Comparative evaluation of the effect of impression ... · Implant insertion in posterior mandible might be angulated due to anatomical considerations. The purpose of this study was

J Clin Exp Dent. 2018;10(11):e1096-102. Effect of impression materials and trays on implant impressions

e1096

Journal section: Prosthetic Dentistry Publication Types: Research

Comparative evaluation of the effect of impression materials and trays on the accuracy of angulated implants impressions

Hakimeh Siadat 1, Zeinab Saeidi 2, Marzieh Alikhasi 3, Somayeh Zeighami 4

1 DDS, MSc; Full Professor, Dental Implant Research Center Dentistry Research Institute and Department of Prosthodontics, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran2 DDS, MSc; Assistant Professor, Department of Prosthodontics, School of Dentistry, Kerman University of Medical Sciences, Kerman, Iran3 DDS, MSc; Associate Professor, Dental Implant Research Center Dentistry Research Institute and Department of Prosthodontics, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran4 DDS, MSc; Associate Professor, Dental Implant Research Center Dentistry Research Institute and Department of Prosthodontics, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran

Correspondence:Dental Implant Research Center Dentistry Research Institute and Department of ProsthodonticsSchool of DentistryTehran University of Medical SciencesTehran, [email protected]

Received: 15/08/2018Accepted: 15/10/2018

Abstract Background: Vinyl Polyether Siloxane is a newly introduced impression material and studies on that is scarce. Implant insertion in posterior mandible might be angulated due to anatomical considerations. The purpose of this study was to compare the dimensional and angular accuracy of impressions using full-arch versus sectional tray and Vinyl Polysiloxane versus Vinyl Polyether Siloxane in angulated implants. Material and Methods: Four implants were placed in dental areas #19, #21, #28 and #30 of a Kennedy class I man-dibular acrylic model with 30° lingual angulation. Twenty sectional and 20 full-arch open trays were made on the primary cast. Impressions were taken using Vinyl Polysiloxane and Vinyl Polyether Siloxane (n=10 in 4 groups); and were poured with type IV dental stone. The coordinate measuring machine was used to measure displacements in the X, Y and Z axes and rotational discrepancies of implants. The data were analyzed using SPSS 22 and two-way ANOVA. Results: Type of tray had no significant effect on the dimensional and angular accuracy of impressions (p > 0.05). Type of impression material significantly affected linear displacement (∆r) (p < 0.05); but it did not significantly affect the rotational displacement (p > 0.05). Conclusion: Vinyl Polysiloxane yielded more accurate impressions of angulated implants.

Key words: Dental implant, impression material, impression tray, vinyl polysiloxane, vinyl polyether silicone, coordinate measuring machine.

doi:10.4317/jced.55227http://dx.doi.org/10.4317/jced.55227

Article Number: 55227 http://www.medicinaoral.com/odo/indice.htm© Medicina Oral S. L. C.I.F. B 96689336 - eISSN: 1989-5488eMail: [email protected] in:

PubmedPubmed Central® (PMC)ScopusDOI® System

Siadat H, Saeidi Z, Alikhasi M, Zeighami S. Comparative evaluation of the effect of impression materials and trays on the accuracy of angulated im-plants impressions. J Clin Exp Dent. 2018;10(11):e1096-102.http://www.medicinaoral.com/odo/volumenes/v10i11/jcedv10i11p1096.pdf


e1097

IntroductionDental implant in the alveolar bone is not surrounded by the periodontal ligament, and assembly of prosthesis over the implant yields a structure composed of prosthe-tic superstructure, implant fixture and bone as one unit (1). Prosthesis-implant misfit causes internal stresses in these three components (1). Stresses due to the lack of passivity of prosthesis lead to mechanical and biologi-cal complications (2). Accurate impression taking and transfer of implant position to the master cast is an im-portant step in fabrication of prosthesis and achieving optimal fit. Impression technique and material are two important factors in obtaining precise fit of implant pros-theses (3,4). In general, two techniques are used for im-plant impression taking (direct or open tray and indirect or closed tray); Direct technique could be done with or without splinting (5). In previous studies the accuracy of impressions taken from angulated implants were same in direct and indirect techniques (5). Furthermore, the-re is no consensus about splinting in angulated implants before impression taking (5).Metal and plastic stock trays and custom trays have also been compared for implant impression taking (6). To minimize impression errors, most studies recommend using a rigid tray irrespective of the type of impression material (6). On the other hand, special acrylic trays have been produced more accurate casts in comparison to the stock trays; because of rigidity and uniform thickness of impression material (6). However, studies on the use of sectional trays are scarce. Geramipanah et al. compared two types of trays and found no significant difference in the accuracy of impressions taken with sectional and full arch trays (2). It is assumed that during taking im-pressions from angulated implants, full-arch trays would undergo greater distortion when removing the tray from bilateral undercuts and consequently, greater stress is created in the impression material, which may cause in-accuracies. In such cases, use of sectional tray may de-crease impression errors since it covers fewer implants and is also less flexible than the full-arch tray (2).Type of impression material is another important factor affecting the accuracy of impressions. In general, pol-yether and Vinyl Polysiloxane (VPS) are considered as the choice impression materials (6). Polyether present dimensional stability and tear resistance and also rigi-dity; while, VPS has better hydrophilicity and higher dimensional stability (6). In a systematic review, Lee et al. did not find any significant difference in the accuracy of these impression materials (3). Due to optimal elastic recovery, VPS is considered as a preferred impression material for taking impressions from angulated implants (4,7,8). Recently, Vinyl Polyether Siloxane (VPES) was introduced to the market, which is a combination of VPS and polyether and has some of the properties of both materials. The manufacturer claims that this mate-

rial has very good flowability and hydrophilicity. Also, this material has double snap property, which decreases the distortion of impression upon completion of working time due to changed viscosity and subsequent formation of cross-links. Also, this material has optimal elasticity and is tasteless and odorless. Considering the information gap on the dimensional and angular accuracy of impressions taken with VPES and sectional tray, this study aimed to assess the accuracy of impressions taken from bilateral angulated implants using sectional versus full arch trays and PVES versus VPS impression materials. The null hypothesis was that type of tray and impression material would have no effect on the dimensional and angular accuracy of im-plant impressions. Material and MethodsA Kennedy class I mandibular acrylic model (Parsateb, Tabriz, Iran) was used in this in vitro experimental study. In order to determine the position of implants, teeth arrangement on acrylic base was done and left and right mandibular first premolar and molar teeth (dental areas #19, #21, #28 and #30) were selected as implant inser-tion areas. Then on each side of edentulous ridge 2 pa-rallel (mesiodistal angulation of implant is not common due to anatomical limitations) holes with 30° lingual angulation were prepared (this is the worse case of an-gulated implants in posterior mandible). Four implants (Implantium, Dentium, Seoul, South Korea) measuring 4.3 mm in diameter and 12 mm in height were inserted at the level of ridge using self cure acrylic resin (Tech-novit 4000; Heraeus Kulzer GmbH & Co., Wehrheim, Germany). Two metal rods were placed at the center of the original model and planes trace by these rods served as the reference planes for measurements in X, Y and Z axes. The reference point for measurement was the cen-ter of anterior rod. Since the position of these cylinders transfer by the impression, we will be able to calculate the coordinates of each implant in each sample irrespec-tive of the 3D displacement of the other implants. As ba-seline data, rotational (θ) and dimensional (X, Y and Z) coordinates of implants were measured using coordinate measuring machine (CMM) (Global DEA, Hexagon, Italy) with 4μm accuracy and a SP25 probe with 1mm diameter (Fig. 1a,b). The machine was first calibrated by placing the probe tip on the calibration ball.One of the most accurate coordinating tools is the Coor-dinate Measuring Machine. CMM measure physical and geometrical properties of the sample. The measurements are performed by touching a point using a probe and dis-playing the coordinates of each point in X, Y, Z axes.To measure the sample’s coordinates, at first the refe-rence planes (X, Y, and Z) were defined. For this purpo-se, the cylinders located at the center of the model were scanned by the machine. The Z plane was defined on the


e1098

Fig. 1: (a) Master model with four angled implants (b) Measurement of displacements in x, y, and z directions and rotational displacement by CMM.

surface of the anterior cylinder. X plane was defined as a line passing through two cylinders and perpendicular to the Z plane. The Y plan was perpendicular to the other two planes. Impression copings were closed on the im-plants and each implant was scanned circularly and the center of implants was used to determine the X, Y and Z coordinates.To measure the angular coordinate of the implants, a delicate flat blade was made. Implants have a hexagon connection. The edge of blade was placed at an angle be-tween the two sides of the hexagon and the other edge of the blade was used to measure its angle with the X axis.For the same seating of the spatial trays, four stops were made in anterior, posterior and lateral sides of master model using autopolymerizing acrylic resin.Four transfer impression copings (DTF 45 11 HL, Im-plantium, Dentium, Seoul, South Korea) were tightened on implants and a closed tray impression was taken from the model by a stock tray and irreversible hydrocolloid (Alginoplast, Heraeus Kulzer GmbH & Co., Wehrheim, Germany). Primary cast was poured with dental stone type III (Tara 250, Kheyzaran, Isfahan, Iran). Two layers of base plate wax (Dentsply, Weybridge, United King-dom) were adapted on the cast and in order to keep the material thickness at 3 mm, three tissue stops were pre-pared (one on incisal edge and two on posterior ridge). light-polymerized resin (Megatray, Megadenta, Rede-berg, Germany) was used and 20 full-arch and 20 sec-tional open trays were made with a thickness of 2mm. The sectional tray was fabricated such a way to cover the two implants placed in the right quadrant. Thirty mi-nutes prior to taking the impression, the internal surfa-ce and 5mm border of the external surface of each tray

were covered with silicone adhesive (Kettenbach GmbH & Co. KG, Eschenburg, Germany). Pick-up impression copings (DPU 45 11 HL, Implantium, Dentium, Seu-ol, South Korea) were screwed onto the implants with 10 Ncm torque (2). Impressions were taken by a single operator and using regular consistency of VPS (Panasil, Kettenbach GmbH & -Co. KG, Eschenburg, Germany) (Fig. 2a,b) and medium consistency of VPES (EXA’len-ce, GC Corporation, Tokyo, Japan) (Fig. 2c,d). Impres-sion gun was used for mixing. Impressions were taken at 23±1°C temperature and 50±10° relative humidity (9). To apply standard load, 1.5kg weight was placed on each tray during the process of polymerization (2). The impression-tray was immersed in water at 36±1°C du-ring the process (2). The path of insertion and removal of trays were in vertical direction. In total, 40 impressions were taken in 4 groups (n=10 in each group) using two types of trays and two types of im-pression materials. Implant analogs were connected to im-pression copings in the impressions and then, beading and boxing were done for each impression. After one hour, the impressions were poured with type IV dental stone (Fuji-rock EP, GC Corporation, Tokyo, Japan). After 40 minutes (as recommended by the manufacturer), the casts were se-parated from the impressions and coded (Fig. 3a,b). The coordinates of each analog were measured using a CMM (Global DEA, Hexagon, Italy). The distance from the center of each analog to the reference point (center of anterior cylinder) in the X, Y and Z axes and also their angular coordinates (θ) were measured. The mea-surements were repeated on each analogue three times, and the mean of each of the measurements in each analo-gue was compared with those obtained from the referen-


e1099

Fig. 2: Impressions made by (a) full-arch tray and PVS material, (b) sectional tray and PVS material, (c) full-arch tray and PVES material, (d) sectional tray and PVES material.

Fig. 3: (a) Final full-arch cast. (b) Final sectional cast.

ce model. To calculate 3D displacement, the following equation was used: (Fig. 4):

Due to normal distribution, the data were analyzed using SPSS version 22 (SPSS Inc., IL, USA) and two-way ANOVA test considering the type of tray and type of impression material. Level of significance was 0.05.

∆r = ∆x% + ∆y% + ∆z%Fig. 4: Formula.

ResultsMean and standard deviation of displacements in X, Y, Z axes, linear (∆r) and rotational discrepancies (∆θ) have been summarized in table 1. P-values of each variable are shown in table 2. The results showed that there were no statistically sig-nificant differences in dimensional (X, Y and Z axes), linear (∆r) and rotational discrepancies (∆θ) between fu-ll-arch and sectional trays (p>0.05). Type of impression material significantly affected the di-


e1100

Material Tray ∆X

(mm)

∆Y

(mm)

∆Z

(mm)

∆r

(mm)

Dq

(°)

PVS Full arch Mean 0.08 0.04 0.05 0.11 0.95

Std.Deviation 0.06 0.02 0.04 0.05 1.23

Minimum 0.01 0.01 0.00 0.04 0.00

Maximum 0.18 0.08 0.12 0.21 4.38

Sectional Mean 0.07 0.06 0.03 0.11 0.87

Std.Deviation 0.05 0.09 0.03 0.08 0.49

Minimum 0.01 0.00 0.00 0.02 0.27

Maximum 0.21 0.40 0.09 0.41 2.36

PVES Full arch Mean 0.11 0.08 0.10 0.20 0.10

Std.Deviation 0.05 0.07 0.16 0.15 1.06

Minimum 0.00 0.01 0.00 0.03 0.01

Maximum 0.20 0.24 0.59 0.63 3.03

Sectional Mean 0.10 0.08 0.08 0.18 1.74

Std.Deviation 0.09 0.06 0.18 0.18 2.51

Minimum 0.00 0.01 0.00 0.03 0.00

Maximum 0.32 0.24 0.81 0.85 9.86

Table 1: Mean and standard deviation of dimensional (∆X, ∆Y, ∆Z), linear (∆r) and angular (∆θ) displacements for trays and materials.

Dq Dr DZ DY DX

0.34 0.08 0.47 0.52 0.64 Tray

0.18 0.01* 0.07 0.03* 0.02* Material

0.23 0.67 0.99 0.39 0.91 Tray and Material

Table 2: P-values of displacements in X, Y, Z axes and linear (∆r) and angular discrepancies (∆θ) for tray, material and their interaction.

mensional accuracy of impressions in X, Y axes and li-near displacement (∆r) (p<0.05), but it had no significant effect on displacement in Z axis and angular discrepancy (∆θ) (p>0.05). Also, the interactions between tray and material had no significant effect on dimensional and angular accuracy of impressions (p>0.05).

Discussion Taking accurate impression is the first step in fabrication of a high-quality prosthetic restoration with precise fit. Impression material and technique play a fundamental role in obtaining accurate impressions (10). This study evaluated the accuracy of impressions taken with two types of trays (full-arch and sectional) and two types of impression materials (VPS and VPES). In the posterior mandible, lingual undercuts are present due to the position of submandibular glands. In order to prevent perforation of the lingual plate, implants are placed angulated in thids region (11). Morphological

assessment of mandibular ridges in a previous study re-vealed that posterior mandibular undercuts were present in 66% of the patients above the inferior alveolar canal and the mean angulation in this area was 57° (11). After tooth extraction, mandibular ridge undergoes resorption of the crestal bone and lingual plate, and depth of under-cuts decreases. Implants are often placed in more than 25° angulations in the clinical setting (2). In the current study, implants were placed with 30° lingual angulation to simulate angular placement of implants due to the presence of undercuts in the posterior mandible. The results of this study showed that impressions taken with full-arch and sectional trays had no significant di-fference in dimensional (X, Y and Z axes), linear (∆r) and angular discrepancies (∆θ). These findings con-firmed the null hypothesis of the study stating that the accuracy of impressions would not be affected by the type of tray. Germipanah et al. evaluated the accuracy of impressions taken from angulated implants (Replace,


e1101

Nobel Biocare) using sectional and full-arch trays and found no significant difference in terms of dimensional or angular discrepancies (2). This result may be due to the short connection length of impression copings of the implant system, which enabled easy removal of the im-pression despite the presence of angulated implants; as a result, the stresses between the coping and impression material were minimized upon removal of the full-arch tray from angulated implants. In their study, the length of connection of copings (Replace system) was 1mm; this value was 1.2mm in the current study using the Implan-tium system. Alikhasi et al. evaluated the effect of 1, 1.5 and 2mm connection lengths of open impression copings on the accuracy of impressions taken from angulated im-plants and reported no significant difference in the accura-cy of impressions when impression copings with less than 2mm connection length were used (12). However, use of copings with longer connections or higher number of im-plants in future studies may yield significant differences. The impressions taken with VPS and VPES impres-sion materials yielded significantly different dimensio-nal accuracy in X, Y axes and linear displacement (∆r) (P<0.05); however, the difference in Z axis and rotatio-nal displacement (∆θ) was not significant. As seen in table 1, the dimensional and angular accuracy of VPS were higher than VPES. Based on these findings, the null hypothesis, stating that the two impression mate-rials would have similar accuracy, was refuted. Kurtulmus et al compared the accuracy of implant im-pressions taken with VPS, VPES and polyether and re-ported that for angulated implants, VPS impressions had higher accuracy than the other two. This has been justi-fied by higher elastic recovery of VPS (7). Vojdani et al. assessed the accuracy of impressions taken from strai-ght and angulated implants using VPES, VPS and pol-yether and showed in angulated implants, VPS yielded the highest accuracy followed by VPES and polyether, respectively (13). A possible explanation would be that elastic recovery is an important property of impression materials, which maintains the dimensional stability of impression when removing the tray and avoids distor-tion that may occur in removal of impression material due to the angulation of implants (12,14). This distortion has a direct correlation with the number of implants and their angulation (12). Using an impression material with such properties decreases permanent distortion due to less stress between the impression coping and the ma-terial, and the accuracy of impressions increases as such (4,12).The interactions between tray and impression material had no significant effect on dimensional and angular ac-curacy of impressions. It means that considering both factor (tray and material), the accuracy of impressions was not significantly different.In vitro design was the main limitations of this study.

Impressions are taken ideally in vitro due to the absence of soft tissue, blood and saliva while these factors in the clinical setting can significantly affect the accuracy of impressions. There is no agreement about acceptable level of implant framework misfit. In 1983, Bernanke was the first per-son who quantify the passive fit, and stated that mis-fit less than 10µm is acceptable. While in 1991, Jemt stated that misfit less than 150 µm is acceptable (15). The framework fitness is affected by factors such as the number and distribution of implants, the rigidity of the framework, the margin location, and the ability of the screw to close the gap (16). The evaluation of the fra-mework fitness in clinic could be done in several ways, like as: alternative finger pressure, direct vision, tactile sensation, radiography, Sheffield test, screw resistance test, disclosing media and 3-Dimensional quantifying systems (15).It is quoted that unavoidable displacement in the implant impression is about 50 µm (15), But there is no enou-gh information about that amount of analogues displa-cement after impression making in current study will cause how much misfit in frameworks. It needs to make framework on the final casts and then evaluate the misfit by methods that mentioned above. It will be possible in future studies.Also, further studies on the accuracy of VPES and sec-tional trays are required. In addition, future studies must focus on different shapes of dental arches, higher number of implants, variable angulations of implants and different implant systems to better elucidate this topic. The clinical implication of this study is that since the ac-curacy of full arch and sectional trays was same, and gi-ven that by full arch cast making record base for recording is easier, for impression making of angulated implants in class I Kennedy, full arch tray and VPS is recommended.

ConclusionsConsidering the limitations of this in vitro study, fo-llowing conclusions were obtained: Type of tray had no significant effect on linear displace-ment (∆r). Type of impression material significantly affected linear displacement (∆r).Rotational discrepancy (∆θ) was not affected by type of tray and material.VPS was more accurate impression material in angula-ted implants compared to VPES.

References1. Vigolo P, Mutinelli S, Fonzi F, Stellini E. An in vitro evaluation of impression techniques for multiple internal- and external-connection implant prostheses. Int J Oral Maxillofac Implants. 2014;29:807-18.2. Geramipanah F, Sahebi M, Davari M, Hajimahmoudi M, Rakhs-han V. Effects of impression levels and trays on the accuracy of im-pressions taken from angulated implants. Clin Oral Implants Res. 2015;26:1098-1105.


e1102

3. Lee H, So JS, Hochstedler J, Ercoli C. The accuracy of implant impressions: a systematic review. J Prosthet Dent. 2008;100:285-91.4. Sorrentino R, Gherlone EF, Calesini G, Zarone F. Effect of implant angulation, connection length, and impression material on the dimen-sional accuracy of implant impressions: an in vitro comparative study. Clin Implant Dent Relat Res. 2010;12:e63-e76.5. Tsagkalidis G, Tortopidis D, Mpikos P, Kaisarlis G, Koidis P. Accu-racy of 3 different impression techniques for internal connection angu-lated implants. J Prosthet Dent. 2015;114:517-236. Gökçen-Rohlig B, Ongül D, Sancakli E, Sermet B. Comparative evaluation of the effects of implant position, impression material, and tray type on implant impression accuracy. Implant Dent. 2014;23:283-8.7. Kurtulmus-Yilmaz S, Ozan O, Ozcelik TB, Yagiz A. Digital evalua-tion of the accuracy of impression techniques and materials in angula-ted implants. J Dent. 2014;42:1551-9.8. Ehsani S, Siadat H, Alikhasi M. The effect of implant connection length on the dimensional impression accuracy of inclined implants. Int J Oral Maxillofac Implants. 2013;28:e315-20.9. Mpikos P, Kafantaris N, Tortopidis D, Galanis C, Kaisarlis G, Koi-dis P. The effect of impression technique and implant angulation on the impression accuracy of external- and internal-connection implants. Int J Oral Maxillofac Implants. 2012;27:1422-8.10. Lee H, Ercoli C, Funkenbusch PD, Feng C. Effect of subgingival depth of implant placement on the dimensional accuracy of the implant impression: an in vitro study. J Prosthet Dent. 2008;99:107-13.11. Chan HL, Brooks SL, Fu JH, Yeh CY, Rudek I, Wang HL. Cross-sec-tional analysis of the mandibular lingual concavity using cone beam computed tomography. Clin Oral Implants Res. 2011;22:201-6.12. Alikhasi M, Siadat H, Rahimian S. The Effect of Implant Angula-tion on the Transfer Accuracy of External-Connection Implants. Clin Implant Dent Relat Res. 2015;17:822-9.13. Vojdani M, Torabi K, Ansarifard E. Accuracy of different impres-sion materials in parallel and nonparallel implants. Dent Res J (Isfa-han). 2015;12:315-22.14. Calesini G, Zarone F, Sorrentino R, et al. Effect of 2 impression techniques on the dimensional accuracy of workingimplant prosthesis models: an in vitro study. J Craniofac Surg. 2014;25:822-7.15. Buzayan MM, Yunus NB. Passive fit in screw retained multi-unit implant prosthesis understanding and achieving: A review of the lite-rature. J Indian Prosthodont Soc. 2014;14:16-23.16. Kan JY, Rungcharassaeng K, Bohsali K, Goodacre CJ, Lang BR. Clinical methods for evaluating implant framework fit. J Prosthet Dent. 1999;81: 7-13.

AcknowledgmentThis study was supported by the Dental Implant Research Center Den-tistry Research Institute, Tehran University of Medical Sciences [grant number 29203-104-03-94].

Conflict of InterestThe authors have declared that no conflict of interest exist.