Registered charity number: 207890 Showcasing research from Massachusetts Institute of Technology, Cambridge, USA, and National Institute of Standards and Technology, Gaithersburg, USA. Aligned carbon nanotube morphogenesis predicts physical properties of their polymer nanocomposites Tomography-driven three-dimensional morphology of aligned carbon nanotube (CNT) polymer nanocomposites is utilized with modelling and simulation to elucidate the underlying mechanisms governing their electrical, thermal, and mechanical behaviour. We find that elastic modulus is governed by local CNT curvature evolution with packing proximity and that transport properties scale with number of CNT–CNT junctions but to different degrees: thermal conductivity increases linearly and electrical conductivity to the ½ power with CNT–CNT junction density, respectively. These findings could enable independent property tuning of these materials for a variety of high value applications. As featured in: rsc.li/nanoscale See J. Alexander Liddle, Brian L. Wardle et al., Nanoscale, 2019, 11, 16327. ISSN 2040-3372 PAPER Lingxing Zeng, Qingrong Qian et al. Electrospun VSe /CNF composite with excellent performance for alkali metal ion batteries Nanoscale rsc.li/nanoscale Volume 11 Number 35 21 September 2019 Pages 16145–16692

Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

  • Upload
    others

  • View
    0

  • Download
    0

Embed Size (px)

Citation preview

Page 1: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Registered charity number: 207890

Showcasing research from Massachusetts Institute of

Technology, Cambridge, USA, and National Institute of

Standards and Technology, Gaithersburg, USA.

Aligned carbon nanotube morphogenesis predicts physical

properties of their polymer nanocomposites

Tomography-driven three-dimensional morphology of aligned

carbon nanotube (CNT) polymer nanocomposites is utilized with

modelling and simulation to elucidate the underlying mechanisms

governing their electrical, thermal, and mechanical behaviour.

We fi nd that elastic modulus is governed by local CNT curvature

evolution with packing proximity and that transport properties

scale with number of CNT–CNT junctions but to diff erent

degrees: thermal conductivity increases linearly and electrical

conductivity to the ½ power with CNT–CNT junction density,

respectively. These fi ndings could enable independent property

tuning of these materials for a variety of high value applications.

As featured in:

rsc.li/nanoscale

See J. Alexander Liddle, Brian L. Wardle et al. , Nanoscale , 2019, 11 , 16327.

ISSN 2040-3372

PAPER Lingxing Zeng, Qingrong Qian et al. Electrospun VSe 1.5 /CNF composite with excellent performance for alkali metal ion batteries

Nanoscalersc.li/nanoscale

Volume 11 Number 35 21 September 2019 Pages 16145–16692

Page 2: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Nanoscale

PAPER

Cite this: Nanoscale, 2019, 11, 16327

Received 18th April 2019,Accepted 16th June 2019

DOI: 10.1039/c9nr03317c

rsc.li/nanoscale

Aligned carbon nanotube morphogenesis predictsphysical properties of their polymernanocomposites†

Bharath Natarajan, ‡§a,b Itai Y. Stein, §c,d Noa Lachman, c,e

Namiko Yamamoto, c,f Douglas S. Jacobs,d Renu Sharma, g

J. Alexander Liddle *g and Brian L. Wardle *c

Carbon nanostructure (CNS) based polymer nanocomposites (PNCs) are of interest due to the superior

properties of the CNS themselves, scale effects, and the ability to transfer these properties anisotropically

to the bulk material. However, measurements of physical properties of such materials are not in agreement

with theoretical predictions. Recently, the ability to characterize the 3D morphology of such PNCs at the

nanoscale has been significantly improved, with rich, quantitative data extracted from tomographic trans-

mission electron microscopy (TEM). In this work, we use new, nanoscale quantitative 3D morphological

information and stochastic modeling to re-interpret experimental measurements of continuous aligned

carbon nanotube (A-CNT) PNC properties as a function of A-CNT packing/volume fraction. The 3D tortu-

osity calculated from tomographic reconstructions and its evolution with volume fraction is used to

develop a novel definition of waviness that incorporates the stochastic nature of CNT growth. The impor-

tance of using randomly wavy CNTs to model these materials is validated by agreement between simulated

and previously-measured PNC elastic moduli. Secondary morphological descriptors such as CNT–CNT

junction density and inter-junction distances are measured for transport property predictions. The scaling

of the junction density with CNT volume fraction is observed to be non-linear, and this non-linearity is

identified as the primary reason behind the previously unexplained scaling of aligned-CNT PNC longitudinal

thermal conductivity. By contrast, the measured electrical conductivity scales linearly with volume fraction

as it is relatively insensitive to junction density beyond percolation. This result verifies prior hypotheses that

electrical conduction in such fully percolated and continuous CNT systems is dominated by the bulk resis-

tivity of the CNTs themselves. This combination of electron tomographic data and stochastic simulations is

a powerful method for establishing a predictive capability for nanocomposite structure–property relations,

making it an essential aid in understanding and tailoring the next-generation of advanced composites.

1. Introduction

Carbon nanostructures (CNSs), when paired with a polymericmatrix, offer a hybrid material system that can be tailored formany high-value applications in addition to beingsustainable,1–6 where both components could be derived fromnaturally occurring precursors.7,8 For example, epoxy systemsreinforced with CNSs, such as graphene,9,10 graphene nano-platelets (GNPs)10 and carbon nanotubes (CNTs),11 wererecently shown to have scale-dependent electrical, thermal,and mechanical properties, making them leading candidatesfor use in applications such as electronic skin, pressuresensors, and protective films.12,13 However, the orders of mag-nitude discrepancies between physical properties forecasted bywell-established theoretical models and the experimentallyobserved material behavior means that the engineering design

†Electronic supplementary information (ESI) available. See DOI: 10.1039/c9nr03317c‡This work was primarily done while at the Center for Nanoscale Science andTechnology, National Institute of Standards and Technology, Gaithersburg,Maryland 20899, USA.§These authors contributed equally to this work.

aCenter for Nanoscale Science and Technology, National Institute of Standards and

Technology, Gaithersburg, Maryland 20899, USAbCorporate Strategic Research, ExxonMobil Research and Engineering, Annandale,

NJ, 08801, USAcDepartment of Aeronautics and Astronautics, Massachusetts Institute of Technology,

Cambridge, Massachusetts 02139, USA. E-mail: [email protected] of Mechanical Engineering, Massachusetts Institute of Technology,

Cambridge, Massachusetts 02139, USAeDepartment of Materials Science and Engineering, Tel Aviv University,

Tel Aviv 6997801, IsraelfDepartment of Aerospace Engineering, The Pennsylvania State University,

University Park, Pennsylvania 16802, USAgPhysical Measurement Laboratory, National Institute of Standards and Technology,

Gaithersburg, Maryland 20899, USA. E-mail: [email protected]

This journal is © The Royal Society of Chemistry 2019 Nanoscale, 2019, 11, 16327–16335 | 16327

Page 3: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

tools necessary for the commercial application of these next-generation materials are lacking. Although previous studieshave shown that the mechanical, thermal, and electrical pro-perties of CNS reinforced polymeric systems are sometimesadequately described using constant intrinsic CNS propertieswith, e.g., a rule-of-mixtures approach, such a simplificationmay not be appropriate when the CNS morphology is altereddue to packing evolution. See Fig. 1A–C for plots illustratingproperty and property prediction results for CNTs, graphene,and GNPs at a variety of volume fractions, which indicate thatconstant values for the elastic modulus and thermal and elec-trical conductivities do not yield accurate performance projec-tions when utilized in conjunction with rule of mixtures(Fig. 1A and B) and percolation theory (Fig. 1C). These gapsbetween predicted and measured material performance alsostem from the complete omission or overly simplistic descrip-tion of the inherent morphology of these materials, particu-larly how the morphology may evolve with volume fraction (Vf ).

Recent work on three-dimensional morphologicalquantification45,46 and modeling of CNS reinforcedpolymers47,48 has shown that a significant amount of stochas-tically-varying local curvature is exhibited by the CNSs present

in the polymer matrix.45 These works also show that suchstructural randomness leads to the formation of a largenumber of van der Waals dominated junctions that may con-tribute to the mechanical and transport properties of sucharchitectures. However, the formation of such junctionscannot be natively described by the assumptions that domi-nate previous theoretical frameworks, which primarily includesimple functional forms, whereas stochastic descriptions aremore representative of the kinetic and diffusive processes bywhich CNSs are synthesized,5,49 e.g., CNTs via chemical vapordeposition.50 See Fig. 1D for an illustration of the simple mor-phological assumptions previously used to model an exemp-lary aligned CNT system, in addition to the visualized three-dimensional CNT topology and the stochastic descriptionsused herein. Further, while the number of junctions formed inCNS architectures is strongly dependent on the CNS volumefraction, very little is currently known about how the junctiondensity evolves with CNS packing proximity (i.e., Vf ).

3D descriptions of CNS morphologies in nanocompositeshave recently been provided using quantitative electrontomography45,46 and small angle X-ray scattering.50

Specifically, we have developed an electron tomographic

Fig. 1 Measured properties of epoxy-based nanocomposites with randomly dispersed or aligned carbon nanotubes (CNTs) and other prevalentcarbon nanostructures (CNSs), i.e., graphene and graphene nano-platelets (GNPs) and morphology assumptions in property prediction tools forA-PNCs: (A) Elastic modulus (E) scaling with CNS volume fraction (Vf ) for random and aligned CNTs,14–25 graphene,26 and GNPs.27 Fitting with arule-of-mixtures equation shown in the legend demonstrates that high Vf aligned CNTs exhibit the highest effective CNS modulus, Eo. (B) Thermalconductivity (k) as a function of CNS Vf for random and aligned CNTs,28–32 graphene,33–37 and GNPs.27,31–33,38,39 Fitting with a rule-of-mixturesequation in the legend demonstrates that graphene and GNPs exhibit the highest effective CNS thermal conductivity, ko, while the best overallthermal conductivity k is measured for the highest Vf CNT nanocomposite. (C) Electrical conductivity (σ) as a function of CNS Vf for random andaligned CNTs,30,40–42 graphene,27,43,44 and GNPs.38 Fitting with the power-law equation shown in the legend indicates that although CNT and gra-phene composites can reach similar σ, since their effective CNS electrical conductivity, σo, is of similar magnitude, their percolation exponent (t ) canvary significantly. (A)–(C) demonstrate that although CNT-based polymer nanocomposites could exhibit the best mechanical and transport pro-perties of all the CNSs, precise morphological descriptors are needed to avoid orders of magnitude over- or under-prediction of resultant physicalproperties. (D) Illustrations of the two commonly assumed morphologies of A-PNCs in comparison to the three-dimensional reconstruction and themorphology generated according to such reconstructions using the current simulation framework.

Paper Nanoscale

16328 | Nanoscale, 2019, 11, 16327–16335 This journal is © The Royal Society of Chemistry 2019

Page 4: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

approach that permits the extraction and quantification of the3D arrangement of aligned CNT forests embedded in a poly-meric matrix (Fig. S1†).45 Morphological metrics describingthe network structure such as alignment, proximity, junctiondensity, and waviness may be obtained from the resultant digi-tized reconstructions with nanometer resolution. Sincealigned CNTs exhibit the best combination of mechanical,thermal, and electrical properties among the previouslystudied CNS reinforced polymer systems (see Fig. 1A),17,29,42

and were also the subject of our recent experimental and com-putational work on their three-dimensional morphology, thissystem was selected to be the focus of the current study.

Here, we use newly available morphogenesis (evolution ofmorphology with increasing Vf ) data from electron tomographyand stochastic simulations, to develop more representativemechanical, thermal, and electrical property prediction toolsfor aligned CNT polymer nanocomposites (A-PNCs) in direc-tions that are both parallel and transverse to the CNT primaryaxis. Firstly, using the tortuosity measured by 3D TEM, weintroduce a new 3D stochastic definition of waviness, which isfound to provide the best match to previously-measuredmodulus data. We then establish the scaling of the CNT–CNTjunction density with CNT Vf. This scaling is used to shedlight on the dependence of transport properties on CNTnetwork structure and its evolution with Vf. We believe that thestructure–property correlations established here will providevaluable insights into many other past and future results fromstudies of similar nanocomposites and aligned CNT struc-tures. More broadly, the findings reported herein are expectedto be generalizable to other CNS-PNC systems with well charac-terized 3D morphology.

2. Results and discussion

The aligned-CNT (A-CNT) polymer nanocomposites in all theprevious studies cited here17,29,42 were fabricated identically.Multiwalled carbon nanotube (MWCNT, (7.65 ± 0.87) nm indiameter, (mean ± one standard deviation)) forests were grownby thermal chemical vapor deposition. The volume fraction ofthese MWCNTs in the as-grown forest was estimated to be≈1%. The CNT forests were then released from the substrate,densified perpendicular to the growth direction to various Vfs,impregnated with an epoxy matrix via capillary action andcured appropriately (Fig. S1e†). Further details of the A-PNCfabrication process are described elsewhere.17,29,42 At allvolume fractions, the epoxy matrix is not measured to havebeen modified by the presence of the A-CNTs, as studied viawide-angle X-ray scattering (WAXS)51 and differential scatteringcalorimetry (DSC).52 This is a critical and useful assumption inthis work as many polymers, particularly thermoplastics, havestrong process-nanostructure interactions causing the polymermorphology and crystallization degree to alter, among othereffects.53–55 Statistically representative 3D reconstructions ofA-CNTs in the A-PNCs of ex situ Vfs of 1.00%, 5.00%, 6.00%and 11.70%, estimated from the change in volume of the

forests before epoxy infiltration, were obtained using electrontomography as described earlier (Fig. S1a–d†).45 The recon-structions were quantified to obtain pertinent morphologicaldata via 3D image analysis.45 This morphological data (Vf, CNTproximity and waviness/tortuosity) is required to build analyti-cal models of the A-PNCs for stochastic simulations.

Our imaging method enables, for the first time, the accu-rate measurement of A-CNT Vf in the nanocomposites (nomin-ally the in situ Vf ), among other quantitative features.45

Comparing the ex situ and in situ Vfs we observe that polymerimpregnation into the porous A-CNT forest causes it to expandlaterally (normal to the alignment axis), resulting in a lower Vfthan that estimated post densification (in situ Vfs of (0.44 ±0.01) %, (2.58 ± 0.25) %, (4.04 ± 0.19) %, (6.89 ± 0.43) %,ex situ Vfs of 1.00%, 5.00%, 6.00% and 11.70%, respectively).From the plot of in situ composite Vf versus the ex situ Vf of thedensified starting material (Fig. S1f†), we find that a correctivefactor of 0.59 can be applied to all the Vf values reportedearlier,17,29,42 which did not account for the polymer-inducedexpansion. The inter-CNT spacings or CNT proximity (Γ) is thesecond morphological factor and can be readily calculatedfrom the tomography data (Fig. S2†). With increased Vf weobserve a non-linear reduction in Γ, which is in excellentagreement with the trends observed in the data obtained fromSEM images of as-grown densified CNT arrays (Fig. S2†).56 Assuggested by Stein et al., the mean spacings take the form:

ΓðVfÞ � δ

ffiffiffiffiffiffiffiffiffiffiffiffiffiffi0:9069Vf

r� 1

� �ð1Þ

where δ is representative of the average coordination numberof the CNTs from the volume.56 We note that unlike prior 1Dmeasurements made using SEM, our automated measure-ments, which sample large volumes of data, allow for morestatistically significant characterization of the Γ distribution.The calculated distributions are observed to be increasinglymonodisperse with increasing Vf (Fig. S2†). Further, these dis-tributions also suggest that the CNT packing density isspatially variant, particularly at lower Vfs.

3D tortuosity of the CNTs, the third morphological factor,is key to stochastic simulations of morphology and can also bequantified from our tomography data. From the skeletonized3D volumes of the 4 different Vf A-PNCs studied (ex situ Vfs of1.00%, 5.00%, 6.00% and 11.70%), we extract tube arc length(l) to Euclidean distance (d ) ratios i.e., tortuosity (l/d ), for tubesegments in the tomographic volume whose lengths are atleast 10 times larger than the diameter of the CNTs (7.65 nm)(Fig. S3a†). The segments have to be at least of this length inorder for us to extract a meaningful, representative waviness.We observe the 3D tortuosity to decrease with increasing Vf,suggesting a straightening of CNTs due to increased confine-ment (Fig. S3b†). However, the tortuosity measured here doesnot explicitly capture the nature or functional form of wavi-ness, which is also an essential morphological descriptor. Thewaviness of CNTs has been previously described using simplesinusoidal and helical functions that neglect the stochastic

Nanoscale Paper

This journal is © The Royal Society of Chemistry 2019 Nanoscale, 2019, 11, 16327–16335 | 16329

Page 5: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

nature of CNT growth.57,58 Here, we employ our novel defi-nition of waviness, which provides a more realistic representa-tion CNT morphology in the form of a “random” helical func-tion. The usual waviness ratio (w) is a scalar measure of wavi-ness that is typically defined as the amplitude over the wave-length of the chosen waviness function. For the randomhelical definition this ratio is modified by a pre-factor asdescribed in other work.47,59 Depending on the assumed geo-metry (i.e. sinusoidal/helical/randomly helical), the 3D tortuos-ity for a given w will vary drastically. The tortuosity versus wplot in Fig. 2B shows how the tortuosity may be converted toan analytical/deterministic waviness (i.e. w) and vice versa.48

Using the 3D morphology data, we first consider the elasticmodulus of the A-PNCs.

2.1 Mechanical properties

The axial and transverse/lateral elastic moduli of these A-PNCsmeasured by Handlin et al.17 are plotted as a function of Vf inFig. 2C. The in situ Vfs shown here are corrected for volumetricexpansion during polymer infiltration (previously-reportedex situ Vf × 0.59). Despite the correction, the measured elasticmoduli are found to be an order of magnitude smaller thanexpected based on simple rule-of-mixtures calculations (seeFig. 1A). For example, at 12.00 vol% CNTs, the expected com-posite modulus is ≈60.0 GPa for a conservative CNT modulusof ≈500 GPa. However, the measured value is 6.4 GPa. In priorwork it has been demonstrated that CNT waviness is theprimary cause of this reduction.17,57 Indeed, pre-straining ofCNT films to reduce waviness has been found to yield signifi-cantly higher elastic modulus values.21 Reciprocally, themodulus of the reinforcing CNT phase (Eo) i.e., the contri-bution of the CNT to the modulus of the nanocomposite, maybe thought of as reducing with increasing waviness. It is poss-ible to calculate the CNT reinforcement modulus, Eo, and itsevolution as a function of waviness using our simulations,47

where each CNT is represented as a series of discrete nodes(Fig. 2A and Fig. S4a†). To apply the appropriate waviness tothe CNTs, the displacement of each node relative to the nodethat precedes it in the x–y plane, is evaluated using the ampli-tude and wavelength. Stochastic waviness is achieved by using2 Gaussian distributions to independently evaluate displace-ments in the lateral directions (x–y). Looking in the axial direc-tion (z) we observe that this is essentially a two-dimensionalrandom walk of a helically wavy CNT (Fig. S4a†). Our simu-lations are run on large ensembles of these CNTs (Fig. 1D andFig. S4a†), at the requisite Vfs, to get a statistically representa-tive reinforcement modulus for the system. The simulated datafor the random helical system is shown in the plot of reinforce-ment modulus (Ef ) versus waviness ratio in Fig. S4b,† where weobserve Ef to decrease with increasing waviness. We note thatlarger ratios between the CNT (Y) and matrix moduli (Em)result in larger reductions in Ef (Fig. S4b†).

Most prior studies have employed a constant waviness ratioto fit moduli measured over a range of Vfs, which leads to astrong under- or over-estimation of the elastic modulusdepending on the Vf at which the waviness was measured.Since waviness changes with the Vf

45,60 – decreasing at higherVfs due to increased crowding – a careful study of the evolutionof waviness with CNT packing is essential to interpret thecomplex dependence of the modulus on Vf. Using themeasured trend in waviness with Vf (Fig. S3†), we generatesinusoidal, helical and randomly helical CNT morphologies atthe Vfs studied by Handlin et al.17 The reinforcement modulusof these CNTs (Ef ) at various Vfs is measured using our simu-lation technique47 and inserted into the rule-of-mixturesformula (EA-PNC = Vf × Ef + (1 − Vf ) × EMatrix) to estimate thecomposite elastic modulus. From Fig. S5,† we note that,despite accounting for the change in waviness with Vf, thesinusoidal and helical assumptions strongly underestimate theA-PNC properties. This indicates that such simplistic defi-

Fig. 2 Deformation modes, morphological descriptors, and modulus modeling: (A) Illustration of the dominant physical mechanisms for CNTmechanical response. (B) Plot of tortuosity versus the analytical waviness ratio (w) for sinusoidal, helical and random helical formulations of wavi-ness.48 The shaded region represents the range of tortuosity (τ) values calculated from tomography data. (C) Elastic modulus (E) of A-PNCs in thelongitudinal (||, parallel to CNT alignment) and transverse (⊥, perpendicular to CNT alignment) directions, and the respective model predictions, as afunction of the in situ CNT volume fraction Vf and accounting for morphology evolution. E scaling for A-PNCs shows that higher Vf mediated wavi-ness reduction leads to significant enhancement in the E previously measured17 in the parallel (||) direction, whereas the perpendicular (⊥) directionsees little benefit with higher Vf.

Paper Nanoscale

16330 | Nanoscale, 2019, 11, 16327–16335 This journal is © The Royal Society of Chemistry 2019

Page 6: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

nitions of waviness are inadequate in describing the mechani-cal performance of these systems (see discussion in Fig. S5†).Remarkably, the random helical definition, which is the firstto account for the stochastic CNT morphology, provides thebest match to the measured nanocomposite modulus (Fig. 2Band Fig. S5†). This result strongly supports the need to expli-citly consider the stochastic nature of CNT morphology, andits evolution with increased crowding.

We note that the model CNT ensembles generated usingthe 3 primary structural descriptors (Vf, proximity and wavi-ness/tortuosity) obtained by tomography, also show agreementwith secondary or derivative structural features such asCNT–CNT junction density (NJ) and the average distancebetween nearest contact points (ξ) (Fig. 3). This agreementfurther validates the random helical formulation developedherein. We obtain NJ (m

−3) by skeletonizing the reconstructed

3D volumes (Fig. S1 and S6†) and tallying the number of CNT–CNT contacts i.e., branches in the skeletonized structures(Fig. 3A).61 We find that, as the CNTs are brought closer, theshort range van der Waals attractions cause them to cluster,45

causing a non-linear increase in NJ, best fit by a power lawequation, NJ (m−3) = 3 × 1021 Vf

1.5. NJ increases by nearlytwo orders of magnitude ((7.24 ± 1.13) × 1020 m−3 to ((5.38 ±0.63) × 1022 m−3) for an order of magnitude increase in in situVf ((0.44 ± 0.01) % to (6.89 ± 0.43) %) (Fig. 3B). We note thatthese experimentally measured NJ values are in good agree-ment (in the order of magnitude, ∼1022 m−3) with earlier com-putational calculations of NJ in CNT films.62 However, thesecalculations predict a quadratic dependence of NJ on Vfwhereas our data shows NJ ∼ Vf

1.5. That said, the earlier worksimplistically assumed that CNTs are rigid rod-like objects,whereas they are only stiff along the local plane of the CNTwall, and rather overall compliant due to shear and bendingmodes (see Fig. 2A).62,63 On the other hand, here we have realestimates from high quality tomography data. The average dis-tance between nearest contact points (ξ) may also be readilycalculated from NJ using:

62

ξ ¼ 8Vf

NJπd2ð2Þ

where d is the average outer diameter of the CNTs = (7.65 ±0.87) nm.45 Eqn (2) makes the usual geometric assumptionthat in aligned arrays, the area fraction of CNTs (in a plane per-pendicular to the CNT axes) is equal to Vf. From eqn (2), wenote that if NJ indeed scaled linearly with Vf, ξ would be a con-stant. However, ξ exhibits an inverse power law dependence onVf (ξ ∼ Vf

−0.5, Fig. 3B) that is much weaker than the inversescaling predicted for randomly contacting uncorrelated rods,62

but consistent with the scaling predictions for diffusion-limited networks of semi-dilute elongated macromoleculespredicted by de Gennes and coworkers (ξ ∼ Vf

−0.5).64,65

We now turn our attention to the transport properties(thermal and electrical conductivity) of the A-PNCs utilizingthe junction density and distance quantification discussedabove.

2.2 Thermal properties

A-PNCs have been proposed as candidate materials forthermal interfaces and thermoelectric power devices, owing tothe excellent thermal properties of CNTs.66,67 These compo-sites have been found to possess some of the highest thermalconductivities, in particular compared to randomly-orientedCNT dispersions.29 However, Marconnet et al.,29 like manyothers before,68,69 observed the axial thermal conductivity ofthe CNT arrays and resultant nanocomposites to fall far shortof what would be expected from a pristine CNT with a modestthermal conductivity of 1000 W m−1 K−1 (Fig. 4B).70 They alsofound the axial composite thermal conductivity to increasenon-linearly with increased Vf, indicating that the simplemodel of parallel CNTs conducting heat within the matrix isunsupported. Additionally, they observed the anisotropy to

Fig. 3 Effects of mechanical densification on the morphology ofA-PNCs. (A) Three-dimensional rendering of the packing morphology ofthe CNTs that comprise A-PNCs showing that although randomness andwaviness is reduced as the volume fraction (Vf ) increases, the CNTsretain non-negligible local curvature. (B) Scaling of the junction densityand average junction separation as a function of Vf extracted from thethree-dimensional reconstructions of A-PNCs showing close agreementwith the random-helical simulation results.

Nanoscale Paper

This journal is © The Royal Society of Chemistry 2019 Nanoscale, 2019, 11, 16327–16335 | 16331

Page 7: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

increase at higher CNT Vf i.e., the axial thermal conductivityincreased more rapidly than the transverse thermal conduc-tivity with increased Vf. In the absence of any variation in theintrinsic CNT properties with densification (invariant ID/IGratios ∼0.7 and diameter), the authors speculated that thereduced thermal conductivity, as well as most of the non-line-arity, is caused by the interaction between CNTs and betweenthe CNT and the polymer. They also suggested that any modelexplaining the dependence of thermal conductivity on CNT Vfshould include the Vf effect on other morphological factors.Our recent imaging methodology facilitates this investigation.45

We plot the thermal conductivity values (k) reported inMarconnet et al. against the corresponding corrected, or in situVfs, (Fig. 4B).29 We find that the best approximation to thetrend in the corrected data is given by (k − km) = (115 ± 17)(W m−1 K−1) Vf

1.56, as opposed to (k − km) = 73 (W m−1 K−1)Vf

1.72, suggested in the original paper (Fig. S7a†).29 Theincrease in the prefactor in this relationship suggests a stron-ger contribution of the CNTs to conduction than originally cal-culated.29 While the power-law dependence might appearsimilar to percolation behavior, we note that such scaling atthe high CNT loadings investigated here has been found to bedue to network characteristics dominated by CNT–CNTcontact resistance.63 Marconnet et al. speculated, in accord-

ance with previous findings, that the upward concave trend inthe data was indicative that the number density of CNT–CNTcontacts (NJ) was increasing (although the nature of thisincrease was then unclear). Now that CNT–CNT contactdensity can be quantified, it appears that the scaling of NJ withVf (NJ ∼ Vf

1.50) in our tomography data (Fig. 4C) is identical tothe thermal conductivity power law behavior (k ∼ Vf

1.50) in thecorrected property data, which validates the original interpret-ation of the data. Additionally, in the plot of the thermal con-ductivity enhancement versus the estimated NJ for the cor-rected Vfs in Marconnet et al., we observe a close-to-lineardependence (discounting the clear outlier indicated by reddata point in Fig. S7b†). Indeed, the CNT networks, growingand interconnecting with the increased Vf, act as “heat pipes”throughout the composite, thus increasing thermal conduc-tivity as their cross-sectional area contribution to the nano-composite increases with Vf.

From our tomography data we are able to provide the firstquantitative support to hypotheses linking morphologicalchanges and the non-linear increase in thermal conductivityin aligned CNT composites. While it is possible for othersources of non-linearity to exist (see details in ESI, Fig. S8 andS9†), the 3D data reveals that the primary source of non-linear-ity is the non-linearly increasing density of CNT–CNT contacts

Fig. 4 Transport properties of A-PNCs in || and ⊥ directions, and the respective morphological model predictions, as a function of the CNT volumefraction (Vf ). (A) Illustration of exemplary A-PNC morphology along with the potential physical mechanisms for each material property. (B) Thermalconductivity (k) evolution for A-PNCs illustrating that the increases previously observed in k are directly proportional to the changes in junctiondensity (NJ). Here k|| ≈ (115 ± 17) W m−1 K−1, and that k⊥ ≈ (35 ± 5) W m−1 K−1. (C) Electrical conductivity (σ) for A-PNCs illustrating that σ increaseswith Vf at a scaling of σ ∝ (NJ)

0.5.

Paper Nanoscale

16332 | Nanoscale, 2019, 11, 16327–16335 This journal is © The Royal Society of Chemistry 2019

Page 8: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

with Vf. A natural conclusion from this newly exposed data isthat, contrary to the original interpretation, in order toincrease the thermal conductivity in a realistic system, withimperfect alignment and continuity, the number of CNT–CNTcontacts needs to be maximized, as it provides more axial path-ways for phonon transport. These findings further emphasizethe importance of network visualization, and allow for betterunderstanding of the origin and limitations on A-PNC thermalconductivity.

2.3 Electrical properties

The excellent axial electrical properties of CNTs make alignedCNT structures and their composites ideal candidates for flex-ible conductors, tactile displays and sensors.5,71–76 We brieflydiscuss previously unpublished electrical conductivity data inlight of the new tomography results. Re-plotting the electricalconductivity (σ) versus the correct in situ Vfs (Fig. 4C), reveals astronger contribution of CNTs to conduction than originallypresumed. However, unlike in the case of thermal conduc-tivity, which scales linearly with NJ (i.e., k ∼ Vf

3/2), the electricalconductivities are found to exhibit a weak (NJ)

0.5 scaling (i.e.,σ ∼ Vf

3/4). Such scaling of electrical conductivity with NJ wasrecently reported for nanowire networks,77,78 and previousstudies on continuous aligned CNT composites have reportedsimilar σ scaling with Vf that is approximately linear innature.22,24,79,80 This observation is in contrast with the percola-tion-like scaling of (σ ∼ Vf

2) commonly observed in randomlydispersed CNT composites.81 This is because A-PNCs are alwaysbeyond percolation axially as the CNTs are continuous. Further,the data also shows the same to be true transversely. Keblinskiet al. suggest that this linear scaling at volume fractions wellabove percolation may be due to the bulk resistivity dominatedconduction, as opposed to contact resistance based conduction(seen with thermal transport in continuous composites andelectrical transport in randomly dispersed CNT composites).63

In such electrical conduction, the non-linear increase in thecontact density does not play a significant role since the con-duction is dependent on the concentration of bulk conductors,i.e., the number of parallel pathways between the electrodes,which is proportional to the Vf.

63 The additional CNT–CNTjunctions do not play a significant role in conduction. Theseresults indicate that the various relevant physical properties ofA-PNCs are sensitive to the evolution of morphological featuresto varying degrees. Our novel characterization of the scaling ofproperties with changing structure provides a basis for theoptimization and design of multifunctional A-PNC properties.

3. Conclusions

Using the newly-acquired high-resolution 3D imaging to re-visit previous experimental results has allowed for betterunderstanding of A-CNT based PNC behavior. Previousinterpretations have been strongly validated in some cases,and significantly modified in others, based on the new nano-scale, quantitative, morphological data. All the properties con-

sidered (thermal, electrical, mechanical) depend to varyingdegrees on Vf, and the 3D data corrects the prior ex situ assess-ments (based on densified volume considerations) to in situones. CNT waviness, strongly dependent on Vf, is a significantfactor in reducing observed modulus trends compared tomoduli predicted by simulations and computational modelingwork elsewhere.47,59 Most importantly, the stochastic nature ofCNT morphology must be accounted for in modeling themechanical properties. CNT–CNT network connections (and thecontinuous CNT length between connections) play a dominantrole in thermal transport; and since they increase non-linearlywith CNT Vf, thermal conductivity should, and indeed does seemto follow this trend. The electrical conductivity, on the otherhand, is found to weakly scale with junction density, therebysuggesting that electron conduction in A-CNT nanocompositeswell beyond percolation is volume-resistivity dominated, ratherthan by the increased participation of CNT junctions. Theseunderstandings, made possible only due to the new 3D data, cannow make PNC tailoring smarter, and more efficient.

Disclaimer

Certain commercial equipment, instruments, software, ormaterials are identified in order to specify the experimentalprocedure adequately. Such identification is not intended toimply recommendation or endorsement by the NationalInstitute of Standards and Technology, nor is it intended toimply that the materials or equipment identified are necess-arily the best available for the purpose.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

This work was supported by ANSYS, Airbus, Embraer, LockheedMartin, Saab AB, Saertex, and Teijin Carbon America throughMIT’s Nano-Engineered Composite aerospace STructures(NECST) Consortium and was carried out in part through theuse of MIT’s Microsystems Technology Laboratories. Research(for B. Natarajan) was supported by a Cooperative ResearchAgreement (CRA) between the University of Maryland and theNational Institute of Standards and Technology (NIST) (grant70NANB10H193). I. Stein was supported (in part) by theDepartment of Defense (DoD) through the National DefenseScience & Engineering Graduate Fellowship (NDSEG) Program.B. Wardle and I. Stein acknowledge partial support from theNational Aeronautics and Space Administration (NASA) SpaceTechnology Research Institute (STRI) for Ultra-StrongComposites by Computational Design (US-COMP), grant numberNNX17AJ32G, and from the U.S. Office of Naval Research undergrant/contract number N00014-13-1-0213. We acknowledgeDr Thomas Lam (NIST) for useful discussions.

Nanoscale Paper

This journal is © The Royal Society of Chemistry 2019 Nanoscale, 2019, 11, 16327–16335 | 16333

Page 9: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Notes and references

1 N. Domun, H. Hadavinia, T. Zhang, T. Sainsbury,G. H. Liaghat and S. Vahid, Nanoscale, 2015, 7, 10294–10329.

2 A. Alam, Y. Zhang, H.-C. Kuan, S.-H. Lee and J. Ma, Prog.Polym. Sci., 2018, 77, 1–18.

3 V. Schroeder, S. Savagatrup, M. He, S. Lin andT. M. Swager, Chem. Rev., 2019, 119, 599–663.

4 J. Kim, M. S. Choi, K. H. Shin, M. Kota, Y. Kang, S. Lee,J. Y. Lee and H. S. Park, Adv. Mater., 2019, 1803444.

5 R. Rao, C. L. Pint, A. E. Islam, R. S. Weatherup,S. Hofmann, E. R. Meshot, F. Wu, C. Zhou, N. Dee,P. B. Amama, J. Carpena-Nuñez, W. Shi, D. L. Plata,E. S. Penev, B. I. Yakobson, P. B. Balbuena, C. Bichara,D. N. Futaba, S. Noda, H. Shin, K. S. Kim, B. Simard,F. Mirri, M. Pasquali, F. Fornasiero, E. I. Kauppinen,M. Arnold, B. A. Cola, P. Nikolaev, S. Arepalli, H.-M. Cheng,D. N. Zakharov, E. A. Stach, J. Zhang, F. Wei, M. Terrones,D. B. Geohegan, B. Maruyama, S. Maruyama, Y. Li,W. W. Adams and A. J. Hart, ACS Nano, 2018, 12, 11756–11784.

6 I. A. Kinloch, J. Suhr, J. Lou, R. J. Young and P. M. Ajayan,Science, 2018, 362, 547 LP–553.

7 V. Kuzmenko, O. Naboka, M. Haque, H. Staaf,G. Göransson, P. Gatenholm and P. Enoksson, Energy,2015, 90, 1490–1496.

8 T. Ramanathan, A. A. Abdala, S. Stankovich, D. A. Dikin,M. Herrera-Alonso, R. D. Piner, D. H. Adamson,H. C. Schniepp, X. Chen, R. S. Ruoff, S. T. Nguyen,I. A. Aksay, R. K. Prud’Homme and L. C. Brinson, Nat.Nanotechnol., 2008, 3, 327–331.

9 H. Kim, A. A. Abdala and C. W. Macosko, Macromolecules,2010, 43, 6515–6530.

10 K. Hu, D. D. Kulkarni, I. Choi and V. V. Tsukruk, Prog.Polym. Sci., 2014, 39, 1934–1972.

11 M. Moniruzzaman and K. I. Winey, Macromolecules, 2006,39, 5194–5205.

12 M. F. L. De Volder, S. H. Tawfick, R. H. Baughman andA. J. Hart, Science, 2013, 339, 535–539.

13 S. K. Kumar, B. C. Benicewicz, R. A. Vaia and K. I. Winey,Macromolecules, 2017, 50, 714–731.

14 Y. Breton, G. Désarmot, J. P. Salvetat, S. Delpeux,C. Sinturel, F. Béguin and S. Bonnamy, Carbon, 2004, 42,1027–1030.

15 M. Omidi, H. Rokni D. T., A. S. Milani, R. J. Seethaler andR. Arasteh, Carbon, 2010, 48, 3218–3228.

16 M. Li, Z. Wang, Q. Liu, S. Wang, Y. Gu, Y. Li and Z. Zhang,Polym. Compos., 2017, 38, 588–596.

17 D. Handlin, I. Y. Stein, R. Guzman de Villoria, H. Cebeci,E. M. Parsons, S. Socrate, S. Scotti and B. L. Wardle, J. Appl.Phys., 2013, 114, 224310.

18 A. Montazeri, J. Javadpour, A. Khavandi, A. Tcharkhtchiand A. Mohajeri, Mater. Des., 2010, 31, 4202–4208.

19 M. R. Ayatollahi, S. Shadlou and M. M. Shokrieh, Mater.Des., 2011, 32, 2115–2124.

20 S. U. Khan, J. R. Pothnis and J.-K. Kim, Composites, Part A,2013, 49, 26–34.

21 P. D. Bradford, X. Wang, H. Zhao, J.-P. Maria, Q. Jia andY. T. Zhu, Compos. Sci. Technol., 2010, 70, 1980–1985.

22 Q. F. Cheng, J. P. Wang, J. J. Wen, C. H. Liu, K. L. Jiang,Q. Q. Li and S. S. Fan, Carbon, 2010, 48, 260–266.

23 T. H. Nam, K. Goto, H. Nakayama, K. Oshima, V. Premalal,Y. Shimamura, Y. Inoue, K. Naito and S. Kobayashi,Composites, Part A, 2014, 64, 194–202.

24 M. Mecklenburg, D. Mizushima, N. Ohtake, W. Bauhofer,B. Fiedler and K. Schulte, Carbon, 2015, 91, 275–290.

25 A. Mikhalchan, T. Gspann and A. Windle, J. Mater. Sci.,2016, 51, 10005–10025.

26 C. E. Corcione, F. Freuli and A. Maffezzoli, Polym. Eng. Sci.,2013, 53, 531–539.

27 F. Wang, L. T. Drzal, Y. Qin and Z. Huang, J. Mater. Sci.,2015, 50, 1082–1093.

28 J. Yang, S. Waltermire, Y. Chen, A. A. Zinn, T. T. Xu andD. Li, Appl. Phys. Lett., 2010, 96, 023109.

29 A. M. Marconnet, N. Yamamoto, M. A. Panzer, B. L. Wardleand K. E. Goodson, ACS Nano, 2011, 5, 4818–4825.

30 J. G. Park, Q. Cheng, J. Lu, J. Bao, S. Li, Y. Tian, Z. Liang,C. Zhang and B. Wang, Carbon, 2012, 50, 2083–2090.

31 A. Yu, P. Ramesh, M. E. Itkis, E. Bekyarova andR. C. Haddon, J. Phys. Chem. C, 2007, 111, 7565–7569.

32 X. Huang, C. Zhi and P. Jiang, J. Phys. Chem. C, 2012, 116,23812–23820.

33 X. Shen, Z. Wang, Y. Wu, X. Liu, Y.-B. He and J.-K. Kim,Nano Lett., 2016, 16, 3585–3593.

34 C.-C. Teng, C.-C. M. Ma, C.-H. Lu, S.-Y. Yang, S.-H. Lee,M.-C. Hsiao, M.-Y. Yen, K.-C. Chiou and T.-M. Lee, Carbon,2011, 49, 5107–5116.

35 Q. Li, Y. Guo, W. Li, S. Qiu, C. Zhu, X. Wei, M. Chen,C. Liu, S. Liao, Y. Gong, A. K. Mishra and L. Liu, Chem.Mater., 2014, 26, 4459–4465.

36 G. Lian, C.-C. Tuan, L. Li, S. Jiao, Q. Wang, K.-S. Moon,D. Cui and C.-P. Wong, Chem. Mater., 2016, 28, 6096–6104.

37 Z. Liu, D. Shen, J. Yu, W. Dai, C. Li, S. Du, N. Jiang, H. Liand C.-T. Lin, RSC Adv., 2016, 6, 22364–22369.

38 X. Tian, M. E. Itkis, E. B. Bekyarova and R. C. Haddon, Sci.Rep., 2013, 3, 1710.

39 H. Yan, Y. Tang, W. Long and Y. Li, J. Mater. Sci., 2014, 49,5256–5264.

40 I. D. Rosca and S. V. Hoa, Carbon, 2009, 47, 1958–1968.41 Q.-P. Feng, J.-P. Yang, S.-Y. Fu and Y.-W. Mai, Carbon, 2010,

48, 2057–2062.42 H. Cebeci, R. Guzman de Villoria, A. J. Hart and

B. L. Wardle, Compos. Sci. Technol., 2009, 69, 2649–2656.43 J. Jia, X. Sun, X. Lin, X. Shen, Y.-W. Mai and J.-K. Kim, ACS

Nano, 2014, 8, 5774–5783.44 X. Liu, X. Sun, Z. Wang, X. Shen, Y. Wu and J.-K. Kim, ACS

Appl. Mater. Interfaces, 2015, 7, 21455–21464.45 B. Natarajan, N. Lachman, T. Lam, D. Jacobs, C. Long,

M. Zhao, B. L. Wardle, R. Sharma and J. A. Liddle, ACSNano, 2015, 9, 6050–6058.

Paper Nanoscale

16334 | Nanoscale, 2019, 11, 16327–16335 This journal is © The Royal Society of Chemistry 2019

Page 10: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

46 K. Gnanasekaran, C. Grimaldi, G. With and H. Friedrich,Adv. Funct. Mater., 2019, 29, 1807901.

47 I. Y. Stein and B. L. Wardle, Nanotechnology, 2016, 27,035701.

48 I. Y. Stein and B. L. Wardle, Phys. Chem. Chem. Phys., 2016,18, 694–699.

49 M. Bedewy and M. Abdulhafez, in Nanotube SuperfiberMaterials, Elsevier, 2019, pp. 31–64.

50 E. R. Meshot, D. W. Zwissler, N. Bui, T. R. Kuykendall,C. Wang, A. Hexemer, K. J. J. Wu and F. Fornasiero, ACSNano, 2017, 11, 5405–5416.

51 B. L. Wardle, D. S. Saito, E. J. García, A. J. Hart,R. Guzman de Villoria and E. A. Verploegen, Adv. Mater.,2008, 20, 2707–2714.

52 S. S. Wicks, PhD thesis, Massachusetts Institute ofTechnology, 2014.

53 J. L. Gair, R. H. Lambeth, D. P. Cole, D. L. Lidston,I. Y. Stein, E. Kalfon-Cohen, A. J. Hsieh, H. A. Bruck,M. L. Bundy and B. L. Wardle, Compos. Sci. Technol., 2018,166, 115–124.

54 D. Roy, A. P. Kotula, B. Natarajan, J. W. Gilman, D. M. Foxand K. B. Migler, Polymer, 2018, 153, 70–77.

55 J. N. Coleman, M. Cadek, K. P. Ryan, A. Fonseca, J. B. Nagy,W. J. Blau and M. S. Ferreira, Polymer, 2006, 47, 8556–8561.

56 I. Y. Stein and B. L. Wardle, Phys. Chem. Chem. Phys., 2013,15, 4033.

57 F. T. Fisher, R. D. Bradshaw and L. C. Brinson, Appl. Phys.Lett., 2002, 80, 4647–4649.

58 U. Vainio, T. I. W. Schnoor, S. Koyiloth Vayalil, K. Schulte,M. Müller and E. T. Lilleodden, J. Phys. Chem. C, 2014, 118,9507–9513.

59 I. Y. Stein, D. J. Lewis and B. L. Wardle, Nanoscale, 2015, 7,19426–19431.

60 H. Cebeci, I. Y. Stein and B. L. Wardle, Appl. Phys. Lett.,2014, 104, 023117.

61 I. Arganda-Carreras, R. Fernández-González, A. Muñoz-Barrutia and C. Ortiz-De-Solorzano, Microsc. Res. Tech.,2010, 73, 1019–1029.

62 P. E. Lyons, S. De, F. Blighe, V. Nicolosi, L. F. C. Pereira,M. S. Ferreira and J. N. Coleman, J. Appl. Phys., 2008, 104,044302.

63 P. Keblinski and F. Cleri, Phys. Rev. B: Condens. Matter,2004, 69, 184201.

64 C. F. Schmidt, M. Baermann, G. Isenberg andE. Sackmann, Macromolecules, 1989, 22, 3638–3649.

65 B. Natarajan, N. D. Orloff, R. Ashkar, S. Doshi, K. Twedt,A. Krishnamurthy, C. Davis, A. M. Forster, E. Thostenson,J. Obrzut, R. Sharma and J. A. Liddle, Carbon, 2016, 108,381–393.

66 H. Huang, C. H. Liu, Y. Wu and S. Fan, Adv. Mater., 2005,17, 1652–1656.

67 F. Rivadulla, C. Mateo-Mateo and M. A. Correa-Duarte,J. Am. Chem. Soc., 2010, 132, 3751–3755.

68 Z. Han and A. Fina, Prog. Polym. Sci., 2011, 36, 914–944.69 A. M. Marconnet, M. A. Panzer and K. E. Goodson, Rev.

Mod. Phys., 2013, 85, 1295–1326.70 M. Fujii, X. Zhang, H. Q. Xie, H. Ago, K. Takahashi,

T. Ikuta, H. Abe and T. Shimizu, Phys. Rev. Lett., 2005, 95,065502.

71 H. Peng, J. Am. Chem. Soc., 2008, 130, 42–43.72 Y. J. Jung, S. Kar, S. Talapatra, C. Soldano, G. Viswanathan,

X. Li, Z. Yao, F. S. Ou, A. Avadhanula, R. Vajtai, S. Curran,O. Nalamasu and P. M. Ajayan, Nano Lett., 2006, 6, 413–418.

73 L. Liu, W. Ma and Z. Zhang, Small, 2011, 7, 1504–1520.74 M. Endo, M. S. Strano and P. M. Ajayan, Potential appli-

cations of carbon nanotubes, in Carbon nanotubes: Topicsin Applied Physics, ed. A. Jorio, G. Dresselhaus andM. S. Dresselhaus, Springer, Berlin, 2008, vol. 111,pp. 13–61.

75 J. Lee, I. Y. Stein, S. S. Kessler and B. L. Wardle, ACS Appl.Mater. Interfaces, 2015, 7, 8900–8905.

76 D. Janas and K. K. Koziol, Nanoscale, 2014, 6, 3037.77 A. Kumar and G. U. Kulkarni, J. Appl. Phys., 2016, 119,

015102.78 R. Gupta, A. Kumar, S. Sadasivam, S. Walia, G. U. Kulkarni,

T. S. Fisher and A. Marconnet, ACS Appl. Mater. Interfaces,2017, 9, 13703–13712.

79 W. Liu, X. Zhang, G. Xu, P. D. Bradford, X. Wang, H. Zhao,Y. Zhang, Q. Jia, F.-G. Yuan, Q. Li, Y. Qiu and Y. Zhu,Carbon, 2011, 49, 4786–4791.

80 X. Wang, P. D. Bradford, W. Liu, H. Zhao, Y. Inoue,J.-P. Maria, Q. Li, F.-G. Yuan and Y. Zhu, Compos. Sci.Technol., 2011, 71, 1677–1683.

81 W. Bauhofer and J. Z. Kovacs, Compos. Sci. Technol., 2009,69, 1486–1498.

Nanoscale Paper

This journal is © The Royal Society of Chemistry 2019 Nanoscale, 2019, 11, 16327–16335 | 16335

Page 11: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Aligned Carbon Nanotube Morphogenesis Predicts

Physical Properties of their Polymer

Nanocomposites

Bharath Natarajan,a,b#† Itai Y. Stein,c,d† Noa Lachman,c,e Namiko Yamamoto,c,f Douglas S.

Jacobs,d Renu Sharma,a J. Alexander Liddle,a Brian L.Wardle c*

aCenter for Nanoscale Science and Technology, National Institute of Standards and Technology,

Gaithersburg, Maryland 20899, USA.bCorporate Strategic Research, ExxonMobil Engineering and

Research Company, Annandale, NJ, 08801, USA. cDepartment of Aeronautics and Astronautics,

Massachusetts Institute of Technology, Cambridge, Massachusetts 02139, USA. dDepartment of

Mechanical Engineering, Massachusetts Institute of Technology, Cambridge, Massachusetts

02139, USA eDepartment of Materials Science and Engineering, Tel Aviv University, Tel Aviv

6997801, Israel. eDepartment of Aerospace Engineering, The Pennsylvania State University,

University Park, Pennsylvania 16802, USA.

† These authors contributed equally to this work

# This work was primarily done while at the Center for Nanoscale Science and Technology,

National Institute of Standards and Technology, Gaithersburg, Maryland 20899, USA

Electronic Supplementary Material (ESI) for Nanoscale.This journal is © The Royal Society of Chemistry 2019

Page 12: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

1. Tomography and Image Analysis

1.1. 3D Reconstruction/Volume Fraction

The morphological information from tomographic TEM referenced in the main text is provided in

Figures S1, S2, and S3.

Figure S1. Volume-rendered reconstructions of (a) (0.44 ± 0.01) %, (b) (2.58 ± 0.25) %, (c) (4.04 ± 0.19) %, (d) (6.89 ± 0.43) % in situ Vf of A-CNT polymer nanocomposites (A-PNCs). The size of reconstructed volumes are: (a) 969 nm × 952 nm × 324 nm (b) 850 nm × 840 nm × 152 nm (c) 848 nm × 836 nm × 177 nm and (d) 764 nm × 841 nm × 211 nm.1 (e) (L to R) Images of neat epoxy (orange color), (0.44 ± 0.01) % and (6.89 ± 0.43) in situ Vf A-PNCs (black color) embedded in epoxy (f) Plot of the in-situ Vf versus as-densified ex situ Vf for the four Vfs of aligned-CNT nanocomposites shown in (a)-(d). Dashed line represents a straight line fit to the data. The uncertainties, which represent one standard deviation in measurements of 3 samples per nanocomposite Vf, are not visible as the error bars are smaller than the datapoints.

Page 13: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

1.2 CNT-CNT Proximity

Figure S2. Average CNT-CNT spacing and junction distances from tomographic TEM data and reconstructions: (a) Volume rendered reconstruction of representative (0.44 ± 0.01) %Vf sample, with typical cross-sectional XZ slice indicated. The centroids of the CNT cross-sections from every XZ slice in the reconstructed volume are obtained by particle analysis on ImageJ and stored along with the slice number. The inter-centroid distances are then calculated using Delaunay triangulation.1 The angle corrected average centroid distance minus the diameter of the CNTs is taken to be the average inter-CNT spacing () for the sample. (b) Average inter-CNT spacing (, nm) calculated from tomographic reconstructions of aligned CNT composites (■, uncertainties represent one standard deviation in measurements of 3 samples per nanocomposite Vf) and from SEM images of densified forests (●, uncertainties as indicated by Stein et. al.2,3) versus in situ Vf. (c) Representative histograms (binned by Freedman-Diaconis rule) of inter-CNT spacing measured from volumes shown in Figure S1, fit with log-normal distributions.

Page 14: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

1.3 Waviness

Figure S3. A-CNT tortuosity and waviness: (a) Illustration of CNTs with varying degrees of tortuosity (l/d) (b) Tortuosity plotted versus the in situ volume fraction (%). (d) 2D waviness ratio calculated from tomographic reconstruction of A-CNT composites (■, uncertainties represent one standard deviation in measurements of 3 samples per composite Vf) and SEM images of densified forests (●) versus the Vf.

The 2D CNT waviness in Figure S3d, defined as the ratio of the amplitude to the wavelength

of a sinusoidal function of the form (where a is the amplitude) may be (𝑤 = 𝑎/2𝜋) 𝑦 = 𝑎 𝑐𝑜𝑠𝑥

obtained from the tortuosity as below.

Page 15: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

𝜋

𝜋𝜋/2

∫‒ 𝜋/2

1 + 𝑎2𝑠𝑖𝑛2(𝑥) 𝑑𝑥

= 𝑙𝑑 (S1)

Although the 2D waviness is in general agreement with those measured from SEM images of as-

grown forests (wforest) in prior work, we find the values measured from polymer infiltrated

composites (wcomposite) to be much lower (e.g., at 4 vol %, wcomposite = 0.169 and wforest = 0.283;

wforest at 18 vol % ~ wcomposite at 0.44% ~ 0.185),4 further highlighting the need for in situ

assessments of the CNT morphology as done here even in a simple and well-controlled PNC

fabrication process as used in processing the A-CNTs via RTM6 epoxy infiltration to A-PNCs. We

surmise that stresses applied by the epoxy matrix during infiltration (capillary-assisted wetting,

or wicking) and curing are responsible for this partial “ironing out” of the waviness. The trends in

waviness (w) with Vf for the random helical system was found to follow the equation: Ʌ(a1(Vf)b1

+ c1 ± c2), where a1 = -0.04967, b1 = 0.3646, c1 = 0.2012, and c2 = 0.008, and Ʌ was evaluated to

be 0.68 ± 0.04. 5

A-PNC modeling results are shown in Figures S4 and S5 to supplement the mechanical modeling

discussion in the main text; similarly, Figure S7 for thermal and electrical conduction.

Page 16: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

2. Properties

2.1 Mechanical Properties

Figure S4. A-PNC random helical morphology and predicted CNT reinforcement modulus, after [5]: (a) Illustration showing top view of representative random helical CNT from a typical A-CNT ensemble employed in simulations (c) Plot of CNT reinforcement modulus (Eo) versus the waviness ratio (w) for various CNT modulus (Y = 1000 GPa) to matrix modulus (Em) ratios after [6].

Page 17: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Figure S5. Plot of A-PNC modulus from Handlin et al.4 versus in situ CNT Vf, with predictions from sinusoidal, helical and random helical waviness formulations shown. The under-prediction of properties by the sinusoidal and helical models is most likely because these idealized formulations overlook the stochastic mechanisms that lead to CNT waviness during growth and polymer infiltration. In reality there is significant nanoscopic surface roughness and CNT wall perturbation, which are only captured via the 'random' helical definition of the waviness.7,8

Page 18: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

2.2 Transport Properties

Figure S6. Volume-rendered reconstructions of (a) (0.44 ± 0.01) % and (b) (6.89 ± 0.43) in situ Vf of A-PNCs shown in Figure S1. The CNT-CNT junctions are highlighted by white dots to visualize the increase in junction density with Vf.

Page 19: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Figure S7. A-PNC axial thermal conductivity enhancements over neat epoxy, measured from the A-PNC samples studied in Marconnet et al. versus: (a) the originally reported using ex situ (■) and corrected or in situ (■) Vffs (The dashed lines represent the power-law fits to the data) (b) the estimated CNT-CNT junction density (NJ, m-3), showing linear scaling. Uncertainties indicated are standard deviations as measured by Marconnet et. al.9

Page 20: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

2.3 Discussion on alternate sources of thermal conduction in A-PNCs:

We note that the dependence of thermal conductivity on CNT-CNT contact density discussed in

the main text may only be true under certain conditions.10,11 Computational studies suggest that

the thermal boundary resistance (TBR) between a CNT and polymer has to be low (~ 10-8 to 10-9

m2K/W), particularly in the transverse conduction orientation, compared to the resistance of the

matrix.10,12 Shenogina et al. find that at relatively high TBRs, the heat dissipation between tubes

in contact and at separations up to 100 nm are identical due to thermal shielding by the matrix.11

For similar reasons, Duong et al. observe the transverse thermal conductivity in A-CNT

nanocomposites to be larger than the matrix only at low TBRs.10 Since Marconnet et al.

demonstrate a relatively small increase in the transverse conductivity in these systems, we

deduce that the CNT-matrix TBRs are indeed relatively low here. While a low TBR is a necessary

condition, it is not sufficient. The increasing trend in the thermal conductivity versus NJ plot also

supposes that the CNT-CNT TBR is comparable to or smaller than the CNT-polymer TBR.

Experimental work finds the area-normalized contact thermal resistance between aligned CNTs

to be on the order of 10-9 m2K/W at room temperature,13 indicating that the necessary and

sufficient conditions for the positive effect of CNT-CNT contacts are likely to have been met in

the nanocomposites studied here comprised of multi-walled A-CNTs and an epoxy matrix. With

the new morphological information presented here, future work to calculate the CNT-CNT and

CNT-polymer TBRs is enabled. The 3D morphological data provides further insight into

morphological features needed for such modeling.

Page 21: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Ensemble measurements on long CNT arrays have shown variations in the CNT alignment and

network structure along the height of the array.14 Furthermore, these studies note that CNTs may

fail to traverse the entire thickness of the array,14 (or to extend to the surface of the polymer)

leading to poor engagement with the source and sink. Since these systems lack perfect alignment

and likely continuity, the increased clustering with Vf also leads to an increased participation of

“lost” CNTs in transport phenomena and therefore higher thermal conductivities. From 3D object

counting,15 we find that the volume fraction of the most prominent bundle increases relatively

linearly with the Vf increase at first, but that the CNTs merge into large clusters (occupying > 40 %

of the CNT volume) as the total Vf increases beyond 4 % (Figure S8a-d). Assuming that, at the

theoretical packing limit of 83.45 %, the largest bundle volume fraction equals the total volume

fraction,2 we fit a 4 parameter asymmetric growth function through the plot of Vf of most

prominent network versus the measured Vf ( ) in Figure S8e. This fit 𝑦 = 1.453(1 ‒ 1/(1 + (

𝑥70.49

)1.69

captures the slow bundling of CNTs at low Vf s, the rapid increase in the rate of bundle formation

beyond 4%, and the slowing of the same process when CNT spacings are smaller than or

comparable to CNT diameters (Figure S8e, inset). We employ this function to estimate the Vfs of

the most prominent network for the corrected volume fractions in Marconnet et al.’s data. Again,

we observe a nearly linear trend in our plot of thermal conductivity enhancement versus the Vf

of the most prominent network, suggesting that the non-linear increase in the engagement of

CNTs in conduction leads in part to the non-linearity in the measured thermal property data

(Figure 4f). We note that this parameter might implicitly account for the effects of CNT contacts.

Page 22: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Another potentially influential factor causing the non-linearity is the improvement in the

alignment quality of the CNT arrays with densification. The increase in CNT alignment has been

theoretically and experimentally found to decrease CNT-CNT contact resistance due to the

increase in contact area going from a cross contact to an aligned contact: CNTs crossing at 90̊

were determined to have 2 orders of magnitude larger resistance than parallel CNTs in

contact.13,16 The new TEM 3D reconstructions allow us to determine the structure tensors of the

individual CNTs, and quantify the distribution around the CNT’s mean alignment (regardless of

the specimen alignment, Figure S9a-d).17 From this data, we find that the degree of alignment

improves with increasing Vf due to the increased spatial restriction imposed by

bundling/clustering. This improvement is shown in the plot of angular dispersion (one standard

deviation in the distribution of orientations about the mean) versus in situ Vf (Figure S9e). We

observe a steady decrease in dispersion of orientations with increasing Vf, suggesting that a

higher percentage of contacts are between CNTs crossing at low angles, which could lead to

improved transport through CNT junctions. While in the lateral direction this improved alignment

is not of particular importance,12 along the CNT axis the CNT resistance could drop significantly,

thereby explaining why anisotropy increases with Vf.

Page 23: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Figure S8. Analysis of bundling and other morphological descriptors contributing to non-linear thermal conductivity increase with in situ Vf of A-CNTs in A-PCNs: Connectivity-analyzed 3D visualizations of (a) 0.44 % (b) 2.6 % (c) 4 % and (d) 6.9 % in situ Vf of A-PNCs obtained from sample volumes shown in Figure 1, with individual clusters labeled according to the adjacent color scale. The units on the scale represent the fraction of CNT in situ Vf occupied by individual bundles. As is evident, at loadings above 4 % the CNTs cluster into larger bundles. (e) the volume fraction of the most prominent network versus the in situ Vf for the four Vfs of aligned-CNT nanocomposites studied here. The inset shows the fit through the data with limits at 83.45 %. The uncertainties represent one standard deviation in measurements of 3 samples per composite Vf. and (c) the volume fraction of the most prominent network. (f) A-PNC axial thermal conductivity enhancements over neat epoxy, measured from the A-PNC samples studied in Marconnet et al. versus the estimated Vf of the most prominent bundle.

Page 24: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

Figure S9. Color-coded orientation analysis of (a) 0.44 % and (b) 6.9% CNT, respectively. (c) and (d) – plotted frequency versus orientation of the volumes in (a) and (b), respectively. (f) Angular Dispersion (°) versus the in situ Vf. The uncertainties represent one standard deviation in measurements of 3 samples per composite Vf.

1 B. Natarajan, N. Lachman, T. Lam, D. Jacobs, C. Long, M. Zhao, B. L. Wardle, R. Sharma and J. A. Liddle, ACS Nano, 2015, 9, 6050–6058.

2 I. Y. Stein and B. L. Wardle, Phys. Chem. Chem. Phys., 2013, 15, 4033.

3 H. Cebeci, I. Y. Stein and B. L. Wardle, Appl. Phys. Lett., 2014, 104, 023117.

4 D. Handlin, I. Y. Stein, R. G. de Villoria, H. Cebeci, E. M. Parsons, S. Socrate, S. Scotti and B. L. Wardle, J. Appl. Phys., 2013, 114, 224310.

5 I. Y. Stein and B. L. Wardle, Nanotechnology, 2016, 27, 035701.

6 I. Y. Stein, D. J. Lewis and B. L. Wardle, Nanoscale, 2015, 7, 19426–19431.

7 V. Balakrishnan, M. Bedewy, E. R. Meshot, S. W. Pattinson, E. S. Polsen, F. Laye, D. N. Zakharov, E. A. Stach and A. J. Hart, ACS Nano, 2016, 10, 11496–11504.

8 E. R. Meshot, D. W. Zwissler, N. Bui, T. R. Kuykendall, C. Wang, A. Hexemer, K. J. J. Wu and F. Fornasiero, ACS Nano, 2017, 11, 5405–5416.

9 A. M. Marconnet, N. Yamamoto, M. A. Panzer, B. L. Wardle and K. E. Goodson, ACS Nano,

Page 25: Aligned carbon nanotube morphogenesis predicts physical properties … › sites › default › files › documents › ... · 2019-09-16 · properties of the CNS themselves, scale

2011, 5, 4818–4825.

10 H. M. Duong, N. Yamamoto, K. Bui, D. V. Papavassiliou, S. Maruyama and B. L. Wardle, J. Phys. Chem. C, 2010, 114, 8851–8860.

11 N. Shenogina, S. Shenogin, L. Xue and P. Keblinski, Appl. Phys. Lett., 2005, 87, 133106.

12 H. M. Duong, N. Yamamoto, D. V Papavassiliou, S. Maruyama and B. L. Wardle, Nanotechnology, 2009, 20, 155702.

13 J. Yang, S. Waltermire, Y. Chen, A. A. Zinn, T. T. Xu and D. Li, Appl. Phys. Lett., 2010, 96, 023109.

14 M. Bedewy, E. R. Meshot, M. J. Reinker and A. J. Hart, ACS Nano, 2011, 5, 8974–8989.

15 M. Doube, M. M. Kłosowski, I. Arganda-Carreras, F. P. Cordelières, R. P. Dougherty, J. S. Jackson, B. Schmid, J. R. Hutchinson and S. J. Shefelbine, Bone, 2010, 47, 1076–1079.

16 A. M. Marconnet, M. A. Panzer and K. E. Goodson, Rev. Mod. Phys., 2013, 85, 1295–1326.

17 R. Rezakhaniha, A. Agianniotis, J. T. C. Schrauwen, A. Griffa, D. Sage, C. V. C. Bouten, F. N. Van de Vosse, M. Unser and N. Stergiopulos, Biomech. Model. Mechanobiol., 2012, 11, 461–473.