BRUKER HTS tape measurementJohn Himbele, Arnaud Badel, Pascal Tixador
2
Outline
• tape specifications ?
• Experimental setups
• Results
• Next steps
3
HTS tape specification
Reference T189 T183 (measured)Ic at 77 K 52 A 46 A
width 4.05 ± 0.03 mm 4.13 mmYBCO 1.7 ± 0.1 µm
Shunt (copper) 25 ± 3 µm x 2Protection (silver) 1.8 ± 0.2 µm
Substrate 97 ± 3 µmTotal thickness 150 ± 5 µm 130 µm
4
Experimental setup in Ø 50 mm
Experimental setup properties
Max. Field 22 T
Max. Current 900 A or more ?
Temperature 4.2 K
Sample length 20 mm
Angle free
Adjust angle of sample
1.3 m
35 mm
Short length measurement
5
Experimental setup in Ø 170 mm
Experimental setup properties
Max. Field 17 T
Max. Current 2 kA
Temperature 4.2 K – 77 K
Sample length 55 mm for measure
Angle 0 and 90°
Adjust angle of sample
1.8 m
115 mm
long length measurement
6
T-183 characteristics at 4.2 K
Critical current under longitudinal field is larger than 900 A between 0 – 21 T.
0 2 5 10 15 20 220
200
400
600
800
1000
1200
Applied magnetic field (T)
Crit
ical
cur
rent
(A)
Ic transverseIc longitudinal (Lower boundary)
375
750
1125
1500
1875
2250
Crit
ical
cur
rent
den
sity
(A/m
m²)
Test made on full width
in Ø50 probe
Je = 405 A/mm² at 18 T ┴
(Ic = 215 A)
Next steps
7
• Test performances of new Ø 50 mm probe above 900 A
• Conduct measurements in Ø 170 mm to cross check results on longer samples
• What of n- value ? Needed for quench calculations !
? Extrapolation for Jc measurement leads to n = 45 : doubtful? Possibilities to test with pulse measurements
Work ongoing with F. Sirois from Montreal on pulse characterization under high field :