HFC 3175 - IEC 60092-359 type SHF-1 - IEC 60502 ST8 - BS7655 :6.1 types LTS1 & LTS3 - VDE 207 HM2 & HM4 - UTP & Telecom cable sheath - IEC 60092-359 type SHF-1 - IEC 60502 ST8 - BS7655 :6.1 types LTS1 & LTS3 - VDE 207 HM2 & HM4 - UTP & Telecom cable sheath APPLICATION PROPERTY HFFR Polyolefin Sheathing Compound for Shipboard & Telecom Cables These compounds are engineered to enhance flame retardant property with ATH based on polyolefin for sheath of Shipboard, Telecom and power cable. It doesn’t emit toxic gases as well as halogen components and show excellent low smoke property. It is also designed to show well-balanced properties of flame retardant property, mechanical property and processing property etc. www.unience.co.kr Density @ 23 o C g/cc ASTM D792 Melt Flow Index (170 o C / 21.6kg) g/10min ASTM D1238 Tensile Strength MPa IEC 60811-1-1 Elongation at Break % After ageing Smoke Density Corrosion test (100 o C/168hrs) T.S Retention Elongation Retention Elongation Retention % IEC 60811-1-2 % Oil Resistance (IRM 902 / 70 o C, 4hrs) T.S Retention % IEC 60811-2-1 % Hot Pressure test (80 o C) % IEC 60811-3-1 Cold Impact test (-15 o C) - IEC 60811-1-4 Flaming (3mm) Ds Max ASTM E662 flaming(0.5mm) PH - IEC 60754-2 Conductivity /Halogen acid gas evolution % IEC 60754-1 Oxygen Index % ASTM D2863 Volume Resistivity Ω.ASTM D257 Hardness Shore D ASTM D2240 Item Unit Test method HFC 3175 1.51 15 12 200 90 85 90 85 20 Pass 90 60 5.0 2.5 Not detected 40 1X10 15 50

HFC 3175 01 - EXTIGEN · 2011. 8. 22. · HFC 3175 - IEC 60092-359 type SHF-1 - IEC 60502 ST8 - BS7655 :6.1 types LTS1 & LTS3 - VDE 207 HM2 & HM4 - UTP & Telecom cable sheath APPLICATION

  • Upload
    others

  • View
    4

  • Download
    0

Embed Size (px)

Citation preview

  • HFC 3175

    - IEC 60092-359 type SHF-1

    - IEC 60502 ST8

    - BS7655 :6.1 types LTS1 & LTS3

    - VDE 207 HM2 & HM4

    - UTP & Telecom cable sheath

    - IEC 60092-359 type SHF-1

    - IEC 60502 ST8

    - BS7655 :6.1 types LTS1 & LTS3

    - VDE 207 HM2 & HM4

    - UTP & Telecom cable sheath

    APPLICATION

    PROPERTY

    HFFR Polyolefin Sheathing Compound for Shipboard & Telecom CablesThese compounds are engineered to enhance flame retardant property with ATH based on polyolefin for sheath of Shipboard, Telecom and power cable. It doesn’t emit toxic gases as well as halogen components and show excellent low smoke property. It is also designed to show well-balanced properties of flame retardant property, mechanical property and processing property etc.

    www.unience.co.kr

    Density @ 23oC g/cc ASTM D792

    Melt Flow Index (170oC / 21.6kg) g/10min ASTM D1238

    Tensile Strength MPaIEC 60811-1-1

    Elongation at Break %

    After ageing

    Smoke Density

    Corrosion test

    (100oC/168hrs)

    T.S Retention

    Elongation Retention

    Elongation Retention

    %IEC 60811-1-2

    %

    Oil Resistance(IRM 902 / 70oC, 4hrs)

    T.S Retention %IEC 60811-2-1

    %

    Hot Pressure test (80oC) % IEC 60811-3-1

    Cold Impact test (-15oC) - IEC 60811-1-4

    Flaming (3mm)Ds Max ASTM E662

    flaming(0.5mm)

    PH -IEC 60754-2

    Conductivity ㎲/㎜

    Halogen acid gas evolution % IEC 60754-1

    Oxygen Index % ASTM D2863

    Volume Resistivity Ω.㎝ ASTM D257

    Hardness Shore D ASTM D2240

    Item Unit Test method HFC 3175

    1.51

    15

    12

    200

    90

    85

    90

    85

    20

    Pass

    90

    60

    5.0

    2.5

    Not detected

    40

    1X1015

    50

  • Main Office China Office1301 MingzhuBuilding, 59ShuichengRoad(S), Shanghai, 201103, P.R.ChinaTEL +86-21-6278-3734 / FAX +86-21-6278-9532

    Marketing Headquarter8F SO8, Garden5 TOOL, 292, Munjung-dong, Songpa-gu, Seoul, 135-884, KoreaTEL +82-2-2047-4722 / FAX +82-2-2047-4709E-mail [email protected]

    1113-10, Namchon-ri, Oaksan-myeon, Cheongwon-gun, Chungcheongbuk-do, 367-882, KoreaTEL +82-43-216-7955 / FAX +82-43-216-7958

    PROCESSING

    - Special compounds can be developed to meet customers specification and requirements.

    - 500 & 750kg Reinforced Carton Box with inner aluminum liner.

    - 25kg Paper bag with inner Aluminum liner.

    CUSTOMIZE

    PACKING

    - It is recommended that this product can be extruded on any conventional extruder equipped with a PE/PVC, 3 stage or barrier r type screw having an L/D ratio of 20~24 : 1 and a compression ratio of 1 . 2~1.8 : 1

    - Should be stored at room temperature between 10~30oC.

    - Maximum storage period in dry and clean place is 6 months unopened and in original packaging.

    - If it has been stored in an opened condition for a long time, use it after drying for 3~4 hrs at 65~70oC. in a dehumidifying dryer.

    - To ensure health and safety, Material Safety Data Sheets (MSDS) is available on request

    www.unience.co.kr

    STORAGE & HANDLING

    Anti-rodent Anti-termite UV Resistance Color

    HFC 3175 01.pdfHFC 3175 02.pdf