HOMOPOLYMER Film (Extrusion) Fiber Extrusion, … Feb 10 Jampilen ADXP680 TYPICAL PROPERTIES VALUE UNIT METHOD Physical Melt Flow Rate (230 oC, 2.16kg) 3.5 g/10min ASTM D1238 Density

New MFR New MFR New MFR New MFR New MFR New MFR New MFR New MFRH1850 1.2 HP522H 2 ADXP699 3.5 HP562R 25 HP502P 16 HP502H 1.8 HP502N 12 HP432C 0.3

HP500H 1.8 HP520H 2 HP420M 8 HP561R 25 HP554P 18 HP550J 3.2 HP554N 12 HP502C 0.3HP501H 2.1 HP528H 2 HP510M 9 HP462R 25 HP562R 25 HP552J 3.2 HP557N 12 H2150 0.3HP532J 3 HP593H 2 HP515M 9 HP561S 33 HP502R 25 HP456J 3.4 HP552N 13 H2450 0.3HP500J 3.2 HP422H 2.1 HP565S 38 HP552R 25 HP510L 6 HP502P 16 HP501D 0.7HP500L 6 HP421H 2.1 HP564S 40 HP561R 25 HP554P 18 HP502H 1.8HP501M 7.5 HP529J 2.6 HP562S 35 HP456H 1.8HP500M 9 HP525J 3 HP640H 2HP500N 12 HP524J 3 HP593H 2HP500P 17 HP528J 3 HP501H 2.1HP371P 18 HP522J 3 HP540J 3.2HA840R 20 HP527J 3 HA840K 3.5HP548R 23 HP425J 3.1 ADXP680 3.5HP400R 25 HP421J 3.1 ADXP699 3.5HP483R 27 ADXP699 3.5 HP540K 3.8HP648S 35 HP420M 8HA701T 45HP648T 53

Staple Fiber

HOMOPOLYMER

Injection Molding

Film (Extrusion) Fiber Extrusion,Thermoforming &

Blow moldingBOPP Cast andBlown

NonwovenSpunbond CF/BCF yarn Raffia and

Strapping

PPCO-DS-41/04 Feb 10

JJaammppiilleenn AADDXXPP668800

TYPICAL PROPERTIES VALUE UNIT METHODPhysicalMelt Flow Rate (230 oC, 2.16kg) 3.5 g/10min ASTM D1238Density 0.9 g/cm3 ASTM D1505

MechanicalFlexural Modulus 2200 MPa ASTM D790Tensile Strength at Yield 41 MPa ASTM D638Tensile Elongation at Yield 5 % ASTM D638Izod Impact Strength (notched) at 23 oC 40 J/m ASTM D256Rockwell Hardness 112 R-Scale ASTM D785ThermalVicat softening point (10N) 158 oC ASTM D1525H.D.T. (0.46 Mpa) 120 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze 15 % ASTM D1003Gloss 75 ---- ASTM D2457

No. 5, North-Falamak St., Eyvanak Blvd., Farahzadi Blvd., Shahrak-e-Qods., Tehran, 1467715171, Iran.Tel: +9821-84286, Fax: +9821-88563100Email: [email protected]

This data and information is considered to be correct and offered in good faith as a guide. But we do not warrant or otherwise guarantee themerchantability, fitness for a particular purpose or suitability of this information, products or processes described.

Description: ″Jampilen ADXP680″ is a special polypropylene type whichfeatures an extremely high stiffness, high gloss, goodtransparency and improved characteristics at high temperatures.It has been especially developed for sheet extrusion,thermoforming and film applications where high rigidity,outstanding transparency and very good thermal characteristicsare needed. The composition of the product complies well withFDA norms and with regulations concerning food contactapplications in major European countries.

Processing Method: Extrusion (Sheet, Film)Thermoforming

Features: High stiffnessHigh glossGood transparencyImproved characteristics at high temperaturesHomopolymer

Typical Applications: Transparent food containersContainers for high temperature filling

Approval:Food

[ PPCO-DS-19/04 Feb 10

JJaammppiilleenn AADDXXPP669999

TYPICAL PROPERTIES VALUE UNIT METHOD

PhysicalMelt Flow Rate (230 oC, 2.16kg) 3.5 g/10min ASTM D1238Density 0.9 g/cm3 ASTM D1505

MechanicalFlexural Modulus 2000 MPa ASTM D790Tensile Strength at Yield 39 MPa ASTM D638Tensile Elongation at Yield 6 % ASTM D638Izod Impact Strength (notched) at 23 oC 40 J/m ASTM D256Rockwell Hardness 112 R-Scale ASTM D785ThermalVicat softening point (10N) 157 oC ASTM D1525H.D.T. (0.46 Mpa) 118 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012



Description: ″Jampilen ADXP699″ is a special polypropylene type whichfeatures an extremely high stiffness, high gloss, goodtransparency and improved characteristics at high temperatures.In particular, it has been developed for BOPP and Cast filmapplications where high rigidity, outstanding transparency andvery good thermal characteristics are required. Strapping madeout of ″Jampilen ADXP699″ shows extremely good creepresistance.The composition of the product complies well with FDA normsand with regulations concerning food contact applications inmajor European countries.

Processing Method:BOPP and Cast Film

Features: High stiffness and rigidityHigh glossGood transparencyImproved characteristics at high temperaturesGood creep resistanceHomopolymer

Typical Applications: Flowers and textile packagingSterilizable and pastorizable food packagingPrinting lamination and tobacco filmStrapping

Approval:Food


JJaammppiilleenn HH11885500

TYPICAL PROPERTIES VALUE UNIT METHODPhysicalMelt Flow Rate (230 oC, 5kg) 1.2 g/10min ISO 1133Density 0.902 g/cm3 ISO 1183

MechanicalTensile Secant Modulus 1300 MPa ISO 527-1, -2Tensile Strength at Yield (50 mm/min) 33 MPa ISO 527-1, -2Tensile Elongation at Yield (50 mm/min) 14 % ISO 527-1, -2Charpy impact strength (Notch A) 23 °C 11 kJ/m2 ISO 179ThermalVicat softening point B50 85 oC ISO 306H.D.T. B (0.45 MPa) 90 oC ISO 75B-1, -2OthersMold shrinkage 1.6-1.8 % -----



Description:″Jampilen H1850″ is a very low flow homopolymer with goodstiffness/toughness balance. The grade features yellowingresistance in contact with cooling water. Typical customer useis automotive expansion tanks.

Processing Method: Injection molding

Features: Low flowGood stiffness/toughness balanceGood yellowing resistanceHomopolymer

Typical Applications:Automotive expansion tanksUnder-the-hood and structural applications

PPCO-DS-97/02 Nov 13


TYPICAL PROPERTIES VALUE UNIT METHODPhysicalMelt Flow Rate (230 oC, 2.16kg) 0.3 g/10min ISO 1133Density 0.9 g/cm3 ISO 1183

MechanicalTensile Secant Modulus (1mm/min) 1300 MPa ISO 527-1, -2Tensile Stength at Yield (50 mm/min) 31 MPa ISO 527-1, -2Tensile Elongation at Yield (50 mm/min) 9 % ISO 527-1, -2Notched izod impact strength ISO 180

23°C, Notch A 6 kJ/m2

0°C, Notch A 2.5 kJ/m2

-30°C, Notch A 1.5 kJ/m2

Shore hardness (Shore D) 70 ----- ISO 868ThermalVicat softening point A50 150 oC ISO 306H.D.T. B (0.45 MPa) 90 oC ISO 75B-1, -2Melting Temperature 165 oC ISO 3146



Description: ″Jampilen H2150″ is a natural, nucleated polypropylenehomopolymer with high melt viscosity for extrusion andcompression molding applications. The product has a high heat-and extraction stability and is not intended for medical andpharmaceutical applications.

Processing Method:Extrusion (pipe, sheet)Compression molding

Features:Low folwNucleatedHomopolymer

Typical Applications:Rigid profiles and sheetIndustrial and chemical containers




MechanicalTensile Secant Modulus (1mm/min) 1400 MPa ISO 527-1, -2Tensile Stength at Yield (50 mm/min) 31 MPa ISO 527-1, -2Tensile Elongation at Yield (50 mm/min) 9 % ISO 527-1, -2Notched izod impact strength ISO 180

23°C, Notch A 6 kJ/m2

0°C, Notch A 2.5 kJ/m2

-30°C, Notch A 1.5 kJ/m2

Shore hardness (Shore D) 70 ----- ISO 868ThermalVicat softening point A50 150 oC ISO 306H.D.T. B (0.45 MPa) 90 oC ISO 75B-1, -2Melting Temperature 165 oC ISO 3146



Description: ″Jampilen H2450″ is a natural, nucleated polypropylenehomopolymer with high melt viscosity for extrusion andcompression molding applications. The product has a high heat-and extraction stability and is not intended for medical andpharmaceutical applications.

Processing Method:Extrusion (pipe, sheet)Compression moulding

Features:

Low folwNucleatedHomopolymer

Typical Applications:Rigid Profiles and Sheet


JJaammppiilleenn HHAA770011TT


PhysicalMelt Flow Rate (230 oC, 2.16kg) 45 g/10min ASTM D1238Density 0.9 g/cm3 ASTM D1505




Description: ″Jampilen HA701T″ is very high flow polypropylene typewhich features an extremely high stiffness, high gloss, goodtransparency and improved characteristics at high temperatures.It has been especially developed for TWIM applications wherehigh flow combined with high rigidity, high gloss and verygood thermal characteristics are needed.Typical applications of ″Jampilen HA701T″ include foodcontainers as well as any applications where high fluidityassociated with high gloss and high stiffness are required.The composition of the product complies well with FDA normsand with regulations concerning food contact applications inmajor European countries.

Processing Method:Injection molding

Features: Very high flowHigh stiffnessHigh glossGood transparencyImproved characteristics at high temperaturesExcellent dimensional stabilityHomopolymer

Typical Applications:TWIM (food containers)

Approval:Food


JJaammppiilleenn HHAA884400KK

TYPICAL PROPERTIES VALUE UNIT METHODPhysicalMelt Flow Rate (230 oC, 2.16kg) 3.5 g/10min ASTM D1238Density 0.9 g/cm3 ASTM D1505

MechanicalFlexural Modulus 2200 MPa ASTM D790Tensile Strength at Yield 40 MPa ASTM D638Tensile Elongation at Yield 5 % ASTM D638Izod Impact Strength (notched) at 23 oC 40 J/m ASTM D256Rockwell Hardness 111 R-Scale ASTM D785ThermalVicat softening point (10N) 158 oC ASTM D1525H.D.T. (0.46 Mpa) 118 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze 22 % ASTM D1003Gloss 65 ---- ASTM D2457



Description: ″Jampilen HA840K″ is a special polypropylene type whichfeatures extremely high stiffness, high gloss, good transparencyand improved characteristics at high temperatures. It has beenespecially developed for extrusion, thermoforming and filmapplications where high rigidity, outstanding transparency andvery good thermal characteristics are needed.The composition of the product complies well with FDA normsand with regulations concerning food contact applications inmajor European countries.

Processing Method: Extrusion (Sheet, Film)Thermoforming

Features: High stiffnessHigh glossGood transparencyImproved characteristics at high temperaturesHomopolymer

Typical Applications: Transparent food containersContainers for high temperature filling

Approval:Food


JJaammppiilleenn HHAA884400RR



MechanicalFlexural Modulus 2350 MPa ASTM D790Tensile Strength at Yield 41 MPa ASTM D638Tensile Elongation at Yield 5 % ASTM D638Izod Impact Strength (notched) at 23 oC 35 J/m ASTM D256Rockwell Hardness 111 R-Scale ASTM D785ThermalVicat softening point (10N) 159 oC ASTM D1525H.D.T. (0.46 Mpa) 128 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze (1mm) 40 % ASTM D1003Gloss (60o) 95 ---- ASTM D2457



Description: ″Jampilen HA840R″ is a special polypropylene type whichfeatures an extremely high stiffness and high gloss. It has beenespecially developed for the production of stiff injection-molded articles where high rigidity is needed. Typicalapplications of ″Jampilen HA840R″ include food packagingcontainers, housewares, small appliances and technical parts.The composition of the product complies well with FDA normsand with regulations concerning food contact applications inmajor European countries.


Features: High stiffnessHigh glossHomopolymer

Typical Applications: Food packaging containersHousewaresFurnitureSmall appliancesTechnical partsCaps and clusures

Approval:Food


JJaammppiilleenn HHPP337711PP



MechanicalFlexural Modulus 1150 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 13 % ASTM D638Izod Impact Strength (notched) at 23 oC 50 J/m ASTM D256Rockwell Hardness 98 R-Scale ASTM D785ThermalVicat softening point (10N) 151 oC ASTM D1525H.D.T. (0.46 Mpa) 99 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze (1mm) 15 % ASTM D1003Gloss (60o) 62 ---- ASTM D2457



Description: ″Jampilen HP371P″ is a polypropylene homopolymer withgamma-ray stabilizing additivation featuring high fluidity andsuperior transparency. The product is designed for theproduction of three-part syringes and a wide range of medicalarticles. ″Jampilen HP371P″ is sterilisable both with gammaand E-beam irradiation and with ETO. Because of the highmelt flow, mold filling is easy and cycle times are short leadingto an excellent processability. Items produced with″Jampilen HP371P″ feature good stiffness, high impactstrength, minimum warpage and high chemical resistance andoffer a really outstanding transparency.


Features: Medium clarityExcellent processabilityGood stiffnessRadiation and ETO sterilizableHigh chemical resistanceHomopolymer

Typical Applications: Three-part syringesMedical articles and healthcare applicationsLabware such as needle hubs, pipette tips, test tubes, jugs,cylinders and containersHigh quality household articlesPackaging components


JJaammppiilleenn HHPP440000RR






Description: ″Jampilen HP400R″ is a high flow homopolymer for injectionmolding and compounding applications that exhibits highstiffness, outstanding processability for shorter cycle times andeasy mold filling.The product is suitable for injection molding applications suchas thin-walled containers and other general purpose packagingitems, toys, vacuum flasks, household and kitchen articles.″Jampilen HP400R″ also is an excellent polymer base forcompounding and masterbatches.″Jampilen HP400R″ is suitable for food contact.

Processing Method: Injection moldingCompounding

Features: Excellent processabilityGood stiffnessHomopolymer

Typical Applications: Thin-walled containersToysVacuum flasksHousehold and kitchen articlesFurniturePolymer base for compounding and masterbatches

Approval:Food


JJaammppiilleenn HHPP442200MM


MechanicalTensile Modulus (1mm/min) 1450 MPa ISO 527-1, -2Tensile strength at Yield (50mm/min) 35 MPa ISO 527-1, -2Tensile elongation at Yield (50mm/min) 10 % ISO 527-1, -2Shore hardness (Shore D) 70 ---- ISO 868ThermalVicat softening point A50 152 oC ISO 306H.D.T. B (0.45 MPa) 85 oC ISO 75B-1, -2



Description: ″Jampilen HP420M″ is a high flow polypropylenehomopolymer designed for the production of biaxially orientedpolypropylene film (BOPP) on tubular double bubble lines andcast film. Typical applications are BOPP packaging, laminatingfilm and drinking straws but also packaging foodstuffs such aspasta, snacks, biscuits, bakery products and confectionery, filmfor packaging for flowers, books stationery, blankets, shirts,knitwear and hosiery.″Jampilen HP420M″ is suitable for food contact.

Processing Method:BOPP Film on tubular double bubble linesCast Film

Features:High flowGood transparencyHomopolymer

Typical Applications:BOPP Films for packaging of flowers, textiles and hosieryDrinking StrawsPackaging of foodstuffs (Snacks, pasta, confectionery, etc)

Approval:Food


JJaammppiilleenn HHPP442211HH






Description:″Jampilen HP421H″ is a modified homopolymer designed forthe very high speed production of coextruded BOPP films. Theproduct is used for the core of the coextruded film structurewith a low seal temperature resin (Jampilen terpolymers) in theoutside layers.″Jampilen HP421H″ allows an outstanding extrusion stabilityand thickness variation control, especially on cascade lines,very high drawability and readiness to a two way orientation.The product contains a reinforced processing stabilization anda package of slip and antistatic agents but does not bear anyantiblocking agents.BOPP films produced with ″Jampilen HP421H″ feature goodmechanical properties, even at low temperatures, excellentbarrier against moisture, odours, oils, fats and oxygen and hightransparency, high gloss and good printability after coronatreatment.

Processing Method: BOPP Film

Features:High impact strength and puncture resistanceExcellent barrier against moisture, odours, oils and oxygenHigh transparency and glossGood printabilityHomopolymer

Typical Applications:Automatic packaging of bakery products, snacks and pastaOverwrapping of boxes and cigarette packetsTextile packaging filmSurface protection filmBarrier film

PPCO-DS-16/06 Oct 15




MechanicalFlexural Modulus 1550 MPa ASTM D790Tensile Strength at Yield 35 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 60 J/m ASTM D256Rockwell Hardness 102 R-Scale ASTM D785ThermalVicat softening point (10N) 154 oC ASTM D1525H.D.T. (0.46 Mpa) 92 oC ASTM D648Accelerated oven ageing in air at 150 oC 500 hours ASTM D3012OpticalHaze (20µ) 0.50 % ASTM D1003



Description: ″Jampilen HP422H″ is a modified homopolymer designed forthe high speed production of BOPP films, wherein anoutstanding extrusion stability, thickness variation control, avery high drawability and readiness to a two way orientationwould be achieved. The product contains a reinforcedprocessing stabilization and features low water carry-overproperties. ″Jampilen HP422H″ does not contain any slip orantistatic agent and is Calcium Stearate free. The Product isparticularly suitable for metalizing film.BOPP films produced with ″Jampilen HP422H″ feature goodmechanical properties, even at low temperatures, excellentbarrier against moisture, odors, oils and oxygen and goodtransparency and gloss.Monolayer or coextruded films made of ″Jampilen HP422H″with a thickness ranging from 20 to 40 µm are used for thepackaging of foodstuffs, cosmetics, CDs and DVDs.

Processing Method:BOPP Film

Features:High impact strengthHigh puncture resistanceGood transparency and glossHomopolymer

Typical Applications: Food packaging filmPackaging of cosmetics, CDs and DVDsBarrier film

Approval:Food

PPCO-DS-129/00 Oct 14

JJaammppiilleenn HHPP442255JJ



MechanicalFlexural Modulus 1400 MPa ASTM D790Tensile Strength at Yield 33 MPa ASTM D638Tensile Elongation at Yield 11 % ASTM D638Izod Impact Strength (notched) at 23 oC 34 Kg-cm/cm ASTM D256ThermalDTUL at 66psi - Unannealed 93 oC ASTM D648OpticalHaze (20µm) 0.5 % ASTM D1003



Description:

″Jampilen HP425J″ is a polypropylene homopolymercontaining Calcium Stearate free stabilization package. It doesnot contain any slip or antiblocking additives. ″JampilenHP425J″ is designed for the high speed production of BOPPfilms. It is used by customers for a broad range of applicationsincluding metallizable films and both plain and coextrudedstructures. BOPP films produced with ″Jampilen HP425J″exhibit balanced mechanical properties, good transparency,gloss and enhanced shrinkage properties.


Features:HomopolymerHigh Speed ProcessCalcium Stearate Free

Typical Applications:Barrier FilmBopp Metallizable Film for PackagingFood Packaging Film

Approval:Food


JJaammppiilleenn HHPP443322CC






Description: ″Jampilen HP432C″ is a homopolymer with high molecularweight and outstanding mechanical properties. The productexihibits excellent processability in extrusion applications andexcellent long-term heat ageing resistance.″Jampilen HP432C″ is well suited for technical extrusionapplications that require both high stiffness and high impactresistance.″Jampilen HP432C″ is suitable for food contact.

Processing Method: Extrusion (Sheet)ThermoformingInjection moldingExtrusion blow molding

Features: High molecular weightExcellent processabilityExcellent long-term heat ageing resistanceHigh stiffness and impact resistanceHomopolymer

Typical Applications: Thick, heavy sheet for industrial applicationsStrappingTubes, profiles and pipesThin sheet for thermoforming dairy tubs and other foodpackagingSmall containers and technical partsWheels, fittings and high performance industrial components

Approval:Food




MechanicalTensile Modulus (1mm/min) 1500 MPa ISO 527-1, -2Tensile Strength at Yield (50mm/min) 34 MPa ISO 527-1, -2Tensile Elongation at Yield (50mm/min) 9 % ISO 527-1, -2Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 97 oC ISO 75B-1, -2



Description: ″Jampilen HP456H″ is a homopolymer, suitable for extrusionand thermoforming applications. It is formulated with a lowwater carry-over additive package. Typical applications of″Jampilen HP456H″ are strapping, monofilaments and tapes.″Jampilen HP456H″ has a wide range of approval for contactwith food.

Processing Method:Extrusion (Raffia and Tapes)Thermoforming

Features:Low water carry-overGood StretchabilityHomopolymer

Typical Applications:Raffia, Tapes and StrappingArtificial GrassGeotextile and agriculture

Approval:Food




MechanicalTensile Modulus (1mm/min) 1500 MPa ISO 527-1, -2Tensile Strength at Yield (50mm/min) 34 MPa ISO 527-1, -2Tensile Elongation at Yield (50mm/min) 10 % ISO 527-1, -2Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23oC 4.0 kJ/m2 ISO 179ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 97 oC ISO 75B-1, -2



Description: ″Jampilen HP456J″ is a homopolymer, suitable for extrusionand thermoforming applications. It is formulated with a lowwater carry-over additive package.″Jampilen HP456J″ is designed for production of ropes andtapes for carpet backing.

Processing Method: Fiber Extrusion (Raffia, Tape, Monofilament)Extrusion (Sheet)Thermoforming

Features: Good stretchabilityLow water carry-overHomopolymer

Typical Applications: Raffia, tapes, strappingArtificial grassGeotextile and agriculture

Approval:Food



TYPICAL PROPERTIES VALUE UNIT METHODPhysicalMelt Flow Rate (230 oC, 2.16kg) 25 g/10min ISO 1133Density 0.9 g/cm3 ISO 1183

MechanicalFlexural Modulus 1450 MPa ISO 178Tensile Strength at Yield 34 MPa ISO 527-1, -2Tensile Elongation at Yield 10 % ISO 527-1, -2Tensile Elongation at Break >50 % ISO 527-1, -2ThermalVicat softening point A50 151 oC ISO 306H.D.T. B (0.45 MPa) 97 oC ISO 75B-1, -2



Description: ″Jampilen HP462R″ is a very narrow molecular weightdistribution homopolymer, suitable for fiber extrusionapplications. It is formulated with an antigasfading stabilisationpackage. ″Jampilen HP462R″ is designed for production ofcontinuous filaments. Typical applications are HTY andspunbond nonwoven.

Processing Method:Extrusion (filament)Fiber Spinning

Features:Controlled rheologyGas-fading resistantNarrow molecular weight distributionHomopolymer

Typical Applications:HTY and spunbond nonwovenFilament YarnGeotextile and AgricultureHygiene NonwovenProtective ClothesWipes and tissues




MechanicalTensile Modulus 1400 MPa ISO 527-1, -2Tensile Strength at Yield 32 MPa ISO 527-1, -2Tensile Elongation at Yield 9 % ISO 527-1, -2Tensile Elongation at Break >50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23 °C 2 kJ/m2 ISO 179Ball indentation hardness (H 358/30) 68 MPa ISO 2039-1ThermalVicat softening point A50 151 oC ISO 306H.D.T. B (0.45 MPa) 80 oC ISO 75B-1, -2



Description: ″Jampilen HP483R″ is a homopolymer for injection moldingwith antistatic and slip agent additivation that exhibits goodstiffness combined with good flowability.The main applications of ″Jampilen HP483R″ are caps,closures, furniture and TWIM.

Processing Method:Injection molding (TWIM)

Features:Good FlowGood stiffnessAntistatic propertiesUnspecified SlipHomopolymer

Typical Applications:TWIMFurnitureCaps and ClosuresHousewaresOpaque Containers








Description: ″Jampilen HP500H″ is a polypropylene homopolymer forgeneral injection molding applications. Besides the highstiffness and good impact strength, ″Jampilen HP500H″ offersgood processability.″Jampilen HP500H″ is suitable for a wide range of applicationssuch as appliance components, textile bobbins, wheels, fittings,caps, closures, and household articles.″Jampilen HP500H″ is suitable for food contact.


Features: Good impact strengthHigh stiffnessGood processabilityHomopolymer

Typical Applications: Appliance componentsTextile bobbinsWheelsFittingsCaps, closuresHousehold articles

Approval:Food








Description: ″Jampilen HP500J″ is a general purpose polypropylenehomopolymer for injection molding applications and combineshigh stiffness and fairly good impact strength with goodprocessability.The grade is suitable for a wide range of applications such ashousewares, caps, closures, small containers, toys, parts forsmall appliances and components for the automotive industry.″Jampilen HP500J″ is also used for compounding. This gradeis suitable for food contact.


Features: Good impact strengthHigh stiffnessGood processabilityHomopolymer

Typical Applications: HousewaresCaps and closuresSmall containersToysParts for small appliancesComponents for the automotive industryCompounding

Approval:Food


JJaammppiilleenn HHPP550000LL






Description:″Jampilen HP500L″ is a polypropylene homopolymer forinjection molding that provides good flow properties, easyprocessing and high stiffness.The main applications of ″Jampilen HP500L″ are housewares,small containers, crates, garden furniture, stadium seats, toys,caps and closures. Other major applications are components forappliances and parts for the automotive industry.″Jampilen HP500L″ is suitable for food contact.


Features: Easy processing and good moldabilityHigh stiffnessGood stretchabilityHomopolymer

Typical Applications: Housewares and components for appliancesSmall containersCratesGarden furnitureStadium seatsToysCaps and closuresParts for the automotive industry

Approval:Food








Description: ″Jampilen HP500M″ is a polypropylene homopolymer suitablefor injection molding applications that due to its good flowproperties offers easy processing. Articles produced from″Jampilen HP500M″ exhibit high stiffness.″Jampilen HP500M″ is widely used for injection moldingconsumer goods such as food containers, housewares, toys andgarden furniture. Other major applications are components forappliances and parts for the automotive industry.″Jampilen HP500M″ is suitable for food contact.


Features: Good flow propertiesEasy processingHigh stiffnessHomopolymer

Typical Applications: HousewaresFood containersGarden furnitureToysComponents for appliancesParts for the automotive industry

Approval:Food


JJaammppiilleenn HHPP550000NN






Description: ″Jampilen HP500N″ is a medium fluidity polypropylenehomopolymer for general purpose injection moldingapplications. Due to its good flow properties, this grade offerseasy mold filling and short cycle times. Articles produced from″Jampilen HP500N″ exhibit good dimensional stability andhigh stiffness.″Jampilen HP500N″ is widely used for injection moldingconsumer goods such as food containers, cool boxes, vacuumflasks, flower pots, toys, garden furniture and small appliances.In the medical sector, ″Jampilen HP500N″ is used for 3-partsyringes and a wide range of health-care items. Otherapplications are closures, caps and crates for products.″Jampilen HP500N″ is suitable for food contact.


Features: Easy mold filling and short cycle timesGood dimensional stabilityHigh stiffnessHomopolymer

Typical Applications: Cool boxes, vacuum flasks, flower potsFood containersGarden furnitureToys3-part syringesClosures, capsCrates

Approval:Food



TYPICAL PROPERTIES VALUE UNIT METHODPhysicalMelt Flow Rate (230 oC, 2.16kg) 17 g/10min ASTM D1238Density 0.9 g/cm3 ASTM D1505MechanicalFlexural Modulus 1550 MPa ASTM D790Tensile Strength at Yield 33 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 30 J/m ASTM D256Rockwell Hardness 103 R-Scale ASTM D785ThermalVicat softening point (10N) 154 oC ASTM D1525H.D.T. (0.46 Mpa) 95 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012



Description: ″Jampilen HP500P″ is a polypropylene homopolymer withgood flow properties for injection molding and compoundingapplications. This grade offers medium-high fluidity, easymold filling and short cycle times. The final items molded with″Jampilen HP500P″ exhibit good dimensional stability andhigh stiffness.The product is well suited for the production of thin-walledarticles and articles with long flow paths. ″Jampilen HP500P″is also an excellent polymer base for compounding andmasterbatches.″Jampilen HP500P″ is suitable for food contact.


Features: Easy mold filling and short cycle timesGood dimensional stabilityHigh stiffnessHomopolymer

Typical Applications: Thin-walled articlesContainersBoxesToysHousehold articlesClosures and capsPolymer base for compounding and masterbatches

Approval:Food


JJaammppiilleenn HHPP550011DD






Description: ″Jampilen HP501D″ is a homopolymer polypropyleneparticularly suitable for extrusion. ″Jampilen HP501D″combines excellent processability with outstanding mechanicalproperties.″Jampilen HP501D″ is suitable for food contact.

Processing Method: Extrusion (Sheet, pipe)Blow molding

Features: Excellent processabilityGood mechanical propertiesHomopolymer

Typical Applications:StrappingSheetProfiles and small diameter pipes such as refills for ball pensNets for olive harvestingSmall and medium sized containers

Approval:Food




MechanicalTensile Modulus (1mm/min) 1450 MPa ISO 527-1, -2Tensile Strength at Yield (50mm/min) 33 MPa ISO 527-1, -2Tensile Elongation at Yield (50mm/min) 9 % ISO 527-1, -2Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23oC 5 kJ/m2 ISO 179ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 85 oC ISO 75B-1, -2



Description: ″Jampilen HP501H″ is a homopolymer for injection mouldingwhich exhibits good stiffness/impact balance at ambienttemperatures.The main applications of ″Jampilen HP501H″ are caps, closuresand furniture.

Processing Method:Injection moldingThermoforming

Features:Good stiffness/impact balanceHomopolymer

Typical Applications:FurnitureCaps and Closures




MechanicalTensile Modulus (1 mm/min) 1500 MPa ISO 527-1, -2Tensile Strenght at Yield (50 mm/min) 34 MPa ISO 527-1, -2Tensile Elongation at Yield (50 mm/min) 9 % ISO 527-1, -2Tensile Elongation at Break (50 mm/min) >50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23 °C 3.5 kJ/m2 ISO 179Ball indentation hardness (H 358/30) 74 MPa ISO 2039-1ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 85 oC ISO 75B-1, -2



Description: ″Jampilen HP501M″ is a homopolymer polypropylene forinjection molding applications that exhibits goodstiffness/impact balance at ambient temperature.The main applications of ″Jampilen HP501M″ are caps andclosures, housewares and furniture.


Features:Good stiffness/impact balanceHomopolymer

Typical Applications:FurnitureInjection Molded Caps and ClosuresHousewares


JJaammppiilleenn HHPP550022CC






Description: ″Jampilen HP502C″ is a high molecular weight polypropylenehomopolymer for extrusion applications. The product featuresexcellent mechanical properties and outstanding long-term heatageing resistance. ″Jampilen HP502C″ is well suited forextrusion applications where both high stiffness and highimpact strength are among primary requirements.″Jampilen HP502C″ is suitable for food contact.

Processing Method: Extrusion (Sheet, pipe)Compression molding

Features: Excellent mechanical propertiesGood long-term heat ageing resistanceHigh stiffness and impact strengthHomopolymer

Typical Applications: Thick sheet for technical and industrial applicationsProfiles and pipes

Approval:Food








Description: ″Jampilen HP502H″ is a polypropylene homopolymerparticularly suitable for the production of sheet forthermoforming, film yarn and monofilament.″Jampilen HP502H″ combines excellent processability withhigh stiffness and is particularly suitable to produce film yarn,both with cast and tubular processes. Textile film yarns have adenier count of not more than 1100 to 1200 and are used for theproduction of bags, industrial fabrics and mats. Film yarn witha denier count ranging from 3000 to 28000 is used for balertwines, packaging twines and ropes.″Jampilen HP502H″ is also well suited for the production ofmonofilament used for brush and broom filling and technicalapplications.

Processing Method:Extrusion (Sheet, film yarn, monofilament )ThermoformingBlow moldingInjection molding

Features: Excellent processabilityHigh stiffnessHomopolymer

Typical Applications: Sheet for thermoforming (drinking beakers, packaging fordairy products, nursery flower pots and trays for fruit, biscuitsand chocolates)Bags, industrial fabrics and matsBaler twines, packaging twines and ropesBrush and broom filling and technical applicationsProfiles and small diameter pipes such as refills for ball pensStrappingBlow molded small containers





MechanicalFlexural Modulus 1550 MPa ASTM D790Tensile Strength at Yield 34 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 30 J/m ASTM D256Rockwell Hardness 102 R-Scale ASTM D785ThermalVicat softening point (10N) 154 oC ASTM D1525H.D.T. (0.46 Mpa) 95 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalGloss (60o) 95 ---- ASTM D2457



Description: ″Jampilen HP502N″ is a medium fluidity polypropylenehomopolymer and is particularly suitable for the production ofheavy denier staple fiber and continuous filament.″Jampilen HP502N″ exhibits good process stability andconstant, high flow during extrusion.″Jampilen HP502N″ is developed for the extrusion of staplefibers for spinning wool system fibers for carpets, rugs andgarments such as overalls and socks.″Jampilen HP502N″ is also suited for the production ofcontinuous filament for ropes, belts and straps. Another typicalapplication of ″Jampilen HP502N″ is the extrusion ofdecorative ribbons.

Processing Method:Fiber Extrusion (Staple fiber, Continuous filament)

Features: Good process stabilityHigh flow during extrusionHomopolymer

Typical Applications: Carpets, rugs and garments such as overalls and socksContinuous filament for ropes, belts and strapsDecorative ribbons

Approval:Food








Description: ″Jampilen HP502P″ is a homopolymer with good flowproperties and medium molecular weight distribution intendedfor fiber extrusion applications.″Jampilen HP502P″ has a high fluidity and best suits for theproduction of staple fibers, bulk continuous filaments (BCF)and continuous filaments (CF). It contains a general purposeformulation of additives with no antigasfading additivation.

Processing Method:Fiber Extrusion

Features: Good Flow PropertiesConsistent processabilityMedium Molecular Weight DistributionHomopolymer

Typical Applications:BCF and CF YarnsStaple fibers

PPCO-DS-25/07 Jul 17

JJaammppiilleenn HHPP551100LL



MechanicalFlexural Modulus 1400 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 9 % ASTM D638Izod Impact Strength (notched) at 23 oC 40 J/m ASTM D256

ThermalVicat softening point (10N) 152 oC ASTM D1525H.D.T. (0.46 MPa) 84 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012



Description:″Jampilen HP510L″ is a polypropylene homopolymer withgood flow properties and is particularly suitable for theextrusion of film yarn, monofilament, cast film and sheet.″Jampilen HP510L″ combines outstanding processability withgood mechanical properties. Film yarn made of″Jampilen HP510L″ is used for baler twines, packaging twinesand ropes.″Jampilen HP510L″ is well suited for the production ofmonofilament used for instance in brush and broom filling andtechnical applications.

Processing Method: Extrusion (Sheet, film yarn, monofilament)Cast film

Features: Good processabilityGood mechanical propertiesHomopolymer

Typical Applications: Baler twines, packaging twines and ropesBrush and broom filling and technical applicationsCoextruded film for packagingThin sheet for stationery foldersSheet for thermoformingGunny sacks

Approval:Food





MechanicalFlexural Modulus 1550 MPa ASTM D790Tensile Strength at Yield 35 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 37 J/m ASTM D256Rockwell Hardness 102 R-Scale ASTM D785ThermalVicat softening point (10N) 154 oC ASTM D1525H.D.T. (0.46 Mpa) 95 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze 1.2 % ASTM D1003Gloss 88 ----- ASTM D2457



Description: ″Jampilen HP510M″ is a homopolymer particularly suited forthe extrusion of cast and water quenched blown films.″Jampilen HP510M″ is formulated with a general purposestabilization package and does not contain any slip orantiblocking agents. This grade exhibits excellentprocessability and outstanding optical properties.″Jampilen HP510M″ renders high gloss finish in laminates andexhibits good printability after Corona treatment.

Processing Method: Cast filmWater quenched blown filmExtrusion (Small pipes)Blow molding

Features: Excellent processabilityGood optical propertiesExcellent glossHomopolymer

Typical Applications: Film for packaging food-stuffs such as pasta, snacks, biscuits,bakery products and confectioneryFilm for packaging of flowers, books, stationery, blankets,shirts, knitwear and hosieryLamination with polyester, polyamide and aluminum forpackaging of snacks, crisps, sweets, coffee, meat products andpre-cooked foodsSmall pipes and drinking strawsBlow molded pigmented bottlesCoextruded sheet

Approval:Food





MechanicalFlexural Modulus 1300 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 40 J/m ASTM D256Rockwell Hardness 95 R-Scale ASTM D785ThermalVicat softening point (10N) 150 oC ASTM D1525H.D.T. (0.46 Mpa) 92 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze 1.2 % ASTM D1003Gloss 86 ---- ASTM D2457



Description:″Jampilen HP515M″ is a polypropulene homopolymerdeveloped for the high speed extrusion of transparent cast andblown films. It is formulated with slip and antiblocking agents.″Jampilen HP515M″ is suitable for the extrusion of lowthickness films and can be used for films from 15 up to 150µm. In comparison with standard polypropylene types for filmproduction, ″Jampilen HP515M″ allows for faster processingdue to its peculiar structure and composition.Films made with ″Jampilen HP515M″ show a good behavioron winding rolls and in cutting section and feature very hightransparency, high gloss and good printability after coronatreatment.

Processing Method: Cast filmBlown film

Features: Excellent processabilityHigh transparency and glossAntiblock propertiesHomopolymer

Typical Applications: Shopping bagsPackaging for snacks, bakery products, books, blankets,hosiery and shirtsStationery foldersTwines and ropes





MechanicalFlexural Modulus 1650 MPa ASTM D790Tensile Strength at Yield 35 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 60 J/m ASTM D256Rockwell Hardness 105 R-Scale ASTM D785ThermalVicat softening point (10N) 154 oC ASTM D1525H.D.T. (0.46 Mpa) 94 oC ASTM D648Accelerated oven ageing in air at 150 oC 500 hours ASTM D3012OpticalHaze (20µ) 0.30 % ASTM D1003



Description:″Jampilen HP520H″ is a homopolymer designed for theproduction of biaxially oriented polypropylene films through avery stable extrusion on stenter and double bubble lines withexcellent thickness control, increased drawability and readinessto a two way orientation.″Jampilen HP520H″ contains a reinforced processingstabilization but does not contain any slip or antiblockingagents. BOPP films produced with this grade feature goodmechanical properties, even at low temperatures, excellentbarrier against moisture, odours, oils, fats and oxygen and hightransparency, high gloss and good printability after coronatreatment.Monolayer films made of ″Jampilen HP520H″ are used forfood packaging, textiles packaging, flower wrappings andadhesive tapes.″Jampilen HP520H″ is suitable for food contact.


Features:High impact strength and puncture resistanceExcellent barrier against moisture, odours, oils and oxygenHigh transparency and glossGood printabilityHomopolymer

Typical Applications: Food packaging, textiles packaging and flower wrappingsAdhesive tapesLamination to other flexible films

Approval:Food





MechanicalFlexural Modulus 1650 MPa ASTM D790Tensile Strength at Yield 35 MPa ASTM D638Tensile Elongation at Yield 12 % ASTM D638Izod Impact Strength (notched) at 23 oC 60 J/m ASTM D256Rockwell Hardness 105 R-Scale ASTM D785ThermalVicat softening point (10N) 154 oC ASTM D1525H.D.T. (0.46 Mpa) 94 oC ASTM D648Accelerated oven ageing in air at 150 oC 500 hours ASTM D3012OpticalHaze (20µm) 0.6 % ASTM D1003



Description: ″Jampilen HP522H″ is a homopolymer for the production ofbiaxially oriented polypropylene films which is particularlysuitable for metallization, both as plain film and in coextrudedstructures. ″Jampilen HP522H″ has been designed to provide avery stable extrusion on stenter lines and to give excellentthickness control, increased drawability and readiness to a twoway orientation. This grade contains a reinforced processingstabilization but does not contain any slip or antiblockingagents and is calcium stearate free. The product features lowwater carry-over properties and is therefore also suitable fortubular BOPP.BOPP films produced with ″Jampilen HP522H″ feature goodmechanical properties, even at low temperatures, excellentbarrier against moisture, odours, oils, fats and oxygen and goodoptical properties.Monolayer or coextruded films made of ″Jampilen HP522H″with a thickness ranging from 20 to 40 µm are used for thepackaging of foodstuffs, cosmetics, CDs and DVDs.″Jampilen HP522H″ is suitable for food contact.


Features: High impact strength and puncture resistanceExcellent barrier against moisture, odours, oils and oxygenGood optical propertiesHomopolymer

Typical Applications: Food packagingPackaging of cosmetics, CDs and DVDsLamination to other flexible films

Approval:Food

PPCO-DS-91/00 Jan 10



MechanicalTensile Modulus (1mm/min) 1370 MPa ISO 527-1, -2Tensile Strength at Yield (50mm/min) 33 MPa ISO 527-1, -2Tensile Elongation at Yield (50mm/min) 11 % ISO 527-1, -2Tensile Elongation at Break (50mm/min) 550 % ISO 527-1, -2Shore hardness (Shore D) 69 ---- ISO 868ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 85 oC ISO 75B-1, -2



Description: ″Jampilen HP522J″ is a new homopolymer grade designed forthe production of biaxially oriented polypropylene films(BOPP) primarily on high speed BOPP lines. This grade ischaracterised by its very broad processing window, easy filmstretchability, good optical properties and reliable filmthickness profile.″Jampilen HP522J″ is suitable for metallization, both asmonolayer and in coextruded structures. It does not contain anyslip or antiblocking agents and it is Calcium Stearate free.Typical applications are BOPP packaging films and Sheet forSolid Phase Thermoforming.″Jampilen HP522J″ is suitable for food contact.

Processing Method:BOPP filmThermoforming

Features:

High clarityHigh glossMedium flowGood ProcessabilityHomopolymer

Typical Applications:BOPP packagingFood Packaging FilmsThermoformed objects and containers

Approval:Food








Description:″Jampilen HP524J″ is a medium flow homopolymer withbimodal molecular weight distribution and good clarityintended for the manufacture of BOPP films.″Jampilen HP524J″ gives reliable and consistent processing onBOPP stenter lines, providing films having high transparencyand gloss with a good balance of film properties. It contains ageneral purpose formulation of additives.The BOPP films obtained from this grade can be used for highquality packaging and laminates.″Jampilen HP524J″ is suitable for food contact.


Features:Medium FlowGood processabilityGood Transparency and GlossHomopolymer

Typical Applications:High quality packaging film for foodLamination to other filmsMedical packaging

Approval: Food





MechanicalFlexural Modulus 1400 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 9 % ASTM D638Izod Impact Strength (notched) at 23 oC 50 J/m ASTM D256ThermalVicat softening point (10N) 152 oC ASTM D1525H.D.T. (0.46 MPa) 84 oC ASTM D648Accelerated oven ageing in air at 150 oC 500 hours ASTM D3012OpticalHaze (20µm) 0.5 % ASTM D1003



Description: ″Jampilen HP525J″ is a medium flow homopolymer withbimodal molecular weight distribution and good clarityintended for BOPP films. The product is suitable formetallizable film, both as monolayer and in coextrudedstructures. It contains a standard processing stabilisation butdoes not contain any slip, antiblocking agents and is calciumstearate free.″Jampilen HP525J″ offers good optical properties, easyprocessing and very stable film profile. Typical applications areBOPP packaging films and Solid Phase Thermoforming sheets.″Jampilen HP525J″ is suitable for food contact.

Processing Method:BOPP FilmThermoforming

Features:Medium FlowGood processabilityGood transparency and glossHomopolymer

Typical Applications:High quality packaging film for foodLamination to other filmsMetalizable filmMedical packagingThermoformed food containers

Approval:Food








Description: ″Jampilen HP527J″ is a medium flow homopolymer withbimodal molecular weight distribution and good clarityintended for production of BOPP films.″Jampilen HP527J″ provides reliable and consistent processingon BOPP stenter lines, rendering films having hightransparency and gloss with a good balance of film properties.Besides the general purpose formulation of additives, this gradecontains antistatic, antiblock and slip agents which will bestcontribute to its final processability and properties.The BOPP films obtained from this grade can be used for highquality packaging and laminates.″Jampilen HP527J″ is suitable for food contact.


Features: Medium FlowGood Transparency and GlossAntistatic and antiblock propertiesExcellent processabilityHomopolymer

Typical Applications:High quality packaging for foodLamination to other filmsMedical packaging

Approval:Food








Description:″Jampilen HP528H″ is a homopolymer designed for themanufacture of coextruded biaxially oriented polypropylene(BOPP) films. The product is used for the core of thecoextruded film structure with a low seal temperature randomcopolymer (Jampilen terpolymers) in the outside layers.″Jampilen HP528H″ has been designed to provide a very stableextrusion on stenter lines and to render excellent thicknesscontrol, increased drawability and readiness to a two wayorientation. The product contains a reinforced processingstabilization and a package of slip and antistatic agents butdoes not contain antiblocking agents. BOPP films producedwith ″Jampilen HP528H″ feature good mechanical properties,high impact strength and puncture resistance, even at lowtemperatures. The films form an excellent barrier againstmoisture, odours, oils, fats and oxygen and feature hightransparency, high gloss and good printability after coronatreatment.″Jampilen HP528H″ is suitable for food contact.


Features: High impact strength and puncture resistanceExcellent barrier against moisture, odours, oils and oxidationHigh transparency and glossGood printabilityHomopolymer

Typical Applications: Automatic packaging of bakery products, snacks and pastaOverwrapping of boxes and cigarette packets

Approval:Food




MechanicalTensile Modulus (1mm/min) 1450 MPa ISO 527-1, -2Tensile Strength at Yield (50mm/min) 34 MPa ISO 527-1, -2Tensile Elongation at Yield (50mm/min) 11 MPa ISO 527-1, -2Tensile Strength at Break (50mm/min) 23 % ISO 527-1, -2Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2Shore hardness (Shore D) 70 ---- ISO 868ThermalVicat softening point A50 156 oC ISO 306H.D.T. B (0.45 MPa) 85 oC ISO 75B-1, -2



Description: ″Jampilen HP528J″ is a polypropylene homopolymer designedfor the production of biaxially oriented polypropylene films(BOPP) and contains a standard processing stabilization as wellas antistatic agent, but does not contain any slip or antiblockingagents and is Calcium Stearate free.″Jampilen HP528J″ offers good optical properties, easyprocessing and very good thickness profile of the films. Typicalapplications are BOPP packaging films.″Jampilen HP528J″ is suitable for food contact.

Processing Method:BOPP film

Features:

High clarity and glossMedium flowGood ProcessabilityHomopolymer

Typical Applications:BOPP PackagingFood Packaging Films

Approval:Food








Description: ″Jampilen HP529J″ is a polypropylene homopolymer designedfor the manufacture of BOPP film on stenter lines.″Jampilen HP529J″ is approved for food contact and medicalapplications.



Typical Applications:Food and medical Packaging

Approval:Food, Medical








Description: ″Jampilen HP532J″ is a heat and detergent resistantpolypropylene homopolymer. The product is designed forinjection molding items which are subject to severeenvironmental conditions as well as extruded tapes and raffia.″Jampilen HP532J″ offers good processability and finisheditems produced by it show good balance of stiffness and impactstrength. ″Jampilen HP532J″ is formulated with a veryeffective heat and detergent stabilisation package for both dryand wet environments. The product also shows a highresistance to solvents and chemicals. In a dry environment,items produced with ″Jampilen HP532J″ can withstand acontinuous heat of 95°C for over 80.000 hours and 70°C forover 1.000.000 hours. In a wet environment, the items canresist to a continuous temperature of 95°C for over 10.000hours and 70°C for over 130.000 hours. In a wet environmentin the presence of detergents, the items can withstand 95°C forover 4.500 hours and 70°C for more than 50.000 hours.

Processing Method: Injection moldingExtrusion (raffia, tape)

Features: Good balance of stiffness and impact strengthGood processabilityHigh resistance to detergent, solvents and chemicalsHigh resistance to heatHomopolymer

Typical Applications: Automotive under-the-hood applicationsComponents for small household appliancesIrons, coffee machines, hair dryers and toastersParts for dish washers, washing machines and refrigeratorsChain links for conveyor belts and textile bobbinsTapes and raffiaFilm wrapFilament yarn

Approval:Food




MechanicalTensile Modulus (1mm/min) 1600 MPa ISO 527-1, -2Tensile Strength at Yield (50mm/min) 37 MPa ISO 527-1, -2Tensile Elongation at Yield (50mm/min) 9 % ISO 527-1, -2Tensile Elongation at Break (50mm/min) >50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23oC 4 kJ/m2 ISO 179ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 90 oC ISO 75B-1, -2OpticalHaze (1mm) 40 % ASTM D1003Gloss (60o) 113 ---- ASTM D2457



Description: ″Jampilen HP540J″ is a nucleated homopolymer for extrusionand thermoforming applications.″Jampilen HP540J″ exhibits good stiffness and transparency.The main applications of ″Jampilen HP540J″ are fruit baskets,trays, transparent drinking cups and containers.″Jampilen HP540J″ is manufactured to the highest standards butspecial requirements apply to certain applications such as foodend-use contact and direct medical use.

Processing Method:ExtrusionThermoformingSolid Phase Press. Form

Features: Good stiffnessGood transparencyNucleatedHomopolymer

Typical Applications:Fruit basketsTraysTransparent drinking cups and containersHousewares


JJaammppiilleenn HHPP554400KK



MechanicalFlexural Modulus 1650 MPa ASTM D790Tensile Strength at Yield 36 MPa ASTM D638Tensile Elongation at Yield 10 % ASTM D638Izod Impact Strength (notched) at 23 oC 50 J/m ASTM D256Rockwell Hardness 105 R-Scale ASTM D785ThermalVicat softening point (10N) 155 oC ASTM D1525H.D.T. (0.46 Mpa) 114 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze 32 % ASTM D1003Gloss (45o) 65 ---- ASTM D2457



Description: ″Jampilen HP540K″ is a polypropylene homopolymerparticularly suitable for thermoforming applications. This gradeoffers high stiffness, excellent processability, good contactclarity and high gloss.″Jampilen HP540K″ is increasingly used for the extrusion ofsheet for thermoforming. It is also used for coextrudedmultilayer sheet with high barrier properties to produceretortable containers.In thermoforming, polypropylene offers some distinctadvantages over conventional materials like PVC and PS.Polypropylene gives extensive food contact credentials, a goodtoughness-stiffness balance and excellent high temperature andchemical resistance. Moreover, polypropylene offers easyrecycling and is environmentally sound.″Jampilen HP540K″ is suitable for food contact.

Processing Method: Extrusion (Sheet)Thermoforming

Features: Excellent processabilityHigh stiffnessGood contact clarityHigh glossHomopolymer

Typical Applications: Vending cupsBlister packsPots for dairy productsTrays for biscuits, chocolates and fruitsRetortable containers ( coextruded multilayer sheet with highbarrier properties)

Approval:Food




MechanicalTensile Modulus (1 mm/min) 1650 MPa ISO 527-1, -2Tensile Strenght at Yield (50 mm/min) 35 MPa ISO 527-1, -2Tensile Elongation at Yield (50 mm/min) 8 % ISO 527-1, -2Tensile Elongation at Break (50 mm/min) >50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23 °C 2.5 kJ/m2 ISO 179Ball indentation hardness (H 358/30) 78 MPa ISO 2039-1ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 95 oC ISO 75B-1, -2



Description: ″Jampilen HP548R″ is a homopolymer polypropylene forinjection molding applications bearing nucleation and antistaticadditivation.″Jampilen HP548R″ exhibits good stiffness combined withgood flowability. The main applications of ″Jampilen HP548R″are caps, closures, furniture and housewares.″Jampilen HP548R″ is suitable for food contact.


Features:

Good FlowGood stiffnessAntistatic propertiesNucleatedHomopolymer

Typical Applications: FurnitureInjection Molded Caps and ClosuresHousewaresTWIM Food ContainersOpaque containers

Approval:Food

PPCO-DS-23/07 Apr 17




MechanicalFlexural Modulus 1400 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 9 % ASTM D638Izod Impact Strength (notched) at 23 oC 50 J/m ASTM D256

ThermalVicat softening point (10N) 152 oC ASTM D1525H.D.T. (0.46 MPa) 84 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012



Description: ″Jampilen HP550J″ is a polypropylene homopolymerparticularly suitable for the extrusion of sheet forthermoforming, film yarn and monofilament. This gradecombines suitable processability with good mechanicalproperties.″Jampilen HP550J″ is designed for the production of films thatcan be converted into stretched tapes for weaving applications.Textile film yarns with a denier count of not more than 1100 to1200 are used for the production of carpet backings, bags,industrial fabrics, mats and artificial grass. Film yarn with adenier count ranging from 3000 to 28000 is used for balertwines, packaging twines and ropes.″Jampilen HP550J″ is suitable for food contact.

Processing Method: Extrusion (film, yarn, monofilament, sheet)Thermoforming


Typical Applications: Stiff sheet for high quality thermoformings such as vendingcups, packaging for dairy products and trays for fruit, biscuitsand chocolatesFilm yarn, raffia, tapes, strappingCarpet backings, bags, industrial fabrics, matsArtificial grassBaler twines, packaging twines and ropesBrush and broom filling and technical applicationsNets for various purposes

Approval:Food




PhysicalMelt Flow Rate (230 oC, 2.16kg) 3.2 g/10min ASTM D 1238Density 0.9 g/cm3 ASTM D 1505

MechanicalFlexural Modulus 1550 MPa ASTM D 790Tensile Strength at Yield 35 MPa ASTM D 638

Tensile Elongation at Yield 12 % ASTM D 638Izod Impact Strength (notched) at 23 oC 55 J/m ASTM D 256Rockwell Hardness 102 R-scale ASTM D 785

ThermalVicat softening point (10N) 156 oC ASTM D 1525H.D.T. (0.46 Mpa) 94 oC ASTM D 648Accelerated oven ageing in air at 150 oC 360 hours ASTM D 3012



Description:″Jampilen HP552J″ is a polypropylene homopolymer for theproduction of film yarn and monofilament and featuresoutstanding processability and low water carry-over properties.″Jampilen HP552J″ is particularly suitable for the high speedextrusion of film yarn for industrial fabrics, heavy duty bags,ropes and twines. The product is also suitable for theproduction of water-quenched blown film and monofilament.″Jampilen HP552J″ is suitable for food contact.

Processing Method: Extrusion (Film yarn, monofilament)Water-quenched blown film

Features: Good processabilityLow water carry-overHomopolymer

Typical Applications: Film yarn for industrial fabrics, heavy duty bagsRopes and twinesBlown film packaging

Approval:Food




MechanicalTensile Modulus 1500 MPa ISO 527-1, -2Tensile Strength at Yield 33 MPa ISO 527-1, -2Tensile Elongation at Yield 11 % ISO 527-1, -2Tensile Elongation at Break >50 % ISO 527-1, -2ThermalVicat softening point A50 153 oC ISO 306H.D.T. B (0.45 MPa) 97 oC ISO 75B-1, -2

No. 5, North-Falamak St., Eyvanak Blvd., Farahzadi Blvd., Shahrak-e-Qods., Tehran, 1467715171, Iran.Tel: +9821-84286, Fax: +9821-88563100

Email: [email protected]


Description: ″Jampilen HP552N″ is a homopolymer suited for extrusionapplications. It is formulated with an antigasfading stabilizationpackage. ″Jampilen HP552N″ is used in the production ofcontinuous filaments and fine denier staple fibers. Typicalapplications are carpets and nonwovens.

Processing Method: Fiber extrusion (Continuous Filament, Staple fiber)Staple fiberCast Film

Features: Gas-fading ResistantHomopolymer

Typical Applications:Nonwoven staple fibersStaple fiberFilament yarnHygiene nonwovenWipes, tissuesCast film





MechanicalFlexural Modulus 1400 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 8 % ASTM D638Izod Impact Strength (notched) at 23 oC 20 J/m ASTM D256ThermalVicat softening point (10N) 152 oC ASTM D1525H.D.T. (0.46 MPa) 84 oC ASTM D648Accelerated oven ageing in air at 150 oC 150 hours ASTM D3012



Description:

″Jampilen HP552R″ is a high melt flow homopolymer for theproduction of CF, BCF and fine denier staple fibers at mediumto high spinning speeds and exhibits excellent antigasfadingproperties.″Jampilen HP552R″ is suitable for nonwoven fabrics fordiapers, medical-sanitary applications and wipes. Anothertypical application is high tenacity continuous filament forstraps for backpacks, sport bags, bulk bags and safety belts.Continuous filament with medium tenacity is used forupholstery and sportswear. ″Jampilen HP552R″ is also suitedfor the production of bulked continuous filament for carpets.″Jampilen HP552R″ is suitable for food contact.

Processing Method: Fiber Extrusion (CF, BCF, staple)Injection molding

Features:High melt flowExcellent antigasfading propertiesGood processabilityHomopolymer

Typical Applications:Wipes and tissuesStraps for backpacks, sport bags, bulk bags and for safety beltsUpholstery and sportswearBulk continuous filament for carpetsNonwoven staple fiberInjection molded articles, housewares, etc

Approval:Food








Description:″Jampilen HP554N″ is a polypropylene homopolymer designedfor the production of fine denier staple fibers for nonwoven,thermobonded fabrics and offers outstanding spinnability,superior thermobonding and excellent antigasfading properties.Fabrics made with ″Jampilen HP554N″ are characterized bysoftness, textile-like appearance and high tear resistance.In comparison with standard polypropylene types forthermobonding applications, ″Jampilen HP554N″ offers somedistinct advantages:

- The processability with the long-spinning technology isoutstanding, resulting in high and uniform fiber quality andless down-time,- A broad thermal bonding window is achieved, whichfacilitates start-up and adjustments of the plant, and- It shows a 20 to 30 % increase in thermal bonding ability.This makes it possible to produce fabrics with a higher tearstrength or with a lower weight per square meter for the samestrength.

Processing Method:Fiber Extrusion

Features: Good spinnabilitySuperior thermobonding propertiesExcellent antigasfading propertiesHigh tear resistanceHomopolymer

Typical Applications: Fabrics for feminine care products, diapers, incontinence pads,medical disposables, wipes and other applications in thehygienic and medical sectorFilters and fabrics for the automotive, clothing and furnitureindustryFine denier staple fiber








Description: ″Jampilen HP554P″ is a high Fluidity polypropylenehomopolymer for the production of fine denier staple fiber withimproved thermo-bonding ability for nonwoven fabrics. Theproduct exhibits excellent antigasfading properties.″Jampilen HP554P″ offers outstanding process stability andspinning behavior on short-spinning lines and some specificlong-spinning lines. The thermal-bonding ability is high andallows the production of nonwoven fabrics with higher tearstrength or with lower weight per square meter for the samestrength.The fabrics made with ″Jampilen HP554P″ are characterizedby softness, textile-like appearance and high tear resistance.The typical applications are overstock for diapers, femininecare products, thermal-bonded nonwovens and incontinencepads. Other applications are wipes, filters and fabrics for theclothing and furniture industry.

Processing Method:Fiber Extrusion (CF, Staple)

Features: Good spinnabilityHigh thermobonding propertiesExcellent antigasfading propertiesHigh tear resistanceGood heat sealHomopolymer

Typical Applications: Nonwoven staple fibersOverstock for diapersFeminine care productsIncontinence padsFilters and fabrics for the clothing and furniture industryFine denier filaments for Carpet face yarnMultifilament yarns




PhysicalMelt Flow Rate (230 oC, 2.16kg) 12 g/10min ASTM D 1238Density 0.9 g/cm3 ASTM D 1505

MechanicalFlexural Modulus 1550 MPa ASTM D 790

Tensile Strength at Yield 34 MPa ASTM D 638

Tensile Elongation at Yield 12 % ASTM D 638Izod Impact Strength (notched) at 23 oC 30 J/m ASTM D 256Rockwell Hardness 102 R-Scale ASTM D 785




Description: ″Jampilen HP557N″ is a medium fluidity homopolymerdesigned for the production of staple fibers and exhibitsexcellent antigasfading properties.″Jampilen HP557N″ offers high process stability and goodthermal-bonding ability. This grade is mainly used for theproduction of staple fibers for nonwoven fabrics for femininecare products, diapers, medical disposables, wipes, filters andlinings.″Jampilen HP557N″ is suitable for food contact.

Processing Method:Fiber Extrusion (Staple)

Features: High process stabilityGood thermal-bonding abilityHomopolymer

Typical Applications: Staple fibers for non-woven fabricsFeminine care productsDiapersMedical disposablesWipes, filters and linings

Approval:Food




MechanicalFlexural Modulus 1350 MPa ISO 178Tensile Strength at Yield 33 MPa ISO 527-1, -2Tensile Elongation at Yield 11 % ISO 527-1, -2Tensile Elongation at Break >50 % ISO 527-1, -2ThermalVicat softening point A50 153 oC ISO 306H.D.T. B (0.45 MPa) 97 oC ISO 75B-1, -2



Description: ″Jampilen HP561R″ is a very narrow molecular weightdistribution homopolymer, suitable for extrusion applications. Itis formulated with an anti-gasfading stabilization package.″Jampilen HP561R″ is designed for the production ofcontinuous filaments. Typical applications are HTY andspunbond nonwoven.

Processing Method:Fiber Extrusion (filament)

Features:Controlled rheologyGas-fading resistantNarrow molecular weight distributionHomopolymer

Typical Applications:Bulk Continuous Filament & Continuous FilamentHTY and spunbond nonwovenFilament yarnGeotextile and agricultureHygiene nonwovenWipes, tissues


JJaammppiilleenn HHPP556611SS


MechanicalTemsile Modulus 1450 MPa ISO 527-1, -2Tensile Strength at Yield 33 MPa ISO 527-1, -2Tensile Elongation at Yield 10 % ISO 527-1, -2Tensile Elongation at Break >50 % ISO 527-1, -2ThermalVicat softening point A50 152 oC ISO 306H.D.T. B (0.45 MPa) 97 oC ISO 75B-1, -2



Description: ″Jampilen HP561S″ is a very narrow molecular weightdistribution homopolymer, suitable for extrusion applications. Itis formulated with an antigasfading stabilization package.″Jampilen HP561S″ is designed for production of continuousfilaments. Typical applications are HTY and spunbondnonwoven.

Processing Method:Fiber Extrusion (filament)

Features: Controlled rheologyGas-fading resistantNarrow molecular weight distributionHomopolymer

Typical Applications:HTY and spunbond nonwovenContinuous FilamentFilament yarnGeotextile and agricultureHygiene nonwovenWipes and tissues








Description: ″Jampilen HP562R″ is a high melt flow homopolymer withnarrow molecular weight distribution for the high speedproduction of low denier continuous filament for spun bonded,nonwoven fabrics.The major applications for spun bonded fabrics made of″Jampilen HP562R″ are diapers, medical and sanitary tissues,protective fabrics for agricultural, industrial and medicalapplications, backings and linings for the furniture, beddingand carpet industries. ″Jampilen HP562R″ can also be used forthe production of partially oriented yarn and bulked continuousfilament.″Jampilen HP562R″ is suitable for food contact.

Processing Method:Fiber Extrusion (CF)

Features: High melt flowNarrow molecular weight distributionHomopolymer

Typical Applications: Spunbonded, nonwoven fabricsDiapers, medical and sanitary tissuesProtective fabrics for agricultural, industrial and medicalapplicationsBackings and linings for the furniture, bedding and carpetindustriesOriented yarn and bulked continuous filament

Approval:Food




PhysicalMelt Flow Rate (230 oC, 2.16kg) 35 g/10min ASTM D 1238Density 0.9 g/cm3 ASTM D 1505

MechanicalFlexural Modulus 1450 MPa ASTM D 790Tensile Strength at Yield 32 MPa ASTM D 638

Tensile Elongation at Yield 10 % ASTM D 638Izod Impact Strength (notched) at 23 oC 30 J/m ASTM D 256Rockwell Hardness 100 R-Scale ASTM D 785




Description:″Jampilen HP562S″ is a very high fluidity homopolymer forthe high speed production of very low denier BCF and CF.″Jampilen HP562S″ exhibits excellent antigasfading propertiesand due to its high homogeneity and very high MFR, it offersstable extrusion and excellent processability on both short andlong spinning lines. This grade allows a high stretch ratio andgives tough, resilient and colourfast fibres.″Jampilen HP562S″ is eminently used for the high speedproduction of bulked continuous filament for carpet face yarns.Another major application is the production of high tenacitycontinuous filament for straps for backpacks, handles for bigbags and safety belts. Continuous filament with mediumtenacity is used for upholstery and heavy duty clothing.″Jampilen HP562S″ is suitable for food contact.

Processing Method:Extrusion (BCF, CF)

Features: High process stabilityExcellent antigasfading propertiesExcellent processabilityHomopolymer

Typical Applications: BCF for carpet face yarnsHigh tenacity CF for straps for backpacksHandles for big bags and safety beltsUpholstery and heavy duty clothing

Approval:Food

PPCO-DS-128/02 Apr 17




MechanicalFlexural Modulus 1400 MPa ASTM D790Tensile Strength at Yield 32 MPa ASTM D638Tensile Elongation at Yield 8 % ASTM D638Izod Impact Strength (notched) at 23 oC 30 J/m ASTM D256ThermalVicat softening point (10N) 152 oC ASTM D1525H.D.T. (0.46 MPa) 84 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012

No. 5, North-Falamak St., Eyvanak Blvd., Farahzadi Blvd., Shahrak-e-Qods., Tehran, 1467715171, Iran.Tel: +9821-84286, Fax: +9821-88563100Email: [email protected] data and information is considered to be correct and offered in good faith as a guide. But we do not warrant or otherwise guarantee themerchantability, fitness for a particular purpose or suitability of this information, products or processes described.

Description: ″Jampilen HP564S″ is a high melt flow rate homopolymer witha narrow molecular weight distribution for the high speedproduction of low denier continuous filament for spunbonded,nonwoven fabrics with an excellent balance of mechanicalproperties and softness. This grade is formulated with an anti-gasfading stabilization package and characterized by consistenthigh speed and low nonwoven weights. The major applicationsfor spunbonded fabrics made of ″Jampilen HP564S″ arediapers, medical and sanitary tissues, protective fabrics foragricultural, industrial and medical applications, backings andlinings for the furniture and carpet industries. This grade canalso be used for the production of partially oriented yarn andbulked continuous filament. ″Jampilen HP564S″ is suitable forfood contact.

Processing Method:Extrusion (Filament)Fiber Spinning

Features:High melt flowNarrow molecular weight distributionEasy processabilityGasfading resistantHomopolymer

Typical Applications:

Spunbonded, nonwoven fabricsFabrics for diapers, feminine care, medical and sanitary tissuesProtective fabrics for agricultural, industrial and medicalapplicationsBackings and linings for the furniture and carpet industriesOriented yarn and bulked continuous filamentWipe and Tissues

Approval:Food








Description: ″Jampilen HP565S″ is a high melt flow rate homopolymer witha narrow molecular weight distribution for the high speedproduction of low denier continuous filament for spunbonded,nonwoven fabrics. The major applications for spunbondedfabrics made of ″Jampilen HP565S″ are diapers, medical andsanitary tissues, protective fabrics for agricultural, industrialand medical applications, backings and linings for the furnitureand carpet industries. This grade can also be used for theproduction of partially oriented yarn and bulked continuousfilament. ″Jampilen HP565S″ is suitable for food contact.

Processing Method:Fiber Extrusion (CF, BCF)

Features: High melt flowNarrow molecular weight distributionHomopolymer

Typical Applications:Spunbonded, nonwoven fabricsFabrics for diapers, medical and sanitary tissuesProtective fabrics for agricultural, industrial and medicalapplicationsBackings and linings for the furniture and carpet industriesOriented yarn and bulked continuous filament

Approval:Food




MechanicalTensile Modulus (1 mm/min) 1500 MPa ISO 527-1, -2Tensile strength at Yield (50 mm/min) 34 MPa ISO 527-1, -2Tensile elongation at Yield (50 mm/min) 11 % ISO 527-1, -2Tensile elongation at Break (50 mm/min) 410 % ISO 527-1, -2Shore hardness (Shore D) 71 ---- ISO 868ThermalVicat softening point A50 152 oC ISO 306H.D.T. B (0.45 MPa) 93 oC ISO 75B-1, -2



Description: ″Jampilen HP593H″ is a new generation polypropylenehomopolymer designed for the production of biaxially orientedpolypropylene films (BOPP) on high speed BOPP lines and ischaracterised by its very broad processing window, easy filmstrechability, good optical properties and stable film thicknessprofile.″Jampilen HP593H″ is suitable for metallizable film, both asmonolayer and in coextruded structures. ″Jampilen HP593H″ isfree of any slip, antiblock agents, Irgafos 168 and CalciumStearate. Typical applications are BOPP packaging films.″Jampilen HP593H″ is suitable for food contact.

Processing Method:BOPP filmThermoforming

Features:High clarityHigh glossGood optical properiesHomopolymer

Typical Applications:BOPP packagingFood packaging films

Approval:Food





MechanicalFlexural Modulus 1750 MPa ASTM D790Tensile Strength at Yield (2 in./min) 37 MPa ASTM D638Tensile Elongation at Yield 9 % ASTM D638Izod Impact Strength (notched) at 23 oC 37 J/m ASTM D256Rockwell Hardness 110 R-Scale ASTM D785ThermalVicat softening point (10N) 155 oC ASTM D1525H.D.T. (0.46 Mpa) 114 oC ASTM D648Accelerated oven ageing in air at 150 oC 360 hours ASTM D3012OpticalHaze 32 % ASTM D1003Gloss 65 ---- ASTM D2457



Description: ″Jampilen HP640H″ is a polypropylene homopolymerspecifically designed for thermoforming application and offersa very high stiffness, excellent contact clarity, high gloss andgood antistatic properties.″Jampilen HP640H″ allows stable, clean and easy processing.Besides excellent optical properties, this grade also offersexcellent organoleptic properties and a good stiffness-impactbalance. The high temperature resistance allows using thisproduct for hot fill applications. ″Jampilen HP640H″ is suitablefor food contact.

Processing Method: Extrusion (Sheet)Thermoforming

Features: Good stiffness/impact balanceExcellent contact clarity and high glossGood antistatic propertiesExcellent optical and organoleptic propertiesLow warpageGood processing stabilityHomopolymer

Typical Applications: Hot fill applicationsVending cupsBlister packsPots for dairy productsTrays for biscuits, chocolates and fruitsClear containers

Approval:Food








Description:″Jampilen HP648S″ is a high melt flow homopolymer with anarrow molecular weight distribution. ″Jampilen HP648S″ isdesigned for the high speed injection molding of thin-walleditems with a good transparency and optimum antistaticproperties. Due to its outstanding flow properties, its very highstiffness and excellent dimensional stability, this grade can bemolded at very high speeds producing thin-walled parts, evenwith complicated shapes, without distortion.In many of applications ″Jampilen HP648S″ can replacetraditional materials such as polystyrene since the productexhibits excellent processability, low residual stress, lowshrinkage and warpage on top of the advantages typical ofpolypropylene such as light weight, low odour transfer, highchemical resistance and a good balance of mechanicalproperties.


Features:High melt flowNarrow molecular weight distributionGood transparencyVery high stiffnessExcellent dimensional stabilityHomopolymer

Typical Applications: Thin-walled packaging in the cosmetic and food industryPensCD and DVD boxesCaps and closuresSmall appliances such as coffee machines and food processorsOffice accessories, disposable razors and camping articles


JJaammppiilleenn HHPP664488TT


MechanicalTensile Modulus (1 mm/min) 1600 MPa ISO 527-1, -2Tensile Strenght at Yield (50 mm/min) 35 MPa ISO 527-1, -2Tensile Elongation at Yield (50 mm/min) 8 % ISO 527-1, -2Tensile Elongation at Break (50 mm/min) 50 % ISO 527-1, -2Charpy impact strength (Notch A) at 23 °C 2 kJ/m2 ISO 179Ball indentation hardness (H 358/30) 80 MPa ISO 2039-1ThermalVicat softening point A50 154 oC ISO 306H.D.T. B (0.45 MPa) 95 oC ISO 75B-1, -2



Description: ″Jampilen HP648T″ is a homopolymer polypropylene forinjection molding applications bearing nucleation and antistaticadditivation.″Jampilen HP648T″ exhibits very good flowability and goodstiffness. The main applications of ″Jampilen HP648T″ are thinwalled injection molding applications especially in dairy andother food packaging products.″Jampilen HP648T″ is suitable for food contact.


Features:Good FlowGood stiffnessAntistatic propertiesNucleatedHomopolymer

Typical Applications:HousewaresTWIM Food ContainersDairy and other food packagingOpaque containers

Approval:Food








Description: ″Jampilen HP502R″ is a high melt flow homopolymer for theproduction of low denier BCF, CF and staple fibers at mediumto high spinning speeds. ″Jampilen HP502R″ offers highhomogeneity, stable extrusion and excellent processability onboth short and long spinning lines. This grade allows highstretch ratio and gives tough and resilient fibers.″Jampilen HP502R″ is widely used for the production ofbulked continuous filament for carpet face yarns. Anothermajor application is the production of high tenacity continuousfilament for straps for backpacks, handles for big bags andsafety belts. Continuous filament with medium tenacity is usedfor upholstery, sportswear and heavy duty clothing.″Jampilen HP502R″ is also suitable for the production of lowdenier staple fibres for the thermobonding.″Jampilen HP502R″ is suitable for food contact.

Processing Method:Fiber Extrusion (BCF, CF, staple)

Features: High melt flowExcellent processabilityStable processingHomopolymer

Typical Applications: Bulked continuous filament for carpet face yarnsHigh tenacity continuous filament for straps for backpacksHandles for big bags and safety beltsUpholstery, sportswear and heavy duty clothingLow denier staple fibers for thermobonding

Approval:Food