Theoretically, maximum Hz stress to avoid permanent deformation is about 1.81 times tensile yield. Reference Maleev and Hartman, Machine Design, 3rd Ed., page 121

Like this post?Star it!Red Flagthis post

diamondjim(Mechanical)7 Jun 06 21:47

Lcubed,Is is Tensile or Yield?My guess is it is 1.81 timeultimate tensile strength.

Like this post?Star it!Red Flagthis post

Lcubed(Structural)8 Jun 06 8:08

Most materials exhibit a tensile yield strength and a compressive yield strength.It is 1.81 times the tensile yield strength.The tensile breaking strength is usually called the ultimate tensile strength, but I recognize that it is also called 'tensile strength', so I should have been more clear.Hope that helps.

Please can anyone help with using Hertz contact stresses? I am designing some equipment for a customer who requires I use a safety factor of 4 on proof strength and 6 on ultimate strength. This is fine when it comes to bending and shear stresses etc, however I'm not sure "what to do" with Hertz stresses. Part of the design uses a hardened steel roller, dia 12 mm, (440C, UTS 930MPa) on a flat steel plate (En24T, proof 650 MPa UTS 850 MPa), loaded both statically and slow moving. I've calculated the compressive and shear stresses according to Roark Table 33 case 2a, however I don't know what to do with them!They are 504 MPa and 168 MPa. I've done the American Railway Engineering Association allowable loading check from the text and my loading has a reserve factor of over 4.Cheers.

Like this post?Star it!Red Flagthis post

prex(Structural)27 May 04 10:20

The limits normally adopted for Hertz's contact stresses are 4 times the allowable stress for linear contact and 5.5 times for point contact. You could divide the Hertz stresses by the same factors before comparing them to your allowables.prex

http://www.xcalcs.comOnline tools for structural design

Like this post?Star it!Red Flagthis post

rattler(Mechanical)27 May 04 11:02

Thanks prex but I don't know the allowables. The Hertz stress is a compressive stress and the peak shear stress is subsurface. I only have material tensile strength information.

Like this post?Star it!Red Flagthis post

prex(Structural)27 May 04 11:09

Your allowable is the minimum of Y/4 and U/6, right?Take the Hertz contact stress intensity (surface stress), divide it by 4 if it is a linear contact (cylinder onto flat) and compare the result to your allowable.prex

http://www.xcalcs.comOnline tools for structural design

Like this post?Star it!Red Flagthis post

rattler(Mechanical)27 May 04 11:18

I'm with you prex! It's thetensilevscompressiveI'm not sure about. Can I compare a Hertz compressive stress with an allowable based on a tensile material strength? Also what do I do with the subsurface shear stress that I have calculated?

Cheers

Like this post?Star it!Red Flagthis post

corus(Mechanical)27 May 04 11:26

Essentially you're comparing stress intensity with the material yield stress and so it is irrelevant whether or not the principal stress is compressive or tensile. The value of stress intensity is always positive.The shear stress limit is generally half the allowable stress intensity limit. If you're comparing bending stresses, for example, with a quarter of yield then by the same token the shear stress should be compared with one eighth of yield.corus

Like this post?Star it!Red Flagthis post

rattler(Mechanical)27 May 04 11:33

Thanks for your help prex and corus.

Prex - could you please give me a reference for your advice "The limits normally adopted for Hertz's contact stresses are 4 times the allowable stress for linear contact and 5.5 times for point contact"? I need to write up my calcs and submit to my customer.

Like this post?Star it!Red Flagthis post

prex(Structural)27 May 04 11:58

Don't know if this will be useful for you, but my reference is the italian code for structural steel 'D.M.9/1/96', where at point '4.7-Fixed and sliding supports' it is said:

Quote:The contact pressures, calculated with Hertz formulae, must be:-for linear contact:l4fd-for point contact:p5,5fdfdis the calculation strength or allowable stress.prex

http://www.xcalcs.comOnline tools for structural design

Like this post?Star it!Red Flagthis post

arto(Mechanical)27 May 04 12:32

FYI-ASME B&PV Code Sec IID allows 1.6xDesign Stress for Bearing Stress on Pressure Vessel Design

Like this post?Star it!Red Flagthis post

rattler(Mechanical)27 May 04 13:08

Does any one else know any limits please for Hertz stress, as the 4 times allowable seems high? The Tribology Handbook page E1.2 concerning contact between a ball and a plane or between two balls states "At heavy loads plastic flow takes place, beginning when Hertz pressure reaches 1.8 x yield stress in tension of softer body"

CheersRattler

Like this post?Star it!Red Flagthis post

diamondjim(Mechanical)1 Jun 04 10:09

This has always been confusing andI have not seen definitive answers.Ball bearings are often life tested withstresses in the 350000 PSI range.The 350000 is more than 2.5 times theUTS of the bearing rings materialswhich have uts values around 123000 PSI.These are surface pressures and notbending stresses but bearing stresses.I have also seen unusually high surfacestresses in gears without failure.I think bearing stresses are published forsome materials.Surely they exceed theuts of the materials.

Like this post?Star it!Red Flagthis post

EnglishMuffin(Mechanical)2 Jun 04 14:56

Well, ultimately the thing that really determines how much surface stress you can stand is the subsurface shear stress. In a situation with purely compressive direct stresses, no material failure can occur, no matter how high those stresses are. The more closely the Hertzian conditions approximate this ideal limiting case, the higher the Hertzian compressive stresses you can stand.

Like this post?Star it!Red Flagthis post

mabaeti(Mining)24 Mar 05 18:12

Rail-wheel allowables from 1.6 to 2.0 times the UTS of the softer material, i think are in DIN (German) standards. Also quoted in Hydraulic gates and Valves by Jack Lewin

Like this post?Star it!Red Flagthis post

mabaeti(Mining)24 Mar 05 18:23

also in EM1110-2-2703, plate B-90 that is a Corps of Engineer manual available on the web, there is implied a factor of 2 times yield for allowable hertz stress, wheel on rail

Theoretically, maximum Hz stress to avoid permanent deformation is about 1.81 times tensile yield. Reference Maleev and Hartman, Machine Design, 3rd Ed., page 121Allowable Contact StressContact stresses are compressive and local and do not cause failure per se, but subsurface shear stress may. The sub surface shear stress is about 1/3 of the compressive principalstress, and most bearing materials have shear allowables about half of the normal tension/compression strength of the material; that means the allowable contact stress is at least 0.5/0.333 or 1.5 times the material allowable compressive stress. Depending on the particular situation, this is for the most part conservative.