BEND & REBEND MACHINE
File Content:
1. Related Standards 2. Product Photos 3. Attachments 4. Technical Specifications 5. Operating 6. References
RELATED STANDARDS
- TS 708 : Steel for the Reinforcement of Concrete – Reinforcing (Turkey) Steel
- BS 4449:2005 + A2:2009 : Steel for Reinforcement of Concrete. Weldable (England) Reinforcing Steel. Bar, Coil and Decoiled Product. Specification.
- DIN 488-7:1986-06 : Reinforcing Steel, Verification of Weldablity of
(Germany) Reinforcing Steel Bars, Test Procedure and Evaluation
- ASTM A615 / A615M – 09a : Standard Specification for Deformed and Plain Carbon-(USA) Steel Bars for Concrete Reinforcement
-----------------------------------------------------------
TS 708
- Bend and Rebend Tests should be conducted on the equipment shown in Figure II. - Bend Test is applied by bending the specimen through an angle of 180°
- Rebend Test consists of bending the specimen through an angle of 90°, and rebending
through at least 45°.
BS 4449
Bend Test ;
When a bend test is requested the specimens selected shall be of sufficient length to ensure free bending. The apparatus used shall provide:
a) continuous and uniform application of force throughout the duration of the bending operations;
b) unrestricted movement of the specimen at points of contact with the apparatus and bending around a pin free to rotate; and
c) close wrapping of the specimen around the pin during the bending operation.
Rebend Test ;
o Sequence of operations
When a rebend test is requested, specimens shall be subjected to the following.
a) The specimen shall be bent through an angle of 45°, and at a temperature of between 5 °C and 30 °C, so as to produce a continuous and uniform bending deformation (curvature) at every section of the bend. The test shall be conducted either:
1) on a bending machine in which the test specimen is supported by plain smooth surfaces or rolls that do not resist longitudinal movement of the test piece; or
2) on a three-point hydraulic bending machine.
The test machine shall be serviceable and able to impart a constant load to the specimen, and
shall be without impact effect. The maximum bending rate shall be 3 rad/min or equivalent. b) The test specimen shall be heated to 100 °C and maintained at this temperature for at least 30 min. NOTE: The method of heating is at the discretion of the manufacturer. c) The test specimen shall be allowed to cool to a temperature of between 5 °C and 30 °C, and partially re-straightened by a steadily applied force, through at least 23°, on the bending machine used in (a).
o Failure in relation to rib damage
In the event of a specimen failing the rebend test, if there is any damage to the ribs caused by carrying out the initial bending, the test shall be considered invalid, and shall be repeated on another specimen.
PRODUCT PHOTOS
ATTACHMENTS
TECHNICAL SPECIFICATIONS
Engine 5,5 kW Electrical Engine
Capacity 6 mm – 50 mm (with 45 kg/mm2 Strength)
Operating Weight 850 kg
Transportation Weight (Wooden Case) 1215 kg
Operating Dimensions 90 x 120 x 100 cm
Transportation Dimensions (Wooden Case) 100 x 127 x 133 cm
Operating Voltage 380 Volt
Power Transmission Mechanical
Speed Control 3 r/min ± 50 %
Bending Radius 6 mm – 175 mm
Control Panel Digital Control Panel
Memory Feature Memorizes up to 10 different angles for 10
different works
Counting Feature Electronic Counter on Digital Panel
Bending Direction Clockwise and Counterclockwise
OPERATING
REFERENCES
1. Qatar Steel Company, Mesaieed / QATAR
2. Dubai Municipality, Dubai / UAE (via Dutco Tennant LLC)
3. Demirsan Haddecilik Sanayi ve Ticaret A.S., Kocaeli / TURKEY