CEMENT CONTENT = 310 kgs / m3
FREE WATER = 140 kgs / m3
FREE W/C RATIO = 0.45
DETERMINATION OF CA & FA CONTENT
310 1 fa 1
FA - 1000 = 140.00 + + X = 744 Kgs
3.15 0.38 2.57 1000
310 1 Ca 1
CA - 1000 = 140.00 + + X = 1247 Kgs
3.15 0.62 2.64 1000
TOTAL DRY CA & FA = 1990 kgs
CEMENT = 310 kgs
CA 20 mm ( SSD ) = 623 kgs
CA 10 mm ( SSD ) = 623 kgs
RIVER SAND ( SSD ) = 521 kgs
CRUSHER SAND ( SSD ) = 223 kgs
WATER = 140 kgs
DENSITY = 2440 kgs
Dy.Quality Head
CONCRETE INDIA
GRADE OF CONCRETE M20
7/25/2019 M20_OPC_310.pdf
2/3
PROJECT : M/s Navayuga Engineering Company Ltd
LOCATION : Bengaluru DATE : 28-01-2016
GRADE OF CONCRETE : M20
TARGET MEAN STRENGTH : 26.60 N/mm2
MAXIMUM SIZE OF AGGREGATE, mm . : 20
SLUMP OF CONCRETE, mm ( AT SITE ) : 120. +/- 20 mm
BASIC DATA
BRAND OF CEMENT : BHARATHI/ULTRA TECH
TYPE OF CEMENT : OPC (53 GRADE)
SPECIFIC GRAVITY OF CEMENT : 3.15
SOURCE OF FINE AGGREGATE ( MANUFACTURED SAND ) :
SOURCE OF FINE AGGREGATE ( CRUSHER SAND ) :
AVE. SPECIFIC GRAVITY OF FINE AGGREGATE : 2.57
WATER ABSORPTION OF FINE AGG ( MANUFACTURED SAND ) % : 2.5
WATER ABSORPTION OF FINE AGG ( CRUSHER SAND ) % : 3.5
FA IN TOTAL AGGREGATE ( MANUFACTURED SAND & CRUSHER SAND ) % : 38.00
SOURCE OF COARSE AGGREGATE :
TYPE OF COARSE AGGREGATE : CRUSHED ROCK
AVE. SPECIFIC GRAVITY OF COARSE AGGREGATE : 2.64
AVE. WATER ABSORPTION OF COARSE AGGREGATE % : 0.5
COARSE AGGREGATE IN TOTAL AGG (20mm & 10mm) % : 62.00
SUPPLIER NAME OF CHEMICAL ADMIXTURE : ECMAS
TYPE OF CHEMICAL ADMIXTURE : SUPERPLASTICIZER
PRODUCT NAME OF CHEMICAL ADMIXTURE : ECMAS HP 890
DOSAGE OF ADMIXTURE - (% BY Wt OF CEMENT) % : 0.55
RECOMMENDED REDOSAGE AT SITE MAX. (% BY Wt OF CEMENT) % : 0.2
CEMENT : 310 Kgs
CA 20 mm ( SSD ) : 623 Kgs
CA 10 mm ( SSD ) : 623 Kgs
M.SAND ( SSD ) : 521 Kgs
CRUSHER SAND ( SSD ) : 223 Kgs
WATER : 140 Kgs
ADMIXTURE : 1.705 Kgs
TOTAL DENSITY OF FRESH CONCRETE : 2442 Kgs
MIX PROPORTION BY WEIGHT
CEMENT F.A C.A
1 : 2.4 : 4.02
Note :-
1 FOR WEIGH BATCHING CORRECTION FOR MOISTURE IN AGGREGATES SHOULD BE DONE DAILY
HOSKOTE
MATERIAL REQUIRED PER CUM OF CONCRETE
Dy.Quality Head
CONCRETE INDIA
CHIKKABALAPUR
CHIKKABALAPUR
7/25/2019 M20_OPC_310.pdf
3/3
The Concrete mix design is a process of selecting suitable ingredient for concrete and determining
their proportions i.e. concrete having a certain minimum compressive strength , workability and
durability. The mix design has been carried out as per stipulation of Indian Standard IS : 10262 - 1982
( Reaff 1989 & 1999 ). Keeping in view the recommended standard deviation and target mean strength .
In this method of mix design,the water content and proportion of fine aggregate corresponding to a
maximum size of aggregate are first determined for referred values of workability water cement ratio
and grading of fine aggregate. The batch weight of materials per unit volume of concrete is finally ,
calculated by the absolute volume method. The mix proportion have suitably modified successively
based on trial mixes to arrive at an optimum mix proportion . It satisfies the requirement of desiredworkability and 28 days strength of concrete .
QUANTITY OF MATERIAL, M3 : 1.000
BY WEIGHT
CEMENT : 310 Kgs
CA 20 mm ( DRY ) : 620 Kgs
CA 10 mm ( DRY ) : 620 Kgs
M.SAND ( DRY ) : 515 Kgs
CRUSHER SAND ( DRY ) : 218 Kgs
WATER : 157 Kgs
ADMIXTURE : 1.705 Kgs
Note
1. For Weigh Batching correction for moisture in aggregate should be done daily.
2. Mix design calculation are based on IS : 10262 & IS : 456
3. Concrete Specimens cured in water & tested as per IS : 516
4. Compressive Strength conducted on standard specimen of 150mm cubes .
5. Proportions of Aggregate may vary, as per grading available at time of pour .
References
1. IS : 10262 - 1982 ( Reaffirmed 1989 - 1999 )
2. IS : 456 - 2000
3. SP : 23
Dy.Quality Head
CONCRETE INDIA
Report on Concrete Mix Design ( M20 )
BATCH SHEET