Subpart 2
PHYSICAL PROPERTIES TABLES
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TE-1 2001 SECTION II
TABLE TE-1THERMAL EXPANSION FOR FERROUS MATERIALS
Coefficients for Carbon and Coefficients for OtherLow Alloy Steels (Group 1) Low Alloy Steels (Group 2) Coefficients for 5Cr1Mo
[Note (1)] [Note (2)] and 29Cr7Ni2MoN SteelsTemperature,
F A B C A B C A B C
70 6.4 6.4 0 7.0 7.0 0 6.5 6.4 0100 6.5 6.5 0.2 7.1 7.1 0.3 6.6 6.5 0.3150 6.7 6.6 0.6 7.3 7.2 0.7 6.7 6.6 0.7200 6.9 6.7 1.0 7.5 7.3 1.1 6.8 6.7 1.1250 7.1 6.8 1.5 7.6 7.3 1.6 6.9 6.8 1.5
300 7.3 6.9 1.9 7.7 7.4 2.1 7.0 6.9 1.9350 7.5 7.0 2.4 7.9 7.5 2.5 7.2 6.9 2.3400 7.7 7.1 2.8 8.0 7.6 3.0 7.3 7.0 2.8450 7.8 7.2 3.3 8.1 7.6 3.5 7.4 7.0 3.2500 8.0 7.3 3.7 8.3 7.7 4.0 7.4 7.1 3.6
550 8.2 7.3 4.2 8.4 7.8 4.5 7.5 7.1 4.1600 8.4 7.4 4.7 8.5 7.8 5.0 7.6 7.2 4.6650 8.5 7.5 5.2 8.6 7.9 5.5 7.7 7.2 5.0700 8.6 7.6 5.7 8.6 7.9 6.0 7.8 7.2 5.5750 8.8 7.7 6.3 8.7 8.0 6.5 7.9 7.3 5.9
800 8.9 7.8 6.8 8.8 8.1 7.1 8.0 7.3 6.4850 9.0 7.9 7.3 8.8 8.1 7.6 8.0 7.4 6.9900 9.1 7.9 7.9 8.9 8.1 8.1 8.1 7.4 7.4950 9.2 8.0 8.4 9.0 8.2 8.7 8.2 7.4 7.9
1000 9.3 8.1 9.0 9.0 8.2 9.2 8.2 7.5 8.4
1050 9.4 8.1 9.6 9.0 8.3 9.7 8.3 7.5 8.91100 9.5 8.2 10.1 9.1 8.3 10.3 8.3 7.6 9.41150 9.5 8.3 10.7 9.1 8.3 10.8 8.4 7.6 9.91200 9.6 8.3 11.3 9.1 8.4 11.4 8.5 7.6 10.41250 9.6 8.4 11.8 9.1 8.4 11.9 8.5 7.7 10.9
1300 9.6 8.4 12.4 9.1 8.4 12.4 8.5 7.7 11.41350 . . . . . . . . . 9.1 8.5 13.0 8.6 7.7 11.91400 . . . . . . . . . 9.1 8.5 13.5 8.6 7.8 12.41450 . . . . . . . . . 9.1 8.5 14.1 . . . . . . . . .1500 . . . . . . . . . 9.1 8.5 14.6 . . . . . . . . .
648
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-1Table TE-1
TABLE TE-1 (CONTD)THERMAL EXPANSION FOR FERROUS MATERIALS
Coefficients for Coefficients for Coefficients for9Cr1Mo Steels 5Ni1/4Mo Steels 8Ni and 9Ni SteelsTemperature,
F A B C A B C A B C
70 5.8 5.8 0 6.2 6.2 0 5.5 5.5 0100 5.9 5.9 0.2 6.3 6.3 0.2 5.7 5.6 0.2150 6.0 5.9 0.6 6.6 6.4 0.6 6.0 5.8 0.6200 6.2 6.0 0.9 6.7 6.5 1.0 6.3 5.9 0.9250 6.3 6.1 1.3 6.9 6.6 1.4 6.5 6.1 1.3
300 6.4 6.2 1.7 7.1 6.7 1.8 6.6 6.2 1.7350 6.5 6.2 2.1 7.2 6.8 2.3 6.8 6.3 2.1400 6.6 6.3 2.5 7.4 6.8 2.7 6.9 6.4 2.5450 6.8 6.3 2.9 7.5 6.9 3.2 7.0 6.5 3.0500 6.9 6.4 3.3 7.6 7.0 3.6 7.2 6.6 3.4
550 7.0 6.5 3.7 7.8 7.1 4.1 7.3 6.6 3.8600 7.1 6.5 4.1 7.9 7.1 4.5 7.4 6.7 4.3650 7.2 6.6 4.6 8.0 7.2 5.0 7.5 6.7 4.7700 7.3 6.6 5.0 8.1 7.3 5.5 7.5 6.8 5.1750 7.4 6.7 5.4 8.2 7.3 6.0 7.6 6.8 5.6
800 7.4 6.7 5.9 8.3 7.4 6.5 7.6 6.9 6.0850 7.5 6.8 6.3 8.4 7.5 7.0 7.7 6.9 6.5900 7.6 6.8 6.8 8.5 7.5 7.5 7.7 7.0 6.9950 7.7 6.9 7.3 8.6 7.6 8.0 7.8 7.0 7.4
1000 7.8 6.9 7.7 8.7 7.6 8.5 7.8 7.0 7.8
1050 7.8 7.0 8.2 8.8 7.7 9.1 . . . . . . . . .1100 7.9 7.0 8.7 8.8 7.8 9.6 . . . . . . . . .1150 8.0 7.1 9.1 8.9 7.8 10.1 . . . . . . . . .1200 8.0 7.1 9.6 9.0 7.9 10.7 . . . . . . . . .1250 8.1 7.1 10.1 . . . . . . . . . . . . . . . . . .
1300 8.1 7.2 10.6 . . . . . . . . . . . . . . . . . .1350 . . . . . . . . . . . . . . . . . . . . . . . . . . .1400 . . . . . . . . . . . . . . . . . . . . . . . . . . .1450 . . . . . . . . . . . . . . . . . . . . . . . . . . .1500 . . . . . . . . . . . . . . . . . . . . . . . . . . .
649
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TE-1 2001 SECTION II
TABLE TE-1 (CONTD)THERMAL EXPANSION FOR FERROUS MATERIALS
Coefficients for 12Cr,12Cr1Al, 13Cr, and Coefficients for Coefficients for
13Cr4Ni Steels 15Cr and 17Cr Steels 27Cr SteelsTemperature,
F A B C A B C A B C
70 5.9 5.9 0 5.3 5.3 0 5.0 5.0 0100 6.0 6.0 0.2 5.4 5.4 0.2 5.1 5.1 0.2150 6.2 6.1 0.6 5.5 5.5 0.5 5.1 5.1 0.5200 6.3 6.2 1.0 5.7 5.5 0.9 5.2 5.2 0.8250 6.4 6.2 1.4 5.8 5.6 1.2 5.3 5.2 1.1
300 6.5 6.3 1.7 5.9 5.7 1.6 5.4 5.2 1.4350 6.6 6.4 2.1 6.0 5.7 1.9 5.4 5.3 1.8400 6.7 6.4 2.5 6.1 5.8 2.3 5.5 5.3 2.1450 6.7 6.4 2.9 6.2 5.8 2.7 5.6 5.3 2.4500 6.8 6.5 3.3 6.3 5.9 3.0 5.7 5.4 2.8
550 6.8 6.5 3.8 6.4 5.9 3.4 5.7 5.4 3.1600 6.9 6.5 4.2 6.5 6.0 3.8 5.8 5.4 3.5650 6.9 6.6 4.6 6.5 6.0 4.2 5.9 5.5 3.8700 7.0 6.6 5.0 6.6 6.1 4.6 5.9 5.5 4.2750 7.1 6.6 5.4 6.7 6.1 5.0 6.0 5.5 4.5
800 7.1 6.7 5.8 6.8 6.1 5.3 6.1 5.6 4.9850 7.2 6.7 6.3 6.8 6.2 5.8 6.2 5.6 5.3900 7.2 6.7 6.7 6.9 6.2 6.2 6.2 5.7 5.6950 7.3 6.8 7.1 7.0 6.3 6.6 6.3 5.7 6.0
1000 7.3 6.8 7.6 7.0 6.3 7.0 6.4 5.7 6.4
1050 7.3 6.8 8.0 7.1 6.3 7.5 6.4 5.8 6.81100 7.4 6.8 8.4 7.1 6.4 7.9 6.5 5.8 7.21150 7.4 6.9 8.9 7.2 6.4 8.3 6.6 5.8 7.61200 7.4 6.9 9.3 7.2 6.4 8.7 6.7 5.9 7.91250 7.5 6.9 9.8 7.2 6.5 9.2 6.7 5.9 8.3
1300 7.5 6.9 10.2 7.3 6.5 9.6 6.8 5.9 8.81350 7.5 7.0 10.7 7.3 6.5 10.0 6.9 6.0 9.21400 7.6 7.0 11.1 7.3 6.6 10.5 6.9 6.0 9.61450 7.6 7.0 11.6 7.3 6.6 10.9 7.0 6.0 10.01500 7.6 7.0 12.0 7.4 6.6 11.4 7.1 6.1 10.4
650
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-1Table TE-1
TABLE TE-1 (CONTD)THERMAL EXPANSION FOR FERROUS MATERIALS
Coefficients for OtherCoefficients for Austenitic Austenitic StainlessStainless Steels (Group 3) Steels (Group 4) Coefficients for
[Note (3)] [Note (4)] Ductile Cast IronTemperature,
F A B C A B C A B C
70 8.5 8.5 0 8.7 8.2 0 . . . 5.7 0100 8.7 8.6 0.3 8.8 8.2 0.3 . . . 5.8 0.2150 9.0 8.8 0.8 8.9 8.4 0.8 . . . 5.9 0.6200 9.3 8.9 1.4 9.0 8.5 1.3 . . . 6.0 0.9250 9.6 9.1 2.0 9.1 8.6 1.8 . . . 6.1 1.3
300 9.8 9.2 2.5 9.1 8.8 2.4 . . . 6.3 1.7350 10.0 9.3 3.2 9.2 8.8 3.0 . . . 6.4 2.1400 10.2 9.5 3.7 9.2 8.9 3.5 . . . 6.5 2.6450 10.3 9.6 4.3 9.2 9.0 4.1 . . . 6.7 3.0500 10.4 9.7 5.0 9.3 9.1 4.7 . . . 6.9 3.5
550 10.6 9.8 5.6 9.3 9.1 5.3 . . . 6.9 4.0600 10.7 9.8 6.3 9.4 9.2 5.8 . . . 7.0 4.4650 10.8 9.9 6.9 9.4 9.2 6.4 . . . 7.0 4.9700 10.9 10.0 7.6 9.4 9.3 7.0 . . . 7.1 5.4750 11.0 10.0 8.2 9.5 9.3 7.6 . . . 7.2 5.9
800 11.1 10.1 8.8 9.5 9.4 8.2 . . . 7.3 6.4850 11.1 10.1 9.5 9.6 9.4 8.8 . . . 7.3 6.9900 11.2 10.2 10.2 9.6 9.5 9.5 . . . 7.4 7.4950 11.3 10.3 10.8 9.7 9.6 10.1 . . . 7.4 7.9
1000 11.4 10.3 11.5 9.7 9.6 10.7 . . . 7.5 8.4
1050 11.5 10.4 12.2 9.8 9.7 11.4 . . . . . . . . .1100 11.6 10.5 12.9 9.8 9.7 12.0 . . . . . . . . .1150 11.6 10.5 13.6 9.9 9.8 12.7 . . . . . . . . .1200 11.7 10.6 14.3 9.9 9.8 13.3 . . . . . . . . .1250 11.8 10.6 15.0 9.9 9.9 14.0 . . . . . . . . .
1300 11.9 10.7 15.7 10.0 9.9 14.7 . . . . . . . . .1350 11.9 10.7 16.4 10.0 10.0 15.3 . . . . . . . . .1400 12.0 10.8 17.2 10.1 10.1 16.0 . . . . . . . . .1450 12.1 10.8 17.9 10.2 10.1 16.7 . . . . . . . . .1500 12.1 10.8 18.6 10.2 10.2 17.5 . . . . . . . . .
651
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TE-1 2001 SECTION II
TABLE TE-1 (CONTD)THERMAL EXPANSION FOR FERROUS MATERIALS
Coefficients for PrecipitationHardened 17Cr4Ni4Cu
Stainless Steels [Note (5)]Temperature,
F A B C
70 5.9 5.9 0100 5.9 5.9 0.2150 5.9 5.9 0.6200 5.9 5.9 0.9250 5.9 5.9 1.3
300 5.9 5.9 1.6350 5.9 5.9 2.0400 5.9 5.9 2.3450 5.9 5.9 2.7500 5.9 5.9 3.1
550 5.9 5.9 3.4600 6.0 5.9 3.8650 6.0 5.9 4.1700 6.0 5.9 4.5750 6.1 6.0 4.9800 6.1 6.0 5.2
Notes appear on following page.
652
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
A02
PART D PROPERTIES Table TE-1Table TE-1
NOTES TO TABLE TE-1
GENERAL NOTES:(a) Coefficient A is the instantaneous coefficient of thermal expansion 106 (in./in./F). Coefficient B is the mean coefficient of thermal
expansion 106 (in./in./F) in going from 70F to indicated temperature. Coefficient C is the linear thermal expansion (in./100 ft) ingoing from 70F to indicated temperature.
(b) For SI units, multiply coefficients A and B by 1.8 to convert to mm/mm/C and divide coefficient C by 2.16 to convert to mm/(mWC).(c) See Table SI-1 for the conversion of temperatures to degrees Celsius.
NOTES:(1) Group 1 alloys (by nominal composition):
Carbon steel 1Cr15MoSi34Ni
12Mo13CrV
CMnCb 1Cr12Mo34Ni
12MoCrVCMnSiCb 1Cr12MoV
34Ni1Mo34Cr
CMnSiV 114Cr12Mo 1Ni
12Cr12Mo
CMnTi 114Cr12MoSi 1
14Ni1Cr12Mo
CSiTi 134Cr12MoCu 1
34Ni34Cr
14MoC14Mo 1
34Cr12MoTi 2Ni
34Cr14Mo
C12Mo 2Cr12Mo 2Ni
34Cr13Mo
12Cr15Mo 2
14Cr1Mo 2Ni112Cr
14MoV12Cr
15MoV 3Cr1Mo 212Ni
12Cr14MoSi
12Ni12Cr
14Mo 234Ni1
12Cr12MoV
12Cr12Mo
12Ni12Cr
14MoV 312Ni
34Cr12NiCu
12Ni12MoV 3
12Ni134Cr
12MoV34Cr
34NiCuAl34Ni
12Cr12MoV 4Ni1
12Cr12MoV
1Cr15Mo34Ni
12CuMo(2) Group 2 alloys (by nominal composition):
Mn14Mo Mn12Mo
34Ni 22Cr5Ni3MoNMn12Mo MnV 23Cr4NiMoCuMn12Mo
14Ni 18Cr5Ni3MoN 25Cr7Ni4MoNMn12Mo
12Ni(3) Group 3 alloys (by nominal composition):
16Cr12Ni2Mo 18Cr8NiN 18Cr13Ni3Mo16Cr12Ni2MoN 18Cr10NiCb 18Cr18Ni2Si16Cr12Ni2MoTi 18Cr10NiTi 19Cr9NiMoW18Cr8Ni 18Cr11Ni 21Cr11NiN
(4) Group 4 alloys (by nominal composition):29Ni20Cr3Cu2Mo 23Cr12Ni 25Cr20Ni2Mo20Cr18Ni6Mo 25Cr12Ni 31Ni31Fe29CrMo22Cr13Ni5Mn 25Cr20Ni 44Fe25Ni21CrMo
(5) These thermal expansion values are representative of solution annealed material. Subsequent precipitation hardening treatments may affectthermal expansion behavior.
653
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TE-2 2001 SECTION II
TABLE TE-2THERMAL EXPANSION FOR ALUMINUM ALLOYS
Coefficients forAluminum Alloys
Temperature,F A B C
70 12.1 12.1 0100 12.5 12.4 0.5150 12.9 12.7 1.2200 13.3 13.0 2.0
250 13.6 13.1 2.8300 13.9 13.3 3.7350 14.2 13.4 4.5400 14.6 13.6 5.4
450 14.8 13.8 6.3500 14.9 13.9 7.2550 15.2 14.1 8.1600 15.3 14.2 9.0
GENERAL NOTES:(a) Aluminum alloys represented by these thermal expansion
coefficients include:A03560 A93003 A95254A24430 A93004 A95454A91060 A95052 A95456A91100 A95083 A95652A92014 A95086 A96061A92024 A95154 A96063
(b) Coefficient A is the instantaneous coefficient of thermal expansion 106 (in./in./F). Coefficient B is the mean coefficient ofthermal expansion 106 (in./in./F) in going from 70F toindicated temperature. Coefficient C is the linear thermalexpansion (in./100 ft) in going from 70F to indicatedtemperature.
(c) For SI units, multiply coefficients A and B by 1.8 to convertto mm/mm/C and divide coefficient C by 2.16 to convert tomm/(mWC).
(d) See Table SI-1 for the conversion of temperatures to degreesCelsius.
654
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-3Table TE-3
TABLE TE-3THERMAL EXPANSION FOR COPPER ALLOYS
Coefficients for Coefficients for Coefficients forCopper Alloys, Coefficients for Coefficients for CopperNickel CopperNickel
C1XXXX Series Bronze Alloys Brass Alloys (70Cu30Ni) (90Cu10Ni)Temperature,
F A B C A B C A B C A B C A B C
70 . . . 9.3 0 . . . 9.6 0 . . . 9.3 0 . . . 8.1 0 . . . . . . . . .100 . . . 9.4 0.3 . . . 9.7 0.4 . . . 9.4 0.4 . . . 8.2 0.3 . . . . . . . . .150 . . . 9.5 0.9 . . . 9.9 1.0 . . . 9.6 1.0 . . . 8.4 0.9 . . . . . . . . .200 . . . 9.6 1.5 . . . 10.0 1.6 . . . 9.8 1.5 . . . 8.5 1.3 . . . . . . . . .250 . . . 9.6 2.1 . . . 10.1 2.3 . . . 9.9 2.2 . . . 8.6 1.9 . . . . . . . . .
300 . . . 9.7 2.7 . . . 10.1 2.8 . . . 10.0 2.8 . . . 8.7 2.4 . . . . . . . . .350 . . . 9.8 3.2 . . . 10.2 3.5 . . . 10.1 3.4 . . . 8.8 3.0 . . . . . . . . .400 . . . 9.8 3.8 . . . 10.2 4.1 . . . 10.2 4.1 . . . 8.9 3.5 . . . . . . . . .450 . . . 9.9 4.5 . . . 10.3 4.8 . . . 10.4 4.7 . . . 9.0 4.1 . . . . . . . . .500 . . . 9.9 5.1 . . . 10.3 5.3 . . . 10.5 5.4 . . . 9.1 4.7 . . . . . . . . .
550 . . . 10.0 5.6 . . . 10.4 6.0 . . . 10.6 6.1 . . . 9.1 5.2 . . . 9.5 5.5600 . . . 10.0 6.1 . . . 10.4 6.6 . . . 10.7 6.8 . . . 9.2 5.9 . . . . . . . . .650 . . . . . . . . . . . . 10.5 7.3 . . . 10.8 7.5 . . . 9.2 6.4 . . . . . . . . .700 . . . . . . . . . . . . 10.5 8.0 . . . 10.9 8.3 . . . 9.2 7.0 . . . . . . . . .750 . . . . . . . . . . . . 10.6 8.6 . . . 11.0 9.0 . . . . . . . . . . . . . . . . . .800 . . . . . . . . . . . . 10.6 9.3 . . . 11.2 9.8 . . . . . . . . . . . . . . . . . .
GENERAL NOTES:(a) Coefficient A is the instantaneous coefficient of thermal expansion 106 (in./in./F). Coefficient B is the mean coefficient of thermal
expansion 106 (in./in./F) in going from 70F to indicated temperature. Coefficient C is the linear thermal expansion (in./100 ft) in goingfrom 70F to indicated temperature.
(b) For SI units, multiply coefficients A and B by 1.8 to convert to mm/mm/C and divide coefficient C by 2.16 to convert to mm/(mWC).(c) See Table SI-1 for the conversion of temperatures to degrees Celsius.
655
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TE-4 2001 SECTION II
TABLE TE-4THERMAL EXPANSION FOR NICKEL ALLOYS
Coefficients for Coefficients for Coefficients forN02200 and N02201 N04400 and N04405 N06002
Temperature,F A B C A B C A B C
70 6.6 6.6 0 7.7 7.7 0 7.3 7.3 0100 6.8 6.8 0.2 7.8 7.8 0.3 7.4 7.4 0.3150 7.1 7.0 0.7 8.0 7.9 0.8 7.5 7.4 0.7200 7.3 7.2 1.1 8.2 8.1 1.3 7.6 7.5 1.2250 7.5 7.4 1.6 8.4 8.2 1.8 7.7 7.6 1.6
300 7.7 7.5 2.1 8.5 8.3 2.3 7.8 7.6 2.1350 7.8 7.6 2.6 8.7 8.4 2.8 7.9 7.7 2.6400 8.1 7.7 3.1 8.8 8.5 3.4 7.9 7.7 3.1450 8.3 7.8 3.6 8.9 8.6 3.9 8.0 7.8 3.5500 8.4 7.9 4.1 9.0 8.7 4.5 8.1 7.8 4.0
550 8.6 8.0 4.6 9.1 8.8 5.1 8.2 7.9 4.5600 8.7 8.1 5.1 9.2 8.8 5.6 8.3 7.9 5.0650 8.8 8.1 5.6 9.3 8.9 6.2 8.4 8.0 5.6700 8.9 8.2 6.2 9.3 8.9 6.7 8.6 8.0 6.1750 9.0 8.2 6.7 9.4 8.9 7.3 8.8 8.1 6.6
800 9.1 8.3 7.2 9.4 8.9 7.8 9.1 8.2 7.2850 . . . 8.4 7.8 . . . 8.9 8.4 . . . 8.3 7.8900 . . . 8.4 8.4 . . . 9.0 8.9 . . . 8.4 8.3950 . . . 8.5 8.9 . . . 9.0 9.5 . . . 8.4 8.9
1000 . . . 8.5 9.5 . . . 9.1 10.1 . . . 8.5 9.5
1050 . . . 8.6 10.1 . . . 9.1 10.7 . . . 8.6 10.11100 . . . 8.6 10.6 . . . 9.1 11.3 . . . 8.6 10.71150 . . . 8.7 11.2 . . . 9.1 11.8 . . . 8.7 11.31200 . . . 8.7 11.8 . . . 9.2 12.4 . . . 8.8 11.91250 . . . 8.8 12.4 . . . 9.2 13.0 . . . 8.8 12.5
1300 . . . 8.8 13.0 . . . 9.2 13.6 . . . 8.9 13.11350 . . . 8.9 13.6 . . . 9.2 14.2 . . . 9.0 13.81400 . . . 8.9 14.2 . . . 9.3 14.8 . . . 9.0 14.41450 . . . . . . . . . . . . 9.3 15.4 . . . 9.1 15.11500 . . . . . . . . . . . . 9.3 16.0 . . . 9.2 15.7
656
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-4
TABLE TE-4 (CONTD) A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
657
Coefficients forN06007
A B C
7.4 7.4 07.4 7.4 0.37.5 7.5 0.77.6 7.5 1.27.7 7.5 1.6
7.8 7.6 2.17.9 7.6 2.68.0 7.7 3.08.1 7.7 3.58.2 7.8 4.0
8.4 7.8 4.58.6 7.9 5.08.8 8.0 5.69.1 8.1 6.19.4 8.2 6.7
9.7 8.3 7.3. . . 8.4 7.9. . . 8.5 8.5. . . 8.6 9.1. . . 8.7 9.7
. . . 8.7 10.3
. . . 8.8 10.9
. . . 8.9 11.5
. . . 9.0 12.2
. . . 9.1 12.8
. . . 9.1 13.5
. . . 9.2 14.1
. . . 9.2 14.8
. . . 9.3 15.4
. . . 9.4 16.1
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN06022
A B C
. . . 6.9 0
. . . 6.9 0.2
. . . 6.9 0.7
. . . 6.9 1.1
. . . 6.9 1.5
. . . 6.9 1.9
. . . 6.9 2.3
. . . 6.9 2.7
. . . 6.9 3.1
. . . 6.9 3.6
. . . 7.0 4.0
. . . 7.0 4.5
. . . 7.1 4.9
. . . 7.2 5.4
. . . 7.3 6.0
. . . 7.4 6.5
. . . 7.5 7.0
. . . 7.5 7.5
. . . 7.6 8.0
. . . 7.7 8.6
. . . 7.8 9.2
. . . 7.9 9.8
. . . 8.0 10.4
. . . 8.1 11.0
. . . 8.2 11.6
. . . 8.3 12.3
. . . 8.4 12.9
. . . 8.5 13.6
. . . 8.6 14.2
. . . 8.7 14.9
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN06030
A B C
. . . 6.7 0
. . . 6.8 0.2
. . . 7.0 0.7
. . . 7.1 1.1
. . . 7.3 1.6
. . . 7.4 2.0
. . . 7.6 2.6
. . . 7.7 3.0
. . . 7.8 3.6
. . . 7.9 4.1
. . . 7.9 4.6
. . . 8.0 5.1
. . . 8.1 5.6
. . . 8.1 6.1
. . . 8.2 6.7
. . . 8.3 7.3
. . . 8.4 7.9
. . . 8.4 8.4
. . . 8.5 9.0
. . . 8.6 9.6
. . . 8.7 10.2
. . . 8.8 10.9
. . . 8.8 11.4
. . . 8.9 12.1
. . . 8.9 12.6
. . . 8.9 13.1
. . . 8.9 13.7
. . . 8.9 14.2
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TE-4
TABLE TE-4 (CONTD)A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
658
Coefficients forN06045
A B C
. . . 6.1 0
. . . 6.4 0.2
. . . 6.7 0.6
. . . 7.1 1.1
. . . 7.4 1.6
. . . 7.7 2.1
. . . 7.9 2.7
. . . 8.1 3.2
. . . 8.1 3.7
. . . 8.2 4.2
. . . 8.2 4.7
. . . 8.3 5.3
. . . 8.4 5.8
. . . 8.4 6.4
. . . 8.5 6.9
. . . 8.6 7.5
. . . 8.6 8.0
. . . 8.7 8.7
. . . 8.7 9.2
. . . 8.8 9.8
. . . 8.9 10.5
. . . 8.9 11.0
. . . 9.0 11.7
. . . 9.1 12.3
. . . 9.2 13.0
. . . 9.2 13.6
. . . 9.3 14.3
. . . 9.4 15.0
. . . 9.4 15.6
. . . 9.5 16.3
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN06059
A B C
. . . 6.5 0
. . . 6.5 0.2
. . . 6.5 0.6
. . . 6.6 1.0
. . . 6.6 1.4
. . . 6.7 1.8
. . . 6.7 2.3
. . . 6.8 2.7
. . . 6.8 3.1
. . . 6.9 3.6
. . . 6.9 4.0
. . . 7.0 4.5
. . . 7.0 4.9
. . . 7.0 5.3
. . . 7.0 5.7
. . . 7.1 6.2
. . . 7.1 6.6
. . . 7.1 7.1
. . . 7.2 7.6
. . . 7.2 8.0
. . . 7.2 8.5
. . . 7.2 9.0
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN06230
A B C
. . . 6.9 0
. . . 6.9 0.2
. . . 6.9 0.7
. . . 7.0 1.1
. . . 7.0 1.5
. . . 7.1 2.0
. . . 7.1 2.4
. . . 7.2 2.9
. . . 7.2 3.3
. . . 7.3 3.8
. . . 7.3 4.2
. . . 7.4 4.7
. . . 7.4 5.2
. . . 7.5 5.7
. . . 7.5 6.1
. . . 7.6 6.7
. . . 7.7 7.2
. . . 7.8 7.8
. . . 7.8 8.2
. . . 7.9 8.8
. . . 7.9 9.3
. . . 8.0 9.9
. . . 8.0 10.4
. . . 8.1 11.0
. . . 8.1 11.5
. . . 8.2 12.1
. . . 8.2 12.6
. . . 8.3 13.2
. . . 8.3 13.7
. . . 8.4 14.4
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-4
TABLE TE-4 (CONTD) A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
659
Coefficients forN06455
A B C
5.8 5.8 06.0 5.9 0.26.3 6.0 0.66.5 6.2 1.06.8 6.3 1.4
7.0 6.4 1.87.1 6.5 2.27.3 6.7 2.67.4 6.8 3.17.5 6.9 3.5
7.6 6.9 4.07.7 7.0 4.57.7 7.1 4.97.8 7.1 5.47.8 7.2 5.9
7.8 7.2 6.3. . . 7.3 6.8. . . 7.3 7.3. . . 7.4 7.8. . . 7.4 8.3
. . . 7.4 8.7
. . . 7.5 9.2
. . . 7.5 9.7
. . . 7.5 10.2
. . . 7.5 10.7
. . . 7.6 11.1
. . . 7.6 11.6
. . . 7.6 12.1
. . . 7.6 12.6
. . . 7.6 13.1
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN06600
A B C
6.8 6.8 06.9 6.9 0.37.2 7.0 0.77.5 7.1 1.17.7 7.2 1.6
7.9 7.3 2.08.1 7.4 2.58.2 7.5 3.08.3 7.6 3.48.4 7.6 3.9
8.5 7.7 4.48.5 7.8 5.08.6 7.8 5.58.7 7.9 6.08.7 8.0 6.5
8.8 8.1 7.1. . . 8.1 7.6. . . 8.2 8.1. . . 8.2 8.7. . . 8.3 9.3
. . . 8.4 9.8
. . . 8.4 10.4
. . . 8.5 11.0
. . . 8.6 11.6
. . . 8.6 12.2
. . . 8.7 12.9
. . . 8.8 13.5
. . . 8.9 14.2
. . . 9.0 14.8
. . . 9.0 15.5
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN06625
A B C
6.7 6.7 06.8 6.8 0.37.0 7.0 0.77.2 7.1 1.17.2 7.2 1.6
7.3 7.2 2.07.3 7.3 2.47.3 7.3 2.97.4 7.3 3.37.4 7.4 3.8
7.5 7.4 4.37.5 7.4 4.77.6 7.4 5.27.7 7.5 5.77.9 7.5 6.1
8.0 7.6 6.7. . . 7.7 7.2. . . 7.7 7.7. . . 7.8 8.2. . . 7.8 8.7
. . . 7.9 9.3
. . . 8.0 9.9
. . . 8.1 10.5
. . . 8.2 11.1
. . . 8.3 11.7
. . . 8.4 12.3
. . . 8.4 13.0
. . . 8.5 13.6
. . . 8.6 14.2
. . . 8.7 14.9
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TE-4
TABLE TE-4 (CONTD)A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
660
Coefficients forN06690
A B C
7.7 7.7 07.8 7.8 0.37.9 7.8 0.88.0 7.9 1.28.0 7.9 1.7
8.1 7.9 2.28.2 8.0 2.78.3 8.0 3.28.3 8.1 3.78.4 8.1 4.2
8.5 8.1 4.78.5 8.2 5.28.7 8.2 5.78.8 8.3 6.28.9 8.3 6.8
9.1 8.3 7.3. . . . . . . . .. . . . . . . . .. . . . . . . . .. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN07718
A B C
7.1 7.1 07.1 7.1 0.37.3 7.2 0.77.4 7.2 1.17.5 7.3 1.6
7.6 7.3 2.07.7 7.4 2.57.8 7.5 3.07.9 7.5 3.48.0 7.6 3.9
8.1 7.6 4.48.2 7.7 4.98.3 7.7 5.48.4 7.8 5.98.5 7.8 6.3
8.6 7.9 6.98.7 7.9 7.48.8 8.0 7.99.0 8.0 8.59.1 8.1 9.0
9.3 8.1 9.59.5 8.2 10.1. . . . . . . . .. . . . . . . . .. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN07750
A B C
6.7 6.7 06.9 6.8 0.27.1 6.9 0.77.2 7.0 1.17.3 7.1 1.5
7.4 7.2 2.07.5 7.3 2.57.6 7.4 2.97.7 7.5 3.47.7 7.5 3.9
7.7 7.5 4.37.7 7.5 4.87.8 7.5 5.37.8 7.6 5.78.0 7.7 6.3
8.1 7.7 6.8. . . . . . . . .. . . . . . . . .. . . . . . . . .. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-4
TABLE TE-4 (CONTD) A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
661
Coefficients forN08031
A B C
. . . 7.7 0
. . . 7.7 0.3
. . . 7.8 0.7
. . . 7.9 1.2
. . . 8.0 1.7
. . . 8.0 2.2
. . . 8.1 2.7
. . . 8.2 3.2
. . . 8.3 3.8
. . . 8.3 4.3
. . . 8.4 4.8
. . . 8.5 5.4
. . . 8.5 5.9
. . . 8.5 6.4
. . . 8.6 7.0
. . . 8.6 7.5
. . . 8.7 8.1
. . . 8.7 8.7
. . . 8.7 9.2
. . . 8.8 9.8
. . . 8.8 10.3
. . . 8.8 10.9
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN08330
A B C
8.1 8.1 08.2 8.1 0.38.3 8.2 0.88.6 8.3 1.38.7 8.4 1.8
8.8 8.5 2.39.0 8.5 2.99.1 8.6 3.49.3 8.7 4.09.4 8.8 4.5
9.5 8.8 5.19.6 8.9 5.79.7 9.0 6.29.8 9.0 6.89.8 9.1 7.4
9.9 9.1 8.0. . . . . . . . .. . . . . . . . .. . . . . . . . .. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN08800, N08810, and N08811
A B C
7.8 7.9 08.1 8.0 0.38.3 8.2 0.88.5 8.3 1.38.7 8.5 1.8
8.8 8.6 2.48.9 8.7 2.99.0 8.8 3.59.1 8.9 4.09.1 8.9 4.6
9.2 9.0 5.29.2 9.0 5.79.3 9.1 6.39.3 9.1 6.99.4 9.2 7.5
9.5 9.2 8.19.7 9.3 8.79.8 9.3 9.3
10.0 9.4 9.910.2 9.4 10.5
10.4 9.5 11.110.6 9.5 11.710.8 9.6 12.411.0 9.6 13.011.2 9.7 13.7
11.4 9.7 14.311.5 9.8 15.011.7 9.8 15.711.8 9.9 16.411.9 10.0 17.2
12.0 10.1 17.912.1 10.2 18.7
. . . 10.3 19.5
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TE-4
TABLE TE-4 (CONTD)A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
661.1
Coefficients forN08825
A B C
7.5 7.5 07.6 7.5 0.37.7 7.6 0.77.8 7.7 1.27.9 7.8 1.7
8.0 7.9 2.28.1 7.9 2.78.2 8.0 3.28.3 8.0 3.78.4 8.1 4.2
8.5 8.1 4.78.6 8.2 5.28.7 8.3 5.88.7 8.3 6.38.8 8.4 6.8
8.9 8.4 7.4. . . . . . . . .. . . . . . . . .. . . . . . . . .. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN10001
A B C
6.0 6.0 06.1 6.1 0.26.3 6.2 0.66.4 6.2 1.06.5 6.3 1.4
6.6 6.4 1.86.6 6.4 2.16.6 6.4 2.56.6 6.4 2.96.7 6.4 3.3
6.7 6.4 3.76.8 6.5 4.16.8 6.5 4.56.9 6.6 5.06.9 6.6 5.4
7.0 6.7 5.9. . . 6.8 6.3. . . 6.8 6.8. . . 6.9 7.2. . . 6.9 7.7
. . . 7.0 8.2
. . . 7.1 8.7
. . . 7.1 9.3
. . . 7.2 9.8
. . . 7.3 10.3
. . . 7.4 10.9
. . . 7.4 11.4
. . . 7.5 12.0
. . . 7.6 12.6
. . . 7.7 13.1
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN10003
A B C
6.2 6.2 06.3 6.2 0.26.5 6.3 0.66.6 6.4 1.06.7 6.5 1.4
6.9 6.6 1.87.0 6.6 2.27.1 6.7 2.77.2 6.7 3.17.3 6.8 3.5
7.4 6.8 3.97.5 6.9 4.47.6 6.9 4.87.7 7.0 5.37.8 7.0 5.7
7.9 7.1 6.2. . . . . . . . .. . . . . . . . .. . . . . . . . .. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TE-4
TABLE TE-4 (CONTD) A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
661.2
Coefficients forN10242
A B C
. . . 5.8 0
. . . 5.8 0.2
. . . 5.9 0.6
. . . 6.0 0.9
. . . 6.1 1.3
. . . 6.1 1.7
. . . 6.2 2.1
. . . 6.3 2.5
. . . 6.3 2.9
. . . 6.4 3.3
. . . 6.5 3.7
. . . 6.5 4.1
. . . 6.6 4.6
. . . 6.6 5.0
. . . 6.7 5.5
. . . 6.7 5.9
. . . 6.7 6.3
. . . 6.8 6.8
. . . 6.8 7.1
. . . 6.8 7.6
. . . 6.8 8.0
. . . 6.8 8.4
. . . 6.8 8.8
. . . 6.9 9.4
. . . 7.0 9.9
. . . 7.2 10.6
. . . 7.5 11.5
. . . 7.7 12.3
. . . 7.8 12.9
. . . 7.9 13.6
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN10276
A B C
6.0 6.0 06.1 6.1 0.26.3 6.2 0.66.5 6.3 1.06.7 6.4 1.4
6.9 6.5 1.87.1 6.6 2.27.3 6.7 2.77.5 6.8 3.17.6 6.9 3.6
7.7 7.0 4.07.8 7.1 4.57.9 7.2 5.08.0 7.2 5.58.0 7.3 5.9
8.1 7.3 6.4. . . 7.4 6.9. . . 7.5 7.4. . . 7.5 8.0. . . 7.6 8.5
. . . 7.7 9.0
. . . 7.7 9.5
. . . 7.8 10.1
. . . 7.8 10.6
. . . 7.9 11.2
. . . 7.9 11.7
. . . 8.0 12.3
. . . 8.0 12.8
. . . 8.1 13.4
. . . 8.1 13.9
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN10629
A B C
. . . 5.5 0
. . . 5.5 0.2
. . . 5.6 0.5
. . . 5.7 0.9
. . . 5.8 1.3
. . . 5.9 1.6
. . . 5.9 2.0
. . . 6.0 2.4
. . . 6.0 2.7
. . . 6.1 3.1
. . . 6.1 3.5
. . . 6.2 3.9
. . . 6.2 4.3
. . . 6.3 4.8
. . . 6.3 5.1
. . . 6.4 5.6
. . . 6.4 6.0
. . . 6.4 6.4
. . . 6.5 6.9
. . . 6.5 7.3
. . . 6.5 7.6
. . . 6.5 8.0
. . . 6.6 8.6
. . . 6.6 8.9
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TE-4
TABLE TE-4 (CONTD)A02THERMAL EXPANSION FOR NICKEL ALLOYS
Temperature,F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
155016001650
661.3
Coefficients forN10665
A B C
5.2 5.3 05.5 5.4 0.25.7 5.6 0.55.9 5.7 0.96.0 5.8 1.3
6.1 5.9 1.66.2 5.9 2.06.3 6.0 2.46.4 6.1 2.86.5 6.1 3.2
6.6 6.2 3.66.7 6.2 4.06.8 6.3 4.46.8 6.3 4.86.9 6.4 5.2
7.0 6.4 5.6. . . 6.5 6.0. . . 6.5 6.5. . . 6.6 6.9. . . 6.6 7.3
. . . 6.6 7.8
. . . 6.6 8.2
. . . 6.7 8.6
. . . 6.7 9.1
. . . 6.7 9.5
. . . 6.7 9.9
. . . 6.7 10.4
. . . 6.8 10.8
. . . 6.8 11.2
. . . 6.8 11.7
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN10675
A B C
. . . 5.7 0
. . . 5.7 0.2
. . . 5.8 0.6
. . . 5.8 0.9
. . . 5.9 1.3
. . . 6.0 1.7
. . . 6.0 2.0
. . . 6.1 2.4
. . . 6.1 2.8
. . . 6.2 3.2
. . . 6.2 3.6
. . . 6.3 4.0
. . . 6.4 4.5
. . . 6.4 4.8
. . . 6.5 5.3
. . . 6.5 5.7
. . . 6.5 6.1
. . . 6.6 6.6
. . . 6.6 7.0
. . . 6.6 7.4
. . . 6.5 7.6
. . . 6.5 8.0
. . . 6.5 8.4
. . . 6.5 8.8
. . . 6.6 9.3
. . . 6.8 10.0
. . . 6.9 10.6
. . . 7.1 11.3
. . . 7.2 11.9
. . . 7.3 12.5
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Coefficients forN12160
A B C
. . . 6.9 0
. . . 7.0 0.3
. . . 7.1 0.7
. . . 7.2 1.1
. . . 7.3 1.6
. . . 7.4 2.0
. . . 7.5 2.5
. . . 7.6 3.0
. . . 7.7 3.5
. . . 7.8 4.0
. . . 7.9 4.6
. . . 7.9 5.0
. . . 8.0 5.6
. . . 8.0 6.0
. . . 8.1 6.6
. . . 8.1 7.1
. . . 8.2 7.7
. . . 8.2 8.2
. . . 8.3 8.8
. . . 8.3 9.3
. . . 8.4 9.9
. . . 8.4 10.4
. . . 8.5 11.0
. . . 8.6 11.7
. . . 8.7 12.3
. . . 8.8 13.0
. . . 8.8 13.5
. . . 8.9 14.2
. . . 9.0 14.9
. . . 9.1 15.6
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
A02
Table TE-4 PART D PROPERTIES Table TE-5
TABLE TE-4 (CONTD)THERMAL EXPANSION FOR NICKEL ALLOYS
Coefficients forR20033
Temperature,F A B C
70 . . . 7.8 0100 . . . 7.9 0.3150 . . . 8.0 0.8200 . . . 8.1 1.3250 . . . 8.2 1.8
300 . . . 8.3 2.3350 . . . 8.4 2.8400 . . . 8.5 3.4450 . . . 8.5 3.9500 . . . 8.5 4.4
550 . . . 8.5 4.9600 . . . 8.5 5.4650 . . . 8.6 6.0700 . . . 8.6 6.5750 . . . 8.7 7.1
800 . . . 8.8 7.7850 . . . 8.8 8.2900 . . . 8.9 8.9950 . . . . . . . . .
1000 . . . . . . . . .
1050 . . . . . . . . .1100 . . . . . . . . .1150 . . . . . . . . .1200 . . . . . . . . .1250 . . . . . . . . .
1300 . . . . . . . . .1350 . . . . . . . . .1400 . . . . . . . . .1450 . . . . . . . . .1500 . . . . . . . . .
1550 . . . . . . . . .1600 . . . . . . . . .1650 . . . . . . . . .
GENERAL NOTES:(a) Coefficient A is the instantaneous coefficient of thermal expansion
106 (in./in./F). Coefficient B is the mean coefficient ofthermal expansion 106 (in./in./F) in going from 70F toindicated temperature. Coefficient C is the linear thermalexpansion (in./100 ft) in going from 70F to indicatedtemperature.
(b) For SI units, multiply coefficients A and B by 1.8 to convert tomm/mm/C and divide coefficient C by 2.16 to convert to mm/(mWC).
(c) See Table SI-1 for the conversion of temperatures to degreesCelsius.
661.4
TABLE TE-5THERMAL EXPANSION FOR TITANIUM ALLOYS
Coefficients forTitanium Alloy, Coefficients for
Grades 1, 2, 3, 7, Titanium Alloy,11, 12, 16, and 17 Grade 9
Temperature,F A B C A B C
70 4.6 4.6 0 4.8 4.7 0100 4.7 4.7 0.2 4.8 4.7 0.2150 4.7 4.7 0.5 4.9 4.8 0.5200 4.8 4.7 0.7 5.0 4.8 0.8250 4.8 4.7 1.0 5.0 4.9 1.1
300 4.8 4.8 1.3 5.1 4.9 1.4350 4.9 4.8 1.6 5.2 5.0 1.7400 4.9 4.8 1.9 5.3 5.0 2.0450 5.0 4.8 2.2 5.4 5.1 2.3500 5.0 4.9 2.5 5.4 5.1 2.6
550 5.0 4.9 2.8 5.5 5.1 3.0600 5.1 4.9 3.1 5.6 5.2 3.3650 5.1 4.9 3.4 . . . . . . . . .700 5.2 5.0 3.8 . . . . . . . . .750 5.2 5.0 4.1 . . . . . . . . .800 5.2 5.1 4.4 . . . . . . . . .
GENERAL NOTES:(a) Coefficient A is the instantaneous coefficient of thermal expansion
106 (in./in./F). Coefficient B is the mean coefficient ofthermal expansion 106 (in./in./F) in going from 70F toindicated temperature. Coefficient C is the linear thermalexpansion (in./100 ft) in going from 70F to indicatedtemperature.
(b) For SI units, multiply coefficients A and B by 1.8 to convertto mm/mm/C and divide coefficient C by 2.16 to convert tomm/(mWC).
(c) See Table SI-1 for the conversion of temperatures to degreesCelsius.
A03
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TCD 2001 SECTION II
TABLE TCDNOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
Carbon and Low Alloy Steels
Material GroupA [Note (1)] Material Group Material Group Material Group Material Group Material GroupPlain Carbon B [Note (2)] C [Note (3)] D [Note (4)] E [Note (5)] F [Note (6)]
Temp., F TC TD TC TD TC TD TC TD TC TD TC TD
70 35.1 0.695 27.5 0.529 23.5 0.458 20.9 0.408 15.9 0.308 12.8 0.256100 34.7 0.674 27.6 0.512 23.6 0.450 21.0 0.397 16.2 0.310 13.1 0.258150 34.1 0.645 27.6 0.496 23.6 0.438 21.2 0.391 16.7 0.313 13.6 0.260200 33.6 0.613 27.6 0.486 23.6 0.425 21.3 0.385 17.1 0.315 14.0 0.261250 32.9 0.585 27.4 0.467 23.5 0.413 21.4 0.378 17.5 0.314 14.4 0.263
300 32.3 0.561 27.2 0.453 23.4 0.401 21.5 0.371 17.8 0.313 14.7 0.262350 31.6 0.534 27.0 0.440 23.3 0.389 21.5 0.364 18.0 0.310 15.0 0.261400 30.9 0.512 26.7 0.428 23.1 0.378 21.5 0.357 18.2 0.305 15.2 0.259450 30.3 0.495 26.3 0.413 22.9 0.367 21.5 0.349 18.4 0.300 15.4 0.256500 29.5 0.472 25.9 0.398 22.7 0.356 21.4 0.341 18.5 0.295 15.6 0.253
550 28.8 0.453 25.5 0.387 22.5 0.346 21.3 0.332 18.5 0.289 15.8 0.249600 28.0 0.433 25.0 0.374 22.2 0.336 21.1 0.323 18.5 0.283 15.9 0.245650 27.3 0.414 24.5 0.360 21.9 0.326 20.9 0.314 18.5 0.274 16.0 0.240700 26.6 0.394 24.0 0.346 21.6 0.315 20.7 0.305 18.5 0.266 16.0 0.235750 25.9 0.374 23.5 0.332 21.3 0.303 20.5 0.295 18.4 0.258 16.1 0.229
800 25.2 0.355 23.0 0.318 21.0 0.292 20.2 0.285 18.3 0.250 16.1 0.222850 24.5 0.335 22.6 0.305 20.7 0.280 20.0 0.274 18.2 0.242 16.2 0.214900 23.8 0.317 22.1 0.291 20.3 0.269 19.7 0.264 18.1 0.233 16.1 0.207950 23.1 0.301 21.5 0.277 20.0 0.258 19.4 0.252 18.0 0.224 16.1 0.199
1000 22.4 0.282 21.0 0.263 19.7 0.247 19.1 0.241 17.8 0.216 16.1 0.192
1050 21.6 0.265 20.5 0.249 19.4 0.236 18.8 0.229 17.6 0.207 16.0 0.1821100 20.9 0.250 19.9 0.237 19.0 0.224 18.5 0.217 17.4 0.198 16.0 0.1741150 20.2 0.234 19.3 0.219 18.7 0.213 18.3 0.205 17.2 0.187 15.9 0.1651200 19.5 0.218 18.7 0.202 18.2 0.200 18.0 0.192 17.0 0.177 15.8 0.1551250 18.7 0.197 18.0 0.184 17.7 0.185 17.7 0.179 16.8 0.166 15.7 0.143
1300 18.0 0.180 17.1 0.159 16.9 0.167 17.2 0.163 16.5 0.153 15.6 0.1311350 17.2 0.134 16.2 0.122 15.6 0.139 16.4 0.136 16.2 0.138 15.5 0.1171400 16.4 0.082 15.6 0.078 15.3 0.077 15.6 0.075 15.8 0.117 15.2 0.1471450 15.9 0.147 15.2 0.155 15.2 0.129 15.4 0.127 15.6 0.144 15.0 0.1651500 15.7 0.162 15.1 0.169 15.1 0.200 15.3 0.197 15.7 0.162 15.0 0.177
662Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TCDTable TCD
TABLE TCD (CONTD)NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Chrome Steels High Alloy Steels
Material Group Material Group Material Group Material Group Material Group Material GroupG [Note (7)] H [Note (8)] I [Note (9)] J [Note (10)] K [Note (11)] L [Note (12)]
Temp., F TC TD TC TD TC TD TC TD TC TD TC TD
70 14.2 0.274 11.6 0.222 9.9 0.188 8.6 0.151 8.2 0.139 6.4 0.115100 14.2 0.271 11.6 0.220 10.1 0.189 8.7 0.152 8.3 0.140 6.6 0.116150 14.3 0.266 11.7 0.217 10.4 0.189 9.0 0.154 8.6 0.142 6.9 0.118200 14.3 0.261 11.7 0.214 10.6 0.189 9.3 0.156 8.8 0.145 7.1 0.121250 14.4 0.256 11.8 0.211 10.9 0.190 9.6 0.158 9.1 0.147 7.4 0.124
300 14.4 0.251 11.8 0.208 11.2 0.190 9.8 0.160 9.3 0.150 7.7 0.126350 14.4 0.246 11.9 0.206 11.4 0.191 10.1 0.162 9.5 0.152 8.0 0.129400 14.5 0.241 11.9 0.203 11.7 0.191 10.4 0.165 9.8 0.155 8.2 0.132450 14.5 0.236 12.0 0.201 12.0 0.191 10.6 0.167 10.0 0.157 8.5 0.135500 14.5 0.231 12.0 0.198 12.2 0.190 10.9 0.170 10.2 0.160 8.8 0.138
550 14.6 0.226 12.1 0.195 12.5 0.190 11.1 0.172 10.5 0.162 9.1 0.141600 14.6 0.221 12.2 0.192 12.7 0.190 11.3 0.174 10.7 0.165 9.3 0.143650 14.6 0.216 12.2 0.189 13.0 0.188 11.6 0.177 10.9 0.167 9.6 0.146700 14.6 0.211 12.3 0.186 13.2 0.186 11.8 0.179 11.2 0.170 9.9 0.149750 14.6 0.206 12.3 0.183 13.4 0.183 12.0 0.181 11.4 0.172 10.1 0.152
800 14.7 0.201 12.4 0.179 13.5 0.180 12.2 0.184 11.6 0.175 10.4 0.155850 14.7 0.196 12.5 0.174 13.6 0.176 12.5 0.186 11.9 0.177 10.6 0.158900 14.7 0.191 12.6 0.170 13.7 0.172 12.7 0.189 12.1 0.179 10.9 0.161950 14.7 0.185 12.6 0.165 13.8 0.167 12.9 0.191 12.3 0.182 11.2 0.164
1000 14.7 0.179 12.7 0.159 13.8 0.160 13.2 0.194 12.5 0.184 11.4 0.167
1050 14.7 0.173 12.8 0.152 13.9 0.153 13.4 0.196 12.8 0.187 11.7 0.1701100 14.7 0.167 12.9 0.145 14.0 0.146 13.6 0.198 13.0 0.189 12.0 0.1731150 14.8 0.159 13.0 0.150 14.1 0.134 13.8 0.201 13.2 0.191 12.2 0.1751200 14.8 0.150 13.1 0.160 14.2 0.129 14.0 0.203 13.4 0.194 12.5 0.1781250 14.8 0.138 13.2 0.169 14.4 0.140 14.3 0.205 13.6 0.196 12.7 0.181
1300 14.8 0.125 13.4 0.176 14.6 0.152 14.5 0.208 13.8 0.198 12.9 0.1841350 14.8 0.106 13.5 0.183 14.8 0.171 14.7 0.210 14.1 0.200 13.2 0.1861400 14.8 0.158 13.7 0.189 15.0 0.185 14.9 0.212 14.3 0.202 13.5 0.1881450 14.8 0.172 13.8 0.194 15.2 0.194 15.1 0.214 14.5 0.205 13.7 0.1901500 14.9 0.173 14.0 0.199 15.4 0.201 15.3 0.216 14.7 0.207 14.0 0.191
663
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TCD
TABLE TCD (CONTD)A02NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Nickel Alloys (Contd)
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
664
NickelN02200
TC TD
. . . . . .
. . . . . .
. . . . . .38.8 . . .38.0 . . .
37.2 . . .36.4 . . .35.4 . . .34.8 . . .34.1 . . .
33.3 . . .32.5 . . .31.7 . . .31.8 . . .32.2 . . .
32.5 . . .32.8 . . .33.1 . . .33.4 . . .33.8 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
Low CNickelN02201
TC TD
. . . . . .
. . . . . .
. . . . . .42.7 . . .41.6 . . .
40.5 . . .39.4 . . .38.3 . . .37.2 . . .36.2 . . .
35.1 . . .34.0 . . .33.7 . . .33.3 . . .33.0 . . .
32.7 . . .33.0 . . .33.4 . . .33.8 . . .34.2 . . .
34.5 . . .34.9 . . .35.2 . . .35.7 . . .36.0 . . .
36.4 . . .36.7 . . .37.1 . . .37.4 . . .37.8 . . .
NiCuN04400
TC TD
12.6 0.22412.9 0.22713.4 0.23413.9 0.24114.5 0.248
15.0 0.25415.6 0.26116.1 0.26716.6 0.27317.0 0.280
17.5 0.28517.9 0.28918.4 0.29118.9 0.29219.4 0.293
19.8 0.29320.4 . . .20.9 . . .21.5 . . .22.0 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
NiCuN04405
TC TD
12.6 . . .12.9 . . .13.4 . . .13.9 . . .14.5 . . .
15.0 . . .15.6 . . .16.1 . . .16.6 . . .17.0 . . .
17.5 . . .17.9 . . .18.4 . . .18.9 . . .19.4 . . .
19.8 . . .20.4 . . .20.9 . . .21.5 . . .22.0 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
NiCrMoFeN06002
TC TD
5.2 0.0875.5 0.0925.9 0.0996.3 0.1056.6 0.110
7.0 0.1177.3 0.1217.6 0.1267.9 0.1328.2 0.137
8.5 0.1418.8 0.1469.1 0.1499.4 0.1529.8 0.157
10.1 0.15910.4 0.16310.7 0.16511.0 0.16711.4 0.172
11.7 0.17412.0 0.17612.3 0.18012.6 0.18212.9 0.181
13.2 0.18213.6 0.18313.9 0.18314.2 0.18314.5 0.183
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TCD
TABLE TCD (CONTD) A02NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Nickel Alloys (Contd)
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
665
NiCrFeMoCuN06007
TC TD
5.8 0.1166.0 0.1176.2 0.1166.4 0.1156.7 0.117
7.0 0.1217.2 0.1237.4 0.1257.7 0.1287.9 0.130
8.2 0.1348.4 0.1368.6 0.1388.9 0.1429.2 0.146
9.4 0.1489.7 0.1519.9 0.154
10.2 0.15710.5 0.160
10.7 0.16211.0 0.16511.3 0.16911.5 0.171
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N06022
TC TD
5.6 . . .5.8 . . .6.1 . . .6.3 . . .6.7 . . .
7.0 . . .7.4 . . .7.8 . . .8.1 . . .8.5 . . .
8.8 . . .9.1 . . .9.4 . . .9.7 . . .
10.1 . . .
10.4 . . .10.7 . . .11.0 . . .11.4 . . .11.7 . . .
12.0 . . .12.3 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N06030
TC TD
5.9 . . .6.1 . . .6.5 . . .6.9 . . .7.3 . . .
7.6 . . .8.0 . . .8.4 . . .8.7 . . .9.1 . . .
9.5 . . .9.8 . . .
10.2 . . .10.5 . . .10.8 . . .
11.1 . . .11.4 . . .11.7 . . .11.9 . . .12.0 . . .
12.2 . . .12.4 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N06045
TC TD
7.5 0.125. . . . . .. . . . . .. . . . . .. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N06059
TC TD
6.0 0.1136.3 . . .6.6 . . .6.9 . . .7.2 . . .
7.4 . . .7.7 . . .7.9 . . .8.2 . . .8.5 . . .
8.7 . . .9.0 . . .9.3 . . .9.5 . . .9.8 . . .
10.0 . . .10.3 . . .10.6 . . .10.8 . . .11.1 . . .
11.4 . . .11.7 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TCD
TABLE TCD (CONTD)A02NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Nickel Alloys (Contd)
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
666
N06230
TC TD
5.2 0.0955.4 0.0975.6 0.1005.9 0.1036.3 0.107
6.6 0.1116.9 0.1147.2 0.1187.5 0.1217.9 0.124
8.2 0.1278.5 0.1308.9 0.1339.2 0.1359.5 0.138
9.8 0.14010.2 0.14410.5 0.14710.8 0.15011.1 0.153
11.4 0.15611.7 0.15812.0 0.16012.3 0.16312.7 0.165
13.0 0.16613.3 0.16713.6 0.16813.9 0.16814.2 0.168
NiMoCrLow CN06455
TC TD
5.8 0.1105.9 0.1126.2 0.1146.5 0.1186.8 0.121
7.1 0.1247.4 0.1277.7 0.1307.9 0.1338.2 0.137
8.5 0.1418.8 0.1459.1 0.1479.3 0.1509.6 0.154
9.9 0.15810.2 0.16210.5 0.16410.8 0.16911.1 0.172
11.5 0.17711.8 0.18112.1 0.18512.5 0.189
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
NiCrFeN06600
TC TD
8.6 0.1548.7 0.1548.9 0.1559.1 0.1569.3 0.158
9.6 0.1609.8 0.163
10.1 0.16510.3 0.16810.6 0.171
10.8 0.17211.1 0.17411.3 0.17711.6 0.17911.8 0.180
12.1 0.18212.3 0.18512.6 0.18612.9 0.18813.2 0.190
13.5 0.19113.8 0.19214.0 0.19414.3 0.19514.6 0.198
14.9 0.19915.2 0.20115.5 0.20415.8 0.20616.0 0.208
NiCrMoCbN06625
TC TD
5.7 0.1105.8 0.1126.0 0.1176.2 0.1216.5 0.121
6.8 0.1227.0 0.1257.2 0.1277.5 0.1307.7 0.132
7.9 0.1348.2 0.1368.4 0.1388.6 0.1408.9 0.142
9.1 0.1449.4 0.1469.6 0.1489.8 0.150
10.1 0.153
10.3 0.15410.6 0.15610.8 0.15711.0 0.15911.3 0.161
11.5 0.16311.8 0.16512.0 0.16712.3 0.16912.6 0.171
NiCrFeN06690
TC TD
6.8 0.1257.0 0.1287.3 0.1317.6 0.1347.9 0.137
8.2 0.1408.5 0.1448.8 0.1479.1 0.1519.4 0.153
9.7 0.15710.0 0.16110.3 0.16410.6 0.16710.9 0.170
11.2 0.17411.5 0.17811.8 0.18012.2 0.18412.5 0.187
12.8 0.19013.1 0.19213.4 0.19413.7 0.19714.0 0.199
14.3 0.20114.6 0.20214.9 0.20415.2 0.20715.5 0.208
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TCD
TABLE TCD (CONTD) A02NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Nickel Alloys (Contd)
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
667
NiCrFeMoCbN07718
TC TD
6.4 0.1206.6 0.1226.8 0.1257.1 0.1297.4 0.132
7.7 0.1357.9 0.1388.2 0.1428.5 0.1458.8 0.148
9.0 0.1529.3 0.1559.6 0.1599.8 0.163
10.1 0.167
10.4 0.17110.7 0.17611.0 0.18211.2 0.19011.5 0.184
11.8 0.18112.0 0.18012.3 0.18012.6 0.17912.8 0.172
13.1 0.16313.3 0.16113.6 0.16013.8 0.16114.1 0.162
70Ni16Cr7FeTiAl
N07750
TC TD
6.9 0.1327.0 0.1327.2 0.1337.4 0.1337.6 0.133
7.8 0.1348.0 0.1368.2 0.1408.4 0.1418.6 0.143
8.8 0.1459.1 0.1489.3 0.1519.5 0.1539.8 0.156
10.0 0.15810.2 0.16010.5 0.16210.7 0.16510.9 0.169
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
CrNiFeMoCuCb
N08020
TC TD
. . . . . .6.9 0.1987.2 0.2077.5 0.2147.8 0.223
8.0 0.2298.3 0.2388.6 0.2468.8 0.2549.1 0.265
9.4 0.2709.7 0.277
10.0 0.28610.2 0.29310.5 0.300
10.8 0.30911.0 . . .11.3 . . .11.6 . . .11.9 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N08031
TC TD
6.7 0.1226.9 . . .7.2 . . .7.5 . . .7.8 . . .
8.1 . . .8.4 . . .8.7 . . .9.0 . . .9.3 . . .
9.6 . . .9.8 . . .
10.1 . . .10.4 . . .10.6 . . .
10.9 . . .11.2 . . .11.5 . . .11.8 . . .12.0 . . .
12.3 . . .12.6 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
NiFeCrSiN08330
TC TD
7.2 0.1317.2 0.1317.4 0.1357.7 0.1418.0 TBD
8.2 TBD8.5 TBD8.8 TBD9.1 TBD9.4 TBD
9.7 TBD10.0 TBD10.3 TBD10.6 TBD10.9 TBD
11.2 TBD11.5 TBD11.8 TBD12.1 TBD12.4 TBD
12.7 TBD13.0 TBD13.2 TBD13.5 TBD13.8 TBD
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TCD
TABLE TCD (CONTD)A02NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Nickel Alloys (Contd)
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
667.1
NiFeCrN08800, N08810,
and N08811
TC TD
6.7 0.1226.8 0.1257.1 0.1297.4 0.1337.7 0.137
8.0 0.1408.3 0.1448.6 0.1478.8 0.1509.1 0.153
9.3 0.1569.6 0.1599.8 0.161
10.1 0.16410.3 0.167
10.6 0.16910.8 0.17111.1 0.17411.3 0.17611.6 0.178
11.9 0.18112.1 0.18312.4 0.18512.7 0.18713.0 0.189
13.2 0.19113.6 0.19213.8 0.19414.2 0.19614.5 0.198
NiFeCrMoCuN08825
TC TD
. . . . . .
. . . . . .
. . . . . .7.1 0.1277.3 0.126
7.6 0.1257.9 0.1298.1 0.1348.4 0.1338.6 0.132
8.9 0.1319.1 0.1309.3 0.1339.6 0.1369.8 0.135
10.0 0.13310.2 0.13210.4 0.13110.7 0.13010.9 0.129
11.1 . . .11.4 . . .11.6 . . .11.8 . . .12.1 . . .
12.4 . . .12.7 . . .12.9 . . .13.3 . . .13.6 . . .
NiMoN10001
TC TD
. . . . . .6.1 0.1156.2 0.1146.4 0.1166.5 0.116
6.7 0.1186.8 0.1177.0 0.1197.2 0.1217.4 0.122
7.5 0.1217.7 0.1248.0 0.1268.2 0.1278.4 0.129
8.7 0.1329.0 0.1359.3 0.1389.7 0.143
10.0 0.145
10.4 0.14910.7 0.15311.1 0.156
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
NiMoCrFeN10003
TC TD
. . . . . .
. . . . . .6.1 0.1146.6 0.1216.8 0.123
7.0 0.1257.2 0.1277.4 0.1307.6 0.1317.8 0.133
8.1 0.1378.3 0.1398.5 0.1438.8 0.1479.0 0.149
9.3 0.1539.5 0.1559.8 0.160
10.1 0.16310.4 0.167
10.7 0.16111.1 0.15411.4 0.15211.7 0.15812.1 0.164
12.5 0.17012.9 . . .13.3 . . .13.7 . . .14.2 . . .
65Ni25Mo8Cr2FeN10242
TC TD
6.3 0.1186.4 0.1196.7 0.1237.0 0.1287.2 0.131
7.5 0.1347.7 0.1378.0 0.1408.2 0.1438.5 0.146
8.8 0.1499.0 0.1539.3 0.1569.5 0.1599.8 0.162
10.1 0.16510.3 0.16910.6 0.17310.8 0.17711.1 0.180
11.3 0.18511.6 0.18911.9 0.19412.1 0.19812.4 0.193
12.7 0.18812.9 0.18313.2 0.17813.4 0.17713.7 0.176
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TCD
TABLE TCD (CONTD) A02NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
High Nickel Alloys (Contd)
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
667.2
NiMoCrN10276
TC TD
. . . TBD5.9 TBD6.2 TBD6.4 TBD6.7 TBD
7.0 TBD7.2 TBD7.5 TBD7.8 TBD8.1 TBD
8.4 TBD8.7 TBD8.9 TBD9.2 TBD9.5 TBD
9.8 TBD10.1 TBD10.4 TBD10.7 TBD11.0 TBD
11.3 TBD11.5 TBD11.8 TBD12.1 TBD
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N10629
TC TD
6.4 0.1246.5 . . .6.8 . . .7.0 . . .7.2 . . .
7.4 . . .7.6 . . .7.8 . . .8.0 . . .8.2 . . .
8.4 . . .8.6 . . .8.9 . . .9.1 . . .9.3 . . .
9.5 . . .9.7 . . .9.9 . . .
10.1 . . .10.3 . . .
10.6 . . .10.8 . . .11.0 . . .12.2 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
NiMoN10665
TC TD
. . . . . .6.8 0.1286.9 0.1297.0 0.1307.2 0.132
7.3 0.1347.5 0.1357.6 0.1377.8 0.1398.0 0.141
8.2 0.1448.4 0.1468.7 0.1498.8 0.1529.1 0.154
9.4 0.1579.6 0.160
10.0 0.16410.3 0.16710.7 0.171
11.0 0.17511.4 0.17911.8 0.18412.2 0.188
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
N10675
TC TD
6.5 0.1156.6 0.1176.8 0.1206.9 0.1237.1 0.126
7.3 0.1297.5 0.1327.8 0.1358.0 0.1378.2 0.140
8.4 0.1438.7 0.1458.9 0.1489.1 0.1529.4 0.155
9.7 0.1589.9 0.161
10.2 0.16410.5 0.16710.8 0.170
11.0 0.17411.3 0.17711.6 0.18011.8 0.18312.1 0.185
12.4 0.18712.7 0.18813.0 0.18813.3 0.18813.7 0.182
N12160
TC TD
6.3 0.1156.4 0.1166.6 0.1176.8 0.1197.1 0.122
7.3 0.1257.6 0.1277.9 0.1308.2 0.1348.5 0.138
8.8 0.1419.0 0.1459.4 0.1499.8 0.153
10.1 0.158
10.5 0.16210.9 0.16611.3 0.17011.6 0.17312.0 0.174
12.4 0.17612.7 0.17713.1 0.17813.5 0.18013.8 0.181
14.2 0.18314.5 0.18414.8 0.18615.0 0.18715.1 0.187
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
2001 SECTION IITable TCD
667.3
TABLE TCD (CONTD)A02A03 NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND
THERMAL DIFFUSIVITY (TD)
High Nickel Alloys(Contd)
Titanium Alloys
Temp., F
70100150200250
300350400450500
550600650700750
800850900950
1000
10501100115012001250
13001350140014501500
R20033
TC TD
7.7 0.1307.9 . . .8.1 . . .8.4 . . .8.6 . . .
8.8 . . .9.1 . . .9.3 . . .9.5 . . .9.8 . . .
10.0 . . .10.3 . . .10.5 . . .10.7 . . .11.0 . . .
11.2 . . .11.4 . . .11.6 . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
Titanium (Gr. 1, 2,3, 7, 11, 12, 16,17, 26, and 27)
TC TD
12.68 0.35912.52 0.35212.25 0.34012.00 0.33111.85 0.322
11.72 0.31411.60 0.30611.45 0.30011.35 0.29411.29 0.290
11.23 0.28611.20 0.28311.17 0.28011.15 0.27811.18 0.276
11.20 0.27511.23 0.27411.30 0.27311.36 0.27211.43 0.271
11.51 0.27011.58 0.270
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
Titanium Grade 9
TC TD
5.12 0.1455.25 0.1475.46 0.1505.67 0.1525.87 0.155
6.06 0.1586.24 0.1606.40 0.1636.55 0.1666.69 0.168
6.81 0.1706.91 0.172. . . . . .. . . . . .. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TCD 2001 SECTION II
TABLE TCD (CONTD)NOMINAL COEFFICIENTS OF THERMAL CONDUCTIVITY (TC) AND THERMAL DIFFUSIVITY (TD)
Aluminum Alloys
A24430 A03560 A91060 A91100 A92014 A92024
Temp., F TC TD TC TD TC TD TC TD TC TD TC TD
70 94.0 2.64 92.0 2.61 135.2 3.72 133.1 3.67 89.9 2.47 85.8 2.36100 94.9 2.64 92.9 2.61 133.7 3.65 131.8 3.61 90.9 2.48 86.9 2.37150 96.1 2.63 94.2 2.60 131.7 3.54 130.0 3.50 92.3 2.48 88.5 2.38200 97.2 2.63 95.4 2.60 130.1 3.46 128.5 3.42 93.6 2.48 90.0 2.39
250 98.1 2.63 96.4 2.59 128.7 3.38 127.3 3.35 94.7 2.48 91.3 2.39300 99.0 2.62 97.4 2.59 127.5 3.31 126.2 3.28 95.7 2.48 92.4 2.40350 99.7 2.61 98.2 2.59 126.5 3.25 125.3 3.23 96.6 2.47 93.4 2.40400 100.4 2.60 98.9 2.58 125.6 3.19 124.5 3.17 97.4 2.47 94.4 2.39
Aluminum Alloys (Contd)
A95052A93003 A93004 & A95652 A95083 A95086
Temp., F TC TD TC TD TC TD TC TD TC TD
70 102.3 2.81 94.0 2.60 79.6 2.22 67.2 1.88 73.4 2.05100 102.8 2.80 94.9 2.60 80.8 2.23 68.7 1.91 74.8 2.08150 103.5 2.78 96.1 2.59 82.7 2.25 70.8 1.94 76.8 2.10200 104.2 2.76 97.2 2.59 84.4 2.27 72.8 1.97 78.7 2.12
250 104.7 2.75 98.1 2.59 85.9 2.28 74.6 1.99 80.3 2.14300 105.2 2.73 99.0 2.58 87.2 2.29 76.2 2.01 81.9 2.16350 105.7 2.71 99.7 2.57 88.4 2.30 77.8 2.03 83.2 2.17400 106.1 2.69 100.4 2.56 89.6 2.30 79.2 2.05 84.5 2.18
Aluminum Alloys (Contd)
A95154& A95254 A95454 A95456 A96061 A96063
Temp., F TC TD TC TD TC TD TC TD TC TD
70 73.4 2.05 77.5 2.15 67.2 1.89 96.1 2.66 120.8 3.34100 74.8 2.08 78.8 2.17 68.7 1.91 96.9 2.66 120.3 3.30150 76.8 2.10 80.8 2.19 70.8 1.94 98.0 2.65 119.7 3.23200 78.7 2.12 82.5 2.21 72.8 1.97 99.0 2.65 119.1 3.18
250 80.3 2.14 84.1 2.23 74.6 2.00 99.8 2.64 118.3 3.13300 81.9 2.16 85.5 2.24 76.3 2.02 100.6 2.63 118.3 3.09350 83.2 2.17 86.7 2.25 77.8 2.04 101.3 2.62 117.9 3.04400 84.5 2.18 87.9 2.25 79.2 2.05 101.9 2.62 117.6 3.00
668
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TCDTable TCD
TABLE TCD (CONTD)
GENERAL NOTES:(a) TC is the thermal conductivity, Btu/hr-ft-F, and TD is the thermal diffusivity, ft2/hr:
TD pTC (Btu/hr-ft-F)
density (lb/ft3) specific heat (Btu/lb-F)
(b) Values of thermal expansion and thermal diffusivity should be used with the understanding that there is an associated 10% uncertainty.This uncertainty results from compositional variations and variables associated with original data acquisition and analysis.
(c) For SI units, multiply TC by 1.7295 to convert to W/(mWK) and TD by 2.5806410-5 to convert to m2/s.(d) See Table SI-1 for the conversion of temperatures to degrees Celsius.
NOTES:(1) Material Group A includes plain carbon steels in which there are no specified amounts of manganese or silicon.(2) Material Group B includes carbon steels in which there are specified amounts of manganese and/or silicon, with or without additional small
amounts of columbium, titanium, or vanadium (microalloyed steels). Also includes:34Cr
12NiCu34Ni
12CuMo1Cr12MoSi 2
12Ni(3) Material Group C includes the following carbonmoly steels:
C14Mo C12Mo
The following low chrome steels:12Cr
15MoV 1Cr12Mo
12Cr14MoSi 1
14Cr12Mo
12Cr12Mo 1
14Cr12MoSi
12Cr12Ni
15Mo 134Cr
12MoCu34Cr
34NiCuAl 134Cr
12MoTi1Cr1Mn14Mo 2Cr
12Mo1Cr15Mo
The following manganese steels:Mn12Mo Mn
12Mo34Ni
Mn12Mo14Ni Mn
12NiVMn12Mo
12Ni MnVThe following nickel steels:
12Ni12Cr
14MoV34Ni1Mo
34Cr12Ni
12MoV 1Ni12Cr
12Mo34Ni
12Cr12MoV 1
14Ni1Cr12Mo
34Ni12Mo
13CrV 312Ni1
34Cr12MoV
34Ni12MoCrV 4Ni1
12Cr12Mo-V
(4) Material Group D includes the following low chrome steels:214Cr1Mo 3Cr1Mo
The following manganese steel:Mn14Mo
The following nickel steels:134Ni
34Cr14Mo 2
34Ni112Cr
12MoV2Ni34Cr
14Mo 5Ni14Mo
2Ni34Cr13Mo 8Ni
2Ni112Cr14MoV 9Ni
2Ni1Cu(5) Material Group E includes:
5Cr12Mo 5Cr12MoTi
5Cr12MoSiTD at 1420F p 0.105 and at 1425F p 0.122 ft2/hr.
(6) Material Group F includes:9Cr1Mo
TD at 1375F p 0.109 ft2/hr.(7) Material Group G includes:
12Cr 13Cr4Ni12Cr1Al 15Cr13Cr 17Cr
(8) Material Group H includes:27Cr
(9) Material Group I includes:17Cr4Ni4Cu 15Cr5Ni3Mo (only to 800F)
669
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TCD 2001 SECTION II
TABLE TCD (CONTD)
NOTES (CONTD):(10) Material Group J includes:
15Cr6NiCuMo (only to 800F) 18Cr8NiS (or Se)17Cr7Ni1Al (only to 800F) 18Cr11Ni18Cr8Ni 23Cr4NiMoCu
These thermal conductivity and diffusivity values are also appropriate for H, L, N, and LN grades of austenitic stainless steels.(11) Material Group K includes:
13Cr8Ni2Mo (only to 800F) 19Cr9NiMoW29Cr7Ni2MoN 21Cr11NiN25Ni15Cr2Ti 22Cr5Ni3MoN29Ni20Cr3Cu2Mo 23Cr12Ni16Cr12Ni2Mo 25Cr7Ni4MoN18Cr5Ni3Mo 25Cr20Ni18Cr10NiCb 25Cr20Ni2Mo18Cr10NiTi 44Fe25Ni21CrMo18Cr13Ni3Mo
These thermal conductivity and diffusivity values are also appropriate for H, L, N, and LN grades of austenitic stainless steels.(12) Material Group L includes:
18Cr18Ni2Si 25Cr12Ni22Cr13Ni5Mn 25Cr35NiNCe24Cr22Ni7.5Mo 31Ni31Fe29CrMo
These thermal conductivity and diffusivity values are also appropriate for H, L, N, and LN grades of austenitic stainless steels.
670
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TM-1Table TM-1
TA
BL
ET
M-1
MO
DU
LI
OF
EL
AS
TIC
ITY
EO
FF
ER
RO
US
MA
TE
RIA
LS
FO
RG
IVE
NT
EM
PE
RA
TU
RE
S
Mod
ulus
ofE
last
icit
yE
pV
alue
Giv
en
106
psi,
for
Tem
pera
ture
,F
,of
Mat
eria
ls
325
20
0
100
7020
030
040
050
060
070
080
090
010
0011
0012
0013
0014
0015
00
Car
bon
stee
lsw
ith
C
0.30
%31
.430
.830
.229
.528
.828
.327
.727
.326
.725
.524
.222
.420
.418
.0..
...
...
...
.C
arbo
nst
eels
wit
hC
>0.
30%
31.2
30.6
30.0
29.3
28.6
28.1
27.5
27.1
26.5
25.3
24.0
22.3
20.2
17.9
15.4
...
...
...
Mat
eria
lG
roup
A[N
ote
(1)]
31.1
30.5
29.9
29.2
28.5
28.0
27.4
27.0
26.4
25.3
23.9
22.2
20.1
17.8
15.3
...
...
...
Mat
eria
lG
roup
B[N
ote
(2)]
29.6
29.1
28.5
27.8
27.1
26.7
26.1
25.7
25.2
24.6
23.9
23.2
22.4
21.5
20.4
19.2
17.7
...
Mat
eria
lG
roup
C[N
ote
(3)]
31.6
31.0
30.4
29.7
29.0
28.5
27.9
27.5
26.9
26.3
25.5
24.8
23.9
23.0
21.8
20.5
18.9
...
Mat
eria
lG
roup
D[N
ote
(4)]
32.6
32.0
31.4
30.6
29.8
29.4
28.8
28.3
27.7
27.1
26.3
25.6
24.6
23.7
22.5
21.1
19.4
...
Mat
eria
lG
roup
E[N
ote
(5)]
33.0
32.4
31.8
31.0
30.2
29.8
29.1
28.7
28.1
27.4
26.8
26.2
25.4
24.5
23.3
22.0
20.5
...
Mat
eria
lG
roup
F[N
ote
(6)]
31.2
30.7
30.1
29.2
28.5
27.9
27.3
26.7
26.1
25.6
24.7
23.2
21.5
19.1
16.6
...
...
...
Mat
eria
lG
roup
G[N
ote
(7)]
30.3
29.7
29.1
28.3
27.6
27.0
26.5
25.8
25.3
24.8
24.1
23.5
22.8
22.1
21.2
20.2
19.2
18.1
S13
800
[Not
e(8
)]31
.530
.930
.329
.428
.728
.127
.526
.926
.325
.725
.024
.4..
...
...
...
...
...
.S
1550
0[N
ote
(9)]
30.5
29.9
29.4
28.5
27.8
27.2
26.6
26.1
25.5
24.9
24.2
23.7
...
...
...
...
...
...
S45
000
[Not
e(1
0)]
31.6
31.0
30.4
29.5
28.8
28.2
27.6
27.0
26.4
25.8
25.1
24.5
...
...
...
...
...
...
S17
400
[Not
e(1
1)]
30.5
29.9
29.4
28.5
27.8
27.2
26.6
26.1
25.5
24.9
24.2
23.7
...
...
...
...
...
...
S17
700
[Not
e(1
2)]
31.6
31.0
30.4
29.5
28.8
28.2
27.6
27.0
26.4
25.8
25.1
24.5
...
...
...
...
...
...
S66
286
[Not
e(1
3)]
31.2
30.7
30.1
29.2
28.5
27.9
27.3
26.7
26.1
25.6
24.8
24.2
...
...
...
...
...
...
Not
esap
pear
onfo
llow
ing
page
.
671
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TM-1 2001 SECTION II
TABLE TM-1 (CONTD)
GENERAL NOTES:(a) For the SI unit, multiply the modulus of elasticity E by 6.895106 kPa.(b) See Table SI-1 for the conversion of temperatures to degrees Celsius.
NOTES:(1) Material Group A consists of the following carbonmolybdenum and manganese steels:
C14Mo Mn12Mo
14NiC12Mo Mn
12Mo12Ni
Mn14Mo Mn12NiV
Mn12Mo MnV(2) Material Group B consists of the following Ni steels:
34Cr12NiCu 1
14Ni1Cr12Mo
34Cr34NiCuAl 1
34Ni34Cr
14Mo12Ni
12Cr14MoV 2Ni1
12Cr14MoV
12Ni12MoV 2Ni1Cu
34Ni12Cr
12MoV 212Ni
34Ni12CuMo 2
34Ni112Cr
12MoV34Ni
12Mo13CrV 3
12Ni34Ni
12MoCrV 312Ni1
34Cr12MoV
34Ni1Mo34Cr 4Ni1
12Cr12MoV
1Ni12Cr12Mo
(3) Material Group C consists of the following 122Cr steels:12Cr
15MoV 1Cr12MoV
12Cr14MoSi 1
14Cr12Mo
12Cr12Mo 1
14Cr12MoSi
1Cr15Mo 134Cr
12MoTi1Cr12Mo 2Cr
12Mo(4) Material Group D consists of the following 2143Cr steels:
214Cr1Mo 3Cr1Mo(5) Material Group E consists of the following 59Cr steels:
5Cr12Mo 7Cr12Mo
5Cr12MoSi 9CrMo, including variations thereof5Cr12MoTi
(6) Material Group F consists of the following chromium steels:12CrAl 15Cr13Cr 17Cr
(7) Material Group G consists of the following austenitic steels:16Cr12Ni 18Cr10NiTi16Cr12Ni2MoN 18Cr13Ni3Mo18Cr3Ni13Mn 18Cr18Ni2Si18Cr8Ni 20Cr6Ni9Mn18Cr8NiN 22Cr13Ni5Mn18Cr8NiS 23Cr12Ni18Cr8NiSe 25Cr20Ni18Cr10NiCb
(8) Also known as 13Cr8Ni2Mo, XM-13, or PH13-8Mo.(9) Also known as 15Cr5Ni3Mo, XM-12, or 15-5PH.
(10) Also known as 15Cr6NiCuMo, Custom 450, or XM-25. Modulus values are for material aged at 900F.(11) Also known as 17Cr4Ni4Cu, Grade 630, or 17-4PH.(12) Also known as 17Cr7Ni1Al, Grade 631, or 17-7PH.(13) Also known as 25Ni15Cr2Ti, Grade 660, or A-286 stainless steel.
672
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TM-2Table TM-2
TABLE TM-2MODULI OF ELASTICITY E OF ALUMINUM AND ALUMINUM ALLOYS
FOR GIVEN TEMPERATURES
Modulus of Elasticity E p Value Given 106 psi, for Temperature, F, of
Material 325 200 100 70 200 300 400 500
A03560 11.4 11.1 10.8 10.3 9.8 9.5 9.0 8.1A95083 11.4 11.1 10.8 10.3 9.8 9.5 9.0 8.1A95086 11.4 11.1 10.8 10.3 9.8 9.5 9.0 8.1A95456 11.4 11.1 10.8 10.3 9.8 9.5 9.0 8.1
A24430 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1A91060 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1A91100 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1A93003 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1A93004 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1A96061 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1A96063 11.1 10.8 10.5 10.0 9.6 9.2 8.7 8.1
A92014 11.7 11.4 11.1 10.6 10.1 9.8 9.2 8.6A92024 11.7 11.4 11.1 10.6 10.1 9.8 9.2 8.6
A95052 11.3 11.0 10.7 10.2 9.7 9.4 8.9 8.3A95154 11.3 11.0 10.7 10.2 9.7 9.4 8.9 8.3A95254 11.3 11.0 10.7 10.2 9.7 9.4 8.9 8.3A95454 11.3 11.0 10.7 10.2 9.7 9.4 8.9 8.3A95652 11.3 11.0 10.7 10.2 9.7 9.4 8.9 8.3
GENERAL NOTES:(a) For the SI unit, multiply the modulus of elasticity E by 6.895106 kPa.(b) See Table SI-1 for the conversion of temperatures to degrees Celsius.
673
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
Table TM-3 2001 SECTION II
TABLE TM-3MODULI OF ELASTICITY E OF COPPER AND COPPER ALLOYS FOR GIVEN
TEMPERATURES
Modulus of Elasticity E p Value Given 106 psi, for Temperature, F, of
Material 325 200 100 70 200 300 400 500 600 700
C93700 11.6 11.4 11.3 11.0 10.7 10.6 10.3 10.1 9.8 9.4
C83600 14.8 14.6 14.4 14.0 13.7 13.4 13.2 12.9 12.5 12.0C92200 14.8 14.6 14.4 14.0 13.7 13.4 13.2 12.9 12.5 12.0
C28000 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8C36500 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8C46400 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8C65500 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8C66100 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8C95200 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8C95400 15.9 15.6 15.4 15.0 14.6 14.4 14.1 13.8 13.4 12.8
C44300 16.9 16.6 16.5 16.0 15.6 15.4 15.0 14.7 14.2 13.7C44400 16.9 16.6 16.5 16.0 15.6 15.4 15.0 14.7 14.2 13.7C44500 16.9 16.6 16.5 16.0 15.6 15.4 15.0 14.7 14.2 13.7C64200 16.9 16.6 16.5 16.0 15.6 15.4 15.0 14.7 14.2 13.7C68700 16.9 16.6 16.5 16.0 15.6 15.4 15.0 14.7 14.2 13.7
C10200 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C10400 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C10500 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C10700 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C11000 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C12000 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C12200 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C12300 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C12500 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C14200 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C23000 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C61000 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C61400 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C65100 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5C70400 18.0 17.7 17.5 17.0 16.6 16.3 16.0 15.6 15.1 14.5
C19400 18.5 18.2 18.0 17.5 17.1 16.8 16.5 16.1 15.6 15.0C60800 18.5 18.2 18.0 17.5 17.1 16.8 16.5 16.1 15.6 15.0C63000 18.5 18.2 18.0 17.5 17.1 16.8 16.5 16.1 15.6 15.0
C70600 19.0 18.7 18.5 18.0 17.6 17.3 16.9 16.6 16.0 15.4C97600 20.1 19.8 19.6 19.0 18.5 18.2 17.9 17.5 16.9 16.2C71000 21.2 20.8 20.6 20.0 19.5 19.2 18.8 18.4 17.8 17.1C71500 23.3 22.9 22.7 22.0 21.5 21.1 20.7 20.2 19.6 18.8
GENERAL NOTES:(a) For the SI unit, multiply the modulus of elasticity E by 6.895106 kPa.(b) See Table SI-1 for the conversion of temperatures to degrees Celsius.
674
Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
PART D PROPERTIES Table TM-4Table TM-4A
02A
03T
AB
LE
TM
-4M
OD
UL
IO
FE
LA
ST
ICIT
YE
OF
HIG
HN
ICK
EL
AL
LO
YS
FO
RG
IVE
NT
EM
PE
RA
TU
RE
S
Mod
ulus
ofE
last
icit
yE
pV
alue
Giv
en
106
psi,
for
Tem
pera
ture
,F
,of
Mat
eria
l
325
20
0
100
7020
030
040
050
060
070
080
090
010
0011
0012
0013
0014
0015
00
N02
200
32.1
31.5
30.9
30.0
29.3
28.8
28.5
28.1
27.8
27.3
26.7
26.1
25.5
25.1
24.5
23.9
23.1
22.4
N02
201
32.1
31.5
30.9
30.0
29.3
28.8
28.5
28.1
27.8
27.3
26.7
26.1
25.5
25.1
24.5
23.9
23.1
22.4
N04
400
27.8
27.3
26.8
26.0
25.4
25.0
24.7
24.3
24.1
23.7
23.1
22.6
22.1
21.7
21.2
20.7
20.0
19.4
N04
405
27.8
27.3
26.8
26.0
25.4
25.0
24.7
24.3
24.1
23.7
23.1
22.6
22.1
21.7
21.2
20.7
20.0
19.4
N06
002
30.5
29.9
29.4
28.5
27.8
27.4
27.1
26.6
26.4
25.9
25.4
24.8
24.2
23.7
23.2
22.6
21.9
21.2
N06
007
29.7
29.2
28.6
27.8
27.1
26.7
26.4
26.0
25.7
25.3
24.7
24.2
23.6
23.2
22.7
22.1
21.4
20.7
N06
022
32.0
31.4
30.8
29.9
29.2
28.7
28.4
28.0
27.7
27.2
26.6
26.0
25.4
25.0
24.4
23.8
23.0
22.3
N06
030
31.4
30.8
30.2
29.3
28.6
28.1
27.8
27.4
27.1
26.7
26.1
25.5
24.9
24.5
23.9
23.3
22.6
21.8
N06
045
30.0
29.4
28.8
28.0
27.3
26.9
26.6
26.2
25.9
25.5
24.9
24.4
23.8
23.4
22.8
22.3
21.6
20.9
N06
059
32.6
32.0
31.4
30.5
29.7
29.3
29.0
28.5
28.2
27.8
27.1
26.5
25.9
25.5
24.9
24.2
23.5
22.7
N06
230
32.7
32.1
31.5
30.6
29.8
29.4
29.1
28.6
28.3
27.8
27.2
26.6
26.0
25.6
24.9
24.3
23.6
22.8
N06
455
31.9
31.3
30.7
29.8
29.1
28.6
28.3
27.9
27.6
27.1
26.5
25.9
25.3
24.9
24.3
23.7
22.9
22.2
N06
600
33.2
32.6
31.9
31.0
30.2
29.8
29.5
29.0
28.7
28.2
27.6
27.0
26.4
25.9
25.3
24.6
23.9
23.1
N06
617
...
...
...
29.2
28.5
28.0
27.7
27.3
27.0
26.6
26.0
25.4
24.8
24.4
23.8
23.2
22.5
21.8
N06
625
32.1
31.5
30.9
30.0
29.3
28.8
28.5
28.1
27.8
27.3
26.7
26.1
25.5
25.1
24.5
23.9
23.1
22.4
N06
690
32.5
31.9
31.2
30.3
29.5
29.1
28.8
28.3
28.1
27.6
27.0
26.4
25.8
25.3
24.7
24.1
23.3
22.6
N07
718
31.0
30.5
29.9
29.0
28.3
27.8
27.6
27.1
26.8
26.4
25.8
25.2
24.7
24.2
...
...
...
...
N07
750
33.2
32.6
31.9
31.0
30.2
29.8
29.5
29.0
28.7
28.2
27.6
27.0
26.4
25.9
25.3
...
...
...
N08
020
30.0
29.4
28.8
28.0
27.3
26.9
26.6
26.2
25.9
25.5
24.9
24.4
23.8
23.4
22.8
22.3
21.6
20.9
N08
031
30.7
30.1
29.6
28.7
28.0
27.6
27.3
26.8
26.5
26.1
25.5
25.0
24.4
24.0
23.4
22.8
22.1
21.4
N08
330
30.0
29.4
28.8
28.0
27.3
26.9
26.6
26.2
25.9
25.5
24.9
24.4
23.8
23.4
22.8
22.3
21.6
20.9
N08
800
30.5
29.9
29.4
28.5
27.8
27.4
27.1
26.6
26.4
25.9
25.4
24.8
24.2
23.8
23.2
22.7
21.9
21.2
N08
810
30.5
29.9
29.4
28.5
27.8
27.4
27.1
26.6
26.4
25.9
25.4
24.8
24.2
23.8
23.2
22.7
21.9
21.2
N08
825
30.0
29.4
28.8
28.0
27.3
26.9
26.6
26.2
25.9
25.5
24.9
24.4
23.8
23.4
22.8
22.3
21.6
20.9
N10
001
33.3
32.7
32.0
31.1
30.3
29.9
29.5
29.1
28.8
28.3
27.7
27.1
26.4
26.0
25.3
24.7
23.9
23.2
N10
003
33.9
33.3
32.7
31.7
30.9
30.4
30.1
29.6
29.3
28.8
28.2
27.6
26.9
26.5
25.8
25.2
24.4
23.6
N10
242
35.5
34.9
34.2
33.2
32.4
31.9
31.5
31.0
30.7
30.2
29.5
28.9
28.2
27.7
27.1
26.4
25.6
24.7
N10
276
31.9
31.3
30.7
29.8
29.1
28.6
28.3
27.9
27.6
27.1
26.5
25.9
25.3
24.9
24.3
23.7
22.9
22.2
N10
629
33.6
33.0
32.3
31.4
30.6
30.1
29.8
29.3
29.0
28.6
27.9
27.3
26.7
26.2
25.6
25.0
24.2
23.4
N10
665
33.6
33.0
32.3
31.4
30.6
30.1
29.8
29.3
29.0
28.6
27.9
27.3
26.7
26.2
25.6
25.0
24.2
23.4
N10
675
33.6
33.0
32.3
31.4
30.6
30.1
29.8
29.3
29.0
28.6
27.9
27.3
26.7
26.2
25.6
25.0
24.2
23.4
N12
160
32.7
32.1
31.5
30.6
29.8
29.4
29.1
28.6
28.3
27.8
27.2
26.6
26.0
25.6
24.9
24.3
23.6
22.8
R20
033
30.3
29.7
29.1
28.3
27.6
27.2
26.9
26.5
26.2
25.8
25.2
24.6
24.1
23.6
23.1
22.5
21.8
21.1
GE
NE
RA
LN
OT
ES
:(a
)F
orth
eS
Iun
it,
mul
tipl
yth
em
odul
usof
elas
tici
tyE
by6.
895
106
kPa.
(b)
See
Tab
leS
I-1
for
the
conv
ersi
onof
tem
pera
ture
sto
degr
ees
Cel
sius
.
675Copyright ASME International Provided by IHS under license with ASME Licensee=Technip/5931917100
Not for Resale, 02/09/2006 02:59:11 MSTNo reproduction or networking permitted without license from IHS
--``,,,```,```,`,``,,`,`,,```,`-`-`,,`,,`,`,,`---
A03
Table TM-5 2001 SECTION II
TABLE TM-5MODULI OF ELASTICITY E OF TITANIUM AND ZIRCONIUM FOR GIVEN TEMPERATURES
Material Modulus of Elasticity E p Value Given 106 psi, for Temperature, F, ofGrade/UNS
No. 70 200 300 400 500 600 700 800
Titanium Alloys
1 (R5025