0.2 and 1.0, respectively.118
[Fig. 3 about here.]119
By repeating this procedure several times, the calculation of several pairs120
(w⋆, τ ⋆) are obtained. By fitting these points it is possible to define the size121
effect law (see Table 1 for suggested expressions of the size effect laws), τ =122
τ (w), that is necessary to calculate the entire R-curve, R (∆a).123
[Table 1 about here.]124
To do that it should be noted that the R-curve is a material parameter and it125
does not depend on w. Therefore, ∂wR = 0. Substituting (10) in the first (11)126
and deriving with respect to w yields:127
∂wR =1
E∂w(
w τ 2u ψ2)
= 0. (12)
Knowing the size effect law, τ = τ (w), under the hypothesis that similar128
specimens are considered (α0 is constant) equation (12) can be solved for129
w = w (∆a). Substituting w = w (∆a) in the first (11) yields the entire R-130
curve. In this case the steady state value can be obtained simply taking the131
limit, for w → +∞, of R in the first of (11):132
Rss = limw→∞
R (∆a) =1
Ew τ 2 ψ2
0 (13)
where ψ0 = ψ (α = α0).133
2.2 Elasto-plastic materials134
The method proposed in the previous section is rigorous for an elastic body135
and it may be used when the plastic region is negligible when compared to the136
characteristic crack length. This is not the case when dealing with cross ply137
laminates loaded in shear where the material behaviour is non–linear. There-138
fore, the R-curve obtained using the method proposed in the previous section139
may substantially differ from the real one. However, this discrepancy should140
affect only the rising part of the R-curve whilst it should not influence its141
plateau. In fact, the steady–state value of the R-curve, Rss, is obtained for an142
infinitely large specimen (see equation (13)) for which LEFM is valid. Sup-143
pose, for example, that the material exhibits a Ramberg–Osgood relationship144
6
between stress and strain in shear:145
γ =τ
G+m
τ0G
(
τ
τ0
)n
(14)
where G, τ0, γ, m, and n, are the shear modulus, the yield stress, the shear146
strain, and the two constants of the Ramberg–Osgood equation, respectively.147
Under linear elastic conditions, the J-integral equals the energy release rate:148
Je =1
Ew τ 2 ψ2 (15)
For a fully plastic cracked body the J-integral reads [17]:149
Jp = mγ0 τ0w g (α) h (α, n)(
τ
τ0
)n+1
(16)
where γ0 is the yield strain of the material, and g and h are two correction150
factors. For an elasto-plastic cracked body the J-integral is normally computed151
superposing the elastic and the fully plastic solutions [18–20]:152
J =1
Ew τ 2 ψ2 (α + αcorr) +mγ0 τ0w g (α) h (α)
(
τ
τ0
)n+1
(17)
where αcorr is the correction for strain hardening. At the peak stress, τu, the153
elasto-plastic J-integral equals the material fracture toughness:154
R =1
Ew τ 2u ψ
2 (α + αcorr) +mγ0 τ0w g (α) h (α)(
τuτ0
)n+1
(18)
It is straightforward to calculate the steady state value of Rss as the limit of155
(18) for w → +∞. Taking into account that the correction factor αcorr = rp/w,156
with rp = rp (n, τ0) being Irwin’s correction, it follows that limw→+∞
αcorr = 0.157
Also, the limit of the second term in (18), Jp, is equal to zero. Without loss158
of generality, suppose that the size effect law can be fitted using a linear159
regression II fit (see Table 1):160
1
w τ 2u= A
1
w+ C (19)
The limit of Jp, when w → +∞, reads:161
7
limw→+∞
Jp = limw→+∞
mγ0 τ−n0 g (α) h (α, n)
w(
A+ Cw)
n+1
2
= 0 (20)
The previous limit is equal to zero because n > 1. Therefore the steady state162
value of the R-curve, Rss, computed as the limit, for w → +∞, of the elasto-163
plastic J-integral is exactly that computed in equation (13) using LEFM.164
3 Numerical Model165
The dimensionless functions φ and ψ are calculated for the problem under166
analysis, using the Finite Element Method (FEM). For this purpose a para-167
metric Finite Element model was created using Python [21] together with the168
Abaqus 6.8-3 Finite Element code [22].169
The characteristic distance w is taken as constant and equal to the unity,170
while the variables are: the shape parameters or, in other words, the crack171
length 0 < α < 1 and the notch length 0.2 < β < 1; and the dimensionless172
parameter ρ that takes into account the effect of the orthotropy of the material173
(0 ≤ ρ ≤ 20). Figure 4(a) shows the mesh of the finite element model while174
figures 4(b)–4(c) show the deformed shape overall the specimen and, in detail,175
in the crack.176
[Fig. 4 about here.]177
The finite element used is the 4-node quadratic, reduced integration element,178
CPS4R. The Virtual Crack Closure Technique (VCCT) [23] is used to compute179
the energy release rates, GI and GII . For this purpose, a Python script was180
written to be used into Abaqus. Both energy release rates are calculated and181
compared to ensure that the crack propagation occurs in mode II. In addition,182
the total energy release rate computed was compared with that obtained from183
the Abaqus built-in method to calculate the J-Integral. This redundant mea-184
sure was used to validate the Python script. Displacements are applied on the185
model and frictionless contact is assumed. The applied load P is calculated186
summing the forces at the reaction nodes.187
Using the results obtained in the FE analysis the correction factor φ is ap-188
proximated by the following polynomial:189
φ =α
1− α
∑
i
∑
j
∑
k
Φijk αi−1 ρj−1 βk−1 (21)
8
where Φijk is the element of the matrix Φ with indexes i, j, and k. The matrix190
Φ is shown in Table 2 .191
[Table 2 about here.]192
The fitting surface φ is shown, together with the numerical points, in Figure 5.193
[Fig. 5 about here.]194
The maximum error of equation (21) in fitting the numerical points is 5%,195
with an average error of 2%. Function ψ can trivially obtained posing β = 1196
in equation (21). However, in order to reduce the error a new fit was calculated.197
The correction factor ψ is computed using the following polynomial:198
ψ =α
1− α
∑
i
∑
j
Ψij αi−1 ρj−1 (22)
where Ψij is the element, with the indexes i and j of the matrix Ψ defined as:199
Ψ =
−0.03644 0.22363 −0.00437 2.21749E−5
5.23616 1.44575 −0.16601 0.00449
−7.39060 −6.89756 0.63003 −0.01629
1.55840 9.24044 −0.79486 0.02025
0.84958 −4.05275 0.33844 −0.00855
(23)
The average error obtained using the expression of equation (22) is 1% while200
the maximum error is less than 2%. Figure 6 shows the comparison between the201
fitting surface ψ and the numerical points obtained using the aforementioned202
finite element model.203
[Fig. 6 about here.]204
4 Experiments205
IM7/8552 16-ply cross-ply ([90/0]8s) laminate with a nominal thickness of 4206
mm is used here. The nominal ply thickness is 0.125 mm, and the details207
of the manufacturing process given in [11]. The pre-crack was machined in a208
CNC machine equipped with a 1 mm drill bit. The Young’s modulus (along209
the orthotropic axes of the material) and the dimensionless parameter ρ of the210
cross-ply are E = 90649MPa and ρ = 8.5, respectively.211
9
The tests were carried out on a universal testing machine with a displace-212
ment rate of 2mm/min. The load was measured with a load cell of 100kN.213
A Iosipescu shear fixture was used to transfer the vertical movement of the214
cross-head of the testing machine in predominant shear at the specimen cen-215
tral section [24]. In particular, this set-up was used to apply mode II loading216
to the modified Iosipescu specimen. A torque wrench was used to tighten the217
sliding wedges of the fixture to a torque of 1Nm. Specimens were centered218
within the fixed and movable parts of the fixture.219
The fracture tests were coupled with digital image correlation (DIC). The220
photo-mechanical set-up is shown in Figure 7. In this work, the ARAMIS DIC-221
2D system by GOM was used [25,26]. A 8-bit Charged Coupled Device (CCD)222
Baumer Optronic FWX20 camera coupled with an Opto-Engineering telecen-223
tric lens TC 23 36 was selected (Table 3). With this type of lens, the mag-224
nification of the optical system can be kept constant over a defined working-225
distance range. The measurement are therefore less sensitive to any parasitic226
out-of-plane movement of the specimen. The gauge section at the specimen227
centre was painted using an airbrush in order to guarantee the refired speckled228
surface for DIC measurements. The illumination and shutter time were then229
adjusted in order to enhance the contrast of the target image. Based on rigid-230
body translation tests carried out systematically before the fracture tests [26],231
an estimation of the displacement and strain resolution was obtained in the232
range of 2×10−2 pixel (0.36 µm) and 0.02-0.04%, respectively.233
[Table 3 about here.]234
[Fig. 7 about here.]235
Six different geometries were tested, indicated with labels from A to F, cor-236
responding to a variation of β from 0.5 to 1.0. Table 4 shows the relevant ge-237
ometrical parameters together with the experimental results obtained. Three238
specimens were tested for each geometry. The dimensionless parameter α0 was239
taken as α0 = 0.5.240
[Table 4 about here.]241
Figure 8 shows the specimen after testing. The specimens failed by mode II242
crack propagation.243
[Fig. 8 about here.]244
The digital image correlation is used to verify the validity of the tests per-245
formed. Figure 9 shows the contour plot of the shear strain, γ12. Any misalign-246
ment in the load condition are checked in this way to ensure a predominant247
mode II crack propagation.248
10
[Fig. 9 about here.]249
Fitting the experimental results shown in Table 4, the law τu (β) is obtained.250
It should be noted that τu (β) is not, strictly speaking, a size effect law because251
it is not obtained scaling all the specimen’s dimension. This law is valid for252
the specimen shown in Figure 1 (with the width W=20 mm). Nevertheless,253
as we showed in the previous section, this specific size effect law can be used254
to obtain part of the R-curve. Due to the fact that τu (β) is not a size effect255
law, no particular caution should be taken in choosing the fitting function to256
use. However, it should be ensured that the strength decreases monotonically257
with β. In other words, it is not necessary to use the fitting formulas suggested258
in Table 1 because some characteristic of those formula are not required (for259
example, to provide a finite value of the strength when the characteristic size260
tends to infinity). The best fitting of the experimental data reported in Table261
4 was obtained with the linear regression II fit:262
1
βτ 2u= Aβ
1
β+ Cβ (24)
The best fitting (R2=0.91) is obtained for Aβ = 6.666 × 10−5MPa−2 and263
Cβ = 4.084 × 10−5MPa−2. The experimental results and the fitted curve are264
shown in Figure 10.265
[Fig. 10 about here.]266
Having obtained the law τu (β), part of the R-curve can be calculated solving267
the systems of equations (8)–(9) as shown in Figure 11.268
[Fig. 11 about here.]269
To obtain the entire R-curve the actual size effect law should be estimated as270
explained in the previous section (see Figure 3).271
A very simple algorithm was written in Matlab for this purpose allowing the272
definition of the points shown in Figure 12. The numerical points obtained273
were fitted again (together with the experimental point for β = 1.0 because274
this point belongs to this size effect law), using the fitting formulas reported275
in Table 4. The best fitting (R2=0.99) was obtained with the linear regression276
II:277
1
wτ 2u= A
1
w+ C (25)
where A = 6.964× 10−5MPa−2 and C = 3.46× 10−6 MPa−2mm−1. The corre-278
11
sponding points and the fitted curve are shown in Figure 12.279
[Fig. 12 about here.]280
Using the size-effect law obtained is possible to extrapolate the entire R-curve281
solving the equations (12) and (11).282
[Fig. 13 about here.]283
The steady state value of the R-curve and the length of fracture process zone284
are calculated as [15]:285
Rss =ψ20
E
1
C= 17.92 kJ/m2
lfpz =ψ0
2 ψ0
A
C= 4.95 mm
(26)
where ψ0 = ψ|α=α0and ψ0 = (∂ψ/∂α)|α=α0
. As previously mentioned, the286
fracture toughness of the 0◦ ply is obtained as twice the fracture toughness of287
the cross ply laminate, R0 (∆a) = 2R (∆a) . Therefore the steady state value288
of the ply fracture toughness is R0ss = 34.4 kJ/m2.289
It is worth to find a simple analytical expression of the R-curve to use in290
strength prediction models. A formula generally used is [11,12,15]:291
R = Rss (1− (1−∆a/lfpz)κ) if 0 ≤ ∆a ≤ lfpz < 0
R = Rss if ∆a ≥ lfpz(27)
For the material system used here the best fit (R2=0.997) is κ = 2.36.292
5 Conclusion293
The main conclusions of this work can be summarized as follows:294
• A new cracked Iosipescu specimens was proposed to measure the intralami-295
nar fracture toughness and R-curve in mode II of fibre reinforced composites.296
• In the impossibility of scaling the specimen a different formulation of the297
classical size effect method was proposed. The new formulation enables the298
measurement of the part of the R-curve that can be calculated once that299
τu = τu (β) is known. Differently from the classical size effect method β is300
12
not a characteristic size but a dimensionless parameter that depends on the301
shape of the specimen.302
• The entire R-curve can be calculated using the classical size effect method303
after determining the size effect law τu = τu (w). This is calculated mapping304
the known portion of the R-curve.305
• The ply steady state value of the fracture toughness for the material system306
investigated was found to be R0ss = 34.4 kJ/m2 and the corresponding307
length of the fracture process zone is 4.95mm.308
The drawbacks of the proposed methods are (i) that the rising part of the309
R–curve may substantially differs from the real one for cross ply laminates310
because the plastic behaviour of the material is ignored, and (ii) the maximum311
crack propagation obtained is limited by the gauge section of the specimen,312
therefore, for material that exhibit very large length of fracture process zone,313
the size effect obtained using this methodology may not be reliable. In this314
case the specimen should be scaled and a different test method should be315
proposed.316
Acknowledgements317
The first and second author would like to acknowledge the support of the318
Portuguese Foundation for Science and Technology under the grants FCT-319
DFRH-SFRH-BPD-78104-2011 and the Ciencia2008 program, respectively.320
References321
[1] E. Abisset, F. Daghia, and P. Ladeveze. On the validation of a damage322
mesomodel for laminated composites by means of open-hole tensile tests323
on quasi-isotropic laminates. Composites Part A: Applied Science and324
Manufacturing, 42(10):1515 – 1524, 2011.325
[2] C. Schuecker and H.E. Pettermann. A continuum damage model for fiber326
reinforced laminates based on ply failure mechanisms. Composite Structures,327
76(12):162 – 173, 2006.328
[3] P. Maimı, P.P. Camanho, J.A. Mayugo, and C.G. Davila. A continuum damage329
model for composite laminates: Part I - constitutive model. Mechanics of330
Materials, 39(10):897 – 908, 2007.331
[4] P.P. Camanho, M.A. Bessa, G. Catalanotti, M. Vogler, and R. Rolfes. Modeling332
the inelastic deformation and fracture of polymer composites part ii: Smeared333
crack model. Mechanics of Materials, 59(0):36 – 49, 2013.334
13
[5] P.P. Camanho, G.H. Ercin, G. Catalanotti, S. Mahdi, and P. Linde. A335
finite fracture mechanics model for the prediction of the open-hole strength of336
composite laminates. Composites Part A: Applied Science and Manufacturing,337
43(8):1219 – 1225, 2012.338
[6] G.H. Ercin, P.P. Camanho, J. Xavier, G. Catalanotti, S. Mahdi, and P. Linde.339
Size effects on the tensile and compressive failure of notched composite340
laminates. Composite Structures, 96(0):736 – 744, 2013.341
[7] E. Martin, D. Leguillon, and N. Carrre. A coupled strength and toughness342
criterion for the prediction of the open hole tensile strength of a composite343
plate. International Journal of Solids and Structures, 49(26):3915 – 3922, 2012.344
[8] G. Catalanotti and P.P. Camanho. A semi-analytical method to predict345
net-tension failure of mechanically fastened joints in composite laminates.346
Composites Science and Technology, 76(0):69 – 76, 2013.347
[9] S.T. Pinho, P. Robinson, and L. Iannucci. Fracture toughness of the tensile and348
compressive fibre failure modes in laminated composites. Composites Science349
and Technology, 66:2069–2079, 2006.350
[10] G. Catalanotti, P.P. Camanho, J. Xavier, C.G. Davila, and A.T. Marques.351
Measurement of resistance curves in the longitudinal failure of composites using352
digital image correlation. Composites Science and Technology, 70(13):1986 –353
1993, 2010.354
[11] G. Catalanotti, J. Xavier, and P.P. Camanho. Measurement of the compressive355
crack resistance curve of composites using the size effect law. Composites Part356
A: Applied Science and Manufacturing, 56(0):300 – 307, 2014.357
[12] G. Catalanotti, A. Arteiro, M. Hayati, and P.P. Camanho. Determination of358
the mode i crack resistance curve of polymer composites using the size-effect359
law. Engineering Fracture Mechanics, 118(0):49 – 65, 2014.360
[13] Fabrice Pierron and Alain Vautrin. Measurement of the in-plane shear strengths361
of unidirectional composites with the iosipescu test. Composites Science and362
Technology, 57(12):1653 – 1660, 1998.363
[14] ASTM D5379–12 Standard Test Method for Shear Properties of Composite364
Materials by the V-Notched Beam Method, 2012.365
[15] Zdenek P. Bazant and Jaime Planas. Fracture and Size Effect in Concrete and366
Other Quasibrittle Materials. CRC Press LLC, 1997.367
[16] Z. Suo, G. Bao, B. Fan, and T.C. Wang. Orthotropy rescaling and implications368
for fracture in composites. Int. J. Solids and Structures, 28:235–248, 1990.369
[17] A.A. Il’yushin. The thoery of small elastic-plastic deformations. Prikadnaia370
Matemetika i Mekhanika, PMM, 10:347–356, 1946.371
[18] Melvin F. Kanninen and Carl H. Popelar. Advanced Fracture Mechanics,372
volume 15 of Oxford Engineering Science Series. Oxford Science Publications,373
1985.374
14
[19] C.F. Shih. J-integral estimates for strain hardening materials in antiplane shear375
using fully plastic solution. Mechanics of crack growth, ASTM STP 950:3–26,376
1976.377
[20] C.F. Shih and J.W. Hutchinson. Fully plastic solutions and large scale yielding378
estimates for plane stress crack problems. Journal of Engineering Materials and379
Technology, 98:289–295, 1976.380
[21] M. Lutz. Learning Python. O’Reilly Media, Inc., 3rd edition, 2008.381
[22] Dassault Systemes. Abaqus Version 6.8–3 Documentation, 2008.382
[23] Ronald Krueger. The virtual crack closure technique: History, approach and383
applications. Technical Report NASA/CR-2002-211628 ICASE Report No.384
2002-10, ICASE, Hampton, Virginia, April 2002.385
[24] J.C. Xavier, N.M. Garrido, M. Oliveira, J.L. Morais, P.P. Camanho, and386
F. Pierron. A comparison between the Iosipescu and off-axis shear test methods387
for the characterization of pinus pinaster Ait. Composites Part A: Applied388
Science and Manufacturing, 35(7-8):827–840, 2004.389
[25] GOM (www.gom.com). ARAMIS, User Manual - Software - v6.0.2-6, 2009.390
[26] J. Xavier, A. de Jesus, J. Morais, and J. Pinto. Stereovision measurements on391
evaluating the modulus of elasticity of wood by compression tests parallel to392
the grain. Construction and Building Materials, 26:207–215, 2012.393
15
List of Figures394
1 Specimen’s geometry (dimensions in mm). 17395
2 Geometry of the virtual specimen. 18396
3 R-curve and mapping procedure. 19397
4 Finite element model of the specimen (α = 0.5, β = 0.5, and398
ρ = 20). 20399
5 φ for different values of α, ρ, and β: fitting surface and400
numerical points. 21401
6 ψ for different values of α and ρ: fitting surface and numerical402
points. 22403
7 Photo–mechanical set-up. 23404
8 Specimens after testing. 24405
9 Field of the shear strains γ12 obtained using Digital Image406
Correlation. 25407
10 τu (β) law, fitting and experiments. 26408
11 Portion of the R-curve obtain solving (8) and (9). 27409
12 Size effect law. 28410
13 R-curve of the investigated laminate. 29411
16
(a) 0 < β < 1
(b) β = 1
Fig. 1. Specimen’s geometry (dimensions in mm).
17
Fig. 2. Geometry of the virtual specimen.
18
Fig. 3. R-curve and mapping procedure.
19
Z
Y
X
(a) mesh
(b) deformed shape and τ12 contour plot
crack tipscracks
(c) detail of the deformed shape
Fig. 4. Finite element model of the specimen (α = 0.5, β = 0.5, and ρ = 20).
20
00.1
0.20.3
0.40.5
0.60.7
0.80.9
0.20.3
0.40.5
0.60.7
0.80.9
1−1
0
1
2
3
4
α [–]β [–]
φ[–
]
ρ = 0
ρ = 20
Fig. 5. φ for different values of α, ρ, and β: fitting surface and numerical points.
21
00.1
0.20.3
0.40.5
0.60.7
0.80.9
0
5
10
15
200
0.5
1
1.5
2
2.5
3
3.5
4
α [–]ρ [–]
ψ[–
]
Fig. 6. ψ for different values of α and ρ: fitting surface and numerical points.
22
Fig. 7. Photo–mechanical set-up.
23
Fig. 8. Specimens after testing.
24
Fig. 9. Field of the shear strains γ12 obtained using Digital Image Correlation.
25
1 1.2 1.4 1.6 1.8 21
1.1
1.2
1.3
1.4
1.5
1.6
1.7
1.8
1.9x 10
−4
1/(βτ
2 u)
[MP
a−
2]
1/β [–]
experimentsfitted curve
Fig. 10. τu (β) law, fitting and experiments.
26
0 0.5 1 1.5 20
2
4
6
8
10
12
∆a [mm]
R[k
J/m
2]
crack driving force curvesR−curve
Fig. 11. Portion of the R-curve obtain solving (8) and (9).
27
0.1 0.15 0.2 0.25 0.3 0.351
1.2
1.4
1.6
1.8
2
2.2
2.4
2.6
2.8x 10
−5
1/w [mm−1]
1/(wτ u
)[M
Pa−
2m
m−
1]
mappingexperimentsfitted curve
Fig. 12. Size effect law.
28
0 2 4 6 8 100
5
10
15
20
25
30
∆a [mm]
R[k
J/m
2]
crack driving force curvesR−curve (experiments)R−curve (mapping)
Rss=17.2kJ/m2
lfpz = 4.95mm
Fig. 13. R-curve of the investigated laminate.
29
List of Tables412
1 Size effect law fits [15]. 31413
2 Elements of Φ matrix. 32414
3 Optical system components and measurement parameters. 33415
4 Experimental results. 34416
30
Table 1Size effect law fits [15].
Regressions fit Formula Fitting parameters Rss lfpz
Bilogarithmic ln σu = lnM√N + w
M , Nφ20
EM2 φ0
2 φ0
N
Linear regression I1
σ2u
= Aw + C A, Cφ20
E
1
A
φ0
2 φ0
C
A
Linear regression II1
wσ2u
= A1
w+ C A, C
φ20
E
1
C
φ0
2 φ0
A
C
31
Table 2Elements of Φ matrix.
k
(i, j) 1 2 3 4 5
(1,1) 1.794 -1.308 0.1716 -0.01097 0.0002523
(1,2) -10.43 13.21 -1.36 0.0792 -0.001765
(1,3) 25.35 -32.6 2.888 -0.1572 0.003473
(1,4) -16.95 38.9 -3.18 0.1614 -0.003451
(1,5) 0.1882 -17.92 1.474 -0.07248 0.001496
(2,1) -0.3254 6.094 -0.6752 0.04665 -0.001181
(2,2) 34.16 -36.52 1.377 -0.08447 0.002929
(2,3) -38.05 64.97 3.783 -0.2963 0.003905
(2,4) -5.217 -85.65 -5.751 0.5185 -0.009382
(2,5) 13.79 53.24 0.8606 -0.1592 0.003198
(3,1) -2.122 -11.88 1.238 -0.0982 0.002733
(3,2) -55.28 34.68 3.842 -0.1465 -0.001238
(3,3) -5.196 -2.537 -30.47 1.794 -0.02811
(3,4) 63.33 34.79 38.99 -2.568 0.04627
(3,5) -4.591 -64.79 -12.11 0.93 -0.01781
(4,1) -0.1686 12.14 -1.385 0.1204 -0.003441
(4,2) 60.16 -18.51 -5.287 0.1265 0.003617
(4,3) -3.963 -45.88 35.77 -1.841 0.024
(4,4) -5.052 14.51 -45.77 2.713 -0.04409
(4,5) -54.11 50.67 14.8 -1.009 0.01765
(5,1) 1.106 -5.201 0.6829 -0.06038 0.001703
(5,2) -29.87 8.16 1.231 0.04213 -0.003985
(5,3) 25.31 13.52 -11.51 0.4595 -0.00217
(5,4) -40.86 0.4896 15.21 -0.782 0.009515
(5,5) 47.24 -22.61 -4.832 0.2949 -0.004118
32
Table 3Optical system components and measurement parameters.
Camera-lens optical system
CCD camera Baumer Optronic FWX20
8 bit, 1624×1236 pixels
lens TC 23 36 Telecentric lens
Magnification: 0.243 ± 3 %
Field Of View: 29.31 × 22.1 mm
Working Distance: 103.5 ± 3 mm
Working F-number: 8
Image recording
Acquisition frequency 1 Hz
Exposure time 0.7 ms
Project parameter – Subset
Subset size 15×15 pixels2 (0.270×0.270 mm2)
Subset step 13×13 pixels2 (0.234×0.234 mm2)
Project parameter – Strain
Strain length 5×5 subsets2 (1.17×1.17 mm2)
Resolution
Displacement 2×10−2 pixel (0.36 µm)
Strain 0.02-0.04%
33
Table 4Experimental results.
specimen β [–] w [mm] τ [MPa] SD [MPa] IC 95% [MPa]
A 0.5 5 107.0 3.0 3.3
B 0.6 6 104.3 4.9 5.5
C 0.7 7 103.3 2.3 2.6
D 0.8 8 102.3 1.1 1.3
E 0.9 9 98.0 1.0 1.1
F 1.0 10 95.0 2.6 2.9
34