http://www.iaeme.com/IJCIET/index.asp 967 [email protected]
International Journal of Civil Engineering and Technology (IJCIET)
Volume 8, Issue 11, November 2017, pp. 967–981, Article ID: IJCIET_08_11_096
Available online at http://http://www.iaeme.com/ijciet/issues.asp?JType=IJCIET&VType=8&IType=11
ISSN Print: 0976-6308 and ISSN Online: 0976-6316
© IAEME Publication Scopus Indexed
ACCIDENTAL OVERLOADING EFFECT ON
THE S-N CURVE OF WELDED JOINT OF
THREE STEEL GRADES
NADJITONON Ngarmaïm
LERTI: Laboratory for Study and Research in Industrial Technology,
Faculty of Exact and Applied Sciences, University of N'Djamena (Chad).
NGARGUEUDEDJIM Kimtangar
LERTI: Laboratory for Study and Research in Industrial Technology,
Faculty of Exact and Applied Sciences, University of N'Djamena (Chad).
Faculty of Exact and Applied Sciences, University of N'Djamena, Chad PB 1027.
BIANZEUBÉ Tikri
National Polytechnic Institute of Mongo (Chad).
RIMASBE BEOSSO Sylvain
GMMA: Mechanics, Materials and Acoustics, Department of Physics,
Faculty of Science, University of Ngaoundéré PB 454 Ngaoundéré Cameroon
ABSTRACT
This paper focuses on the analysis of the fatigue behaviour of soldered points of
tree grades of steel under loading with accidental overload. For analyzing the
sensitivity of the material to accidental overloads four expressions of F-N curve are
selected. Two accidental overload ratios (1.4 and 2.3) are applied.
The experimental results and those of the four F-N models indicate the beneficial
effect of accidental overloading for the stresses greater than the level stress of the
pivot point. Below this level of stress, accidental overload is detrimental to the
material. F-N curve obtained with a ratio 2.3 shows that the breaking strength Rm of
the material is greater than that of the curve F-N ratio 1.4. But, the value D of the
endurance limit obtained with a ratio 2.3 is lower than that obtained with a ratio of
1.4.
Key words: Accidental fatigue overload, welded sheet metal, welded joints, overload
sensitivity, S-N curves.
Cite this Article: NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar,
BIANZEUBÉ Tikri and RIMASBE BEOSSO Sylvain, Accidental Overloading Effect
on the S-N Curve of Welded Joint of Three Steel Grades. International Journal of
Civil Engineering and Technology, 8(11), 2017, pp. 967–981.
http://www.iaeme.com/IJCIET/issues.asp?JType=IJCIET&VType=8&IType=11
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 968 [email protected]
1. INTRODUCTION
Thanks to their excellent corrosion resistance properties, toughness and ductility the steel
HE360D, XE360D and XES are used in the automobile to achieve the hulls. The assembly of
the different parts is done by spot welding. These steels also have certain properties that
influence their behaviour and thus their cyclic fatigue resistance [1]. If the mechanical
properties of the new steels Very High Strength (THR) allow for a reduction of the plate
thickness, holding mechanical final assembly depends on the weld joints. Works on the
cyclical behaviour and fatigue resistance of the spot welding, in the presence of accidental
overload, have been the subject of studies of the team of Pascal Fatigue Institute of Clermont
Ferrand [2]. In this work, we study the sensitivity expressions of S-N curves when a periodic
accidental overload is applied. Two loading ratios (1.4 and 2.3) with respect to the base load
were used. Results of four expressions of S-N curve of their welded points and experimental,
including their sensitivity to accidental overloads, are compared in this research. The variation
of certain mechanical characteristics as the ultimate tensile strength Rm and the endurance
limit D are highlighted,
2. OBJECTIVE OF THE STUDY
The objectives of all fatigue tests on specimens welded by spot are, first the study of the
influence of accidental overloads occurring at regular intervals on their fatigue strength, and
secondly , to highlight the sensitivity of the expressions of the S-N curve overload. This study
is conducted for three different steel grades welded following a conforming adjustment to
industrial welding process. Two overload levels, from the analysis of loads, are often
encountered when driving vehicles and used for calculation of durability of automotive
components under service loading. The accidental overloads have an occurrence of an
overload cycle after 99 basic cycles. The overload ratio (maximum overload cycle on the
maximum value of the basic cycle) are equal to 1.4 or 2.3. The influence of load cycles is
analyzed in terms of life and / or maximum permissible value of the force of the basic cycles
for a life of 2.106 cycle regarded as the threshold of endurance in the automotive sector.
3. STUDY OF THE FATIGUE STRENGTH OF THE WELDED SPOT
The fatigue strength of a material is defined by the S-N curve, constructed in a stress-life
diagram (σa-N), established for a load ratio or mean stress given and constant frequency. The
endurance limit is conventionally defined to 2.106 cycles in the automotive environment. The
life N (number of cycles) is usually the sum of the numbers of cycles to initiation and
propagation of the crack to rupture. Given the difficulties to define in the critical area of the
weld points, a level representative of the constraint imposed cyclic loading, the fatigue
strength of welded point is defined by the F-N curve, where F is the maximum force applied
cycles to the test piece.
3.1. The factors of influence on the life of the welded point
Several factors influence the fatigue life of an assembly. It is essential to know and analyze
these factors well for reliable design. These key factors are recalled below.
3.2. Factors related to mechanical loading [4, 5]
3.2.1. Mean Stress
Experimental observations have shown that when a static positive stress σm is superimposed
on the cyclic loading amplitude σa the lifetime of the specimen or work piece decreases. The
reverse effect is also observed in the presence of an average compressive stress. For taking
this phenomenon into account, additional tests may be performed to establish a Haigh
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 969 [email protected]
diagram giving for a life fixed N, the allowable alternating stress σa according to the average
stress σm. Several mathematical models of the diagram such as the straight line of Goodman,
model of CETIM and the parabola of Gerber were made.
3.2.2. Frequency
The frequency of application of charging cycles is also a mechanical parameter which should
not be overlooked. When it increases, the life generally varies in the same direction, except in
the case where this increase would result in a heating of the material. In this context, we must
avoid to load a piece at frequencies close to its natural frequency to avoid dynamic
amplification effects (resonance).
3.2.3. Nature Forces Applied
The nature of the efforts is an important parameter. Indeed, various endurance limits are
obtained depending on the type of applied stress (tensile, bending, torsion). S-N curve is thus
valid for a given type of load. In the case of a variable amplitude loading, the loading
sequence is also an important factor. For an even distribution of stress cycles, different lives
are obtained if the load blocks are applied by increasing or decreasing amplitude. This is
explained by the fact that the stresses of high amplitude have more effect on the initiation and
propagation of cracks, and the level of increase in the damages related to a given cycle
depends on the level of damage reaches when it is applied.
3.3. Materials and Specimens of the Study
3.3.1. Materials
Three steels (HE360D, XE360D and XES) were selected because of their better mechanical
characteristics in the manufacture of automobile chassis (Renault). They are developed by
ArcelorMittal in the form of hot-rolled sheet. The plate thickness of the steel HE360D is 2.5
mm while the other two sheets of steel is 1.2 mm. The specimens from these plates are made
of their delivery condition and welding settings for industrial practice. The mechanics
behaviour of welded joints of each specimen was established for monotonous tensile tests
leaded to failure.
3.3.2. Description of Test Specimens
The test specimen consists of two thin sheets of dimensions 124 x 30 (mm) with a covering
surface 38 x 30 (mm). The two sheets (of the same material) are joined by the spot welding
method. At thickness almost, specimens used for fatigue tests are similar (Figure.1).
Given the specimen geometry, two types of misalignment (concentricity defect and
angular inclination defect) may be present (Figure.2). These defects will generate static stress
and strain (proportional to the applied forces) which will be added to the stress and strain of
applied load related.
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 970 [email protected]
Figure 1 Definition of the specimen [2].
Figure.2: (a): concentricity defect (spacing d); (b):
angular inclination defect (θ angle) [2].
Figure.3: Test tube mounted in a stiffener
with functional games. [2].
For solving these defects, the specimens are mounted in a tightener (Figure.3).
3.4. Description Loading
The test pieces produced are loaded in corrugated tensile of load ratio R equal to 0.1. This
type of loading is often called tensile shear because these two tensile forces applied to the two
sheets assembled by a welded spot will produce a shearing of the welded spot in the plane of
contact between the sheets. Fatigue tests were carried out on servohydraulique fatigue
machine MTS 810 (maximal capacity = ± 100 kN) of Mechanical and Engineering Laboratory
of IUT of Montluçon. All tests are conducted at room temperature and at a frequency of 30
Hz under load of constant amplitude and at 20 Hz for the fatigue testing of variable amplitude.
For measuring the effect of accidental overloads on the fatigue behaviour of plates
assembled by welded point, tests at two different ratios of accidental overload have been
made (Figure.4).
(a) (b)(a) (b)
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 971 [email protected]
Figure 4 Description of the loading sequence comprising accidental overloading ratio R every 100
cycles.
3.5. Expressions of F-N Curves used
Four expressions of F-N curves (maximum force of the basic cycle - life) are used. They are
those of Stromeyer, Wöhler, Basquin and Nadjitonon [6 - 10]. They are presented as linear
according to the following equations.
• Model Stromeyer: DFFlogbaNlog (1)
• Model Wöhler: bFaNlog (2)
• Model Basquin: FlogbaNlog (3)
• Model Nadjitonon:
F
FloglogbaNlog m (4)
Where the parameters a and b are related to the model and specific to the materials; they
are determined by the least squares method;
Fm is the ultimate force to break, F the maximal force and FD the strength to the endurance
limit of the reference material (loaded without accidental overload).
3.6. Results Analysis Method
The analysis is performed with respect to the relative difference E(%) of the number of cycles
given by the four expressions of F-N curves selected. This relative difference E is given by
the following equation:
100N
NNE
4,1
3,24,1 (5)
Where N1.4 and N2.3 are the numbers of cycles given by the expressions of the curve F-N
corresponding to the load ratio of 1.4 and 2.3 respectively.
Equation (5) allows assessing the sensitivity of welded points of these steels to accidental
overloads which may occur in actual use parts welded points. The behaviour between the two
F-N curves for the two accidental overload ratios is analyzed.
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 972 [email protected]
3.7. Results and Discussion
For each case of met-loading material, the results obtained with the four F-N curve models
(Stromeyer, Wöhler, Basquin and Nadjitonon) are presented in the form of the force-number
of cycles curves, plotted in the plane (log10 (N) log10 (F)) and compared to the experimental
curve.
The Table.1 shows the test results for the three grades of steel under loading with both
accidental overload ratios.
Table 1 Experimental data of maximum load and number of cycles for the three steel grades under
accidental overload ratios R = 1.4 and R = 2.3 [2].
Material
Static loading data Fatigue loading data
Fm (N) F(N) R = 1.4 R=2.3
FD (N) N1.4 (cycles) FD (N) N2.3 (cycles)
Steel HE360D 24270
3500
3375
3 032 400
3554
3 008 600
4000 1 422 100 3 008 600
4500 727 600 718 600
5000 409 600 410 600
5500 261 800 251 800
6000 176 200 177 200
Steel XE360D 12540
3500
2634
3 033 400
2625
3 037 000
4000 1 430 100 1 469 100
4500 731 900 708 700
5000 413 600 413 600
5500 252 800 258 800
6000 172 000 178 200
Steel XES 9480
3500
2958
5 322 200
2500
4 674 100
4000 1 946 778 1 857 300
4500 887 625 886 800
5000 414 676 467 800
5500 249 796 278 800
6000 154 187 183 000
The curves of evolution of the maximum force according to the number of cycles for the
four expressions of the F-N curve in the plane (log10(N) log10(F)) have similar appearance for
the two ratios of accidental load (R = 1.4 and R = 2.3). Overall expressions Wöhler (Wo) of
Nadjitonon (Na) and Basquin (Ba) are close to the experimental (Exp). Those of Stromeyer
(Stro) are highly offset from the other; it has a high inflection as shown in Figure.5.
Figure.5: F-N Curves based on accidental overload ratios for HE360D steel.
5,1
5,3
5,5
5,7
5,9
6,1
6,3
6,5
3,54 3,59 3,64 3,69 3,74
LOG10(N)
LOG10(F)
Steel HE360DStro-R1,4
Stro-R2,3
Wo-R1,4
Wo-R2,3
Na-R1,4
Na-R2,3
Ba-R1,4
Ba-R2,3
Exp-R1,4
Exp-R2,3
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 973 [email protected]
Figure 6 Plots of separated F-N curves based on accidental overload ratios for HE360D steel.
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 974 [email protected]
Figure 7 Relative difference E (%) of cycle numbers for HE360D steel.
The plotted separate curves corresponding to the four expressions have offset downwards
of the curve accidental overload ratio of 2.3 relative to that of the curve accidental overload
ratio of 1.4, for HE360D steel (Figure.6). It is the same for the experimental curve with the
two ratios. We can say that the overloading has a detrimental effect on the fatigue strength of
soldered points of this material for all the curves because the number of cycles decreases
when the ratio of the overload moves from 1.4 to 2.3. The relative difference in terms of
number of cycles, for both reports load does not exceed 1.5% for the four expressions
(Figure.7). This evidence is mixed when looking at the experimental plots for the two ratios
because the relative difference may reach 3.8% when the load increases. A corresponding
inflection is observed also around the point where the relative difference is 3.8% when the
load ratio Fm/FD is above 1.5.
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 975 [email protected]
3.7.2. XE360D Steel
The evolution curves of maximum strength according to the number of cycles for the four
expressions in the plane (log10(N) log10(F)) are, like the HE360D steel, similar appearance for
the two accidental overload ratios. Again, these are the expressions of Wöhler, Nadjitonon
and Basquin which are close to experimental ones. Those of Stromeyer are strongly shifted as
shown in Figure.8.
Figure 8 Curves F-N based on accidental overload ratios for XE360D steel.
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 976 [email protected]
Figure 9 Plots of separated F-N curves based on accidental overload ratios for XE360D steel.
Figure 10 Relative difference E (%) of cycle numbers for XE360D steel.
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 977 [email protected]
Figure.10 shows that, in ascending order of the loads applied, the relative variation of the
number of cycles is between -2.5% and 0.5% for the four expressions of F-N curve. This
variation between positive and negative values shows that the F-N curve for R = 2.3, rotates
relative to the R = 1.4 in the counterclockwise (trigonometric direction).
It means that there exists a charge level defining the pivot point below which the level of
accidental overload is harmful to the welded point, and beyond the overload is beneficial. The
variation of the relative difference of cycle numbers for the experimental results is between -
3.5% and 3.5%.The curve presents an inflection around the pivot point. The accidental
overload is harmful at this point and beneficial elsewhere.
3.7.3. XES Steel
The plots evolution of the maximum force according to the number of cycles in the plane
(log10(N) log10(F)) for the four expressions have this time appearance greatly offset from
those given by the HE360D and XE360D steels for the both accidental overload ratios. Again,
these are the expressions of Wöhler, Nadjitonon and the Basquin which are close to
experimental ones. Those of Stromeyer are strongly shifted as shown in figure.11.
Figure 11 Curves F-N based on accidental overload ratios to the XES steel.
It is found that, in ascending order of the applied loads, the relative variation of the
number of cycles is contained between 0.47% to -2.3% for the four expressions of the F-N
curve. It means that the S-N curves of load ratio 2.3 rotate in the counterclockwise relative to
that of the load ratio equal 1.4. That shows that there is a charge level defining the pivot point
below which the accidental overload is beneficial, and above which the overload is
detrimental to the material.
The abscissa of the pivot point for the expressions of Wöhler, Basquin and Nadjitonon as
well as that of experimental curves is between 3.63 and 3.68. While the abscissa of pivot point
corresponding to the expression of Stromeyer is between 3.68 and 3.73.
The figure.12 presents the pivoting of the curves of the four models as well as the
experimental curves.
5
5,2
5,4
5,6
5,8
6
6,2
6,4
6,6
6,8
7
3,53 3,58 3,63 3,68 3,73 3,78
LOG10(N)
LOG10(F)
Steel XES
Stro.R=1,4
Stro.R=2,3
Wo.R=1,4
Wo.R=2,3
Na.R=1,4
Na.R=2,3
Ba.R=1,4
Ba.R=2,3
ExpR=1,4
ExpR=2,3
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 978 [email protected]
Figure 12 Plots of separated F-N curves based on accidental overload ratios to the XES steel.
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 979 [email protected]
Figure 13 Relative difference E (%) of number of cycles (R = 2.3 and R = 1.4) for the XES steel.
Accidental overload is beneficial for heavy loads greater than that corresponding to the
pivot point. From the analysis of the results of the three grades of steel, we can say that for the
high numbers of cycles (N> 106 cycles) the fatigue resistance depends essentially on the level
of hardness of the material. For the intermediate and low numbers of cycles, it is the ductility
which becomes predominant. The hard steel HE360D has a weak fatigue resistance due to its
low ductility. While for small deformations, it has better resistance. There is a reverse result
for mild steel XSE. The semi-hard steel XE360 has an intermediate behaviour.
The essential elements in the design of structures are knowledge of the behaviour of this
structure under various stresses illustrated by the F-N curve, the quantification of the gradual
degradation of the material constituting the mechanical component by damage accumulation
Accidental Overloading Effect on the S-N Curve of Welded Joint of Three Steel Grades
http://www.iaeme.com/IJCIET/index.asp 980 [email protected]
laws and the severity of a state of multiaxial stress (repeated or alternating fatigue limits)
compared to simple statements.
Figure 14 (a) Negative effect of overloading in fatigue (gap between the F-N curves of the two
overload ratios) on the hard steel; (b): harmful and beneficial effects (pivoting of the two F-N curves
around a pivot point) of the accidental overload level on mild and semi-hard steel.
In the case of accidental overload, the F-N curves show a change of tensile strength Rm
(Figure.14a) and the endurance limit D when accidental overload ratio varies (Figure.14b).
These two parameters have inverse variations illustrating the harmful and beneficial
effects of an accidental overload in terms of number of cycles (reducing and increasing of the
number of cycles). That seems to reflect the expressions of the F-N curve of the three grades
of steel (hard, semi-hard and mild) [5, 11].
5. CONCLUSIONS
The study of the sensitivity of the three grades of steel to periodic accidental overloads reveals
that:
- The effects of the periodic accidental overloads are detrimental to the fatigue strength for
hard steel HE360D. The effect produces a marked weakening of fatigue properties.
- The effects of these surcharges are beneficial to the fatigue strength for semi-hard steel
XE360D and mild steel XES. They can significantly increase the life.
In summary, the accidental overloads occurring at the frequency of overload every 99
basic cycles are beneficial to the fatigue strength of soldered points of mild and semi-hard
steel.
REFERENCES
[1] C. KPODEKON, L. TALEB, S. TAHERI, 24-28 August 2009. Study of the effect of pre-
hardening on the lifetime of an austenitic stainless steel 304L - 19th French Congress of
Mechanics, Marseille.
[2] Bianzeubé TIKRI, February 2012. Study of the influence of overloads on behavior the
fatigue behavior of spot welded steels. Thesis of Doctorate of the University Blaise
Pascal-Clermont Ferrand II, Order n ° N °: D.U. 2224 EDSPIC, 553p.
[3] Sylvain DANCETTE, 2009. Mechanical behavior of spot welds: Mechanisms and
Prediction Strategies for Automotive Steel Sheet. Doctoral Thesis Order N ° 2009-ISAL-
0039, 228p.
[4] Jean LEMAITRE and Jean-Louis CHABOCHE, 1996. Mechanics of solid materials.
Edition: DUNOD, 2nd edition, 544p.
NADJITONON Ngarmaïm, NGARGUEUDEDJIM Kimtangar, BIANZEUBÉ Tikri and
RIMASBE BEOSSO Sylvain
http://www.iaeme.com/IJCIET/index.asp 981 [email protected]
[5] Claude BATIA and Jean-Paul BAILLON, 1980. The fatigue of materials and structures.
Edition Maloine S.A. (Collection University of Compiegne), 547p.
[6] N. NGARMAIM, B. TIKRI, B. BASSA, N. KIMTANGAR, F. PENNEC & J-L.
ROBERT, 2014. A New Expression of the Curve S-N in Fatigue based on the Concept of
the "Weakest Link" of Weibull By. Global Journal of Researches in Engineering: A
Mechanical and Mechanical Engineering Volume 14 Issue 3 Version 1.0.
[7] Christian LALANNE, 1999. Mechanical vibrations and shocks. Tome I Damage by
Fatigue. Edition HERMES Sciences. Paris 389p.
[8] Christian LALANNE. Vibration and Mechanical Shocks Volume 4: Damage by Fatigue
Edition HERMES Sciences p383.
[9] Ngarmaim Nadjitonon, 2010. Contribution to the modeling of fatigue damage. Doctorate
thesis of the Blaise Pascal University Clermont-Ferrand II, Order number: D.U 2057 -
EDSPIC: 99ISAL0056.
[10] N. KIMTANGAR, 2003. Contribution to the study of the laws of fatigue damage. Thesis
of the INSA of Lyon, Order No. 03 ISAL 0025, 115p.
[11] J.-P. LARALD, 1986. Resistance of Materials II: Compound stresses. Collection of
Industries. Edition MASSON, 260p.
[12] Satyam Kumar, Dr. Uday Krishna Ravella , Atul Kumar Shrivastava, Dr.Midathoda Anil
and Dr. S. K. Kumar Swamy A Review on Human Cervical Fatigue Measurement
Technologies and Data Analysis Methods. International Journal of Mechanical
Engineering and Technology, 8(7), 2017, pp. 1474–1484.
[13] G. Boopathy, K.R. Vijayakumar and M. Chinnapandian. Fabrication and Fatigue Analysis
of Laminated Composite Plates. International Journal of Mechanical Engineering and
Technology, 8(7), 2017, pp. 388–396.
[14] P. Radha Krishna Prasad, P. Ravinder Reddy and K. Eshwar Prasad. Effect of Welding
Parameters on Mechanical Properties of Friction Stir Welded Joints of AA6082 and
AA6061 Aluminium Alloys. International Journal of Mechanical Engineering and
Technology, 8(6), 2017, pp. 564–574.
[15] G. Vamsi Durga Mohan, K. S. Rao and P. Srinivasa Rao. Enhancement in Mechanical
Properties of Vibratory Welded Joints: An Overview. International Journal of Mechanical
Engineering and Technology, 8(2), 2017, pp. 50–55.