Coiled pipe markers are moulded polyester identification strips, used to display information on both interior andexterior pipework. Each individual supply can be tailored to suit any client’s standards, including dual languageand both corporate and national legislation. Our experienced surveying team can work from Piping andInstrumentation Diagrams, which allows for an accelerated turnaround.

Using a fully certified installation team, Seaward Safety also offers an international installation service, whichcan be conducted offshore, in shipyards/quayside or in refineries, all over the world.

Our coiled pipe markers are manufactured using high quality, industrial standard UV inks, which produces ahighly durable print. To further protect our pipe markers from heat and contaminants, we also apply aprotective layer of clear overlaminate, which enables us to offer a prolonged life of 7 years. Each marker hasa double sided tape strip, which is stuck to itself on application and not to the pipe.

Typical pipe marker information (not limited to):-- Color code- Content and Direction of flow- To and From- Line Number and/or P&I.D. reference number- Pressures

Key benefits:- Durable and long lasting.- Temperature range: -40ºC to 200ºC.- Coiled self-locking material; keeps secure even on angled or vertical pipes.- Excellent thermal and dimensional stability.

Coiled Pipe Markers

www.seawardsafety.comenquiries@seawardsafety.com +44 (0) 1502 512834

Products to compliment are also available from Seaward Safety, including our Pipe Marking Color Code Board.

AIR / AR

BULK - GRANEL /MIXING - MISTURA

FRESH WATER /ÁGUA DOCE

SEA WATER /ÁGUA SALGADA

FLUID / FLUIDO

CO2

FIRE WATER / ÁGUA

ACID / ÁCIDO

ALKALINES / ÁLCALIS

FIRE / FOGO

COMPLETION / COMPLETAÇÃO

COMPLETION / COMPLETAÇÃO

LIQUID MUD LOW PRESSURE / LAMA LÍQUIDA BAIXA PRESSÃO

SYSTEM / SISTEMA

AIR BULK / AR DE GRANEL

AIR INSTRUMENT / AR INSTRUMENTAL

AIR VENTILATION / AR VENTILAÇÃO

BARITE / BARITINA

BENTONITE / BENTONITA

CEMENT / CIMENTO

DRILL WATER / ÁGUA INDUSTRIAL

ENGINE COOLING / ARREFECIMENTO DE MOTORES

POTABLE / POTÁVEL

HIGH PRESSURE / ALTA PRESSÃO

STEAM / VAPOR

BALLAST / LASTRO

CIRCULATION / CIRCULAÇÃO

BRINE / SALMOURA

ACETYLENE / ACETILENO

CEMENT / HIGH PRESSURE / CIMENTO, ALTA PRESS OÃ

WHITE / BRANCO

WHITE / BRANCO

WHITE / BRANCO

WHITE / BRANCO

WHITE / BRANCO

WHITE / BRANCO

PIPE COLOR /COR DA TUBULAÇÃO

BASIC BAND COLOR /COR BÁSICA DE FAIXA

VIOLET / LILÁS

LIGHT GREEN /VERDE CLARO

WHITE / BRANCO

IDENTIFICATION - DESCRIPTION /IDENTIFICAÇÃO - DESCRIÇÃO

ALKALINES / ÁLCALIS

DRILL WATER / ÁGUA INDUSTRIAL

ENGINE COOLING /ARREFECIMENTO DE MOTORES

STEAM / VAPOR

ACETYLENE / ACETILENO

POTABLE / POTÁVEL

HIGH PRESSURE / ALTA PRESSÃO

EXAMPLE /EXEMPLO

DRILL WATERÁGUA INDUSTRIAL

ENGINE COOLINGARREFECIMENTO DE MOTORES

HIGH PRESSUREALTA PRESSÃO

POTABLEPOTÁVEL

STEAMVAPOR

ACETYLENEACETILENO

TECHNICAL SPECIFICATIONS

Property Test method Unit Values

Gen

era

l Film thickness

Area Yield

Unit Weight

Density

micron

2m /kg

2g/m

g/cc

100

7.1

140

1.39

Mech

an

ical

Tensile strength at break(minimum)

ASTM D882-83(23°C, 50% rh, strain rate 50% min)

14MD

TD

Stress at 5% strain (F5)MD

TD

Elongation at breakMD

TD

Slip (co-efficient ofstatic friction)

ASTM D1894-79 (modified)

ASTM D1505

2kgf/mm

2kgf/mm

%

17

8

8

120

120

0.4

Color (D65 - 10°)

Op

tical

Gloss

Total light transmittance(maximum)

ASTM E313-79

ASTM D2457-90 (Gardner 60°)

ASTM D1003-77 (Gardner Hazemeter)

%

%

L* = 97.8a* = 0.1b* = -3.2

45

8

Upper melt temperature

Coefficient of thermal expansion (between 20 & 50°C)

MD

TD

Shrinkage(175 micron film)

MD

TD

ASTM E794-85

5 mins at 190°C

°C

cm/cm/°C

%

255 to 260-619 x 10-616 x 10

3

1

Th

erm

al

PO

LYE

ST

ER

SU

BS

TR

AT

E

PR

OT

EC

TIV

E O

VE

RL

AM

INA

TE

On clean, dry substrate

Instron Tensile Tester as above

158°F (70°C), 48 hours

PSTC-1, 15 min, RT 70°F (21°C)

TLMI Release at 90°, 300 in/min(760 cm/min)

Gloss Meter 60° Reflection

Micrometer, Federal Bench Type

Tensile Tester with 2-in (51mm) jawseparation; crosshead speed of

12 in/min. (5.1 mm/s), web direction

On clean, dry substrate

Applied to etched aluminium panels24hrs prior to testing. 100% releasehumidity, 100°F (38°C) for 500 hrs.

Film applied to etched aluminiumpanels 24hrs prior to testing.

Immersed 30 minutes at 70°F (21°C),stabilized 24hrs before inspection

Surface Finish

Thickness

Tensile Strength

Elongation

Application Temperature Range

Humidity Resistance

Gasoline Resistance

Dimensional Stability

Peel Adhesion

Liner Release

Service Temperature Range

40 - 100°F optimum

> 130%

20-mils

80-90% (Gloss)35-45% (Satin)05-10% (Matte)

3-mil (75 micron)

10 lb/in width

-20 - 150°F

No appreciable effect

1.8 kg/cm width

4.4 - 38°C optimum

-29 - 65°C

No appreciable effect

0.51 mm

2.5 lb/in 0.45 kg/cm

120 g/2 in width 47 g/cm width

PROPERTY TEST METHODS TYPICAL VALUE

Coiled Pipe Markers