MC-FastKickHardening Accelerator of a new GenerationDipl.-Ing. Maria Luisa Pérez Vergara
MC FOR CONCRETE INDUSTRY
About Product
111
• For concrete , reinforced and pre-stressed (except Germany) concrete
• Free of corrosion promoting substances
MC-FastKick
About Product
MC-FastKick 111
- Faster strength development of concrete and mortar
- For reinforced and prestressed concrete (except Germany)
- Plasticizing / water reducing effect
- fullfils the requirements of superplasticizer according to EN 934-2, T3.1/3.2
Reaction mechanism
- MC-FastKick positively influences the crystal growth of C-S-H-Phases in concrete.
- Fast development of crystalline structures on top of initial amorphous(non-crystalline) areas.
Natural crystal growth, high packing density, „smooth“ low surface area
Controlled crystal growth, „rough“ high surface area
Reaction mechanism
- Significantly higher early strength development without negativ effects toother concrete properties.
Natural crystal growth, high packing density, „smooth“ low surface area
Controlled crystal growth, „rough“ high surface area
Advantages of MC-FastKick
High early strength development
- Reduced cycle times
- Increased productivity
- Savings of investments in moulds when double mould occupancy isachieved
- On-schedule completion of construction projects
Advantages of MC-FastKick
Compensation of low temperatures
- Construction site progress ensured
- Reduction of heating costs and additional winter measures
- Preservation and possible increase of final strength
- Reduction of demoulding times
- Reduced waiting times for finishing trowelled concrete
- Possible reduction of dark discoloration on surfaces
Advantages of MC-FastKick
Plastification
- Significant increase of slump by up to two classes
- Reduction of superplisticizer dosage
- Water reduction (respectively w/c – reduction)
- Savings due to possible binder reduction
Co
mp
ress
ive
stre
ng
th[N
/mm
2 ]
PF 3130 PF 3130+1% MC-FastKick
PF 3130+2% MC-FastKick
PF 3130+3% MC-FastKick
PF 3130+4% MC-FastKick
8h
24h
Early strength development with CEM I 52,5 R
Early strength development with CEM I 52,5 R
Fields of Application
- Prefabrication of concrete
- RMC
- Concrete goods (semi-dry concrete)
increasedproductivity
admixture reduction
water reduction
cement reduction
Concrete
accelerationplastification
MC-FastKickheat reduction
Fields of Application
Increased productivity, demoulding after 6-7 hours
Fields of Application
up to 3 production cycles in 24h
Fields of Application
Increased productivity
Fields of Application
Reduction of dark discoloration on surfaces
Fields of Application
Shorter demoulding times and assured construction progress at lowtemperatures.
Fields of Application
Shorter waiting times for finishing smoothed concretes
Summary
Concrete
PlastificationAcceleration
price benefit
same productivityat cold temperature
better accelerationhigher 28 d strength
reduced energy costs
higher efficiencyprice benefit
reduction of heating
reduction of cement
MC-FastKick
Stay up to dateon MC!
Dianummer 1Dianummer 2MC-FastKick �Hardening Accelerator of a new Generation�Dipl.-Ing. Maria Luisa Pérez Vergara�About Product About Product Reaction mechanism Reaction mechanism Advantages of MC-FastKick Advantages of MC-FastKick Advantages of MC-FastKick Early strength development with CEM I 52,5 R Early strength development with CEM I 52,5 R Fields of ApplicationDianummer 14 Fields of Application Fields of Application Fields of Application Fields of Application Fields of Application Fields of Application SummaryDianummer 22