CHROMATE CONVERSION COATINGS

by Fred W. Eppensteiner (Retired) and Melvin R. Jenkins

MacDermid Inc., New Hudson, Mich.

Chromate conversion coatings are produced on various metals by chemical or electro- chemical treatment with mixtures of hexavalent chromium and certain other compounds. These treatments convert the metal surface to a superficial layer containing a complex mixture of chromium compounds. The coatings are usually applied by immersion, although spraying, brushing, swabbing, or electrolytic methods are also used. A number of metals mad their alloys can be treated; notably, aluminum, cadmium, copper, magnesium, silver, and zinc.

The appearance of the chromate film can vary, depending on the formulation of the bath, the basis metal used, and the process parameters. The films can be modified from thin, clear:bright and blue-bright, to the thicker, yellow iridescent, to the heaviest brown, olive drab, and black films: A discussion of specific formulations is not included in this article because of the wide variety of solutions Used to produce the numerous types of finishes. It is intended to present sufficient general information to permit proper selection and operation of chromating baths. Proprietary products, which are designed for specific applications, a~e available from suppliers.

PROPERTIES AND USES

Phys ica l Character i s t i c s Most~. chromate films are soft and gelatinous when freshly formed. Once dried, they

slowly harden or "set" with age and become hydrophobic, less soluble, and more abrasion resistant. Although heating below 150°F (66°C) is of benefit in hastening this aging process, prolonged heating above 150°F may produce excessive dehydration of the film, with consequent reduction of its protective value. Coating thickness rarely exceeds 0.00005 in., and often is on the order of several microinches. The amount of metal removed in forming the chromate film will vary with different processes.

Variegated colors normally are obtained on chromating, and are due mainly to interference colors of the thinner films and to the presence of chromium compounds in the film. Because the widest range of treatments available .is for zinc, coatings for this metal afford an excellent example of how color varies with film thickness. In the case of electroplated zinc, clear-bright and blue-bright coatings are the thinnest..The blue-brights may show interference hues ranging from red, purple, blue, and green, to a trace of. yellow, especially when viewed against a white background. Next, in order of increasing thickness; come the iridescent yellows, browns, bronzes, olive drabs, and blacks.

Physical variations in the metal surface, such as those produced by polishing, machining, etching, etc., also affect the apparent color of the coated surface. The color of the thinner coatings on zinc can also be affected indirectly by chemical polishing, making the finish appear whiter.

Corrosion Prevention Chromate conversion coatings can provide exceptionally good corrosion resistance,

depending upon the basis metal, the treatment used, and the film thickness. Protection is due both to the corrosion-inhibiting effect of hexavalent chromium contained in the film and to the physical barrier presented by the film itself. Even scratched or abraded films retain a great

497

deal of their protective value because the hexavalent chromium content is slowly leachable in contact with moisture, providing a self-healing effect.

The degree of protection normally is proportional to film thickness; therefore, thin, clear coatings provide the least corrosion protection, the light iridescent coatings form an intermediate group, and the heavy olive drab to brown coatings result in maximum corrosion protection. The coatings are particularly useful in protecting metal against oxidation that is due to highly humid storage conditions, exposure to marine atmospheres, handling or fingerpiint "marking, and other conditions that normally cause corrosion of metal.

Bonding of Organic Finishes The bonding of paint, lacquer, and organic finishes to chromate conversion coatings is

excellent. In addition to promoting good initial adhesion, their protective nature prevents subsequent loss of adhesion that is due to underfilm corrosion. This protection continues even thought he finish has been scratched through to the bare metal. It is necessary that the organic finishes used have good adhesive properties, because bonding must take place on a smooth, chemically clean surface; this is not necessary with phosphate-type conversion coatings, which supply mechanical adhesion that is due to the crystal structure of the coating.

Chemical Polishing Certain chromate treatments are designed to remove enough basis metal during the

film-forming process to produce a chemical polishing, or brightening, action. Generally used for decorative work, most of these treatments produce very thin, almost colorless films. Being thin, the coatings have little optical covering power to hide irregularities. In fact, they may accentuate large surface imperfections. In some instances, a leaching or "bleaching" step subsequent to chromating is used to remove traces of color from the film.

If chemical-polishing chromates are to be used on electroplated articles, consideration must be given to the thickness of the metal deposit. Sufficient thickness is necessary to allow for metal removal during the polishing operation.

Absorbency and Dyeing When initially formed, many films are capable of absorbing dyes, thus providing a

convenient and economical method of color coding. These colors supplement those that can be produced during the chromating operation, and a great variety of dyes is available for this purpose. Dyeing operations must be conducted on freshly formed coatings. Once the coating is dried, it becomes nonabsorbent and hydrophobic and cannot be dyed. The color obtained with dyes is related to the character and type of chromate film. Pastels are produced with the thinner coatings, and the darker colors are produced with the heavier chromates. Some decorative use of dyed finishes has been possible when finished with a clear lacquer topcoat, though caution is required because the dyes may not be lighffast.

In a few cases, film colors can be modified by incorporation of other ions or dyes added to the treatment solution.

Hardness Although most coatings are soft and easily damaged while wet, they become reasonably

hard and will withstand considerable handling, stamping, and cold forming. They will not, however, withStand continued scratching or harsh abrasion. A few systems have been developed that- possess some degree of "wet-hardness," and these will withstand moderate handling before drying.

498'

LUSTER-OH has your solution...

Zinc Solutions Acid Zinc-full bright level ductile deposits over a wide current density range. Superior plate distribution, high temperature tolerance, rack or barrel. Alkaline Zinc- Low metal formulations for either rack or barrel. Excellent distribution and throwing power, low stress, easily chromated. Cyanide Zinc- a full range system for rack or barrel, with excellent throwing power and temperature tolerance. Zinc-Cobalt- full bright deposits for bat rack and barrel. Nickel Solutions High performance addition agents for outstanding brightness and leveling. Single addition systems for both rack and barrel. Copper Solutions Non-Cyanide Copper' bright deposits, excellent adhesion over a wide current density range. Suitable for both rack and barrel, strike or plate. Cyanide Copper- semi-bright deposits with grain refining and leveling. Used in both rack and barrel. Chrome Solutions Uniform plate distribution and increased rote of deposition. Low concentrations provide low cost makeup, production and waste treatment.

Special Solutions I.uster-Lac 404-increased corrosion protection over chromated zinc surfaces. 1 O0 hours to white corrosion over blue bright, 500 hours over yellow chromate. Sealer 90- post treatment for chromated zinc for extensive corrosion protection. Chromate Conversion Coatings-Attractive, decorative finishes for maximum protection. One simple low-cost operation. Available for zinc, cadmium, die castings, brass, copper & aluminum in clear-brite, blue-brite, iridescent, black or dyed films. Blakodize®chemical black treatment for steel and stainless Steel provides lustrous, rich black finish. Excellent abrasion and corrosion resistance. Rust Preventative #1 for post treatment after phosphatizing, black oxide or other surface conditions.

... equipment , too! Sterling Portable Plating Barrels- Exclusive mesh or square hole design. Plates faster, dries and rinses better. Withstands all plating solutions, up to 200 ° . Sterling Baskets- Rugged polyprepylene or stainless steel construction end mesh liner. Available in 12"xl 2", 6"x6", 21/4"x4" sizes.

Data sheets and prices on request.

l , l l S T I P , I t - l l l m + Luster-On Products Inc.

54 Waltham Avenue, Springfield, MA 01109 • 413-739-2541 1 - 8 0 0 - 8 8 8 - 2 5 4 1

Heat Resistance Prolonged heating of chromate films at temperatures substantially above 150°F (66°C)

can decrease their protective value dramatically. There are two effects of heating that are believed to be responsible for this phenomenon. One is the insolubilization of the hexavalent chromium, which renders it ineffective as a corrosion inhibitor. The second involves shrinking and cracking of the film, which destroys its physical integrity and its value as a protective barrier.

Many factors, such as the type of basis metal, the coating thickness, heating time, temperature, and relative humidity of the heated atmosphere, influence the degree of coating damage. Thus, predictions are difficult to make, and thorough performance testing is recommended if heating of the coating is unavoidable.

The heat resistance of many chromates can be improved by certain posttreatments or "sealers." Baking at paint-curing temperatures after an organic finish has been applied is a normal practice and does not appear to affect the properties of the treatment film.

Electrical Resistance The contact resistance of articles that have been protected with a chromate conversion

coating is generally much lower than that of an unprotected article that has developed corroded or oxidized surfaces. As would be expected, the thinner the coating, the lower the contact resistance, i.e., clear coatings have the least resistance, iridescent yellow coatings have slightly more, and the heavy, olive drab coatings have the greatest. If exposure of an article to corrosive conditions is anticipated, the choice of a coating thickness normally involves a compromise between a very thin fi lm--which, although having very low initial contact resistance, is likely to allow early development of high electrical resistance corrosion products--and a heavier film, with somewhat higher initial contact resistance, but which is likely to remain relatively constant for a longer period under corrosive conditions.

Fabrication Resistance Welding. Thin chromate films do not interfere appreciably with spot, seam,

or other resistance-welding operations. Aluminum coated with a thin, nearly colorless film, for example, can be spot welded successfully with no increase in welding machine settings over those required for bare metal. Metal coated with thicker, colored films also can be resistance welded. The increased contact resistance of thicker coatings, however, necessitates using slightly higher machine settings.

Fusion Welding. These operations, likewise, are not hampered by the presence of chromate films. It has been repotted, in fact, that chromate treatments on aluminum actually facilitate inert gas welding of this metal and its alloys, producing contamination-free welds.

Soldering. Cadmium and silver surfaces coated with thin chromate films can be soldered without difficulty using a mild organic flux. Conflicting reports exist regarding the solderabilty of chromated zinc surfaces.

Mechanical Fastening. The assembly of chromated parts using bolts, rivets, and other mechanical fastening devices usually results in local damage to the chromate film. Corrosion protection in these areas will depend upon the effectiveness of the self-healing properties of the surrounding coating.

Summary of Common Uses Table I summarizes the most common applications of chromate conversion coatings.

MATERIALS OF CONSTRUCTION

Generally, suppliers of proprietaries recommend materials for use with their products, which are resistant to oxidants, fluorides, chlorides, and acids. Materials that have been found

500

Table I. Common Uses of Chromate Conversion Coatings

General Usage

Corrosion Paint Chemical Metal Metal Resistance Base Polish Coloring Remarks

Aluminum X X X

Cadmium X X X X

Copper X X X X

Magnesium X X Silver X Zinc X X X X

Economical replacement for anodiz ing if abrasion resistance is not required. Used to "touch-up" damaged areas on anodized surfaces.

Thin coatings prevent "spotting out" of brass and copper electrodepos its. No fumes generated during chemical polishing.

to be satisfactory for most chromating applications are stainless steels and plastics. Stainless steels such as 304, 316, 317, and 347 are suitable for tanks and heaters where chlorides are absent. Containers and tank linings can be made from plastics such as polyvinyl chloride (PVC), polyvinylidine chloride (PVDC), polyethylene, and polypropylene. Acid-resistant brick or chemical stoneware is satisfactory for some applications, but is subject to attacks by fluorides.

Parts-handling equipment is made of stainless steel, plastisol-coated mild steel, or plastic. Mild steel can be used for leaching tanks because the solutions are generally alkaline,

whereas tanks for dyeing solutions, which are slightly acid, should be of acid-resistant material.

Usually, ventilation is not necessary because most chromate solutions are operated at room temperature and are nonfuming. Where chromating processes are heated, they should be ventilated.

FILM FORMATION

Mechanism The films in most common use are formed by the chemical reaction of hexavalent

chromium with a metal surface in the presence of other components, or "activators," in an acid solution. The hexavalent chromium is partially reduced to trivalent chromium during the reaction, with a concurrent rise in pH, forming a complex mixture consisting largely of hydrated basic chromium chromate and hydrous oxides of both chromium and the basis metal. The composition of the film is rather indefinite, because it contains varying quantities of the reactants, reaction products, and water of hydration, as well as the associated ions of the particular systems.

There are a number of factors that affect both the quality and the rate of formation of chromate coatings. Of the following items, some ar e peculiar to chromating; many derive simply from good shop practice. A working understanding of these factors will be helpful in obtaining high-quality, consistent results. Different formulations are required to produce satisfactory chromate films on various metals and alloys. Similarly, the characteristics of the chromate film produced by any given solution can vary with minor changes in the metal or alloy surface. Commonly encountered examples of this follow.

501

Effect of Basis Metals Aluminum Alloys. The ease with which coatings on aluminum carl be produced, and the

degree of protection afforded by them, can vary significantly with the alloying constituents and/or the heat treatment of the part being processed. In general, low alloying constituent metals that are not heat treated are easiest to chromate and provide the maximum resistance to corrosion. Conversely, wrought aluminum, which is high in alloying elements (especially silicon, copper, or zinc) or which has undergone severe heat treatment, is more difficult to coat uniformly and is more susceptible to corrosive attack. High silicon casting alloys present similar problems. The effect of these metal differences, however, can be minimized by proper attention to the cleaning and pretreatment steps. Most proprietary treatment instructions contain detailed information regarding cleaning, desmutting, etc., of the various alloys.

Magnesium Alloys. As in the case of aluminum, the alloying element content and the type of heat treatment affect the chromating of magnesium. With the exception of the dichromate treatments listed as Type III in Military Specification MIL-M-3171, all of the treatments available can be used on all the tnagnesium alloys.

Zinc Alloys. Chromate conversion coatings on zinc electroplate are affected by impurities codeposited with the zinc. For example, dissolved cadmium, copper, and lead in zinc plating solutions can ultimately cause dark chromated films. Similarly, dissolved iron in noncyanide zinc plating solutions can create chromating problems. Furthermore, the activity of zinc deposits from cyanide and noncyanide solutions can differ sufficiently to produce variations in the chromate film character.

Variations in the composition of zinc die casting alloys and hot-dipped galvanized surfaces can also affect chromate film formation; however, in the latter case, the result is usually difficult to predict, due to the wide variations encountered in spelter composition, cooling rates, etc. Large differences in the chromate coating from spangle to spangle on a galvanized surface are not uncommon. This is especially evident in the heavier films.

Copper Alloys. Since chromate treatments for copper and its alloys can be used to polish chemically as well as to form protective films, the grain structure of the part becomes important, in addition to its alloying content. Whereas fine-grained, homogeneous material responds well to chromate polishing, alloys such as phosphor bronze and heavily leaded brass usually will acquire a pleasing but matte finish. ! n addition, treatment of copper alloys, which contain lead in appreciable amounts, may result in the formation o f a surface layer of powdery, yellow lead chromae.

Effects of pH One of the more important factors in controlling the formation of the chromate film is the

pH of the treatment solution. For any given metal/chromate solution system, there will exist a pH at which the rate of coating formation is at a maximum. As the pH is lowered from this point, the reaction products increasingly become more soluble, tending to remain in solution rather than deposit as a coating on the metal surface. Even though the rate of metal dissolution increases, the coating thickness will remain low. Chemical-polishing chromates for zinc, cadmium, and copper are purposely operated in this low pH range to take advantage of the increased rate of metal removal. The chromate films produced in these cases can be so thin that they are nearly invisible. Beyond this point, further lowering 'of the pH is sufficient to convert most chromate treatments into simple acid etchants.

Increasing the pH beyond the maximum noted above will gradually lower the rate of metal dissolution and coating formation to the point at which the reaction, for all practical purposes, ceases.

Hexavalent Chromium Concentration Although the presence of hexavalent chromium is essential, its concentration in many

treatment solutions can vary widely with limited effect, compared with that of pH. For

502

with the New Look in Metal Fi ... nishing Processes from

D E V E ' C O C O R P O R A T I O N

METAL FINISHING CHEMICALS & PROCESSES * Chromate Conversion • Aluminum Finishing

Coatings • Black Oxide Finishing • Cleaners • Heat Treating • Plating Brighteners • Phosphate Coatings

.(ZN, NI, CAD, CHROME, COPPER) • Rust Preventatives

424 Fairview. Street • Belvidere, IL 61008 • 815/544-9797 • FAX 815/544:-5188

example, the chromium concentration in a typical aluminum treatment solution can varyas much as 100% without substantially affecting the film-formation rate, as long as the pH is held constant. In chromating solutions for zinc or cadmium, the hexavalent chromium can vary fairly widely from its optimum concentration if the activator component is in the proper ratio and the pH is constant.

Activators Chromate films normally will not form without the presence of certain anions in

regulated amounts. They are commonly referred to as "activators' and include acetate, formate, sulfate, chloride, fluoride, nitrate, phosphate, and sulfamate ions. The character, rate of formation, and properties of the chromate film vary with the particular activator and its concentration. Consequently, many proprietary formulations have been developed for specific applications and they are the subject of numerous patents. Usually, these proprietary processes contain the optimum concentrations of the activator and other components; therefore, the user need not be concerned with the selection, separate addition, or control of the activator.

OPERATING CONDITIONS

In addition to the chemical make-up of the chromating solution, the following factors also govern film formation. Once established for a given operation, these parameters should be held constant.

Treatment Time. Immersion time, or contact time of the metal surface and the solution, can vary from as little as 1 second to as much as 1 hour, depending on the solution being used and metal being treated. If prolonged treatment times are required to obtain desired results, a fault in the system is indicated and should be corrected.

Solution Temperature. Chromating temperatures vary from ambient to boiling, depend- ing on the particular solution and metal being processed. For a given.system, an increase in the -solution temperature will accelerate both. the film-forming rate and the rate of attack on the metal surface. Thiskcan result in- a change in the character of the chromate film. Thus, temperatures should be adequately maintained to ensure consistent results.

Solution Agitation. Agitation of the working solution, or movement of the work in the solution, generally speeds the reaction and proyides more uniform film formation. Air agitation and spraying have been used for this purpose. There are, however, a few exceptions where excessive agitation will-produce unsatisfactory films.

Solution Contamination Although the presence of an activator in most treatment solutions is vital, an excessive

concentration of this component, or the presence of the wrong activator, can be very detrimental. Most metal-finishi~ng operations include sources of potential activator contami~ nation in the form of cleaners, pickles, deoxidizers, and desmutters. Unlessproper precautions are taken, the chromate solution can easily become contaminated through drag-in of inadequately rinsed parts, drippage from racks carried over the solution, etc.

A common'source of contamination is that resulting from improperly cleaned work. If allowed to go unchecked, soils can build on the surface of the solution to the point at which even cleanwork becomes resoiled on entering the treatment tank, resulting in.blotchy, uneven coatings.

Other contaminants to be considered are those produced by the reactions occurring in the treatment solution itself. With very few exceptions, part of the trivalent chromium formed and

504

part of the basis metal dissolved during the coating reaction remain in the solution. Small' amounts of these contaminants can be beneficial, and "broken-in" solutions often produce more consistent results. As the concentration of these metal contaminants increases, effective film formation will be inhibitedl For a certain period, this effect can be counteracted by adjustments, such as lowered pH and increased hexavalent chromium concentration. Even- tually, eyen these techniques become ineffective, at which point the solution must be discarded or a portion withdrawn and replaced with fresh solution.

Rinsing and Drying Once a chromate film has been formed satisfactorily, the surface should be rinsed as soon

as possible. Transfer times from the chromating stage to the rinsing stage should be short in order to minimize the continuing reaction that takes place on the part.

Although rinsing should be thorough, this step can also affect the final character of the chromate film and should be controlled with respect to time and temperature, for consistent results.

Prolonged rinsing or the use of very hot rinsewater can dissolve, or leach, the more soluble hexavalent chromium compounds from a freshly formed coating, resulting in a decrease in protective value. I fa hot rinse is used to aid drying, avoid temperatures over about 150°F (66°C) for more than a few seconds. This leaching effect sometimes is used to advantage. In instances in which a highly colored or iridescent coating may be objectionable, a prolonged rinse in hot water can be used as a "bleaching" step to bring the color to an acceptable level. Instead of hot water leaching, some systems incorporate dilute acids and alkalis to accelerate this step.

Solution Control Because most chromate processes are proprietary, it is suggested that the suppliers'

instructions be followed for solution make-up and control. Even though specific formulations- will not be discussed, certain general principles can be outlined, which apply generally to chromate solutions. The combination of hexavalent chromium concentration, activator type and concentration, and pH, i.e., the "chemistry" of the solution, largely determines the type of coating that will be obtained, or whether a coating can be obtained at all, at given temperatures and immersion times. It is important that these factors making up the "chemistry" of the solution be properly controlled. As the solution is depleted through use, it is replenished by maintenance additions,.as indicated by control tests or the appearance of the work.

Fortunately, analysis for each- separate ingredient in a chromate bath is not necessary for proper control. A very effective control method uses pH and hexavalent chromkrm analysis. The pH is determined with a pH meter and the chromium is determined by a simple titration. Indicators and pH papers are not recommended because of discoloration by the chromate solution. Additions are made to the solution to keep these two factors within operating limits. The amount of control actually required for a given treatment depends on how wide its operating limits are, and on the degree of uniformity of resnlts desired. Control by pH alone is adequate in some cases.

COATING EVALUATION

Chromate conversion coatings are covered by many internal company standards and/or U.S. government and American Society for Testing and Materials (ASTM) specifications. These standards usually contain sections on the following methods of evaluation.

505

Table II. Typical Salt Spray Data for Electroplated Zinc

Treatment Hours to White Corrosion

Untreated <8 Clear chromate 24-100 Iridescent yellow 100-200 Olive drab 100-500

Visual Inspection The easiest way to evaluate chromate conversion coatings is to observe the color,

uniformity of appearance, smoothness, and adhesion. Type of color and iridescence is a guide to film thickness, which is considered proportional to protective value; however, visual inspection by itself is not sufficient to indicate the protective value of the coating, especially if the film has been overheated during drying.

Accelerated Corrosion Test The salt spray test, ASTM B 117, is the most common accelerated test developed in

specification form. Although some disagreement exists as to the correlation of salt spray tests to actual performance, it remains in many specifications. Variations in results are often obtained when tested in different salt spray cabinets, and even in different locations within the same cabinet. Coatings should be aged for at least 24 hours before testing, for consistent results. Generally, specifications require a minimum exposure time before visible corrosion forms. Typical salt spray test data are provided in Tables II to IV.

Humidity Tests There appears to be no standard specification covering humidity tests for unpainted

chromate conversion coatings. Evaluations are conducted under various conditions and cycles. Humidity tests may be more useful than salt spray tests, as they correspond to the normal environment better than the salt spray, except in marine atmospheres.

Table III. Typical Salt Spray Data for Copper and Brass

Treatment Hours to Green Corrosion

Copper, untreated <24 Copper, bright chromate 24 Copper, heavy chromate 50 Brass, untreated 24 Brass, bright chromate 100 Brass, heavy chromate 150

Table IV. Typical Salt Spray Data for Aluminum

Hours to White Corrosion

Alloy No Treamwnt Clear Yellow-Brown

3003 24 60-120 250-800 2024 ~ <24 40-80 150=600 413.0 <24 12-24 50-250

~Heat treatment will affect the final results.

506

Water Tests Immersion tests in distilled or deionized water have proven valuable in simulating such

conditions as water accumulation in chromated zinc die castings, e.g., carburetors and fuel pumps.

Coatings applied on hot-dipped galvanized surfaces in strip mills are often tested by stacking wet sheets and weighing the top sheet. Periodic checks are made to determine when corrosion products first develop. The tests should be conducted at relatively constant temperatures to ensure consistent results.

Chemical and Spot Tests The amount of hexavalent chromium in the film can be an indication of the corrosion

protection afforded by the coating. Analytical procedures for small amounts of chromium on treated surfaces are comparatively rapid, quantitative, and reproducible. Consequently, chemical analysis for the chromium content of the film appears to be a valuable tool. It would not be suitable, however, for predicting the performance of bleached, overheated, excessively dehydrated coatings.

Total coating weight is sometimes used as an indication of corrosion resistance. It is derived by weighing a part having a known surface area before and after chemically stripping only the chromate film.

Spot tests are used to test corrosion resistance by dissolving the chromate coating and reacting with the basis metal. The time required to produce a characteristic spot determines empirically the film thickness or degree of corrosion protection. It is advisable to use these tests as comparative tests only, always spotting an untreated and treated surface at the same time. Frequently, the spot tests are sufficient only to indicate differences between treated and untreated surfaces. Reproducibility is not good because aging affects the results.

Performance Tests for Organic Finishes Paint, lacquer, and other organic finishes on chromate conversion coatings are tested in

numerous ways to evaluate bonding and corrosion protection. These include pencil-hardness, cross-hatch, bending, impact, and tape tests with or without prior exposure to water or salt spray.

SPECIFICATIONS

A list of the more commonly used specifications covering chromate conversion coatings on different basis metals follows. Only the basic specification or standard number is listed, and reference should be made only to the appropriate revision of any particular document.

Aluminum

AMS 2473--Chemical Treatment for Aluminum Base A l loys~ene r a l Purpose Coat- ing

AMS 2474~Chemical Treatment for Aluminum Base Alloys--Low Electrical Resis- tance Coating

ASTM D 1730~Pieparation of Aluminum and Aluminum Alloy Surfaces for Painting MIL-C-5541~hemical Films and Chemical Film Material for Aluminum and Alumi-

num Alloys MIL-C-8170~Chemical Conversion Materials for Coating Aluminum and Aluminum

Alloys MIL-W-6858--Welding, Resistance: Aluminum, Magnesium, etc.; Spot and Seam

507

Cadmium

AMS 2400--Cadmium Plating AMS 2416--Nickel-Cadmium Plating, Diffused AMS 2426--Cadmium Plating, Vacuum Deposition ASTM B 201--Testing Chromate Coatings on Zinc and Cadmium Surfaces MIL-C-8837--Cadmium Coating (Vacuum Deposited) QQ-P-416--Plating, Cadmium (Electrodeposited)

Magnesium

AMS 2475 Protective Treatments, Magnesium Base Alloys MIL-M-3171--Magnesium Alloy, Process for Pretreatment and Prevention of Corrosion

on MIL-W-6858--Welding, Resistance: Aluminum, Magnesium, etc.; Spot and Seam

Silver

QQ-S-365--Silver Plating, Electrodeposited, General Requirements for

Zinc

AMS 2402 Zinc Plating ASTM B 201~Test ing Chromate Coatings on Zinc and Cadmium Surfaces ASTM D 2092--Preparation of Zinc-Coated Steel Surfaces for Painting MIL-A-81801--Anodic Coatings for Zinc and Zinc Alloys MIL-C-17711--Coatings, Chromate, for Zinc Alloy Castings and Hot-Dip Galvanized

Surface MIL-T-12879--Treatments, Chemical, Prepaint and Corrosion Inhibitive, for Zinc

Surfaces MIL-Z-17871--Zinc, Hot-Dip Galvanizing QQ-Z-325--Zinc Coating, Electrodeposited, Requirements for

SPECIAL TREATMENTS

Solutions containing chromium compounds are used in some processes where disagree- ment exists" as to whether these form "true" chromate conversion coatings or combination coatings, or act as passivating processes.

Electrolytic Processes Although early chromate conversion coatings for zinc were electrolytically applied, this

method has been largely replaced by immersion processes. More recently, the use of electric current has reappeared with solutions containing mixtures of chromates, phosphates, fluorides, etc., to produce "anodic coatings." The coatings, however, are not similar to anodic coatings such as those produced on aluminum. The coatings on zinc surfaces are complex combinations of chromates, phosphates, oxides, etc. They are formed with 100-200 V AC or

508

DC, and the flitted coating will withstand more than 1,000 hr of salt spray. The process is used where outstanding corrosion resistance is needed. The coating also exhibits superior hardness, heat resistance, thickness, and dielectric strength when compared with normal chromate conversion coatings. Colors range from dark green to charcoal for different processes.

Electrolytic treatments using chromium compounds are also applied to steel strip, where chromium along with oxides, etc., are deposited in a very thin, discontinuous film. These processes, which promote lacquer and paint adhesion, may be more chromium plate than chromate coating.

Coatings on Beryllium It has been reported that chromate conversion coatings can be applied to beryllium to

retard high-temperature oxidation in humid air.

Chromate-Phosphate Treatments Chromate-phosphate treatments are based on chromate-phosphate mixtures and form a

combination conversion coating on aluminum. The coating can appear practically colorless to a light-green hue. These treatments have been used to impact color for decorative purposes or to provide an imposed base for subsequent lacquer or paint operations.

C o n t i n e n t a l 5 u r l ~ c w

Tr®a#nent; , Inc,

C o n t i n e n t a l S u r f a c e T r e a t m e n t 6801 Engle Rd., Suite J, M i dd l ebu rg Hrs., Ohio 44130

P.O. Box 81873, Cleveland, Ohio 44181 Phone: 440-239-9710 • Fax: 440-239-9705

1--888-CST-TREAT (1-888-278-8732) E-mail: CSTvlatin~@aol.com

v

CST is p r o u d to in t roduce its n e w line of Trivalent Conversion Coatings Futura III, Fu tu ra Plus and Chromiting

Exclusively from SurTec ® GmbH, Germany

• Pa ten ted h igh corrosion Clear-Blue Chromate Fu tu ra III and Fu tu ra P lus u p to 50 hou r s neut ra l sal ts sp ray

• C h r o m i t i n g ®, for the e l iminat ion of hexavalen t -ve l low ch rome convers ion coatings, this l ight green yel low ir idescent ch roma te is Heat Treatable resul t ing in a m in ima l loss of corrosion protection. Patent p e n d i n g

• Superior Products of Top Qual i ty and Per formance • Economic saving, based on the re la t ionship be t ween price a n d pe r fo rmance • E n v i r o n m e n t a l l y fr iendly p roduc t s easy to ana lyze and was te treat

Continental Surface Treatment also offers a full r ange of spray, soak, and ul trasonic cleaners for all you r c leaning applicat ions. Call or fax u s for more informat ion on these and other a d v a n c e d pla t ing processes.

• Dis t r ibutor inquir ies we l come •

509