SX-2M1 Halogen Free Flame Retardant Cable Compounds Product Information:

SX-2M1 is thermoplastic, flame retardant and halogen free compound on polyolefinic basis. It can be used for production of energy, signal and control cables.

Properties of this compound comply with the requirements of EN 50363-0 type M1, EN 50363-7 type TI6, EN 50363-8 type TM7, EN 50290-2-27, VDE 0207 Part 24 type HM2, VDE 0207 Part 23 type HJ2, VDE 0250 Part 215 type HM5, BS 7655 type LTS1 & LTS3, IEC 60092-359 type SHF1, IEC 60502 ST8.

Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 9 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,51 Hardness ISO 868 Shore D 47 Mechanical Properties Tensile Strength ISO 527 Mpa 13 Elongation at Breake ISO 527 % 180 Heat Ageing (100 °C, 168 h) DIN VDE 027 ∆ Strength % -30a)

∆ Elongation % ±40 Heat Ageing (100 °C, 240 h) IEC 60811 ∆ Strength % ±10 ∆ Elongation % -24 Tear Strength ASTM D 1938 N/mm 8 Chemical Properties Halogen Content EN 50267-2-1 % <0,5 Max. pH EN 50267-2-2/IEC 60754-2 - >4.3 Conductivity EN 50267-2-2/IEC 60754-2 µS/mm <10 Hot Pressure Test at 80 °C IEC 60811 % <50 Cold Flex ISO 458-2 °C -18±2 Cold Bend (-15 °C±2 °C) BS 7655-6.1 - No Cracks Cold Elongation (-15 °C±2 °C) BS 7655-6.1 - 30 Min. Cold Impact (-15 °C±2 °C) BS 7655-6.1 - Pass Water Absorption IEC 60811 mg/cm2 <5.0 LOI ISO 4589 % 37 Smoke Density EN-61034 % trasmittance >80 Volume Resistivity 20 °C (Alternating Polarity Method) ASTM D257 Electrodes Ω.cm 1.1015

Other Properties Oil IRM 902 oil (50 °C, 72 h) IEC 60811-2-1 ∆ Strength % 15 ∆ Elongation % 7 Oil IRM 902 oil (70 °C, 6 h) IEC 60811-2-1 ∆ Strength % 20 ∆ Elongation % 10

a) Any upper limit is determined Processing: Extrusion Temperatures: 115 °C – 125 °C – 130 °C – 135°C – 145°C – 155 °C Packaging: It is packaged as 1250 kg in octabin.




SX-2E1 Halogen Free Flame Retardant Cable Compounds Product Information: SX-2E1 is thermoplastic, flame retardant and halogen free compound on polyolefinic basis. It can be used for production of energy, signal and control cables.


Product Data:











Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 5±1 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,46±0,01 Hardness ISO 868 Shore D 47 Mechanical Properties Tensile Strength ISO 527 Mpa 12 Elongation at Breake ISO 527 % 175 Heat Ageing (100 °C, 168 h) DIN VDE 027 ∆ Strength % -30a)









Product Data:










Product Data:











Product Data:










Product Data:








SX-2K5 FLEX Halogen Free Flame Retardant Cable Compounds

Product Information:

SX-2K5 FLEX is thermoplastic, flame retardant and halogen free compound on polyolefinic basis. It can be used for production of energy, signal and control cables.

Properties of this compound comply with the requirements of VDE 0207 Part 24 type HM2, EN 50363-8 type TM7, EN 50363-7 type TI6.

Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 4±1 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,46±0,01 Hardness ISO 868 Shore D 42 Mechanical Properties Tensile Strength ISO 527 Mpa 14 Elongation at Break ISO 527 % 240 Heat Ageing (100 °C, 168 h) DIN VDE 027 ∆ Strength % -30a)



a) Any upper limit is determined. Processing: Extrusion Temperatures: 115 °C – 120 °C – 125 °C – 130 °C – 135°C – 145°C Packaging: It is packaged as 1250 kg in octabin.






Product Data:








SX-FR03 Halogen Free Flame Retardant Cable Compounds

Product Information: SX-FR03 is a low smoke zero halogen (LSZH), UV stabilised. It is natural jacketing compound combining with extrusion properties. This product designed for jacket for 90 °C installation cables and 1Kv voltage cables. SX-FR03 is based on the element Carbon, Hydrogen, Oxygen, Silicon and Calcium. Therfore, this product will be the significant constituents of the combustion gases. The properties of this compound comply with the requirements EN 50363—8 TM7, VDE 0207 Teil 24 (HM2, HM4 & HM5), BS 7655 LTS1-4 Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (190°C-2,16 kg) ASTM D 1238-10 gr/10 min 0,8 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,18 Hardness ISO 868 Shore A 39 Mechanical Properties Tensile Strength ISO 527 Mpa 12 Elongation at Break ISO 527 % 550 Heat Ageing (100 °C, 240 h) IEC 60811 ∆ Strength % < 20

∆ Elongation % < 20 Chemical Properties Halogen Content EN 50267 % <0,5 Max. pH EN 50267-2-2/IEC 60754-2 - 5,3 Conductivity EN 50267-2-2/IEC 60754-2 µS/mm 1,5 Hot Pressure Test (240 h, 100 °C) IEC 60811 % 19 Cold Bend(-40 °C) IEC 60811-1-4 PASS Cold Impact (-40°C) IEC 60811-1-4 PASS Water Absorption (100 °C, 24h) IEC 60811 mg/cm2 0,11 LOI ISO 4589 % 31 Volume Resistivity IEC 60093 PΩ.cm 45 Dielectric Strenght IEC 60243 Kv/mm >20

Processing: 115°C – 120 °C – 125°C – 130 °C – 135 °C – 140 °C – 145°C Packaging: It is packaged as 1000 kg in octabin. Storage&Handling: SX-FR03 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:








SX-4VV Halogen Free Flame Retardant Cable Compounds Product Information: SX-4VV is thermoplastic halogen free, flame retardant and low smoke emission compound, for cable insulation and sheating. It can be used for the production of energy, signal and control cables. The properties of this compound comply with the requirements of EN 50363-0 type M1, EN 50363-7 type TI7, IEC 60502 ST8, VDE 0207 Part 24 type HM2-HM4, BS 7655 type LTS1 – LTS2 & LTS3 – LTS4, EN 50290-2-27, UNE 21123-4:2010 – ANNEX A-Table1 type DMZ-E, IEC 60092-359 type SHF1. Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 5,5±1 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,47±0,01 Hardness ISO 868 Shore D 48 Mechanical Properties Tensile Strength ISO 527 Mpa 12 Elongation at Break ISO 527 % 185 Heat Ageing (110 °C, 168 h) IEC 60811 ∆ Strength % -30a)

∆ Elongation % ±40 Heat Ageing (100 °C, 240 h) IEC 60811 ∆ Strength % ±3 ∆ Elongation % -20 Tear Strength ASTM D 1938 N/mm 10 Chemical Properties Halogen Content EN 50267 % <0,5 Max. pH EN 50267-2-2/IEC 60754-2 - >4.3 Conductivity EN 50267-2-2/IEC 60754-2 µS/mm <10 Hot Pressure Test (80 °C) IEC 60811 % <50 Cold Flex ISO 458-2 °C -18±2 Cold Bend (-15 °C±2 °C) BS 7655-6.1 - No Cracks Cold Elongation (-15 °C±2 °C) BS 7655-6.1 - 30 Min. Cold Impact (-15 °C±2 °C) BS 7655-6.1 - Pass Water Absorption IEC 60811 mg/cm2 <5.0 LOI ISO 4589 % 40 Smoke Density EN-61034 % trasmittance >80 Volume Resistivity 20 °C (Alternating Polarity Method) ASTM D257 Electrodes Ω.cm 1.1015 Other Properties Oil IRM 902 oil (50 °C, 72 h) IEC 60811-2-1 ∆ Strength % 5 ∆ Elongation % 10 Oil IRM 902 oil (70 °C, 6 h) IEC 60811-2-1 ∆ Strength % 10 ∆ Elongation % 15 Water Immersion Test (70 °C, 4 h) BS:7655-6.1 ∆ Strength % 30 Max. ∆ Elongation % 30 Max.

a) Any upper limit is determined. Processing: Extrusion Temperatures: 115°C – 125°C – 135 °C – 145 °C – 155°C Packaging: It is packaged as 1250 kg in octabin.






Product Data:








SX-4VUV Halogen Free Flame Retardant Cable Compounds Product Information: SX-4VUV is thermoplastic halogen free, flame retardant and low smoke emission compound with UV resistance for cable insulation and sheating. It can be used for the production of energy, signal and control cables. The properties of this compound comply with the requirements of EN 50363-0 type M1, EN 50363-7 type TI7, IEC 60502 ST8, VDE 0207 Part 24 type HM2-HM4, BS 7655 type LTS1 – LTS2 & LTS3 – LTS4, EN 50290-2-27, UNE 21123-4:2010 – ANNEX A-Table1 type DMZ-E, IEC 60092-359 type SHF1. Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 5±1 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,47±0,01 Hardness ISO 868 Shore D 47 Mechanical Properties Tensile Strength ISO 527 Mpa 13 Elongation at Break ISO 527 % 185 Heat Ageing (110 °C, 168 h) IEC 60811 ∆ Strength % -30a)

∆ Elongation % ±40 Heat Ageing (100 °C, 240 h) IEC 60811 ∆ Strength % ±3 ∆ Elongation % -20 Tear Strength ASTM D 1938 N/mm 10 Chemical Properties Halogen Content EN 50267 % <0,5 Max. pH EN 50267-2-2/IEC 60754-2 - >4.3 Conductivity EN 50267-2-2/IEC 60754-2 µS/mm <10 Hot Pressure Test (80 °C) IEC 60811 % <50 Cold Flex ISO 458-2 °C -18±2 Cold Bend (-15 °C±2 °C) BS 7655-6.1 - No Cracks Cold Elongation (-15 °C±2 °C) BS 7655-6.1 - 30 Min. Cold Impact (-15 °C±2 °C) BS 7655-6.1 - Pass Water Absorption IEC 60811 mg/cm2 <5.0 LOI ISO 4589 % 40 Smoke Density EN-61034 % trasmittance >80 Volume Resistivity 20 °C (Alternating Polarity Method) ASTM D257 Electrodes Ω.cm 1.1015 Other Properties Oil IRM 902 oil (50 °C, 72 h) IEC 60811-2-1 ∆ Strength % 5 ∆ Elongation % 10 Oil IRM 902 oil (70 °C, 6 h) IEC 60811-2-1 ∆ Strength % 10 ∆ Elongation % 15 Water Immersion Test (70 °C, 168 h) BS:7655-6.1 ∆ Strength % 11 ∆ Elongation % 3

a) Any upper limit is determined. Processing: Extrusion Temperatures: 115°C – 125°C – 135 °C – 145 °C – 155°C Packaging: It is packaged as 1250 kg in octabin.







Product Data:










Product Data:








SX-4N Halogen Free Flame Retardant Cable Compounds

Product Information: SX-4N is thermoplastic halogen free, flame retardant and low smoke emission compound, for cable insulation and sheating. It can be used for the production of energy, signal and control cables. The properties of this compound comply with the requirements of EN 50363-0 type M1, EN 50363-7 type TI7, IEC 60502 ST8, VDE 0207 Part 24 type HM2-HM4, BS 7655 type LTS1 – LTS2 & LTS3 – LTS4, EN 50290-2-27, UNE 21123-4:2010 – ANNEX A-Table1 type DMZ-E, IEC 60092-359 type SHF1. Product Data:

Property Test Method Unit Value Phisical Properties Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 5 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,47 Hardness ISO 868 Shore D 47 Mechanical Properties Tensile Strength ISO 527 Mpa 12 Elongation at Break ISO 527 % 190 Heat Ageing (110 °C, 168 h) IEC 60811 ∆ Strength % -30a)

∆ Elongation % ±40 Tear Strength ASTM D 1938 N/mm 8 Chemical Properties Halogen Content EN 50267 % <0,5 Max. pH EN 50267-2-2/IEC 60754-2 - >4.3 Conductivity EN 50267-2-2/IEC 60754-2 µS/mm <10 Hot Pressure Test (80 °C) IEC 60811 % <50 Cold Flex ISO 458-2 °C -18±2 Cold Bend (-15 °C±2 °C) BS 7655-6.1 - No Cracks Cold Elongation (-15 °C±2 °C) BS 7655-6.1 - 30 Min. Cold Impact (-15 °C±2 °C) BS 7655-6.1 - Pass Water Absorption IEC 60811 mg/cm2 <5.0 LOI ISO 4589 % 39 Smoke Density EN-61034 % trasmittance >80 Volume Resistivity 20 °C (Alternating Polarity Method) ASTM D257 Electrodes Ω.cm 1.1015 Other Properties Oil IRM 902 oil (50 °C, 72 h) IEC 60811-2-1 ∆ Strength % 5 ∆ Elongation % 10 Oil IRM 902 oil (70 °C, 6 h) IEC 60811-2-1 ∆ Strength % 10 ∆ Elongation % 15

a) Any upper limit is determined. Processing: 115°C – 125°C – 135 °C – 145°C – 155°C Packaging: It is packaged as 1250 kg in bigbag or octabin.






Product Data:










Product Data:











Product Data:










Product Data:





KABKOM KİMYA SANAYİ VE TİCARET A.Ş. Barbaros Mah. Dereboyu Cad. Ahlat Sk. Varyap Meridian E 1 Blok K:30 D:185 Ataşehir, İstanbul/TURKEY

Tel: +90 216 540 48 66 (pbx), Fax: +90 216 540 48 65 www.kabkom.com.tr [email protected]

SX-8450-LBK LLDPE Black Jacketing Compounds

Product Information: SX-8450-LBK is a black LLDPE compund it has broad molecular weight disturibitation. Which provides excellent processability, excellent environmental stress crack resistance, free ofdie drool and excellent physical toughness. SX-8450-LBK contains 2,5 % well-dispersed carbon black. It i designed for jacketing of energy and communication cables. The proparties of this compound comply with the requrements ASTM D 1248 Type 1, Class C, Category 4, Grade E4, E5, J3, W2, W3, W4, ISO 1872-PE, KCHL, 23-D012, BS6234:Type H03C, TS2, IEC 60502:ST3, ST7, IEC 60540:ST3, ST7, ICEA:S-61-402, S-84-608-1988, Telcordia:GR-421, ANSI:C8-35. Product Data:

Packaging: It is packaged as 1000 kg in octabin. Processing: Extrusion Temperatures: 180 °C – 190 °C – 200 °C – 210°C – 220°C – 230 °C Storage&Handling: Shelf life 90 day. SX-8450-LBK should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.

Property Test Method Unit Value Phisical Properties Melt Flow Rate (190°C-2,16 kg) ASTM D1238 gr/10 min Max. 1 Spesific Weight (23°C) ASTM D1505 gr/cm³ 0,935±0,005 Hardness ASTM D2240 Shore D 49 Mechanical Properties Tensile Strength ASTM D638 kg/cm2 Min 20 Elongation at Break ASTM D638 % Min 900 Heat Ageing (110 °C, 10 d) ASTM D638 ∆ Elongation at Break % Min 300 ESCR (F0, 50 °C, 10% Igepal) ASTM D1693 hrs > 1000 Electrical Properties DC Volume Resistivity IEC 60093 Ω.cm 1.1015 Dielectric Strength (2 mm thickness) IEC 60243 kV/mm Min 20 Dielectric Constant @ 1 MHz ASTM D150 - Max 2,3 Dissipation Factor @ 1 MHz ASTM D150 - Max 0,005 Thermal Properties Brittleness Temperature ASTM D746 ᵒC <-70






Product Data:







SX-8450-HBK HDPE Black Jacketing Compounds

Product Information: SX-8450-HBK is a black HDPE compund it has broad molecular weight disturibitation. Which provides excellent processability, excellent environmental stress crack resistance, free ofdie drool and excellent physical toughness. SX-8450-HBK contains 2,5 % well-dispersed carbon black. It i designed for jacketing of energy and communication cables. The proparties of this compound comply with the requrements ASTM D 1248 Type 1, Class C, Category 4, Grade E4, E5, J3, W2, W3, W4, ISO 1872-PE, KCHL, 23-D012, BS6234:Type H03C, TS2, IEC 60502:ST3, ST7, IEC 60540:ST3, ST7, ICEA:S-61-402, S-84-608-1988, Telcordia:GR-421, ANSI:C8-35. Product Data:

Packaging: It is packaged as 1000 kg in octabin. Processing: Extrusion Temperatures: 180 °C – 190 °C – 200 °C – 220°C – 230°C Storage&Handling: Shelf life 90 day. SX-8450-HBK should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.

Property Test Method Unit Value Phisical Properties Melt Flow Rate (190°C-2,16 kg) ASTM D1238 gr/10 min Max. 0,3 Spesific Weight (23°C) ASTM D1505 gr/cm³ 0,949±0,01 Hardness ASTM D2240 Shore D 60±1 Carbon Black Content ASTM D1603 wt% 2,5 Carbon Black Dispersion ISO 18553 - Max 2,5 Mechanical Properties Tensile Strength ASTM D638 kg/cm2 Min 25 Elongation at Break ASTM D638 % Min 900 Heat Ageing (110 °C, 10 d) ASTM D638 ∆ Elongation at Break % Min 500 ESCR (F0, 50 °C, 10% Igepal) ASTM D1693 hrs > 5000 Oxidative Induction Time (200°C, Al) ASTM D3895 min Min 30 Chemical Properties Hot Pressure Test at 110 °C IEC 60811 % <50 Water Absorption IEC 60811 mg/cm² ≤0,01 Volume Resistivity 20 °C (Alternating Polarity Method) ASTM D257 Electrodes Ω.cm 1.1015 Thermal Properties Vicat Softening Temperature ISO 306 ᵒC ≥115 Electrical Properties Dielectric Strength (2 mm thickness) IEC 60243 kV/mm No breakdown at 10






Product Data:





BEDDING COMPOUNDS

www.kabkom.com.tr






Product Data:







HFFR-D3 Halogen Free Flame Retardant Bedding Cable Compounds Product Information: HFFR-D3 is halogen free flame retardant bedding compound based on polyolefine resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion or tandem, high temperature level at the extruder and type of the screw.This compound is flexible and drummable also suitable for armoured cables. Product Data:

Property Test Method Unit Value

Phisical Properties

Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 90±10

Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,60±0,02

Hardness ISO 868 Shore D 43

Mechanical Properties

Tensile Strength ISO 527 Mpa 4

Elongation at Break ISO 527 % 350

LOI ISO 4589 % 31

Chemical Properties

Halogen Content EN 50267-2-1 % <0,5 Max.

Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions Processability on most HFFR/PVC/PE extrusion equipment

Processing: Extrusion Temperatures: 120°C – 130°C – 135°C – 140°C – 145°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HFFR-D3 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:







HFFR-PE30 Halogen Free Flame Retardant Bedding Cable Compounds Product Information: HFFR-PE30 is halogen free flame retardant bedding compound based on polyolefin resin. This compound is easy to process, increase the overall production rate,maintain good mechanical properties and provides better surface quality. HFFR-PE30 is designed only for tandem processing to prevent sticking to XLPE insulation without any talk usage. Product Data:


Phisical Properties

Melt Flow Rate (190°C- kg) ASTM D 1238-10 gr/10 min 80±10


Hardness ISO 868 Shore A 79±2

Moisture Content Internal Method (110°C) % <0,1

Chemical Properties


LOI ISO 4589 % 33 Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions Processability on most HFFR/PVC/PE extrusion equipment Processing: Extrusion Temperatures: 115°C – 120°C – 125°C – 130°C – 135°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HFFR-PE30 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:







HFFR-D44 Halogen Free Flame Retardant Bedding Cable Compounds

Product Information: HFFR-D44 is halogen free flame retardant bedding compound based on polyolefine resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion, high temperature level at the extruder and type of the screw.HFFR-D44 is flexible and drummable also suitable for armoured cables. Product Data:


Phisical Properties







LOI ISO 4589 % 32

Chemical Properties



Processing: Extrusion Temperatures: 120°C – 130°C – 135°C – 140°C – 145°C Storage&Handling: HFFR-D44 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:







HFFR-68B Halogen Free Flame Retardant Bedding Cable Compounds Product Information: HFFR-68B is halogen free flame retardant bedding compound based on polyolefine resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion, high temperature level at the extruder and type of the screw.HFFR-68B is specially produced for BS6724 standart. Product Data:


Phisical Properties






Elongation at Break ISO 527 % 90±10

LOI ISO 4589 % 50

Chemical Properties



Processing: Extrusion Temperatures: 100°C – 110°C – 115°C – 120°C – 125°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HFFR-68B should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:







HFFR-70C Halogen Free Flame Retardant Bedding Cable Compounds Product Information: HFFR-70C is halogen free flame retardant bedding compound based on polyolefine resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality.HFFR-70C is designed only for co-extrusion or tandem processing and help to pass Category C fire tests. Product Data:


Phisical Properties



Hardness ISO 868 Shore D 32±1


LOI ISO 4589 % 49±1

Chemical Properties



Processing: Extrusion Temperatures: 100°C – 110°C – 115°C – 120°C – 125°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HFFR-70C should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:







HFFR-76B2 Halogen Free Flame Retardant Bedding Cable Compounds

Product Information: HFFR-76B2 is halogen free flame retardant bedding compound based on polyolefine resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion, high temperature level at the extruder and type of the screw.HFFR-76B2 is flexible and drummable also usable for CPR applications. Product Data:


Phisical Properties







LOI ISO 4589 % >65

Chemical Properties


Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions High LOI Processability on most HFFR/PVC/PE extrusion equipment

Processing: Extrusion Temperatures: 100°C – 110°C – 115°C – 120°C – 125°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HFFR-76B2 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:







HFFR-86B2 Halogen Free Flame Retardant Bedding Cable Compounds Product Information: HFFR-86B2 is halogen free flame retardant bedding compound based on Polyolefin resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. HFFR-86B2 is designed only for co-extrusion processes and tandem processing.Highly recommended for B2 Class CPR applications. Product Data:


Phisical Properties



Hardness ISO 868 Shore A 81



LOI ISO 4589 % >80 Chemical Properties Halogen Content EN 50267-2-1 % Max.0,5

Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions Processability on most HFFR/PVC/PE extrusion equipment. High LOI

Processing: Extrusion Temperatures: 100°C – 110°C – 115°C – 120°C – 125°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HFFR-86B2 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:







HF-PE15 Halogen Free Bedding Cable Compounds Product Information: HF-PE15 is halogen free bedding compound based on polyolefin resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. HF-PE15 is designed only for tandem processing to prevent sticking to XLPE insulation without any talk usage. Product Data:


Phisical Properties





Chemical Properties



Processing: Extrusion Temperatures: 115°C – 120°C – 125°C – 130°C – 135°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HF-PE15 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:







HF-UNT Halogen Free Flame Retardant Bedding Cable Compounds Product Information: HF-UNT is halogen free flame retardant bedding compound based on polyolefine resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion or tandem lines, high temperature level at the extruder and type of the screw. HF-UNT is flexible and drummable compound, suitable for armoured cables. Product Data:


Phisical Properties







LOI ISO 4589 % 31

Chemical Properties



Processing: Extrusion Temperatures: 120°C – 130°C – 135°C – 140°C – 145°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HF-UNT should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:







HF-PE80 Halogen Free Bedding Cable Compounds Product Information: HF-PE80 is halogen free bedding compound based on polyolefin resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality.HF-PE15 is designed only for tandem processing to prevent sticking to XLPE insulation without any talk usage. Product Data:


Phisical Properties

Melt Flow Rate (190°C- kg) ASTM D 1238-10 gr/10 min 15±3




Chemical Properties

Halogen Content EN 50267-2-1 % <0,5 Max. Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions Processability on most HFFR/PVC/PE extrusion equipment Processing: Extrusion Temperatures: 115°C – 120°C – 125°C – 130°C – 135°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: HF-PE80 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:







HF-EPM Rubber Bedding Cable Compounds Product Information: HF-EPM is halogen free compound based on EPDM resin. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion or tandem process, low temperature level at the extruder and type of the screw. Product Data:


Phisical Properties

Resin - - EPDM






Elongation at Breake ISO 527 % 450

Chemical Properties


Special Features: Excellent processing properties. Low smoke and reduced toxic or corrosive gas emissions. Processability on most RUBBER extrusion equipment.

Processing: Extrusion Temperatures: 70°C – 80°C – 85°C – 90°C – 95°C Packaging: It is packaged as 25 kg PE bags on 1250 kg pallets. Storage&Handling: HF-EPM should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:







PE COMPOUND Bedding Cable Compounds Product Information: PE COMPOUND is bedding compound for PVC insulated and coated cable. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion and tandem, high temperature level at the extruder and type of the screw.It is designed for preventing sticking between PVC insulating and PVC jacketing. Product Data:


Phisical Properties



Hardness ISO 868 Shore D 35±2

Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions Processability on most HFFR/PVC/PE extrusion equipment Processing: Extrusion Temperatures: 115°C – 125C – 130°C – 135°C – 145°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: PE COMPOUND should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:







PE1 COMPOUND Bedding Cable Compounds Product Information: PE1 COMPOUND is bedding compound for PVC insulated and coated cable. This compound is easy to process, increase the overall production rate, maintain good mechanical properties and provides better surface quality. It can be processed without any need co-extrusion and tandem lines, high temperature level at the extruder and type of the screw.It is designed for armoured cables to prevent sticking between PVC insulating and PVC jacketing. Product Data:


Phisical Properties




Special Features: Excellent processing properties Low smoke and reduced toxic or corrosive gas emissions Processability on most HFFR/PVC/PE extrusion equipment Processing: Extrusion Temperatures: 120°C – 125°C – 130°C – 135°C – 140°C –145°C Packaging: It is packaged as 1250 kg in bigbag. Storage&Handling: PE1 COMPOUND should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:





ADDITIVES

www.kabkom.com.tr






Product Data:








FR-HC Flame Retardant Masterbatch

Product Information: FR-HC is based on a synergist brominated flame retardant compound. It is used for forming char of the compound and also it helps to improve flame retardancy properties. Because of the nano-size of the active material inside it also used for improvement agent of mechanical properties. Typical Applications: Flame retardant, char forming. For XLPE compound recommended feeding ratio: 10 – 15 % For PE compound recommended feeding ratio: 10 – 20 % For PP compound recommended feeding ratio: 10 – 15 % For PVC compound recommended feeding ratio: 5 – 10 % For HFFR compound recommended feeding ratio: 3,5 – 4,5 % Product Data

Property Test Method Unit Value Phisical Properties Carrier Resin - - LLDPE Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 25±5 Density ASTM D 792 g/cm3 1,79±0,03

Packaging: It is packaged as 25 kg in aluminum bags, 1250 kg pallets. Storage&Handling: FR-HC should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:








KK-ABSORB


KK-ABSORB is Moisture-Absorber based on a Polyethylene Resin.

Typical Applications:

KK-ABSORB is suitable for the absorption of moisture when used with recycling materials as well as for applications which are sensitive to moisture. It is also suitable for virgin materials or masterbatches contains inorganic substances based on PP, PE, PS etc.

KK-ABSORB is specially developed for the use in thin films (<50µ).

Moisture problems occur mainly after the recycling of the following materials:

DSD (Post consumer waste such as PE, PP and PS) Chalk or talc filled products LLDPE, HDPE, PP, (HI)PS, ABS, PA, PET, etc.

Recommendation of addition rate:

Recycling 1-3% Extrusion of agglomerates 2-5% Drying of highly filled Compounds 1-3% Moisture sensitive applications 1-3%

It is also used for virgin materails or masterbatches with inorganic materials

Product Data:

Property Test Method Unit Value Phisical Properties Based Resin - - LLDPE Melt Flow Rate (190°C-5 kg) ASTM D 1238-10 gr/10 min 0,5-1,2 Spesific Weight (23°C) ASTM D-792 gr/cm³ 1,85±0,02 Moisture Internal Method % ≤0,015 Ash Content ASTM D 5601-30 % 75

Packaging: It is packaged as 5 kg in aluminum bag, 25 kg boxes. Food Regulation: KK-ABSORB is suitable for food contact applications. For detailed information, please contact the Kabkom Kimya Sales Office. Storage&Handling: KK-ABSORB should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:








KK-AOX6810 Synergistic Antioxidant Masterbatch

Synergistic processing and long-term thermal stabilizer system Product Applications: KK-AOX6810 can be applied in polyolefins, such as polyethylene, polypropylene, polybutene and olefin copolymers such as ethylene-vinylacetate copolymers. Also, its use is recommended fort he processing of polymers such as polyacetals, polyamides ann polyurethanes, polyesters, PVC, styrene homo- and copolymers, ABS, elastomers such as butyl rubber (IIR), SBS, SEBS, EPM and EPDM as well other synthetic rubbers, adhesives, natural and synthetic tackifier resins and other organic substrates. Typical Applications: Usage/Addition rate : 1-5 % Product Data

Property Unit Value Phisical Properties Carrier Resin - LLDPE Density g/cm3 0,89±0,02 Total Additive Content % 20

Packaging: It is packaged as 15 kg in aluminum bags, 600 kg pallets. Storage&Handling: KK-AOX6810 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:








KK-EL670 Elastomer

Product Information: KK-EL670 is an ethylene-octene copolymer produced using metallocene polymerization catalyst and solution process technology. This resin is an excellent impact modifier for plastics and offers unique performance capabilities for compounded products. Product Applications: General purpose thermoplastic elastomers, Polymer modification Product Performance:

Improved impact strength in polypropylene Excellent filler acceptance Available as pellet form Outstanding toughness with flexible performance Reduction of product weight

Product Data:

Property Test Method Unit Value Resin Properties Melt Flow Rate (190°C-2,16 kg) ASTM D 1238-10 gr/10 min 5 Spesific Weight (23°C) ASTM D-792 gr/cm³ 0,870 Mooney viscosity, ML1+4 @121°C ASTM D 1646 °C 9 Physical Properties Tensile Strength ISO 527 Mpa 5,5 Elongation at Breake ISO 527 % >1000 Flexural Modulus, 1% ASTM D 790 Mpa 13 Hardness ASTM D 2240 Shore A 70

Tear Strength ISO 868 kN/m 38 Thermal Properties Melting Point, DSC - °C 58 Glass Transition Temperature - °C -55

Packaging: It is packaged as 25 kg in PE bags, 1250 kg pallets. Storage&Handling: KK-EL670 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:








KK-H Flame Retardant Masterbatch

Product Information: The KK-H, based on a LLDPE resin, flame retardant compound. %80 imidacloprid of the active ingredient. These active substances the synergistic effect of various flame retardant mixture. Typical Applications: It is used flame reterdant applications. Product Data

Property Test Method Unit Value Phisical Properties Carrier Resin - - LLDPE Melt Flow Rate (190°C-5 kg) ASTM D 1238-10 gr/10 min 5±1 Density ASTM D 792 g/cm3 2,23±0,03

Packaging: It is packaged as 25 kg in aluminum bags, 1250 kg pallets. Storage&Handling: KK-H should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:








KK-H1 Flame Retardant Synergist

Product Information: KK-H1 is flame retardant synergist material for PVC applications. It is also used for forming char of the PVC compound. Because of nanosize active material. It also helps improve homogenist of inorganic materials. Typical Applications: PVC 5-10% Product Data:

Property Test Method Unit Value Phisical Properties Color ASTM E 1164 / ASTM D 1003 - White Bulk Density Internal Method g/cm3 0,785 Oil Absorbtion ASTM D 1483 g 15,613

Particle Size ASTM D 7928-17 D(50) (µm) 2,356 D(97) (µm) 6,158 <2 µm (%) 39,12

Sieve(45 micron/325 mesh) ISO 787/7 % 0,479 Storage&Handling: KK-H1 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:








KK-MD1024 Metal Deactivator Masterbatch

Product Applications: KK-MD1024 was especially developed for short and long term stabilization of low voltage power cable insulation (XLPE) using silane cross-linking technologies, such as the one-step technology. The antioxidant protects the polymer against thermal degradation and the metal deactivator inhibits the catalytic degradation effect of transition metal ions. The recommended dosage depends on ageing test requirements, on the type of polyetylene and on te type of silane used. It enables the cable producer to meet the requirements of international standards. Typical Applications: Usage/Addition rate : 1-3 % Product Data

Property Unit Value Phisical Properties Carrier Resin - LLDPE Melt Flow Rate (190°C-2,16 kg) gr/10 min 1,1±0,03 Density g/cm3 0,88±0,02 Total Additive Content % 15 Thermal Stability °C 260

Packaging: It is packaged as 15 kg in aluminum bags, 600 kg pallets. Storage&Handling: KK-MD1024 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.







Product Data:










Product Data:








KK-S1142 Silicone Masterbatch

Product Information: Silicone Masterbatch KK-S1142 is a pelletized formulation contain 50% ultra high molecular weight siloxane polymer dispersed in Polyolefin resin. Suitable for all Polyolefin compatible resin system to improve the processing properties and surface quality. Compare with traditional additives like silicone oil, amide, wax etc, it’ s much more efficient for lubricity and without any migrate. Product Applications:

LSFOH/LSIH cable compounds LDPE/ATH.EVA/ATH halogen-free retardant polyolefin cable materials PE Packaging film Silicone core pipe

Typical Applications: Usage/Addition rate: 0,5-5% Product Data

Property Unit Value Name - KK-S1142 Appearance - White pellet Support - Polyolefin Bulk Density g/ml 0,60±0,2 Specific Gravitiy g/cm³ 1,03 Heat Stability °C 300 Silicone Content % 50 Food Approval - YES Hazardous Substances - NO

Processing Temperature: 130-180°C Packaging: It is packaged as 15 kg in aluminum bags, 600 kg pallets. Storage&Handling: KK-S1142 should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:








KK-SBBC Styrene-Butadiene Block Copolymer


Oil-extended radial block copolymer High strength and low viscosity High tensile strength Reprocess able

Product Applications:

Footwear compounding Plastics modification

Product Data:

Property Test Method Unit Value Typical Properties BD/SM Content ASTM D 1416 % 53-47/53-57 Ash Content ASTM D 5630 % ≤1 Oil Content ASTM D 5774 % 26-31 Melt Flow Rate (190°C-5 kg) ASTM D 1238-10 gr/10 min 9-15 Spesific Weight (23°C) ASTM D-792 gr/cm³ 0,92-0,95 Hardness ASTM D 2240 Shore A 90-94

Volatile Matter ASTM D 5668 % ≤0,5 Packaging: It is packaged as 20 kg in PE bags, 800 kg pallets. Storage&Handling: KK-SBBC should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:








KK-UK Flame Retardant Masterbatch

Product Information: Most plastics are combustible and many applications require fire-resistant properties. KK-UK masterbatches inhibit or prevent the combustion process. Material is in pellet form. It is convenient for processing temperature higher than 260°C. Typical Applications: Extrusion-pipes, cable channer. Enjection molding (HDPE, LDPE, LLDPE). Flame retardancy, char forming. For XLPE compound recommended feeding ratio: 10 – 15 % For LLDPE compound recommended feeding ratio: 10 – 20 % For PP compound recommended feeding ratio: 10 – 15 % For HDPE compound recommended feeding ratio: 12 – 15 % For PVC compound recommended feeding ratio: 5 – 10 % For HFFR compound recommended feeding ratio: 3,5 – 4,5 % Product Data

Property Test Method Unit Value Phisical Properties Carrier Resin - - LLDPE Melt Flow Rate (150°C-21,6 kg) ASTM D 1238-10 gr/10 min 23±5 Density ASTM D 792 g/cm3 2,64±0,03

Packaging: It is packaged as 25 kg in aluminum bags, 1250 kg pallets. Storage&Handling: KK-UK should be stored in a manner that avoids direct exposure to sunlight and heat. The storage area should also be dry. KABKOM does not provide a warranty for quality deterioration that is a result of faulty storage conditions.






Product Data:





QUALITY CONTROL LABORATORY

ANALYSIS AND STANDARDS

Document Number KK.FR.128 Version No / Date 26.10.2018 Page 1 / 1

Prepared Eda AÇIKSÖZ Confirming Özgür İPEK

ANALYSIS NAME STANDARDS MELT FLOW RATE ASTM D 1238-13 DENSITY (SOLID) ASTM D 792 -13

DENISTY (LIQUID) ASTM D 4052 BULK DENSITY INTERNAL METHOD

SPECIFIC DENSITY ASTM D 792-13 ASH CONTENT ASTM D 5630-13

MOISTURE INTERNAL METHOD COLOR ASTM E 1164-12/ ASTM D 1003-13

VISCOSITY ASTM D 445 FLASH POINT OF OIL ASTM D 92

IODINE NUMBER OF OIL ASTM D 1959-97 FATTY ACID NUMBER OF OIL ASTM D 1980-87 PEROXIDE NUMBER OF OIL ASTM D 1832:1987

FATTY ACID NUMBER OF WAX ASTM D 1386 FREE FATTY ACID NUMBER OF OIL ASTM D 1980-87

UNSAPONIFIABLES NUMBER OF OIL ASTM D 1965 SAPONIFICATION NUMBER OF OIL ASTM D 94-07

GLOSS ASTM E 1164-12/ ASTM D 1003-13 PARTICLE SIZE ASTM D 7928-17

OIL ABSORPTION OF FILLER AND PIGMENTS ASTM D 1483 TITIAN RATIO OF PIGMENTS ASTM D 1394

STEARIC ACID RATIO OF FILLERS INTERNAL METHOD TENSILE STRENGTH ASTM D 638-14 ELONGATION RATE ASTM D 638-14 HARDNESS SHORE A ISO 868/ ASTM D 2240-15e1 HARDNESS SHORE D ISO 868/ ASTM D 2240-15e1

TEARING STRENGTH TEST ASTM D 1938-19 MINERAL OIL IMEERSION TEST IEC 60811-404

HOT-SET IEC 60811-507 THERMAL AGING ASTM D 3045-18

LOW TEMPERATURE AGING TS EN 50363-3 WATER ABSORPTION TS EN ISO 62

LABORATORY BLOWN FILM EXTRUDER - LABORATORY EXTRUDER -

MOISTURE CONTENT OF WAX TS EN ISO 3251 HALOGEN CONTENT TS EN 60754-1 pH / CONDUCTIVITY TS EN 60754-2

LOI ISO 4589 UL 94 FLAME TS EN 61386-1

POLIMERIC BLENDS ISO 11357-1 GLASS TRANSITION TEMPERATURE ISO 11357-2

TEMPERATURE OF MELTING AND CRYSTALLIZATION ISO 11357-3 DSC DETERMINATION OF SPECIFIC HEAT CAPACITY ISO 11357-4

DSC DETERMINATION OF CHARACTERISTIC REACTION-CURVE TEMPERATURES ISO 11357-5

DSC DETERMINATION OF OXIDATION INDUCTION TIME ISO 11357-6 CHARACTTERIZATION OF POLYMERS ASTM E 1131-08 (ISO 11358)

FT-IR ASTM E 168-16 / ASTM E 1252-98 SIEVE ISO 787-7